Electrical Resistivity and Phase Evolution of Fe–N Binary System at High Pressure and High Temperature

Partitioning experiments and the chemistry of iron meteorites indicate that the light element nitrogen could be sequestered into the metallic core of rocky planets during core–mantle differentiation. The thermal conductivity and the mineralogy of the Fe–N system under core conditions could therefore influence the planetary cooling, core crystallization, and evolution of the intrinsic magnetic field of rocky planets. Limited experiments have been conducted to study the thermal properties and phase relations of Fe–N components under planetary core conditions, such as those found in the Moon, Mercury, and Ganymede. In this study, we report results from high-pressure experiments involving electrical resistivity measurements of Fe–N phases at a pressure of 5 GPa and temperatures up to 1400 K. Four Fe–N compositions, including Fe–10%N, Fe–6.4%N, Fe–2%N, and Fe–1%N (by weight percent), were prepared and subjected to recovery experiments at 5 GPa and 1273 K. These experiments show that Fe–10%N and Fe–6.4%N form a single hexagonal close-packed phase (ɛ-nitrides), while Fe–2%N and Fe–1%N exhibit a face-centered cubic structure (γ-Fe). In separate experiments, the resistivity data were collected during the cooling after compressing the starting materials to 5 GPa and heating to ~1400 K. The resistivity of all compositions, similar to the pure γ-Fe, exhibits weak temperature dependence. We found that N has a strong effect on the resistivity of metallic Fe under rocky planetary core conditions compared to other potential light elements such as Si. The temperature-dependence of the resistivity also revealed high-pressure phase transition points in the Fe–N system. A congruent reaction, ε ⇌ γ’, occurs at ~673 K in Fe–6.4%N, which is ~280 K lower than that at ambient pressure. Furthermore, the resistivity data provided constraints on the high-pressure phase boundary of the polymorphic transition, γ ⇌ α, and an eutectoid equilibrium of γ’ ⇌ α + ε. The data, along with the recently reported phase equilibrium experiments at high pressures, enable construction of a phase diagram of the Fe–N binary system at 5 GPa.