Next Article in Journal
Mechanically Recycled PLA Films Reinforced with Rice Husk and Carbonized Rice Husk Particles
Previous Article in Journal
From Environmental Burden to Energy Resource: Waste Plastic-Derived Carbons for Sustainable Batteries and Supercapacitors
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 18
Issue 8
10.3390/polym18080984
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Color Stability and Photo-Degradation of Steamed Beech Wood with False Heartwood Under UV Exposure

by
Michal Dudiak
*,
Eva Výbohová
and
Ladislav Dzurenda
Faculty of Wood Sciences and Technology, Technical University in Zvolen, T.G. Masaryka 24, 960 01 Zvolen, Slovakia
*
Author to whom correspondence should be addressed.
Polymers 2026, 18(8), 984; https://doi.org/10.3390/polym18080984
Submission received: 26 March 2026 / Revised: 10 April 2026 / Accepted: 15 April 2026 / Published: 17 April 2026
(This article belongs to the Section Biobased and Biodegradable Polymers)
Browse Figures
Versions Notes

Abstract

This work analyses the influence of hydrothermal treatment (steaming) on the color stability and photochemical degradation of beech wood (Fagus sylvatica L.) with false heartwood under the influence of UV radiation. Samples in the native state and after steaming at temperatures of 105 °C (Mode I) and 120 °C (Mode II) were exposed to simulated aging in a Xenotest device for 360 h. Color changes were assessed in the color space CIE L*a*b* and surface chemical changes using ATR-FTIR spectroscopy. The results showed that unsteamed wood darkens significantly under the influence of UV radiation (ΔL* = −10.2), while wood steamed at 120 °C shows the opposite trend—lightening (ΔL* = +8.8). The color difference ΔE* reached values of 12 to 16 units for unsteamed wood, which indicates a complete color change. Steaming at higher temperatures successfully homogenizes the color of the sapwood and false heartwood and ensures their subsequent uniform visual aging.

1. Introduction

Beech wood (Fagus sylvatica L.) is classified as a diffusely porous wood species without natural heartwood, which may develop false heartwood at an older age. It is a brown-to-red wood with a higher content of lignin and some groups of extractives, which differs from sapwood not only in color but also in texture. Although it sometimes contains less of these compounds, it still exhibits different physical and chemical properties [1]. The formation of false heartwood is influenced by ecological conditions and the growth environment of the tree, with the key factor being the penetration of air into the trunk through wounds on the bark or branches. This process leads to the oxidation of carbohydrates and starches in living or partially dead cells, which results in the formation of polyphenolic compounds. These subsequently spread to the surrounding tissue and cause its typical brown-to-red color. The differences between sapwood and false heartwood have a fundamental impact on wood processing, including steaming technology [2,3,4,5,6,7,8,9,10].
Wood steaming is a technological process in which wood is treated with saturated water steam in high-temperature closed devices, such as autoclaves. Its main aim is to improve the technological properties of wood, such as its flexibility, color uniformity, and reduction of internal stresses. When exposed to steam at temperatures from 100 to 140 °C, some cell wall components, especially lignin and hemicelluloses, are hydrolyzed, which leads to a change in the structure of the wood. Already in the initial stages of heat treatment, partial hydrolysis of hemicelluloses and the release of water-soluble substances take place. These chemical transformations depend on the temperature and duration of the process and lead to the gradual decomposition of polysaccharides. Under the influence of the acids present, such as acetic and formic acids, the oxidation of carbohydrates and pectins occurs, which dehydrates pentoses and forms 2-furaldehyde [11,12,13,14].
At the same time, changes in the lignin structure occur, where quinonemetide structures, free radicals, and phenolic hydroxyl groups are formed, which leads to the formation of new quinone-type structures. These changes are manifested by visible darkening of the wood, which affects not only its appearance, but also its physical and mechanical properties [11,12,15,16,17].
The color of wood is one of the key physical and aesthetic properties which significantly affects its use, especially in the furniture industry and in the production of floors and other decorative elements. Its character is determined by the presence of various chemical components, such as lignin, tannins, and other organic substances contained in the cellular structure of wood. The steaming process causes chemical reactions that change these components, which is subsequently manifested by a change in the color of the wood. In the case of beech wood, these changes can be significant—while the light part of the wood (sapwood) tends to fade, the false heartwood can either darken or lighten, depending on the steaming parameters, such as temperature and duration of the process [18,19].
The color of wood also changes due to long-term exposure to sunlight on its surface. Under the influence of radiation, the surface of the wood most often darkens and acquires a yellow-to-brown hue. Many scientific works deal with this change in the color of wood [20,21,22,23,24,25], or after accelerated weathering [14,16,20,26,27,28,29,30,31,32,33].
The sunlight that hits the wood is partly reflected and partly absorbed. The infrared component of the spectrum is converted into heat, while UV radiation and part of visible light (wavelength λ = 200–400 nm) initiate photochemical reactions, primarily photolytic and photooxidative processes, which take place mainly in lignin, but also in polysaccharides and other accompanying substances of wood. Lignin is the most susceptible to photodegradation, absorbing 80–85% of UV radiation, while carbohydrates absorb 5–20% and accompanying substances approximately 2% [21]. These reactions lead to the cleavage of lignin macromolecules, resulting in the formation of phenolic hydroperoxides, free radicals, and carbonyl and carboxyl groups. To a lesser extent, polysaccharides also undergo depolymerization, which breaks down into molecules with a lower degree of polymerization, while gaseous products such as CO, CO2, and H2 are also formed [15,20,22,23,24,34,35,36].
The aim of this work is to analyze the color stability of beech wood with false heartwood after steaming with saturated water vapor, through simulated aging using UV radiation in the Xenotest Q-SUN Xe-3-H device Q-Lab Corporation, Westlake, OH, USA. Changes in wood color are evaluated using the CIE L*a*b* color space coordinates, the total color difference ∆E*, and ATR-FTIR spectroscopy.

2. Materials and Methods

2.1. Material

For the purposes of the research, 25 beech trunks (length 6.2 m) exhibiting false heartwood were selected. The timber was sourced from the Central Slovakian region, specifically from the Štiavnické vrchy locality (GPS coordinates: 48.4161247 N, 18.8593111 E). Subsequently, beech blanks with false heartwood with a moisture content of wp = 58.1 ± 3.7% were produced by longitudinal and transverse sawing with the following dimensions: thickness: h = 40 mm, width: w = 200 mm, length: d = 900. In total, 15 pieces for each mode were steamed in a pressure autoclave: APDZ 240 at Sundermann s.r.o. (Banská Štiavnica, Slovakia), according to the modes listed in Table 1, in order to unify the color difference between the light sapwood and the darker zone of the false heartwood. The principle of the procedure and the conditions of the technological process of steaming beech wood are given in the publication [37].
Both unsteamed and steamed beech blanks were dried to a final moisture content of w = 10 ± 0.5%, using a low-temperature regime to preserve the treatment-induced color. Drying was performed in a KAD 1 × 6 conventional hot-air dryer (KATRES s.r.o., Jihlava, Czech Republic) following a specific two-stage protocol [38]. After drying, the blanks were machined using a JET JPT-410HH milling machine (STROJE Slovensko, Banská Bystrica, Slovakia) equipped with a helical cutter head. This process achieved a high-quality surface with a mean roughness (Ra) of 3.0 to 5.0 µm, ensuring optimal conditions for subsequent optical measurements. Experimental samples with dimensions of h = 15 mm, width w = 100 mm, and length d = 100 mm were prepared, with each specimen containing both sapwood and false heartwood zones for color fastness testing.

2.2. Color Measurement of Beech Wood

The surface color of unsteamed and steamed beech wood samples with false heartwood was analyzed in the CIE L*a*b* color space using a tristimulus colorimeter Color Reader CR-10 (Konica Minolta, Tokyo, Japan). The color space CIE L*a*b* is three-dimensional and covers the entire range of human color perception. It is based on the opposing color model of human vision, where red and green form an opposing pair and blue and yellow form an opposing pair. This makes CIE*a*b* a Hering opposing color space. The nature of the transformations also characterizes it as a color space with a chromatic value. The lightness value, L*, defines black at 0 and white at 100. The a* axis is relative to the opposing colors of the green–red color, with negative values towards green and positive values towards red. The b* axis represents the opposing colors of the blue–yellow color, with negative numbers towards blue and positive numbers towards yellow. Measurements were performed using a D65 light source, an 8 mm diameter optical sensing aperture, and a CIE 10° standard observer, which is recommended for evaluating wood surface color due to its better correlation with visual perception on larger areas. The color measurements were performed on the radial surfaces of the wood samples before and after irradiation.
The color evaluation of beech wood with false heartwood in the CIE L*a*b* color space before irradiation is shown in Table 2.
The overall color variation ΔE* of beech wood surfaces containing false heartwood, induced by UV exposure, was calculated in accordance with the ISO 11664-4 standard [39] using the following formula:
Δ E * = L 360 * − L 0 * 2 + a 360 * − a 0 * 2 + b 360 * − b 0 * 2
where L*0; a*0; b*0 values in the color space coordinates of the surface of dried milled non-steamed and steamed beech wood before exposure;
L*360; a*360; b*360 values in the color space coordinates of the surface of dried milled non-steamed and steamed beech wood after exposure to UV radiation in the xenotest [39].

2.3. Exposure of Beech Wood to UV Radiation in a Test Chamber

To simulate indoor UV degradation, samples were exposed to a full-spectrum xenon arc lamp (1800 W) in a Q-SUN Xe-3-H test chamber for a total duration of τ = 360 h. The environmental parameters were set to a dry mode with a black panel temperature of 63 °C and an irradiance of 0.35 W/m2—340 nm. Colorimetric data were collected systematically throughout the irradiation period at τ = 24 h increments.

2.4. Determination of Chemical Changes in Wood Using ATR-FTIR Spectroscopy

The chemical changes on the surface of the wood samples induced by UV irradiation were analyzed using FTIR spectroscopy. The measurements were performed with a Nicolet iS 10 FTIR spectrometer (Thermo Fisher Scientific, Madison, WI, USA) equipped with an attenuated total reflectance (ATR-FTIR) accessory featuring a diamond crystal. The following scanning parameters were applied: a wavenumber range of 4000–650 cm−1, 32 scans per measurement, and a spectral resolution of 4 cm−1. The obtained spectra were evaluated using the OMNIC 9 spectroscopic software. The band ratios (e.g., H1592/H1370) were calculated from the peak heights (H) of the respective absorption bands.

2.5. Processing and Formal Statistical Testing of Experimental Data

To assess the correlation between different sample sets, the experimental data were processed using the TIBCO Statistica 14.0 program (TIBCO Software Inc., Palo Alto, CA, USA). The assessment involved both t-tests and ANOVA to determine if observed color changes were statistically significant. All relationships were interpreted based on the calculated p-values, and the resulting trends were visualized graphically.

3. Results and Discussion

The color of unsteamed and steamed beech wood with false heartwood before and after UV irradiation in the Q-SUN Xe-3-H test chamber is shown in Figure 1.
Visual evaluation of samples exposed in the Q-SUN Xe-3-H chamber confirmed that the reaction of the wood surface to UV radiation is critically dependent on its previous heat treatment.
In unsteamed beech wood, we observed a significant loss of the original light white-yellow-gray color. Due to the influence of photochemical reactions, the surface visibly darkened and acquired a rich yellow-brown hue. This phenomenon is explained by [15,40] by the degradation of lignin and extractives, which creates new chromophoric groups, mainly of the quinone type, that intensively absorb visible light in the blue region of the spectrum, which we perceive as yellowing and browning.
The steaming process fundamentally changes not only the initial color of the wood, but also the kinetics of its changes during simulated aging: Mode I (105 °C): The original pale pink-brown color obtained by steaming showed a slight darkening and shift to brown-yellow shades after exposure. In terms of visual stability, this mode appears to be more stable than native wood, which is also confirmed by the lower values of the total color difference ΔE* compared to unsteamed sapwood. Mode II (120 °C): We noted the most interesting trend in samples steamed with saturated water steam at a temperature of 120 °C. The originally saturated brown-red color lightened under the influence of UV radiation. This phenomenon of lightening (increase in the L* coordinate) in dark steamed wood indicates that the thermodegradation products (formed during steaming in an autoclave) are less stable to UV radiation than native lignin and that their gradual decomposition or lightening occurs under the action of light.
The results show that although steaming successfully homogenizes the color between sapwood and false heartwood, their subsequent photochemical stability remains affected by the intensity of the thermal treatment. While at 105 °C, the processes of formation of new chromophores dominate (darkening), at 120 °C, the degradation processes of existing dyes prevail (lightening).
Experimental data obtained by measuring color coordinates in the CIE Lab* space were subjected to statistical analysis of variance (ANOVA) to determine the influence of two factors: steaming mode and length of UV exposure, and were graphically drawn in Figure 2, Figure 3, Figure 4 and Figure 5.
The analysis confirmed that before irradiation, there was a significant difference (p < 0.001) in lightness between unsteamed white (77.8 ± 1.9) and false core (66.6 ± 1.7).
Unsteamed samples: UV radiation caused a sharp and statistically significant decrease in lightness L* in the first 96 h of exposure (from 77.8 to approximately 68.0). The total decrease in lightness in white was 10.2 units.
Steamed samples (Mode II): The statistical model showed the opposite trend, where, after the initial phase, a lightening of the surface occurred. The lightness of samples steamed at 120 °C increased by 8.8 (sapwood) and 8.5 (false heartwood), indicating suppression of darkening due to the previous heat treatment.
Coordinate a*: An initial decrease was recorded for unsteamed sapwood, followed by an increase of 5.3 units, which is visually perceptible as browning. For steamed wood (Mode II), this change was statistically insignificant (0.0 to 0.5), indicating a high stability of the red shade after steaming.
Coordinate b*: All samples showed a statistically significant increase in yellowness. The highest photochemical yellowing rate was measured for unsteamed sapwood (Δb* = 11.9) and for steamed sapwood at 105 °C (Δb* = 10.5).
Visual and physical changes in the color of the wood surface are a direct consequence of photochemical reactions initiated by UV radiation in the wavelength range λ = 200–400 nm. The main recipient of this radiation is lignin, which absorbs up to 80–85% of the incident energy, leading to its degradation and the formation of new chromophoric groups (carbonyl, carboxyl groups, and free radicals) [15,41].
The significant darkening of unsteamed wood is in accordance with the works of [20,41], who attribute this phenomenon to the formation of new chromophoric structures, such as quinones and carbonyl groups.
An interesting finding is the behavior of samples steamed at a higher temperature (120 °C). These samples lighten after exposure to UV radiation. This phenomenon may be explained by the fact that higher steaming temperatures are associated with a more pronounced disruption of the lignin–carbohydrate complex, thereby making lignin more accessible to subsequent photochemical processes. Consequently, the formation of chromophoric structures increases, which initially manifests as darker coloration of the wood [42]. However, these newly formed chromophores are less resistant to UV radiation than native lignin and are subject to lightening or further photochemical decomposition upon exposure to light, which leads to an increase in the lightness L*.
Analysis of the ΔE* graph (Figure 6) for unsteamed and steamed beech samples reveals fundamental differences in the kinetics and intensity of their photodegradation. The ΔE* graph shows that the most drastic changes occur in the initial phase of exposure (first 48–96 h). After just 24 h of irradiation in the Q-SUN chamber, the ΔE* values for all variants exceed the threshold of 3.0, which is classified as a “very noticeable change” according to the National Bureau of Standards (NBS) criteria [43].
For unsteamed sapwood, the ΔE* reaches values in the range of 12 to 15 units after 360 h, which represents a “completely different color” compared to the original state. This steep increase is in line with the work of [44], who state that native lignin on the surface of hardwoods undergoes immediate photooxidation to form dark chromophoric products.
The graphs clearly differentiate the surface resistance according to the steaming temperature:
Steaming at 105 °C (Mode I): These samples show slightly lower final ΔE* values than unsteamed wood, but the trend is still increasing, dominated mainly by the increase in yellowness (Δb*).
Steaming at 120 °C (Mode II): Although the initial ΔE* value is high, the curve tends to stabilize early. Unlike unsteamed wood, where ΔE* is driven by darkening, in the 120 °C mode, the resulting difference is the result of lightening. This fact is important from a design perspective: while unsteamed beech turns brown-gray over time, steamed beech at higher temperatures retains its brightness and only changes its color undertone.
From an industrial perspective, the most significant finding is the convergence of the ΔE* curves for sapwood and false heartwood for steamed samples. While in the untreated state, the difference in their photochemical response is low (sapwood visually degrades faster), the steaming process increases these differences. Statistically insignificant differences between ΔE* of sapwood and false heartwood at 120 °C confirm that heat treatment not only unifies the initial shade, but also ensures uniform visual aging of the wood surface.
In order to identify chemical changes in beech sapwood and false heartwood, ATR-FTIR analysis was performed (Figure 7 and Figure 8).
In unsteamed wood, the proportion of aromatic structures is higher in the false heartwood than in the sapwood. This is indicated by the higher relative intensity values of the H1592/H1370 and H1504/H1370 cm−1 bands in the false heartwood spectrum (1.89 and 0.93, respectively) compared with the sapwood spectrum (1.44 and 0.85, respectively). Lignin contributes mainly to the intensity of these absorption bands; however, to a lesser extent, aromatic nuclei from some groups of extractives may also contribute.
As a result of steaming, the absorption band with a maximum at 1504 cm−1 shifts to a higher wavenumber. A detailed analysis of the spectra revealed that during the steaming process, especially in mode II, a new absorption band at 1518 cm−1 is formed, which overlaps with the original band at 1504 cm−1. This suggests that pseudo-lignin is formed by condensation of polysaccharide degradation products. Similar aromatic aggregates formed during thermal or hydrothermal processing have been reported by other authors [45,46,47,48].
After irradiation, a rapid decrease or complete disappearance of the absorption bands at 1504 cm−1, 1461 cm−1, 1423 cm−1, 1326 cm−1, and 1235 cm−1 was observed. This is mainly associated with the degradation of lignin. This is in agreement with [49], who found a statistically significant relationship between lignin decay indicated by the I1507/I1375 peak ratio and the chromatic coordinates L* and a* under the artificial photo-irradiation of normal and red heart beech wood.
The change in the shape of the absorption band and its intensity is also evident in the wavenumber range between 1350 and 1290 cm−1. While in the spectra of wood before irradiation, a single absorption band with a maximum at 1327 cm−1 is present in this region, in the spectra of wood after irradiation, a doublet with maxima at 1333 and 1316 cm−1 is observable, with the band at 1316 cm−1 being more intense. These changes indicate the degradation of the S-ring plus the condensed G-ring in the lignin macromolecule, since the band at 1333 cm−1 belongs to the S-ring plus the condensed G-ring in the lignin macromolecule and the band at 1316 cm−1 to the CH2 wagging in cellulose.
Other significant changes in the FTIR spectrum induced by UV radiation relate to the absorption bands of carbonyl groups (Table 3). The absorption band of unconjugated C=O groups at 1736 cm−1, and the band of conjugated C=O and C=C, and aromatic ketones at 1650 cm−1 increase markedly in all samples under the influence of UV radiation. Changes in the intensity of the absorption band at 1736 cm−1 are influenced by several processes, which often have opposing effects on this band. On the one hand, the degradation of hemicelluloses, which preferentially occurs during steaming, leads to a decrease in their intensity. On the other hand, oxidation reactions—occurring mainly due to UV irradiation—lead to the formation of new carbonyl and carboxyl groups, which results in an increased intensity of the absorption bands at 1736 cm−1 and 1650 cm−1.
It is known that lignin is the most UV-sensitive component among all wood constituents [22,30,34]. Degradation of lignin’s aromatic bonds results in the generation of free radicals. These radicals subsequently react with oxygen, yielding carbonyl groups [50]. However, the decrease in lignin on the wood surface also disrupts the lignin–carbohydrate complex and makes the cellulose structure accessible to UV radiation, thereby improving the conditions for cellulose oxidation [45,49].
The observed relationships between changes in characteristic lignin absorption bands (evaluated via FTIR peak ratios) and chromaticity coordinates suggest that the total color difference (ΔE*) serves as a reliable indicator of photochemical degradation within the lignin–carbohydrate complex on beech wood surfaces. Our analysis demonstrates a strong correlation between ΔE* kinetics and the intensity of surface photochemical transformations. Specifically, high ΔE* values across all sample types correspond directly to the decrease in absorbance within the aromatic skeleton regions of the FTIR spectra.

4. Conclusions

The research confirmed that the steaming of beech wood with false heartwood significantly affects its visual and chemical response to UV radiation. While unsteamed beech wood undergoes intense yellowing and darkening due to photooxidation of native lignin, wood steamed at 120 °C shows a lightening, which is caused by the decomposition of less stable chromophores formed during the steaming process. Steaming at this higher temperature not only successfully unifies the initial color shade between sapwood and false heartwood, but also ensures their statistically identical visual aging over time. In addition, high stability of the red shade was recorded for wood steamed at 120 °C, while changes in the a* coordinate due to UV radiation were statistically insignificant. From the point of view of industrial use in interiors, it can be stated that the most suitable technology for achieving a color-stable and visually uniform surface of beech material with false heartwood is steaming with saturated water steam at a temperature of 120 °C.

Author Contributions

M.D. designed the whole study; M.D., E.V. and L.D. conducted data collection, modeling, and results analysis; M.D. and E.V. wrote the original draft paper; M.D., E.V. and L.D. revised and edited the paper. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by the Slovak Research and Development Agency under the contract no. APVV-21-0051 “Research of false heartwood and sapwood of Fagus sylvatica L. wood in order to eliminate color differences by the process of thermal treatment with saturated water steam”.

Data Availability Statement

The original contributions presented in this study are included in the article. Further inquiries can be directed to the corresponding author.

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Dzurenda, L.; Dudiak, M.; Kučerová, V. Differences in Some Physical and Chemical Properties of Beechwood with False Heartwood, Mature Wood and Sapwood. Forests 2023, 14, 1123. [Google Scholar] [CrossRef] [Scilit]
  2. Bauch, J.; Koch, G. Biologische und Chemische Untersuchungen über Holzverfarbungen der Rotbuche (Fagus sylvatica L.) und 332 Möglichkeiten Vorbeugender Maßnahmen; Abschlussbericht; Bundesforschungsanstalt für Forst- und Holzwirtschaft; Universität Hamburg: Hamburg, Germany, 2001. [Google Scholar]
  3. Račko, V.; Čunderlik, I. Qualitative and quantitative evaluation of false heartwood in beech logs of various age and qualitative structure. Wood Res. 2006, 51, 1–10. [Google Scholar]
  4. Molnár, S.; Németh, R.; Fehér, S.; Tolvaj, L.; Papp, G.; Varga, F. Technical and technological properties of Hungarian beech wood consider the red heart. Wood Res. 2001, 46, 21–30. [Google Scholar]
  5. Račko, V.; Čunderlík, I. Mature wood as a limiting factor in the formation of a false heartwood beech (Fagus sylvatica L.). Acta Fac. Xylologiae Zvolen 2010, 52, 15–24. [Google Scholar]
  6. Molnar, S.; Tolvaj, L. Colour homogenisation of different wood species by steaming. In Interaction of Wood with Various Forms of Energy; Technical University in Zvolen: Zvolen, Slovakia, 2002; pp. 119–122. [Google Scholar]
  7. Dzurenda, L.; Dudiak, M. Cross-correlation of color and acidity of wet beech wood in the process of thermal treatment with saturated steam. Wood Res. 2021, 66, 105–116. [Google Scholar] [CrossRef] [Scilit]
  8. Barański, J.; Klement, I.; Vilkovská, T.; Konopka, A. High temperature drying process of beech wood (Fagus sylvatica L.) with different zones of sapwood and red false heartwood. BioResources 2017, 12, 1861–1870. [Google Scholar] [CrossRef] [Scilit]
  9. Kollmann, F.P. Technologie des Holzes und der Holzwerkstoffe: Erster Band: Anatomie, Biologie, Chemie, Physik, Elastizität und Festigkeit; Springer: Berlin/Heidelberg, Germany, 1951. [Google Scholar]
  10. Kutnar, A.; Sernek, M.; Kamke, F.A.; Feist, W.C. Characterization and properties of false heartwood in beech trees. Wood Sci. Technol. 2017, 51, 453–467. [Google Scholar] [CrossRef]
  11. Fengel, D.; Wegener, G. Wood: Chemistry, Ultrastructure, Reactions; Walter de Gruyter: Berlin, Germany, 1989; p. 613. [Google Scholar]
  12. Sundqvist, B.; Karlsson, O.; Westremark, U. Determination of formic-acid and acid concentrations formed during hydrothermal treatment of birch wood and its relation to color, strength and hardness. Wood Sci. Technol. 2006, 40, 549–561. [Google Scholar] [CrossRef] [Scilit]
  13. Dzurenda, L. Colouring of Beech Wood during Thermal Treatment using Saturated Water Steams. Acta Fac. Xylologiae Zvolen 2014, 56, 13–22. [Google Scholar]
  14. Klement, I.; Vilkovská, T.; Vilkovský, P.; Uhrín, M. Comparison of Pressure and Atmospheric Steaming Processes and Their Effects on Selected Properties of Beech Wood (Fagus sylvatica L.). Appl. Sci. 2025, 15, 13066. [Google Scholar] [CrossRef] [Scilit]
  15. Hon, N.S.D.; Shiraishi, N. Wood and Cellulosic Chemistry; CRC Press: Boca Raton, FL, USA, 2001; p. 928. ISBN 9780824700249. [Google Scholar]
  16. Geffert, A.; Vybohová, E.; Geffertová, J. Characterization of the changes of colour and some wood components on the surface of steamed beech wood. Acta Fac. Xylologiae Zvolen 2017, 59, 49–57. [Google Scholar] [CrossRef] [Scilit]
  17. Výbohová, E.; Geffertová, J.; Geffert, A. Impact of steaming on the chemical composition of maple wood. BioResources 2018, 13, 5862–5874. [Google Scholar] [CrossRef] [Scilit]
  18. Lichtenegger, H.; Müller, U. Wood and Wood Products: A Guide for Architects and Builders; Springer: Berlin/Heidelberg, Germany, 2010. [Google Scholar]
  19. Tiemann, L.K.; Müller, U.; Schneider, P. The influence of steaming on color change in beech wood. Eur. J. Wood Wood Prod. 2013, 71, 597–603. [Google Scholar] [CrossRef]
  20. Baar, J.; Gryc, V. The analysis of tropical wood discoloration caused by simulated sunlight. Eur. J. Wood Wood Prod. 2011, 70, 263–269. [Google Scholar] [CrossRef] [Scilit]
  21. Gandelová, L.; Horáček, P.; Šlezingerová, J. The Science of Wood; Mendel University of Agriculture and Forestry in Brno: Brno, Czech Republic, 2009; p. 176. [Google Scholar]
  22. Müller, U.; Rätzsch, M.; Schwanninger, M.; Steiner, M.; Zöbl, H. Yellowing and IR-changes of spruce wood as result of UV-irradiation. J. Photochem. Photobiol. B Biol. 2003, 69, 97–105. [Google Scholar] [CrossRef] [Scilit]
  23. Pandey, K.K. Study of the effect of photo-irradiation on the surface chemistry of wood. Polym. Degrad. Stab. 2005, 90, 9–20. [Google Scholar] [CrossRef] [Scilit]
  24. Persze, L.; Tolvaj, L. Photodegradation of wood at elevated temperature: Colour change. J. Photochem. Photobiol. B Biol. 2012, 108, 44–47. [Google Scholar] [CrossRef] [Scilit]
  25. Denes, L.; Lang, E.M. Photodegradation of heat-treated hardwood veneers. J. Photochem. Photobiol. B Biol. 2013, 118, 9–15. [Google Scholar] [CrossRef] [Scilit]
  26. Milić, G.; Todorović, N.; Popadić, R. Influence of steaming on drying quality and colour of beech timber. Glas. Šumarskog Fak. 2015, 83–96. [Google Scholar] [CrossRef] [Scilit]
  27. Kúdela, J.; Kubovský, I. Accelerated-ageing-induced photo-degradation of beech wood surface treated with selected coating materials. Acta Fac. Xylologiae Zvolen 2016, 2, 27–36. [Google Scholar] [CrossRef] [Scilit]
  28. Dzurenda, L. The effect of UV radiation in Xenotest 450 on the colour of steamed beech wood during the process of simulatdageing. Ann. Wars. Univ. Life Sci. For. Wood Technol. 2019, 106, 114–119. [Google Scholar]
  29. Varga, D.; Tolvaj, L.; Molnar, Z.; Pasztory, Z. Leaching efect of water on photodegraded hardwood species monitored by IRspectroscopy. Wood Sci. Technol. 2020, 54, 1407–1421. [Google Scholar] [CrossRef] [Scilit]
  30. Cogulet, A.; Blanchet, P.; Landry, V. Wood degradation under UV irradiation: A lignin characterization. J. Photochem. Photobiol.B Biol. 2016, 158, 184–191. [Google Scholar] [CrossRef] [Scilit] [PubMed]
  31. Zborowska, M.; Stachowiak-Wencek, A.; Waliszewska, B.; Prądzyński, W. Colorimetric and FTIR ATR spectroscopy studies of degradative effects of ultraviolet light on the surface of exotic ipe (Tabebuia sp.) wood. Cellul. Chem. Technol. 2016, 50, 71–76. [Google Scholar]
  32. Teaca, C.-A.; Rosu, D.; Bodirlau, R.; Rosu, L. Structural changes in wood under arteficial UV light irradiation determined by FTIR spectroscopy and color measurement—A brief review. BioResources 2014, 8, 1478–1507. [Google Scholar]
  33. Li, Y.; Liu, M.; Huang, Z.; Zhang, Y.; Wei, P.; Zhu, Z. Fabrication of Tannic Acid–Metal Ion Complex-Dyed Oak Veneer and Elucidation of Its Weathering Resistance Mechanism. Polymers 2024, 16, 575. [Google Scholar]
  34. Zivkovic, V.; Arnold, M.; Radmanovic, K.; Richter, K.; Turkulin, H. Spectral sensitivity in the photodegradation of fir wood (Abies alba Mill.) surfaces: Colour changes in natural weathering. Wood Sci. Technol. 2014, 48, 239–252. [Google Scholar] [CrossRef] [Scilit]
  35. Geffertová, J.; Geffert, A.; Vybohová, E. The effect of UV irradiation on the colour change of the spruce wood. Acta Fac. Xylologiae Zvolen 2018, 60, 41–50. [Google Scholar] [CrossRef] [Scilit]
  36. Chang, T.C.; Chang, H.T.; Chang, S.T. Influences of extractives on the photodegradation of wood. Polym. Degrad. Stab. 2010, 95, 516–521. [Google Scholar] [CrossRef] [Scilit]
  37. Dzurenda, L.; Dudiak, M. Homogenization of the Color of Beech Sapwood and False Heartwood by the Steaming Process. Forests 2024, 15, 1009. [Google Scholar] [CrossRef] [Scilit]
  38. Dzurenda, L. Mode for hot air drying of steamed beech blanks while keeping the colors ac-quired in the steaming process. Acta Fac. Xylologiae Zvolen 2022, 64, 81–88. [Google Scholar] [CrossRef]
  39. ISO/CIE 11664-4:2019; Colorimetry—Part 4: CIE 1976 L*a*b* Colour Space. International Organization for Standardization: Geneva, Switzerland, 2019.
  40. Reinprecht, L. Wood Protection; Technical University in Zvolen: Zvolen, Slovakia, 2008; p. 450. [Google Scholar]
  41. Schaller, C.; Rogez, D. New Approaches in Wood Coating Stabilization. J. Coat. Technol. Res. 2007, 4, 401–409. [Google Scholar] [CrossRef] [Scilit]
  42. Zhang, P.; Wei, Y.; Liu, Y.; Gao, J.; Chen, Y.; Fan, Y. Heat-Induced Discoloration of Chromophore Structures in Eucalyptus Lignin. Materials 2018, 11, 1686. [Google Scholar] [CrossRef] [Scilit] [PubMed]
  43. Judd, D.B. Color in Business, Science and Industry; John Wiley and Sons: New York, NY, USA, 1952. [Google Scholar]
  44. Tolvaj, L.; Mitsui, K. Light-Induced Color Changes of Wood during and after Steaming. J. Wood Sci. 2005, 51, 242–246. [Google Scholar]
  45. Kačík, F.; Jurczyková, T.; Bálintová, M.; Kmeťová, E.; Výbohová, E.; Kačíková, D. Saccharide alterations in spruce wood due to thermal and accelerated aging processes. Polymers 2025, 17, 1265. [Google Scholar] [CrossRef] [Scilit]
  46. Jiang, J.; Peng, Y.; Ran, Y.; Cao, J. Pseudo Lignin Formed from Hygrothermally Treated Holocellulose and Its Effect on Fungal Degradation. Ind. Crops Prod. 2022, 184, 115004. [Google Scholar] [CrossRef] [Scilit]
  47. Kučerová, V.; Výbohová, E. The Changes of Cellulose in Hydrolysis of Willow (Salix alba L.) Wood. Chem. Listy 2014, 108, 1084–1089. [Google Scholar]
  48. Shinde, S.D.; Meng, X.; Kumar, R.; Ragauskas, A.J. Recent Advances in Understanding the Pseudo-Lignin Formation in a Lignocellulosic Biorefinery. Phys. Sci. Rev. 2018, 3, 20170155. [Google Scholar] [CrossRef] [Scilit]
  49. Bonifazi, G.; Calienno, L.; Capobianco, G.; Monaco, A.L.; Pelosi, C.; Picchio, R.; Serranti, S. Modeling color and chemical changes on normal and red heart beech wood by reflectance spectrophotometry, Fourier Transform Infrared spectroscopy and hyperspectral imaging. Polym. Degrad. Stab. 2015, 113, 10–21. [Google Scholar] [CrossRef] [Scilit]
  50. Hofmann, T.; Tolvaj, L.; Visi-Rajczi, E.; Varga, D. Chemical changes of steamed timber during short-term photodegradation monitored by FTIR spectroscopy. Eur. J. Wood Prod. 2022, 80, 841–849. [Google Scholar] [CrossRef] [Scilit]
Polymers 18 00984 g001
Figure 1. Visual comparison of the surface of beech wood with false heartwood in the native state and after steaming (105 °C and 120 °C) before and after UV irradiation in the Q-SUN Xe-3-H test chamber.
Figure 1. Visual comparison of the surface of beech wood with false heartwood in the native state and after steaming (105 °C and 120 °C) before and after UV irradiation in the Q-SUN Xe-3-H test chamber.
Polymers 18 00984 g001
Polymers 18 00984 g002
Figure 2. Kinetics of changes in the lightness coordinate L* of beech sapwood and false heartwood depending on the time of UV exposure.
Figure 2. Kinetics of changes in the lightness coordinate L* of beech sapwood and false heartwood depending on the time of UV exposure.
Polymers 18 00984 g002
Polymers 18 00984 g003
Figure 3. Effect of UV irradiation duration on changes in the chromatic coordinate a* in unsteamed and steamed samples.
Figure 3. Effect of UV irradiation duration on changes in the chromatic coordinate a* in unsteamed and steamed samples.
Polymers 18 00984 g003
Polymers 18 00984 g004
Figure 4. The course of changes in the chromatic coordinate b*, indicating the degree of photochemical yellowing of the sample surface during 360 h of exposure.
Figure 4. The course of changes in the chromatic coordinate b*, indicating the degree of photochemical yellowing of the sample surface during 360 h of exposure.
Polymers 18 00984 g004
Polymers 18 00984 g005
Figure 5. Total differences in color coordinates ΔL*, Δa*, and Δb* after the end of simulated aging for individual beech wood variants.
Figure 5. Total differences in color coordinates ΔL*, Δa*, and Δb* after the end of simulated aging for individual beech wood variants.
Polymers 18 00984 g005
Polymers 18 00984 g006
Figure 6. Influence of UV radiation on the size of the total color difference ΔE* of unsteamed and steamed wood.
Figure 6. Influence of UV radiation on the size of the total color difference ΔE* of unsteamed and steamed wood.
Polymers 18 00984 g006
Polymers 18 00984 g007
Figure 7. ATR-FTIR spectra of unsteamed and steamed sapwood of beech before and after UV irradiation.
Figure 7. ATR-FTIR spectra of unsteamed and steamed sapwood of beech before and after UV irradiation.
Polymers 18 00984 g007
Polymers 18 00984 g008
Figure 8. ATR-FTIR spectra of unsteamed and steamed false heartwood of beech before and after UV irradiation.
Figure 8. ATR-FTIR spectra of unsteamed and steamed false heartwood of beech before and after UV irradiation.
Polymers 18 00984 g008
Table 1. Parameters of pressure steaming for beech wood color unification.
Table 1. Parameters of pressure steaming for beech wood color unification.
Steaming ModesConditions for Steaming Beech Wood
Temperature
[°C]		Pressure
[MPa]		Time
[h]
Mode I1050.12218
Mode II1200.1999
Table 2. Color space CIE L*a*b* coordinate values of unsteamed and steamed beech wood before irradiation.
Table 2. Color space CIE L*a*b* coordinate values of unsteamed and steamed beech wood before irradiation.
Visual Assessment of Wood ColorNumber of MeasurementsColor Coordinates in the Color Space CIE L*a*b*
L*a*b*
Unsteamed sapwoodlight white-gray-yellow color6077.8 ± 1.9 8.5 ± 1.016.3 ± 1.6
Unsteamed false heartwoodpale pink-brown color6066.6 ± 1.711.7 ± 1.118.8 ± 1.4
Steamed mode I_sapwoodred-brown color6069.5 ± 1.213.4 ± 0.819.6 ± 1.0
Steamed mode I_false heartwood6069.2 ± 1.513.1 ± 0.819.4 ± 1.2
Steamed mode II_sapwoodrich brown-red color6051.6 ± 1.213.1 ± 0.918.1 ± 1.0
Steamed mode II_false heartwood6052.0 ± 1.413.2 ± 0.718.2 ± 0.9
Table 3. Relative intensities of absorption bands of carbonyl groups in infrared spectra of unsteamed and steamed beech wood.
Table 3. Relative intensities of absorption bands of carbonyl groups in infrared spectra of unsteamed and steamed beech wood.
H1736/H1370H1650/H1370
Unsteamed_sapwood1.870.94
Unsteamed_sapwood_UV3.821.59
Unsteamed_false heartwood1.801.09
Unsteamed_false heartwood_UV3.821.94
Steamed mode I_sapwood2.080.95
Steamed mode I_sapwood_UV3.741.71
Steamed mode I_false heartwood1.900.86
Steamed mode I_false heartwood_UV4.052.00
Steamed mode II_sapwood1.790.83
Steamed mode II_sapwood_UV4.171.98
Steamed mode II_false heartwood1.880.93
Steamed mode II_false heartwood_UV3.741.99
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Dudiak, M.; Výbohová, E.; Dzurenda, L. Color Stability and Photo-Degradation of Steamed Beech Wood with False Heartwood Under UV Exposure. Polymers 2026, 18, 984. https://doi.org/10.3390/polym18080984

AMA Style

Dudiak M, Výbohová E, Dzurenda L. Color Stability and Photo-Degradation of Steamed Beech Wood with False Heartwood Under UV Exposure. Polymers. 2026; 18(8):984. https://doi.org/10.3390/polym18080984

Chicago/Turabian Style

Dudiak, Michal, Eva Výbohová, and Ladislav Dzurenda. 2026. "Color Stability and Photo-Degradation of Steamed Beech Wood with False Heartwood Under UV Exposure" Polymers 18, no. 8: 984. https://doi.org/10.3390/polym18080984

APA Style

Dudiak, M., Výbohová, E., & Dzurenda, L. (2026). Color Stability and Photo-Degradation of Steamed Beech Wood with False Heartwood Under UV Exposure. Polymers, 18(8), 984. https://doi.org/10.3390/polym18080984

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop