Next Article in Journal
High-Content Lithium Aluminum Titanium Phosphate-Based Composite Solid Electrolyte with Poly(ionic liquid) Binder
Next Article in Special Issue
Properties of 3D-Printed Polymer Fiber-Reinforced Mortars: A Review
Previous Article in Journal
Improved Wood-Bond Strengths Using Soy and Canola Flours with pMDI and PAE
Previous Article in Special Issue
The Micro–Macro Interlaminar Properties of Continuous Carbon Fiber-Reinforced Polyphenylene Sulfide Laminates Made by Thermocompression to Simulate the Consolidation Process in FDM
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 14
Issue 7
10.3390/polym14071273
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Communication

Industrial Implementation of Aluminum Trihydrate-Fiber Composition for Fire Resistance and Mechanical Properties in Glass-Fiber-Reinforced Polymer Roofs

by
Mohammad Zainudin
1,
Kuncoro Diharjo
1,*,
Mujtahid Kaavessina
2,
Djoko Setyanto
3 and
Ubaidillah Ubaidillah
1
1
Mechanical Engineering Department, Engineering Faculty, Universitas Sebelas Maret, Surakarta 57126, Indonesia
2
Chemical Engineering Department, Engineering Faculty, Universitas Sebelas Maret, Surakarta 57126, Indonesia
3
Mechanical Engineering Department, Atma Jaya Catholic University of Indonesia, Jakarta 12930, Indonesia
*
Author to whom correspondence should be addressed.
Polymers 2022, 14(7), 1273; https://doi.org/10.3390/polym14071273
Submission received: 7 February 2022 / Revised: 8 March 2022 / Accepted: 14 March 2022 / Published: 22 March 2022
(This article belongs to the Special Issue Fibre-Reinforced Polymer Composite)
Browse Figures
Versions Notes

Abstract

:
It is difficult to obtain suitable fire resistance and mechanical properties for glass-fiber-reinforced polymer (GFRP) roof material in industrial applications. Although some efforts to improve the fire resistance properties of GFRP have been carried out, in practice this sometimes degrades the mechanical properties. Therefore, the base materials, such as filler and reinforcing fiber, must be appropriately combined to simultaneously improve both fire resistance and mechanical properties. The present study examines improvements in GFRP roof material by investigating the effect of aluminium trihydrate (ATH) as a filler and the combination of a chopped strand mat (CSM) with woven roving (WR) and stitched mat (STM) fibers as the reinforcement in a composite GFRP roof structure. The roof samples were prepared following industrial machine standards using the specified materials. The mechanical properties of GFRP were evaluated using tensile, flexural and impact tests, following ASTM D638, ASTM D790 and ASTM D256 standards, respectively. The fire properties were examined through fire tests following the ASTM D635 standard. The results show that the GFRP roof composed of CSM/WR fibers had a 40% higher tensile strength (103.5 MPa) compared with the GFRP roof without CSM fibers (73.8 MPa). The flexural strength of the GFRP roof with CSM/WR fibers was also 57% higher than the roof without fibers, with a ratio of 315.61 MPa to 201 MPa. With the use of CSM/WR fibers, the fire resistance also increased by 23%, resulting in a ratio of 4.31 mm/min to 5.32 mm/min. These results demonstrate that the combination of CSM/WR fibers as a reinforcement would be an excellent option for producing an improved GFRP roof with better industrial properties, especially when producing improved GFRP roofs using a continuous lamination machine.

1. Introduction

Glass-fiber-reinforced polymer (GFRP) consists of high-strength fibers within a polymer resin, namely, unsaturated polyester resins (UP resins). Compared with pure UP resins, the utilization of glass fiber is typically preferred to enhance the strength, stiffness, corrosion resistance, fatigue resistance, or strength-to-weight ratio of the polymer. In industry, GFRP is generally utilized in airplanes, electronic components, automotive applications, railways, and sporting goods. The widespread use of GFRP composites results from the ease with which their mechanical properties can be modified as desired. However, due to the effects of tropical climatic variables (ultraviolet, humidity, temperature fluctuations, rain, etc.), the mechanical properties of GFRP are prone to deterioration over time [1,2]. Additionally, GFRP composites tend to have a combustible matrix because unsaturated polyester resins are polymers with chains containing considerable amounts of carbon and hydrogen [3]. This problem is often solved by adding fillers into the matrix to increase the polymer fire resistance, some of which include aluminium trihydrate (ATH), boric acid (AB), and sodium silicate (Na2SiO3).
Several previous studies have revealed the effect of fire retardants on GFRP composites, both on their mechanical and physical properties [4,5,6,7,8,9]. The type of fire retardant used, as well as its load, significantly affects the mechanical properties. In general, adding a fire retardant reduces mechanical properties [4]. The addition of ATH to GFRP as a filler has been observed to weaken tensile strength, which decreases due to poorer bonding between the filler powder, matrix, and the glass fiber used [5,6,7]. It is also argued that the addition of ATH is not recommended for applications that require heavy loading due to the associated decrease in mechanical properties. In contrast, F. Perez-Salinas et al. [8] revealed that the addition of 9% ATH does not significantly impact the tensile strength and modulus of elasticity of the composites compared with the addition of magnesium hydroxide. However, the addition of ATH filler can enhance fire resistance by decreasing the burning rate [9].
Moreover, various fire-retardant fillers, such as ATH, DeBDE, Sb2O3, and TCP, have been tested to produce compounds with the desired properties. ATH has been demonstrated to particularly improve mechanical properties; however, even loading up to 60% does not confer any fire-retardant properties [10]. Additionally, Kaleg et al. [11] found that aluminium trihydrate (Al(OH)3) filler was able to increase the initial temperature of the decomposition of UP resin, thereby reducing the burning rate of GFRP composites.
Other studies have revealed that reinforcing fibers might affect the properties of GFRP composites [12,13,14,15]. The addition of reinforcing materials such as glass or carbon fiber can increase the strength and modulus of rPP/clay composite, thereby making possible its application as a structural component in vehicle bodies [16]. Abburi Lakshman Kumar et al. [17] observed that the direction of fiber reinforcement impacted the mechanical properties and machinability of GFRP composites. A fiber direction of ±45 exhibited improved tensile and flexural strength compared with a 0/90 combination. Bushra Rashid et al. [18] reported that the mechanical properties of the composites improved as the number of layers of glass fiber increased. Composites with Woven/UP resin showed better effect strength, whereas CSM/UP resin composites showed preferable flexural strength over Woven/UP resin. Notwithstanding, the mixture composite Woven/CSM/UP resin had by far the best mechanical properties [17,18].
Given the benefits, the need for industrially manufactured GFRP composite roofing with improved mechanical properties and fire resistance is significantly growing among users. Therefore, the creation of GFRP composite roofs with improved properties has become necessary. Recent developments in GFRP composite roofing with CSM fiber reinforcement have included adding sand material to the matrix to increase fire resistance [19,20,21]. However, these products are still only made on a laboratory scale using hand lay-ups, rather than a roof-making machine due to the constraints when setting process parameters in the machine. This is a shortcoming because the market demand for GFRP composite roofing has increased.
On the other hand, no composite roofs have been manufactured that use fire-retardant ATH as a filler and reinforcing fiber from a combination of CSM, Woven, or even Stitchmat (STM) fibers. One example of GFRP composite roofs currently available is that produced by PT Intec Persada, Indonesia [22]. This GFRP roof is made of a composite of UP resin matrix and 30% ATH filler, reinforced with CSM E-glass fiber. Based on the specifications, the roof has a tensile strength of 73.8 MPa, a flexural strength of 201 MPa, a burning rate of 5 mm/min, and its properties could be still further improved [23]. Therefore, this study investigates the use of ATH as a filler with a combination layer configuration of E-glass fibers such as CSM, WR, and STM with the aim of developing a GRFP composite roof with better fire resistance and mechanical properties than those currently available on the market.

2. Materials and Methods

This study addresses the need to improve the performance of GRFP composite roofs made at a composite roofing factory at PT. Intec Persada, Tangerang, Indonesia [22]. The matrix was composed of unsaturated polyester resin (UP resin) and aluminium trihydrate (ATH) (orthophthalic UP resin, PT. Justus Kimiaraya, Jakarta, Indonesia, YUKALAC®, LP1QEX, Lot #: A1400613 AG). Up to 1% of the methyl ethyl ketone peroxide (MEKP) of the total resin volume was used to initiate the matrix hardening process. In addition, ATH delivered by PT. Kawaguchi Kimia Indonesia under the code BW153 was used as a fire-retardant filler. All the materials were used directly without any treatment.
The reinforcing fiber used was an E-glass CSM of Jushi, Tongxiang, China with a density of 450 g/m2 (CSM 450) and 300 g/m2 (CSM 300), E-glass WR with a density of 200 g/m2 (WR 200), and an E-glass stitch mat with a density of 450 g/m2 (STM 450).
Two- or three-ply composite plates were fabricated by employing a hand lay-up method. E-glass fibers within CSM 300, CSM 450, WR 200, and STM 450 were impregnated with the matrix. MEKP was used as a catalyst, which was first added to the resins to start the polymerization process. A gel coat was applied as a decorative and protective surface on the outside layer. The layer configurations of the three samples are tabulated in Table 1.
The amount of ATH used in Sample 1 was 30% and increased to 45% for Samples 2 and 3. Each sheet was designed with a thickness of up to 1.5 mm. Then, to match the actual roof, each composite sheet was molded by pressing between molds in the form of a roof sheet. Then, a curing process at room temperature was performed, as shown in Figure 1a,b.
Figure 2 shows a schematic of the continuous lamination process [24]. Two sheets of plastic film were used to wrap the composite layer. The reinforcing fiber used was CSM, roving, or STM. The reinforcing fiber with resin mixed with the initiator was synthesized in bulk. Curing was carried out at a temperature of 50–140 °C in an oven at a 60–120 kg/h production rate. UP resin liquid mixed with the initiator was dropped on the bottom plastic film; then, chopped strand mat or pieces of roving were placed on top. Wet-out rolls removed air bubbles. Next, the plastic film was coated on the top side. Finally, the entire layer was pulled into the oven by the pulling system and heated with a specified temperature distribution: experience has shown that good lamination results are obtained at a resin gel temperature of 80–90 °C and a peak exothermic temperature of 150–165 °C. The flat or corrugated sheets produced in the oven were cured into solids and then cut to the desired length.
Our GFRP composite roof had two UV protection layers: an anti-UV film layer and an anti-UV gel-coat layer. Double-layer protection as shown in Figure 3 maintains the quality of the composite roof, making it more durable against weather, UV rays, and humidity.
The flexural properties of the GFRP roof were ascertained from the three-point bending test following the ASTM D790 standard. The test samples were obtained by cutting from the flat section of the sheets for each type of GFRP composite. There were seven samples of each composite being tested with the thickness of each sample measured to be 50.8 mm long by 12.7 mm wide using a UTM JTM-UTS510 series testing machine at room temperature with a test speed of 1.4 mm/min. The tests for tensile properties were performed on each sample according to ASTM D638. The tensile test was conducted on five samples of each composite tested, and the dimensions of each test specimen were 115 mm long, 25 mm gauge length and 6 mm width as required by ASTM D638 Type IV. The tensile test was conducted using a UTM Shimadzu Type AG-250kN Plus with a test speed of 2 mm/min. An Izod type impact test was performed according to ASTM D256. There were five test pieces of each sample with the dimensions 63.5 × 12.7 × 3.2 mm. The test was performed using a standard-sized cantilever beam clamped vertically into the tester stop with a 2 mm V-notch at a 45-degree angle just above the clamp. Based on the test configuration shown in Figure 4, the impact energy was calculated by the formula E = W.R (cos α − cos β) in Joule.
The rate of burning was in reference to the ASTM D635 standard as illustrated in Figure 5, the fireside propagation on flammable materials in a horizontal position was assessed on five test pieces of each sample. SEM observations were employed to determine the morphology of the specimen fracture surface, especially on the bond between the filler and the matrix. An SEM observation using a ZEISS EVO 10 apparatus at 15 kV also aimed to examine the filler dispersion of the matrix. We observed the likelihood of filler agglomeration within the matrix. The thermogravimetric analysis (TGA) test was conducted to measure the change in mass (decrease or increase in mass) and the rate of change of mass as a function of temperature. The TGA test was conducted by measuring the mass of the sample in a pan using a precision balance placed in the furnace. In measuring the mass degradation of polymer composite specimens, the test environment used controlled atmospheric air. The heating rate parameter was set at 10 °C/min and the test temperature range was from room temperature to 600 °C. Finally, a differential scanning calorimetry (DSC) test was also carried out which was used to determine the endothermic and exothermic reactions of the specimen.

3. Result and Discussion

Table 2 exhibits the test result of all samples in this research. The bar graph in Figure 6 shows that the GFRP composite roof of Sample 3 had a higher tensile strength than Samples 2 or 1. The tensile strength of the composite roof of Sample 3 reached 103.5 Mpa, which was higher than the tensile strength of Sample 2 (75.7 Mpa) and Sample 1 (73.8 Mpa). This indicates that the glass fiber inserted into the matrix as reinforcement increased the tensile strength. Glass fibers are typically used to improve strength, stiffness, and fatigue resistance, or enhance the strength-to-weight ratio over pure UP resin [11,21]. As illustrated in the data above, the tensile strength was not subject to the type of composite matrix reinforcement—CSM, STM, or WR—but was strongly influenced by the composite density. A similar situation was reported in previous studies, showing that the number of reinforcing fiber layers does affect the mechanical strength properties of GFRP composites [17,18,21]. In this study, Sample 3 had a greater density than Samples 1 and 2.
Figure 7 shows that the flexural strength of the GFRP material for Sample 3 was almost identical to that of Sample 2. However, it was higher than Sample 1. The flexural strength of Sample 3 reached 315.61 Mpa, which was not substantially different from that of the GFRP in Sample 2 (302.39 Mpa); however, the flexural strength of Sample 3 was higher than that of Sample 1 (201 Mpa). Therefore, it can be deduced that different layer combinations (CSM/STM or CSM/WR) can provide space for movement, leading to a higher flexural strength vis à vis the strength of the same layer combination (CSM/CSM) in Samples 2 and 3.
Impact testing was carried out to determine how much energy was absorbed by the GFRP composite roof before fracture. As shown in Figure 8, the GFRP composite roof of Sample 3 had increased impact strength compared with Sample 2 and Sample 1, exhibiting a ratio of 92,598:92,629.5:92,700 J/m2.
A burn test was conducted to determine the burning rate of the samples. In this test, all composites were tested following the ASTM D635 standard and included in the HB class (horizontal burning), where the burn rate was still below 75 mm/min. It was discovered that the linear burn rate of the GFRP composite roof in Sample 1 reached 5.32 mm/min, whereas Samples 2 and 3 had linear burn rates of 4.63 mm/min and 4.31 mm/min, respectively, as shown in Figure 9. The findings demonstrate that the layer type (CSM, WR, or STM) does not substantially affect the burning rate, although altering the layer density does increase fire resistance.
Composites with STM fibers can improve the mechanical performance by up to 20% compared with CSM fiber types. The reasons are that STM fibers are parallel non-crimp fibers that can withstand strain immediately after loading, and their higher density can be incorporated into laminates compared with CSM. The fibers behave more as a unidirectional layer [25]. It can be argued that the more significant the volume fraction of the reinforcing fiber, the higher the strength and stiffness values of the resulting composite [26]. In the current experiment, the density of the sample with WR reinforcement was greater than that of CSM or STM reinforcement, which is consistent with the rule of mixture. However, there is a maximum volume fraction for the reinforcing fiber, which is determined by the length and orientation of the selected reinforcing fiber [26].
The decrease in the combustion rate of Sample 1 was caused by heat absorption. The thermal energy was reduced in the composite due to the presence of H2O. In other words, a reduction in thermal energy causes the burning rate of the composite to decrease [27]. Umberto Berardi et al. [28] reported that as the mass of ATH is increased, the mass-loss rate per unit area (MLRPUA) diminishes, and the burn rate decreases. Adding aluminium hydroxide as a fire retardant will decrease the burn rate. It breaks down at around 180 °C (356 °F) due to exposure to too much heat and releases water vapor.
The additional density resulting from the reinforcement material can increase fire resistance even at a minimal composition [29]. Additionally, the use of glass fiber in the phenolic matrix could result in high tensile strength and good fire resistance, as per the UL94 standard [30]. Here, the dehydration of ATH and cleavage of the ester bond result in the first significant mass loss, forming volatile products such as H2O, dicyclopentadiene, benzaldehyde, and dimethyl phthalate [31].
Adding ATH to UP resin composites increases both the limiting oxygen index (LOI) and ATH load, improving fire resistance [32]. Increased fire resistance indicates that ATH may prolong the time to ignition (TTI) and reduce the heat release rate (HRR) [33]. The particle size of ATH affects the fire resistance of the UP resin; thus, equal mass ratios of submicron fillers and nanofillers provide the most straightforward fire resistance [34]. High ATH loads also result in an increase in the modulus of elasticity and a decrease in fracture elongation, increasing the stiffness and brittleness of the composite. The modulus of elasticity of the UP resin’s 40% ATH load is 2.41 Gpa, 29.57% higher than the modulus of elasticity of the pure UP resin [35]. Increasing the ATH load of a GFRP composite tends to reduce the bending strength. The addition of ATH particles to GFRP composites can result in the non-uniform distribution of ATH particles and increased strain concentration in the fracture process [27]. Therefore, the addition of ATH may reduce the strength and make the GFRP more brittle.
The SEM image in Figure 10a shows the arrangement of the stitched mat fibers in the cross-sectional direction, where the fiber-like portion of the seam reinforces the woven fibers that form it. A stitched mat reinforcing fiber structure has more fibers than woven or CSM reinforcement. The stitched mat fibers have a coiled fiber in a seam, allowing for better bonding between the fibers than CSM. In addition, the higher density of WR reinforcing fibers compared with reinforcements with STM or CSM fibers indicates more mechanical strength, which is also consistent with the mixture principle [26].
This study shows that the increase in ATH content in GFRP composites up to 45% tends to form agglomerations. As shown in Figure 10b, agglomeration produces an inhomogeneous distribution of particles, weakening the interaction between the filler and the matrix [36]. In addition, ATH agglomeration triggers stress concentration in the area around the particles, resulting in decreases in the mechanical properties of the composite [24]. In summary, ATH is a rigid particle that is difficult to deform; therefore, an increase in ATH content in the UP resin can cause an increase in the modulus of elasticity of the composite.
The ATH content in UP resin showed a decrease in mass degradation due to the release of moisture. The tested specimens exhibited a loss of moisture up to a temperature of 250 °C [37,38]. As shown in the TGA curve in Figure 11, at a temperature of 250 °C, Sample 1 showed a mass degradation of 3.7%, whereas Sample 2 and Sample 3 exhibited 2.9% and 2.15%, respectively. These figures indicate that Sample 1 experienced the highest decomposition when the moisture release process occurred. This is consistent with the SEM images which show that ATH particles tend to form agglomerations in the UP resin. The decomposition temperature at 50% mass degradation of Sample 1 was 380 °C. Meanwhile, the decomposition temperature at 50% mass degradation of Sample 2 and Sample 3 increased by 100 °C and 144 °C, respectively, compared with Sample 1. The decomposition of UP resin in each sample occurred at a temperature of 280 °C to 400 °C. At temperatures above 400 °C, the graph in Figure 11 shows a relatively flat line. This indicates that decomposition did not continue even though the specimen temperatures increased. The final residue of these samples contained alumina which has a melting temperature of 2054 °C, much higher than the melting temperature of UP resin [32,33].
From the TGA test results curve in Figure 11, it can be seen that in Sample 1 there was a mass reduction of about 0.05% at a temperature of 130 °C, whereas about 0.3% and 1% mass reductions occurred in Samples 2 and 3, respectively. This mass reduction occurred due to evaporation of moisture and other materials on the surface of the composite [39]. At temperatures above 280 °C, a very significant mass reduction began to occur up to a temperature of 400 °C. The gradual decrease in mass above 400 °C could be due to the slow oxidation of stable carbon produced during decomposition [39].
As shown in the DSC test result curve in Figure 12, in Sample 1, from the beginning of the test, the curve showed a slow endothermic reaction which is indicated by a near horizontal sloping curve. At temperatures less than 200 °C, the absorbed heat resulted in moisture evaporation and volatilization due to the initial decomposition process [39]. The curve began to rise at 280 °C and an exothermic peak occurs at 400 °C, due to the thermal oxidation of the volatiles with oxygen which generates heat (exothermic). The occurrence of these peaks was due to the large energy required during thermal decomposition to break the crosslinks of polystyrene, which was then followed by evaporation of polystyrene and volatiles [33]. The temperature continued to increase so that endothermic peaks appeared at 370 °C and 380 °C (close to 400 °C). This solid phase oxidation came from the slow oxidation of stable carbon produced during decomposition [40].
In Sample 2 and Sample 3, before the temperature of 300 °C, an endothermic peak was seen at 280 °C. This endothermic reaction describes the start of the thermal decomposition of the composite which produces volatiles. As these volatiles break down into smaller fractions they oxidize more readily [41]. The exothermic peak appears at 400 °C. This exothermic reaction describes the thermal oxidation of volatiles with oxygen which produces heat. ATH filler will prevent the oxidation that occurs following the endothermic reaction during filler decomposition. Filler decomposition produced water vapor which played a role in reducing the combustion rate. The water vapor escapes the fire and dissolves the concentration of combustible gases from the polymer matrix. This process limits oxygen access on the composite surface [37]. As the ATH filler began to decompose at 200 ºC, the endothermic reaction of ATH and water vapor during decomposition absorbed the heat of combustion and dissolved combustible gases. In addition, ceramic alumina (Al2O3), which functions as an insulating layer against heat, will be formed [42]. The exothermic peak that occurred in the three samples with the filler was around 400 °C, which means it was in the main decomposition area, where the greatest mass degradation occurred in the TGA test. This illustrated the severance of the polystyrene crosslink, which was then followed by the evaporation of the polystyrene and volatiles [33].

4. Conclusions

The GFRP composite roof using the combination of CSM/WR fibers had a 40% higher tensile strength than the GFRP roof with CSM/CSM fibers as reinforcement, with a respective ratio of 103.5:73.8 MPa. The flexural strength of the former was 57% higher than that of the latter. Furthermore, for the three types of the GFRP roofs investigated there was little difference in the impact strengths, which were 92,700 J/m2, 92,629 J/m2, and 92,598 J/m2 for Samples 1, 2, and 3, respectively. The fire resistance, as estimated by the linear burn rate of the investigated GFRP roofs, differed by 23% between the roof with the combination of CSM/WR fibers and that with CSM/CSM fibers as reinforcement, which corresponds to a ratio of 4.31:5.32 mm/min. This investigation offers promising applications in producing new, improved GFRP roofs with better mechanical characteristics and fire resistance properties. Combining CSM/WR fibers as reinforcement is recommended to produce new and improved GFRP roofs using a continuous lamination machine.

Author Contributions

Conceptualization, K.D. and M.K.; methodology, M.Z.; formal analysis, M.Z., D.S. and M.K.; investigation, M.Z.; resources, K.D. and U.U.; data curation, K.D. and U.U.; writing—original draft preparation, M.Z.; writing—review and editing, M.Z. and U.U.; visualization, M.Z.; supervision, K.D., M.K. and U.U. All authors have read and agreed to the published version of the manuscript.

Funding

This research and APC were funded by Universitas Sebelas Maret under PNBP funding 2022 (Hibah Unggulan Terapan).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

Special thanks to Alex Hendro, President Director of PT Intec Persada, Indonesia, for allowing and facilitating the first author to use the company’s facilities to conduct the research. This research was funded by Universitas Sebelas Maret.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Mousay, M.; Chai, Y.Y.; Doh, S.I.; Lim, K.S. Degradation of Glass Fiber Reinforced Polymer (GFRP) Material Exposed to Tropical Atmospheric Condition, Key Engineering Materials; Trans Tech Publications Ltd.: Bäch, Switzerland, 2021; Volume 879, pp. 265–274. [Google Scholar] [CrossRef]
  2. Zainudin, M.; Diharjo, K.; Kaavessina, M.; Setyanto, D. The properties degradation of exposed GFRP roof. AIP Conf. Proc. 2018, 1931, 030063. [Google Scholar] [CrossRef] [Green Version]
  3. Kandola, B.K.; Ebdon, J.R. Flammability and Thermal Stability of Unsaturated Polyester Resin-Based Blends and Composites. In Unsaturated Polyester Resins; Elsevier Inc.: Amsterdam, The Netherlands, 2019; pp. 435–469. [Google Scholar]
  4. Ramadan, N.; Taha, M.; La Rosa, A.D.; Elsabbagh, A. Towards Selection Charts for Epoxy Resin, Unsaturated Polyester Resin and Their Fiber-Fabric Composites with Flame Retardants. Materials 2021, 14, 1181. [Google Scholar] [CrossRef]
  5. Deswan; Setyanto, D. ATH AS a filler of vinylester RESIN. Int. J. Mech. Prod. Eng. Res. Dev. 2020, 10, 2953–2964. [Google Scholar]
  6. Ming, G.; Hao, W.; Yanxia, W.; Tengfei, S.; Weihong, W. Flame retardancy and mechanical properties of a novel intumescent flame-retardant unsaturated polyester. J. Vinyl Addit. Technol. 2014, 22, 350–355. [Google Scholar]
  7. Youchuan, W.; Zhang, L.; Yunyun, Y.; Xufu, C. The investigation of flammability, thermal stability, heat resistance and mechanical properties of unsaturated polyester resin using AlPi as fire retardant. J. Therm. Anal. Calorim. 2015, 122, 1331–1339. [Google Scholar] [CrossRef]
  8. Pérez-Salinas, C.F.; Castro, C.B.; Valencia, E.R.; Freire, O.F. Influence of Fire Retardants on the Mechanical Properties of Glass Fiber Reinforced Compounds in Polymeric Matrix Epoxy and Polyester. IOP Conf. Ser. Mater. Sci. Eng. 2019, 628, 12001. [Google Scholar] [CrossRef]
  9. Yunshu, Z.; Yuan, Y.; Qingwu, Z. Effects of Dimethyl Methylphosphonate, Aluminum Hydroxide and Ammonium Polyphosphate on the Fire resistance and Thermal Properties of Unsaturated Polyester Resin. IOP Conf. Ser. Mater. Sci. Eng. 2018, 394, 22029. [Google Scholar] [CrossRef]
  10. Daulath, B.R.; Vasanthakumari, R. Optimization Studies in Fire retardant Fiber Reinforced Plastic Composites for Roofing Applications. Int. J. Chem. Res. 2012, 2, 26–33. [Google Scholar]
  11. Kaleg, S. Pengaruh Fire Retardant Aluminum Tri-Hydroxide Dan Filler Montmorillonite Terhadap Ketahanan Bakar Dan Kekuatan Flexural Komposit Unsaturated Polyester Resin–Serat Gelas. Master’s Thesis, Universitas Sebelas Maret, Surakarta, Indonesia, 2018. [Google Scholar]
  12. Xiangxiu, C.; Li, Y.; Zhiyong, Z.; Hong, W.; Guozheng, L.; Aijuan, G. New glass fiber/bismaleimide composites with significantly improved fire resistance, higher mechanical strength and lower dielectric loss. Compos. Part B Eng. 2015, 71, 96–102. [Google Scholar]
  13. Brown, J.R.; Mathys, Z. Reinforcement and matrix effects on the combustion properties of glass reinforced polymer composites. Compos. Part A Appl. Sci. Manuf. 1997, 28, 675–681. [Google Scholar] [CrossRef]
  14. Kandola, B.; Krishnan, L.; Ebdon, J. Blends of unsaturated polyester and phenolic resins for application as fire-resistant matrices in fiber-reinforced composites: Effects of added fire retardants. Polym. Degrad. Stab. 2014, 106, 129–137. [Google Scholar] [CrossRef]
  15. Scudamore, M.J. Fire Performance Studies on Glass-reinforced Plastic Laminates. Fire Mater. 1994, 18, 313–325. [Google Scholar] [CrossRef]
  16. Diharjo, K.; Suharty, N.S.; Nusantara, A.E.B.; Afandi, R. The Effect of Sokka Clay on the Tensile and Burning Properties of rPP/Clay Composite. Adv. Mater. Res. 2015, 1123, 338–342. [Google Scholar] [CrossRef]
  17. Bushra, R.; Amal, S.; Muameer, E.; Aymen, R.M. Mechanical properties of hybrid woven roving and chopped strand mat glass fabric reinforced polyester composites Mater. Res. Express 2019, 6, 105208. [Google Scholar] [CrossRef]
  18. Abburi, L.K.; Prakash, M. The effect of fiber orientation on mechanical properties and machinability of GFRP composites by end milling using cutting force analysis. Polym. Polym. Compos. 2021, 29, S178–S187. [Google Scholar] [CrossRef]
  19. Shin, Y.B. Manufacturing Method for Glass Fiber Reinforced Plastic and Glass Fiber Reinforced Plastic Using the Same and Building Panel Thereof. Patent KR102181541 (B1), 23 November 2020. [Google Scholar]
  20. Shin, Y.B. Manufacturing Method for Glass Fiber Reinforced Plastic and Glass Fiber Reinforced Plastic Using the Same and Building Panel and Manufacturing Method Thereof. Patent KR102152089 (B1), 7 September 2020. [Google Scholar]
  21. Mariatti, M.; Chum, P.K. Effect of Laminate Configuration on the Properties of Glass Fiber-reinforced Plastics (GFRPs) Mixed Composites. J. Reinf. Plast. Compos. 2005, 24, 1713–1721. [Google Scholar] [CrossRef]
  22. Available online: https://intecpersada.com/fibrealum/(accessed on 10 February 2021).
  23. Setyanto, D.; Jamasri; Suhendro, B.; Tontowi, A.E. Alumina as a Filler in UPR Matrix for FRP Composite Roofing Sheets. Int. J. Mater. Sci. 2012, 7, 191–202. [Google Scholar]
  24. Debnath, S.; Ranade, R.; Wunder, S.L.; McCoo, J. Interface effects on mechanical properties of particle reinforced composites. Dent. Mater. 2004, 20, 677–686. [Google Scholar] [CrossRef]
  25. GURIT. Guide to Composites. Available online: www.gurit.com (accessed on 10 February 2021).
  26. Gibson, R.F. Principles of Composite Material Mechanics; Mc Graw Hill, Inc.: New York, NY, USA, 1994. [Google Scholar]
  27. Sonnier, R.; Otazaghine, B.; Viretto, A.; Apolinario, G.; Ienny, P. Improving the fire resistance of flax fabrics by radiation grafting of phosphorus compounds. Eur. Polym. J. 2015, 68, 313–325. [Google Scholar] [CrossRef]
  28. Umberto, B.; Nicholas, D. Thermal and Fire Characteristics of FRP Composites for Architectural Applications. Polymers 2015, 7, 2276–2289. [Google Scholar] [CrossRef] [Green Version]
  29. Dong, Q.; Gao, C.; Ding, Y.; Wang, F.; Wen, B.; Zhang, S.; Wang, T.; Yang, M. A polycarbonate/magnesium oxide nanocomposite with high fire resistance. J. Appl. Polym. Sci. 2012, 123, 1085–1093. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  30. Diharjo, K.; Sutrisno; Triyono; Afandi, R.; Himawanto, D.A. Enhancing of fire resistance on CFRP using Sokka-clay particle for lightweight car body panel. In Proceedings of the 2014 International Conference on Electrical Engineering and Computer Science ICEECS, Denpasar, Indonesia, 24–25 November 2014; pp. 188–192. [Google Scholar]
  31. Tingting, Q.; Fanliang, G.; Changhai, L.; Shouxiang, L. Study of the thermal degradation of flame-retardant polyester GFRP using TGA and TG-FTIR-GC/MS. J. Therm. Anal. Calorim. 2021, 1–18. [Google Scholar] [CrossRef]
  32. Maheshwari, N.; Thakur, S.; Neogi, P.; Neogi, S. UV resistance and fire retardant property enhancement of unsaturated polyester composite. Polym. Bull. 2015, 72, 1433–1447. [Google Scholar] [CrossRef]
  33. Hapuarachchi, T.D.; Peijs, T. Aluminium trihydrate in combination with ammonium polyphosphate as fire retardants for unsaturated. Express Polym. Lett. 2009, 3, 743–751. [Google Scholar] [CrossRef]
  34. Tibiletti, L. Thermal degradation and fire behaviour of unsaturated polyesters filled with metallic oxides. Polym. Degrad. Stab. 2011, 96, 67–75. [Google Scholar] [CrossRef]
  35. Zhao, Q.; Jia, Z.; Li, X.; Ye, Z. Effect of Al(OH)3 Particle Fraction on Mechanical Properties of Particle-Reinforced Composites Using Unsaturated Polyester as Matrix. Fail. Anal. Preven. 2010, 10, 515–519. [Google Scholar] [CrossRef]
  36. Baskaran, R.; Sarojadevi, M.; Vijayakusumar, C.T. Unsaturated polyester nanocomposite filled with nanoalumina. Springer J. Mater. Sci. 2011, 446, 4864–4871. [Google Scholar]
  37. Mouritz, A.P.; Gibson, A.G. Fire Properties of Polymer Composite, Materials; Springer: Berlin/Heidelberg, Germany, 2006. [Google Scholar]
  38. Widmann, G. Interpreting TGA Curves. UserCom 2001, 1, 1–20. [Google Scholar]
  39. Salasinska, K.; Celi, M.; Barczewski, M.; Leszczy, M.K.; Borucka, M.; Kozikowski, P. Fire behavior of flame retarded unsaturated polyester resin with high nitrogen content additives. Polym. Test. 2020, 84, 106379. [Google Scholar] [CrossRef]
  40. Halim, Z.A.B.; Yajid, M.A.M.; Nurhadi, F.A.; Ahmad, N.; Hamdan, H. Effect of silica aerogel—Aluminium trihydroxide hybrid filler on the physio-mechanical and thermal decomposition behaviour of unsaturated polyester resin composite. Polym. Degrad. Stab. 2020, 182, 109377. [Google Scholar] [CrossRef]
  41. Pawelec, W. New Families of Highly Efficient, Halogen-Free Flame Retardants for Polypropylene (PP). Ph.D. Thesis, Laboratory of Polymer Technology Center of Excellence for Functional Materials Department of Chemical Engineering Åbo Akademi University, Turku, Finland, 2014. [Google Scholar]
  42. Zhang, Z.; Han, Y.; Li, T.; Wang, T.; Gao, T.; Liang, Q.; Chen, L. Polyaniline/montmorillonite nanocomposites as an effective flame retardant and smoke suppressant for polystyrene. Synth. Metals 2016, 221, 28–38. [Google Scholar] [CrossRef]
Polymers 14 01273 g001 550
Figure 1. (a,b) Layering and molding of a GFRP composite roof.
Figure 1. (a,b) Layering and molding of a GFRP composite roof.
Polymers 14 01273 g001
Polymers 14 01273 g002 550
Figure 2. A schematic of continues laminating process.
Figure 2. A schematic of continues laminating process.
Polymers 14 01273 g002
Polymers 14 01273 g003 550
Figure 3. The layer structure of the GRFP roof.
Figure 3. The layer structure of the GRFP roof.
Polymers 14 01273 g003
Polymers 14 01273 g004 550
Figure 4. Izod type Impact test according to ASTM D256.
Figure 4. Izod type Impact test according to ASTM D256.
Polymers 14 01273 g004
Polymers 14 01273 g005 550
Figure 5. Burn test equipment according to ASTM D635.
Figure 5. Burn test equipment according to ASTM D635.
Polymers 14 01273 g005
Polymers 14 01273 g006 550
Figure 6. Tensile strength of GFRP composite roofs.
Figure 6. Tensile strength of GFRP composite roofs.
Polymers 14 01273 g006
Polymers 14 01273 g007 550
Figure 7. Flexural strength of GFRP composite roofs.
Figure 7. Flexural strength of GFRP composite roofs.
Polymers 14 01273 g007
Polymers 14 01273 g008 550
Figure 8. Impact strength of GFRP composite roofs.
Figure 8. Impact strength of GFRP composite roofs.
Polymers 14 01273 g008
Polymers 14 01273 g009 550
Figure 9. Linear burning rate of GFRP composite roofs.
Figure 9. Linear burning rate of GFRP composite roofs.
Polymers 14 01273 g009
Polymers 14 01273 g010 550
Figure 10. Micrograph result: (a) SEM of ATH distribution in UP resin; (b) SEM of stitch mat GFRP composite roof fracture.
Figure 10. Micrograph result: (a) SEM of ATH distribution in UP resin; (b) SEM of stitch mat GFRP composite roof fracture.
Polymers 14 01273 g010
Polymers 14 01273 g011 550
Figure 11. TGA curve result.
Figure 11. TGA curve result.
Polymers 14 01273 g011
Polymers 14 01273 g012 550
Figure 12. DSC curve result.
Figure 12. DSC curve result.
Polymers 14 01273 g012
Table
Table 1. Layer configurations of the composite.
Table 1. Layer configurations of the composite.
SampleLayer Configuration
Sample 1CSM 300—CSM 450 (existing GFRP composite roof)
Sample 2CSM 300—STM 450
Sample 3CSM 300—WR 200—CSM 300
Table
Table 2. Data sample test result.
Table 2. Data sample test result.
Type of SampleTensile TestFlexural TestIzod Impact TestBurn Test
No of SpecimenForce(max)
(N)		Strength
(Mpa)		AVR
(Mpa)		No of SpecimenForce(max)
(N)		Strength
(Mpa)		AVR
(Mpa)		No of SpecimenEnergy
(J)		Strength
(J/m2)		AVR
(J/m2)		No of SpecimenBurning Time
(min)		Linear Burning Rate
(mm/min)		AVR
(mm/min)
Sample 11652.134672.540073.8178.3205.5686201.0013.63560290,213.4404792,700.4112.805.555.32
2707.047975.3702277.1234.226723.63627990,230.24489212.755.25
3682.679973.2175377.1177.906533.63627992,762.21605313.074.90
4702.524874.4200476.9200.303343.63627993,237.91972413.035.37
5701.322673.4523578.8178.988253.63627997,058.02400512.985.16
679.4206.8151 612.555.74
777.4203.2057 713.025.30
Sample 21902.454086.462775.71131.2344.4521302.3913.63987693,330.1602192,690.019.855.694.63
2758.211066.24822127.8292.573623.63987689,630.04797213.724.23
3597.000059.36053125.7372.921433.63933290,306.00898311.353.70
4857.234085.92454125.3326.372043.63987693,330.16021413.254.75
5832.915080.57385115.1237.145853.63987696,548.44159510.885.33
6109.3286.9559 612.384.28
7110.2256.3183 713.384.41
Sample 311060.6100124.9240103.51124.1286.3580315.6113.62278392,891.8685392,597.7110.785.194.31
2906.269096.96342128.2259.976723.62278392,182.7703029.354.92
3839.3920102.48203124.2320.979433.62175192,156.51497312.523.91
4924.230095.17944136.7356.065843.62175192,865.4112448.504.82
5908.639098.02835131.4300.815153.62175192,891.86853510.024.39
6130.6340.1770 612.053.49
7132.4344.8655 713.673.44
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Zainudin, M.; Diharjo, K.; Kaavessina, M.; Setyanto, D.; Ubaidillah, U. Industrial Implementation of Aluminum Trihydrate-Fiber Composition for Fire Resistance and Mechanical Properties in Glass-Fiber-Reinforced Polymer Roofs. Polymers 2022, 14, 1273. https://doi.org/10.3390/polym14071273

AMA Style

Zainudin M, Diharjo K, Kaavessina M, Setyanto D, Ubaidillah U. Industrial Implementation of Aluminum Trihydrate-Fiber Composition for Fire Resistance and Mechanical Properties in Glass-Fiber-Reinforced Polymer Roofs. Polymers. 2022; 14(7):1273. https://doi.org/10.3390/polym14071273

Chicago/Turabian Style

Zainudin, Mohammad, Kuncoro Diharjo, Mujtahid Kaavessina, Djoko Setyanto, and Ubaidillah Ubaidillah. 2022. "Industrial Implementation of Aluminum Trihydrate-Fiber Composition for Fire Resistance and Mechanical Properties in Glass-Fiber-Reinforced Polymer Roofs" Polymers 14, no. 7: 1273. https://doi.org/10.3390/polym14071273

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop