1. Introduction
One of the greatest problems connected with sustainable development is the depletion of global natural resources. The global construction industry uses over 40 billion tons of aggregates per year, with even up to 4 billion tons corresponding to Europe. It should be noted that up to 91% of aggregates used in Europe are of natural aggregates [
1]. Along with the development of the construction industry, the amount of construction waste (i.e., concrete, masonry and ceramic rubble, plaster, wallpaper residues, adhesives, paints, door and window woodwork, and installation waste) systematically increases, and their storage is problematic [
2]. Construction waste mainly originates from demolition and dismantling of unused concrete structures, road and railway construction, the destructive effects of natural disasters, as well as by-products from production plants [
3]. According to the European statistics, in 2016 the construction wastes constituted over 36% of total wastes generated in the EU [
4]. Therefore, the possibility of using recycled aggregates (RA) becomes increasingly important. Such aggregate contributes to reduced exploitation of natural resources, costs of construction waste disposal as well as supports the sustainable development of the construction industry [
5,
6].
The International Union of Laboratories and Experts in Construction Materials, Systems and Structures (RILEM) [
7] distinguishes three types of recycled aggregates:
Type I—aggregate from masonry rubble;
Type II—aggregate from concrete rubble;
Type III—aggregates comprising at least 80% natural aggregates.
At present, recycled aggregate is most often utilized in road construction as a road base, sidewalk base, as well as pavement for squares and parking lots [
8,
9,
10,
11]. This is connected with certain limitations of the aggregate obtained from concrete. Numerous studies indicate that recycled aggregate is characterized by lower density and greater water absorptivity improvement [
12,
13,
14,
15,
16]. According to Surendar et al. [
17], water absorptivity increases along with the increase in the recycled aggregate substitution of natural aggregate. Moreover, recycled aggregate is characterized by greater absorptivity and increases the water demand, which may affect the hydration process [
18]. The aggregate obtained from concrete rubble indicates lower mechanical strength than natural aggregates as well as greater susceptibility to abrasion and crushing value. Studies proved that the compressive strength of concrete decreases with the increasing degree of natural aggregate substitution with recycled aggregate [
12,
13,
14,
15,
16,
19].
The main issue with the aggregates from concrete rubble, is the double interfacial transition zone (ITZ) between the aggregate and the old adhered mortar as well as between the new and old ITZ. The old paste is porous and contains microcracks, which contributes to the increased absorptivity of the recycled aggregate [
17]. Numerous studies prove that the content of old adhered mortar increases along with the aggregate crushing degree, which is connected with the technological production process [
6]. Suryawanshi et al. [
13] observed that there is a relationship between the fraction size of the recycled aggregate and the amount of the remaining adhered mortar. According to the authors, the amount of old adhered mortar encapsulating the aggregate increases as the aggregate size decreases. This is connected with the aggregate processing method. As the concrete is being crushed into finer aggregate, old mortar accumulates in the pores of fine aggregate [
14].
These issues can be solved by using high strength recycled aggregates. Earlier studies [
20] indicated that the concrete with recycled aggregate from crushed high performance concrete (HPC) has much more favorable properties compared with the concrete containing the aggregate from ordinary concretes. Adjukiewicz et al. [
21] observed that high strength concretes can be obtained with 100% recycled coarse aggregate from the concretes characterized by the strength of 60 MPa. Gonzalez-Corominas et al. [
22] observed an increase in the compressive strength resulting from the incorporation of aggregates from the concretes with the strength of 100 MPa. HPC comprises, i.a. microsilica, which reduces porosity and permeability of concrete [
23,
24,
25]. Studies prove [
26] that HPC with recycled aggregate achieves similar compressive strength to that of the concretes with natural aggregate.
The aim of the work was to analyze of the results of experimental studies on high strength recycled aggregate in high performance concretes (HPC). Short-term experiments were conducted, including elastic modulus, deflection, load-bearing capacity, and cracks in the beam under increasing load.
3. Results and Discussion
The compressive strength values, measured after three periods of curing (7, 14, 28 days) as well as tensile bending strength after 28 days of curing are presented in
Table 5, as well as
Figure 4 and
Figure 5.
The results indicate that the concrete made of recycled aggregate is characterized by lower compressive strength in each of the curing periods (
Figure 4) and 26% lower flexural strength after 28 days (
Figure 5). It was also observed that the percentage of compressive strength reduction decreased progressively with time. While the early strength of concrete with recycled concrete aggregate after 7 days was 15% lower in comparison to the concrete with natural aggregate, after 28 days of curing, this difference increased to 20%. The concretes with recycled aggregate were also characterized by greater compressive strength increase after 7–28 days, compared to NCAC.
A reduction in the compressive strength of the concrete containing recycled aggregate has already been described in numerous publications [
38,
39,
40,
41,
42]. This phenomenon is connected with the presence of old cement mortar and microcracks appearing during the crushing of concrete [
38]. The concrete with recycled aggregate contains double interfacial transition zones (ITZ) between the old adhered mortar and new ITZ [
39]. Due to the porosity of the old adhered mortar, ITZ between the old and new mortar is characterized by low adhesion and high water absorption [
40]. As a result, the concrete with recycled aggregate is characterized by lower strength than the concrete with natural aggregate. Moreover, recycled aggregate with higher capillary absorption compared to natural aggregate results in the supply of insufficient amount of water required for the hydration of cement particles, thus forming weaker C-S-H phase [
41,
42]. The studies on the HPC with recycled aggregate were conducted by Tu et al. [
41]. Their results show that the samples containing solely recycled aggregate achieve 20–30 (%) lower compressive strength compared with the HPC comprising mixed aggregate (recycled coarse aggregate and natural fine aggregate) during all curing periods. Mohammed et al. [
43] noted that the concretes with f
cm,28 = 70 MPa, reached 14% lower compressive strength when the natural aggregate was completely substituted with recycled aggregate and 3% lower when the substitution amounted to 50%. The concretes with recycled aggregate also achieved lower flexural strength than the concrete with recycled aggregate. The authors [
43] also observed a reduction in flexural strength of 18 and 5 (%) at 50 and 100 (%) aggregate substitution, respectively, compared to the reference concrete.
Moreover, Andreu et al. [
26] observed that HPC with recycled aggregate achieved similar or higher tensile bending strength compared to the concrete with natural aggregate. Complete substitution of natural aggregate with the recycled aggregate obtained from the concrete with the strength of 40 MPa reduced the flexural strength by about 20%. In turn, the application of concrete aggregate with higher strength (60, 100 MPa) improved the tensile strength in bending test by 20% or enabled to achieve a comparable result to the reference concrete, respectively.
Despite the lower mechanical properties of RCAC compared to the high-strength concretes with high strength, made of NCA, the concretes with recycled aggregate were characterized by greater compressive strength values, reaching approximately 100 MPa. Thus, higher strength parameters can be achieved by increasing the designed compressive strength.
The properties of concrete, out of which the aggregate is obtained, have significant influence on the mechanical properties of new concrete [
26]. Therefore, the concrete with the recycled aggregate obtained from high-strength materials also achieved high strength properties. Poon et al. [
44] compared the properties of the recycled aggregates obtained from normal-strength concretes (NPC) and HPC. It turned out that the porosity of the HPC aggregates was less than half the value exhibited by the aggregates from NPC. The Mercury Intrusion Porosimetry (MIP) analyses indicated the sizes of pores in the HPC aggregates to be lower than 0.1 μm, whereas the pores in the aggregates from ordinary concrete reached less than 1μm. Smaller pore distribution in the HPC aggregates can be attributed to the presence of pozzolanic additives in old concrete matrix, which improved the matrix-aggregate ITZ. The HPC aggregate is characterized by dense ITZ with low total pore volume compared to normal-strength concretes.
The strength tests [
44] indicated that the concrete with RCA from ordinary concrete reached 20 and 20.5 (%) lower compressive strength after 7 and 28 days of curing, respectively, compared to the concrete with HPC aggregate. Moreover, the compressive strength of the concretes with the RCA-HPC aggregate following 28 days of curing was only 6.8% lower than the concrete with natural aggregate. Kou et al. [
45] showed that the compressive strength of HPC with recycled aggregate from the concretes characterized by compressive strength of 80–100 (MPa), achieved 65 MPa. In addition, the achieved strength was comparable to the strength of the concretes with natural aggregate. According to Gonzales-Corominas et al. [
22], the compressive strength in the early curing period is dependent on the amount of free water, rather than the quality of aggregate. The recycled HPC aggregate with moderate moisture content absorbs the entire free water, lowering the initial w/c ratio in ITZ during the early hydration process. This leads to the release of water and self-hardening in the later period and filling the ITZ with the newly created hydrates. As a result, the cement–aggregate bonding improves [
22];
The concrete strength largely depends on the mortar–aggregate ITZ [
26]. ITZ can be improved through the application of silica fume, which—owing to its thickening abilities—increases the density of ITZ [
46,
47]. Corinaldesi et al. [
48] showed that the concrete with recycled aggregate and 10% silica fume addition reached 25% and 38% greater compressive strength after 28 days of curing, than the concrete with natural aggregate and the concrete with recycled aggregate without additives, respectively. Authors [
47] observed that the recycled aggregates containing calcium hydroxide improve the pozzolanic properties of silica fume and fly ash. Interestingly, the concretes with silica fume reached 14% higher modulus of elasticity compared with the reference concrete.
Table 6 presents the mean values of modulus of elasticity for the cylindrical samples with known strength values.
The concretes made from recycled aggregate were characterized by 15% lower modulus of elasticity compared to the concretes made of natural aggregate.
Figure 6 presents the samples during the elastic modulus E
cm,28 test.
This is confirmed in the studies by Wagih et al. [
49], where 100% substitution of natural aggregate with recycled aggregate reduced the modulus of elasticity by 15% compared to the reference concretes. The authors of the paper noticed a beneficial influence of silica fume application on the elastic modulus increase, which improves the ITZ between the old adhered mortar and new mortar, acting as microfiller. The silica fume addition in the concretes with 100% recycled aggregate increased E
cm,28 by 17% compared to the concrete without additive. The studies by Andreu et al. [
26] showed that all concretes containing the recycled aggregate obtained from concretes of varying strength (40, 60, and 100 MPa) were characterized by lower modulus of elasticity compared to the concrete with natural aggregate. Nevertheless, it should be noted that the concretes with recycled aggregate obtained modulus of elasticity in the range of 37.15–48.54 GPa, which is relatively high. Moreover, the authors [
26] observed that the modulus of elasticity increases along with the strength of concrete, from which the aggregate was obtained. While the concretes made of the aggregate obtained from the 40 MPa strength concrete were characterized by 26.3% lower elastic modulus than the reference concrete, the concretes with HPC aggregate (100 MPa) reached the value which was only 3.7% lower than conventional concrete. According to Neville [
50] the modulus of elasticity of concrete largely depends on the modulus of aggregate forming the concrete. In turn, Andreu et al. [
26] observed that the modulus of elasticity strictly depends on the density of the material. Since the concretes with recycled aggregate are characterized by lower density; thus, the modulus of elasticity is lower than that of the concrete with natural aggregate [
51]. In the above-mentioned studies, the concretes with greater compressive strength were characterized by higher modulus of elasticity. The correlations between elastic modulus and compressive strength are presented in
Figure 7.
The graph clearly shows close correlation between the modulus of elasticity and the compressive strength of concrete. This is also confirmed by the previous studies conducted by the authors [
30]. Similar conclusions were also drawn by Góra et al. [
52]. The authors also emphasize the influence of aggregate crushing resistance on the modulus of elasticity of concrete. The concretes containing the aggregate with low crushing resistance had lower moduli of elasticity. Since recycled aggregates are characterized by low crushing resistance [
12,
13,
14,
15,
16], the concretes produced using these aggregates have lower modulus of elasticity.
The values of deflections of the beams in the middle of the span are show in
Table 7 and
Figure 8.
The results of studies indicate that reinforced concrete made of natural aggregate shows smaller deflection compared to the concrete containing recycled aggregate. In case of the applied load of 45 kN, this value is almost 2.5-fold lower than RCAC. The greatest RCAC beam deflection, amounting to 9.08 mm, was noted after applying the load of 45 kN; in turn, the beam with natural aggregate was loaded with 50 kN, achieving the deflection of 11.23 mm.
Figure 9 represents a reinforced concrete T-beam during the bending test.
Observations of the deflections during the bending test were also conducted by Khan et al. [
53]. The studies conducted by the authors confirmed that the reinforced beams with recycled aggregate content of 30% of total coarse aggregate as well as fine natural aggregate exhibited twice greater deflection, compared to the beams made of natural aggregate.
Lapko et al. [
54,
55] observed that concrete beams containing RCA crack faster and are characterized by greater deflections compared to the beams made of natural aggregate. While the considered beams exhibited comparable deflections in the tension zone, the deflections in the compression zone of the beams with recycled aggregate were 45% greater, compared to the concretes with natural aggregate. The authors also observed a similar destruction mechanism in all beams, regardless of the type of aggregate, resulting from plastification of reinforcement in the tension zone.
The load bearing capacity of our T-beam was tested until destruction occurred. All beams, based on natural aggregates and high strength recycled aggregates, were destroyed through plastification of reinforcement in the tension zone.
Table 8 presents the values of rupture force and breaking moments of T-beams.
The studies indicate that the strength of reinforced RCAC T-beam, despite similar values, is 7.6% lower compared to the beam made of natural aggregate. A reduction in the load bearing capacity of the reinforced concrete beams following the substitution of natural aggregate with recycled aggregate was confirmed in other studies [
54,
55,
56,
57]. According to Arezoumandi et al. [
58] the lower breaking moment of the concrete with recycled aggregate is caused by double ITZ in RAC and the related zone porosity as well as numerous microcracks in the aggregate occurring in the course of recycled aggregate processing.
Saara-Paz et al. [
59] observed a decrease in the bending moment value along with the increasing substitution of natural aggregate with recycled one in the concretes with the w/c ratio equal to 0.65 and 0.50. Complete natural aggregate substitution in the concretes with w/c = 0.65 reduced the bending moment by 34%, whereas the same amount of substitution in the concretes with lower w/c decreased the bending moment by 28%, compared to the concrete with natural aggregate.
According to Xiao et al. [
60], the load bearing capacity of a RA beam results from the tensile reinforcement and compressed zone dependent on often random compressive strength of the concrete with the recycled aggregate. The authors’ statistical study, showed that recycled aggregate with non-uniform quality increases the scatter of the concrete compressive strength results. Mukherjee et al. [
61] while analyzing the statistical strength parameters of concrete made of recycled aggregate, noticed that the coefficient of variation of the compressive strength is 30% higher in the case of recycled aggregates compared to the concrete made of natural aggregates.
Fahmy et al. [
62] investigated reinforcement concrete beams with different natural aggregate substitution degree. The studies showed that the reinforcement concrete beams with 25% substitution of natural coarse aggregate with recycled one reached the load bearing capacity comparable to the reference concrete. It should be noted that increasing the substitution of natural coarse aggregate with recycled aggregate to 50% improved the tensile load bearing capacity by 11.4%. According to the authors, the increased tensile load bearing capacity was caused by improved maximum load. As a result, the yield strength of the beam with recycled aggregate increased by 13.5%. The authors [
62] drew attention to the fact that despite a similar crack morphology of the beam with 50% RCA to the reference beam, the beam with recycled aggregate exhibited a lower number of cracks.
In our testing, despite a lower breaking moment in the concretes with recycled aggregate, all beams were characterized by the same destruction mechanism.
Figure 10 presents the dependence of the applied load on the crack width in the investigated beams.
The cracks on all beams had a similar appearance. The first perpendicular cracks were observed at the load of 15 kN. They occurred in the middle zone, in the area of constant bending moment. Due to a very small opening of the cracks at this load, it seems that only the surface lime layer was cracked. Initially, the image of diagonal cracks was similar to that of perpendicular cracks, with similar opening values and high inclination angles. A substantial increase in the influence of diagonal cracks on the whole cracking image occurred under the load of 35 kN. They started in the zone between the area of applied forces and supports, and then propagated in the direction of point applied forces.
Figure 11 shows crack shaping and development in the test samples.
Propagation of cracks at different stages was observed by Yang et al. [
63]. The authors observed a greater number of cracks at the initial cracking stage in the beams with recycled aggregate (RA), compared to the beams with natural aggregate. This phenomenon was attributed to weaker ITZ and the remains of old adhered mortar on the recycled aggregate. Despite a greater amount of cracks in a RAC beam, the authors observed similar crack propagation both in the concretes with natural and recycled aggregate. The cracks appeared in the flexure zone and then propagated in the compressed zone until beam destruction. Arezoumandi et al. [
58], while investigating reinforced concrete beams with recycled aggregate, observed that despite similar morphology and crack propagation, the beams with RA were characterized by smaller distance between cracks on the beam span compared to the beams with natural aggregate. The authors [
58] also observed lower rigidity of the beams with RA after cracking moment, which confirms the attainment of lower moduli of elasticity of the concretes with recycled aggregate.