Next Article in Journal
Simplified Calculation Model and Experimental Validation of the Force Transfer Ratio of Steel–Concrete Joint of Hybrid Box Girder
Next Article in Special Issue
Effect of CrF3 Addition on Photoluminescence Properties of Lead-Free Cs4SnBr6−xFx Zero-Dimensional Perovskite
Previous Article in Journal
Antimicrobial Properties of Chitosan-Modified Cotton Fabric Treated with Aldehydes and Zinc Oxide Particles
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 16
Issue 14
10.3390/ma16145093
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effects of Film Thickness on the Residual Stress of Vanadium Dioxide Thin Films Grown by Magnetron Sputtering

by
Yuemin Wang
1,2,3,
Xingang Li
4,
Xiangqiao Yan
5,
Shuliang Dou
5,*,
Yao Li
5 and
Lei Wang
1,*
1
Shenzhen Key Laboratory of Polymer Science and Technology, College of Materials Science and Engineering, Shenzhen University, Shenzhen 518060, China
2
College of Physics and Optoelectronic Engineering, Shenzhen University, Shenzhen 518060, China
3
Jiangxi Construction Engineering (Group) Construction Industry Investment Corporation Limited, Nanchang 330029, China
4
Jiangxi Construction Engineering (Group) Corporation Limited, Nanchang 330029, China
5
Center for Composite Materials and Structure, Harbin Institute of Technology, Harbin 150080, China
*
Authors to whom correspondence should be addressed.
Materials 2023, 16(14), 5093; https://doi.org/10.3390/ma16145093
Submission received: 3 April 2023 / Revised: 5 July 2023 / Accepted: 15 July 2023 / Published: 19 July 2023
(This article belongs to the Special Issue Advanced Optical Materials: Design, Fabrication, Measurement and Application)
Browse Figures
Review Reports Versions Notes

Abstract

:
Vanadium dioxide (VO2) thin films of different thicknesses were prepared by regulating the deposition time (2, 2.5, 3, and 3.5 h). The impact of deposition time on the microstructure, surface morphology, and cross-section morphology was investigated. The results showed that the grain size increased with the film thickness. Meanwhile, the influence of film thickness on the residual stress was evaluated by X-ray diffraction. The phenomenon of “compressive-to-tensile stress transition” was illustrated as the thickness increased. The change of dominant mechanism for residual stress was used for explaining this situation. First, the composition of residual stress indicates that growth stress play a key role. Then, the effect of “atomic shot peening” can be used to explain the compressive stress. Lastly, the increased grain size, lower grain boundary density, and “tight effect” in the progress of film growth cause tensile stress.

1. Introduction

Vanadium dioxide (VO2) undergoes an invertible semiconductor–metal transition (SMT) at approximately 68 °C, together with dramatic variations in optical and electrical properties [1]. Based on these unique phenomena, VO2 is widely used in thermal switching [2], smart windows [3,4], smart thermal control coating [5,6,7,8], infrared stealth devices [9], and so on. Different deposition methods may affect the morphology, structure, and other characteristics. According to the reaction medium involved, deposition methods can be divided into gas- and solution-based deposition [10]. Gas-based deposition is mainly composed of chemical vapor deposition (CVD) [11] and physical vapor deposition (PVD) [12]. Solution-based deposition includes sol–gel [13], the electrochemical process [14], the hydrothermal process [15], and polymer-assisted deposition [16]. The sol–gel process is a typical wet chemical technique, and due to its fine control ability of chemical compositions, it has been extensively used to synthesize films doped with other elements. Polymer-assisted deposition is a versatile strategy for the deposition of high-quality polycrystalline films, providing a cheap and scalable alternative method for the sol–gel process. The hydrothermal method is an approach to fabricating nano-scale thin films and has the advantage of precise phase control. The hydrothermal product is a metastable or mixture phase, which makes the preparation of specific thermochromic VO2 films more difficult. The electrochemical approach has the ability to deposit thin films on substrates with complex geometries. It requires a conducting substrate, which is very helpful for device fabrication. CVD is a common industrial technique for depositing high-performance thin films, but it has the limitations of vapor transport and the equipment required is usually complex and expensive. Compared to other methods, the competitive advantages of the magnetron sputtering process include remarkable homogeneity and compactness in products, promising scalability in large-scale substrates, and high efficiency in deposition.
In practical terms, thin films are mostly used in the formation of films/substrates. Superimposed differences in preparation conditions and methods result in thin film/substrate materials in a complex stress state, leading to inevitable residual stress during the preparation process [17,18,19]. Residual stress is the main reason for functional failure. Generally, tensile stress triggers cracking, while compressive stress triggers wrinkles and bubbling [20]. These failures destruct the configurational integrity and physical properties of thin films. At present, research on residual stress for thin films is facing many difficulties. On the one hand, it is hard to interpret the generation mechanism. The stress originates from some structural imperfections (such as impurities, vacancies, grain boundaries, dislocations, and stacking faults), surface energy, and lattice mismatch [21,22]. It involves complex physical and chemical processes and relates to nucleation and grain growth. Different growth stages or deposition conditions can lead to different stress mechanisms playing a leading role. The exploration of the mechanism of residual stress generation is still in an early stage. Existing mechanism models include the impurity effect [23], lattice mismatch [24], atomic shot peening [25], and grain boundary elimination [26]. On the other hand, there are many factors during film preparation and post-treatment that affect the stress. For example, the influence of characteristic parameters (reaction conditions [27], substrates [28], annealing temperature [29], and thickness [30]) has become a research focus. Asa’ad et al. evaluated the influence of sputtering power, sputtering pressure, and annealing time on the residual stress of sputtered tantalum thin films [31]. Kusaka et al. investigated the crystal orientation and residual stress development in AlN films at various input powers [32]. Liu et al. studied the impact of substrate temperature on the structural and attribute evolution of magnetron-sputtered Ti6Al4V films [33]. Unfortunately, there are few reports on the systematic study of the residual stress of VO2 thin films, and only some qualitative speculation exists, such as the effect of phase transition [34,35,36,37]. In addition, the test method is also a key point in the study of the residual stress of thin films. Traditional measurement methods such as drilling, ring strain relief, and ultrasound cannot meet the testing requirements of micro-nano-scale thin films [38]. For instance, the installation and alignment of the sample is very difficult, and the resolution cannot be satisfied. Moreover, size and surface effects make analysis more complex. Therefore, some calculation methods are continuing to be improved. For example, the curvature method based on Stoney’s formula is suitable for measuring almost all types of thin films [39], while the X-ray diffraction technique can be used on typically crystalline thin films [40], and the Raman spectroscopy is used for amorphous thin films [41].
In this paper, VO2 thin films of different thicknesses were prepared by magnetron sputtering. The impact of film thickness, grain size, microstructure, and morphology on residual stress was explored. At the same time, the dominant mechanism of residual stress is discussed in detail.

2. Experiment Details

VO2 thin films were deposited on ITO substrates by magnetron sputtering with a metal vanadium target (99.99%, Φ 76.2 mm). A turbo-molecular pump was used to realize a base vacuum of less than 5 × 10−3 Pa. A mixture of Ar (99.9999% purity) and O2 (99.9999% purity) was introduced into the chamber. The main fabrication parameters are shown in Table 1. The deposition time was changed to regulate the thickness of the films. Then, the samples were heat-treated at 400 °C for 2 h in order to obtain high crystalline VO2.
The crystalline structures of the samples were characterized using an X-ray diffraction diffractometer (Empyrean, Malvern Panalytical, Almelo, Netherlands) with Al-Kαradiation. The vibrational modes were determined using Raman microscopy (XploRA PLUS, HORIBA Scientific, Montpellier, France) with a 532 nm laser. The film morphology was observed through an atomic force microscope (Dimension3100, BRUKER, Bremen, Germany), along with scanning electron microscopy (Supra, Zeiss, Oberkochen, Germany). The reflectance of the samples was characterized using infrared spectroscopy (VERTEX-70, BRUKER, Bremen, Germany).
In this paper, the X-ray diffraction approach was employed to test residual stress [42]. X-ray diffraction is an important, attractive, and nondestructive measurement technique that allows evaluating the average residual stress. This method consists of measuring the lattice spacing of a specific plane at different tilt angles. According to the theory of elasticity and Bragg diffraction, the residual stress can be obtained by Equation (1):
σ = K ⋅ M
where M = ∂ ( 2 θ ) / ∂ ( sin 2 ψ ) , K = − E / 2 ( 1 + υ ) cot θ 0 , K is the stress constant, θ 0 is the diffraction half-angle without stress, and ψ is the angle between the normal from the sample surface and the normal from the diffractive crystal surface.

3. Results and Discussion

3.1. Structural Characterization

Figure 1a indicates the Raman spectroscopy for the VO2 thin films. In the case of different deposition times, obvious Raman bands were discovered at 190, 221, 304, 385, 504, and 610 cm−1. In general, the intensity and width of the Raman peaks were weak and wide for thinner films. However, the phenomenon did not exist in this work, because the four kinds of films were relatively thick. The peak locations, symmetry assignments, and spectral characteristics are similar to those in other studies, and proved high crystallinity of thin films [43,44,45]. It is worth noting that there was no ITO Raman peak in this spectroscopy, because VO2 has high absorption for 532 nm wavelength.
Figure 1b shows the infrared reflectance spectra that formed for VO2 thin films under semi-conductive and metallic states. In the cold state (insulating, M-phase, a monoclinic-like structure), the VO2 thin films indicated high infrared transmittance. After interference with ITO, wave troughs formed. With the increase in deposition time, the wave trough appeared red-shifted and the modulation amplitude started to increase. After the phase transition (metallic, R-phase, a rutile-like structure), the VO2 thin film changed from high infrared transmission to high reflection. These changes also indicate that high-performance VO2 thin films had been prepared.
Figure 2a shows the XRD patterns for VO2 thin films with different deposition times. Diffraction peaks located at 27.81°, 55.56°, and 70.58° can clearly be observed. These conditions were regarded as the VO2 (011), (−213), and (−132) planes (JCPDS 43-1051). The (011) peaks were far more powerful than others, corresponding to other reports [43,46]. The intensity of the VO2 (011) peaks showed an acute growing tendency as the deposition time increased. This demonstrates that the crystallinity of VO2 thin films can be improved through increasing the thickness. In addition, no other impurity peaks were observed except for ITO, indicating the formation of high-performance thin films.
Figure 2b shows the grain sizes and full width at half-maximum (FWHM) of VO2 (011) peaks with different deposition times. It can be concluded that the grain size increased with increasing deposition time. As the thickness increased, the full width at half-maximum decreased from 0.299° to 0.197°, while the grain sizes increased from 27.11 to 41.14 nm, calculated using the Scherrer formula. Similar phenomena have also been reported [43,47,48].

3.2. Morphology

Figure 3 indicates the surface morphology of the VO2 thin films with various deposition times. It can be seen that the surface of all films were predominantly flat without obvious cracks, revealing that the surface morphology was independent of thickness in this research.
Figure 4 shows the cross-section morphology of the VO2 thin films on ITO substrates with various deposition times. The cross-section images were used to determine the film thickness and analyze the process of growth. The films were homogeneous and dense and for all films, the morphology can be characterized as compact packing of columns. Similar columnar-like growth can also be observed for the VO2 films deposited by magnetron sputtering in other research works [43,47]. The film thickness was found to vary from 460 to 720 nm as the deposition time increased from 2 to 3.5 h.
Figure 5 shows AFM images of the surface morphology of the VO2 films with four different thicknesses. Under different conditions, all of the films exhibited a flat surface and tightly packed morphology, which is similar to the phenomenon observed by SEM. The average surface roughness, measured by AFM, was approximately 4.3 nm (more details in the Supporting Information (a)) (more details in the Supporting Information (Figure S1)).

3.3. Residual Stress

The X-ray diffraction method was performed to measure the residual stress (more details in the Supporting Information (Figure S2)). The residual stress obtained is plotted in Figure 6 as a function of deposition time. The thinnest film had the highest compressive stress of −9.009 GPa, while the film resulting from a 3.5 h deposition time had the highest tensile stress of 18.42 GPa. This indicates that as the film thickness increased, the residual stress presented the phenomenon of “compression-to-tensile stress transition.”
According to the deposition and formation process of thin films, the residual stress consists of thermal stress, interface stress, and growth stress [49,50,51]. Growth stress comes from structural drawbacks in the growth progress, while thermal and interface stresses occur due to mismatch of the thin film and substrate. First, at the initial stage of film deposition, if there is a large difference between the film and substrate or quite a high density of defects and impurities, interface mismatch occurs and leads to interface stress. However, previous work has shown that when the film thickness in the range of sub-microns, interface stress does not play a critical role in the total residual stress [46].
Second, thermal stress is generated when annealing due to mismatch of the CTE (coefficient of thermal expansion) between the film and the substrate. On the basis of the analytical model proposed by Tsui (Supporting Information (c)) [50], thermal stress is the function of temperature, thickness, elastic modulus, and CTE. According to the model, when the thickness of the thin film is far less than the substrate, the film thickness has little effect on the thermal stress. Thermal stress in this study was simulated, and it can be seen in the Supporting Information (Figure S3). The results revealed that the thermal stress ranged from −0.21 to 0.023 GPa, so the impact on the residual stress can be ignored. Therefore, the change of residual stress in this work should be considered the influence of growth stress.
The formation of growth stress involves complex physical and chemical processes, which are the result of multiple mechanisms. As shown in Figure 6, residual stress can be divided into two parts: Compressive stress and tensile stress. In the first part, the “atomic shot peening” effect is the main control mechanism [51], which is linked to the clash from neutral inert gas atoms as the film grows. In the progress of sputtering, these adatoms from the film surface are hit by the incident ions and become imbedded in film’s sub-surface through knock-on. The misfitted atoms produce a strain area in the circumambient matrix, thus bringing about a kind of compressive stress among films.
When the film growth proceeds to a certain stage, the dominating mechanism is changed. The transition from compressive to tensile stress may be interpreted as being caused by two reasons. On the one hand, in the process of film deposition, the surface atoms do not have enough time to diffuse, and the metastable structure undergoes a spontaneous ordering process. Ordered atoms, along with the annihilation of pores and drawbacks, bring about volume shrinkage and densification of thin films, triggering a natural trend of the films for the sake of promoting tensile stress owning the film thickness. When the tensile stress of this “tight effect” exceeds the compressive stress caused by the “atomic shot peening” effect, tensile stress gradually occurs. On the other hand, the grain size increases with the film thickness, and the density of grain boundaries decreases. In this case, there is less probability of excess atoms occurring for the purpose of being inserted into the grain boundaries, so the compressive stress decreases and gradually transforms into tensile stress. To sum up, the thickness not only affects the grain size, but also causes the transition of the dominant mechanism for residual stress.

4. Conclusions

In conclusion, VO2 thin films of different thicknesses deposited onto ITO substrates were prepared by direct current magnetron sputtering. The results proved that the grain size increases with the film thickness. The values of residual stresses varied from the compressive to tensile state as the thickness increased. On the one hand, the “atomic shot peening” effect can be used to explain the compressive stress. On the other hand, the increased grain size, lower grain boundary density, and “tight effect” by film growth can cause the tensile stress. The transition of the dominant mechanism for residual stress was used to explain the phenomenon of “compressive-to-tensile stress transition.” The results of this study could be beneficial for the design and application of many functional materials.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/ma16145093/s1, Figure S1: The surface roughness of VO2 thin film measured by AFM; Figure S2: θ–2θ scans for reflection at different inclination angle ψ; Figure S3: The thermal stress of VO2 thin film with 720 nm thickness.

Author Contributions

Conceptualization, S.D. and Y.W.; methodology, X.L. and X.Y.; software, X.Y.; formal analysis, X.L.; investigation, Y.W. and S.D.; writing—original draft preparation, Y.W.; writing—review and editing, L.W.; supervision, Y.L.; funding acquisition, L.W. All authors have read and agreed to the published version of the manuscript.

Funding

This work was financially supported by the National Natural Science Foundation of China (grant nos. 52272291, 22075185, and 51773118), the Guangdong Basic and Applied Basic Research Foundation (grant no. 2019A1515111040), and the funding program of Foshan supporting policies for promoting the service industry of scientific achievements in universities (grant no. 2019XCC08).

Institutional Review Board Statement

The study did not require ethical approval.

Informed Consent Statement

Not applicable.

Data Availability Statement

All data presented in this study are available upon request from the corresponding author.

Conflicts of Interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

References

  1. Zhang, Y.; Xiong, W.; Chen, W.; Zheng, Y. Recent progress on vanadium dioxide nanostructures and devices: Fabrication, properties, applications and perspectives. Nanomaterials 2021, 11, 338. [Google Scholar] [CrossRef]
  2. Ren, Y.; Zhou, T.; Jiang, C.; Tang, B. Thermally switching between perfect absorber and asymmetric transmission in vanadium dioxide-assisted metamaterials. Opt. Express 2021, 29, 7666–7679. [Google Scholar] [CrossRef]
  3. Vu, T.D.; Xie, H.; Wang, S.; Hu, J.; Zeng, X.; Long, Y. Durable vanadium dioxide with 33-year service life for smart windows applications. Mater. Today Energy 2022, 26, 100978. [Google Scholar] [CrossRef]
  4. Wei, H.; Gu, J.; Ren, F.; Zhang, L.; Xu, G.; Wang, B.; Song, S.; Zhao, J.; Dou, S.; Li, Y. Smart materials for dynamic thermal radiation regulation. Small 2021, 17, 2100446. [Google Scholar] [CrossRef]
  5. Li, Z.; Zhao, S.; Shao, Z.; Jia, H.; Huang, A.; Jin, P.; Cao, X. Deterioration mechanism of vanadium dioxide smart coatings during natural aging: Uncovering the role of water. Chem. Eng. J. 2022, 447, 137556. [Google Scholar] [CrossRef]
  6. Dou, S.; Xu, H.; Zhao, J.; Zhang, K.; Li, N.; Lin, Y.; Pan, L.; Li, Y. Bioinspired microstructured materials for optical and thermal regulation. Adv. Mater. 2021, 33, 2000697. [Google Scholar] [CrossRef]
  7. Dou, S.; Zhang, W.; Ren, F.; Gu, J.; Wei, H.; Chen, X.; Xu, G.; Yan, X.; Zhan, Y.; Zhao, J.; et al. The infrared optical performance of VO2 film prepared by HiPIMS. Mater. Chem. Phys. 2021, 259, 124042. [Google Scholar] [CrossRef]
  8. Wei, H.; Gu, J.; Ren, F.; Geng, C.; Guan, H.; Liang, S.; Fan, Q.; Zhao, J.; Wang, C.; Dou, S.; et al. Kirigami-Inspired Reconfigurable Thermal Mimetic Device. Laser Photonics Rev. 2022, 16, 2200383. [Google Scholar] [CrossRef]
  9. Wei, H.; Yan, X.; Gu, J.; Ren, F.; Dong, X.; Guan, H.; Geng, C.; Liang, S.; Fan, Q.; Li, L.; et al. A universal approach to fabricating infrared-shielding smart coatings based on vanadium dioxide. Sol. Energy Mater. Sol. Cells 2022, 241, 111728. [Google Scholar] [CrossRef]
  10. Wang, S.; Liu, M.; Kong, L.; Long, Y.; Jiang, X.; Yu, A. Recent progress in VO2 smart coatings: Strategies to improve the thermochromic properties. Prog. Mater. Sci. 2016, 81, 1–54. [Google Scholar] [CrossRef]
  11. Rajeswaran, B.; Umarji, A.M. Defect engineering of VO2 thin films synthesized by Chemical Vapor Deposition. Mater. Chem. Phys. 2020, 245, 122230. [Google Scholar] [CrossRef]
  12. Vu, T.D.; Chen, Z.; Zeng, X.; Jiang, M.; Liu, S.; Gao, Y.; Long, Y. Physical vapour deposition of vanadium dioxide for thermochromic smart window applications. J. Mater. Chem. C 2019, 7, 2121–2145. [Google Scholar] [CrossRef]
  13. El-Desoky, M.M.; Morad, I.; Ali, M.A.; Ali, A.M.; Sayed, M.A.; Algami, H.; Abd-Rehim, A.F. Annealing temperatures effect on the electrical and structural properties of nanocrystalline vanadium dioxide films prepared by Sol–Gel technique. Appl. Phys. A 2021, 127, 366. [Google Scholar] [CrossRef]
  14. Wei, T.; Li, Q.; Yang, G.; Wang, C. An electrochemically induced bilayered structure facilitates long-life zinc storage of vanadium dioxide. J. Mater. Chem. A 2018, 6, 8006–8012. [Google Scholar] [CrossRef]
  15. Kim, J.; Paik, T. Recent advances in fabrication of flexible, thermochromic vanadium dioxide films for smart windows. Nanomaterials 2021, 11, 2674. [Google Scholar] [CrossRef]
  16. Devthade, V.; Lee, S. Synthesis of vanadium dioxide thin films and nanostructures. J. Appl. Phys. 2020, 128, 231101. [Google Scholar] [CrossRef]
  17. Chen, Y.S.; Lin, C.C.; Chin, T.S.; Chang, J.Y.J.; Sung, C.K. Residual stress analysis of electrodeposited thick CoMnP monolayers and CoMnP/Cu multilayers. Surf. Coat. Technol. 2022, 434, 128169. [Google Scholar] [CrossRef]
  18. Dutta, S.; Pandey, A. Overview of residual stress in MEMS structures: Its origin, measurement, and control. J. Mater. Sci. Mater. Electron. 2021, 32, 6705–6741. [Google Scholar] [CrossRef]
  19. Dive, V.; Lakade, S. Recent research progress on residual stress measurement using non-destructive testing. Mater. Today: Proc. 2021, 47, 3282–3287. [Google Scholar] [CrossRef]
  20. Rao, Z.; Berman, S.; Yang, P.; Depla, D.; Chason, E. Understanding residual stress in thin films: Analyzing wafer curvature measurements for Ag, Cu, Ni, Fe, Ti, and Cr with a kinetic model. J. Appl. Phys. 2021, 130, 135304. [Google Scholar] [CrossRef]
  21. Jiang, G.; Haiyang, F.; Bo, P.; Renke, K. Recent progress of residual stress measurement methods: A review. Chin. J. Aeronaut. 2021, 34, 54–78. [Google Scholar]
  22. Oettel, H.; Wiedemann, R. Residual stresses in PVD hard coatings. Surf. Coat. Technol. 1995, 76, 265–273. [Google Scholar] [CrossRef]
  23. Alvarez-Vera, M.; Hdz-García, H.M.; Díaz-Guillén, J.C.; Muñoz-Arroyo, R.; Acevedo-Davila, J.L.; Mtz-Enriquez, A.I.; Badillo, C.F. Tribological performance of Ti nanolayer coating post plasma nitriding treatment on Co based alloy. Wear 2021, 477, 203798. [Google Scholar] [CrossRef]
  24. Wu, B.; Yu, Y.; Wu, J.; Shchelkanow, I.; Ruzic, D.; Huang, N.; Leng, Y. Tailoring of titanium thin film properties in high power pulsed magnetron sputtering. Vacuum 2018, 150, 144–154. [Google Scholar] [CrossRef]
  25. Choi, H.M.; Choi, S.K.; Anderson, O.; Bange, K. Influence of film density on residual stress and resistivity for Cu thin films deposited by bias sputtering. Thin Solid Film. 2000, 358, 202–205. [Google Scholar] [CrossRef]
  26. Chason, E.; Guduru, P.R. Tutorial. Understanding residual stress in polycrystalline thin films through real-time measurements and physical models. J. Appl. Phys. 2016, 119, 191101. [Google Scholar] [CrossRef]
  27. Österlund, E.; Ross, G.; Caro, M.A.; Paulasto-Kröckel, M.; Hollmann, A.; Klaus, M.; Meixner, M.; Genzel, C.; Koppinen, P.; Pensala, T.; et al. Stability and residual stresses of sputtered wurtzite AlScN thin films. Phys. Rev. Mater. 2021, 5, 035001. [Google Scholar] [CrossRef]
  28. Li, H.; Sun, P.; Cheng, D.; Liu, Z. Effects of deposition temperature on structure, residual stress and corrosion behavior of Cr/TiN/Ti/TiN films. Ceram. Int. 2021, 47, 34909–34917. [Google Scholar] [CrossRef]
  29. Lim, W.C.; Singh, J.P.; Kim, Y.; Song, J.; Chae, K.H.; Seong, T.Y. Effect of thermal annealing on the properties of ZnO thin films. Vacuum 2021, 183, 109776. [Google Scholar] [CrossRef]
  30. Xi, Y.; Gao, K.; Pang, X.; Yang, H.; Xiong, X.; Li, H.; Volinsky, A.A. Film thickness effect on texture and residual stress sign transition in sputtered TiN thin films. Ceram. Int. 2017, 43, 11992–11997. [Google Scholar] [CrossRef]
  31. Bunting, A.; Cheung, R. Evaluation of residual stress in sputtered tantalum thin-film. Appl. Surf. Sci. 2016, 371, 571–575. [Google Scholar]
  32. Kusaka, K.; Taniguchi, D.; Hanabusa, T.; Tominaga, K. Effect of input power on crystal orientation and residual stress in AlN film deposited by dc sputtering. Vacuum 2000, 59, 806–813. [Google Scholar] [CrossRef]
  33. Liu, G.; Yang, Y.; Huang, B.; Luo, X.; Ouyang, S.; Zhao, G.; Jin, N.; Li, P. Effects of substrate temperature on the structure, residual stress and nanohardness of Ti6Al4V films prepared by magnetron sputtering. Appl. Surf. Sci. 2016, 370, 53–58. [Google Scholar] [CrossRef]
  34. Long, S.; Cao, X.; Li, N.; Xin, Y.; Sun, G.; Chang, T.; Bao, S.; Jin, P. Application-oriented VO2 thermochromic coatings with composite structures: Optimized optical performance and robust fatigue properties. Sol. Energy Mater. Sol. Cells 2019, 189, 138–148. [Google Scholar] [CrossRef]
  35. Balakrishnan, V.; Ko, C.; Ramanathan, S. Size effects on stress relaxation across the metal-insulator transition in VO2 thin films. J. Mater. Res. 2011, 26, 1384–1387. [Google Scholar] [CrossRef]
  36. Tsai, K.Y.; Chin, T.S.; Shieh HP, D.; Ma, C.H. Effect of as-deposited residual stress on transition temperatures of VO2 thin films. J. Mater. Res. 2004, 19, 2306–2314. [Google Scholar] [CrossRef] [Green Version]
  37. Viswanath, B.; Ko, C.; Ramanathan, S. Thermoelastic switching with controlled actuation in VO2 thin films. Scr. Mater. 2011, 64, 490–493. [Google Scholar] [CrossRef]
  38. Tabatabaeian, A.; Ghasemi, A.R.; Shokrieh, M.M.; Marzbanrad, B.; Baraheni, M.; Fotouhi, M. Residual stress in engineering materials: A review. Adv. Eng. Mater. 2022, 24, 2100786. [Google Scholar] [CrossRef]
  39. Hayase, T.; Waki, H.; Adachi, K. Residual stress change in thermal barrier coating due to thermal exposure evaluated by curvature method. J. Therm. Spray Technol. 2020, 29, 1300–1312. [Google Scholar] [CrossRef]
  40. Schuster, T.; Plöger, J.; Louis, A.K. Depth-resolved residual stress evaluation from X-ray diffraction measurement data using the approximate inverse method. Int. J. Mater. Res. 2022, 94, 934–937. [Google Scholar] [CrossRef]
  41. Das, B.; Brodard, P.; Bandyopadhyay, P.P. Raman spectroscopy assisted residual stress measurement of plasma sprayed and laser remelted zirconia splats and coatings. Surf. Coat. Technol. 2019, 378, 124920. [Google Scholar] [CrossRef]
  42. Ali, A.; Chiang, Y.W.; Santos, R.M. X-ray diffraction techniques for mineral characterization: A review for engineers of the fundamentals, applications, and research directions. Minerals 2022, 12, 205. [Google Scholar] [CrossRef]
  43. Zhu, M.; Wang, H.; Li, C.; Qi, H.; Zhang, D.; Lv, W. Thickness-modulated thermochromism of vanadium dioxide thin films grown by magnetron sputtering. Surf. Coat. Technol. 2019, 359, 396–402. [Google Scholar] [CrossRef]
  44. Petrov, G.I.; Yakovlev, V.V.; Squier, J. Raman microscopy analysis of phase transformation mechanisms in vanadium dioxide. Appl. Phys. Lett. 2002, 81, 1023–1025. [Google Scholar] [CrossRef]
  45. Pan, M.; Liu, J.; Zhong, H.; Wang, S.; Li, Z.; Chen, X.; Lu, W. Raman study of the phase transition in VO2 thin films. J. Cryst. Growth 2004, 268, 178–183. [Google Scholar] [CrossRef]
  46. Yang, Z.; Ko, C.; Ramanathan, S. Metal-insulator transition characteristics of VO2 thin films grown on Ge (100) single crystals. J. Appl. Phys. 2010, 108, 073708. [Google Scholar] [CrossRef] [Green Version]
  47. Wei, X.B.; Wu, Z.M.; Xu, X.D.; Tang, J.J.; Li, W.Z.; Jiang, Y.D. Growth mode and texture study in vanadium dioxide thin films deposited by magnetron sputtering. J. Phys. D Appl. Phys. 2008, 41, 055303. [Google Scholar] [CrossRef]
  48. Brassard, D.; Fourmaux, S.; Jean-Jacques, M.; Kieffer, J.C.; El Khakani, M.A. Grain size effect on the semiconductor-metal phase transition characteristics of magnetron-sputtered VO2 thin films. Appl. Phys. Lett. 2005, 87, 051910. [Google Scholar] [CrossRef]
  49. Spaepen, F. Interfaces and stresses in thin films. Acta Mater. 2000, 48, 31–42. [Google Scholar] [CrossRef]
  50. Tsui, Y.C.; Clyne, T.W. An analytical model for predicting residual stresses in progressively deposited coatings Part 1, Planar geometry. Thin Solid Film. 1997, 306, 23–33. [Google Scholar] [CrossRef]
  51. Windischmann, H. Intrinsic stress in sputter-deposited thin films. Crit. Rev. Solid State Mater. Sci. 1992, 17, 547–596. [Google Scholar] [CrossRef]
Materials 16 05093 g001 550
Figure 1. (a) Raman spectra of the VO2 thin films with different deposition times. (b) The reflectance spectra of VO2 thin films with different deposition times.
Figure 1. (a) Raman spectra of the VO2 thin films with different deposition times. (b) The reflectance spectra of VO2 thin films with different deposition times.
Materials 16 05093 g001
Materials 16 05093 g002 550
Figure 2. (a) XRD patterns of the VO2 thin films with different deposition times. (b) Grain sizes and XRD FWHM of the VO2 peaks with different deposition times.
Figure 2. (a) XRD patterns of the VO2 thin films with different deposition times. (b) Grain sizes and XRD FWHM of the VO2 peaks with different deposition times.
Materials 16 05093 g002
Materials 16 05093 g003 550
Figure 3. The surface morphology of the VO2 thin films with various deposition times: (a) 2 h, (b) 2.5 h, (c) 3 h, and (d) 3.5 h.
Figure 3. The surface morphology of the VO2 thin films with various deposition times: (a) 2 h, (b) 2.5 h, (c) 3 h, and (d) 3.5 h.
Materials 16 05093 g003
Materials 16 05093 g004 550
Figure 4. The cross-section morphology of the VO2 thin films on ITO substrates with various deposition times: (a) 2 h, (b) 2.5 h, (c) 3 h, and (d) 3.5 h.
Figure 4. The cross-section morphology of the VO2 thin films on ITO substrates with various deposition times: (a) 2 h, (b) 2.5 h, (c) 3 h, and (d) 3.5 h.
Materials 16 05093 g004
Materials 16 05093 g005 550
Figure 5. AFM images of the VO2 thin films with various deposition times: (a) 2 h, (b) 2.5 h, (c) 3 h, and (d) 3.5 h.
Figure 5. AFM images of the VO2 thin films with various deposition times: (a) 2 h, (b) 2.5 h, (c) 3 h, and (d) 3.5 h.
Materials 16 05093 g005
Materials 16 05093 g006 550
Figure 6. The residual stress of VO2 thin films with different deposition times.
Figure 6. The residual stress of VO2 thin films with different deposition times.
Materials 16 05093 g006
Table
Table 1. The main fabrication parameters in the experiment.
Table 1. The main fabrication parameters in the experiment.
SamplesTemperature
(°C)		Time
(h)		Pulse Width (μs)Pulse Frequency
(Hz)		Pressure
(Pa)		Ar:O2 Ratio (sccm)Average
Power
(W)
S14002.0502000.980:1.4200
S24002.5502000.980:1.4200
S34003.0502000.980:1.4200
S44003.5502000.980:1.4200
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Wang, Y.; Li, X.; Yan, X.; Dou, S.; Li, Y.; Wang, L. Effects of Film Thickness on the Residual Stress of Vanadium Dioxide Thin Films Grown by Magnetron Sputtering. Materials 2023, 16, 5093. https://doi.org/10.3390/ma16145093

AMA Style

Wang Y, Li X, Yan X, Dou S, Li Y, Wang L. Effects of Film Thickness on the Residual Stress of Vanadium Dioxide Thin Films Grown by Magnetron Sputtering. Materials. 2023; 16(14):5093. https://doi.org/10.3390/ma16145093

Chicago/Turabian Style

Wang, Yuemin, Xingang Li, Xiangqiao Yan, Shuliang Dou, Yao Li, and Lei Wang. 2023. "Effects of Film Thickness on the Residual Stress of Vanadium Dioxide Thin Films Grown by Magnetron Sputtering" Materials 16, no. 14: 5093. https://doi.org/10.3390/ma16145093

APA Style

Wang, Y., Li, X., Yan, X., Dou, S., Li, Y., & Wang, L. (2023). Effects of Film Thickness on the Residual Stress of Vanadium Dioxide Thin Films Grown by Magnetron Sputtering. Materials, 16(14), 5093. https://doi.org/10.3390/ma16145093

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.