Low Core Losses of Fe-Based Soft Magnetic Composites with an Zn-O-Si Insulating Layer Obtained by Coupling Synergistic Photodecomposition
Abstract
1. Introduction
2. Experimental
2.1. Procedure
2.2. Characterization
3. Results and Discussion
4. Conclusions
Supplementary Materials
Author Contributions
Funding
Institutional Review Board Statement
Informed Consent Statement
Conflicts of Interest
References
- Schoppa, A.; Delarbre, P. Soft Magnetic Powder Composites and Potential Applications in Modern Electric Machines and Devices. IEEE Trans. Magn. 2014, 50, 1–4. [Google Scholar] [CrossRef]
- Wu, S.; Fan, J.L.; Liu, J.X.; Gao, H.X.; Zhang, D.H.; Sun, A.Z. Synthesis and Magnetic Properties of Soft Magnetic Composites Based on Silicone Resin-Coated Iron Powders. J. Supercond. Nov. Magn. 2018, 31, 587–595. [Google Scholar] [CrossRef]
- Azimi-Roeen, G.; Kashani-Bozorg, S.F.; Nosko, M.; Nagy, S.; Matko, I. Formation of Al/(Al13Fe4 + Al2O3) Nano-composites via Mechanical Alloying and Friction Stir Processing. J. Mater. Eng. Perform. 2018, 27, 471–482. [Google Scholar] [CrossRef]
- Protsenko, V.S.; Vasil’eva, E.A.; Smenova, I.V.; Baskevich, A.S.; Danilenko, I.A.; Konstantinova, T.E.; Danilov, F.I. Electrodeposition of Fe and Composite Fe/ZrO2 Coatings from a Methanesulfonate Bath. Surf. Eng. Appl. Electrochem. 2015, 51, 66–75. [Google Scholar] [CrossRef]
- Taghvaei, A.H.; Ebrahimi, A.; Gheisari, K.; Janghorban, K. Analysis of the magnetic losses in iron-based soft magnetic composites with MgO insulation produced by sol-gel method. J. Magn. Magn. Mater. 2010, 322, 3748–3754. [Google Scholar] [CrossRef]
- Li, J.X.; Yu, J.; Li, W.C.; Che, S.L.; Zheng, J.W.; Qiao, L.; Ying, Y. The preparation and magnetic performance of the iron-based soft magnetic composites with the Fe@Fe3O4 powder of in situ surface oxidation. J. Magn. Magn. Mater. 2018, 454, 103–109. [Google Scholar] [CrossRef]
- Nie, W.; Yu, T.; Wang, Z.G.; Wei, X.W. High-performance core-shell-type FeSiCr@MnZn soft magnetic composites for high-frequency applications. J. Alloys Compd. 2021, 864, 158215. [Google Scholar] [CrossRef]
- Guo, R.D.; Wang, S.M.; Yu, Z.; Sun, K.; Jiang, X.N.; Wu, G.H.; Wu, C.J.; Lan, Z.W. FeSiCr@NiZn SMCs with ultra-low core losses, high resistivity for high frequency applications. J. Alloys Compd. 2020, 830, 154736. [Google Scholar] [CrossRef]
- Zheng, J.W.; Zheng, H.D.; Lei, J.; Qiao, L.; Ying, Y.; Cai, W.; Li, W.C.; Yu, J.; Liu, Y.H.; Huang, X.L.; et al. Structure and magnetic properties of Fe-based soft magnetic composites with an Li-Al-O insulation layer obtained by hydrothermal synthesis. J. Alloys Compd. 2020, 816, 152617. [Google Scholar] [CrossRef]
- Chen, J.C.; Guo, H.S.; Zhong, X.X.; Fu, J.Y.; Huang, S.J.; Xie, X.H.; Li, L.Z. Microstructural and magnetic properties of core-shell FeSiAl composites with Ni0.4Zn0.45Co0.15Fe2O4 layer by sol-gel method. J. Magn. Magn. Mater. 2021, 529, 167774. [Google Scholar] [CrossRef]
- Luo, Z.; Fan, X.; Feng, B.; Yang, Z.; Chen, D.; Jiang, S.; Wang, J.; Wu, Z.; Liu, X.; Li, G.; et al. Highly enhancing electromagnetic properties in Fe-Si/MnO-SiO2 soft magnetic composites by improving coating uniformity. Adv. Powder Technol. 2021, 32, 4846–4856. [Google Scholar] [CrossRef]
- Shi, X.Y.; Chen, X.Y.; Wan, K.; Zhang, B.W.; Duan, P.T.; Zhang, H.; Zeng, X.D.; Liu, W.; Su, H.L.; Zou, Z.Q.; et al. Enhanced magnetic and mechanical properties of gas atomized Fe-Si-Al soft magnetic composites through adhesive insulation. J. Magn. Magn. Mater. 2021, 534, 168040. [Google Scholar] [CrossRef]
- Chan, L.W.; Liu, X.H.; Heng, P.W.S. Liquid phase coating to produce controlled-release alginate microspheres. J. Microencapsul. 2005, 22, 891–900. [Google Scholar] [CrossRef]
- Lei, J.; Zheng, J.W.; Zheng, H.D.; Qiao, L.; Ying, Y.; Cai, W.; Li, W.C.; Yu, J.; Lin, M.; Che, S.L. Effects of heat treatment and lubricant on magnetic properties of iron-based soft magnetic composites with Al2O3 insulating layer by one-pot synthesis method. J. Magn. Magn. Mater. 2019, 472, 7–13. [Google Scholar] [CrossRef]
- Zhou, M.; Peng, X.L. Fundamentals of Magnetics and Magnetic Materials; Zhejiang University Press: Hangzhou, China, 2019; pp. 175–176. [Google Scholar]
- Li, W.C.; Li, W.; Ying, Y.; Yu, J.; Zheng, J.W.; Qiao, L.; Li, J.; Zhang, L.; Fan, L.; Wakiya, N.; et al. Magnetic and Mechanical Properties of Iron-Based Soft Magnetic Composites Coated with Silane Synergized by Bi2O3. J. Electron. Mater. 2021, 50, 2425–2435. [Google Scholar] [CrossRef]
- Shi, W.X.; Yang, J.; Wang, T.J.; Jin, Y. Surface organic modification of magnetic iron oxide black particles. Acta Phys.-Chim. Sin. 2001, 17, 507–510. [Google Scholar] [CrossRef]
- Berbotti, G. General properties of power losses in Soft ferromagnetic Materials. IEEE Trans. Magn. 1988, 24, 621. [Google Scholar] [CrossRef]
- Zheng, J.W.; Zheng, D.N.; Qiao, L.; Ying, Y.; Tang, Y.P.; Cai, W.; Li, W.C.; Yu, J.; Li, J.; Che, S.L. High permeability and low core loss Fe-based soft magnetic composites with Co-Ba composite ferrite insulation layer obtained by sol-gel method. J. Alloys Compd. 2022, 893, 162107. [Google Scholar] [CrossRef]
- Li, W.C.; Wang, Z.J.; Ying, Y.; Yu, J.; Zheng, J.W.; Qiao, L.; Che, S.L. In-situ formation of Fe3O4 and ZrO2 coated Fe-based soft magnetic composites by hydrothermal method. Ceram. Int. 2019, 45, 3864–3870. [Google Scholar] [CrossRef]
- Li, W.C.; Pu, Y.Y.; Ying, Y.; Kang, Y.; Yu, J.; Zheng, J.W.; Qiao, L.; Li, J.; Che, S.L. Magnetic properties and related mechanisms of iron-based soft magnetic composites with high thermal stability in situ composite-ferrite coating. J. Alloys Compd. 2020, 829, 154533. [Google Scholar] [CrossRef]
- Guziewicz, E.; Godlewski, M.; Wachnicki, L.; Krajewski, T.A.; Luka, G.; Gieraltowska, S.; Jakiela, R.; Stonert, A.; Lisowski, W.; Krawczyk, M.; et al. ALD grown zinc oxide with controllable electrical properties. Semicond. Sci. Technol. 2012, 27, 074011. [Google Scholar] [CrossRef]
Element (at%) | Zn(C2H5)2 | Zn(C2H5)2 + C6H14 | KH550 | KH550 and (Zn(C2H5)2 + C6H14) |
---|---|---|---|---|
Fe | 88.27 | 98.26 | 99.65 | 97.57 |
Zn | 11.73 | 1.74 | 0 | 2.17 |
Si | 0 | 0 | 0.35 | 0.26 |
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations. |
© 2022 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/).
Share and Cite
Wang, S.; Zheng, J.; Zheng, D.; Qiao, L.; Ying, Y.; Tang, Y.; Cai, W.; Li, W.; Yu, J.; Li, J.; et al. Low Core Losses of Fe-Based Soft Magnetic Composites with an Zn-O-Si Insulating Layer Obtained by Coupling Synergistic Photodecomposition. Materials 2022, 15, 8660. https://doi.org/10.3390/ma15238660
Wang S, Zheng J, Zheng D, Qiao L, Ying Y, Tang Y, Cai W, Li W, Yu J, Li J, et al. Low Core Losses of Fe-Based Soft Magnetic Composites with an Zn-O-Si Insulating Layer Obtained by Coupling Synergistic Photodecomposition. Materials. 2022; 15(23):8660. https://doi.org/10.3390/ma15238660
Chicago/Turabian StyleWang, Siyuan, Jingwu Zheng, Danni Zheng, Liang Qiao, Yao Ying, Yiping Tang, Wei Cai, Wangchang Li, Jing Yu, Juan Li, and et al. 2022. "Low Core Losses of Fe-Based Soft Magnetic Composites with an Zn-O-Si Insulating Layer Obtained by Coupling Synergistic Photodecomposition" Materials 15, no. 23: 8660. https://doi.org/10.3390/ma15238660
APA StyleWang, S., Zheng, J., Zheng, D., Qiao, L., Ying, Y., Tang, Y., Cai, W., Li, W., Yu, J., Li, J., & Che, S. (2022). Low Core Losses of Fe-Based Soft Magnetic Composites with an Zn-O-Si Insulating Layer Obtained by Coupling Synergistic Photodecomposition. Materials, 15(23), 8660. https://doi.org/10.3390/ma15238660