Next Article in Journal
The Effect of Steel and Polypropylene Fibers on the Properties of Horizontally Formed Concrete
Next Article in Special Issue
Effective Doping of Single-Walled Carbon Nanotubes with Polyethyleneimine
Previous Article in Journal
Effects of the Processing Parameters of Friction Stir Processing on the Microstructure, Hardness and Tribological Properties of SnSbCu Bearing Alloy
Previous Article in Special Issue
Carbon Nanotubes Dispersion Assessment in Nanocomposites by Means of a Pulsed Thermographic Approach
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 13
Issue 24
10.3390/ma13245838
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Rapid Preparation of MWCNTs/Epoxy Resin Nanocomposites by Photoinduced Frontal Polymerization

by
Guofeng Hu
1,
Wanli Fu
1,2,
Yumin Ma
1,
Jianping Zhou
1,3,*,
Hongbo Liang
1,3,
Xinmei Kang
4 and
Xiaolin Qi
4
1
School of Material Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China
2
State-Owned Assets Management Division, Nanchang Hangkong University, Nanchang 330063, China
3
Jiangxi Provincial Engineering Research Center for Surface Technology of Aeronautical Materials, Nanchang Hangkong University, Nanchang 330063, China
4
Aviation Key Laboratory of Science and Technology on Life-Support Technology, Xiangyang 441000, China
*
Author to whom correspondence should be addressed.
Materials 2020, 13(24), 5838; https://doi.org/10.3390/ma13245838
Submission received: 25 October 2020 / Revised: 8 December 2020 / Accepted: 15 December 2020 / Published: 21 December 2020
(This article belongs to the Special Issue Carbon Nanotube Based Composites: Processing, Properties, Modeling and Application)
Browse Figures
Versions Notes

Abstract

:
Due to their excellent mechanical and thermal properties and medium resistance, epoxy/carbon nanotubes and nanocomposites have been widely used in many fields. However, the conventional thermosetting process is not only time- and energy-consuming, but also causes the agglomeration of nanofillers, which leads to unsatisfactory properties of the obtained composites. In this study, multi-walled carbon nanotubes (MWCNTs)/epoxy nanocomposites were prepared using UV photoinduced frontal polymerization (PIFP) in a rapid fashion. The addition of MWCNTs modified by a surface carboxylation reaction was found to enhance the impact strength and heat resistance of the epoxy matrix effectively. The experimental results indicate that with 0.4 wt % loading of modified MWCNTs, increases of 462.23% in the impact strength and 57.3 °C in the glass transition temperature Tg were achieved. A high-performance nanocomposite was prepared in only a few minutes using the PIFP approach. Considering its fast, energy-saving, and environmentally friendly production, the PIFP approach displays considerable potential in the field of the fast preparation, repair, and deep curing of nanocomposites and coatings.

Graphical Abstract

1. Introduction

Owing to their great aspect ratio, excellent mechanical properties, electrical conductivity, and chemical/thermal stability, carbon nanotubes (CNTs) have been extensively studied by researchers in the field of materials science [1,2,3,4,5]. However, due to their extremely high surface energy, CNTs are difficult to evenly disperse during the preparation of CNT-doped composite materials, which has greatly limited their wide application in the field of composites [6]. Therefore, the surface modification of CNTs is particularly necessary in the preparation of CNT-doped composites [7,8,9,10]. Currently, two modifying methods have been developed to improve the dispersion of CNTs: noncovalent and covalent modification. The former mainly includes ball milling, mechanical stirring, and ultrasonication [11,12,13]; the latter mainly involves the introduction of reactive groups, such as carboxyl, hydroxyl, and amino groups, onto the surface of CNTs by oxidizing and etching under the action of H2SO4 and HNO3 or other strong oxidants [14,15].
Epoxy resin (EP) is one of the most widely used thermosetting resins due to its excellent mechanical and bonding properties, chemical resistance, and processing simplicity [16,17,18,19]. However, its cured products usually have a high crosslinking density, making them vulnerable to external force impacts. To overcome the relatively poor impact resistance and environmental stress-cracking resistance of epoxy condensates, the addition of inorganic nanoparticles, glass fibers, graphene, and CNTs to epoxy resin has been extensively explored [20,21,22,23,24,25]. Particularly, using modified CNTs as fillers to prepare CNTs/epoxy nanocomposites has been reported [26,27]. For example, Akram et al. constructed epoxy nanocomposites with polyacrylonitrile/multi-walled CNTs and a polyacrylonitrile/carbon nanofiber aerogels scaffold [28].
Frontal polymerization (FP) is a new type of polymerization that can transform monomers into polymers quickly through an exothermic reaction [29,30]. Compared to the traditional polymerization reaction, FP exhibits various advantages: it has a high reaction rate and a short reaction time; it consumes a low amount of energy; and it is environmentally friendly [31]. Frontal polymerization is classified into thermal frontal polymerization (TFP), photo frontal polymerization (PFP), and isothermal frontal polymerization (IFP) [32,33]. There are now many studies on TFP and PFP [30,34,35,36,37,38]. For instance, Sangermano et al. successfully prepared a glass-fiber-reinforced epoxy resin composite through the PFP approach. Zhu et al. successfully cured tripropylene glycol diacrylate (TPGDA) through a UV-triggered frontal polymerization [39].
In this study, nanocomposites of epoxy and multi-walled carbon nanotubes (MWCNTs) were rapidly prepared via photoinduced frontal polymerization. The MWCNTs were first subjected to surface medication through a carboxylation reaction. The influence of adding the modified MWNCTs to the frontal polymerization process and the properties of the obtained nanocomposites were then further investigated in detail.

2. Materials and Methods

2.1. Materials

The epoxy resin used in this study was 3,4-epoxycyclo-hexyl formate 3′,4′-epoxycyclohexyl methyl ester (EP-211), purchased from Tianjin Synthetic Material Research Institute Co., Ltd., Tianjin, China. The carbon nanotubes used were multi-walled carbon nanotubes (diameter < 8 nm, purity > 98%), purchased from Chengdu Organic Chemicals Co., Ltd., Chinese Academy of Science, Chengdu, China. P-aminobenzoic acid (PABA, C7H7NO2) (McLean Biochemistry Co., Ltd., Shanghai, China) was used to modify the surface of the MWCNTs. Isopentyl nitrite (C5H11NO2, McLean Biochemistry Co., Ltd., Shanghai, China) was used as the catalyst for the carboxylation modification reaction. The boron trifluoride-amine complex (Beijing Huineng Rubber Chemical Co., Ltd., Beijing, China) was used as the thermal initiator (TI), and a mixture of hexafluoroantimonate sulfonium onium salts (Changzhou Qiangli Electronic Materials Co., Ltd., Changzhou, China) was used as the photoinitiator (PI). N,N-dimethylformamide (DMF) was purchased from Xilong Science Co., Ltd., Shantou, China. All materials were used as received without further purification.

2.2. Surface Carboxylation Modification of MWCNTs

To enhance the compatibility of the MWCNTs with the epoxy matrix, a carboxylation reaction was conducted. Firstly, MWCNTs were dispersed in distilled water at room temperature for 1 h using an ultrasonic disperser. Then, a certain proportion of isopentyl nitrite and various amounts of PABA ((MWCNTs)/(PABA) = 1:1, 1:5, 1:10, 1:15 wt/wt) were added to the flask, which was equipped with a condenser and a drying tube. The mixture was stirred at 80 °C for 18 h. Afterward, the resulting substances were washed with DMF five times and collected by filtration. Carboxylic-functionalized MWCNTs (MWCNTs-COOH) were finally obtained by drying in a vacuum oven at 50 °C for 24 h.

2.3. Preparation of MWCNTs/Epoxy Resin Nanocomposites Via UV-Light-Induced FP

The scheme of the experimental device is shown in Figure S1 in the Supplementary Materials. An optical-cable-directed UV-point light source (Shenzhen Blue Spectrum Rich Ltd., Shenzhen, China) was used to trigger the frontal polymerization, with its optical cable placed over the left end of a glass tank measuring 15 cm × 1.5 cm × 1.7 cm. Additionally, a K-type thermocouple connected to a digital recorder was used to monitor the temperature profile of the polymerization reaction.
The procedure was similar to that presented in [34], with slight modifications. During each experiment, the glass tank was first preheated in an oven set at 55 °C. Various amounts of modified MWCNTs (0.2–1 wt %), PI, and epoxy resin were added to a 50 mL round-bottom flask and mixed with a sonicator for 10 min. The flask was then transferred to a constant-temperature oil bath. The mixture in the flask was stirred at 55 °C with a magnetic stirrer, and a vacuum pump was used to degas the mixture until bubbles were no longer observed in the flask. Afterwards, a 2 wt % TI was added to the flask, and the mixture was continuously stirred for another 10 min. Finally, the mixture was quickly poured into the preheated glass tank, and the UV point source was immediately powered on at a setting of 10 W/cm2 to start the frontal polymerization process. Once the polymerization front formed (usually in dozens of seconds), the UV light was turned off, and the front continued to propagate horizontally to the right until all the monomers were transformed into cured products, and the MWCNTs/epoxy nanocomposites were obtained. During the reaction process, a THTZ408R-type infrared thermal imager (Tenghui Temperature Control Instrument Factor Ltd., Ningbo, China) was used to record the temperature profile and the moving feature of the polymerization front as a function of time.

2.4. Characterization and Measurements

The chemical structure of the modified MWCNTs and the nanocomposite products was characterized using a VERTEX70-type Fourier transform infrared spectroscopy (FT-IR, BRUKER Co., Ltd., Woodlands, Germany) and a Kratos AXIS X-ray photoelectron spectroscopy (XPS, KRATOS Co., Ltd., Kyoto, Japan). FT-IR measurements were carried out under ATR (Attenuated Total Reflection) mode with a 700–4000 cm−1 scanning range, accumulating 16 scans for each spectrum at 25 °C. X-ray photoelectron spectroscopy (XPS) measurements were carried out on an Escalab 250 Xi spectrometer (Thermo Scientific, Waltham, MA, USA). A monochromatic Al-Kα radiation source (1486.74 eV) and a PHOIBOS 150 hemispherical electron analyzer (SPECS, Berlin, Germany) were used with the spectrometer. An X-ray power of 25 W, a take-off angle of 45°, and a pass energy of 20 eV were used to capture 10 scans for each sample.
The viscosity measurement was performed at 25 °C in a Rotary viscometer (NDJ-79, Shanghai Changji Geological Instrument Co., Ltd., Shanghai, China) with a diameter die of 0.5 mm.
The fracture surfaces of the nanocomposite specimens after impact test were observed using an FEI Quanta250 scanning electron microscopy (SEM, FEI Co., Ltd., Brno, Czech) with an operating voltage of 15 kV. To increase the conductivity, the sample was sprayed with gold.
Thermogravimetric analysis (TGA) was performed on a Diamond TG/DTA (Perkin Elmer, Waltham, MA, USA) thermogravimetric analysis analyzer with a temperature range of 20–800 °C. The heating rate was 10 °C /min and the flow rate of nitrogen was 20 mL/min. The difference between the residual mass after degradation of modified carbon nanotubes and that of original carbon nanotubes was regarded as the grafting amount of PABA.
Dynamic thermal mechanical (DMA) tests were performed using a TA Q800 dynamic mechanical thermal analyzer (TA Instruments, New Castle, DE, USA) with a temperature range of 25–250 °C and a frequency of 1 Hz. The heating rate was 5 K/min and the flow rate of nitrogen was 30 mL/min. The dimension of the samples used for the testing was 35 mm × 12 mm × 3.5 mm.
The impact properties of the nanocomposite specimens were measured using an RG-30 impact testing machine (Zhonghang Times Instrument Equipment Co., Ltd., Beijing, China) in accordance with ASTM D256-10. Each sample was tested three times, and the results were averaged.

3. Results

3.1. Structural Characterization

To enhance the dispersion and compatibility of MWCNTs in epoxy oligomers and cured products, the functionalization of MWCNTs was carried out by grafting carboxyl groups onto their surfaces. Functionalization of the initial sidewall of MWCNTs proceeded via the reaction between P-aminobenzoic acid (PABA) and the carbon nanotube surface in the presence of an oxidizing agent. As shown in Scheme 1, isoamyl nitrite first reacts with PABA to form diazonium salt of PABA. Diazonium benzoate is very unstable, and easily decomposes at a slightly higher temperature and produces a cation in its para position. The cation reacts with the double bond on the surface of the MWCNTs to graft benzoic acid group onto their surfaces.
The chemical structure of MWCNTs after being modified by PABA via carboxylation reaction was characterized by FT-IR and XPS measurements.
Figure 1 shows the FT-IR spectra of MWCNTs before and after the surface modification. Two new peaks appeared in the PABA-modified MWCNTs curve: the peak at 1700 cm−1 corresponded to carbonyl groups (C=O), and the peak at 1400 cm−1 corresponded to carboxyl groups (–COO) [25]. The presence of these two peaks indicated that PABA had been grafted successfully onto the surface of the MWCNTs.
XPS analysis is an efficient method to evaluate the chemical bonds grafted onto CNTs [40]. Figure 2 and Figure 3 show the XPS spectra of prime and PABA-modified MWCNTs. The inset graph in Figure 2 shows the deconvolution of the C1s spectrum of prime MWCNTs, in which the main peak at 284.6 ± 0.2 eV was assigned to the graphitic C–C bond and the 284.1 ± 0.2 eV was assigned to the C=C bond. In contrast, the C1s spectrum of the modified MWCNTs shown in the inset of Figure 3 demonstrates the existence of an –O–C=O bond (corresponding to the peak at 288.8 ± 0.2 eV) and a C–O bond (corresponding to the peak at 286.5 ± 0.2 eV), which also indicated the successful grafting of PABA onto the surface of MWCNTs.
Figure 4 shows the TGA curves of prime and modified MWCNTs. The PABA-modified MWCNTs underwent a three-step degradation. The first degradation occurred below 200 °C, which could mainly be due to the evaporation of adsorbed and bounded water. The second degradation occurred in the temperature range of 200–260 °C, which could be attributed to the degradation of PABA, which was suggested by the degradation curve of pure PABA (as shown in Figure S2). The third degradation step, in the temperature range of 260–800 °C, was mainly due to the thermal decomposition of the C–C bonds of MWCNTs. Using the thermogram of the PABA-modified MWCNTs, the optimum ratio of MWCNTs/PABA that could be used in the modification reaction was determined to be 1:5, as the residual mass of the modified MWCNTs was the minimum in this case. The corresponding surface grafting rate of PABA was calculated to be 10.6%. Furthermore, the grafting rate was found to decrease when the ratio of MWCNTs/PABA exceeded 1:5, implying that an excess of PABA input is not favorable for the surface carboxylation reaction between MWCNTs and PABA molecules.

3.2. Preparation of PABA-Modified MWCNTs/Epoxy Resin Nanocomposites Via Photoinduced Frontal Polymerization

To prepare the MWCNTs/epoxy nanocomposite using the PIFP method, 221-type alicyclic epoxy resin with a high heat-release ability was used as the resin matrix, mixed triarylhexafluoroantimonium salt was used as cationic photoinitiator, and boron trifluoride-amine complex was used as the TI. During the process, two types of reaction occurred successively. First a photolysis reaction occurred, during which an active strong acid was generated through the decomposition of photoinitiators under UV irradiation, and the epoxy groups in surface resin began a cationic ring-opening polymerization under the action of the strong acid. Second, a thermal curing of the epoxy resin occurred, during which the thermal initiator (boron trifluoride amine complex) decomposed rapidly due to the heat released in the first stage. The epoxy oligomers reacted with the BF3-amine to form an oxonium cation, and the ring-opening polymerization occurred in a chain mode according to the cationic reaction process, until the whole resin cured completely. The mechanism is shown in Scheme 2.
Front velocity (Vf) and maximum temperature (Tmax) are two key parameters to be considered during a frontal polymerization reaction [41,42,43]. Suitable values of Vf and Tmax must be achieved in order to realize a stable FP reaction.
Figure 5 plots the front position as a function of time during the preparation of MWCNTs/epoxy nanocomposites via photoinduced FP. The experimental data in all four sets conformed to well-fitted straight lines on the graph, indicating that the polymerization front propagated at a constant velocity, which is a typical feature of FP [34]. Table 1 lists the corresponding Vf values calculated according to the line slope. The data suggest a decreasing trend of Vf with the increase in the content of the fillers. One main reason could be the increase in viscosity of the mixture solution (as shown in Table 2). The higher the filler content, the greater the viscosity of the mixture system [44]. High viscosity hinders thermal diffusion, thus reducing the frontal velocity Vf. The effect of conductive particles should also be considered [45,46]. When CNTs were added to the polymer, nanoparticles absorbed some amount of the released heat from the material (due to specific heat) and reduced the energy density, since less resin is available per unit volume. However, at the same time, the thermally conductive nanoparticles conducted the heat away from the front preheated the resin and accelerated the front reaction. These two phenomena had opposite effects on the frontal reaction. Since the front velocity of neat resin (0.81 cm/min) is much lower than that with MWCNTs added, it is thought that the addition of a small amount of conductive fillers is favorable in the frontal polymerization reaction. Additionally, the data in Table 1 show that the Vf of the PABA-modified MWCNTs/epoxy resin system was greater than that of the unmodified MWCNTs/epoxy resin system, although the viscosity of the unmodified MWCNTs/epoxy system was lower than that of modified MWCNTs/epoxy system. Except for the enhanced dispersibility and compatibility, the incorporation of carboxyl groups onto the surfaces of MWCNTs may play a crucial role in the frontal polymerization reaction, due to the change in exothermicity during the curing process caused by the reaction between the carboxyl groups and epoxy oligomers.
Figure 6 shows the temporal distribution of temperature of the photoinduced FP of PABA-modified MWCNTs/epoxy resin system, and Table 3 shows the maximum temperature determined from the corresponding profile. The data show that the Tmax value decreased with the increase in the content of the modified MWCNTs, which agrees well with the trend in frontal velocity, confirming a rule that a higher frontal reaction temperature Tmax is needed to maintain the fast front reaction rate Vf. Additionally, Figure S3 shows the Tmax of the system with PABA-modified MWCNTs added is higher than that of the system with unmodified MWCNTs added, and the time needed to reach the highest reaction temperature Tmax for the former is less than that needed for the latter, suggesting that the active groups on the surface of the modified MWCNTs participate in the FP reaction and help release more heat during the curing process. Therefore, we concluded the epoxy oligomers with modified MWCNTs added are better for heat conduction due to their enhanced dispersity and compatibility.
A phenomenon known as propagating angle, which increases with the increase in addition of fillers, was previously discovered in frontal polymerization reactions [34]. In our study, such a feature was also observed. In our parallel experiments, a propagating angle of 16°, 21.35°, 26.01°, 37.79°, and 54.60° was clearly observed when the content of modified MWCNTs was 0, 0.2, 0.4, 0.6, and 0.8 wt %, respectively (Figure 7). The increase in the propagating angle and an increase in the filler loading was ascribed to the augment of the viscosity of the reaction system, which greatly inhibited the occurrence of thermal convection and reduced the Vf value. A slow propagating velocity usually accompanied a large propagating angle, resulting in uniform material properties.

3.3. Properties of Modified MWCNTs/Epoxy Resin Nanocomposite Prepared by Photoinduced Frontal Polymerization

Figure 8 shows the TGA curves of pure epoxy resin and its nanocomposites filled with various amounts of PABA-modified MWCNTs. The weight-loss rate of epoxy nanocomposites decreased as the content of modified MWCNTs increased. The condensate of pure epoxy resin substantially decomposed at ~520 °C, while the residual mass of the epoxy nanocomposites continued to increase when the loading of the modified MWCNTs increased. The residual mass of the three composites was 7.5%, 10.8%, and 12%, respectively, suggesting that the addition of modified MWCNTs enhanced the retention of the epoxy resin. Since MWCNTs resist heat and conduct temperatures well, the modified MWCNTs dispersed in the epoxy matrix absorbed and transferred energy to the external environment quickly once heated, resulting in better heat resistance in the corresponding nanocomposites.
Figure 9 shows the tanδ–T curves that were recorded in the DMA testing of the epoxy nanocomposites, and Figure 10 plots the corresponding glass transition temperature determined from the tanδ ~ T curves. The Tg value increased at first, but then decreased along with the increase in the MWCNTs content. The Tg of pure epoxy resin was 88.8 °C, but the Tg of the nanocomposites reached a maximum value of 146.1 °C when the content of modified MWCNTs reached 0.4 wt %. Even when the filler loading reached 0.8 wt %, the related Tg (105.1 °C) was still higher than for pure epoxy resin. These results indicate that the addition of modified MWCNTs can effectively enhance the heat resistance of the epoxy matrix, due to the strengthened interface between the matrix and the filler after the surface-carboxylation modification reaction.
The impact properties of the epoxy nanocomposites with various amount of PABA-modified MWCNTs added were tested (Figure 11). In comparison, the impact properties of the composites with various amounts of unmodified MWCNTs addition are also presented. The impact strength of the composites increased at first, and then decreased along with the increase in the loading of MWCNTs. When the content of the modified MWCNTs was 0.4 wt %, the impact strength jumped to its highest value (28.39 MPa), an increase of 462.23% compared to that of the pure epoxy resin (3.76 MPa), and 34.23% higher than that of the composite with 0.4 wt % unmodified MWCNTs added (21.14 MPa). The results showed that PABA-modified MWCNTs can effectively enhance the impact property of the epoxy composite better than unmodified MWCNTs. However, when the content of MWCNTs exceeded 0.4 wt %, the impact strength value of the composites began to decrease. This could be ascribed to the increase in the viscosity of the mixture, which reduced the dispersibility of the fillers [41].
Figure 12 shows an SEM photograph of the impact fracture of the epoxy nanocomposites with the content of various modified MWCNTs loaded. Smooth and flat features were observed in the sample of pure epoxy resin condensate, indicating a typical brittle fracture (Figure 12a). With modified MWCNTs added, the fracture of the nanocomposite samples became rougher, and displayed numerous scaly structures. This ductile characteristic resulted from the good compatibility, uniform dispersion, and enhanced interface bonding strength between the matrix and the fillers. When external force was applied, the carbon nanotubes developed a large number of microcracks. The network structure formed by the carbon nanotubes in the matrix resin effectively hindered crack propagation and absorbed the impact energy, thus enhancing the impact strength of the composite material. However, the agglomeration of fillers tended to occur when adding too many MWCNTs, leading to a drop in impact strength.

4. Conclusions

In this study, MWCNTs/epoxy resin nanocomposites were rapidly prepared using UV photoinduced frontal polymerization. After modification by PABA via carboxylation reaction, MWCNTs exhibited enhanced dispersibility and compatibility with the epoxy matrix. The addition of 0.4 wt % modified MWCNTs to epoxy oligomers greatly enhanced the toughness and heat resistance of the obtained nanocomposites, which demonstrated an increase of 462.23% in impact strength and an increase of 57.3 °C in the glass transition temperature Tg compared to pure epoxy resin condensate. The findings indicate that PIFP is a facile, rapid, and efficient approach for preparation of high-performance thermosetting nanocomposites, and it exhibits potential in the fields of fast repairing and deep curing.

Supplementary Materials

The following are available online at https://www.mdpi.com/1996-1944/13/24/5838/s1, Figure S1: Scheme of the device used for photoinduced frontal polymerization; Figure S2: TGA curves of pure epoxy resin; Figure S3: The temporal distribution of temperature of the unmodified MWCNTs/epoxy and PABA-modified MWCNTs/epoxy reaction system with different filler loading.

Author Contributions

Conceptualization, J.Z., X.K.; methodology, W.F., J.Z., H.L. and X.Q.; formal analysis, G.H., W.F., J.Z. and H.L.; investigation, G.H. and Y.M.; writing—original draft preparation, G.H. and W.F.; writing—review and editing, J.Z. and H.L.; supervision, J.Z., X.Q.; project administration, X.K.; funding acquisition, X.Q. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Aeronautical Science Foundation of China, grant number 20162956005.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Harik, V. Mechanics of the high aspect ratio carbon nanotubes. In Mechanics of Carbon Nanotubes; Academic Press: Cambridge, MA, USA, 2018; pp. 107–134. [Google Scholar]
  2. Yazdi, M.; Asl, V.H.; Pourmohammadi, M.; Roghanimamaqani, H. Mechanical properties, crystallinity, and self-nucleation of carbon nanotube-polyurethane nanocomposites. Polym. Test. 2019, 79, 106011. [Google Scholar] [CrossRef]
  3. Haghgoo, M.; Ansari, R.; Hassanzadeh-Aghdam, M.K. Prediction of electrical conductivity of carbon fiber-carbon nanotube-reinforced polymer hybrid composites. Compos. Part B Eng. 2019, 167, 728–735. [Google Scholar] [CrossRef]
  4. Zhilyaeva, M.A.; Shulga, E.V.; Shandakov, S.D.; Sergeichev, I.V.; Nasibulin, A.G. A novel straightforward wet pulling technique to fabricate carbon nanotube fibers. Carbon 2019, 15, 69–75. [Google Scholar] [CrossRef]
  5. Jintoku, H.; Matsuzawa, Y.; Yoshida, M. Dual use of anionic azobenzene derivative as dispersant and dopant for carbon nanotubes for enhanced thermal stability of transparent conductive films. Carbon 2019, 152, 247–254. [Google Scholar] [CrossRef]
  6. Pan, J.; Bian, L. A physics investigation for influence of carbon nanotube agglomeration on thermal properties of composites. Mater. Chem. Phys. 2019, 236, 121777–121786. [Google Scholar] [CrossRef]
  7. Marta, S.; Yu, L.; Zhao, L.; Ania, C.O.; Titiricic, M.M. Surface Modification of CNTs with N-Doped Carbon: An Effective Way of Enhancing Their Performance in Supercapacitors. ACS Sustain. Chem. Eng. 2014, 2, 1049–1055. [Google Scholar]
  8. Miao, J.; Dong, X.; Xu, Y.; Zhai, Z.; Zhang, L.; Ren, B.; Liu, Z. Preparation and electrochemical performance of 1,4-naphthaquinone-modified carbon nanotubes as a supercapacitor material. Org. Electron. 2019, 73, 304–310. [Google Scholar] [CrossRef]
  9. Huang, H.; Liu, M.; Jiang, R.; Chen, J.; Wei, Y. Fabrication and characterization of hyperbranched polyglycerol modified carbon nanotubes through the host-guest interactions. Mater. Sci. Eng. C 2018, 91, 458–465. [Google Scholar] [CrossRef]
  10. Lee, M.; Kwon, W.; Kwon, D.; Lee, E.; Jeong, E. Fracture toughness of the novel in-situ polytriazolesulfone modified epoxy resin for carbon fiber/epoxy composites. J. Ind. Eng. Chem. 2019, 77, 461–469. [Google Scholar] [CrossRef]
  11. Alshamma, F.A.; Jassim, O.A. An efficient way to produce nanocomposites of pure copper reinforced by carbon nano tubes carboxylic. J. Mater. Res. Technol. 2019, 8, 3795–3799. [Google Scholar] [CrossRef]
  12. Gumaste, J.L.; Singh, S.K.; Mukherjee, P.S.; Sahay, S.S.; Mishra, B.K. An efficient and inexpensive method for the production of multi-wall carbon nano tubes by the thermal plasma route. Trans. Indian Inst. Met. 2009, 62, 229–231. [Google Scholar] [CrossRef]
  13. Liu, Y.T.; Yao, T.T.; Zhang, W.S.; Wu, G.P. Laser welding of carbon nanotube networks on carbon fibers from ultrasonic-directed assembly. Mater. Lett. 2019, 236, 244–247. [Google Scholar] [CrossRef]
  14. Thi Mai Hoa, L. Characterization of multi-walled carbon nanotubes functionalized by a mixture of HNO3/H2SO4. Diam. Relat. Mater. 2018, 89, 43–51. [Google Scholar] [CrossRef]
  15. Shih, M.-W.; Chin, C.-J.M.; Yu, Y.-L. The role of oxygen-containing groups on the adsorption of bisphenol-A on multi-walled carbon nanotube modified by HNO3 and KOH. Process. Saf. Environ. Prot. 2017, 112, 308–314. [Google Scholar] [CrossRef]
  16. Zhang, P.; Kan, L.; Zhang, X.Y.; Li, R.; Qiu, C.Q.; Ma, N.; Wei, H. Super molecularly toughened and elastic epoxy resins by grafting 2-ureido-4[1H]-pyrimidone moieties on the side chain. Eur. Polym. J. 2019, 116, 126–133. [Google Scholar] [CrossRef]
  17. Chen, K.; Zhao, X.; Zhang, F.; Wu, X.; Wang, X. Influence of gamma irradiation on the molecular dynamics and mechanical properties of epoxy resin. Polym. Degrad. Stab. 2019, 168, 108940–108947. [Google Scholar] [CrossRef]
  18. Rad, E.R.; Vahabi, H.; Anda, A.R.; Saeb, M.R.; Thomas, S. Bio-epoxy resins with inherent flame retardancy. Prog. Org. Coat. 2019, 135, 608–612. [Google Scholar] [CrossRef]
  19. Gibson, G. Epoxy resins. In Brydson’s Plastics Materials; Butterworth–Heinemann: Oxford, UK, 2017; pp. 773–797. [Google Scholar]
  20. Turk, M.; Hamerton, I.; Ivanov, D.S. Ductility potential of brittle epoxies: Thermomechanical behaviour of plastically-deformed fully-cured composite resins. Polymer 2017, 120, 43–51. [Google Scholar] [CrossRef]
  21. Jin, S.; Qian, L.; Qiu, Y.; Chen, Y.; Xin, F. High-efficiency flame retardant behavior of bi-DOPO compound with hydroxyl group on epoxy resin. Polym. Degrad. Stab. 2019, 166, 344–352. [Google Scholar] [CrossRef]
  22. Wilkinson, A.N.; Kinloch, I.A.; Othman, R.N. Low viscosity processing using hybrid CNT-coated silica particles to form electrically conductive epoxy resin composites. Polymer 2016, 98, 32–38. [Google Scholar] [CrossRef] [Green Version]
  23. Sangermano, M.; D’Anna, A.; Marro, C.; Klikovits, N.; Liska, R. UV-activated frontal polymerization of glass fiber reinforced epoxy composites. Compos. Part B Eng. 2018, 143, 168–171. [Google Scholar] [CrossRef]
  24. Shioya, M.; Kuroyanagi, Y.; Ryu, M.; Morikawa, J. Analysis of the adhesive properties of carbon nanotube- and graphene oxide nanoribbon-dispersed aliphatic epoxy resins based on the Maxwell model. Int. J. Adhes. Adhes. 2018, 84, 27–36. [Google Scholar] [CrossRef]
  25. Chen, S.; Chen, L.; Wang, Y.M.; Wang, C.W.; Zhang, D.H. Preparation of nanocomposites with epoxy resins and thiol-functionalized carbon nanotubes by thiol-ene click reaction. Polym. Test. 2019, 77, 105912–105921. [Google Scholar] [CrossRef]
  26. Irzhak, V.I.; Dzhardimalieva, G.I.; Uflyand, I.E. Structure and properties of epoxy polymer nanocomposites reinforced with carbon nanotubes. J. Polym. Res. 2019, 26, 220–246. [Google Scholar] [CrossRef]
  27. Gholami, H.; Arab, H.; Mokhtarifar, M.; Maghrebi, M.; Baniadam, M. The effect of choline-based ionic liquid on CNTs’ arrangement in epoxy resin matrix. Mater. Des. 2016, 91, 180–185. [Google Scholar] [CrossRef]
  28. Dourani, A.; Haghgoo, M.; Hamadanian, M. Multi-walled carbon nanotube and carbon nanofiber/polyacrylonitrile aerogel scaffolds for enhanced epoxy resins. Compos. Part B Eng. 2019, 176, 107299–107308. [Google Scholar] [CrossRef]
  29. Yourdkhani, M.; Koohbor, B.; Lamuta, C.; Dean, L.M. Thermo-mechanical properties of thermoset polymers and composites fabricated by frontal polymerization. In Mechanics of Composite, Hybrid and Multifunctional Materials; Springer International Publishing: Cham, Switzerland, 2019; pp. 89–91. [Google Scholar]
  30. Jianping Zhou, S.J.; Fu, W.; Zhao, H.; Liu, Z. Curing of epoxy resin by UV-light triggered descending frontal polymerization. Chem. J. Chin. Univ. 2015, 36, 1019–1024. [Google Scholar]
  31. Mariani, A.; Alzari, V.; Monticelli, O.; Pojman, J.A.; Caria, G. Polymeric nanocomposites containing polyhedral oligomeric silsesquioxanes prepared via frontal polymerization. J. Polym. Sci. Part A Polym. Chem. 2007, 45, 4514–4521. [Google Scholar] [CrossRef]
  32. Tsegay, N.M.; Du, X.Y.; Liu, S.S.; Wang, C.F.; Chen, s. Frontal polymerization for smart intrinsic self-healing hydrogels and its integration with microfluidics. J. Polym. Sci. Part A Polym. Chem. 2018, 56, 1412–1423. [Google Scholar] [CrossRef]
  33. Pomogailo, A.D.; Singh, S.; Tandon, P. Frontal polymerization of acrylamide complex with nanostructured ZnS and PbS: Their characterizations and sensing applications. Sens. Actuators B Chem. 2015, 207, 460–469. [Google Scholar]
  34. Zhou, J.; Jia, S.; Fu, W.; Liu, Z.; Tan, Z. Fast curing of thick components of epoxy via modified UV-triggered frontal polymerization propagating horizontally. Mater. Lett. 2016, 176, 228–231. [Google Scholar] [CrossRef]
  35. Goli, E.; Parikh, N.A.; Yourdkhani, M.; Hibbard, N.G.; Geubelle, P.H. Frontal polymerization of unidirectional carbon-fiber-reinforced composites. Compos. Part A Appl. Sci. Manuf. 2020, 130, 105689. [Google Scholar] [CrossRef]
  36. Sangermano, M.; Antonazzo, I.; Sisca, L.; Carello, M. Photoinduced cationic frontal polymerization of epoxy-carbon fibre composites. Polym. Int. 2019, 68, 1662–1665. [Google Scholar] [CrossRef] [Green Version]
  37. Vyas, S.; Zhang, X.; Goli, E.; Geubelle, P.H. Frontal vs. bulk polymerization of fiber-reinforced polymer-matrix composites. Compos. Sci. Technol. 2020, 198, 108303. [Google Scholar] [CrossRef]
  38. Goli, E.; Peterson, S.R.; Geubelle, P.H. Instabilities driven by frontal polymerization in thermosetting polymers and composites. Compos. Part B Eng. 2020, 199, 10830. [Google Scholar] [CrossRef]
  39. Zhu, F.; Song, Y.; Liu, S.; Nie, Y. Preparation of polymerizable thermal initiator and its application in photo-induced thermal frontal polymerization. Eur. Polym. J. 2019, 118, 107–112. [Google Scholar] [CrossRef]
  40. Neves, J.C.; de Castro, V.G.; Assis, A.L.S.; Veiga, A.G.; Rocco, M.L.M.; Silva, G.G. In-situ determination of amine/epoxy and carboxylic/epoxy exothermic heat of reaction on surface of modified carbon nanotubes and structural verification of covalent bond formation. Appl. Surf. Sci. 2018, 436, 495–504. [Google Scholar] [CrossRef]
  41. Nuvoli, D.; Alzari, V.; Nuvoli, L.; Rassu, M.; Sanna, D.; Mariani, A. Synthesis and characterization of poly(2-hydroxyethylacrylate)/beta-cyclodextrin hydrogels obtained by frontal polymerization. Carbohydr. Polym. 2016, 150, 166–171. [Google Scholar] [CrossRef]
  42. Li, J.; Jie, J.; Xia, J.; Li, B. Preparation of konjac glucomannan-based superabsorbent polymers by frontal polymerization. Carbohydr. Polym. 2012, 87, 757–763. [Google Scholar] [CrossRef]
  43. Viner, V.G.; Pojman, J.A.; Golovaty, D. The effect of phase change materials on the frontal polymerization of a triacrylate. Phys. D Nonlinear Phenom. 2010, 239, 838–847. [Google Scholar] [CrossRef]
  44. Rahatekar, S.S.; Koziol, K.; Butler, S.A. Optical microstructure and viscosity enhancement for an epoxy resin matrix containing multiwall carbon nanotubes. J. Rheol. 2006, 50, 599–610. [Google Scholar] [CrossRef]
  45. Goli, E.; Robertson, I.D.; Agarwal, H.; Pruitt, E.L.; Grolman, J.M.; Geubelle, P.H.; Moore, J.S. Frontal polymerization accelerated by continuous conductive elements. J. Appl. Polym. Sci. 2019, 136, 47418. [Google Scholar] [CrossRef]
  46. Goli, E.; Gai, T.; Geubelle, P.H. Impact of Boundary Heat Losses on Frontal Polymerization. J. Phys. Chem. B 2020, 124, 6404–6411. [Google Scholar] [CrossRef] [PubMed]
Materials 13 05838 sch001 550
Scheme 1. Surface modification of MWCNTs by PABA.
Scheme 1. Surface modification of MWCNTs by PABA.
Materials 13 05838 sch001
Materials 13 05838 g001 550
Figure 1. FT-IR spectra of MWCNTs before and after modification.
Figure 1. FT-IR spectra of MWCNTs before and after modification.
Materials 13 05838 g001
Materials 13 05838 g002 550
Figure 2. XPS spectra for unmodified MWCNTs. The inset shows the C1s spectra of prime MWCNTs.
Figure 2. XPS spectra for unmodified MWCNTs. The inset shows the C1s spectra of prime MWCNTs.
Materials 13 05838 g002
Materials 13 05838 g003 550
Figure 3. XPS spectra for PABA-modified MWCNTs. The inset shows the C1s spectra of modified MWCNTs.
Figure 3. XPS spectra for PABA-modified MWCNTs. The inset shows the C1s spectra of modified MWCNTs.
Materials 13 05838 g003
Materials 13 05838 g004 550
Figure 4. TGA curves of prime MWCNTs and PABA-modified MWCNTs.
Figure 4. TGA curves of prime MWCNTs and PABA-modified MWCNTs.
Materials 13 05838 g004
Materials 13 05838 sch002 550
Scheme 2. Mechanism of PIFP used for preparation of MWCNTs/epoxy nanocomposites.
Scheme 2. Mechanism of PIFP used for preparation of MWCNTs/epoxy nanocomposites.
Materials 13 05838 sch002
Materials 13 05838 g005 550
Figure 5. Front position versus time for the photoinduced FP of MWCNTs/epoxy resin.
Figure 5. Front position versus time for the photoinduced FP of MWCNTs/epoxy resin.
Materials 13 05838 g005
Materials 13 05838 g006 550
Figure 6. The temporal distribution of temperature of PABA-modified MWCNTs/epoxy reaction system with different modified MWCNTs contents.
Figure 6. The temporal distribution of temperature of PABA-modified MWCNTs/epoxy reaction system with different modified MWCNTs contents.
Materials 13 05838 g006
Materials 13 05838 g007 550
Figure 7. The propagating angles observed during the preparation of the epoxy resin nanocomposites via the PIFP approach with various contents of PABA-modified MWCNTs. These images were recorded using an infrared thermal imager. P, polymers (cured products); M, monomers (mixture of epoxy oligomers, PI, and TI). Each PIFP reaction propagated horizontally to the right.
Figure 7. The propagating angles observed during the preparation of the epoxy resin nanocomposites via the PIFP approach with various contents of PABA-modified MWCNTs. These images were recorded using an infrared thermal imager. P, polymers (cured products); M, monomers (mixture of epoxy oligomers, PI, and TI). Each PIFP reaction propagated horizontally to the right.
Materials 13 05838 g007
Materials 13 05838 g008 550
Figure 8. TGA curves of epoxy nanocomposites with the content of various PABA-modified MWCNTs.
Figure 8. TGA curves of epoxy nanocomposites with the content of various PABA-modified MWCNTs.
Materials 13 05838 g008
Materials 13 05838 g009 550
Figure 9. tanδ–T curves of epoxy nanocomposites with the content of various PABA-modified MWCNTs.
Figure 9. tanδ–T curves of epoxy nanocomposites with the content of various PABA-modified MWCNTs.
Materials 13 05838 g009
Materials 13 05838 g010 550
Figure 10. The Tg of epoxy nanocomposites with the content of various PABA-modified MWCNTs.
Figure 10. The Tg of epoxy nanocomposites with the content of various PABA-modified MWCNTs.
Materials 13 05838 g010
Materials 13 05838 g011 550
Figure 11. The impact strength of epoxy composites with the content of various PABA-modified MWCNTs.
Figure 11. The impact strength of epoxy composites with the content of various PABA-modified MWCNTs.
Materials 13 05838 g011
Materials 13 05838 g012 550
Figure 12. SEM images of the fracture of pure epoxy and its nanocomposite filled by PABA-modified MWCNTs: (a) pure epoxy resin; and (b) 0.2, (c) 0.4, (d) 0.6, (e) 0.8, and (f) 1.0 wt %.
Figure 12. SEM images of the fracture of pure epoxy and its nanocomposite filled by PABA-modified MWCNTs: (a) pure epoxy resin; and (b) 0.2, (c) 0.4, (d) 0.6, (e) 0.8, and (f) 1.0 wt %.
Materials 13 05838 g012
Table
Table 1. The Vf of the photoinduced FP of MWCNTs/epoxy resin.
Table 1. The Vf of the photoinduced FP of MWCNTs/epoxy resin.
Content of MWCNTs (wt %)00.20.40.60.81.0
Vf of Modified MWCNTs/Epoxy (cm/min)0.813.153.042.722.541.43
Vf of Unmodified MWCNTs/Epoxy (cm/min)0.812.892.632.412.150.98
Table
Table 2. Viscosity of the MWCNTs/epoxy resin mixture solution.
Table 2. Viscosity of the MWCNTs/epoxy resin mixture solution.
Content of MWCNTs (wt %)00.20.40.60.81.0
Viscosity of Modified MWCNTs/Epoxy (mPa·s)165179185198206224
Viscosity of Unmodified MWCNTs/Epoxy (mPa·s)165133139146165192
Table
Table 3. Tmax of PABA-modified MWCNTs/epoxy resin mixture.
Table 3. Tmax of PABA-modified MWCNTs/epoxy resin mixture.
Content of Modified MWCNTs (wt %)0%0.2%0.4%0.6%0.8%
Tmax (°C)234.5227.9226.6224.2211.3
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Hu, G.; Fu, W.; Ma, Y.; Zhou, J.; Liang, H.; Kang, X.; Qi, X. Rapid Preparation of MWCNTs/Epoxy Resin Nanocomposites by Photoinduced Frontal Polymerization. Materials 2020, 13, 5838. https://doi.org/10.3390/ma13245838

AMA Style

Hu G, Fu W, Ma Y, Zhou J, Liang H, Kang X, Qi X. Rapid Preparation of MWCNTs/Epoxy Resin Nanocomposites by Photoinduced Frontal Polymerization. Materials. 2020; 13(24):5838. https://doi.org/10.3390/ma13245838

Chicago/Turabian Style

Hu, Guofeng, Wanli Fu, Yumin Ma, Jianping Zhou, Hongbo Liang, Xinmei Kang, and Xiaolin Qi. 2020. "Rapid Preparation of MWCNTs/Epoxy Resin Nanocomposites by Photoinduced Frontal Polymerization" Materials 13, no. 24: 5838. https://doi.org/10.3390/ma13245838

APA Style

Hu, G., Fu, W., Ma, Y., Zhou, J., Liang, H., Kang, X., & Qi, X. (2020). Rapid Preparation of MWCNTs/Epoxy Resin Nanocomposites by Photoinduced Frontal Polymerization. Materials, 13(24), 5838. https://doi.org/10.3390/ma13245838

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop