Substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 for Less Hygroscopicity and Low Thermal Expansion Properties

1
Collage of Electric Power, North China University of Water Resources and Electric Power, Zhengzhou 450011, China
2
Henan Key Laboratory of Photovoltaic Materials and Low Dimensional Materials Science Laboratory, Henan University, Kaifeng 475004, China
*
Authors to whom correspondence should be addressed.
Materials 2019, 12(23), 3945; https://doi.org/10.3390/ma12233945
Submission received: 11 October 2019 / Revised: 22 November 2019 / Accepted: 24 November 2019 / Published: 28 November 2019

Abstract

:
In this investigation, ZrxY2−xVxMo3−xO12 (0 ≤ x ≤ 1.4) is developed and the effects of the substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 on the hygroscopicity and thermal expansion property are investigated. For the smaller substitution content (x ≤ 0.5), their crystal structures remain orthorhombic, while there is crystal water still in the lattice. The linear coefficients of thermal expansions (CTEs), for x = 0.1, 0.3, 0.5, and 0.7, are about −4.30 × 10−6, −0.97 × 10−6, 0.85 × 10−6, and 0.77 × 10−6 K−1, respectively, from 476 to 773 K, which means that the linear CTE could be changed linearly with the substitution content of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12. As long as the substitution content reaches x = 1.3/1.4, almost no hygroscopicity and low thermal expansion from room temperature are obtained and are discussed in relation to the crystal structure and microstructure.

1. Introduction

Most materials expand when heated, which come from anharmonic lattice vibrations, which increases the distance between atoms. There are abnormal materials, which contract when heated and are called negative thermal expansion (NTE) materials. NTE materials have attracted tremendous attention due to their potential applications in manufacturing zero thermal expansion devices and matching the coefficients of thermal expansion (CTEs) between different materials [1,2,3]. The mechanisms of NTE are extensively investigated [4,5,6,7]. More and more NTE materials have being discovered [8,9,10,11,12,13]. The NTE properties come from different mechanisms for different crystal structures, such as the magnetostrictive effect [14,15], anharmonic lattice vibration effect [16], ferroelectric polarization effect [1], and charge transfer effect [17]. There are many experimental means to research NTE mechanisms: Neutron/X-ray pair distribution function analysis, extended X-ray absorption fine structure, infrared absorption spectrum, Raman scattering spectroscopy, etc. All of these gradually promote the practical applications of NTE materials.
However, some drawbacks of NTE materials limit their practical application, such as narrow NTE temperature range, smaller NTE coefficient, metastable structure, hygroscopicity, much higher phase transition temperature than room temperature (RT), etc. [18,19,20,21]. A2M3O12 family materials have wide NTE temperature ranges and stable structures. However, the A3+ ion radius can affect their phase transition temperature and hygroscopicity. For example, Fe2Mo3O12 crystallizes in monoclinic structures at RT and a phase transition from monoclinic to orthorhombic structure on takes place at high temperatures and then NTE could present. Y2Mo3O12 has heavy hygroscopicity in the atmospheric environment at RT, with the crystal water limiting the transverse vibration of bridge oxygen atom in A-O-M linkage (it is responsible for NTE). NTE could only be present after releasing crystal water. The hygroscopicity of Y2Mo3O12 could be reduced by using the ion-substitution (Ce3+ [22], Fe3+ [23], La3+ [24], and (LiMg)3+ [25]) method. Aliovalent substitution of Mo6+ and W6+ for V5+ in ZrV2O7 does not change its structure [26,27]. Dual-ion substitutions could change the phase temperature and thermal expansion coefficient [8,9,10,28]. Dual-ion substitutions of Fe3+/Mo6+ for Zr4+/V5+ in ZrV2O7 can obtain near zero thermal expansion material [8].
In order to avoid hygroscopicity of Y2Mo3O12 and to obtain controllable thermal expansion coefficient material, partial substitution may be necessary for both Y and Mo sites and may require enhancing the solubility of dopants. In this work, we develop Y2−xZrxMo3−xVxO12 material using Zr4+/V5+ to substitute Y3+/Mo6+ in Y2Mo3O12, and investigate the substitution effects on their thermal expansion properties and hygroscopicity in detail. It is shown that the linear CTE could be changed linearly with the substitution content of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12. A near zero thermal expansion is obtained when x = 1.3/1.4.

2. Materials and Methods

Y2−xZrxMo3−xVxO12 (0.0 ≤ x ≤ 1.4) were synthesized by a solid-state method using Y2O3, ZrO2, MoO3, and V2O5 as raw materials. The raw materials were mixed according to stoichiometric amounts of Y2O3, ZrO2, MoO3, and 3% excess V2O5 of desirable materials and were then ground in a mortar for 3 h and pressed into tablets with measuring about 10 mm in length and diameter 10 mm. This was followed by sintering at 1073 K (0.0 ≤ x ≤ 0.7) and 973 K (x = 1.3/1.4) for 4 h and cooling naturally to RT.
The linear thermal expansion coefficients of Y2−xZrxMo3−xVxO12 were measured on a dilatometer (LINSEIS DIL L76, Linseis Messgeräte GmbH, Selb, Germany). Thermogravimetric analysis (TG) of the powder samples were performed with an Ulvac Sinku-Riko DSC (Model 1500M/L, ULVAC, Methuen, MA, USA) in the temperature range of 298–873 K with the heating and cooling rates of 10 K/min. XRD measurements of the powder samples were carried out with an X-ray diffractometer (Model X’Pert PRO, Malvern Panalytical Ltd., Malvern, UK) to identify the crystalline phase. Raman spectroscopy (Renishaw MR-2000 Raman spectrometer, Renishaw, Wotton-under-Edge, UK) was used to characterize the vibrational property of lattice. The microstructures of the as-prepared pristine and modified block Y2Mo3O12 were recorded using a scanning electron microscopy (SEM, FEI Quanta 250, FEI, Hillsboro, OR, USA) with an accessory of energy dispersive spectrometer (EDS).

3. Results and Discussion

3.1. Low Thermal Expansion and Hygroscopicity

Figure 1a shows the relative linear length change curves of Y2−xZrxMo3−xVxO12 (0.0 ≤ x ≤ 1.4). For the sample with x = 0.1 in Y2−xZrxMo3−xVxO12, the thermal expansion property was similar to the reported Y2Mo3O12 (x = 0.0) [22,23], indicating that less substitution of Zr/V for Y/Mo in Y2Mo3O12 could not change the crystal structure of Y2Mo3O12. However, for x = 0.3, the thermal contraction and thermal expansion corresponding to the release of adsorbed and crystal water before 476 K reduced remarkably, indicating obvious reduction of the hygroscopicity (Figure 1b) [29]. The NTE trend after the release of crystal water (>476 K) lowered, suggesting that the translation of bridge O in Y-O-Mo and the rotation of polyhedraYO6/MoO4 related to NTE were limited by the substitutions of Zr/V for Y/Mo in Y2Mo3O12. For the weight loss curve of the sample x = 0.5, after the release of crystal water, there was a slight weight increase, which should have been related to instrument error.
The detailed estimation of the linear CTEs of the samples with x = 0.0, 0.1, 0.3, 0.5, and 0.7 were about −8.18, −4.30 × 10−6, −0.97 × 10−6, 0.85 × 10−6, and 0.77 × 10−6 K−1, respectively, from 476 to 773 K, suggesting that the linear CTE could be changed gradually with the substitution amount of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12. Additionally, even near zero thermal expansion could be realized for x = 0.7. It is interesting that, so long as the substitution reached x = 1.3/1.4, RT was observed almost without hygroscopicity and low thermal expansion (Figure 1a,b).

3.2. Crystal Structure

To make the relationship between the thermal expansion property and crystal structure change clear, with the substitution amount of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12, XRD patterns and Raman spectra of Y2−xZrxMo3−xVxO12 were performed. Figure 2a shows the XRD patterns of Y2−xZrxMo3−xVxO12 at RT with x = 0.0, 0.1, 0.3, 0.5, 1.0, 1.3, and 1.4 (for comparison, the XRD patterns of the samples with x = 0.2, 0.4, and 0.7 are also presented in Figure S1). For x = 0.0, there were only four diffraction peaks corresponding to the fully hydrated form of Y2Mo3O12·3H2O [22,23,24,25]. The XRD spectra had minor changes with the increase of Zr4+/V5+, without diffraction peaks from other materials (such as ZrMo2O8, YVO4, ZrO2, and ZrV2O7), which agreed with the results of the thermal expansion. These mean that there was crystal water in the lattice. For x = 0.3–0.5, the diffraction peaks corresponded to that of Y2Mo3O12, with the space group of Pbcn. However, for x ≥ 1.0, the primary diffraction peaks corresponded to Zr(MoO4)2 or YVO4 (Figure 2b), which indicated that there was a mixture of Zr(MoO4)2 and YVO4.
Figure 2c shows the Raman spectra of Y2−xZrxMo3−xVxO12. For x = 0.1, there were three primary Raman bonds similar to 940, 821, and 334 cm−1 and that of Y2Mo3O12, due to the presence of crystal water [22,23,25]. Additionally, two weak peaks at 258 and 887 cm−1 were also detected, which should have been related to Zr-O or V-O vibrations. In particular, for x = 0.7, the three bonds became sharp, presented a blue shift, and even split to two peaks (821 cm−1 → 811 and 834 cm−1) [23], which suggested the decreased effect of crystal water. For x = 1.3/1.4, the Raman peaks changed so much that the main peak was replaced by the peak at 745 cm−1, which should have been related to the formation of new phases corresponding to the result from XRD patterns (Figure 2a).
Figure 2d shows a high wave number Raman spectra of Y2−xZrxMo3−xVxO12. There was only one bond at about 1611 cm−1 for x = 0.1 and 0.3, which was ascribed to the bending (υ2 + υ4) vibrations of OH. This indicated that there was crystal water in the samples. However, this bond disappeared for x ≥ 0.5, which meant that the substitutions of Zr/V for Y/Mo could inhibit the entry of water into the lattice.
In order to further check the effect of the substitution of Zr4+/V5+ for Y3+/Mo6+ on the hygroscopicity of Y2Mo3O12, the microstructures of Y2−xZrxMo3−xVxO12 were performed by SEM and EDS spectra (Figure 3a–g and Figure 3a′–g′ for x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.7, and 1.4, respectively). For x = 0.1, the SEM image showed aggregation grains separated from some pores due to the heavy hygroscopicity (Figure 3a) [22,29]. For x = 0.2 and 0.3, the aggregation grains were bigger than that of 0.1, and the number of pores become less and less due to the reduction of hygroscopicity (Figure 3b,c). For x = 0.4, grains bonded together just like the binder, and far less pores were observed (Figure 3d). This means that the hygroscopicity of Y2Mo3O12 was suppressed by the substitution of Zr4+/V5+ for Y3+/Mo6+. However, amorphous grains were observed for x = 0.5 (Figure 3e), and even for x = 0.7, there were several, big, long columnar particles with smooth surfaces relating to the grain melting (Figure 3f). The EDS spectrum of x = 0.7 presented elements of Zr, V, Y, Mo, and O (Figure 3f′). For x = 1.3 and 1.4, the small grains and laminar structures were observed, which could relate to the two phases of Zr(MoO4)2 and YVO4, which corresponded to the XRD result (Figure 3g,g″,h).
From the SEM images (from x = 0.0 to x = 0.4), it can be seen that the pores reduced, suggesting that the hygroscopicity decreased with the increased substitution of Zr4+/V5+ for Y3+/Mo6+. The low thermal expansion (for x = 1.4 and 1.3) could have been related to the formation of two phases of Zr(MoO4)2 and YVO4. Zr(MoO4)2 present in the NTE [30], while YVO4 showed positive thermal expansion (Figure 4), and consequently, they canceled out one another’s thermal expansion and low thermal expansion was obtained.

4. Conclusions

The effect substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 on the hygroscopicity and thermal expansion property were investigated. For the smaller substitution content (ZrxY2−xVxMo2−xO12, x ≤ 0.5), their crystal structures remained orthorhombic. However, there was crystal water still in lattice. The adsorbed water disappeared with the increase of substitution content (x = 0.7). The linear CTEs for x = 0.1–0.7 could have been changed linearly with the substitution amount of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12. For x ≥ 1.0, low thermal expansion, and nonhygroscopicity from RT could be obtained, relating to the two phases of Zr(MoO4)2 and YVO4. The results suggested that bi-substitution could be a better way to reduce the hygroscopicity and to improve the thermal expansion property of Y2Mo3O12.

Supplementary Materials

The following are available online at https://www.mdpi.com/1996-1944/12/23/3945/s1, Figure S1: XRD patterns of Y2-xZrxMo3-xVxO12, for x = 0.2, 0.4 and 0.7.

Author Contributions

Conceptualization, X.L. and B.Y.; methodology, L.X. and Q.X.; validation, L.C. and H.Q.; formal analysis, B.Y.; investigation, X.L.; resources, Q.M.; data curation, H.Q.; writing—original draft preparation, Q.M.; writing—review and editing, X.L.

Funding

This research was funded by the National Science Foundation of China (No. 51702097, 11574083), Program for Innovative Research Team (in Science and Technology) in University of Henan Province (No.16IRTSTHN017), the Key Scientific Research Projects of Henan Province, China (15B140004), Henan Science and Technology Development Project (182102210241), Key projects of science and technology research of Henan Provincial Department of Education (18A140014), and Industrial Science and Technology Research Projects of Kaifeng, Henan Province, China (1501049).

Conflicts of Interest

The authors declare no conflicts of interest.

References

  1. Chen, J.; Wang, F.F.; Huang, Q.Z.; Hu, L.; Song, X.P.; Deng, J.X.; Yu, R.B.; Xing, X.R. Effectively control negative thermal expansion of single-phase ferroelecrics of PbTiO3-(Bi,La)FeO3 over a giant range. Sci. Rep. 2013, 3, 2458. [Google Scholar] [CrossRef] [PubMed]
  2. Yan, J.; Sun, Y.; Wen, Y.C.; Chu, L.H.; Wu, M.M.; Huang, Q.Z.; Wang, C.; Lynn, J.W.; Chen, Y.L. Relationship between spin ordering, entropy, and anomalous lattice variation in Mn3Sn1-ε SiεC1-δ compounds. Inorg. Chem. 2014, 53, 2317–2324. [Google Scholar] [CrossRef] [PubMed]
  3. Yao, W.J.; Jiang, X.X.; Huang, R.J.; Li, W.; Huang, C.J.; Lin, Z.S.; Li, L.F.; Chen, C.T. Area negative thermal expansion in a beryllium borate LiBeBO3 with edge sharing tetrahedral. Chem. Commun. 2014, 50, 13499–13501. [Google Scholar] [CrossRef] [PubMed]
  4. Yuan, B.H.; Liu, X.S.; Song, W.B.; Cheng, Y.G.; Liang, E.J.; Chao, M.J. High substitution of Fe3+ for Zr4+ in ZrV1.6P0.4O7 with small amount of FeV0.8P0.2O4 for low thermal expansion. Phys. Lett. A 2014, 378, 3397–3401. [Google Scholar] [CrossRef]
  5. Yan, J.; Sun, Y.; Wang, C.; Chu, L.H.; Shi, Z.X.; Deng, S.H.; Shi, K.W.; Lu, H.Q. Tensile ductility of nanotwinned austenitic grains in an austenitic steel. Scripta Mater. 2014, 84, 19–22. [Google Scholar] [CrossRef]
  6. Hu, L.; Chen, J.; Fan, L.L.; Ren, Y.; Rong, Y.C.; Pan, Z.; Deng, J.X.; Yu, R.B.; Xing, X.R. Zero thermal expansion and ferromagnetism in cubic Sc1-xMxF3 (M = Ga, Fe) over a wide temperature range. J. Am. Chem. Soc. 2014, 136, 13566–13569. [Google Scholar] [CrossRef]
  7. Wu, M.M.; Hu, Z.B.; Liu, Y.T.; Chen, D.F. Thermal expansion properties of Ln2-xCrxMo3O12 (Ln=Er and Y). Mater. Res. Bull. 2009, 44, 1943–1947. [Google Scholar] [CrossRef]
  8. Yuan, B.H.; Liu, X.S.; Mao, Y.C.; Wang, J.Q.; Guo, J.; Cheng, Y.G.; Song, W.B.; Liang, E.J.; Chao, M.J. Avoiding the intermediate phase Zr2WP2O12 to develop a larger-negative-thermal-expansion-coefficient material Zr2W2P2O15. Mater. Chem. Phys. 2016, 170, 162–167. [Google Scholar] [CrossRef]
  9. Ge, X.H.; Mao, Y.C.; Liu, X.S.; Cheng, Y.G.; Yuan, B.H.; Liang, E.J.; Chao, M.J. Negative thermal expansion and broad band photoluminescence in a novel material of ZrScMo2VO12. Sci. Rep. 2016, 6, 24832. [Google Scholar] [CrossRef]
  10. Cheng, Y.G.; Liang, Y.; Mao, Y.C.; Ge, X.H.; Yuan, B.H.; Guo, J.; Liang, E.J.; Chao, M.J. A novel material of HfScW2PO12 with negative thermal expansion from 140 K to 1469 K and intense blue photoluminescence. Mater. Res. Bull. 2017, 85, 176–180. [Google Scholar] [CrossRef]
  11. Hemberger, J.; von Nidda, H.-A.K.; Tsurkan, V.; Loidl, A. Spin-driven Phonon splitting in bond frustrated ZnCr2Se4. Phys. Rev. Lett. 2006, 97, 087204. [Google Scholar] [CrossRef] [PubMed]
  12. Pokharel, G.; May, A.F.; Parker, D.S.; Calder, S.; Ehlers, G.; Huq, A.; Kimber, S.A.J.; Suriya Arachchige, H.; Poudel, L.; McGuire, M.A.; et al. Negative thermal expansion and magnetoelastic coupling in the breathing pyrochlore lattice material LiGaCr4S8. Phys. Rev. B 2014, 90, 060414. [Google Scholar] [CrossRef]
  13. Takenaka, K.; Okamoto, Y.; Shinoda, T.; Katayama, N.; Sakai, Y. Colossal negative thermal expansion in reduced layered ruthenate. Nat. Commun. 2017, 8, 14102. [Google Scholar] [CrossRef] [PubMed]
  14. Gautam, K.; Shukla, D.K.; Francoual, S.; Bednarcik, J.; Mardegan, J.R.L.; Liermann, H.P.; Sankar, R.; Chou, F.C.; Phase, D.M.; Strempfer, J. Large negative thermal expansion in the cubic phase of CaMn7O12. Phys. Rev. B 2017, 95, 144112. [Google Scholar] [CrossRef]
  15. Song, X.Y.; Sun, Z.H.; Huang, Q.Z.; Rettenmayr, M.; Liu, X.M.; Seyring, M.; Li, G.N.; Rao, G.H.; Yin, F.X. Adjustable zero thermal expansion in antiperovskite manganese nitride. Adv. Mater. 2011, 23, 4690–4694. [Google Scholar] [CrossRef] [PubMed]
  16. Bridges, F.; Keiber, T.; Juhas, P.; Billinge, S.J.L.; Sutton, L.; Wilde, J.; Kowach, G.R. Local vibrations and negative thermal expansion in ZrW2O8. Phys. Rev. Lett. 2014, 112, 045505. [Google Scholar] [CrossRef]
  17. Long, Y.W.; Hayashi, N.; Saito, T.; Azuma, M.; Muranaka, S.; Shimakawa, Y. Temperature-induced A–B intersite charge transfer in an A-site-ordered LaCu3Fe4O12 perovskite. Nature 2009, 458, 60–64. [Google Scholar] [CrossRef]
  18. Liu, X.S.; Yuan, B.H.; Cheng, Y.G.; Liang, E.J.; Zhang, W.F. Combined influences of A3+ and Mo6+ on monoclinic-orthorhombic phase transition of negative-thermal-expansion A2Mo3O12. J. Alloy. Compd. 2019, 776, 236–241. [Google Scholar] [CrossRef]
  19. Liu, X.S.; Cheng, F.X.; Wang, J.Q.; Song, W.B.; Yuan, B.H.; Liang, E.J. Synthesis, thermal expansion and optical properties of (1-x) NaAl (MoO4)2-xNaEr(MoO4)2 ceramics. J. Alloy. Compd. 2013, 553, 1–7. [Google Scholar] [CrossRef]
  20. Yuan, B.H.; Yuan, H.L.; Song, W.B.; Liu, X.S.; Cheng, Y.G.; Chao, M.J.; Liang, E.J. High solubility of hetero-valence ion (Cu2+) for reducing phase transition and thermal expansion of ZrV1.6P0.4O7. Chin. Phys. Lett. 2014, 31, 076501. [Google Scholar] [CrossRef]
  21. Yuan, B.H.; He, X.K.; Chen, L.L.; Wang, W.S.; Cheng, T.; Liang, E.J. Electrical properties and dielectric relaxation behavior of zirconium vanadate. Ceram. Int. 2018, 44, 21621–21625. [Google Scholar] [CrossRef]
  22. Liu, X.S.; Cheng, Y.G.; Liang, E.J.; Chao, M.J. Interaction of crystal water with the building block in Y2Mo3O12 and the effect of Ce3+ doping. Phys. Chem. Chem. Phys. 2014, 16, 12848–12857. [Google Scholar] [CrossRef] [PubMed]
  23. Li, Z.Y.; Song, W.B.; Liang, E.J. Structures, Phase Transition, and Crystal Water of Fe2-xYxMo3O12. J. Phys. Chem. C 2011, 115, 17806–17811. [Google Scholar] [CrossRef]
  24. Liu, H.F.; Wang, X.C.; Zhang, Z.P.; Chen, X.B. Synthesis and thermal expansion properties of Y2-xLaxMo3O12 (x = 0, 0.5, 2). Ceram. Int. 2012, 38, 6349–6352. [Google Scholar] [CrossRef]
  25. Cheng, Y.G.; Liu, X.S.; Song, W.B.; Yuan, B.H.; Wang, X.L.; Chao, M.J.; Liang, E.J. Relationship between hygroscopicity reduction and morphology evolution of Y2Mo3O12 doped with (LiMg) 3+. Mater. Res. Bull. 2015, 65, 273–278. [Google Scholar] [CrossRef]
  26. Sahoo, P.P.; Sumithra, S.; Madras, G.; Row, T.N.G. Synthesis, structure, negative thermal expansion, and photocatalytic property of Mo doped ZrV2O7. Inorg. Chem. 2011, 50, 8774–8781. [Google Scholar] [CrossRef]
  27. Liu, Q.Q.; Yang, J.; Sun, X.J.; Cheng, X.N.; Tang, H.; Li, H.H. Influence of W doped ZrV2O7 on structure, negative thermal expansion property and photocatalytic performance. Appl. Surf. Sci. 2014, 313, 41–47. [Google Scholar] [CrossRef]
  28. Chen, D.X.; Yuan, B.H.; Cheng, Y.G.; Ge, X.H.; Jia, Y.; Liang, E.J.; Chao, M.J. Phase transition and near-zero thermal expansion in ZrFeMo2VO12. Phys. Lett. A 2016, 380, 4070. [Google Scholar] [CrossRef]
  29. Liu, X.S.; Yuan, B.H.; Cheng, Y.G.; Ge, X.H.; Liang, E.J.; Zhang, W.F. Avoiding the invasion of H2O into Y2Mo3O12 by coating with C3N4 to improve negative thermal expansion properties. Phys. Chem. Chem. Phys. 2017, 19, 13443–13448. [Google Scholar] [CrossRef]
  30. Lind, C.; Wilkinson, A.P.; Hu, Z.B.; Short, S.; Jorgensen, J.D. Synthesis and properties of the negative thermal expansion material cubic ZrMo2O8. Chem. Mater. 1998, 10, 2335–2337. [Google Scholar] [CrossRef]
Figure 1. (a) Relative length change and (b) thermogravimetric analysis (TG) of Y2−xZrxMo3−xVxO12.
Figure 1. (a) Relative length change and (b) thermogravimetric analysis (TG) of Y2−xZrxMo3−xVxO12.
Materials 12 03945 g001
Figure 2. XRD patterns (a,b) and Raman spectra (c,d) of Y2−xZrxMo3−xVxO12.
Figure 2. XRD patterns (a,b) and Raman spectra (c,d) of Y2−xZrxMo3−xVxO12.
Materials 12 03945 g002
Figure 3. Scanning electron microscopy (SEM) images (ah) and the corresponding energy dispersive spectrometer (EDS) spectra (a′–h′) of Y2−xZrxMo3−xVxO12 for x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.7, and 1.4, respectively, and SEM images (h″ and i) of x = 1.4 and 1.3.
Figure 3. Scanning electron microscopy (SEM) images (ah) and the corresponding energy dispersive spectrometer (EDS) spectra (a′–h′) of Y2−xZrxMo3−xVxO12 for x = 0.0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.7, and 1.4, respectively, and SEM images (h″ and i) of x = 1.4 and 1.3.
Materials 12 03945 g003aMaterials 12 03945 g003bMaterials 12 03945 g003c
Figure 4. Relative linear length change of YVO4 prepared with Y2O3 and V2O5 raw materials using the same temperature as Y2−xZrxMo3−xVxO12. The linear coefficients of thermal expansions (CTE) is about 6.02 × 10−6 K−1.
Figure 4. Relative linear length change of YVO4 prepared with Y2O3 and V2O5 raw materials using the same temperature as Y2−xZrxMo3−xVxO12. The linear coefficients of thermal expansions (CTE) is about 6.02 × 10−6 K−1.
Materials 12 03945 g004

Share and Cite

MDPI and ACS Style

Ma, Q.; Chen, L.; Qi, H.; Xu, Q.; Yuan, B.; Liu, X.; Xu, L. Substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 for Less Hygroscopicity and Low Thermal Expansion Properties. Materials 2019, 12, 3945. https://doi.org/10.3390/ma12233945

AMA Style

Ma Q, Chen L, Qi H, Xu Q, Yuan B, Liu X, Xu L. Substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 for Less Hygroscopicity and Low Thermal Expansion Properties. Materials. 2019; 12(23):3945. https://doi.org/10.3390/ma12233945

Chicago/Turabian Style

Ma, Qiang, Lulu Chen, Heng Qi, Qi Xu, Baohe Yuan, Xiansheng Liu, and Lei Xu. 2019. "Substitutions of Zr4+/V5+ for Y3+/Mo6+ in Y2Mo3O12 for Less Hygroscopicity and Low Thermal Expansion Properties" Materials 12, no. 23: 3945. https://doi.org/10.3390/ma12233945

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop