Search Results (6)

Hot-rolled backup rolls are widely used in steel rolling and usually need to be repaired by arc hardfacing after becoming worn. However, a corrugated-groove defect commonly occurs on the roll surface due to the uneven hardness distribution in the hardfacing layers, affecting the proper usage of the roll. Accordingly, a new swing-arc submerged arc welding (SA-SAW) process is proposed to attempt to solve this drawback. The microstructure and hardness are then investigated experimentally for both SAW and SA-SAW hardfacing layers. It is revealed that a self-tempering effect occurs in the welding pass bottom and the welding pass side neighboring the former pass for both processes, refining the grain in the two areas. In all the zones, including the self-tempering zone (STZ), heat-affected zone (HAZ), and not-heat-affected zone in the welding pass, both SAW and SA-SAW passes crystallize in a type of columnar grain, where the grains are the finest in STZ and the coarsest in HAZ. In addition, the arc swing improves the microstructure homogeneity of the hardfacing layers by obviously lowering the tempering degree in HAZ while promoting the even distribution of the arc heat. Accordingly, the hardness of the SA-SAW bead overall increases and distributes more uniformly with a maximum difference of < 80 HV_0.5 along the horizontal direction of the bead. This hardness difference in SA-SAW is accordingly decreased by ~38.5% compared to that of the SAW bead, further indicating the practicability of the new process. Full article

Reduced activation ferritic (RAF) martensitic steels are promising candidates for the first wall of fusion reactors. However, current manufacturing capabilities call for these components to be made by welding wrought plates. This limits design freedom and necessitates the use of post-weld heat treatments (PWHT) in accordance with the boiler and pressure vessel code. Additive manufacturing (AM) can offer a unique solution to solve this challenge by leveraging the layer-wise deposition strategy to come up with temper bead deposition techniques to eliminate post-processing heat treatments (PPHT). However, it is necessary to benchmark the properties of RAF steels fabricated by AM with their wrought counterparts to identify the process-structure-property correlation, which is the goal of this study. The study demonstrates that while tensile properties at room temperature and high temperatures are satisfactory, the as fabricated and samples after PPHT have significant heterogeneity in tensile elongation. This has been attributed to the presence of discontinuities in the build. The as-fabricated samples have an average tensile strength of 1190 + 12 MPa and an average elongation of 15 + 5% at room temperature and 658 ± 20 MPa ultimate tensile strength (UTS) and 14 ± 7% at 600 °C. After the post-weld heat treatment, mechanical properties decrease to around 600–650 MPa and an elongation between 20–25% at room temperature to 300 MPa UTS and 25–28% elongation at 600 °C. The characterization of microstructures at various length scales demonstrates that the as-fabricated structure has a significant fraction of delta ferrite in a lath martensitic matrix. No precipitates could be identified in the as-fabricated structure. PPHT led to a decrease in the area fraction of delta ferrite and precipitation of M₂₃C₆ and MX. Detailed characterization clearly demonstrates that the lack of precipitates in the as-fabricated structure could be due to the slow tempering response of the alloy. Finally, the needs to develop new alloys to achieve the objectives stated above are articulated. Full article

Welded constructions are subject to high stresses during operation. One solution for improving the behavior in exploitation of welded constructions in various cases is to use the welding technique “temper bead welding” (TBW). In the paper, the optimization of the geometry of the welded joints by the TBW technique was performed. Thus, corner welded joints made of S355 steel were analyzed. To make the welded joints, three layers of welding seams were deposited, and the intermediate layers were processed through cutting with various radii. To analyze the influence of the size of these rays on the behavior of welded constructions, a research program based on factorial experiences was designed. The samples were tested in terms of fatigue behavior by applying loads between ±8 kN and ±12 kN. The research also focused on determining the hardness of the materials in the joints welded and on determining the microstructure of the materials in the heat affected zone (HAZ). Research has shown that it is possible to improve the characteristics of joints made by the TBW technique in the sense that it can be achieved an improvement in fatigue stress, a decrease in the hardness of the HAZ material and an improvement in the metallographic structure of the HAZ material, meaning that it has a structure made of ferrite and fine pearlite. Full article

In this paper the influence of in situ local heat treatment performed by additional stitches on the weldability of high-strength low-alloy (HSLA) S355J2C+N steel was tested. The investigated steel is characterized by high susceptibility to cold cracking. It is necessary to find a method to improve the quality of welded joints. The local heat treatment was applied as an effect of bead-on plate welding made on the face of a Tekken test joint. The specimens were made by the use of covered electrodes in the water environment. For testing weldability, Tekken test specimens were made. Then, the different number of the pad welds with different overlapping were laid on the face of the tested welds. Non-destructive (NDT) visual and penetrant tests were undertaken. During the NDT, imperfections like shape mistakes and spatters were found. Then, metallographic macro- and microscopic testing were performed. The macroscopic observations proved that water environment can generate imperfections like cracking and pores. However, for specimens with additional stitches the number of imperfections decreased. Microscopic tests proved that the proposed technique affected the structure of the heat-affected zone (HAZ). The specimens without the application of additional stitches are characterized by brittle bainitic and martensitic structure. Specimens, in which the additional stitches were applied, contain tempered martensite, fine ferrite and fine pearlite in their HAZ. It was also observed that the number of cracks decreased for in situ local heat-treatment specimens. The final step was Vickers HV10 hardness measurement. These measurements confirmed previous results. The heat from additional stitches affected the steel by significantly decreasing the hardness by 80–100 HV10. The results of experiments showed that the heat from pad welds provided microstructural changes in heat-affected zones and a decrease in the susceptibility to cold cracking, which results in improvement in the weldability of HSLA steel in wet welding conditions. Full article

This paper presents examinations of the role of the bead sequence in underwater welding. Two specimens of wet welded layers made by covered electrodes with the use of normalized S355G10+N steel were welded by a reasonable bead sequence. For each specimen, metallographic macro- and micro-scopic tests were done. Then, Vickers HV10 hardness measurements were conducted for each pad weld in the welded layer. The results show that welding in the water environment carries many problems in the stability of the welding arc, which influences the properties of the welds. The effects of refining and tempering the structure in heat-affected zones of earlier laid beads was observed, which provides a reduction of hardness. The possibility of applying two techniques while welding the layer by the wet method is described. It is stated that a reasonable bead sequence can decrease the hardness in heat-affected zones up to 40 HV10. Tempering by heat from next beads can also change the microstructure in this area by tempering martensite and can decrease susceptibility to cold cracking. Full article

Thermo-mechanically rolled S460ML steel was chosen for welding in underwater wet welding conditions by covered electrodes. The main aim of this study was to check the weldability for fillet welds in a water environment by controlled thermal severity (CTS) tests and to check the influence of temper bead welding (TBW) on the weldability of the investigated steel. Non-destructive and destructive tests showed that S460ML steel has a high susceptibility to cold cracking. In all joints, hardness in the heat-affected zone (HAZ) was extended to the 400 HV10 values. Microscopic testing showed the presence of microcracks in the HAZ of all welded joints. TBW was chosen as the method to improve the weldability of the investigated steel. This technique allows for the reduction of the maximum hardness in the HAZ below the critical value of 380 HV10, as stated by the EN-ISO 15614-1:2017. It was determined that for S460ML steel, from the point of view of weldability, the pitch between two beads should be in the range 75%–100%. Also, if the pitch between two beads increases, the hardness, grain size, and number of cracks decreases. In all specimens where the hardness of the HAZ was below 380 HV10, there were no microcracks. Full article