Search Results (2)

This study investigates the biodegradation behavior of poly(butylene succinate) (PBS) copolyesters containing dilinoleic acid (DLA) co-monomeric units and wood flour (WF) as a filler. PBS-DLA is a segmented thermoplastic elastomer (TPE), where the soft amorphous phase is formed by DLA ester segments, while the hard phase consists of crystallizable PBS domains. Wood–plastic composites (WPCs) were prepared with WF at weight fractions of 10%, 20%, 30%, and 40% wt. and analyzed in terms of surface morphology, chemical structure, mechanical performance, and thermal stability before and after biodegradation in soil conditions. The results of microscopic analysis confirmed that the PBS-DLA copolymer and its composites undergo surface biodegradation as manifested by increased surface roughness and microcrack formation, particularly in composites with a higher WF content. ATR FT-IR spectroscopy indicated oxidation and hydrolysis, supporting the hypothesis of progressive surface erosion. Mechanical tests showed a decline in tensile strength and elongation at break, with the most pronounced changes in composites containing 20% WF. Thermal analysis (DSC, DMTA, and TGA) confirmed that the PBS-DLA copolymer retains its thermoplastic elastomeric behavior after a 3-month biodegradation experiment. The storage modulus (E′) remained stable, while only minor variations in melting and crystallization temperatures were observed. These findings reinforce the hypothesis of surface erosion rather than a bulk degradation mechanism. Given their biodegradability and retained thermoplastic behavior, WPC composites based on PBS-DLA copolyester could be promising for eco-friendly applications where controlled degradation is desirable, such as in packaging, agriculture, or biodegradable consumer goods. Full article

Cardiac surgical approaches require the development of new materials regardless of the polyurethanes used for pulsatile blood pumps; therefore, an innovative biomaterial, a copolymer of poly(ethylene terephthalate) and dimer fatty acid (dilinoleic acid) modified with D-glucitol, hereafter referred to as PET/DLA, has been developed, showing non-hemolytic and atrombogenic properties and resistance to biodegradation. The aim of this work was to evaluate in vivo inflammatory responses to intramuscular implantation of PET/DLA biomaterials of different compositions (hard to soft segments). Two copolymers containing 70 and 65 wt.% of hard segments, as in poly(ethylene terephthalate) and dilinoleic acid in soft segments modified with D-glucitol, were used for implantation tests to monitor tissue response. Medical grade polyurethanes Bionate II 90A and Bionate II 55 were used as reference materials. After euthanasia of animals (New Zealand White rabbits, n = 49), internal organs and tissues that contacted the material were collected for histopathological examination. The following parameters were determined: peripheral blood count, blood smear with May Grunwald–Giemsa staining, and serum C-reactive protein (CRPP). The healing process observed at the implantation site of the new materials after 12 weeks indicated normal progressive collagenization of the scar, with an indication of the inflammatory–resorptive process. The analysis of the chemical structure of explants 12 weeks after implantation showed good stability of the tested copolymers in contact with living tissues. Overall, the obtained results indicate great potential for PET/DLA in medical applications; however, final verification of its applicability as a structural material in prostheses is needed. Full article