Search Results (3)

Introduction: A modular head–neck adapter system may help surgeons restore the proximal hip biomechanics in revision hip arthroplasty. However, the clinical and radiographic 5-year outcomes of the system are still scarcely reported. The aim of this study is the assessment of (1) complications and survival rates, (2) clinical and (3) radiological outcomes of the modular head–neck adapter system with a ceramic head in revision hip arthroplasty at 5 years. Methods: 32 revision hip arthroplasties using a modular head–neck adapter system and a ceramic head were retrospectively recorded. Preoperative demographic and implant features were collected. Clinical and radiographic outcomes, failures and reasons for re-revisions were recorded at the last follow-up. Results: A mean follow-up of 59.8 ± 26 months was achieved. The survival rate was 90.6% at 5 years. Post-operative complications occurred in nine cases (28.1%): two dislocations (6.2%), one aseptic cup loosening (3.1%) requiring re-revision, one (3.1%) persistent pelvic pseudotumor requiring embolization. No mechanical failures of the adapter or ceramic head occurred. The mean post-operative HHS score was 84.4 points. Thirteen cases (40.6%) showed optimal radiographic cup osseointegration, and 17 hips (53.1%) showed valid stem osseointegration. The mean post-operative femoral offset was 48.84 mm, larger than the contralateral side (p = 0.02). The post-operative lateralization of the hip joint was 38.09 mm, close to the contralateral side (p = 0.4). Conclusions: In revisions, the modular head–neck adapter system with ceramic head provided good clinical outcomes and acceptable radiographic reconstruction of hip biomechanics, with a survival rate of 87.9% at 5 years. Full article

The purpose of the present study was to compare the wear behavior of ceramic-on-vitamin-E-diffused crosslinked polyethylene (Vit-E XLPE) hip bearings employing the gold standard oxide ceramic, zirconia (ZrO₂)-toughened alumina (Al₂O₃) (ZTA, BIOLOX^®delta) and a new non-oxide ceramic, silicon nitride (Si₃N₄, MC^2®). In vitro wear test was performed using a 12-station hip joint simulator. The test was carried out by applying the kinematic inputs and outputs as recommended by ISO 14242-1:2012. Vitamin-E-diffused crosslinked polyethylene (Vit-E XLPE) acetabular liners (E1^®) were coupled with Ø28-mm ZTA and Si₃N₄ femoral heads. XLPE liner weight loss over 5 million cycles (Mc) of testing was compared between the two different bearing couples. Surface topography, phase contents, and residual stresses were analyzed by contact profilometer and Raman microspectroscopy. Vit-E XLPE liners coupled with Si₃N₄ heads produced slightly lower wear rates than identical liners with ZTA heads. The mean wear rates (corrected for fluid absorption) of liners coupled with ZTA and Si₃N₄ heads were 0.53 ± 0.24 and 0.49 ± 0.23 mg/Mc after 5 Mc of simulated gait, respectively. However, after wear testing, the ZTA heads retained a smoother topography and showed fewer surface stresses than the Si₃N₄ ones. Note that no statistically significant differences were found in the above comparisons. This study suggests that the tribochemically formed soft silica layer on the Si₃N₄ heads may have reduced friction and slightly lowered the wear of the Vit-E XLPE liners. Considering also that the toughness of Si₃N₄ is superior to ZTA, the present wear data represent positive news in the future development of long-lasting hip components. Full article

Biolox^® delta has been widely used in joint replacements thanks to its high strength and wear resistance. In this study, eleven Biolox^® delta femoral head retrievals affected by metal transfer (MT) were analysed by Raman spectroscopy to estimate the tetragonal to monoclinic zirconia phase transformation, whose occurrence may compromise ceramic chemical stability and mechanical strength. The residual stress state was evaluated by both Raman and photoemission spectroscopy. V_m monoclinic zirconia contents were higher near the centre of the articulating surface and in the MT area than in the border control area of the retrievals. In only one retrieval, stress related to MT appeared a more severe condition, able to induce zirconia phase transformation; for all the others, stresses related to loading in the central region and related to MT, were conducive to a zirconia phase transformation of nearly the same extent. V_m depth profiling analyses showed that the transformation involved different thicknesses in different samples. Raman data allowed for the investigation of the mechanism of zirconia phase transformation and confirmed that the growth stage was absent and the nucleation stage was not occurring as freely as it would in unconstrained zirconia. Full article