Next Article in Journal
Electrospun PCL Patches with Controlled Fiber Morphology and Mechanical Performance for Skin Moisturization via Long-Term Release of Hemp Oil for Atopic Dermatitis
Previous Article in Journal
Unraveling the Role of Drug-Lipid Interactions in NSAIDs-Induced Cardiotoxicity
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Membranes
Volume 11
Issue 1
10.3390/membranes11010025
membranes-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Dye Separation and Antibacterial Activities of Polyaniline Thin Film-Coated Poly(phenyl sulfone) Membranes

by
Javed Alam
1,*,
Arun Kumar Shukla
1,
Mohammad Azam Ansari
2,
Fekri Abdulraqeb Ahmed Ali
3 and
Mansour Alhoshan
1,3,4
1
King Abdullah Institute for Nanotechnology, King Saud University, Riyadh 11451, Saudi Arabia
2
Department of Epidemic Disease Research, Institute of Research and Medical Consultation, Imam Abdulrahman Bin Faisal University, Dammam 31441, Saudi Arabia
3
Chemical Engineering Department, College of Engineering, King Saud University, Riyadh 11451, Saudi Arabia
4
K. A. CARE Energy Research and Innovation Center at Riyadh, Riyadh 11451, Saudi Arabia
*
Author to whom correspondence should be addressed.
Membranes 2021, 11(1), 25; https://doi.org/10.3390/membranes11010025
Submission received: 30 November 2020 / Revised: 22 December 2020 / Accepted: 23 December 2020 / Published: 29 December 2020
(This article belongs to the Section Polymeric Membranes)
Browse Figures
Review Reports Versions Notes

Abstract

:
We fabricated a nanofiltration membrane consisting of a polyaniline (PANI) film on a polyphenylsulfone (PPSU) substrate membrane. The PANI film acted as a potent separation enhancer and antimicrobial coating. The membrane was analyzed via scanning electron microscopy and atomic force microscopy to examine its morphology, topography, contact angle, and zeta potential. We aimed to investigate the impact of the PANI film on the surface properties of the membrane. Membrane performance was then evaluated in terms of water permeation and rejection of methylene blue (MB), an organic dye. Coating the PPSU membrane with a PANI film imparted significant advantages, including finely tuned nanometer-scale membrane pores and tailored surface properties, including increased hydrophilicity and zeta potential. The PANI film also significantly enhanced separation of the MB dye. The PANI-coated membrane rejected over 90% of MB with little compromise in membrane permeability. The PANI film also enhanced the antimicrobial activity of the membrane. The bacteriostasis (BR) values of PANI-coated PPSU membranes after six and sixteen hours of incubation with Escherichia coli were 63.5% and 95.2%, respectively. The BR values of PANI-coated PPSU membranes after six and sixteen hours of incubation with Staphylococcus aureus were 70.6% and 88.0%, respectively.

Graphical Abstract

1. Introduction

Membrane separation techniques for water and wastewater treatment have been increasingly utilized to address the global challenge of water scarcity. These techniques have intrinsic advantages, such as facile scalability, low environmental impact, and most importantly, continuous separation in combination with other conventional processes [1,2,3,4,5,6]. Membrane processes to treat water provide several benefits. However, the inherently hydrophobic nature of the polymers used for membrane preparation is a disadvantage [7,8,9,10]. Membranes are prone to fouling due to their hydrophobic nature, so more power is required to force water flow. Consequently, the membrane must be replaced frequently. Several strategies have been employed to mitigate fouling, including pretreatment of the feed water and hydrophilic modification of the membranes. Hydrophilic polymers and nanoparticles with functional groups have been used to modify membrane surfaces via various approaches, such as coating, grafting, and bulk modification. Surface coatings have recently generated significant interest as an attractive means of hydrophilic membrane modification [9,11,12,13,14,15,16,17,18,19]. Surface coatings offer several advantages, such as low cost and facile adoption. The stability of a coating can be improved by tailoring its thickness and enhancing crosslinking.
In this study, a polyphenylsulfone (PPSU) membrane was used as a substrate and coated with a polyaniline (PANI) membrane. The properties of PPSU membranes are superior to those of membranes prepared from other sulfones, such as polysulfone and polyethersulfone (PES) [20,21,22]. However, the intrinsically hydrophobic nature of PPSU is often viewed as a limitation. Hence, we deposited a thin PANI film on the surface of a PPSU membrane to enhance its separation performance. PANI is an intrinsically conductive polymer that has been applied as a hydrophilic modifier to develop membranes for various separation applications. These include water treatment, gas separation, and fuel cell applications [23,24,25,26,27,28,29]. PANI can be utilized as a bulk powder. It can also be used to cast films and fabricate nanoparticles or fibers. Its acid-base doping chemistry facilitates the construction of membranes with switchable surface wettability properties and tunable pore sizes [28,30,31]. PANI is an ideal membrane modifier, because it is both hydrophilic and insoluble in water. PANI systems have ion exchanging properties and are environmentally sustainable. In several recent studies, PANI and sulfonated PANI were used as additives to prepare hydrophilic PPSU membranes [32,33]. To the best of our knowledge, PANI has been investigated primarily as a bulk powder. However, it has not been utilized to cast films on PPSU substrate membranes to enhance their surface properties. We generated a PANI film on a PPSU substrate membrane via the oxidative polymerization of an aniline monomer. The PANI-coated PPSU membrane was then compared to an unmodified PPSU membrane in terms of hydrophilicity, surface charge, contact angle, antibacterial activity, and separation performance via the filtration of a methylene dye solution.

2. Materials and Methods

2.1. Materials

Distilled aniline, hydrochloric acid (HCl, ACS reagent, 37%), N-methyl-2-pyrrolidone (NMP, >98%), and ammonium persulfate (NH4)2S2O8 (APS, reagent grade, 98%) were used as received from Aldrich, (Kenilworth, NJ, USA). Polyphenylsulfone (PPSU) (Ultrason P 3010) was supplied by BASF (Berlin, Germany). Polyvinylpyrrolidone (PVP, average MW 10,000), methylene blue (MW 373), and sodium azide (≥99.5%) were purchased from Aldrich (Kenilworth, NJ, USA). Deionized (DI) water was obtained from a Milli-Q water purification system.

2.2. Fabrication of PPSU Support Membrane

The PPSU support membrane was prepared using a phase inversion method as described previously [20]. Dried PPSU (17 wt.%) and 10 wt.% PVP were both dissolved in N-methyl-2-pyrrolidone with gentle stirring for 3 h at 60 ± 5 °C. When no air bubbles were visible in the homogeneous mixture, it was hand-cast onto a clean and dry glass plate to a thickness of 100 ± 3 μm using a blade. The glass plate was gently placed in a coagulation bath containing distilled water for phase inversion. Within one minute, the membrane floated to the surface of the water. The membrane was removed, rinsed with DI water, and stored in an aqueous solution of 0.2% sodium azide to prevent microbial contamination.

2.3. Deposition of a PANI Thin Film on the PPSU Membrane

A PANI film was grown on the surface of the PPSU substrate via the chemical oxidation of monomeric aniline. APS served as the oxidant, and HCl was used as a doping agent. The PPSU membrane was immersed in DI water for 1 h to remove any residual chemicals, then taped to a clean glass plate. Monomeric aniline (0.2 mL) was added to 1 M HCl (5 mL), and the mixture was stirred at room temperature. APS (0.01 g) was dissolved in DI water (0.25 mL), and the solutions were combined and stirred for 20 s to ensure complete mixing. The mixture was then poured over the surface of the PPSU membrane. The film turned purple at the beginning of the polymerization process. The color of the film changed to green, which confirmed the formation of PANI as an emeraldine salt. The PANI film was rinsed with DI water to remove granular PANI, then dried and stored in a desiccator. The following steps were performed to deposit a uniform PANI film using a ‘pouring’ method. (1) A solution to be polymerized was poured over the surface of the PPSU membrane and kept for 25 s. (2) The temperature to polymerize aniline was 25 °C, and (3) the low concentration of monomeric aniline (0.2 mL) played a great role in depositing a uniform PANI film over the surface of the PPSU membrane. Most important, it was merely the first cycle of PANI film deposition. Finally, the PANI/PPSU membrane sample was rinsed with DI water at a rate of 0.4 mL/s for 30 s to remove weakly bound PANI oligomers from substrate membrane. Formation of the PANI thin film on the PPSU membrane and the oxidative polymerization process are illustrated schematically in Figure 1.

2.4. Characterization

2.4.1. Scanning Electron Microscopy (SEM)

SEM imaging was performed to examine the surface and cross-sectional morphology of the membranes using a SEM (JEOL, Tokyo, Japan). Membrane samples with areas of approximately 0.5 cm2 were taped to supports and sputtered with a Pt coating to a thickness of ~10 nm. The membranes were oriented perpendicularly to the incident electron beam to obtain cross-sectional images. The SEM images were collected at an accelerating voltage of 10 kV and a working distance of 6.4 mm at various magnifications.

2.4.2. Atomic Force Microscopy (AFM)

The topography of the deposited PANI film was analyzed using a Nanoscope V MultiMode atomic force microscope (Veeco, San Jose, CA, USA). Scans were conducted at a frequency of 0.999 Hz using a Si tip in tapping mode. The surface roughness and structure were evaluated in a 5 μm × 5 μm area of the sample using the instrumental software (6.13).

2.4.3. Contact Angle Measurements

The hydrophilicity of the membranes was quantified via the sessile drop method. Contact angles were measured using a goniometer (Atension, MAC 200, Biolin Scientific, Amsterdam, The Netherlands) equipped with a digital camera and image analysis software. Water droplets with volumes of 3 ± 1 µL were placed at five different places on the membrane surface using a microliter syringe. The profile of each water droplet relative to the membrane surface was recorded as a two-dimensional image using the digital camera. Each reported contact angle (θ) is the average of five measurements.

2.4.4. Zeta Potential Measurements

The surface streaming potentials were measured using a SurPASS Electrokinetic analyzer (Anton Paar GmbH, Graz, Austria) to determine the zeta potentials of the membranes over a range of pH values. The zeta potential is an indicator of surface charge. The zeta potential of each membrane was measured after clamping the membrane in a cell with an adjustable gap. Titration was performed from pH 2.5 to pH 6 using a 0.01 mM KCl solution and 0.25 M HCl. The reported zeta potentials of the membranes were obtained from measurements at two locations on each sample.

2.5. Membrane Performance Assessment

2.5.1. Experimental Setup and Water Filtration Procedure

A CF042 crossflow filtration system (Sterlitech, Kent, WA, USA) was used to evaluate membrane performance, water flux, and solute rejection. The active area of each membrane in the crossflow cell was 42 cm2. DI water was used to pressurize each membrane at 10 bar for 1 h, which allowed the water permeation flux to reach a steady state. After compaction, each membrane sample was mounted on the filtration cell assembly. The DI water flux was measured again under the same conditions for at least 1 h. For the final water flux measurements, the operative pressure was reduced to 6 bar. The flux was recorded as the mean of the 10 most recent water flux values. The permeated water was collected, and the DI water permeation flux was calculated using Equation (1).
Jw = V/(A × Δt),
where Jw is the water permeation flux through the membrane (L m−2 h−1), V is the collected permeate volume (L), A is the active membrane area (m2), and Δt is the permeation time (h).

2.5.2. Experimental Setup Used to Evaluate MB Dye Rejection

The DI water was drained from the storage feed tank, and the MB stock solution was added to assess rejection at a constant pressure of 6 bar. The permeate water was collected at intervals. Absorbance by MB was measured at 620 nm using a Cary 60 ultraviolet-visible (UV-VIS) spectrophotometer (Agilent Technologies, Santa Clara, CA, USA). Rejection (%) was then calculated using Equation (2).
R (%) = (1 − Cp/Cf) × 100,
where R is the rejected amount of MB (%), Cp is the concentration of MB in the permeate, and Cf is the concentration of MB in the feed solution.

2.6. Antibacterial Activities and Anti-Adhesive Properties of the Membranes

2.6.1. Antibacterial Activity

The antibacterial activities of the pristine PPSU and PANI-coated PPSU membranes against Gram-negative E. coli ATCC 25922 and Gram-positive S. aureus ATCC 25923 were evaluated using a standard plate counting technique. Luria Bertani (LB) broth was used to prepare each bacterial inoculum. The E. coli and S. aureus suspensions were added to separate wells in a 12-well culture plate. Pieces 2 cm2 in size were cut from each membrane, placed in the wells with the bacterial suspensions, and incubated at 37 °C. After six hours of incubation, 100 μL aliquots were collected from the wells and poured onto fresh LB agar plates. The plates were stored overnight in a bacteriological incubator at 37 °C. The same procedure was performed after 16 hours of incubation in the 12-well culture plate. The number of colonies on each plate was counted, and the percentage of growth inhibition (Br) was calculated using Equation (3).
Br (%) = [(A − B)/A] × 100,
where A is the number of colonies on the pristine membrane (control), and B is the number of colonies on the membrane coated with PANI.

2.6.2. Effects of PANI on Bacterial Cell Morphology and Adhesion

SEM was used to analyze changes in the morphology and adhesion of bacterial cells grown on the PANI-coated and pristine PPSU membranes. The E. coli and S. aureus cultures were incubated with 2 cm2 pristine PPSU and PANI-coated PPSU membrane samples in 12-well culture plates at 37 °C for 12 h. After incubation, each membrane was removed from the plate and washed with phosphate buffered saline (PBS) to remove loosely attached cells. The membranes were then fixed using 4% glutaraldehyde and dehydrated in 30%, 50%, 70%, 90%, and 100% ethanol for 10 min each. The membranes were dried and coated with Au for SEM imaging at an accelerating voltage of 20 kV.

3. Results and Discussion

3.1. Membrane Morphology

Cross-sectional views of the unmodified PPSU and PANI-coated PPSU membranes are shown in Figure 2. The PANI thin film on the surface of the porous PPSU substrate is clearly visible in Figure 2b. The thickness of the PANI film was on the nanometer scale. The PANI film was dense, and its surface was free of defects. The PANI film had a uniform thickness, and it adhered tightly to the skeleton of the PPSU membrane.
Figure 3 shows the effect of the PANI film on the PPSU membrane structure (i.e., surface porosity-view and mean pore diameter). As shown in the results, the PANI/PPSU membrane film had a nanoporous structure with pores less than 5 nm in diameter (Figure 3b). Moreover, the top-surface texture parameters to quantify the magnitude of the peak material volume Vmp, core material Vmc, core void Vvc, and valley void Vvv were calculated by analyzed the SEM image with the ImageJ® software and Mountains® surface imaging software. It can be clearly seen in Figure 3a,b, Vmp (peak material volume) decreased significantly. On the whole, the deposition of the PANI film helped in diminishing irregularities, grooves, and macro voids over the surface of the PPSU membrane.
AFM was performed to examine the surface features of the membranes. The AFM results are shown in Figure 4. The two- and three-dimensional AFM images of the unmodified PPSU membrane in Figure 4a,b showed that its surface contained ridges and valleys. There were also large crater-like structures, deep grooves, small honeycomb-shaped micro-pits, and globular protrusions scattered across the membrane surface. However, the surface topography of the PANI-coated membrane was smoother and less wrinkled. The PANI-coated membrane had a smooth surface with an average roughness (Ra) value of 3.15 nm (Figure 4d), which was notably smaller than that of the unmodified PPSU membrane (4.02 nm). Most of the ridges and valleys were filled in by the PANI film. The AFM results also showed that deposition of the PANI film assisted with the nanometer membrane surface preparation. The surface of the PANI film contained hemispherical nano pillars. These features were highly significant, because they facilitated water permeation and separation.

3.2. Membrane Hydrophilicity

The water contact angle is used to quantify the wetting behavior of membrane surfaces. Membranes with water contact angles below 90° are generally considered hydrophilic, meaning that water spreads easily across the surface. We found that pristine PPSU membranes were relatively hydrophobic with a water contact angle of 65° (Figure 5). The PANI-coated PPSU membrane also demonstrated hydrophilic behavior with a contact angle of 55°. The obtained results were in agreement with those reported previously in the literature. The decrease in the water contact angle due to deposition of the PANI film was consistent with the observations of other researchers. For instance, Huang et al. [34] reported that PANI membranes in their base form were quite hydrophobic. However, when the PANI was doped, the positive charges induced in the polymer chains and the negatively charged counterions increased hydrophilicity. Epstein et al. explained that the protonation of PANI doped with HCl gave rise to a polar conduction band, which led to a metallic state.
Doping increased the concentration of ionic charges in the conducting polymers, which indicated that intermolecular attraction between water and doped PANI would be stronger [35,36,37]. Doping has great potential for tuning the surface properties of PANI. It is therefore surprising that dopants, such as HCl and H2SO4, do not react chemically with the PANI polymer. Rather, they are in close proximity to the PANI polymer main chains. Depending on the type of dopant and its polarity, the presence of ionic charges on the PANI surface make it more hydrophilic. In addition, intermolecular hydrogen bonds formed between PANI and H2O, which strengthened intermolecular interactions between PANI and water. The combination of these factors made the surface of the PANI-coated PPSU membrane more hydrophilic [38,39].

3.3. Zeta Potentials of the Membrane Surfaces

The zeta potential is a measure of the electrical charge on a material surface, and its magnitude is an important measure of membrane fouling, wettability, and the rejection of charged and uncharged solutes. Zeta potential is plotted as a function of pH for both membranes in Figure 6. The zeta potentials were calculated from the streaming potentials, which were measured using an electrokinetic analyzer.
The unmodified PPSU membrane had a zeta potential (ζ) of −10.5 mV. The zeta potential of the PANI-coated PPSU membrane shifted from −10.5 to −1.7 mV as the pH increased from 2.5 to 7.5. This could be attributed to the presence of –NH groups in the positively charged PANI polymer chains on the modified membrane surface. Positively charged groups, such as amino groups, contribute to a decrease in the magnitude of ζ. In other words, they cause a positive shift in the zeta potential. The pHiep values of the PANI-coated membrane and the unmodified PPSU membrane were 5.2 and 3.4, respectively. The PANI-coated PPSU membrane had a higher pHiep value due to the large number of –NH groups in the cationic PANI polymer chains.

3.4. Water Permeability and Rejection of the MB Dye

The contact angle on the unmodified PPSU membrane (65°) indicated that it was less hydrophilic than the PANI-coated PPSU membrane, which had a contact angle of 55°. The more hydrophilic nature of the PANI-coated membrane led to stronger interactions with water, which favored an increase in the permeability of the PANI-coated PPSU membrane to water (Figure 7).
The increased permeability could be attributed to the nanometer-scale thickness of the PANI film, which significantly decreased the resistance of the membrane to flowing water. These results were consistent with those reported previously in the literature. Ahmad et al. reported on PANI nanoparticles that enhanced water permeability and improved the anti-fouling performance of membranes, which was due to an increase in hydrophilicity. Moreover, in the literature, researchers demonstrated that PANI–H2O complexes formed as a result of H–O----H–N and C–N----H–O intermolecular hydrogen bond formation [38,39,40]. This strengthened the interaction between PANI and water molecules, which resulted in high water permeation.
In terms of membrane rejection efficacy, the performance of the PANI-coated PPSU membrane was excellent. It rejected over 90% of the MB dye (Figure 8). These results could be interpreted in two ways. The presence of PANI molecules on the membrane surface led to a positive shift in the zeta potential from −10.5 to −1.7 mV, which increased the repulsive force between PANI molecules and the MB dye. The size exclusion mechanism was more dominant based on the porosity of the membrane surface [41,42,43]. The sizes of the pores in the PANI-coated PPSU membrane were in the nanoscale range, which increased rejection efficacy. Overall properties of developed PANI-coated PPSU membrane shown in Table 1.

3.5. Antibacterial Activities of the Membranes

The antimicrobial activity of pristine PANI and PANI nanocomposites, including PANI-Ag, PANI-Au, PANI-Ag-Au [44,45], PANI/PVA/Ag [46], PANI/Ag-Pt, PANI/Pt, PANI/Pt-Pd [47,48], CoFe2O4/PANI/Ag [49], Cu/PANI [50], and PBT-g-MA/PANI [51], against streptococci, Bacillus subtilis, staphylococci, E. coli, Klebsiella sp., Pseudomonas aeruginosa, Salmonella, and Shigella, is well documented in the biomedical literature. However, few studies have focused on biofouling of PANI composite membranes and their application for ultrafiltration, desalinization, and wastewater treatment. Razali et al. [52] reported that PANI nanoparticles blended with PES membranes and improved both biofouling performance and antibacterial activity. To the best of our knowledge, no reports on the antibacterial activities of PANI-coated PPSU membranes against E. coli and S. aureus have been published. E. coli and S. aureus were used in this study, because these strains are generally used as biological indicators to assess water contamination [40,50].
PANI nanoparticles served as hydrophilic polymeric materials in this study, and we deposited them on a PPSU membrane. A new membrane formed as PANI was deposited on the PPSU support, which had enhanced biofouling resistance and antimicrobial properties for water purification. The antibacterial activities of a pristine PPSU membrane sample and a PANI-coated PPSU membrane sample against E. coli are shown in Figure 9. The activities of both types of membrane against S. aureus are shown in Figure 10. There were many more bacterial colonies on the pristine PPSU membranes, which did not exhibit antibacterial activities.
The PANI-coated PPSU membrane had superior antibacterial activity, which inhibited attachment and growth of the bacteria. Similar results were reported for PES/PANI membranes against E. coli and Bacillus sp. [52]. Based on our calculated growth inhibition (Br) values, the PANI-coated PPSU membrane reduced the growth of E. coli by 63.5% within six hours. Within 16 hours, the PANI-coated PPSU membrane reduced E. coli growth by 95.2%. The Br values of the PANI-coated PPSU membrane against S. aureus after six and sixteen hours of exposure were 70.6% and 88.0%, respectively.

3.6. Effects of PANI Deposition on the Morphology and Adhesion of Model Bacterial Cells

SEM analysis was performed to investigate the effects of the PANI film on the morphology and adhesion of E. coli and S. aureus cells after 12 h and 24 h of incubation. The SEM images of pristine PPSU membranes incubated with E. coli and S. aureus showed smooth surfaces with compact and intact cell walls and membranes (Figure 11). In contrast, the surface morphologies of both E. coli and S. aureus cells grown on PANI-coated PPSU membranes were irregular and abnormal. PANI restricted the attachment and colonization of the bacteria to a greater extent (Figure 11). The cell walls of E. coli were severely damaged with a large number of visible high degree indentations and cavities. Collapse of the indentations and cavities ruptured the cytoplasmic membranes, resulting in leakage of the cytoplasmic contents and solutes. Bogdanović et al. [50] reported that the death of E. coli cells following treatment with Cu/PANI was caused by the direct rupture of bacterial cell membranes.
It has been reported that the effect of PANI coatings on Gram-positive S. aureus differs from their effect on E. coli cells. The S. aureus cells grown on pristine PPSU were typically spherical in shape with intact cell walls and no damage. However, cells on the PANI-coated PPSU membrane were damaged. Their surfaces were rougher and contained cavities. Although the cell membranes did not collapse, significantly fewer cells grew on the PANI-coated PPSU membrane. The colony counting results and SEM data clearly showed that the PANI-coated PPSU membrane was more effective against Gram-negative E. coli than Gram-positive S. aureus. Similar results were reported by Dhivya et al. [53]. This may be have been due to differences between the cell wall structures of the bacteria. The cell walls of Gram-positive bacteria are comprised of complex, rigid, and thick (20–80 nm) peptidoglycan layers that provide protection and few anchoring sites for PANI chains [53]. In contrast, the cell walls of Gram-negative bacteria consist of thin (7–8 nm) peptidoglycan layers and negatively charged lipopolysaccharides that attract PANI. Dhivya et al. [53] reported that PANI chains with positively charged amino groups bonded and anchored to negatively charged lipopolysaccharides and damaged the cell membranes, which was due to changes in the potential gradient across the ion channels [53].
The exact mode of PANI activity is not clear, but it has been reported that antimicrobial activity against various types of bacteria depends on surface hydrophilicity [54], electrostatic interactions [55], the presence of amino groups [51,56], direct physical contact, and high molecular weight. PANI increases the interfacial area between bacteria and nanocomposites and the length of the polymer chains. PANI and PANI nanocomposites attach and anchor to bacterial cell walls, which disrupts their integrity and permeability. Gizdavic-Nikolaidis et al. [57] proposed that the disruption of cell walls and leakage of critical cytoplasmic contents caused Gram-positive and Gram-negative bacteria to die. This was attributed to direct cationic binding of PANI to components in the cell walls due to electrostatic interactions.

4. Conclusions

In this study, a nanofiltration membrane was fabricated by depositing a PANI film on a PPSU substrate membrane. The PANI coating was a potent separation enhancer with powerful antimicrobial activity. The deposited PANI film led to significant changes, including a fine-tuned nanometer pore size and rejection of over 90% of MB dye. The PANI coating also enhanced surface properties, which was indicated by greater hydrophilicity and a shift in the zeta potential from −10 to −1.7 mV. The PANI-coated membrane displayed a permeance of 20 L·m−2·h−1·bar−1. This was because the ~200 nm thick PANI film provided low-resistance transport channels, which enhanced membrane permeability. The PANI film also made the PPSU membrane more resistant to bacteria and significantly inhibited the growth of E. coli.

Author Contributions

J.A. and A.K.S. planned the scientific idea and designed the experiments. J.A., A.K.S. and F.A.A.A. developed the methodology, prepared and characterized the membranes, and performed the experiments. M.A.A. accomplished the antimicrobial study of the membranes. M.A. supervised the research team. J.A., M.A.A. and A.K.S. analyzed and interpreted all the data and wrote the manuscript. All authors contributed to and proofread the manuscript and agreed to the published version of the manuscript.

Funding

The authors extend their appreciation to the Deputyship for Research & Innovation, “Ministry of Education” in Saudi Arabia for funding this research work through the project number IFKSURG-1439-085.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Acknowledgments

The authors thank the Deanship of Scientific Research and RSSU at King Saud University for their technical support.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Lau, W.J.; Ismail, A.F.; Misdan, N.; Kassim, M.A. A recent progress in thin film composite membrane: A review. Desalination 2012, 287, 190–199. [Google Scholar] [CrossRef] [Green Version]
  2. Le, N.L.; Nunes, S.P. Materials and membrane technologies for water and energy sustainability. Sustain. Mater. Technol. 2016, 7, 1–28. [Google Scholar] [CrossRef] [Green Version]
  3. Pandey, N.; Shukla, S.K.; Singh, N.B. Water purification by polymer nanocomposites: An overview. Nanocomposites 2017, 3, 47–66. [Google Scholar] [CrossRef]
  4. Mokhena, T.C.; Luyt, A.S. Development of multifunctional nano/ultrafiltration membrane based on a chitosan thin film on alginate electrospun nanofibres. J. Clean. Prod. 2017, 156, 470–479. [Google Scholar] [CrossRef]
  5. Abou Hammad, A.B.; Hemdan, B.A.; El Nahrawy, A.M. Facile synthesis and potential application of Ni0.6Zn0.4Fe2O4 and Ni0.6Zn0.2Ce0.2Fe2O4 magnetic nanocubes as a new strategy in sewage treatment. J. Environ. Manage. 2020, 270, 110816. [Google Scholar] [CrossRef]
  6. Shukla, A.K.; Alam, J.; Ali, F.A.A.; Alhoshan, M. Efficient soluble anionic dye removal and antimicrobial properties of ZnO embedded-polyphenylsulfone membrane. Water Environ. J. 2020, 0, 1–15. [Google Scholar] [CrossRef]
  7. Richards, H.L.; Baker, P.G.L.; Iwuoha, E. Metal Nanoparticle Modified Polysulfone Membranes for Use in Wastewater Treatment: A Critical Review. J. Surf. Eng. Mater. Adv. Technol. 2012, 2, 183–193. [Google Scholar] [CrossRef] [Green Version]
  8. Phelane, L.; Muya, F.N.; Richards, H.L.; Baker, P.G.L.; Iwuoha, E.I. Polysulfone Nanocomposite Membranes with improved hydrophilicity. Electrochim. Acta 2014, 128, 326–335. [Google Scholar] [CrossRef]
  9. Kang, G.; Cao, Y. Application and modification of poly(vinylidene fluoride) (PVDF) membranes—A review. J. Memb. Sci. 2014, 463, 145–165. [Google Scholar] [CrossRef]
  10. Shukla, A.K.; Alam, J.; Rahaman, M.; Alrehaili, A.; Alhoshan, M.; Aldalbahi, A. A Facile Approach for Elimination of Electroneutral/Anionic Organic Dyes from Water Using a Developed Carbon-Based Polymer Nanocomposite Membrane. Water. Air. Soil Pollut. 2020, 231. [Google Scholar] [CrossRef]
  11. Rana, D.; Matsuura, T. Surface modifications for antifouling membranes. Chem. Rev. 2010, 110, 2448–2471. [Google Scholar] [CrossRef] [PubMed]
  12. Shin, D.H.; Kim, N.; Lee, Y.T. Modification to the polyamide TFC RO membranes for improvement of chlorine-resistance. J. Memb. Sci. 2011, 376, 302–311. [Google Scholar] [CrossRef]
  13. Dadashi Firouzjaei, M.; Arabi Shamsabadi, A.; Aghapour Aktij, S.; Seyedpour, S.F.; Sharifian Gh., M.; Rahimpour, A.; Rabbani Esfahani, M.; Ulbricht, M.; Soroush, M. Exploiting Synergetic Effects of Graphene Oxide and a Silver-Based Metal−Organic Framework To Enhance Antifouling and Anti- Biofouling Properties of Thin-Film Nanocomposite Membranes. ACS Appl. Mater. Interfaces 2018, 10, 42967–42978. [Google Scholar] [CrossRef] [PubMed]
  14. Wang, J.; Wang, Y.; Zhang, Y.; Uliana, A.; Zhu, J.; Liu, J.; Van Der Bruggen, B. Zeolitic Imidazolate Framework/Graphene Oxide Hybrid Nanosheets Functionalized Thin Film Nanocomposite Membrane for Enhanced Antimicrobial Performance. ACS Appl. Mater. Interfaces 2016, 8, 25508–25519. [Google Scholar] [CrossRef] [PubMed]
  15. Liu, G.; Jin, W.; Xu, N. Graphene-based membranes. Chem. Soc. Rev. 2015, 44, 5016–5030. [Google Scholar] [CrossRef]
  16. Zhu, S.; Shi, M.; Zhao, S.; Wang, Z.; Wang, J.; Wang, S. Preparation and characterization of a polyethersulfone/polyaniline nanocomposite membrane for ultrafiltration and as a substrate for a gas separation membrane. RSC Adv. 2015, 5, 27211–27223. [Google Scholar] [CrossRef]
  17. Guo, J.; Kim, J. Modifications of polyethersulfone membrane by doping sulfated-TiO2 nanoparticles for improving anti-fouling property in wastewater treatment. RSC Adv. 2017, 7, 33822–33828. [Google Scholar] [CrossRef] [Green Version]
  18. Fei, F.; Le Phuong, H.A.; Blanford, C.F.; Szekely, G. Tailoring the Performance of Organic Solvent Nanofiltration Membranes with Biophenol Coatings. ACS Appl. Polym. Mater. 2019, 1, 452–460. [Google Scholar] [CrossRef]
  19. Li, G.; Liu, B.; Bai, L.; Shi, Z.; Tang, X.; Wang, J.; Liang, H.; Zhang, Y.; Van der Bruggen, B. Improving the performance of loose nanofiltration membranes by poly-dopamine/zwitterionic polymer coating with hydroxyl radical activation. Sep. Purif. Technol. 2020, 238, 116412. [Google Scholar] [CrossRef]
  20. Shukla, A.K.; Alam, J.; Alhoshan, M.; Dass, L.A.; Muthumareeswaran, M.R. Development of a nanocomposite ultrafiltration membrane based on polyphenylsulfone blended with graphene oxide. Sci. Rep. 2017, 7, 41976–41987. [Google Scholar] [CrossRef] [Green Version]
  21. Wang, Y.; Górecki, R.P.; Stamate, E.; Norrman, K.; Aili, D.; Zuo, M.; Guo, W.; Hélix-Nielsen, C.; Zhang, W. Preparation of super-hydrophilic polyphenylsulfone nanofiber membranes for water treatment. RSC Adv. 2019, 9, 278–286. [Google Scholar] [CrossRef] [Green Version]
  22. Bhat, S.A.; Zafar, F.; Mondal, A.H.; Mirza, A.U.; Rizwanul Haq, Q.M.; Nishat, N. Efficient removal of Congo red dye from aqueous solution by adsorbent films of polyvinyl alcohol/melamine-formaldehyde composite and bactericidal effects. J. Clean. Prod. 2020, 255, 120062. [Google Scholar] [CrossRef]
  23. Alam, J.; Dass, L.A.; Alhoshan, M.S.; Mohammad, A.W. Advances in Membrane Development Based on Electrically Conducting Polymers. Adv. Polym. Technol. 2012, 32, E189–E197. [Google Scholar] [CrossRef]
  24. Additive, S.P.; Mcverry, B.T.; Temple, J.A.T.; Huang, X.; Marsh, K.L.; Hoek, E.M.V.; Kaner, R.B. Fabrication of Low-Fouling Ultra fi ltration Membranes Using a Hydrophilic, Self-Doping Polyaniline Additive. Chem. Mater. 2013, 25, 3597–3602. [Google Scholar]
  25. Guillen, G.R.; Farrell, T.P.; Kaner, R.B.; Hoek, E.M.V. Pore-structure, hydrophilicity, and particle filtration characteristics of polyaniline–polysulfone ultrafiltration membranes. J. Mater. Chem. 2010, 20, 4621. [Google Scholar] [CrossRef]
  26. Sairam, M.; Nataraj, S.K.; Aminabhavi, T.M.; Roy, S.; Madhusoodana, C.D. Polyaniline membranes for separation and purification of gases, liquids, and electrolyte solutions. Sep. Purif. Rev. 2006, 35, 249–283. [Google Scholar] [CrossRef]
  27. Zhao, S.; Wang, Z.; Wei, X.; Zhao, B.; Wang, J.; Yang, S.; Wang, S. Performance improvement of polysulfone ultrafiltration membrane using PANiEB as both pore forming agent and hydrophilic modifier. J. Memb. Sci. 2011, 385–386, 251–262. [Google Scholar] [CrossRef]
  28. Zhou, X.; Zhang, Z.; Men, X.; Yang, J.; Xu, X.; Zhu, X.; Xue, Q. Fabrication of superhydrophobic polyaniline films with rapidly switchable wettability. Appl. Surf. Sci. 2011, 258, 285–289. [Google Scholar] [CrossRef]
  29. Bhadra, S.; Khastgir, D.; Singha, N.K.; Lee, J.H. Progress in preparation, processing and applications of polyaniline. Prog. Polym. Sci. 2009, 34, 783–810. [Google Scholar] [CrossRef]
  30. Leng, W.; Zhou, S.; Gu, G.; Wu, L. Wettability switching of SDS-doped polyaniline from hydrophobic to hydrophilic induced by alkaline/reduction reactions. J. Colloid Interface Sci. 2012, 369, 411–418. [Google Scholar] [CrossRef]
  31. Fan, Z.; Wang, Z.; Duan, M.; Wang, J.; Wang, S. Preparation and characterization of polyaniline/polysulfone nanocomposite ultrafiltration membrane. J. Memb. Sci. 2008, 310, 402–408. [Google Scholar] [CrossRef]
  32. Rong, G.; Zhou, D.; Pang, J. Preparation of high-performance antifouling polyphenylsulfone ultrafiltration membrane by the addition of sulfonated polyaniline. J. Polym. Res. 2018, 25, 66. [Google Scholar] [CrossRef]
  33. Batrinescu, G.; Constantin, M.A.; Cuciureanu, A.; Nechifor, G. Polysulfone–Polyaniline-Type Membranes Obtained in aSteady-State System: Structural and HydrodynamicCharacteristics. Polym. Eng. Sci. 2014, 54, 1640–1647. [Google Scholar] [CrossRef]
  34. Huang, S.-C.; Ball, I.J.; Kaner, R.B. Polyaniline membranes for pervaporation of carboxylic acids and water. Macromolecules 1998, 31, 5456–5464. [Google Scholar] [CrossRef]
  35. Yue, J.; Epstein, A.J. XPS study of self-doped conducting polyaniline and parent systems. Macromolecules 1991, 24, 4441–4445. [Google Scholar] [CrossRef]
  36. Epstein, A.J.; Ginder, J.M.; Zuo, F.; Bigelow, R.W.; Woo, H.-S.; Tanner, D.B.; Richter, A.F.; Huang, W.-S.; MacDiarmid, A.G. Insulator-to-metal transition in polyaniline. Synth. Met. 1987, 18, 303–309. [Google Scholar] [CrossRef] [Green Version]
  37. Luo, Y.; Guo, R.; Li, T.; Li, F.; Liu, Z.; Zheng, M.; Wang, B.; Yang, Z.; Luo, H.; Wan, Y. Application of Polyaniline for Li-Ion Batteries, Lithium–Sulfur Batteries, and Supercapacitors. ChemSusChem 2019, 12, 1591–1611. [Google Scholar] [CrossRef]
  38. Zheng, W.; Angelopoulos, M.; Epstein, A.J.; MacDiarmid, A.G. Experimental evidence for hydrogen bonding in polyaniline: Mechanism of aggregate formation and dependency on oxidation state. Macromolecules 1997, 30, 2953–2955. [Google Scholar] [CrossRef]
  39. Zhang, Y.; Duan, Y.; Liu, J. The Effect of Intermolecular Hydrogen Bonding on the Polyaniline Water Complex. J. Clust. Sci. 2017, 28, 1071–1081. [Google Scholar] [CrossRef] [Green Version]
  40. Nahrawy, A.M.E.; Bakr, A.M.; Hammad, A.B.A.; Hemdan, B.A. High performance of talented copper/magneso-zinc titanate nanostructures as biocidal agents for inactivation of pathogens during wastewater disinfection. Appl. Nanosci. 2020, 10, 3585–3601. [Google Scholar] [CrossRef]
  41. Jiang, M.; Ye, K.; Lin, J.; Zhang, X.; Ye, W.; Zhao, S.; Van der Bruggen, B. Effective dye purification using tight ceramic ultrafiltration membrane. J. Memb. Sci. 2018, 566, 151–160. [Google Scholar] [CrossRef]
  42. Jin, P.; Yuan, S.; Zhang, G.; Zhu, J.; Zheng, J.; Luis, P.; Van der Bruggen, B. Polyarylene thioether sulfone/sulfonated sulfone nanofiltration membrane with enhancement of rejection and permeability via molecular design☆. J. Memb. Sci. 2020, 608, 118241. [Google Scholar] [CrossRef]
  43. Abdulhamid, M.A.; Park, S.-H.; Vovusha, H.; Akhtar, F.H.; Ng, K.C.; Schwingenschlögl, U.; Szekely, G. Molecular engineering of high-performance nanofiltration membranes from intrinsically microporous poly(ether-ether-ketone). J. Mater. Chem. A 2020, 8, 24445–24454. [Google Scholar] [CrossRef]
  44. Boomi, P.; Prabu, H.G.; Manisankar, P.; Ravikumar, S. Study on antibacterial activity of chemically synthesized PANI-Ag-Au nanocomposite. Appl. Surf. Sci. 2014, 300, 66–72. [Google Scholar] [CrossRef]
  45. Tamboli, M.S.; Kulkarni, M.V.; Patil, R.H.; Gade, W.N.; Navale, S.C.; Kale, B.B. Nanowires of silver-polyaniline nanocomposite synthesized via in situ polymerization and its novel functionality as an antibacterial agent. Colloids Surfaces B Biointerfaces 2012, 92, 35–41. [Google Scholar] [CrossRef]
  46. Ghaffari-Moghaddam, M.; Eslahi, H. Synthesis, characterization and antibacterial properties of a novel nanocomposite based on polyaniline/polyvinyl alcohol/Ag. Arab. J. Chem. 2014, 7, 846–855. [Google Scholar] [CrossRef] [Green Version]
  47. Boomi, P.; Prabu, H.G.; Mathiyarasu, J. Synthesis, characterization and antibacterial activity of polyaniline/Pt-Pd nanocomposite. Eur. J. Med. Chem. 2014, 72, 18–25. [Google Scholar] [CrossRef]
  48. Boomi, P.; Prabu, H.G.; Mathiyarasu, J. Synthesis and characterization of polyaniline/Ag-Pt nanocomposite for improved antibacterial activity. Colloids Surfaces B Biointerfaces 2013, 103, 9–14. [Google Scholar] [CrossRef]
  49. Kooti, M.; Kharazi, P.; Motamedi, H. Preparation, characterization, and antibacterial activity of CoFe2O4/polyaniline/Ag nanocomposite. J. Taiwan Inst. Chem. Eng. 2014, 45, 2698–2704. [Google Scholar] [CrossRef]
  50. Bogdanović, U.; Vodnik, V.; Mitrić, M.; Dimitrijević, S.; Škapin, S.D.; Žunič, V.; Budimir, M.; Stoiljković, M. Nanomaterial with High Antimicrobial Efficacy—Copper/Polyaniline Nanocomposite. ACS Appl. Mater. Interfaces 2015, 7, 1955–1966. [Google Scholar] [CrossRef]
  51. Wu, C. Preparation and characterization of an aromatic polyester/polyaniline composite and its improved counterpart. Express Polym. Lett. 2012, 6, 26–40. [Google Scholar] [CrossRef]
  52. Razali, N.F.; Mohammad, A.W.; Hilal, N. Effects of polyaniline nanoparticles in polyethersulfone ultrafiltration membranes: Fouling behaviours by different types of foulant. J. Ind. Eng. Chem. 2014, 20, 3134–3140. [Google Scholar] [CrossRef]
  53. Dhivya, C.; Vandarkuzhali, S.A.A.; Radha, N. Antimicrobial activities of nanostructured polyanilines doped with aromatic nitro compounds. Arab. J. Chem. 2019, 12, 3785–3798. [Google Scholar] [CrossRef] [Green Version]
  54. Prabhakar, P.K.; Raj, S.; Anuradha, P.R.; Sawant, S.N.; Doble, M. Biocompatibility studies on polyaniline and polyaniline–silver nanoparticle coated polyurethane composite. Colloids Surfaces B Biointerfaces 2011, 86, 146–153. [Google Scholar] [CrossRef]
  55. Liang, X.; Sun, M.; Li, L.; Qiao, R.; Chen, K.; Xiao, Q.; Xu, F. Preparation and antibacterial activities of polyaniline/Cu0.05Zn0.95O nanocomposites. Dalt. Trans. 2012, 41, 2804–2811. [Google Scholar] [CrossRef]
  56. Wu, C.-S. Aliphatic–aromatic polyester–polyaniline composites: Preparation, characterization, antibacterial activity and conducting properties. Polym. Int. 2012, 61, 1556–1563. [Google Scholar] [CrossRef]
  57. Gizdavic-Nikolaidis, M.R.; Bennett, J.R.; Swift, S.; Easteal, A.J.; Ambrose, M. Broad spectrum antimicrobial activity of functionalized polyanilines. Acta Biomater. 2011, 7, 4204–4209. [Google Scholar] [CrossRef]
Membranes 11 00025 g001 550
Figure 1. Schematic diagram of PANI thin film preparation via oxidative polymerization.
Figure 1. Schematic diagram of PANI thin film preparation via oxidative polymerization.
Membranes 11 00025 g001
Membranes 11 00025 g002 550
Figure 2. Cross-sectional scanning electron microscope (SEM) images of (a) the Poly (phenyl sulfone) (PPSU) support and (b) the PANI-coated PPSU membrane.
Figure 2. Cross-sectional scanning electron microscope (SEM) images of (a) the Poly (phenyl sulfone) (PPSU) support and (b) the PANI-coated PPSU membrane.
Membranes 11 00025 g002
Membranes 11 00025 g003 550
Figure 3. The surface porosity-view of the membranes (a) PPSU support, (b) PANI-deposited PPSU and denoted as peak material volume (Vmp), valley void volume (Vvv), core material volume (Vmc), and core void volume (Vvc).
Figure 3. The surface porosity-view of the membranes (a) PPSU support, (b) PANI-deposited PPSU and denoted as peak material volume (Vmp), valley void volume (Vvv), core material volume (Vmc), and core void volume (Vvc).
Membranes 11 00025 g003
Membranes 11 00025 g004 550
Figure 4. Representative 2D and 3D AFM images of the surfaces of (a,b) the PPSU support and (c,d) the PANI-coated PPSU membrane.
Figure 4. Representative 2D and 3D AFM images of the surfaces of (a,b) the PPSU support and (c,d) the PANI-coated PPSU membrane.
Membranes 11 00025 g004
Membranes 11 00025 g005 550
Figure 5. Water contact angles of the membranes.
Figure 5. Water contact angles of the membranes.
Membranes 11 00025 g005
Membranes 11 00025 g006 550
Figure 6. Zeta potentials of the PPSU support membrane and the PANI-coated PPSU membrane as a function of pH.
Figure 6. Zeta potentials of the PPSU support membrane and the PANI-coated PPSU membrane as a function of pH.
Membranes 11 00025 g006
Membranes 11 00025 g007 550
Figure 7. Permeability of the membranes to pure water as a function of pressure.
Figure 7. Permeability of the membranes to pure water as a function of pressure.
Membranes 11 00025 g007
Membranes 11 00025 g008 550
Figure 8. Rejection of the MB dye by the PPSU support membrane and the PANI-coated PPSU membrane.
Figure 8. Rejection of the MB dye by the PPSU support membrane and the PANI-coated PPSU membrane.
Membranes 11 00025 g008
Membranes 11 00025 g009 550
Figure 9. Antimicrobial properties of pristine PPSU and PANI-coated PPSU membranes assessed by plate counting. Plates incubated after the growth of E. coli on a pristine PPSU membrane for (a) 6 h and (c) 16 h. Plates incubated after the growth of E. coli on a PANI-coated membrane for (b) 6 h and (d) 16 h.
Figure 9. Antimicrobial properties of pristine PPSU and PANI-coated PPSU membranes assessed by plate counting. Plates incubated after the growth of E. coli on a pristine PPSU membrane for (a) 6 h and (c) 16 h. Plates incubated after the growth of E. coli on a PANI-coated membrane for (b) 6 h and (d) 16 h.
Membranes 11 00025 g009
Membranes 11 00025 g010 550
Figure 10. Antimicrobial properties of pristine and PANI-coated PPSU membranes assessed by plate counting. Plates incubated after the growth of S. aureus on a pristine PPSU membrane for (a) 6 h and (c) 16 h. Plates incubated after the growth of S. aureus on a PANI-coated PPSU membrane for (b) 6 h and (d) 16 h.
Figure 10. Antimicrobial properties of pristine and PANI-coated PPSU membranes assessed by plate counting. Plates incubated after the growth of S. aureus on a pristine PPSU membrane for (a) 6 h and (c) 16 h. Plates incubated after the growth of S. aureus on a PANI-coated PPSU membrane for (b) 6 h and (d) 16 h.
Membranes 11 00025 g010
Membranes 11 00025 g011 550
Figure 11. SEM images of features in at 5 kV, 1000 X, 6.5 WD collected to evaluate adhesion and the morphologies of E. coli and S. aureus cells on pristine PPSU and PANI-coated PPSU membranes after incubation for 6 h and 12 h.
Figure 11. SEM images of features in at 5 kV, 1000 X, 6.5 WD collected to evaluate adhesion and the morphologies of E. coli and S. aureus cells on pristine PPSU and PANI-coated PPSU membranes after incubation for 6 h and 12 h.
Membranes 11 00025 g011
Table
Table 1. Properties of the prepared membranes in this study.
Table 1. Properties of the prepared membranes in this study.
MembranesIsoelectric Point (pHiep)Water Permeability
(L·m−2·h−1·bar−1)		Dye Rejection
(%)
PPSU membrane3.420.3 ± 33 ± 0.5
PANI-coated PPSU membrane5.253.5 ± 596 ± 2
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Alam, J.; Shukla, A.K.; Ansari, M.A.; Ali, F.A.A.; Alhoshan, M. Dye Separation and Antibacterial Activities of Polyaniline Thin Film-Coated Poly(phenyl sulfone) Membranes. Membranes 2021, 11, 25. https://doi.org/10.3390/membranes11010025

AMA Style

Alam J, Shukla AK, Ansari MA, Ali FAA, Alhoshan M. Dye Separation and Antibacterial Activities of Polyaniline Thin Film-Coated Poly(phenyl sulfone) Membranes. Membranes. 2021; 11(1):25. https://doi.org/10.3390/membranes11010025

Chicago/Turabian Style

Alam, Javed, Arun Kumar Shukla, Mohammad Azam Ansari, Fekri Abdulraqeb Ahmed Ali, and Mansour Alhoshan. 2021. "Dye Separation and Antibacterial Activities of Polyaniline Thin Film-Coated Poly(phenyl sulfone) Membranes" Membranes 11, no. 1: 25. https://doi.org/10.3390/membranes11010025

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.