Next Article in Journal
Structure and Performance of Bentonite-Enhanced Superabsorbent Gels for Water Absorption and Methylene Blue Adsorption
Previous Article in Journal
Gelatin–Chitosan–PVA Hydrogels Incorporating Trichoderma and Their Application in the Control of Phytopathogens
Previous Article in Special Issue
Metallogels as Hybrid Metal-Organic Soft Materials: Classification, Fabrication Pathways and Functional Applications
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Nanostructured Hydrogels: A Method to Prevent Biofilms on Implantable Medical Devices

by
Hasani G. Jayasinghe
1,†,
Ujith S. K. Madduma-Bandarage
2,† and
Sundar V. Madihally
3,*
1
Math, Business, Science & Technology Division, University of New Mexico-Gallup, 705 Gurley Ave., Gallup, NM 87301, USA
2
Department of Chemistry, New Mexico Institute of Mining and Technology, Lopez Hall 221, 801 Leroy Place, Socorro, NM 87801, USA
3
School of Chemical Engineering, Oklahoma State University, 420 Engineering North, Stillwater, OK 74078, USA
*
Author to whom correspondence should be addressed.
These authors contributed equally to this work.
Gels 2026, 12(2), 146; https://doi.org/10.3390/gels12020146
Submission received: 8 January 2026 / Revised: 30 January 2026 / Accepted: 2 February 2026 / Published: 5 February 2026
(This article belongs to the Special Issue Polymeric Hydrogels for Biomedical Application (2nd Edition))

Abstract

Microbial biofilms pose significant health risks by causing infections associated with prosthetic and indwelling medical devices. Factors such as the high tolerance levels of biofilm microorganisms to antibiotics and the inability of antimicrobial agents to penetrate the biofilm matrix render antibiotic-based treatment methods ineffective against biofilm-related infections. Surfaces patterned with nanoscale topographical features have shown promising results in controlling the attachment of microorganisms. Therefore, nanopatterning of surfaces provides an excellent alternative to the existing antibiotic-based therapies. There are many techniques, such as photolithography and soft lithography, for patterning polymer or metal surfaces. However, depending on the cost, toxicity, feature size, and material compatibility, these methods have limitations. Although hydrogels have garnered special interest as biomaterials due to their biocompatibility and resemblance to the natural biological environment, hydrogels with surface nanopatterns have not been widely investigated as anti-biofouling materials. The applicability of hydrogels in biomedical applications and the importance of inhibiting microbial biofilms underscore the need for further research into the manufacturing of nanoengineered hydrogels with diverse topographical features. In this review, we discuss how nanostructured hydrogels inhibit biofilm formation. Further, we discuss nanopatterning methods, their limitations, advantages, and disadvantages. This article also highlights the current state of research on nanostructured hydrogels and associated challenges.

1. Introduction

Microorganisms such as bacteria and fungi naturally exist in two distinct states: planktonic cells or sessile aggregates (biofilms) [1]. In the planktonic state, microorganisms float freely. In the sessile state, they remain aggregated or attached to a surface, which can be either biological or non-biological. Biofilms can also be found on liquid surfaces, appearing as submerged or floating mats. A microbial biofilm can be defined as a coherent cluster of microbial cells embedded in a matrix and is more tolerant to most antimicrobial agents and host defense systems than the planktonic cells [1]. In sessile biofilms, these microorganisms attach irreversibly to the surface or other cells and secrete extracellular polymeric substances (EPS), including polysaccharides, lipids, proteins, and nucleic acids. The extracellular polymers facilitate the attachment of cells to one another and the formation of a matrix in which the cells remain embedded. In biofilms, multiple colonies of a single species or different species with varying functionalities can aggregate to form dense, organized communities [2]. The cells in the biofilm are genetically and physiologically different from their planktonic counterparts, as these organisms in biofilms exhibit slow growth rates, express genes involved in the production of EPS, and show high tolerance to antimicrobial agents and host defense systems [3,4].
Biofilms can grow on medical devices and implants that stay in the human body for prolonged periods, leading to device failure and/or severe health issues. These biofilm microorganisms are responsible for most chronic persistent infections, such as cystic fibrosis, periodontitis, rhinosinusitis, osteomyelitis, and kidney infections [2,4]. The low susceptibility of these biofilms to antimicrobial agents and the difficulties in penetrating antibiotics through the biofilm matrix render antibiotic-based therapies ineffective for treating biofilm-related diseases, resulting in severe health issues. Therefore, various other strategies have been investigated to prevent the formation of biofilms. Among these approaches, modifying the biomaterial surface with different topographical features has become an attractive option. As the global demand for prosthetics and medical devices is continuously increasing, device-related infections have become a serious issue in the healthcare and biomedical fields [4]. Thus, it creates additional research opportunities to develop biomaterials with improved antimicrobial/antiadhesive properties.
Hydrogels, a type of network polymer that can retain large amounts of water, have been extensively studied for their potential biomedical applications. Additionally, hydrogels are currently utilized in numerous applications as biomaterials. Thus, the formation of biofilms on the hydrogel surface creates problems and limits the use of hydrogels as biomaterials. Therefore, the fabrication of hydrogels that can prevent the formation of biofilms is essential. Nanopatterning has been explored for inhibiting biofilms on various materials, including metals, silicon, and polymers. However, studies investigating nanopatterned hydrogels as anti-biofouling materials are limited.
The antifouling properties of hydrogels have been discussed elsewhere [5]. A review by Takayuki Murosaki et al. detailed how marine sessile organisms avoid using seaweeds and fish as substrates for attachment, as these substrates contain hydrogels [6]. Also, other articles have been published focusing on the fabrication of antifouling surfaces for marine applications [7,8,9]. Here, they highlighted the chemical nature of the hydrogels that prevent attachment, such as the presence of hydroxy and sulfonic groups. Moreover, some articles focused on the antifouling activity of hydrogels against biofilms, particularly those based on nanomaterial-integrated coatings [10] and bioactive antifouling coatings. Another recently published article mentions the use of nanostructured hydrogels as biofouling materials, but it does not delve into nanostructured hydrogels [11]. Since other review articles discuss most other methods for modifying hydrogels to enhance their antifouling performance in detail, we intend this article to provide a comprehensive overview of nanostructured hydrogels, with particular focus on antifouling applications in biomaterials.
Rigid nanopatterned substrates can also facilitate the antifouling activity [12,13]. Although these rigid surfaces exhibit greater mechanical strength than hydrogels, their use in biological applications may be limited. Rigid substrates are more useful for marine or industrial applications [14,15]. Because hydrogels are more compatible with biological surfaces, this review focuses on strategies to enhance hydrogel properties to prevent biofilm formation, specifically through physical modifications. Here, we have discussed surface patterning techniques and their role in preventing microbial attachment. Also, the soft, water-rich structure of hydrogels physically blocks fouling organisms. Furthermore, it is easy to incorporate other modifications, such as nanoparticles to enhance antifouling activity, into hydrogels. However, their limited durability and reduced mechanical strength will limit the range of applications for hydrogels. There is also a current discussion of using hybrid methods to enhance the antifouling properties of materials [14].

2. Biofilms on Medical Devices and Implants

2.1. Formation of Microbial Biofilms

A biofilm progresses through five different stages [3,16] (Figure 1): reversible/irreversible attachment of cells, formation of microbial colonies, formation of 3-dimensional biofilms, maturation, and detachment from the biofilm. Initially, planktonic microorganisms attach loosely to the surface. Initial attachment involves physical interactions such as electrostatic interactions, van der Waals forces, steric interactions, and appendages (pilli or flagella) of the microorganism [17]. Also, macromolecules, such as proteins, adsorb to the surface and form a conditioning layer, facilitating the attachment of microbes. The attached cells then secrete chemicals or extracellular polymeric substances (EPS) to strengthen their attachment to the surface (adhesion) and support attachment to one another (cohesion). The formation of EPS attracts cells and supports the formation of microbial colonies in the second stage. During the third stage, the cells proliferate rapidly to form 3-dimensional, multilayered colonies. These colonies further develop and subsequently reach the fourth stage. Biofilms can adopt different structures, such as flat plaques or mushrooms, depending on the availability of nutrients and other environmental factors [16,18]. The formation of multilayered biofilms also relies on the ability of the bacteria involved to attach to each other [17]. In the fifth stage, cells in the biofilm detach and return to the initial planktonic stage. The cells or cell clusters detach from the biofilm, either actively or passively, and disseminate onto a new surface, forming new colonies.
Attachment to surfaces and the formation of biofilms are advantageous for bacterial cells in many ways [19]. The channels in the EPS layer distribute nutrients and oxygen [20]. Some bacteria acquire metabolites and cofactors directly from the substrate [21,22]. The EPS provides mechanical stability and protection from mechanical damage and shear when attached to non-biological surfaces [23]. On biological surfaces, the extracellular polymeric matrix protects the cells in the biofilms from the host organism’s defense system and antimicrobial agents or antibiotics by acting as a barrier that prevents penetration of those attacking molecules to reach the embedded cells [16,24]. The depletion of nutrients and accumulation of waste in the biofilm cause changes in the microenvironment. Consequently, the cells in biofilms enter a slow-growing state and become less susceptible to the external factors that can attack them [2].

2.2. Biomaterials, Biofilms, and Influence on Human Health

Biofilms can grow on medical devices and implants that dwell in the human body for extended periods. These medical devices and implants include catheters, needles, pacemakers, endotracheal tubes, mechanical heart valves, prosthetic joints, contact lenses, and voice prostheses [16]. These biomaterials can become contaminated by bacteria and other microbes during the surgery or at any time during their stay in the body [4]. The most common types of microorganisms that form biofilms on medical devices are Staphylococcus aureus, Staphylococcus epidermidis, Enterococcus faecalis, Escherichia coli, Streptococcus viridans, Klebsiella pneumoniae, Pseudomonas aeruginosa, Proteus mirabilis, Candida albicans, and Candida tropicalis [16,25]. Table 1 summarizes different types of microorganisms that form biofilms on prosthetic and medical devices.
According to the estimates from the National Institute of Health, biofilms are responsible for more than 80% of microbial infections [42,43]. Biofilms can be formed by a single species (monospecies biofilms) or by a complex community consisting of organisms such as bacteria, fungi, and algae (multispecies biofilms) [44]. Table 2 provides a comparison of different biofilms.
Biofilm-associated infections can involve both Gram-negative and Gram-positive bacteria, e.g., oral cavity, diabetic foot infections, otitis media, and cystic fibrosis [56].
The biofilms grown on indwelling medical devices and implants pose detrimental health issues as they cause infections such as bloodstream infections and urinary tract infections, or device failure [16]. Moreover, cells detached from mature biofilms can spread to other organs, resulting in chronic infections [25]. The biofilm-related diseases include, but are not limited to, cystic fibrosis, otitis media, periodontitis, native valve endocarditis, chronic bacterial prostatitis, rhinosinusitis, osteomyelitis, non-healing chronic wounds, meningitis, kidney infections, and prosthesis and implantable device-related infections [4,17,57,58,59]. Additionally, these microorganisms are responsible for other medical conditions such as chronic inflammation and delayed wound healing, etc. [18,60]. Generally, antibiotics have low efficacy against biofilm-related infections due to decreased susceptibility of the microbes in biofilms to antibiotics and the failure of antimicrobial agents to penetrate the biofilm matrix [61]. Also, antibiotics and their doses selected based on the phenotype of planktonic cells of the pathogen may not effectively treat the biofilm-related diseases due to the different phenotypes of cells that grow in biofilms [2]. The treatment methods for these infections mostly require prolonged antibiotic therapy and/or surgical procedures to replace the infected device. Also, the microorganisms can re-colonize and form biofilms on the new implant or device [62]. The complexity and ineffectiveness of treating biofilm-related infections necessitate exploring alternative strategies to prevent biofilm formation on medical devices and implants.

3. Strategies That Can Prevent the Formation of Biofilms

In general, the methods used to combat biofilms involve different strategies: prevention of adhesion of microbes, disruption of the extracellular matrix of premature biofilms, killing the cells, and degradation of mature biofilms [63,64,65]. The methods that inhibit biofilms on biomaterials, as shown in Figure 2, can be classified as physical, chemical, or biological methods [66,67,68]. These approaches inhibit the formation of biofilms passively or actively [69]. The passive strategies target the prevention of adhesion of microbial cells onto the biomaterial surface without interfering with the biological activities of related microorganisms, whereas the active methods kill the microorganisms [69].
A convenient way to eradicate biofilms on medical devices and prostheses is to prevent the initial attachment of microorganisms onto the biomaterial surface. Attachment of microorganisms onto a biomaterial surface can be interfered with by tailoring the surface properties, such as surface energy, topography, functional groups, hydrophobicity/hydrophilicity, roughness, stiffness, and charge [70,71,72].
The most common surface modification techniques that inhibit biofilms on medical implants include anti-biofouling coatings generated using biomolecules, zwitterionic polymers, hydrophobic polymers, and hydrophilic polymers, or surface grafting [25,71,73,74,75,76,77,78]. Several authors have reviewed these approaches [4,25,70,79], and therefore, are not included in this review.
Various methods used to combat biofilms on biomaterials have advantages and disadvantages. Table 3 summarizes the advantages and disadvantages of these methods [67,80,81,82].

4. Nanotechnology-Based Methods to Prevent the Formation of Biofilms

As an alternative to conventional techniques, nanotechnological methods have been extensively studied for preventing biofilms on biomaterials. The nanotechnology-based approaches mainly include the incorporation of nanoparticles into a biomaterial or the modification of the biomaterial surface with nanoscale topographical features [83].

4.1. Incorporation of Nanoparticles

The use of nanoparticles to combat biofilms has been extensively studied and reviewed recently [3,84,85]. Different types of nanoparticles include metals, metal oxides, lipids, peptides, and polymers or composites of these types [3,86]. Furthermore, these nanoparticles can be categorized as antiadhesive nanoparticles, biocidal nanoparticles, bioactive nanoparticles, reactive oxygen species-releasing nanoparticles, and stimuli-responsive nanoparticles based on their biofilm prevention mechanism [3]. Application of nanoparticle-based therapies to control biofilms has several advantages: successful penetration into the biofilms, preferential delivery of drugs/antibiotics to the target site, controlled delivery of antimicrobial agents for extended periods, delivery of multiple agents for combined treatment, and improved efficacy [58]. Although nanoparticle-based approaches show promising results in controlling microbial biofilms, they also have some drawbacks. For example, the emergence of microbial strains resistant to antimicrobial agents such as silver and copper is the main disadvantage [87,88]. Also, the antimicrobial agents in the storage can be depleted over time, decreasing the effectiveness of the treatment [89].
Mechanisms of biofilm inhibition by nanoparticles include the generation of reactive oxygen species (ROS), the inhibition of quorum sensing, the degradation of the biofilm matrix, and enhanced drug permeability [90]. Nanoparticles accumulated on the bacterial cell membrane increase the bacterial permeability. Moreover, metallic nanoparticles can generate ROS that can cause oxidative damage to cellular components, such as DNA, lipids, and proteins. Metallic ions released from nanoparticles can disrupt DNA replication by reducing intracellular ATP [91].
Nanoparticles also inhibit Quorum Sensing, the molecular communication system essential for colony growth and biofilm development [92]. Table 4 summarizes the mechanisms by which nanoparticles inhibit biofilms.

4.2. Surface Patterning, Nanotopography, and Microbial Attachment

Although the chemical modifications improve the antimicrobial properties of the biomaterial, they may affect the biocompatibility and other favorable properties [106,107]. In contrast, patterning surfaces with different topographical features is a physical modification that does not affect the chemical, physical, or biological properties of the bulk material [108]. However, surface patterns determine the surface properties of the material that control interactions between microorganisms and the material. For instance, the introduction of nanotopographical features alters the surface stiffness, which is crucial for interacting with biological entities, without affecting the bulk chemical properties of the substrate. Therefore, in biomaterials, surface patterning is used to facilitate the integration of host tissues at the implantation site and the synthetic biomaterial for optimum functionality [109].
Since the surface texture determines the surface properties, the attachment of microorganisms on materials with different surface topographical features has been extensively studied [110,111,112,113]. The studies are based on three main categories of surface topographies: irregular or random patterns, regular or defined patterns, and hierarchical structures [110]. Random topographies lack properly defined dimensions. In contrast, regular patterns have clearly defined topographical features. Hierarchical structures contain two or more types of topographical features with varying dimensions.
Numerous studies investigate the attachment of microbes to surfaces lacking well-defined surface features. The surfaces are subjected to various treatments, including chemical etching and mechanical roughening, to alter their properties, including surface energy and roughness. Surface roughness was used as the main parameter to describe the differences between the surfaces [114,115]. In one study [116], nanorough titanium substrates, prepared by the electron beam evaporation technique, exhibit reduced attachment of S. aureus, S. epidermidis, and P. aeruginosa compared to flat controls. The same study revealed that the method used to create nanostructures also plays a vital role in controlling bacterial attachment. Here, the nanotubular and nanotextured titanium substrates generated by the anodization processes increased the bacterial adhesion. Another study [117] reports a correlation between the roughness and the attachment of S. aureus and E. coli onto titania surfaces. In this study, the patterned surface was generated by the supersonic cluster beam deposition method. As the roughness increased from ~16 nm to ~32 nm, the attachment of bacteria and the formation of biofilm were decreased. In another example [118], the titanium surfaces treated to obtain ultra-fine grain sizes promoted the adhesion of S. aureus and P. aeruginosa. Additionally, nanophase titania surfaces with high roughness in the nanometer regime demonstrate the increased attachment of Pseudomonas fluorescens and Pseudomonas putida [119]. Moreover, various studies report that a clear relationship does not exist between bacterial adhesion and the surface roughness of different materials such as glass, stainless steel, and metal oxides [120,121,122,123]. Contradictory results and a poor understanding of how these random topographies affect microbial attachment can be attributed to limitations in evaluating dimensions of random structures, variation in roughness measurements, and physiological differences among the tested bacteria [20,110].
As explained above, surface roughness does not correlate with microbial attachment. Therefore, it is crucial to investigate the attachment of microorganisms onto surfaces with defined structures. Several studies have investigated the attachment of microbes to micro/ nanoengineered surfaces with various topographies, including wells or pits, [112,124] pillars, [89,106,125] protrusions, [108,126] and grooves, [127,128] (Figure 3). These surface topography features at micron and submicron levels show profound effects on the attachment of microorganisms such as bacteria and fungi [126].
Unlike on a flat substrate, the entire surface is not accessible to the cells on a patterned surface. Here, the cells can access only the feature tops; hence, the available surface area for bacterial attachment decreases. The adhesion of Gram-positive, round-shaped S. aureus (~1 μm) and S. epidermidis (~1.5 μm) was significantly decreased when the surface of polyurethane substrates was patterned with nanopillars of diameters ~400–500 nm and heights ~600 nm–700 nm [106]. It is noteworthy that the feature sizes are smaller than the cells; thus, the cells experience reduced surface area, resulting in lower attachment. Similarly, the silica substrates containing circular (diameter 500 nm) or rectangular (1 × 1.5 μm or 1 × 2 μm) wells resulted in low attachment of Gram-negative E. coli (pathogenic and nonpathogenic strains) and P. fluorescens compared to the unpatterned controls [112]. In contrast, Gram-positive Listeria innocua showed attachment patterns similar to those on patterned silica surfaces and on the smooth controls. On the other hand, alumina (ceramic) membranes containing 20 nm and 200 nm pores showed lower attachment of nonpathogenic E. coli strains and L. innocua than the smooth control samples. Pathogenic E. coli and P. fluorescens showed an opposite trend with low attachment on the smooth alumina substrates [112]. The opposing trends confirm that attachment depends on the type of bacteria, the material, and the surface topography. According to the same study, the surface topography influences the morphology of bacterial cells, and the cells exhibited a preferential orientation to maximize the interactions with the substrate [112].
When the surface textures and gaps are smaller than the microbial cells, the entire cells cannot lie on the features or fit into the gap. Instead, the cells align according to the pattern [129] or stay across the trenches connecting neighboring features as a bridge [127]. Therefore, microbes can be preferentially aligned by adjusting the feature size and the gap. For instance, arrays of high-aspect-ratio (HAR) nanoposts generated on epoxy substrates demonstrated a guided alignment of P. aeruginosa cells [89,129]. The bacterial cells were oriented along the posts, normal to the surface, when the spacing between adjacent posts (~0.9 μm) was smaller than the rod-like P. aeruginosa cell (~1.2–1.5 μm). The cells lay on the surface when the spacing was close to the length of a cell. Similarly, E. coli cells preferentially settled down in the spacings or valleys between the square protrusions on poly(dimethyl siloxane) (PDMS) substrates [130]. The cells are positioned in the valleys when the valleys are larger than the protruding feature. The cells stayed on top of the large protrusions (feature size > 20 μm × 20 μm) because the protrusions are large enough to hold the cells [130]. A similar study [124] reports the evaluation of the retention of P. aeruginosa, S. aureus, and C. albicans on silicon wafers coated with titanium substrates. The substrates contained pits of varying diameters (ranging from 0.2 μm to 2 μm). S. aureus (1 μm) showed the highest retention, whereas C. albicans (4 to 5 μm) had the lowest retention. It is clear that the retention of microbes depends on the size of the pit and the size of the cell [130].
Although surface patterns reduce the attachment of microorganisms, the opposite can occur depending on the organism. Ref. [128] and the stiffness of the material [89]. The attachment of E. coli was increased when the PDMS surface was patterned with arrays of microscale hexagonal features (height 2.7 μm and diameter 3 μm) separated by nanoscale trenches (440 nm) [128]. Here, the trenches were too small for the cells to fit into, but the cells used flagella to adhere to the surface. Since flagella can access nanoscale trenches, cells experience a higher surface area on patterned substrates than on flat samples. Consequently, patterned surfaces showed an increased attachment compared to the unpatterned analogues [128]. As well, the aggregation of P. aeruginosa cells was greater on the epoxy substrates containing HAR nanoposts [89]. The high aggregation of cells on a patterned surface can be attributed to the high stiffness of epoxy. Although studies show that stiff surfaces promote microbial attachment, little is known about the mechanosensing of prokaryotic cells [72]. Mechanosensing is the biological ability of cells and organisms to detect and respond to mechanical forces, such as pressure, stretch, and stiffness, in their environment—a well-established and crucial cellular function in eukaryotic cells. A study by Liyun Wang et al. found that surfaces with higher elasticity exhibit greater changes in mechanical stress and strain in the bacterial envelope than lower-elasticity surfaces. Adhesion to higher-elastic surfaces increases cyclic-di-GMP levels, a second messenger used in signal transduction in many bacteria, thereby reducing motility and decreasing detachment [131]. Figure 4 depicts the different orientations of microbial cells that maximize interactions between the cell and the substrate.
Overall, feature size and spacing between features control the attachment of microbes to a surface. The feature size and the gap between structures affect the attachment and ordering of the microbes, as well as the morphology and size of the cells. The cells alter their shapes and adopt various orientations to maximize the interactions with the substrate when attaching to the textured surfaces. Also, the characteristics of attaching cells, such as the presence of flagella, play an important role in adhering to a surface [106,127,128,132].
Surfaces engineered with subcellular-level features can also affect the morphology of the microbial aggregates. The micro- and nanoscale trenches patterned on a gold surface affect the adhesion of P. fluorescens cells and aggregation [127]. The cells formed well-ordered aggregates on the surfaces containing random nanostructures. The features with defined dimensions present on the substrates inhibited the formation of ordered aggregates.
Other studies report the use of biomimetic surface-patterned substrates to control microbial adhesion. One such pattern mimics the surface features present on the shark’s skin. PDMS elastomer with a topography similar to shark skin (Shark AFTM) exhibited lower attachment and aggregation of S. aureus than the unpatterned surfaces [108,126]. S. aureus was chosen for the study due to the matching sizes of cells and the Shark AFTM features (width and spacing between the adjacent structures = 2 μm and depth = 2 μm). Also, it is noteworthy that most studies correlate the attachment of microbes to surface topography; however, in some cases, no apparent effect was found [133].
In addition to reducing the accessible surface area, nanostructures introduce bactericidal properties [125,132,134,135]. For example, sharp nanotopographical features patterned on the surface of silicon wafers killed the E. coli and S. aureus cells attached to the silicon surface [132]. The bactericidal effect was enhanced by coating the textured surfaces with chitosan, a biopolymer that has antibacterial properties. The spherical, Gram-positive S. aureus cells were attached on top of the nanostructures and between the structures, whereas Gram-positive, rod-shaped E. coli cells could not settle in between the nanostructures. Nevertheless, both types of bacteria deformed to achieve the best orientation on the patterned surfaces. Similarly, the bactericidal effect and reduced adhesion of E. coli were observed when the surface of poly(methyl methacrylate) (PMMA) films was patterned with nanopillars [125]. The optimum spacing between neighboring pillars was found to be in the range 130–380 nm. The bactericidal effect of a nanoengineered surface can be attributed to the cell lysis resulting from the high level of stress caused by the sharp tips of nanostructures [125]. Upon settling down on the nanostructures, the microbial cells stretch and deform. During this process, the sharp nanotips can rupture the cell walls and membranes, ultimately killing the cells [132,135]. The fabrication of nanostructured surfaces that can kill microorganisms is inspired by examples found in nature, such as cicada wings [136].
Decreased attachment of microbial cells on the patterned surfaces can be a result of the superhydrophobicity of the surface [128]. Structures on patterned surfaces may trap air in between spaces, making penetration of water (or other liquids) into the gaps difficult. So, the liquid droplets stay on top of the structures. This state is known as the Cassie-Baxter state. In that case, only the feature tops are available for the microbes, consequently reducing the attachment [128]. In the Cassie-Baxter state, the adhesion between the liquid droplet and the solid surface is low; therefore, the droplet can move easily on the surface. The surface is known to be superhydrophobic [69]. Same as the liquid droplets, any other particle, such as dirt or microbial cells, adheres weakly to such surfaces. A liquid droplet that rolls on a superhydrophobic surface may encounter a particle and carry the particle with the droplet, creating a self-cleaning surface [69]. Although the Cassie-Baxter state allows the liquid droplet to interact only with the feature tops, over time, the liquid can replace the air trapped between the structures. The wetting state transitions to another state known as the Wenzel state, allowing the microbial cells to reach the surface. At initial time points where the Cassie–Baxter conditions exist, the patterned surfaces exhibit a low microbial attachment. As time passes, the wetting state converts to the Wenzel state, the cells can reach the surface between the structures, and the attachment increases [128].
Inspired by nature, surfaces containing hierarchical patterns have been examined as a strategy that prevents colonization of microorganisms [137,138,139]. As reported in one study, the attachment of P. aeruginosa was decreased on a titanium surface patterned with hierarchical structures that mimic the surface topography of the lotus (Nelumbo nucifera) leaf [139]. In contrast, increased attachment of S. aureus was observed on the same surface pattern, indicating that the surface features alone cannot determine attachment of microorganisms. The difference in attachment was attributed to the shapes of the bacteria (rod-shaped P. aeruginosa vs. spherical S. aureus).
In general, nanostructures on biomaterial surfaces control biofilms by reducing accessible surface area, promoting self-cleaning, or exerting bactericidal effects (Figure 5). Therefore, patterning surfaces with nanoscale topographies is an effective method for eliminating biofilms from biomaterial surfaces, without using antimicrobial agents or chemicals that can cause side effects.

5. Hydrogels as Biomaterials

Hydrogels are network polymers that can retain large quantities of water or biological fluids due to the network structure formed by crosslinking between the polymer chains [140]. By absorbing water, these polymer networks become gel-like soft materials that can mimic the natural biological environment. The properties of hydrogels can be easily tailored by adjusting parameters such as chemical composition, crosslinking, surface topography, and architecture to suit specific applications. Hydrogels have garnered significant interest as biomaterials due to their porous structure, tunable properties, soft nature, and favorable biological properties such as biocompatibility and biodegradability [141,142]. In particular, the biological applications of hydrogels are drug delivery systems, scaffolding materials in tissue engineering, wound dressings, prosthetic and wearable medical devices, and biosensors, to name a few [143,144,145,146]. Although some studies of hydrogels and biomaterials are still in the preliminary stages, various hydrogel-based products are commercially available [147]. Most of these applications require the biomaterial to stay in contact with the human body for extended periods. Hence, biofilm-related issues constitute a significant concern for hydrogel-based biomaterials. Nanotechnological strategies have been integrated to introduce antimicrobial properties into hydrogels. For instance, antimicrobial hydrogels have been fabricated by incorporating nanoparticles [148,149,150,151,152,153].

5.1. Current Status and Novel Trends in Surface-Patterned Hydrogels as Antibiofouling Materials

Hydrogels containing various topographical features have been extensively studied in biological and biomedical applications to control the attachment, functions, and behavior of cells [154,155,156,157,158,159]. Although nanopatterning has been explored as a method to mitigate biofilms on various materials, including silicon, titanium, and polymers, studies that involve nanopatterned hydrogels are limited. Since hydrogels are well-known for their biomaterial applications, it is essential to study nanopatterned hydrogels for antibiofouling applications. Being hydrophilic polymers, hydrogels possess antiadhesive properties as hydrophilic polymer coatings show low adhesion of microorganisms and biomolecules such as polymers [79]. Thus, patterning hydrogels with nanotopographic features will further enhance their intrinsic antiadhesive nature.
The surface patterns generated in most studies are static, meaning they remain unchanged over time. Maintaining the functionality of these static textures is challenging, as biological factors and interactions with cells may degrade the material’s original architecture, leading to loss of antibiofouling properties [20]. Currently, another technique known as dynamic topography, inspired by nature, is being investigated as a solution to overcome these challenges associated with the static topography approaches [160,161,162]. Dynamic topography is a bioinspired approach in which the surface and topographical features change repeatedly, subsequently facilitating delamination of bacteria attached to the surface [160]. Therefore, materials with dynamic topography are considered self-cleaning surfaces. The changes in the surface can be induced by external stimuli such as pH, electrical signals, temperature, etc. [162]. The ability to change the surface in response to external factors is an excellent property for an antibiofouling biomaterial. Hydrogels are popular stimuli-responsive materials, as these network polymers can change their swelling in response to external factors [163]. Moreover, the soft, gel-like nature of hydrogels is beneficial for controlling the formation of biofilms. As previously shown, the aggregation of bacterial cells to form biofilms can be inhibited by using arrays of nanoposts on soft polymers [89]. Considering the suitability of hydrogels for applications as biomaterials that are in contact with the human body, their soft nature, and their stimuli responsiveness, further research is necessary to develop hydrogels with dynamic nanotopographical features.

5.2. Fabrication of Surface-Patterned Hydrogels

Fabrication of surface structures involves several techniques. Figure 6 shows some of the widely used techniques. In photolithography, a desired pattern is initially created on a mask (e.g., a silicon wafer), transferred onto a reactive polymer layer known as a resist, and subsequently replicated onto another substrate [164].
Photolithography is a standard method that is used to generate micron-level structures; however, fabrication of nanoscale features requires advanced lithography techniques such as deep ultraviolet (UV) and extreme UV photolithography, X-ray lithography, focused ion beam (FIB) lithography, and electron beam writing [165]. Since these advanced methods are expensive and require sophisticated conditions, a low-cost alternative known as soft lithography has been developed [165,166]. In soft lithography, the original pattern generated on a master material, such as a silicon wafer, is transferred to another substrate using an intermediate soft organic or polymeric material as the mold. Although there are various soft lithography methods, such as microcontact printing, embossing, replica molding, micromolding in capillaries (MIMIC), and microtransfer molding, not all of them can pattern nanoscale features. Among these different methods, replica molding and microtransfer molding can successfully pattern the delicate structures in the nanometer range [165]. In replica molding, the use of an elastomeric mold allowed the transfer of the pattern from the master, enabling the fabrication of complex structures with different sizes, shapes, and periodicities. Unlike the replica molding technique, which can pattern thick substrates, microtransfer molding can pattern only a thin film (thickness of 100 nm or less) of a polymer. Additionally, there are limitations on the materials that can be patterned using these lithography methods. For example, photolithography can directly pattern only polymers with photosensitive additives [166]. Various techniques for patterning polymers with micron and submicron-level topographical features have been reviewed [167]. Table 5 compares alternative lithography methods used for patterning hydrogels.
Patterning hydrogel surfaces is challenging due to their swelling properties, adhesion, and low mechanical strength [173,174]. Replica molding has been successfully used to pattern poly(2-hydroxyethyl methacrylate) (poly(HEMA))-based hydrogels with surface structures in the micrometer scale [175,176]. Swelling-induced delamination of the hydrogel from the PDMS mold ensures complete and uniform transfer of the pattern onto the hydrogel [175]. However, patterning hydrogels with nanofeatures may require adjustments to the existing methodologies, as the pattern transfer becomes more difficult with decreasing feature size. Therefore, the conditions should be optimized based on the hydrogel system and dimensions of the pattern. Recently published papers discuss the effects of surface patterns on properties and applications of hydrogels, and various methods and techniques used to create surface patterns [177,178]. Table 6 summarizes surface-patterned hydrogel systems.

5.3. Limitations of Surface-Patterned Hydrogels

Although hydrogels can be developed as antifouling biomaterials, their inherent properties can limit their applications. Hydrogels become soft when swollen in water. High water content and soft nature result in low mechanical properties, which may be incompatible with certain applications, such as orthopedic and dental implants [183]. As discussed in Section 5.2, producing hydrogels with nanoscale surface patterns is challenging because these fragile features can collapse. For example, nanostructures with high aspect ratios (HARs) may be unstable and collapse. Additionally, achieving high fidelity in the patterning process is another challenge [184].

6. Future Perspective

Patterning surfaces with nanotopographical features is a strategy that can prevent the formation of microbial biofilms on implants and indwelling medical devices. Nanopatterned materials inhibit the attachment of microorganisms and the aggregation of cells to form biofilms by altering surface properties, such as hydrophobicity and stiffness, and limiting available contact sites for cell interaction. The application of nanometer-scale surface features to alleviate attachment of microorganisms has been investigated across a broad range of materials, including silicon, metals and metal oxides, ceramics, and polymers. Nonetheless, the application of nanopatterning to develop antibiofouling hydrogels has not been widely studied, despite surface-patterned hydrogels being well known for their applications as biomaterials. Therefore, further research is needed to develop antifouling nanopatterned hydrogels. Patterning hydrogels with different nanoscale features is challenging yet worthwhile to study, as nanopatterned hydrogels offer a promising solution to biofilm-related problems associated with medical implants. Researchers should also consider the features of the target microorganism, such as type, size, and shape, when fabricating nanopatterned hydrogels for antifouling biomaterial applications. Furthermore, dynamic topography can be applied to hydrogels to restrict the attachment of microbes, simultaneously offering self-cleaning capability. Additionally, understanding the interactions of microorganisms with these soft polymeric materials is necessary to develop biomaterials that meet expectations, and is another important area to focus on.
A more modern approach to addressing problems associated with traditional surface patterning methods is to use machine learning. Machine learning can be used to optimize fabrication parameters, thereby improving reproducibility and scalability [185].
Overall, future research should focus more on optimizing existing techniques or developing new methods to fabricate stable, cost-effective, eco-friendly nanostructured hydrogels. Moreover, depending on the target application, hydrogel properties, such as mechanical strength, durability, and biocompatibility, must be optimized. The antifouling properties of nanostructured hydrogels can be enhanced by incorporating other materials, such as metal or polymer nanoparticles. There is a research gap in this area that needs more attention, as it has the potential to develop antimicrobial surfaces with structural features rather than relying on harmful chemicals.

Author Contributions

Conceptualization, S.V.M.; methodology, writing—original draft preparation, H.G.J. and U.S.K.M.-B.; writing—review and editing, H.G.J., U.S.K.M.-B. and S.V.M. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Data Availability Statement

This is a review paper and no new data was acquired.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Bjarnsholt, T. Introduction to Biofilms. In Biofilm Infections; Bjarnsholt, T., Jensen, P.Ø., Moser, C., Høiby, N., Eds.; Springer: New York, NY, USA, 2011; pp. 1–9. [Google Scholar]
  2. Costerton, J.W.; Stewart, P.S.; Greenberg, E.P. Bacterial Biofilms: A Common Cause of Persistent Infections. Science 1999, 284, 1318–1322. [Google Scholar] [CrossRef] [PubMed]
  3. Ramasamy, M.; Lee, J. Recent Nanotechnology Approaches for Prevention and Treatment of Biofilm-Associated Infections on Medical Devices. Biomed Res. Int. 2016, 2016, 1851242. [Google Scholar] [CrossRef]
  4. Khatoon, Z.; McTiernan, C.D.; Suuronen, E.J.; Mah, T.-F.; Alarcon, E.I. Bacterial biofilm formation on implantable devices and approaches to its treatment and prevention. Heliyon 2018, 4, e01067. [Google Scholar] [CrossRef]
  5. He, M.; Huang, Y.; Wang, J.; Chen, Z.; Xie, J.; Cui, Z.; Xu, D.; Zhang, X.; Yao, W. Advances in polysaccharide-based antibacterial materials. Int. J. Biol. Macromol. 2025, 308, 142598. [Google Scholar] [CrossRef]
  6. Murosaki, T.; Ahmed, N.; Gong, J.P. Antifouling properties of hydrogels. Sci. Technol. Adv. Mater. 2011, 12, 064706. [Google Scholar] [CrossRef]
  7. Nwuzor, I.C.; Idumah, C.I.; Nwanonenyi, S.C.; Ezeani, O.E. Emerging trends in self-polishing anti-fouling coatings for marine environment. Saf. Extrem. Environ. 2021, 3, 9–25. [Google Scholar]
  8. Kio, M.; Klauda, J. Advances in emerging hydrogel fouling-release coatings for marine applications. J. Coat. Technol. Res. 2024, 21, 827–856. [Google Scholar]
  9. Wang, Y.; Zhou, X.; He, L.; Zhou, X.; Wang, Y.; Zhou, P. Research Progress on Using Modified Hydrogel Coatings as Marine Antifouling Materials. Mar. Drugs 2024, 22, 546. [Google Scholar] [CrossRef]
  10. Li, X.; Yu, Z.; Wang, J.; Zhang, J.; Zhao, W.; Wang, L.; Wang, F.; Xu, D. Nanomaterials Reinforced Antifouling Coatings: From Strategic Design to Potential Applications. Adv. Mater. 2026, 38, e14795. [Google Scholar]
  11. Xu, Y.; Luan, X.; He, P.; Zhu, D.; Mu, R.; Wang, Y.; Wei, G. Fabrication and Functional Regulation of Biomimetic Interfaces and Their Antifouling and Antibacterial Applications: A Review. Small 2024, 20, 2308091. [Google Scholar]
  12. Tullii, G.; Donini, S.; Bossio, C.; Lodola, F.; Pasini, M.; Parisini, E.; Galeotti, F.; Antognazza, M.R. Micro- and Nanopatterned Silk Substrates for Antifouling Applications. ACS Appl. Mater. Interfaces 2020, 12, 5437–5446. [Google Scholar] [CrossRef]
  13. Kim, T.; Kwon, S.; Lee, J.; Lee, J.S.; Kang, S. A metallic anti-biofouling surface with a hierarchical topography containing nanostructures on curved micro-riblets. Microsyst. Nanoeng. 2022, 8, 6. [Google Scholar]
  14. Priya, S.; Malviya, R.; Srivastava, S.; Siang, T.C.; Aseeri, A.A. Bioinspired nanostructured surfaces for antimicrobial and antifouling applications. Colloid Interface Sci. Commun. 2026, 70, 100863. [Google Scholar]
  15. Donnelly, B.; Sammut, K.; Tang, Y. Materials Selection for Antifouling Systems in Marine Structures. Molecules 2022, 27, 3408. [Google Scholar] [CrossRef]
  16. Donlan, R.M. Biofilm Formation: A Clinically Relevant Microbiological Process. Clin. Infect. Dis. 2001, 33, 1387–1392. [Google Scholar] [CrossRef]
  17. Gupta, P.; Sarkar, S.; Das, B.; Bhattacharjee, S.; Tribedi, P. Biofilm, pathogenesis and prevention—A journey to break the wall: A review. Arch. Microbiol. 2016, 198, 1–15. [Google Scholar] [PubMed]
  18. Hall-Stoodley, L.; Costerton, J.W.; Stoodley, P. Bacterial biofilms: From the Natural environment to infectious diseases. Nat. Rev. Microbiol. 2004, 2, 95–108. [Google Scholar] [CrossRef] [PubMed]
  19. Tuson, H.H.; Weibel, D.B. Bacteria–surface interactions. Soft Matter 2013, 9, 4368–4380. [Google Scholar] [CrossRef]
  20. Cheng, Y.; Feng, G.; Moraru, C.I. Micro- and Nanotopography Sensitive Bacterial Attachment Mechanisms: A Review. Front. Microbiol. 2019, 10, 191. [Google Scholar] [CrossRef] [PubMed]
  21. Fletcher, M.; Marshall, K.C. Are Solid Surfaces of Ecological Significance to Aquatic Bacteria? In Advances in Microbial Ecology: Volume 6; Marshall, K.C., Ed.; Springer: Boston, MA, USA, 1982; pp. 199–236. [Google Scholar]
  22. Nevin, K.P.; Kim, B.C.; Glaven, R.H.; Johnson, J.P.; Woodard, T.L.; Methé, B.A.; Didonato, R.J.; Covalla, S.F.; Franks, A.E.; Liu, A.; et al. Anode biofilm transcriptomics reveals outer surface components essential for high density current production in Geobacter sulfurreducens fuel cells. PLoS ONE 2009, 4, e5628. [Google Scholar] [CrossRef]
  23. Simões, M.; Pereira, M.O.; Vieira, M.J. Effect of mechanical stress on biofilms challenged by different chemicals. Water Res. 2005, 39, 5142–5152. [Google Scholar] [CrossRef]
  24. Costerton, J.W.; Lewandowski, Z.; Caldwell, D.E.; Korber, D.R.; Lappin-Scott, H.M. Microbial Biofilms. Annu. Rev. Microbiol. 1995, 49, 711–745. [Google Scholar] [CrossRef]
  25. Chen, M.; Yu, Q.; Sun, H. Novel strategies for the prevention and treatment of biofilm related infections. Int. J. Mol. Sci. 2013, 14, 18488–18501. [Google Scholar] [CrossRef] [PubMed]
  26. Orenstein, R.; Wong, E.S. Urinary tract infections in adults. Am. Fam. Physician 1999, 59, 1225–1234, 1237. [Google Scholar] [PubMed]
  27. Soto, S.M. Importance of Biofilms in Urinary Tract Infections: New Therapeutic Approaches. Adv. Biol. 2014, 2014, 543974. [Google Scholar] [CrossRef]
  28. Weinstein, R.A.; Darouiche, R.O. Device-Associated Infections: A Macroproblem that Starts with Microadherence. Clin. Infect. Dis. 2001, 33, 1567–1572. [Google Scholar]
  29. Jamal, M.; Ahmad, W.; Andleeb, S.; Jalil, F.; Imran, M.; Nawaz, M.A.; Hussain, T.; Ali, M.; Rafiq, M.; Kamil, M.A. Bacterial biofilm and associated infections. J. Chin. Med. Assoc. 2018, 81, 7–11. [Google Scholar] [CrossRef]
  30. Gominet, M.; Compain, F.; Beloin, C.; Lebeaux, D. Central venous catheters and biofilms: Where do we stand in 2017? APMIS 2017, 125, 365–375. [Google Scholar] [CrossRef] [PubMed]
  31. Szczotka-Flynn, L.B.; Imamura, Y.; Chandra, J.; Yu, C.; Mukherjee, P.K.; Pearlman, E.; Ghannoum, M.A. Increased resistance of contact lens-related bacterial biofilms to antimicrobial activity of soft contact lens care solutions. Cornea 2009, 28, 918–926. [Google Scholar] [CrossRef]
  32. Arciola, C.R.; Campoccia, D.; Montanaro, L. Implant infections: Adhesion, biofilm formation and immune evasion. Nat. Rev. Microbiol. 2018, 16, 397–409. [Google Scholar] [CrossRef]
  33. Davidson, D.J.; Spratt, D.; Liddle, A.D. Implant materials and prosthetic joint infection: The battle with the biofilm. EFORT Open Rev. 2019, 4, 633–639. [Google Scholar] [CrossRef] [PubMed]
  34. Okada, M.; Kashiwase, K.; Hirata, A.; Nemoto, T.; Matsuo, K.; Murakami, A.; Ueda, Y. Bacterial Contamination During Pacemaker Implantation Is Common and Does Not Always Result in Infection. Circ. J. 2015, 79, 1712–1718. [Google Scholar] [CrossRef]
  35. Leonhard, M.; Schneider-Stickler, B. Voice Prostheses, Microbial Colonization and Biofilm Formation. In Biofilm-Based Healthcare-Associated Infections: Volume I; Donelli, G., Ed.; Springer International Publishing: Cham, Switzerland, 2015; pp. 123–136. [Google Scholar]
  36. Bauters, T.G.M.; Moerman, M.; Vermeersch, H.; Nelis, H.J. Colonization of Voice Prostheses by Albicans and Non-Albicans Candida Species. Laryngoscope 2002, 112, 708–712. [Google Scholar]
  37. Elving, G.J.; van der Mei, H.C.; Busscher, H.J.; van Weissenbruch, R.; Albers, F.W. Comparison of the microbial composition of voice prosthesis biofilms from patients requiring frequent versus infrequent replacement. Ann. Otol. Rhinol. Laryngol. 2002, 111, 200–203. [Google Scholar] [CrossRef] [PubMed]
  38. Gil-Perotin, S.; Ramirez, P.; Marti, V.; Sahuquillo, J.M.; Gonzalez, E.; Calleja, I.; Menendez, R.; Bonastre, J. Implications of endotracheal tube biofilm in ventilator-associated pneumonia response: A state of concept. Crit. Care 2012, 16, R93. [Google Scholar] [CrossRef]
  39. Vandecandelaere, I.; Matthijs, N.; Van Nieuwerburgh, F.; Deforce, D.; Vosters, P.; De Bus, L.; Nelis, H.J.; Depuydt, P.; Coenye, T. Assessment of Microbial Diversity in Biofilms Recovered from Endotracheal Tubes Using Culture Dependent and Independent Approaches. PLoS ONE 2012, 7, e38401. [Google Scholar]
  40. Thomas, M.; D’Silva, J.A.; Borole, A.J.; Chilgar, R.M. Periprosthetic atypical mycobaterial infection in breast implants: A new kid on the block! J. Plast. Reconstr. Aesthetic Surg. 2013, 66, e16–e19. [Google Scholar] [CrossRef]
  41. Feldman, E.M.; Kontoyiannis, D.P.; Sharabi, S.E.; Lee, E.; Kaufman, Y.; Heller, L. Breast Implant Infections: Is Cefazolin Enough? Plast. Reconstr. Surg. 2010, 126, 779–785. [Google Scholar] [CrossRef]
  42. Fleming, D.; Rumbaugh, K.P. Approaches to Dispersing Medical Biofilms. Microorganisms 2017, 5, 15. [Google Scholar] [CrossRef]
  43. Rumbaugh, K.P. How well are we translating biofilm research from bench-side to bedside? Biofilm 2020, 2, 100028. [Google Scholar] [CrossRef]
  44. Zhao, A.; Sun, J.; Liu, Y. Understanding bacterial biofilms: From definition to treatment strategies. Front. Cell. Infect. Microbiol. 2023, 13, 1137947. [Google Scholar] [CrossRef] [PubMed]
  45. Oliva, A.; Stefani, S.; Venditti, M.; Di Domenico, E.G. Biofilm-Related Infections in Gram-Positive Bacteria and the Potential Role of the Long-Acting Agent Dalbavancin. Front. Microbiol. 2021, 12, 749685. [Google Scholar]
  46. Pompilio, A.; Scribano, D.; Sarshar, M.; Di Bonaventura, G.; Palamara, A.T.; Ambrosi, C. Gram-Negative Bacteria Holding Together in a Biofilm: The Acinetobacter baumannii Way. Microorganisms 2021, 9, 1353. [Google Scholar] [CrossRef]
  47. Iñigo, M.; Del Pozo, J.L. Fungal biofilms: From bench to bedside. Rev. Esp. Quimioter. 2018, 31, 35–38. [Google Scholar]
  48. Jeong, G.-J.; Khan, F.; Tabassum, N.; Cho, K.-J.; Kim, Y.-M. Strategies for controlling polymicrobial biofilms: A focus on antibiofilm agents. Int. J. Antimicrob. Agents 2024, 64, 107243. [Google Scholar] [CrossRef]
  49. Anju, V.T.; Busi, S.; Imchen, M.; Kumavath, R.; Mohan, M.S.; Salim, S.A.; Subhaswaraj, P.; Dyavaiah, M. Polymicrobial Infections and Biofilms: Clinical Significance and Eradication Strategies. Antibiotics 2022, 11, 1731. [Google Scholar] [CrossRef]
  50. Rajagopal, M.; Walker, S. Envelope Structures of Gram-Positive Bacteria. Curr. Top. Microbiol. Immunol. 2017, 404, 1–44. [Google Scholar]
  51. Ruhal, R.; Kataria, R. Biofilm patterns in gram-positive and gram-negative bacteria. Microbiol. Res. 2021, 251, 126829. [Google Scholar] [CrossRef]
  52. Zarnowski, R.; Westler, W.M.; Lacmbouh, G.A.; Marita, J.M.; Bothe, J.R.; Bernhardt, J.; Lounes-Hadj Sahraoui, A.; Fontaine, J.; Sanchez, H.; Hatfield, R.D.; et al. Novel entries in a fungal biofilm matrix encyclopedia. mBio 2014, 5, e01333-14. [Google Scholar] [CrossRef]
  53. Martinez, L.R.; Fries, B.C. Fungal Biofilms: Relevance in the Setting of Human Disease. Curr. Fungal Infect. Rep. 2010, 4, 266–275. [Google Scholar] [CrossRef] [PubMed]
  54. Sadiq, F.A.; Burmølle, M.; Heyndrickx, M.; Flint, S.; Lu, W.; Chen, W.; Zhao, J.; Zhang, H. Community-wide changes reflecting bacterial interspecific interactions in multispecies biofilms. Crit. Rev. Microbiol. 2021, 47, 338–358. [Google Scholar] [CrossRef]
  55. Kernien, J.F.; Snarr, B.D.; Sheppard, D.C.; Nett, J.E. The Interface between Fungal Biofilms and Innate Immunity. Front. Immunol. 2017, 8, 1968. [Google Scholar] [CrossRef]
  56. Peters Brian, M.; Jabra-Rizk Mary, A.; O’May Graeme, A.; Costerton, J.W.; Shirtliff Mark, E. Polymicrobial Interactions: Impact on Pathogenesis and Human Disease. Clin. Microbiol. Rev. 2012, 25, 193–213. [Google Scholar] [CrossRef]
  57. Bjarnsholt, T. The role of bacterial biofilms in chronic infections. APMIS 2013, 121, 1–58. [Google Scholar] [CrossRef]
  58. Srivastava, S.; Bhargava, A. Biofilms and human health. Biotechnol. Lett. 2016, 38, 1–22. [Google Scholar] [CrossRef]
  59. Rimondini, L.; Cochis, A.; Varoni, E.; Azzimonti, B.; Carrassi, A. Biofilm Formation on Implants and Prosthetic Dental Materials. In Handbook of Bioceramics and Biocomposites; Antoniac, I.V., Ed.; Springer International Publishing: Cham, Switzerland, 2014; pp. 1–37. [Google Scholar]
  60. Veerachamy, S.; Yarlagadda, T.; Manivasagam, G.; Yarlagadda, P.K. Bacterial adherence and biofilm formation on medical implants: A review. Proc. Inst. Mech. Eng. H 2014, 228, 1083–1099. [Google Scholar] [CrossRef]
  61. Habash, M.; Reid, G. Microbial biofilms: Their development and significance for medical device-related infections. J. Clin. Pharmacol. 1999, 39, 887–898. [Google Scholar] [CrossRef] [PubMed]
  62. Oliveira, W.F.; Silva, P.M.S.; Silva, R.C.S.; Silva, G.M.M.; Machado, G.; Coelho, L.C.B.B.; Correia, M.T.S. Staphylococcus aureus and Staphylococcus epidermidis infections on implants. J. Hosp. Infect. 2018, 98, 111–117. [Google Scholar] [CrossRef] [PubMed]
  63. Yang, L.; Liu, Y.; Wu, H.; Song, Z.; Høiby, N.; Molin, S.; Givskov, M. Combating biofilms. FEMS Immunol. Med. Microbiol. 2012, 65, 146–157. [Google Scholar] [CrossRef]
  64. Blackledge, M.S.; Worthington, R.J.; Melander, C. Biologically inspired strategies for combating bacterial biofilms. Curr. Opin. Pharmacol. 2013, 13, 699–706. [Google Scholar] [CrossRef] [PubMed]
  65. Masák, J.; Čejková, A.; Schreiberová, O.; Řezanka, T. Pseudomonas biofilms: Possibilities of their control. FEMS Microbiol. Ecol. 2014, 89, 1–14. [Google Scholar] [CrossRef]
  66. Yin, W.; Xu, S.; Wang, Y.; Zhang, Y.; Chou, S.H.; Galperin, M.Y.; He, J. Ways to control harmful biofilms: Prevention, inhibition, and eradication. Crit. Rev. Microbiol. 2021, 47, 57–78. [Google Scholar] [CrossRef]
  67. Sonnleitner, D.; Sommer, C.; Scheibel, T.; Lang, G. Approaches to inhibit biofilm formation applying natural and artificial silk-based materials. Mater. Sci. Eng. C 2021, 131, 112458. [Google Scholar] [CrossRef]
  68. Hindieh, P.; Yaghi, J.; Assaf, J.C.; Chokr, A.; Atoui, A.; Tzenios, N.; Louka, N.; Khoury, A.E. Emerging Multimodal Strategies for Bacterial Biofilm Eradication: A Comprehensive Review. Microorganisms 2025, 13, 2796. [Google Scholar] [CrossRef]
  69. Balaure, P.C.; Grumezescu, A.M. Recent Advances in Surface Nanoengineering for Biofilm Prevention and Control. Part I: Molecular Basis of Biofilm Recalcitrance. Passive Anti-Biofouling Nanocoatings. Nanomaterials 2020, 10, 1230. [Google Scholar] [CrossRef]
  70. Banerjee, I.; Pangule, R.C.; Kane, R.S. Antifouling coatings: Recent developments in the design of surfaces that prevent fouling by proteins, bacteria, and marine organisms. Adv. Mater. 2011, 23, 690–718. [Google Scholar] [CrossRef]
  71. De Prijck, K.; De Smet, N.; Coenye, T.; Schacht, E.; Nelis, H.J. Prevention of Candida albicans Biofilm Formation by Covalently Bound Dimethylaminoethylmethacrylate and Polyethylenimine. Mycopathologia 2010, 170, 213–221. [Google Scholar] [CrossRef] [PubMed]
  72. Lichter, J.A.; Thompson, M.T.; Delgadillo, M.; Nishikawa, T.; Rubner, M.F.; Van Vliet, K.J. Substrata Mechanical Stiffness Can Regulate Adhesion of Viable Bacteria. Biomacromolecules 2008, 9, 1571–1578. [Google Scholar] [CrossRef] [PubMed]
  73. Barraud, N.; Hassett, D.J.; Hwang, S.-H.; Rice, S.A.; Kjelleberg, S.; Webb, J.S. Involvement of Nitric Oxide in Biofilm Dispersal of Pseudomonas aeruginosa. J. Bacteriol. 2006, 188, 7344–7353. [Google Scholar] [CrossRef]
  74. Chelmowski, R.; Köster, S.D.; Kerstan, A.; Prekelt, A.; Grunwald, C.; Winkler, T.; Metzler-Nolte, N.; Terfort, A.; Wöll, C. Peptide-Based SAMs that Resist the Adsorption of Proteins. J. Am. Chem. Soc. 2008, 130, 14952–14953. [Google Scholar] [CrossRef] [PubMed]
  75. Chen, S.; Cao, Z.; Jiang, S. Ultra-low fouling peptide surfaces derived from natural amino acids. Biomaterials 2009, 30, 5892–5896. [Google Scholar] [CrossRef]
  76. Cassinelli, C.; Morra, M.; Pavesio, A.; Renier, D. Evaluation of interfacial properties of hyaluronan coated poly(methylmethacrylate) intraocular lenses. J. Biomater. Sci. Polym. Ed. 2000, 11, 961–977. [Google Scholar] [CrossRef]
  77. Boelens, J.J.; Tan, W.-F.; Dankert, J.; Zaat, S.A.J. Antibacterial activity of antibiotic-soaked polyvinylpyrrolidone-grafted silicon elastomer hydrocephalus shunts. J. Antimicrob. Chemother. 2000, 45, 221–224. [Google Scholar] [CrossRef]
  78. Gottenbos, B.; van der Mei, H.C.; Klatter, F.; Nieuwenhuis, P.; Busscher, H.J. In vitro and in vivo antimicrobial activity of covalently coupled quaternary ammonium silane coatings on silicone rubber. Biomaterials 2002, 23, 1417–1423. [Google Scholar] [CrossRef]
  79. Francolini, I.; Donelli, G. Prevention and control of biofilm-based medical-device-related infections. FEMS Immunol. Med. Microbiol. 2010, 59, 227–238. [Google Scholar] [CrossRef]
  80. Li, P.; Yin, R.; Cheng, J.; Lin, J. Bacterial Biofilm Formation on Biomaterials and Approaches to Its Treatment and Prevention. Int. J. Mol. Sci. 2023, 24, 11680. [Google Scholar] [CrossRef] [PubMed]
  81. Alum, E.U.; Gulumbe, B.H.; Izah, S.C.; Uti, D.E.; Aja, P.M.; Igwenyi, I.O.; Offor, C.E. Natural product-based inhibitors of quorum sensing: A novel approach to combat antibiotic resistance. Biochem. Biophys. Rep. 2025, 43, 102111. [Google Scholar] [CrossRef] [PubMed]
  82. Ye, J.; Qiu, W.; Xie, J. Quorum sensing systems in biofilm formation and the potential application of natural quorum sensing inhibitors in aquatic product preservation. Food Res. Int. 2025, 221, 117623. [Google Scholar] [CrossRef]
  83. Damodaran, V.B.; Murthy, N.S. Bio-inspired strategies for designing antifouling biomaterials. Biomater. Res. 2016, 20, 18. [Google Scholar] [CrossRef] [PubMed]
  84. Malaekeh-Nikouei, B.; Fazly Bazzaz, B.S.; Mirhadi, E.; Tajani, A.S.; Khameneh, B. The role of nanotechnology in combating biofilm-based antibiotic resistance. J. Drug Deliv. Sci. Technol. 2020, 60, 101880. [Google Scholar] [CrossRef]
  85. Baptista, P.V.; McCusker, M.P.; Carvalho, A.; Ferreira, D.A.; Mohan, N.M.; Martins, M.; Fernandes, A.R. Nano-Strategies to Fight Multidrug Resistant Bacteria—“A Battle of the Titans”. Front. Microbiol. 2018, 9, 1441. [Google Scholar]
  86. Bharathi, D.; Lee, J. Polysaccharide-based nanomaterials and hydrogels for antibiofilm and wound healing applications. Int. J. Biol. Macromol. 2025, 320, 145899. [Google Scholar] [CrossRef]
  87. Silver, S.; Phung, L.T.; Silver, G. Silver as biocides in burn and wound dressings and bacterial resistance to silver compounds. J. Ind. Microbiol. Biotechnol. 2006, 33, 627–634. [Google Scholar] [CrossRef]
  88. Trevors, J.T. Silver resistance and accumulation in bacteria. Enzym. Microb. Technol. 1987, 9, 331–333. [Google Scholar] [CrossRef]
  89. Epstein, A.K.; Hochbaum, A.I.; Kim, P.; Aizenberg, J. Control of bacterial biofilm growth on surfaces by nanostructural mechanics and geometry. Nanotechnology 2011, 22, 494007. [Google Scholar] [CrossRef]
  90. Joshi, A.A.; Patil, R.H. Nanoparticles targeting biofilms: A new era in combating antimicrobial resistance. Med. Microecol. 2025, 26, 100156. [Google Scholar] [CrossRef]
  91. Sedighi, O.; Bednarke, B.; Sherriff, H.; Doiron, A.L. Nanoparticle-Based Strategies for Managing Biofilm Infections in Wounds: A Comprehensive Review. ACS Omega 2024, 9, 27853–27871. [Google Scholar] [CrossRef] [PubMed]
  92. Aflakian, F.; Hashemitabar, G. Biosynthesized silver nanoparticles at subinhibitory concentrations as inhibitors of quorum sensing, pathogenicity, and biofilm formation in Pseudomonas aeruginosa PAO1. Heliyon 2025, 11, e42899. [Google Scholar] [CrossRef]
  93. Rai, M.; Yadav, A.; Gade, A. Silver nanoparticles as a new generation of antimicrobials. Biotechnol. Adv. 2009, 27, 76–83. [Google Scholar] [CrossRef] [PubMed]
  94. Ma, X.; Tang, W.; Yang, R. Bioinspired nanomaterials for the treatment of bacterial infections. Nano Res. 2024, 17, 691–714. [Google Scholar]
  95. Zafar, N.; Madni, A.; Khalid, A.; Khan, T.; Kousar, R.; Naz, S.S.; Wahid, F. Pharmaceutical and Biomedical Applications of Green Synthesized Metal and Metal Oxide Nanoparticles. Curr. Pharm. Des. 2020, 26, 5844–5865. [Google Scholar] [CrossRef] [PubMed]
  96. Vahedi, M.; Hosseini-Jazani, N.; Yousefi, S.; Ghahremani, M. Evaluation of anti-bacterial effects of nickel nanoparticles on biofilm production by Staphylococcus epidermidis. Iran. J. Microbiol. 2017, 9, 160–168. [Google Scholar]
  97. Swolana, D.; Kępa, M.; Idzik, D.; Dziedzic, A.; Kabała-Dzik, A.; Wąsik, T.J.; Wojtyczka, R.D. The Antibacterial Effect of Silver Nanoparticles on Staphylococcus Epidermidis Strains with Different Biofilm-Forming Ability. Nanomaterials 2020, 10, 1010. [Google Scholar] [CrossRef]
  98. da Cunha, K.F.; Albernaz, D.T.F.; Garcia, M.d.O.; Allend, S.O.; Hartwig, D.D. Silver nanoparticles (AgNPs) in the control of Staphylococcus spp. Lett. Appl. Microbiol. 2022, 76, ovac032. [Google Scholar]
  99. Ali, S.; Sudha, K.G.; Thirumalaivasan, N.; Ahamed, M.; Pandiaraj, S.; Rajeswari, V.D.; Vinayagam, Y.; Thiruvengadam, M.; Govindasamy, R. Green Synthesis of Magnesium Oxide Nanoparticles by Using Abrus precatorius Bark Extract and Their Photocatalytic, Antioxidant, Antibacterial, and Cytotoxicity Activities. Bioengineering 2023, 10, 302. [Google Scholar] [CrossRef] [PubMed]
  100. Applerot, G.; Lipovsky, A.; Dror, R.; Perkas, N.; Nitzan, Y.; Lubart, R.; Gedanken, A. Enhanced Antibacterial Activity of Nanocrystalline ZnO Due to Increased ROS-Mediated Cell Injury. Adv. Funct. Mater. 2009, 19, 842–852. [Google Scholar] [CrossRef]
  101. Radulescu, D.-M.; Surdu, V.-A.; Ficai, A.; Ficai, D.; Grumezescu, A.-M.; Andronescu, E. Green Synthesis of Metal and Metal Oxide Nanoparticles: A Review of the Principles and Biomedical Applications. Int. J. Mol. Sci. 2023, 24, 15397. [Google Scholar] [CrossRef]
  102. Dwivedi, S.; Wahab, R.; Khan, F.; Mishra, Y.K.; Musarrat, J.; Al-Khedhairy, A.A. Reactive Oxygen Species Mediated Bacterial Biofilm Inhibition via Zinc Oxide Nanoparticles and Their Statistical Determination. PLoS ONE 2014, 9, e111289. [Google Scholar]
  103. Friedman, A.J.; Phan, J.; Schairer, D.O.; Champer, J.; Qin, M.; Pirouz, A.; Blecher-Paz, K.; Oren, A.; Liu, P.T.; Modlin, R.L.; et al. Antimicrobial and Anti-Inflammatory Activity of Chitosan–Alginate Nanoparticles: A Targeted Therapy for Cutaneous Pathogens. J. Investig. Dermatol. 2013, 133, 1231–1239. [Google Scholar] [CrossRef]
  104. Mazzantini, D.; Massimino, M.; Calvigioni, M.; Rossi, V.; Celandroni, F.; Lupetti, A.; Batoni, G.; Ghelardi, E. Anti-Staphylococcal Biofilm Effects of a Liposome-Based Formulation Containing Citrus Polyphenols. Antibiotics 2024, 13, 318. [Google Scholar] [CrossRef]
  105. Wang, X.; Hu, J.; Chen, C.; Lu, J.; Liu, C.; Ning, Y.; Lu, F. Berberine@AgNPs@Carboxylated chitosan hydrogel dressing with immunomodulatory and anti-biofilm properties promotes wound repair in drug-resistant bacterial infections. Int. J. Biol. Macromol. 2025, 315, 144496. [Google Scholar] [CrossRef]
  106. Xu, L.-C.; Siedlecki, C.A. Submicron-textured biomaterial surface reduces staphylococcal bacterial adhesion and biofilm formation. Acta Biomater. 2012, 8, 72–81. [Google Scholar] [CrossRef] [PubMed]
  107. Basak, P.; Adhikari, B.; Banerjee, I.; Maiti, T.K. Sustained release of antibiotic from polyurethane coated implant materials. J. Mater. Sci. Mater. Med. 2008, 20, 213–221. [Google Scholar] [CrossRef] [PubMed]
  108. Mann, E.E.; Manna, D.; Mettetal, M.R.; May, R.M.; Dannemiller, E.M.; Chung, K.K.; Brennan, A.B.; Reddy, S.T. Surface micropattern limits bacterial contamination. Antimicrob. Resist. Infect. Control 2014, 3, 28. [Google Scholar] [CrossRef]
  109. Gordon, A.T.; Lutz, G.E.; Boninger, M.L.; Cooper, R.A. Introduction to Nanotechnology: Potential Applications in Physical Medicine and Rehabilitation. Am. J. Phys. Med. Rehabil. 2007, 86, 225–241. [Google Scholar] [PubMed]
  110. Crawford, R.J.; Webb, H.K.; Truong, V.K.; Hasan, J.; Ivanova, E.P. Surface topographical factors influencing bacterial attachment. Adv. Colloid Interface Sci. 2012, 179–182, 142–149. [Google Scholar] [CrossRef]
  111. Perera-Costa, D.; Bruque, J.M.; González-Martín, M.L.; Gómez-García, A.C.; Vadillo-Rodríguez, V. Studying the Influence of Surface Topography on Bacterial Adhesion using Spatially Organized Microtopographic Surface Patterns. Langmuir 2014, 30, 4633–4641. [Google Scholar] [CrossRef]
  112. Hsu, L.C.; Fang, J.; Borca-Tasciuc, D.A.; Worobo, R.W.; Moraru, C.I. Effect of Micro- and Nanoscale Topography on the Adhesion of Bacterial Cells to Solid Surfaces. Appl. Environ. Microbiol. 2013, 79, 2703–2712. [Google Scholar] [CrossRef] [PubMed]
  113. Mitik-Dineva, N.; Wang, J.; Mocanasu, R.C.; Stoddart, P.R.; Crawford, R.J.; Ivanova, E.P. Impact of nano-topography on bacterial attachment. Biotechnol. J. 2008, 3, 536–544. [Google Scholar] [CrossRef]
  114. Bollenl, C.M.L.; Lambrechts, P.; Quirynen, M. Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention: A review of the literature. Dent. Mater. 1997, 13, 258–269. [Google Scholar] [CrossRef]
  115. Medilanski, E.; Kaufmann, K.; Wick, L.Y.; Wanner, O.; Harms, H. Influence of the Surface Topography of Stainless Steel on Bacterial Adhesion. Biofouling 2002, 18, 193–203. [Google Scholar] [CrossRef]
  116. Puckett, S.D.; Taylor, E.; Raimondo, T.; Webster, T.J. The relationship between the nanostructure of titanium surfaces and bacterial attachment. Biomaterials 2010, 31, 706–713. [Google Scholar] [CrossRef]
  117. Singh, A.V.; Vyas, V.; Patil, R.; Sharma, V.; Scopelliti, P.E.; Bongiorno, G.; Podestà, A.; Lenardi, C.; Gade, W.N.; Milani, P. Quantitative characterization of the influence of the nanoscale morphology of nanostructured surfaces on bacterial adhesion and biofilm formation. PLoS ONE 2011, 6, e25029. [Google Scholar] [CrossRef]
  118. Truong, V.K.; Lapovok, R.; Estrin, Y.S.; Rundell, S.; Wang, J.Y.; Fluke, C.J.; Crawford, R.J.; Ivanova, E.P. The influence of nano-scale surface roughness on bacterial adhesion to ultrafine-grained titanium. Biomaterials 2010, 31, 3674–3683. [Google Scholar] [CrossRef]
  119. Park, M.R.; Banks, M.K.; Applegate, B.; Webster, T.J. Influence of nanophase titania topography on bacterial attachment and metabolism. Int. J. Nanomed. 2008, 3, 497–504. [Google Scholar] [CrossRef][Green Version]
  120. Mitik-Dineva, N.; Wang, J.; Truong, V.K.; Stoddart, P.; Malherbe, F.; Crawford, R.J.; Ivanova, E.P. Escherichia coli, Pseudomonas aeruginosa, and Staphylococcus aureus Attachment Patterns on Glass Surfaces with Nanoscale Roughness. Curr. Microbiol. 2009, 58, 268–273. [Google Scholar] [CrossRef]
  121. An, Y.H.; Friedman, R.J.; Draughn, R.A.; Smith, E.A.; Nicholson, J.H.; John, J.F. Rapid quantification of staphylococci adhered to titanium surfaces using image analyzed epifluorescence microscopy. J. Microbiol. Methods 1995, 24, 29–40. [Google Scholar] [CrossRef]
  122. Li, B.; Logan, B.E. Bacterial adhesion to glass and metal-oxide surfaces. Colloids Surf. B Biointerfaces 2004, 36, 81–90. [Google Scholar]
  123. Boulangé-Petermann, L.; Rault, J.; Bellon-Fontaine, M.N. Adhesion of streptococcus thermophilus to stainless steel with different surface topography and roughness. Biofouling 1997, 11, 201–216. [Google Scholar] [CrossRef]
  124. Whitehead, K.A.; Colligon, J.; Verran, J. Retention of microbial cells in substratum surface features of micrometer and sub-micrometer dimensions. Colloids Surf. B Biointerfaces 2005, 41, 129–138. [Google Scholar] [PubMed]
  125. Dickson, M.N.; Liang, E.I.; Rodriguez, L.A.; Vollereaux, N.; Yee, A.F. Nanopatterned polymer surfaces with bactericidal properties. Biointerphases 2015, 10, 021010. [Google Scholar] [CrossRef] [PubMed]
  126. Chung, K.K.; Schumacher, J.F.; Sampson, E.M.; Burne, R.A.; Antonelli, P.J.; Brennan, A.B. Impact of engineered surface microtopography on biofilm formation of Staphylococcus aureus. Biointerphases 2007, 2, 89–94. [Google Scholar] [CrossRef]
  127. Díaz, C.; Schilardi, P.L.; Salvarezza, R.C.; de Mele, M.F.L. Nano/Microscale Order Affects the Early Stages of Biofilm Formation on Metal Surfaces. Langmuir 2007, 23, 11206–11210. [Google Scholar] [CrossRef] [PubMed]
  128. Friedlander, R.S.; Vlamakis, H.; Kim, P.; Khan, M.; Kolter, R.; Aizenberg, J. Bacterial flagella explore microscale hummocks and hollows to increase adhesion. Proc. Natl. Acad. Sci. USA 2013, 110, 5624–5629. [Google Scholar]
  129. Hochbaum, A.I.; Aizenberg, J. Bacteria Pattern Spontaneously on Periodic Nanostructure Arrays. Nano Lett. 2010, 10, 3717–3721. [Google Scholar] [CrossRef]
  130. Hou, S.; Gu, H.; Smith, C.; Ren, D. Microtopographic Patterns Affect Escherichia coli Biofilm Formation on Poly(dimethylsiloxane) Surfaces. Langmuir 2011, 27, 2686–2691. [Google Scholar] [CrossRef]
  131. Wang, L.; Wong, Y.-C.; Correira, J.M.; Wancura, M.; Geiger, C.J.; Webster, S.S.; Touhami, A.; Butler, B.J.; O’Toole, G.A.; Langford, R.M.; et al. The accumulation and growth of Pseudomonas aeruginosa on surfaces is modulated by surface mechanics via cyclic-di-GMP signaling. npj Biofilms Microbiomes 2023, 9, 78. [Google Scholar] [CrossRef]
  132. Tripathy, A.; Pahal, S.; Mudakavi, R.J.; Raichur, A.M.; Varma, M.M.; Sen, P. Impact of Bioinspired Nanotopography on the Antibacterial and Antibiofilm Efficacy of Chitosan. Biomacromolecules 2018, 19, 1340–1346. [Google Scholar] [CrossRef] [PubMed]
  133. Campoccia, D.; Montanaro, L.; Agheli, H.; Sutherland, D.S.; Pirini, V.; Donati, M.E.; Arciola, C.R. Study of Staphylococcus aureus adhesion on a novel nanostructured surface by chemiluminometry. Int. J. Artif. Organs 2006, 29, 622–629. [Google Scholar] [CrossRef]
  134. Ivanova, E.P.; Hasan, J.; Webb, H.K.; Gervinskas, G.; Juodkazis, S.; Truong, V.K.; Wu, A.H.F.; Lamb, R.N.; Baulin, V.A.; Watson, G.S.; et al. Bactericidal activity of black silicon. Nat. Commun. 2013, 4, 2838. [Google Scholar] [CrossRef]
  135. Kyle, N.; Adam, B.; Alan, C.; Dennis, L. Adhesion-dependent rupturing of Saccharomyces cerevisiae on biological antimicrobial nanostructured surfaces. J. R. Soc. Interface 2015, 12, 20140999. [Google Scholar] [CrossRef]
  136. Ivanova, E.P.; Hasan, J.; Webb, H.K.; Truong, V.K.; Watson, G.S.; Watson, J.A.; Baulin, V.A.; Pogodin, S.; Wang, J.Y.; Tobin, M.J.; et al. Natural Bactericidal Surfaces: Mechanical Rupture of Pseudomonas aeruginosa Cells by Cicada Wings. Small 2012, 8, 2489–2494. [Google Scholar] [CrossRef]
  137. Ma, J.; Sun, Y.; Gleichauf, K.; Lou, J.; Li, Q. Nanostructure on Taro Leaves Resists Fouling by Colloids and Bacteria under Submerged Conditions. Langmuir 2011, 27, 10035–10040. [Google Scholar] [CrossRef]
  138. Crick, C.R.; Ismail, S.; Pratten, J.; Parkin, I.P. An investigation into bacterial attachment to an elastomeric superhydrophobic surface prepared via aerosol assisted deposition. Thin Solid Film. 2011, 519, 3722–3727. [Google Scholar] [CrossRef]
  139. Fadeeva, E.; Truong, V.K.; Stiesch, M.; Chichkov, B.N.; Crawford, R.J.; Wang, J.; Ivanova, E.P. Bacterial Retention on Superhydrophobic Titanium Surfaces Fabricated by Femtosecond Laser Ablation. Langmuir 2011, 27, 3012–3019. [Google Scholar] [CrossRef]
  140. Peppas, N.A.; Bures, P.; Leobandung, W.; Ichikawa, H. Hydrogels in pharmaceutical formulations. Eur. J. Pharm. Biopharm. 2000, 50, 27–46. [Google Scholar] [CrossRef]
  141. Peppas, N.A.; Hilt, J.Z.; Khademhosseini, A.; Langer, R. Hydrogels in biology and medicine: From molecular principles to bionanotechnology. Adv. Mater. 2006, 18, 1345–1360. [Google Scholar] [CrossRef]
  142. Kopeček, J. Hydrogel biomaterials: A smart future? Biomaterials 2007, 28, 5185–5192. [Google Scholar] [CrossRef]
  143. Koehler, J.; Brandl, F.P.; Goepferich, A.M. Hydrogel wound dressings for bioactive treatment of acute and chronic wounds. Eur. Polym. J. 2018, 100, 1–11. [Google Scholar] [CrossRef]
  144. Gupta, A.; Kowalczuk, M.; Heaselgrave, W.; Britland, S.T.; Martin, C.; Radecka, I. The production and application of hydrogels for wound management: A review. Eur. Polym. J. 2019, 111, 134–151. [Google Scholar] [CrossRef]
  145. Hockaday, L.A.; Duan, B.; Kang, K.H.; Butcher, J.T. 3D-Printed Hydrogel Technologies for Tissue-Engineered Heart Valves. 3D Print. Addit. Manuf. 2014, 1, 122–136. [Google Scholar] [CrossRef]
  146. Zhang, X.; Xu, B.; Puperi, D.S.; Wu, Y.; West, J.L.; Grande-Allen, K.J. Application of hydrogels in heart valve tissue engineering. J. Long Term Eff. Med. Implant. 2015, 25, 105–134. [Google Scholar]
  147. Caló, E.; Khutoryanskiy, V.V. Biomedical applications of hydrogels: A review of patents and commercial products. Eur. Polym. J. 2015, 65, 252–267. [Google Scholar] [CrossRef]
  148. Ng, V.W.L.; Chan, J.M.W.; Sardon, H.; Ono, R.J.; García, J.M.; Yang, Y.Y.; Hedrick, J.L. Antimicrobial hydrogels: A new weapon in the arsenal against multidrug-resistant infections. Adv. Drug Deliv. Rev. 2014, 78, 46–62. [Google Scholar] [CrossRef] [PubMed]
  149. Alarcon, E.I.; Udekwu, K.I.; Noel, C.W.; Gagnon, L.B.P.; Taylor, P.K.; Vulesevic, B.; Simpson, M.J.; Gkotzis, S.; Islam, M.M.; Lee, C.-J.; et al. Safety and efficacy of composite collagen–silver nanoparticle hydrogels as tissue engineering scaffolds. Nanoscale 2015, 7, 18789–18798. [Google Scholar] [CrossRef]
  150. Wahid, F.; Zhong, C.; Wang, H.-S.; Hu, X.-H.; Chu, L.-Q. Recent Advances in Antimicrobial Hydrogels Containing Metal Ions and Metals/Metal Oxide Nanoparticles. Polymers 2017, 9, 636. [Google Scholar] [CrossRef] [PubMed]
  151. Nešović, K.; Janković, A.; Radetić, T.; Vukašinović-Sekulić, M.; Kojić, V.; Živković, L.; Perić-Grujić, A.; Rhee, K.Y.; Mišković-Stanković, V. Chitosan-based hydrogel wound dressings with electrochemically incorporated silver nanoparticles—In vitro study. Eur. Polym. J. 2019, 121, 109257. [Google Scholar]
  152. Lopez-Carrizales, M.; Mendoza-Mendoza, E.; Peralta-Rodriguez, R.D.; Pérez-Díaz, M.A.; Portales-Pérez, D.; Magaña-Aquino, M.; Aragón-Piña, A.; Infante-Martínez, R.; Barriga-Castro, E.D.; Sánchez-Sánchez, R.; et al. Characterization, antibiofilm and biocompatibility properties of chitosan hydrogels loaded with silver nanoparticles and ampicillin: An alternative protection to central venous catheters. Colloids Surf. B Biointerfaces 2020, 196, 111292. [Google Scholar] [CrossRef]
  153. Yazdimamaghani, M.; Vashaee, D.; Assefa, S.; Walker, K.J.; Madihally, S.V.; Köhler, G.A.; Tayebi, L. Hybrid macroporous gelatin/bioactive-glass/nanosilver scaffolds with controlled degradation behavior and antimicrobial activity for bone tissue engineering. J. Biomed. Nanotechnol. 2014, 10, 911–931. [Google Scholar] [CrossRef]
  154. You, J.; Raghunathan, V.K.; Son, K.J.; Patel, D.; Haque, A.; Murphy, C.J.; Revzin, A. Impact of nanotopography, heparin hydrogel microstructures, and encapsulated fibroblasts on phenotype of primary hepatocytes. ACS Appl. Mater. Interfaces 2015, 7, 12299–12308. [Google Scholar] [CrossRef]
  155. Hu, Y.; You, J.-O.; Aizenberg, J. Micropatterned hydrogel surface with high-aspect-ratio features for cell guidance and tissue growth. ACS Appl. Mater. Interfaces 2016, 8, 21939–21945. [Google Scholar]
  156. Santander-Borrego, M.; Taran, E.; Shadforth, A.M.A.; Whittaker, A.K.; Chirila, T.V.; Blakey, I. Hydrogels with Lotus Leaf Topography: Investigating Surface Properties and Cell Adhesion. Langmuir 2017, 33, 485–493. [Google Scholar] [CrossRef] [PubMed]
  157. Guvendiren, M.; Burdick, J.A. The control of stem cell morphology and differentiation by hydrogel surface wrinkles. Biomaterials 2010, 31, 6511–6518. [Google Scholar] [CrossRef]
  158. Vignesh, S.; Gopalakrishnan, A.; M.R., P.; Nair, S.V.; Jayakumar, R.; Mony, U. Fabrication of micropatterned alginate-gelatin and k-carrageenan hydrogels of defined shapes using simple wax mould method as a platform for stem cell/induced Pluripotent Stem Cells (iPSC) culture. Int. J. Biol. Macromol. 2018, 112, 737–744. [Google Scholar] [CrossRef]
  159. Jayasinghe, H.G.; Madihally, S.V.; Vasquez, Y. Formation of stem cell aggregates and their differentiation on surface-patterned hydrogels based on poly(2-hydroxyethyl methacrylate). ACS Appl. Bio Mater. 2019, 2, 4911–4921. [Google Scholar] [CrossRef]
  160. Pocivavsek, L.; Ye, S.-H.; Pugar, J.; Tzeng, E.; Cerda, E.; Velankar, S.; Wagner, W.R. Active wrinkles to drive self-cleaning: A strategy for anti-thrombotic surfaces for vascular grafts. Biomaterials 2019, 192, 226–234. [Google Scholar] [PubMed]
  161. Epstein, A.K.; Hong, D.; Kim, P.; Aizenberg, J. Biofilm attachment reduction on bioinspired, dynamic, micro-wrinkling surfaces. New J. Phys. 2013, 15, 095018. [Google Scholar] [CrossRef]
  162. Shivapooja, P.; Wang, Q.; Orihuela, B.; Rittschof, D.; López, G.P.; Zhao, X. Bioinspired Surfaces with Dynamic Topography for Active Control of Biofouling. Adv. Mater. 2013, 25, 1430–1434. [Google Scholar] [CrossRef] [PubMed]
  163. Zarzar, L.D.; Aizenberg, J. Stimuli-Responsive Chemomechanical Actuation: A Hybrid Materials Approach. Acc. Chem. Res. 2014, 47, 530–539. [Google Scholar] [CrossRef]
  164. Thompson, L.F. An Introduction to Lithography. In Introduction to Microlithography; American Chemical Society: Washington, DC, USA, 1983; Volume 219, pp. 1–13. [Google Scholar]
  165. Zhao, X.-M.; Xia, Y.; Whitesides, G.M. Soft lithographic methods for nano-fabrication. J. Mater. Chem. 1997, 7, 1069–1074. [Google Scholar] [CrossRef]
  166. Xia, Y.; Whitesides, G.M. Soft lithography. Annu. Rev. Mater. Sci. 1998, 28, 153–184. [Google Scholar] [CrossRef]
  167. del Campo, A.; Arzt, E. Fabrication approaches for generating complex micro- and nanopatterns on polymeric surfaces. Chem. Rev. 2008, 108, 911–945. [Google Scholar] [CrossRef]
  168. Cutiongco, M.F.A.; Goh, S.H.; Aid-Launais, R.; Le Visage, C.; Low, H.Y.; Yim, E.K.F. Planar and tubular patterning of micro and nano-topographies on poly(vinyl alcohol) hydrogel for improved endothelial cell responses. Biomaterials 2016, 84, 184–195. [Google Scholar]
  169. Kim, J.; Minh, N.H.; Kwon, D.I.; Kim, K.; Kang, D.H.; Yeong-Eun, Y.; Yoon, J.S. Photonic crystal hydrogels based on highly reproducible molding method. Sci. Rep. 2025, 15, 26044. [Google Scholar] [CrossRef]
  170. Hribar, K.C.; Choi, Y.S.; Ondeck, M.; Engler, A.J.; Chen, S. Digital Plasmonic Patterning for Localized Tuning of Hydrogel Stiffness. Adv. Funct. Mater. 2014, 24, 4922–4926. [Google Scholar] [CrossRef]
  171. Posada, V.M.; Ramírez, J.; Civantos, A.; Fernández-Morales, P.; Allain, J.P. Ion-bombardment-driven surface modification of porous magnesium scaffolds: Enhancing biocompatibility and osteoimmunomodulation. Colloids Surf. B Biointerfaces 2024, 234, 113717. [Google Scholar] [PubMed]
  172. Posada, V.M.; Marin, A.; Mesa-Restrepo, A.; Nashed, J.; Allain, J.P. Enhancing silk fibroin structures and applications through angle-dependent Ar+ plasma treatment. Int. J. Biol. Macromol. 2024, 257, 128352. [Google Scholar]
  173. Tang, M.D.; Golden, A.P.; Tien, J. Molding of three-dimensional microstructures of gels. J. Am. Chem. Soc. 2003, 125, 12988–12989. [Google Scholar] [CrossRef] [PubMed]
  174. Kim, H.N.; Kang, D.-H.; Kim, M.S.; Jiao, A.; Kim, D.-H.; Suh, K.-Y. Patterning methods for polymers in cell and tissue engineering. Ann. Biomed. Eng. 2012, 40, 1339–1355. [Google Scholar] [CrossRef]
  175. Jayasinghe, H.G.; Tormos, C.J.; Khan, M.; Madihally, S.; Vasquez, Y. A soft lithography method to generate arrays of microstructures onto hydrogel surfaces. J. Polym. Sci. Part B Polym. Phys. 2018, 56, 1144–1157. [Google Scholar] [CrossRef]
  176. Chandra, D.; Taylor, J.A.; Yang, S. Replica molding of high-aspect-ratio (sub-)micron hydrogel pillar arrays and their stability in air and solvents. Soft Matter 2008, 4, 979–984. [Google Scholar]
  177. Cui, L.; Yao, Y.; Yim, E.K.F. The effects of surface topography modification on hydrogel properties. APL Bioeng. 2021, 5, 031509. [Google Scholar] [CrossRef]
  178. He, G.; Liu, W.; Liu, Y.; Wei, S.; Yue, Y.; Dong, L.; Yu, L. Antifouling hydrogel with different mechanisms: Antifouling mechanisms, materials, preparations and applications. Adv. Colloid Interface Sci. 2025, 335, 103359. [Google Scholar]
  179. Dundar Arisoy, F.; Kolewe, K.W.; Homyak, B.; Kurtz, I.S.; Schiffman, J.D.; Watkins, J.J. Bioinspired Photocatalytic Shark-Skin Surfaces with Antibacterial and Antifouling Activity via Nanoimprint Lithography. ACS Appl. Mater. Interfaces 2018, 10, 20055–20063. [Google Scholar] [CrossRef] [PubMed]
  180. Arias, S.L.; Cheng, M.K.; Civantos, A.; Devorkin, J.; Jaramillo, C.; Allain, J.P. Ion-Induced Nanopatterning of Bacterial Cellulose Hydrogels for Biosensing and Anti-Biofouling Interfaces. ACS Appl. Nano Mater. 2020, 3, 6719–6728. [Google Scholar]
  181. Park, H.-H.; Sun, K.; Seong, M.; Kang, M.; Park, S.; Hong, S.; Jung, H.; Jang, J.; Kim, J.; Jeong, H.E. Lipid-Hydrogel-Nanostructure Hybrids as Robust Biofilm-Resistant Polymeric Materials. ACS Macro Lett. 2019, 8, 64–69. [Google Scholar]
  182. Heedy, S.; Marshall, M.E.; Pineda, J.J.; Pearlman, E.; Yee, A.F. Synergistic Antimicrobial Activity of a Nanopillar Surface on a Chitosan Hydrogel. ACS Appl. Bio Mater. 2020, 3, 8040–8048. [Google Scholar] [CrossRef]
  183. Wang, M.; Zheng, Y.; Yin, C.; Dai, S.; Fan, X.; Jiang, Y.; Liu, X.; Fang, J.; Yi, B.; Zhou, Q.; et al. Recent Progress in antibacterial hydrogel coatings for targeting biofilm to prevent orthopedic implant-associated infections. Front. Microbiol. 2023, 14, 1343202. [Google Scholar] [CrossRef]
  184. Chandra, D.; Yang, S. Stability of High-Aspect-Ratio Micropillar Arrays against Adhesive and Capillary Forces. Acc. Chem. Res. 2010, 43, 1080–1091. [Google Scholar] [PubMed]
  185. Ullah, A.; Kim, D.Y.; Lim, S.I.; Lim, H.-R. Hydrogel-Based Biointerfaces: Recent Advances, Challenges, and Future Directions in Human–Machine Integration. Gels 2025, 11, 232. [Google Scholar] [PubMed]
Figure 1. Stages in the formation of microbial biofilms on a surface.
Figure 1. Stages in the formation of microbial biofilms on a surface.
Gels 12 00146 g001
Figure 2. The classification of strategies used to combat biofilms on biomaterials.
Figure 2. The classification of strategies used to combat biofilms on biomaterials.
Gels 12 00146 g002
Figure 3. Types of regular nanotopographies.
Figure 3. Types of regular nanotopographies.
Gels 12 00146 g003
Figure 4. Microorganisms orient in different ways to overcome barriers that restrict the attachment to a surface. (a) The entire substrate is available for microbial attachment, (b) When the spacing or gap between the neighboring features is larger than the size of a cells, the microbial cell can lie between the features, (c) Gaps smaller than the size of a microbe force cells to stay on top of the features, decreasing the accessible surface area, and (d) Microbes with appendages like flagella can fit into the trenches to access the surface between the features.
Figure 4. Microorganisms orient in different ways to overcome barriers that restrict the attachment to a surface. (a) The entire substrate is available for microbial attachment, (b) When the spacing or gap between the neighboring features is larger than the size of a cells, the microbial cell can lie between the features, (c) Gaps smaller than the size of a microbe force cells to stay on top of the features, decreasing the accessible surface area, and (d) Microbes with appendages like flagella can fit into the trenches to access the surface between the features.
Gels 12 00146 g004
Figure 5. Different mechanisms through which nanopatterned surfaces combat biofilms.
Figure 5. Different mechanisms through which nanopatterned surfaces combat biofilms.
Gels 12 00146 g005
Figure 6. Widely used surface patterning techniques.
Figure 6. Widely used surface patterning techniques.
Gels 12 00146 g006
Table 1. Types of microorganisms that form biofilms on indwelling medical devices and implants.
Table 1. Types of microorganisms that form biofilms on indwelling medical devices and implants.
Medical Device/ImplantType of MicroorganismReferences
Urinary catheters E. coli, Providencia stuartii, Enterococcus, Pseudomonas, Enterobacter, Candida, and Serratia species[26,27,28]
Central venous cathetersS. aureus, S. epidermidis, P. aeruginosa, Bacilli, Klebsiella, and Candida species[29,30]
Contact lensesP. aeruginosa, Serratia marcescens, S. aureus[31]
Prosthetic jointsS. aureus, S. epidermidis, P. aeruginosa, E. coli, Streptococcus, and Enterococcus species[32,33]
Mechanical heart valvesS. aureus, S. epidermidis, Streptococcus, Bacillus, Enterococcus, and Candida species[29]
Intravascular devices (cardiac pacemakers)S. aureus, S. epidermidis, Propionibacterium acnes[28,34]
Voice prosthesesRothia dentocariosa, Staphylococcus, Streptococcus, Escherichia, Enterobacter, Proteus, Pseudomonas, and Candida species[35,36,37]
Endotracheal tubeS. aureus, S. epidermidis, Kocuria varians, Acinetobacter baumannii, P. aeruginosa[38,39]
Breast implantsS. aureus and S. epidermidis[40,41]
Table 2. A comparison of different biofilms.
Table 2. A comparison of different biofilms.
Bacterial BiofilmsFungal BiofilmsMixed (Polymicrobial) Biofilms
Gram-PositiveGram-Negative
Contains species such as S. aureus, S. epidermidis, E. faecalis, and Streptococcus pneumoniae [45]Contains species such as E. coli, K. pneumoniae, A. baumannii, P. mirabilis, and P. aeruginosa [46] Contains Candida species, including C. parapsilosis, C. tropicalis, C. krusei, and C. glabrata, and other species such as Cryptococcus neoformans, Coccidioides immitis, Aspergillus species, Fusarium species, Blastoschizomyces capitatus, Malassezia pachydermatis, Pneumocystis species, Trichosporon asahii, Rhizopus species, and Rhizomucor species [47]Contain bacteria (Gram-positive/negative) and fungi, may contain viruses or algae [48,49]
Secrete polysaccharides, proteins, teichoic and lipoteichoic acids, membrane vesicles (MV), and extracellular DNA (eDNA) [50,51]Secrete polysaccharides, amyloid proteins, lipopolysaccharides (LPS), outer membrane vesicles (OMVs), and specific types of amyloid fibers [51]Polysaccharides, proteins, lipids, and Edna [52]. For example, biofilms of C. albicans contain proteins, chitins, DNA, and β-1,3 glucan carbohydrates. C. neoformans biofilms consist of xylose, mannose, glucose, and several minor sugars. A. fumigatus produces galactosaminogalactan and galactomannan as the major polysaccharides [53]Compared to other types, they have higher biofilm masses, higher community cell count, enhanced metabolic activity, prominent antimicrobial tolerance, and changes in spatial organization and structure [54]
Can grow on catheters and prosthetic implants [45]Can be found in water bodies and mammalian intestine [51]Can grow on central urinary catheters, venous catheters, prosthetic valves, left ventricular assist devices, and oral devices, such as dentures [55]Found in the oral cavity, mammalian intestines, and implantable medical devices [48]
Note: Gram-negative bacteria have lipopolysaccharides (LPS) in their cell membrane. In contrast, Gram-positive bacteria have teichoic acid (TA) in their cell wall. Both LPS and TA, which provide charges on the outer surface of bacteria, may influence bacterial adherence to surfaces. Therefore, these compounds may influence biofilm formation [51]. Both Gram-positive and Gram-negative bacterial biofilms are found in similar environments, such as moist surfaces with access to nutrients.
Table 3. Advantages and disadvantages of general methods used to prevent biofilms.
Table 3. Advantages and disadvantages of general methods used to prevent biofilms.
MethodAdvantagesDisadvantages
Surface topographical modificationsDo not use antibiotics or any other drugs that can be toxic to host tissues (morphologically disturb microbial attachment). No antibiotic resistance. Do not affect the properties of the bulk material (e.g., biocompatibility)There is a chance to form the biofilm if host proteins (in blood and serum) are attached to the surface.
Antimicrobial coatings (antibiotics, antimicrobial peptides (AMPs), etc.)Active only on the site of application. Increases the concentration of the antimicrobial agent locally. Low chance of antimicrobial resistance when AMPs are usedEffective only for a short time due to the limited supply of the antimicrobial agent
Incorporation of antibiotics Can locally increase the antibiotic concentration May be effective only for a short period due to the depletion of materials.
May cause local toxicity to the host tissues
Incorporation of nanoparticlesPreferential and controlled delivery over a long period of time. Delivery of multiple agents simultaneously improved efficacyCan be incompatible and toxic to the host tissue. Environmental safety issues
Use of biological inhibitorsSome agents exhibit multiple effects, such as interfering with signaling pathways and destroying mature biofilms. Low toxicity to the host tissueMay become cytotoxic at high concentrations. Poor solubility and rapid metabolic degradation may cause issues.
Table 4. Mechanisms of biofilm inhibition by nanoparticles.
Table 4. Mechanisms of biofilm inhibition by nanoparticles.
Type of NanoparticlesMechanismTested OrganismRefs.
Metal nanoparticles (e.g., Ag, Au, Pt, Ni, Cu, etc.)Generation of ROS, disruption of biofilm matrix, membrane disruption, and inhibition of biofilm adhesion proteinsVarious Gram-positive and negative bacteria, S. aureus, S. epidermidis, E. coli, Bacillus subtilis[93,94,95,96,97,98]
Metal oxide nanoparticles (e.g., ZnO, Fe3O4, MgO)Generation of ROS, Immune modulation, Disruption of established biofilms, Membrane disruptionP. aeruginosa, S. aureus, E. coli[99,100,101,102]
Polymers (e.g., Chitosan-alginate)Membrane disruptionS. aureus, P. acnes[103]
Liposome-based nanoparticlesTarget delivery of antibiofilm agents, Enhanced penetrationS. aureus[104]
Composites (e.g., Berberine, silver nanoparticles, and carboxylated chitosan) Membrane disruptionS. aureus[105]
Table 5. A comparison of alternative lithography methods.
Table 5. A comparison of alternative lithography methods.
Patterning TechniqueAdvantagesDisadvantagesRefs.
Casting
Crosslinking of the hydrogel in a patterned mold
Simple, economical, and versatile method. Has the potential to pattern non-planar surfacesLimited to micron-sized patterns due to the low wetting properties between the hydrogel and the mold[168]
Nanoimprint lithography (NIL)
A hot embossing process conducted at high pressure
A low-cost, high-throughput patterning methodLimited use with hydrogel materials due to required high pressure and high temperature conditions, a complex imprinting process, high mold-fabrication costs, demolding that can cause pattern distortion or sticking, and molds that are prone to wear or contamination over repeated cycles.[169]
Digital plasmonic patterning (DPP)
Uses nanoparticles with plasmonic resonance to pattern a computer-generated pattern on hydrogel
Stiffness can be modulated by varying the laser intensity, writing speed, and digital pattern, thereby providing greater flexibility and eliminating the need for multiple polymer solutions or physical masks.High cost
Time consuming
[170]
Directed plasma nanosynthesis (DPNS)
Uses Ion bombardment to generate nanostructures on hydrogels
Can fabricate high-precision nanostructures, a cost-effective, eco-friendly solution due to the use of non-toxic Argon plasmaExpensive[171,172]
Table 6. A summary of surface-patterned hydrogel systems.
Table 6. A summary of surface-patterned hydrogel systems.
PolymerFeature SizeFabrication MethodTested OrganismRef.
poly(ethylene terephthalate) shark skin patterns combined with titanium dioxide (TiO2) nanoparticlesMold 1: height: 3 µm, width: 2 µm, pitch: 4 µm
Mold 2: height: 1.6 μm, width: 1.3 μm, pitch: 4 μm
Shark skin patterns were made with solvent-assisted soft nanoimprint lithography E. coli K12 MG1655[179]
Bacterial cellulose493 nm (etched thickness)Directed plasma nanosynthesis (DPNS)None (Mentioned the potential of antifouling applications)[180]
polyethylene glycol-based polymer grafted with 2-methacryloyloxyethyl phosphorylcholine
(nano needles)
50 nm in tip diameter, 200 nm in bottom diameter, 300 nm in height, and 500 nm in center-to-center pitchUltraviolet (UV) replica molding techniqueE. coli, B. subtilis[181]
Chitosan hydrogel films with nanopillarsPattern 1: Periodicity 320 nm, diameter 120 nm, height 230 nm, aspect ratio 1:9; pattern 2: Periodicity 500 nm, diameter 190 nm, height 400 nm, aspect ratio 2:1solvent-assisted dropcast lithographyP. aeruginosa (bacteria) and Fusarium oxysporum (Fungi)[182]
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Jayasinghe, H.G.; Madduma-Bandarage, U.S.K.; Madihally, S.V. Nanostructured Hydrogels: A Method to Prevent Biofilms on Implantable Medical Devices. Gels 2026, 12, 146. https://doi.org/10.3390/gels12020146

AMA Style

Jayasinghe HG, Madduma-Bandarage USK, Madihally SV. Nanostructured Hydrogels: A Method to Prevent Biofilms on Implantable Medical Devices. Gels. 2026; 12(2):146. https://doi.org/10.3390/gels12020146

Chicago/Turabian Style

Jayasinghe, Hasani G., Ujith S. K. Madduma-Bandarage, and Sundar V. Madihally. 2026. "Nanostructured Hydrogels: A Method to Prevent Biofilms on Implantable Medical Devices" Gels 12, no. 2: 146. https://doi.org/10.3390/gels12020146

APA Style

Jayasinghe, H. G., Madduma-Bandarage, U. S. K., & Madihally, S. V. (2026). Nanostructured Hydrogels: A Method to Prevent Biofilms on Implantable Medical Devices. Gels, 12(2), 146. https://doi.org/10.3390/gels12020146

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Article metric data becomes available approximately 24 hours after publication online.
Back to TopTop