Next Article in Journal
High Electrochemical Performance Phosphorus-Oxide Modified Graphene Electrode for Redox Supercapacitors Prepared by One-Step Electrochemical Exfoliation
Previous Article in Journal
Photocatalytic Degradation of Tetracycline Hydrochloride via a CdS-TiO2 Heterostructure Composite under Visible Light Irradiation
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 8
Issue 6
10.3390/nano8060416
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Modified Sequential Deposition Route through Localized-Liquid-Liquid-Diffusion for Improved Perovskite Multi-Crystalline Thin Films with Micrometer-Scaled Grains for Solar Cells

by
Tao Ling
,
Xiaoping Zou
*,
Jin Cheng
,
Xiao Bai
,
Haiyan Ren
and
Dan Chen
Research Center for Sensor Technology, Beijing Key Laboratory for Sensor, Ministry of Education Key Laboratory for Modern Measurement and Control Technology, School of Applied Sciences, Beijing Information Science and Technology University, Jianxiangqiao Campus, Beijing 100101, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2018, 8(6), 416; https://doi.org/10.3390/nano8060416
Submission received: 13 May 2018 / Revised: 30 May 2018 / Accepted: 6 June 2018 / Published: 9 June 2018
Browse Figures
Versions Notes

Abstract

:
High-class perovskite film with beautiful surface morphology (such as large-size grain, low defect density, good continuity and flatness) is normally believed to be a very important factor for high-efficiency perovskite solar cells (PSCs). Here, we report a modified sequential deposition route through localized-liquid-liquid-diffusion (LLLD) for qualified perovskite multi-crystalline thin films with micrometer-scaled grains for solar cells. We adopted a contact-type drop method to drop Methylammonium iodide (MAI) solution and have successfully used high-concentration MAI solution (73 mg/mL) to transform PbI2 film into high-class perovskite film via our route. A high efficiency of 10.7% was achieved for the device with spongy carbon film deposited on a separated FTO-substrate as a counter electrode under one sun illumination, which is the highest efficiency (as 2.5 times as previous efficiency) ever recorded in perovskite solar cells with a such spongy carbon/FTO composite counter electrode. The preparation techniques of high-class perovskite thin films under ambient conditions and the cheap spongy carbon/FTO composite counter electrode are beneficial for large-scale applications and commercialization.

Graphical Abstract

1. Introduction

In recent years, perovskite solar cells (PSCs) have been recognized as the most promising alternative to conventional photovoltaic devices due to their high efficiency and simple process [1,2,3]. High-class perovskite thin film, with beautiful surface morphology (such as large-size grain, low defect density, good continuity, and flatness), is normally believed to be a very important factor for high-efficiency perovskite solar cells [4,5,6,7,8]. M. Grätzel et al. firstly developed the sequential deposition method (so-called two-step method) to prepare CH3NH3PbI3 perovskite thin films [9]. Since then, a lot of effort has been paid to developing the two-step method, similar to the two-step spin-coating process [10,11,12], and Xu et al. have demonstrated that the two-step spin coating method enables perovskite layer morphology to control and easily fabricate products [13]. Previous researchers prepared perovskite films via the conventional two-step coating method with a necessary step of PbI2 layer annealing [9,10,11,12,13]. In fact, we found the properties of the perovskite thin film are very sensitive to the annealing time of PbI2 layer especially under the dry ambient conditions used in our experiments.
Xu et al.’s previous study on the effect of humidity on the crystallization of two-step spin-coated perovskites suggested that appropriate moisture can facilitate the reaction between PbI2 and MAX (X = I, Cl), whereas the PbI2 film reacts with MAX slowly a under dry inert atmosphere [14]. H2O helps MAI to penetrate into the thick PbI2 to form thick film with a pure MAPbI3 phase and produce bigger gains by slowing down the perovskite crystallization rate [15]. However, the dry atmosphere (~10% relative humidity) was our experimental condition.
In order to explore the effect of the annealing time of PbI2 thin film on properties of corresponding perovskite thin film, we annealed PbI2 film at 70 °C for 0 s, 10 s, and 20 s, respectively. We found that the 0 s annealing PbI2 film was more conducive to the formation of high-class perovskite films in our experiment, which means that the sequential deposition route through LLLD is more conducive to the formation of qualified perovskite multi-crystalline films. In addition, we adopted a contact-type drop method to drop MAI solution in order to reduce the damage of MAI solution to PbI2 thin liquid film (illustrated in Figure 1).
Previously, if MAI concentration is too high (≥70 mg/mL), most of the PbI2 precursor gets dissolved and exists as PbI42− in the solution, and only very little can reprecipitate to form MAPbI3 nanostructures [16]. Im et al. found that the size of the MAPbI3 cuboids increases with decreasing CH3NH3I concentration [17]. However, the MAI concentration in our experiment was 73 mg/mL and the corresponding MAI solution also successfully transformed PbI2 film into high-class perovskite film via LLLD. A high-class perovskite film with micrometer-scaled grain, low defect density, densification, and flatness was obtained by our process.
The tune of the formation process and composition of the light-absorber layer in PSCs has contributed to obtaining certified power conversion efficiencies (PCE) > 20% [18,19]. These PCEs have been obtained while perovskite solar cells were prepared using the single-step method (in combination with solvent engineering) or sequential deposition method or vapor deposition with an important step of device fabrication being the thermal evaporation of metals to form the counter electrode (CE). However, the cost of these metallic CEs is prohibitively high for large-scale applications and commercialization.
Up to now, some researchers have developed carbon CEs to cut the costs of perovskite devices [20,21,22,23]. Yang et al. prepared a 2.6%-efficient perovskite solar cell with candle soot film deposited on a separated substrate as the carbon/FTO composite counter electrode [22]. In our research group, previously, a spongy carbon/FTO composite structure was adopted as a counter electrode and the corresponding cell achieved 4.24% power conversion efficiency (PCE) [23]. The perovskite solar cell was prepared via a modified sequential deposition route through LLLD under dry ambient conditions and got a 10.7% PCE in the size of 0.2 cm2, which is the highest efficiency ever recorded in perovskite solar cells with such a spongy carbon/FTO composite counter electrode.

2. Materials and Methods

2.1. Materials

Fluorine-doped SnO2 (FTO) substrates were obtained from Dalian HeptaChroma Solar Technology Development Corp (Dalian, China). N,N-dimethylformamide (DMF) and dimethyl sulfoxide (DMSO) were purchased from Sa’en Chemical Technology Corp (Shanghai, China). PbI2, 18NR-T TiO2 paste (mp-TiO2), acidic titanium dioxide solution (bl-TiO2), Methylammonium iodide (MAI), and isopropyl alcohol (IPA) were purchased from Shanghai MaterWin New Materials Corp, (Shanghai, China). Spiro-OMeTAD solution was purchased from Xi’an Polymer Light Technology Corp (Xi’an, China).

2.2. Device Fabrication

Fluorine-doped SnO2 (FTO) substrates were ultrasonically cleaned with mixed solution (detergent and deionized water), glass water (acetone:deionized water:2-propanol = 1:1:1), and alcohol, respectively. Before using, the FTO was cleaned by Ultraviolet Ozone (UVO) for 90 min. Compact TiO2 layer (bl-TiO2) was deposited on FTO substrate by spin-coating an acidic titanium dioxide solution at 2000 rpm for 60 s. Then the substrate was annealed on a hotplate at 100 °C for 10 min, and sintered in a muffle furnace at 500 °C for 30 min. Mesoporous TiO2 film (mp-TiO2) was coated on bl-TiO2 thin film by spin coating using a commercial 18NR-T TiO2 paste (4%, solid content) at 2000 rpm for 30 s. Subsequently, the substrate was dried on a hotplate at 100 °C for 10 min, and then sintered in a muffle furnace at 500 °C for 60 min. After that, 599.3 mg of PbI2 was dissolved in a component solvent (DMF:DMSO = 9.5:0.5) and then spin-coated onto a TiO2 (bl-TiO2 and mp-TiO2) layer at 1500 rpm for 30 s, and then annealed on a hotplate at 70 °C for 0 s, 10 s, and 20 s, respectively.
After the PbI2 film had cooled down to room temperature, the MAI solution (73 mg in 1 mL IPA) was spin coated onto the PbI2 layer at 1500 rpm for 30 s (without loading time), and then a thermal annealing of 150 °C for 15 min under low humidity air condition (~10% humidity) was processed. The hole transporting layer was deposited on top of the perovskite layer by 3000 rpm for 30 s using a commercial 2,2′,7,7′-tetrakis(N,N-dip-methoxyphenylamine)-9,9′-spirobifluorene (Spiro-OMeTAD) solution. Finally, some cleaned FTO glasses were used as substrates to obtain the soot of a burning candle as spongy carbon CEs. The spongy carbon films on FTO glasses were then pressed on the as-prepared uncompleted devices.

2.3. Characterization

An X-ray diffractometer (XRD) (Broker, D8 Focus, Beijing, China) was used to obtain XRD spectra from samples of perovskite films deposited on mp-TiO2/bl-TiO2/FTO substrates. The morphologies of these perovskite films were watched by a scanning electron microscope (SEM) (Zeiss SIGMA). The as-prepared devices were measured under full sun illumination (AM 1.5, 100 mW/cm2).

3. Results and Discussion

In order to reduce the possible damage of the MAI solution to PbI2 thin liquid film, we adopted a contact-type drop method to drop MAI solution (illustrated in Figure 1a), and the resulting perovskite films are shown in Figure 1b. In contrast to the non-contact-type drop method, this drop method reduced the damage of the MAI solution to PbI2 thin film according to Figure 1b.
The perovskite films were prepared by sequential deposition route with PbI2 0 s, 10 s, and 20 s annealing, which are named as sample A, sample B, and sample C, respectively. Scanning electron microscopy (SEM) images and image of perovskite layers prepared by two-step spin-coating with different PbI2 annealing times are shown in Figure 2. We found that the surfaces of the perovskite layers gradually became a white color with the increase of PbI2 annealing time, according to the image (Figure 2a) of the perovskite layers. From the surface SEM image (Figure 2b–d), it can be found that sample A showed obvious densification, sample B and C have double layers, and the bottom layer is dense and the top layer is loose. PbI2 solution film reacts with MAI solution to form a high-class perovskite thin film with beautiful surface morphology (such as large-size grain, low defect density, good continuity, and flatness) via LLLD, whereas, PbI2 solid film reacts with MAI solution to form loose perovskite thin film via localized-solid-liquid-diffusion (LSLD). The bottom layers of sample B and C are observed to contain large-size grain, but the top layer of sample B shows some small square holes and the top layer of sample C shows massive square unordered holes.
In the cross-sectional SEM image (Figure 2e) of sample A, we can see the FTO layer, bl-TiO2 layer, mp-TiO2 layer and perovskite layer clearly from the bottom to the top, and the longitudinal size of perovskite grains equal to the film thickness. This qualified perovskite film (sample A) indicates that the modified sequential deposition route through LLLD is beneficial to the growth of perovskite crystals under dry ambient condition and enhancement of the corresponding photovoltaic performance.
Figure 3 shows XRD pattern of the samples prepared by two-step spin-coating method with different PbI2 annealing times. According to the Figure 3, there are no peaks of PbI2 (corresponding to ~26°) and MAI (corresponding to ~19°), which means there are no residuals of PbI2 and MAI in the samples, and the compositions of perovskites in the samples are very pure. As the PbI2 annealing time increased to 10 s, the (004) peak of the tetragonal structure for CH3NH3PbI3 emerged, which indicates a phase transition from cubic to tetragonal structure [24]. This result suggest that the perovskite in sample A and bottom layers of sample B and C is cubic structure, and the perovskite in top layers of sample B and C is tetragonal structure. In addition, the intensity ratio (~2.06) of the highest peak (110) of sample A to its secondary peak (220) is lightly above that of others (~1.93 and ~2.01). The above points means the crystal structure of sample A is better than others and sequential deposition route through LLLD is more propitious to the formation of qualified perovskite multi-crystalline films, which can enhance the corresponding device efficiency.
Schematic illustrations for LLLD and LSLD for qualified perovskite multi-crystalline film are shown in Figure 4a. As PbI2 annealing time increases, its solid part and the ratio of LLLD with MAI solution decreases. The changes in the morphology of the perovskite have finally happened. Due to the 0 s annealing PbI2 film was the solution state, and MAI could more easily diffuse to the PbI2 thin film interior via LLLD and transform PbI2 film into a high-class cubic structure perovskite film. Moreover, the PbI2 thin film had some of the solvent of DMF, which could facilitate perovskite conversion, improve the film morphology, and reduce crystal defects, and thus enhance charge transfer efficiency [25]. Due to the annealing time being relatively short, there are double layers in the 10 s annealing PbI2 film and 20 s annealing PbI2 film. The top layer is solid state, as a result of contacting with air during the spin-coating. MAI is difficult to diffuse to the solid top layer of the PbI2 thin film interior via LSLD and transform into poor perovskite film with a tetragonal structure. The bottom layer is in solution state for having not made contact with air during the spin-coating, which is similar to sample A, and can be transformed into a high-class cubic structure perovskite film. The hydrolysis of perovskite must be reduced because it was prepared in dry air. A combination of the above factors lead to the high-class perovskite films being fabricated by the sequential deposition route through LLLD under dry ambient conditions and the structure of the corresponding devices with the low-cost spongy carbon/FTO composite counter electrode is shown in Figure 4b.
Figure 5a,b show the light current-voltage (J-V) curves from reverse scan (RS) for the devices with a carbon/FTO composite electrode and gold electrode, measured under simulated sunlight with an intensity of 100 mW/cm2 (AM 1.5 G). According to the J-V curve, it is found that the device (corresponding to PbI2 0 s annealing) via the modified sequential deposition route through LLLD showed the best performance in major parameters (such as Voc, Jsc and PCE, and their detailed values can be seen in Table 1) and the others showed obvious attenuation in major parameters. To be sure of the efficacy of our new coating processes and the reliability of current density data, we measured the IPCE of the devices with a carbon/FTO composite electrode, and the results are shown in Figure 5c. Generally, the device performance is increased with the decrease of PbI2 annealing times, indicating that the sequential deposition route through LLLD is more conducive to the formation of qualified perovskite multi-crystalline films under dry ambient conditions.
According to the data of Table 1, it can be found that the photovoltaic performance of contact-type processed PSCs is better than the non-contact-type processed PSCs. This further validates the reduced damage of the MAI solution to the PbI2 thin film when dropping the MAI solution via contact-type method. A high efficiency of 10.7% was achieved for the device with the carbon/FTO composite electrode. Although this efficiency is not the highest in PSCs, it is the highest efficiency (as 2.5 times as previous efficiency) ever recorded in PSCs with such a spongy carbon/FTO composite counter electrode. Furthermore, the preparation techniques of high-class perovskite thin films and the cheap spongy carbon/FTO composite counter electrode, under absolute ambient conditions, are beneficial for large-scale applications and commercialization.

4. Conclusions

A modified sequential deposition route through LLLD was more conducive to the formation of qualified perovskite multi-crystalline thin films with micrometer-scaled grain, low defect density, densification, and flatness under dry ambient condition. The two diffusion mechanisms of LLLD and LSLD were suggested and preliminarily confirmed. A contact-type drop method to drop MAI solution can reduce the damage of MAI solution to PbI2 thin films, and high-concentration MAI solution can also transform PbI2 film into high-class perovskite film via our route. Moreover, a perovskite solar cell was prepared via the modified sequential deposition route through LLLD under absolute ambient conditions and got a 10.7% PCE in a size of 0.2 cm2, which is the highest efficiency ever recorded in perovskite solar cells with such a spongy carbon/FTO composite counter electrode. Obviously, a great deal of production of high-efficiency perovskite solar cells, with a low-cost spongy carbon/FTO composite counter electrode, under an absolutely ambient atmosphere, is possible.

Author Contributions

T.L. wrote the paper, designed the experiments. J.C. analyzed the data. X.B. and D.C. prepared the samples. H.R. performed all the measurements. X.Z. supervised the project. All authors commented and approved the paper.

Funding

This research was funded by Project of Natural Science Foundation of China (61376057), Project of Natural Science Foundation of Beijing (Z160002), Opened Fund of the State Key Laboratory on Integrated Optoelectronics (IOSKL2016KF19) and Beijing Key Laboratory for Sensors of BISTU (KF20181077203).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Park, N.-G. Organometal perovskite light absorbers toward a 20% efficiency low-cost solid-state mesoscopic solar cell. J. Phys. Chem. Lett. 2013, 4, 2423–2429. [Google Scholar] [CrossRef]
  2. Yin, X.; Guo, Y.J.; Xue, Z.; Xu, P.; He, M.; Liu, B. Performance enhancement of perovskite-sensitized mesoscopic solar cells using Nb-doped TiO2 compact layer. Nano Res. 2015, 8, 1997–2003. [Google Scholar] [CrossRef]
  3. Yang, W.S.; Noh, J.H.; Jeon, J.N.; Kim, Y.C.; Ryu, S.C.; Seo, S.J.; Seok, S.I.I. High-performance photovoltaic perovskite layers fabricated through intramolecular exchange. Science 2015, 348, 1234–1237. [Google Scholar] [CrossRef] [PubMed]
  4. Stranks, S.D.; Eperon, G.E.; Grancini, G.; Menelaou, C.; Alcocer, M.J.P.; Leijtens, T.; Herz, L.M.; Petrozza, A.; Snaith, H.J. Electron-Hole Diffusion Lengths Exceeding 1 Micrometer in an Organometal Trihalide Perovskite Absorber. Science 2013, 342, 341–344. [Google Scholar] [CrossRef] [PubMed]
  5. Xing, G.; Mathews, N.; Sun, S.; Lim, S.S.; Lam, Y.M.; Gratzel, M.; Mhaisalkar, S.; Sum, T.C. Long-range Balanced Electron- and Hole-Transport Lengths in Organic-Inorganic CH3NH3PbI3. Science 2013, 342, 344–347. [Google Scholar] [CrossRef] [PubMed]
  6. Eperon, G.E.; Burlakov, V.M.; Docampo, P.; Goriely, A.; Snaith, H.J. Morphological Control for High Performance, Solution-Processed Planar Heterojunction Perovskite Solar Cells. Adv. Funct. Mater. 2014, 24, 151–157. [Google Scholar] [CrossRef]
  7. Chen, Z.; Li, H.; Tang, Y.; Huang, X.; Ho, D.; Lee, C.-S. Shape-Controlled Synthesis of Organolead Halide Perovskite Nanocrystals and Their Tunable Optical Absorption. Mater. Res. Express 2014, 1, 015034. [Google Scholar] [CrossRef]
  8. Yin, W.J.; Shi, T.; Yan, Y. Unique Properties of Halide Perovskites as Possible Origins of the Superior Solar Cell Performance. Adv. Mater. 2014, 26, 4653–4658. [Google Scholar] [CrossRef] [PubMed]
  9. Burschka, J.; Pellet, N.; Moon, S.-J.; Humphry-Baker, R.; Gao, P.; Nazeeruddin, M.K.; Grätzel, M. Sequential Deposition as a Route to High-Performance Perovskite-Sensitized Solar Cells. Nature 2013, 499, 316–319. [Google Scholar] [CrossRef] [PubMed]
  10. Xiao, Z.; Dong, Q.; Bi, C.; Shao, Y.; Yuan, Y.; Huang, J. Solvent Annealing of Perovskite-Induced Crystal Growth for Photovoltaic-Device Efficiency Enhancement. Adv. Mater. 2014, 26, 6503–6509. [Google Scholar] [CrossRef] [PubMed]
  11. Xiao, Z.; Bi, C.; Shao, Y.; Dong, Q.; Wang, Q.; Yuan, Y.; Wang, C.; Gao, Y.; Huang, J. Efficient, High Yield Perovskite Photovoltaic Devices Grown by Interdiffusion of Solution-Processed Precursor Stacking Layers. Energy Environ. Sci. 2014, 7, 2619–2623. [Google Scholar] [CrossRef]
  12. Chae, J.; Dong, Q.; Huang, J.; Centrone, A. Chloride Incorporation Process in CH3NH3PbI3-xClx Perovskites via Nanoscale Bandgap Maps. Nano Lett. 2015, 15, 8114–8121. [Google Scholar] [CrossRef] [PubMed]
  13. Xu, Y.; Zhu, L.; Shi, J.; Lv, S.; Xu, X.; Xiao, J.; Dong, J.; Wu, H.; Luo, Y.; Li, D.; Meng, Q. Efficient Hybrid Mesoscopic Solar Cells with Morphology-Controlled CH3NH3PbI3-xClx Derived from Two-Step Spin Coating Method. ACS Appl. Mater. Interfaces 2015, 7, 2242. [Google Scholar] [CrossRef] [PubMed]
  14. Xu, Y.; Zhu, L.; Shi, J.; Xu, X.; Xiao, J.; Dong, J.; Wu, H.; Luo, Y.; Li, D.; Meng, Q. The Effect of Humidity upon the Crystallization Process of Two-Step Spin-Coated Organic-Inorganic Perovskites. ChemPhysChem 2016, 17, 112–118. [Google Scholar] [CrossRef] [PubMed]
  15. Chiang, C.H.; Nazeeruddin, M.K.; Grätzel, M.; Wu, C.G. The synergistic effect of H2O and DMF towards stable and 20% efficiency inverted perovskite solar cells. Energy Environ. Sci. 2017, 10, 808–817. [Google Scholar] [CrossRef]
  16. Fu, Y.; Meng, F.; Rowley, M.B.; Thompson, B.J.; Shearer, M.J.; Ma, D.; Hamers, R.J.; Wright, J.C.; Jin, S. Solution growth of single crystal methylammonium lead halide perovskite nanostructures for optoelectronic and photovoltaic applications. J. Am. Chem. Soc. 2015, 137, 5810–5818. [Google Scholar] [CrossRef] [PubMed]
  17. Im, J.H.; Jang, I.H.; Pellet, N.; Grätzel, M.; Park, N.G. Growth of CH3NH3PbI3 cuboids with controlled size for high-efficiency perovskite solar cells. Nat. Nanotechnol. 2014, 9, 927–932. [Google Scholar] [CrossRef] [PubMed]
  18. Kojima, A.; Teshima, K.; Shirai, Y.; Miyasaka, T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 2009, 131, 6050–6051. [Google Scholar] [CrossRef] [PubMed]
  19. Yang, W.S.; Park, B.-W.; Jung, E.H.; Jeon, N.J.; Kim, Y.C.; Lee, D.U.; Shin, S.S.; Seo, J.; Kim, E.K.; Noh, J.H.; et al. Iodide management in formamidinium-lead-halide-based perovskite layers for efficient solar cells. Science 2017, 356, 1376–1379. [Google Scholar] [CrossRef] [PubMed]
  20. Mei, A.; Li, X.; Liu, L.; Ku, Z.; Liu, T.; Rong, Y.G.; Xu, M.; Hu, M.; Chen, J.; Yang, Y.; et al. A hole-conductor-free, fully printable mesoscopic perovskite solar cell with high stability. Science 2014, 345, 295–298. [Google Scholar] [CrossRef] [PubMed]
  21. Habisreutinger, S.N.; Leijtens, T.; Eperon, G.E.; Stranks, S.D.; Nicholas, R.J.; Snaith, H.J. Carbon nanotube/polymer composites as a highly stable hole collection layer in perovskite solar cells. Nano Lett. 2014, 14, 5561–5568. [Google Scholar] [CrossRef] [PubMed]
  22. Wei, Z.; Yan, K.; Chen, H.; Yi, Y.; Zhang, T.; Long, X.; Li, J.; Zhang, L.; Wang, J.; Yang, S. Cost-efficient clamping solar cells using candle soot for hole extraction from ambipolar perovskites. Energy Environ. Sci. 2014, 7, 3326–3333. [Google Scholar] [CrossRef]
  23. Zhang, N.; Guo, Y.; Yin, X.; He, M.; Zou, X. Spongy carbon film deposited on a separated substrate as counter electrode for perovskite-based solar cell. Mater. Lett. 2016, 182, 248–252. [Google Scholar] [CrossRef]
  24. Luo, D.; Yu, L.; Wang, H.; Zou, T.; Luo, L.; Liu, Z.; Lu, Z. Cubic structure of the mixed halide perovskite CH3NH3PbI3-xClx via thermal annealing. RSC Adv. 2015, 5, 85480–85485. [Google Scholar] [CrossRef]
  25. Wu, J.; Xu, X.; Zhao, Y.; Shi, J.; Xu, Y.; Luo, Y.; Li, D.; Wu, H.; Meng, Q. DMF as an additive in two-step spin coating method for 20% conversion efficiency perovskite solar cells. ACS Appl. Mater. Interfaces 2017, 9, 26937–26947. [Google Scholar] [CrossRef] [PubMed]
Nanomaterials 08 00416 g001 550
Figure 1. Schematic illustrations for drop method and picture of perovskite films: (a) Schematic illustrations for contact-type method and non-contact-type method to drop MAI solution; (b) Picture of perovskite films dropped by contact-type method and non-contact-type method.
Figure 1. Schematic illustrations for drop method and picture of perovskite films: (a) Schematic illustrations for contact-type method and non-contact-type method to drop MAI solution; (b) Picture of perovskite films dropped by contact-type method and non-contact-type method.
Nanomaterials 08 00416 g001
Nanomaterials 08 00416 g002 550
Figure 2. SEM images and picture: (a) Surface picture of perovskite films prepared by sequential deposition route with different PbI2 annealing times (0 s, 10 s and 20 s; corresponding sample A, sample B and sample C); (b–d) Surface SEM images of sample A, sample B and sample C; (e) Cross-sectional SEM image of sample A.
Figure 2. SEM images and picture: (a) Surface picture of perovskite films prepared by sequential deposition route with different PbI2 annealing times (0 s, 10 s and 20 s; corresponding sample A, sample B and sample C); (b–d) Surface SEM images of sample A, sample B and sample C; (e) Cross-sectional SEM image of sample A.
Nanomaterials 08 00416 g002
Nanomaterials 08 00416 g003 550
Figure 3. X-ray diffraction (XRD) patterns of perovskite films prepared by sequential deposition route with different PbI2 annealing times.
Figure 3. X-ray diffraction (XRD) patterns of perovskite films prepared by sequential deposition route with different PbI2 annealing times.
Nanomaterials 08 00416 g003
Nanomaterials 08 00416 g004 550
Figure 4. Schematic illustration for diffusion mechanisms and structure of devices: (a) Schematic illustration for the mechanisms of LLLD and LSLD for perovskite multi-crystalline film; (b) Structure of devices with low-cost spongy carbon/FTO composite counter electrode.
Figure 4. Schematic illustration for diffusion mechanisms and structure of devices: (a) Schematic illustration for the mechanisms of LLLD and LSLD for perovskite multi-crystalline film; (b) Structure of devices with low-cost spongy carbon/FTO composite counter electrode.
Nanomaterials 08 00416 g004
Nanomaterials 08 00416 g005 550
Figure 5. J-V curves from reverse scan (RS) and monochromatic incident photon-to-electron conversion efficiency (IPCE) of PSCs prepared by sequential deposition route with different PbI2 annealing times: (a) J-V curves for the devices with carbon/FTO composite electrode; (b) J-V curves for the devices with gold electrode; (c) IPCE of devices with carbon/FTO composite electrode.
Figure 5. J-V curves from reverse scan (RS) and monochromatic incident photon-to-electron conversion efficiency (IPCE) of PSCs prepared by sequential deposition route with different PbI2 annealing times: (a) J-V curves for the devices with carbon/FTO composite electrode; (b) J-V curves for the devices with gold electrode; (c) IPCE of devices with carbon/FTO composite electrode.
Nanomaterials 08 00416 g005
Table
Table 1. Parameters of contact-type or non-contact-type processed PSCs with carbon/FTO composite electrode or gold electrode prepared by sequential deposition route with different PbI2 annealing times under RS.
Table 1. Parameters of contact-type or non-contact-type processed PSCs with carbon/FTO composite electrode or gold electrode prepared by sequential deposition route with different PbI2 annealing times under RS.
T a (s)DM bEM cJsc d (mA/cm−2)Voc e (v)FF fPCE g (%)
0non-contact-typecarbon/FTO17.190.950.487.89
contact-typecarbon/FTO19.891.000.5410.70
non-contact-typegold19.691.020.6613.29
contact-typegold20.181.050.7014.86
10contact-typecarbon/FTO17.490.890.497.64
contact-typegold19.111.040.6412.73
20contact-typecarbon/FTO14.220.840.566.66
contact-typegold19.660.980.519.73
a T: PbI2 annealing times; b DM: Drop method of MAI solution; c EM: Electrode materials; d Jsc: Short-circuit photocurrent density; e Voc: Open-circuit voltage; f FF: Fill factor; g PCE: Power conversion efficiency.

Share and Cite

MDPI and ACS Style

Ling, T.; Zou, X.; Cheng, J.; Bai, X.; Ren, H.; Chen, D. Modified Sequential Deposition Route through Localized-Liquid-Liquid-Diffusion for Improved Perovskite Multi-Crystalline Thin Films with Micrometer-Scaled Grains for Solar Cells. Nanomaterials 2018, 8, 416. https://doi.org/10.3390/nano8060416

AMA Style

Ling T, Zou X, Cheng J, Bai X, Ren H, Chen D. Modified Sequential Deposition Route through Localized-Liquid-Liquid-Diffusion for Improved Perovskite Multi-Crystalline Thin Films with Micrometer-Scaled Grains for Solar Cells. Nanomaterials. 2018; 8(6):416. https://doi.org/10.3390/nano8060416

Chicago/Turabian Style

Ling, Tao, Xiaoping Zou, Jin Cheng, Xiao Bai, Haiyan Ren, and Dan Chen. 2018. "Modified Sequential Deposition Route through Localized-Liquid-Liquid-Diffusion for Improved Perovskite Multi-Crystalline Thin Films with Micrometer-Scaled Grains for Solar Cells" Nanomaterials 8, no. 6: 416. https://doi.org/10.3390/nano8060416

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop