Next Article in Journal
Design of Superlubricity System Using Si3N4/Polyimide as the Friction Pair and Nematic Liquid Crystals as the Lubricant
Next Article in Special Issue
Improving the Recyclability of an Epoxy Resin through the Addition of New Biobased Vitrimer
Previous Article in Journal
Morphological Evolution of Hybrid Block Copolymer Particles: Toward Magnetic Responsive Particles
Previous Article in Special Issue
Investigating the Mechanical, Thermal, and Crystalline Properties of Raw and Potassium Hydroxide Treated Butea Parviflora Fibers for Green Polymer Composites
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 15
Issue 18
10.3390/polym15183691
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Comparative Study of Flax and Pineapple Leaf Fiber Reinforced Poly(butylene succinate): Effect of Fiber Content on Mechanical Properties

by
Taweechai Amornsakchai
1,2,3,*,
Sorn Duangsuwan
1,2,
Karine Mougin
4 and
Kheng Lim Goh
5,6
1
Polymer Science and Technology Program, Department of Chemistry, Faculty of Science, Mahidol University, Phuttamonthon 4 Road, Salaya, Nakhon Pathom 73170, Thailand
2
Center of Sustainable Energy and Green Materials, Faculty of Science, Mahidol University, Phuttamonthon 4 Road, Salaya, Nakhon Pathom 73170, Thailand
3
TEAnity Team Co., Ltd., 40/494 Soi Navamintra 111, Khet Bueng Kum, Bangkok 10230, Thailand
4
Institut de Science des Matériaux de Mulhouse, IS2M-CNRS-UHA, 15, Rue Jean Starcky, B.P.2488, 68057 Mulhouse, CEDEX, France
5
Mechanical Design and Manufacturing Engineering, Newcastle University in Singapore, 172A Ang Mo Kio Avenue 8 #05-01, SIT@NYP Building, Singapore 567739, Singapore
6
Faculty of Science, Agriculture & Engineering, Newcastle University, Newcastle upon Tyne NE1 7RU, UK
*
Author to whom correspondence should be addressed.
Polymers 2023, 15(18), 3691; https://doi.org/10.3390/polym15183691
Submission received: 11 August 2023 / Revised: 3 September 2023 / Accepted: 4 September 2023 / Published: 7 September 2023
(This article belongs to the Special Issue Sustainable Biopolymer-Based Composites: Processing, Characterization, and Application)
Browse Figures
Versions Notes

Abstract

:
In this study, we compare the reinforcing efficiency of pineapple leaf fiber (PALF) and cultivated flax fiber in unidirectional poly(butylene succinate) composites. Flax, known for robust mechanical properties, is contrasted with PALF, a less studied but potentially sustainable alternative. Short fibers (6 mm) were incorporated at 10 and 20% wt. levels. After two-roll mill mixing, uniaxially aligned prepreg sheets were compression molded into composites. At 10 wt.%, PALF and flax exhibited virtually the same stress–strain curve. Interestingly, PALF excelled at 20 wt.%, defying its inherently lower tensile properties compared to flax. PALF/PBS reached 70.7 MPa flexural strength, 2.0 GPa flexural modulus, and 107.3 °C heat distortion temperature. Comparable values for flax/PBS were 57.8 MPa, 1.7 GPa, and 103.7 °C. X-ray pole figures indicated similar matrix orientations in both composites. An analysis of extracted fibers revealed differences in breakage behavior. This study highlights the potential of PALF as a sustainable reinforcement option. Encouraging the use of PALF in high-performance bio-composites aligns with environmental goals.

Graphical Abstract

1. Introduction

In recent decades, escalating global concern over climate change has prompted a significant shift towards sustainable and environmentally friendly practices across various industries. One of the pressing issues we face today is the increasing level of carbon dioxide (CO2) in the Earth’s atmosphere, contributing to the greenhouse effect and subsequent climate change. As scientists and researchers strive to combat this challenge, exploring alternative materials and manufacturing processes becomes crucial in reducing our reliance on petroleum-based products while simultaneously addressing CO2 emissions using different concepts such as carbon capture utilization and storage (CCUS) using expensive modern technologies [1,2].
Plants, through the process of photosynthesis, have the remarkable ability to convert CO2 into organic compounds, effectively sequestering this greenhouse gas and mitigating its impact on the environment. Leveraging the inherent qualities of natural fibers in composite materials offers a promising avenue to not only decrease dependence on fossil fuel-derived resources, but also actively sequester CO2. By incorporating these natural fibers into polymer matrices, composites can be fabricated with improved mechanical properties [3,4,5] while simultaneously contributing to carbon capture and reduced environmental impact [6], similar to using wood, but much easier and with lower production cost. Although there are different types of natural fibers with a range of mechanical properties [4,7,8,9,10], perhaps it is fair to say that flax and hemp are the most successful commercial examples [11,12].
This study aims to conduct a comparative analysis between two types of natural fibers: flax and pineapple leaf fiber. Flax fiber, derived from the stem of the flax plant (Linum usitatissimum), has long been recognized for its mechanical strength and versatility [13,14]. On the other hand, pineapple leaf fiber, obtained from the waste of pineapple cultivation, has emerged as a potential alternative due to its abundance and renewability [15,16,17,18,19]. Although these two fibers have been studied for a long time, there is still some discrepancy in their reported mechanical properties (cf. Table 1 in [4], Table 2 in [15]). PALF has been used successfully in reinforcing different polymer matrices [20,21,22] despite the much lower than expected mechanical properties [23] compared to those of flax [24]. So far, there has been no direct comparison in the reinforcement efficiency of the two fibers, and thus this is the main objective of the present work. They are used to reinforce bio-based poly(butylene succinate) (PBS), which provokes an intensive interest among industry and researchers [25,26] and has been employed in automotive applications [27]. Here, we seek to investigate the influence of fiber content on the performance of the resulting composite materials.
Through this comparative study, we aim to contribute to the growing body of research dedicated to sustainable materials and their potential applications. By examining the mechanical properties of flax and pineapple leaf fiber composites, we can gain insights into their suitability for various engineering and manufacturing applications while also addressing the urgent need for carbon sequestration.

2. Materials and Methods

2.1. Materials

Poly (butylene succinate) (PBS, BioPBS FZ91PM/FZ91PB), produced from the polymerization of bio-based succinic acid and 1,4-butanediol, was used as the polymer matrix. The material was supplied by PTT MCC Biochem Company Limited (Bangkok, Thailand) and had a density of 1.26 g/cm3 and a melt index of 5 g/10 min (190 °C, 2.16 kg). Its reported molecular weight (Mw) was approximately 170 kDa [28].
Flax fiber (LINTEX, ~6 mm in length) was supplied by Dehondt Composites (Port-Jérôme-sur-Seine, France). According to the Alliance for European Flax-Linen and Hemp, the European flax is dew retted and mechanically scutched [29]. The fiber was supplied already cut to the specified calibrated length intended for composite reinforcement [30]. Pineapple leaf fibers (PALF, ~6 mm in length) were prepared from fresh pineapple leaves using the procedure presented in the literature [17]. Fresh pineapple leaves were collected from Bang Yang District, Phitsanulok Province, Thailand. The leaves were cut across their length into pieces 6 mm long, ground with a stone grinder, and dried to yield the whole ground leaf (WGL). The WGL was further processed by crushing it with a high-speed blender, followed by sieving to achieve the separation between the non-fibrous component and the PALF. The loose particulate non-fibrous component, with a particle size smaller than approximately 1 mm², was able to pass through the sieve. In contrast, the curly and entangled PALF remained on the sieve, highlighting its distinctive physical properties. For visual reference, photographs of both PALF and flax fibers are presented in Figure 1.

2.2. Composite Prepreg Preparation

Prior to the melt-mixing process, all materials were dried overnight in a hot air oven at 80 °C. The PBS pellets were then heated and melted on a two-roll mill (W100T, Dr. Collin GmbH, Maitenbeth, Germany) for 2 min at a speed of 30 rpm. The front and back roll temperatures were 125 °C and 100 °C, respectively. Subsequently, a predetermined amount of fiber (10 and 20 wt.% of total weight (PBS + fiber)) was gradually added over a period of 3 min. The mixing speed was then increased to 48 rpm, and the mixing continued for another 10 min to achieve a homogenous molten mixture.
The resulting molten mixture was carefully pulled out with slight stretching to maintain the alignment of the fiber parallel to the machine direction. It was then allowed to cool and solidify, forming prepreg, as illustrated in Figure 2. The composites were designated as 10PALF, 20PALF, 10Flax and 20Flax, denoting the respective content of the fiber in the composites.

2.3. Compressed Sheet Preparation

Composite sheets were prepared by stacking ten layers of prepreg between two flat metal sheets and a 3 mm spacer to prevent the excessive flow of the material and the disturbance of the fiber alignment. The stacked prepregs were preheated for 5 min under slight pressure. Then, they were pressed under a pressure of 1500 psi for 5 min, followed by cooling under the same pressure for 5 min. The compression molding was carried out at a temperature of 140 °C to destroy the matrix orientation and allow only fiber contribution to be observed [31].

2.4. Characterizations

2.4.1. Fibers’ Chemical Composition

The chemical compositions of PALF and flax fibers were determined according to standard methods [32,33,34,35] through a certified local laboratory. Chemical composition is reported in terms of cellulose, holocellulose, acid-soluble lignin and acid-insoluble lignin.
The surface chemical compositions of PALF and flax fibers were observed using Fourier-transform infrared spectroscopy in an attenuated total reflectance mode (ATR-FTIR, Frontier, Perkin Elmer, Waltham, MA, USA). Spectra were recorded with 16 scans over the range of 4000 to 500 cm−1 with a resolution of 4 cm−1.

2.4.2. X-ray Diffraction

X-ray diffraction patterns of the composites were recorded using an X-ray Diffractometer (XRD) (D8 DISCOVER, Bruker AXS GmbH, Karlsruhe, Germany) over the 2θ range between 5° and 80° with a step size of 0.02°. The X-ray wavelength was 1.54 Å (Ni-filtered CuKα). Pole figures for different samples were obtained with a cradle sample stage on the same machine. The data were analyzed with DEFFRAC.TEXTURE software (V4.1).

2.4.3. Scanning Electron Microscopy (SEM)

Fibers’ shapes and sizes and the fractured surfaces of composites were observed using a scanning electron microscope (JSM-IT500, JEOL, Tokyo, Japan) with an accelerating voltage of 10 kV. Prior to observation, a thin layer of platinum was coated on the samples.

2.4.4. Thermal Properties

The melting and crystallization behavior of the composites were determined with a differential scanning calorimeter (DSC) (Q200-RCS90, TA Instruments, New Castle, DE, USA). The samples were first heated from 25 to 200 °C, held for 5 min to completely melt all the crystals, cooled to −70 °C and then heated again to 200 °C. The heating and cooling rate was 10 °C/min under a nitrogen atmosphere. The positions of the melting peak (Tm), enthalpy of fusion (ΔHf) and crystallization peak (Tc) were determined for each sample using the instrument software. The degree of crystallinity (Xc) was calculated using Equation (1).
X c = ∆ H f ∆ H f 0   ( 1 - W f )   ×   100 %
where ∆ H f 0 is the enthalpy of fusion for 100% crystalline PBS, which is taken as 110.3 J/g [36], and W f is the weight fraction of fiber in the composites.
In addition, the heat deflection temperature (HDT) was determined with a Gotech testing machine (HV-3000-P3C, Gotech Testing Machines Inc., Taichung City, Taiwan). The specimen sizes were 120 × 13 × 3 mm3. The test was performed following ASTM-D648 under the three-point bending mode with a span of 100 mm under a constant load of 0.455 MPa and a heating rate of 2 °C/min. HDT was determined as the temperature at which the specimen bends to 0.25 mm.

2.4.5. Mechanical Properties

Flexural testing: The test was carried out on a universal testing machine (Instron 5569, Instron, High Wycombe, UK) at a crosshead speed of 5 mm/min, 1 kN of load cell and a support span length of 48 mm. The specimens were cut from compressed sheets into strips 12.7 mm wide with a long axis parallel to the machine direction. The average values of flexural strength and secant modulus at 1% stain from 5 specimens were reported.
Impact testing: The test was carried out on a pendulum impact testing machine (HIT5.5P, Zwick/Roell, Ulm, Germany) in Izod configuration. The impact specimens were cut from compressed sheets into strips 60 mm long and 12.7 mm wide. The samples were notched with a Zwick/Roell manual notch cutting machine. The notches were cut across the machine direction. Average values of 5 specimens were reported.

3. Results

3.1. PALF and Flax Characteristics

3.1.1. Fiber Composition and Structure

Table 1 displays the chemical composition of PALF and flax fiber. In general, the chemical composition of the two fibers is very similar. PALF has a slightly higher holocellulose content than flax fiber, while flax has about 10% greater cellulose content than PALF. PALF also has about 1.5 times higher acid-soluble lignin content than flax. The greater content of hemicellulose (the difference between holocellulose and cellulose) is reflected in the FTIR spectra shown in Figure 3a, in which the peaks at 1731 cm−1 and 1244 cm−1 correspond to the C=O stretching of hemicellulose and lignin and the C–O stretching in lignin, respectively [37,38]. The peak at 2918 cm−1 corresponds to the C–H stretching of methyl groups (–CH3) in both hemicellulose and cellulose [39].
The lower hemicellulose content in flax is a result of the enzymatic degradation of the binding material during dew retting [14]. For PALF, only mechanical force was used in the preparation of the fiber. Therefore, not much material was removed.
The crystalline structures of PALF and flax fibers were investigated using X-ray diffraction techniques. The diffraction patterns are shown in Figure 3b. Both fibers exhibited a similar characteristic pattern to cellulose Type I [40]. However, the patterns differed significantly in the resolution and sharpness of the peaks; flax fiber has much sharper peaks than PALF. This indicates that the crystalline structure in flax fiber is more perfect and possibly larger than in PALF. This difference could be the main reason for the higher mechanical performance of flax fiber.

3.1.2. Scanning Electron Microscopy (SEM)

Figure 4 compares the size and shape of the two fibers. PALF had both large bundles and fine elementary fibers. The fibers were not straight, but contained a lot of kinks. On the other hand, flax fibers were rather straight and had both isolated small fibers and bundles of fibers. Flax featured larger fiber bundles than PALF. Additionally, both PALF and flax fibers contained non-fibrous components. The variations in fiber size and shape can be attributed to the specific fiber preparation techniques employed.

3.1.3. Prepreg Appearance

Figure 5 displays the photographs of PALF/PBS and flax/PBS prepregs. PALF/PBS has a pale color, while flax/PBS is brownish with a much greater number of dark spots of non-fibrous components. Both PALF and flax fibers appear evenly dispersed throughout the prepregs, indicating thorough mixing and alignment, as highlighted by the dark lines within elongated red circles.

3.2. Mechanical Properties of Composites

3.2.1. Flexural Properties

Figure 6 displays representative stress–strain curves of PALF/PBS and flax/PBS composites containing different fiber contents, and also that of PBS. With a fiber content of 10 wt.%, the stress at different strains increased over that of PBS throughout the whole range of strain. The composites had roughly similar failure strains to that of PBS. At 10 wt.% content, PALF/PBS and flax/PBS composites exhibited virtually the same behavior.
When the fiber content was increased to 20 wt.%, the stress for the flax/PBS composite increased slightly over that of 10 wt.%, and then the stress gradually decreased and the composite failed at a slightly lower strain than the composite with 10 wt.% fiber. The PALF/PBS composite with 20 wt.% fiber content exhibited a much-improved performance but failed at a much lower strain than the flax/PBS composite.
The average values for the flexural strength and flexural modulus of these composites are shown in Figure 7. The average flexural strength increased from 47 MPa to approximately 54 MPa for both PALF/PBS and flax/PBS composites containing 10 wt.% fiber, and to 70.7 and 57.8 MPa for PALF/PBS and flax/PBS with 20 wt.% fiber, respectively. A similar trend was observed for the flexural modulus. The average flexural modulus increased from 0.90 GPa to 1.25 GPa for both PALF/PBS and flax/PBS composites containing 10 wt.% fiber, and to 2.03 and 1.70 GPa for PALF/PBS and flax/PBS with 20 wt.% fiber, respectively.
The above results clearly indicate a better reinforcement efficiency of PALF over that of flax, despite its inferior mechanical properties. Doubling the flax content from 10 wt.% to 20 wt.% caused the flexural modulus to increase by approximately 10%, but it caused only a marginal change in flexural strength. PALF, on the other hand, caused both the flexural modulus and flexural strength to increase by approximately 62% and 31%, respectively, under a similar change. The reasons for this will be addressed later.

3.2.2. Impact Properties

Figure 8 displays the notched Izod impact strengths of PALF/PBS and flax/PBS composites containing different fiber contents. The introduction of 10 wt.% of fiber to PBS resulted in an impact strength reduction to approximately 70% and 64% of that of PBS for PALF and flax, respectively. With a further increase in fiber content to 20 wt.%, the impact strength dropped even further, to approximately 62% and 54% of that of PBS for PALF and flax, respectively. This indicates that PALF contributes to a smaller reduction in the impact strength of the composite compared to flax fibers. The decrease in impact strength in natural fiber-filled polymers is an anticipated outcome due to the increase in material stiffness and the presence of stress concentrators within [41,42,43]. A more detailed discussion on the reason for the comparatively smaller reduction in impact strength in the PALF system will follow.

3.3. Thermal Properties

3.3.1. DSC

The melting and crystallization behavior of PBS in the composites is shown in Table 2. The presence of both PALF and flax fibers has a negligible effect on the melting temperature (Tm), degree of crystallinity (Xc), and crystallization temperature of PBS (Tc). Thus, it may be stated that both PALF and flax fibers do not influence matrix crystallization, similar to the results observed in other systems [44,45].

3.3.2. HDT

Figure 9 displays the heat distortion temperature (HDT) of the composites along with the base PBS. At 10 wt.%, both PALF and flax had a negligible effect on HDT. However, when the fiber content was increased to 20 wt.%, PALF caused a larger increase than flax fiber, being approximately 10 °C and 6 °C higher than that of the base matrix. This is the consequence of the increase in flexural modulus of the respective materials.

3.4. Fracture Surfaces

Figure 10 shows the impact fracture surfaces of PALF/PBS and flax/PBS composites containing different fiber contents. Broken fibers are seen end-on, indicating a good alignment of the fibers along the machine direction (toward the observer). For 10 wt.% fiber, a larger number of fiber bundles can be seen in the PALF/PBS composite compared to the flax/PBS composite. When the fiber content was increased to 20 wt.%, a smaller number of large fiber bundles could be observed, indicating the breaking of large fiber bundles into finer elementary fibers. This phenomenon is likely due to the increase in the viscosity of the mixture (resulting from the higher fiber content), which facilitates higher stress transfer and thus breaks the bundles into finer elementary fibers.

4. Discussion

The nearly identical curves seen for 10 wt.% PALF/PBS and flax/PBS in Figure 6 signify a remarkable parity in reinforcing efficiency between the two types of fibers, even amidst their distinct mechanical properties. Intriguingly, at a higher fiber content of 20 wt.%, PALF exhibited significantly greater reinforcing efficiency than flax fiber. These findings merit a more in-depth examination.
It is known that for short fiber composites, the mechanical behavior of the composite is determined by several factors, including the mechanical properties of the reinforcing fiber, its orientation, the fiber aspect ratio, the fiber volume fraction, and the nature of the interface between the fiber and the matrix [46]. While we kept most starting parameters of the two types of fibers as close as possible, such as their length, amount, and mixing procedure, the only known parameter that was different was the mechanical properties of the fibers, with flax having much superior values. Surprisingly, this difference in mechanical properties alone does not fully explain the stark difference in reinforcing efficiency. Therefore, a deeper analysis of the internal structure of the composites, including matrix structure, matrix orientation, and fiber dimension, is required.

4.1. Matrix Orientation via Pole Figures

The production method for uniaxial prepreg employed in this work could lead to matrix orientation [31]. This had been destroyed during the compression molding by using a high compression molding temperature, as previously described. XRD was used to confirm this. Figure 11a displays the XRD patterns of composite prepregs and sheets. Prepregs display very strong intensity, while the sheets show much less intensity, indicating much relaxation of the polymer matrix. Pole figures for all samples were then determined using the most intense peak, at around 22.7°, which was associated with the (110) plane of PBS crystalline [47].
Pole figures for all samples for the (110) plane are shown in Figure 11b. It is clearly evident that the peak intensity of the prepregs is concentrated in the center, indicating a preferred matrix orientation in all prepregs. The presence of a high-intensity region supports the fact that the (110) reflection of the drawn PBS film lies on the equator [48]. However, when the sample was compressed at 140 °C, the previous orientation disappeared. These results are consistent with the previous XRD and DSC findings. Notably, with an increased fiber content in the sample compressed at 140 °C, a relatively weak molecular orientation can still be observed in the case of PALF/PBS. This suggests that the presence of fibers could slow down the relaxation of the matrix in the vicinity of the fiber, as suggested in the literature [31]. However, it could be assumed that such a marginal orientation of PBS in the PALF/PBS composite would play no role in enhancing the PALF/PBS composite over that of the flax/PBS composite (cf. Figure 7).

4.2. Reinforcing Fiber in the Matrix

It has been reported that fibers such as jute, flax [49], PALF [50], kenaf [51], poplar wood, radiata pine, and rice husk [52] can break down during incorporation into a polymer matrix, resulting in a lower reinforcing efficiency. To determine whether such a situation had occurred, the fibers were extracted from the composites using hot chloroform. Figure 12 displays optical images (Olympus BX51TRF, Olympus Optical Co. Ltd., Tokyo, Japan) of PALF and flax fibers that were extracted from PALF/PBS and flax/PBS composites with 20 wt.% fiber. It is clear that PALF remained long, while flax broke into very short pieces. In both cases, fine elementary fibers and large bundles can be seen. Thus, it is unquestionable that such fragmented flax fibers would not be able to reinforce the composite effectively. PALF, which remains long, can still effectively reinforce the composite [53]. The longer PALF also gives composites with higher impact strength and HDT (cf. Figure 8 and Figure 9). This observation supports our previous works, where PALF has been shown to outperform short Kevlar in reinforcing rubber matrices [22], and with an appropriate adhesion promoter the effectiveness can be further improved [54].
As stated above, all kinds of fiber are prone to breakage during compounding with polymer matrices due to different breakage mechanisms [55] depending on the fiber characteristics, and this includes PALF. It can be easily envisaged that by reducing the stress involved during compounding, either by increasing the temperature or reducing mixing speed, the breakage could be reduced or minimized. Mixing with a two-roll mill involves a much lower shear stress than with an internal mixer or screw extruder. It is clear from the results above that flax fiber still breaks, while PALF does not. The fact that PALF can maintain its length during mixing with thermoplastics and provide a high reinforcement efficiency certainly encourages its use in this form. Given that the starting length is long enough, and large fiber bundles break into finer elementary fibers during mixing, resulting in a significantly increased aspect ratio, composites with greatly improved properties can be obtained. Moreover, the utilization of PALF offers a promising ecological advantage. Compared to purposely cultivated fibers (such as flax, hemp, and kenaf), PALF exhibits lower carbon emissions and a reduced environmental footprint. Additionally, the use of PALF contributes to sustainable waste management practices by repurposing agricultural waste, making it a more environmentally friendly alternative for composite reinforcement. These ecological benefits further underscore the potential of PALF as a viable and eco-conscious solution in advancing sustainable materials across various industries, especially those that require higher performance or thinner parts.

5. Conclusions

In this study, we compared PALF with cultivated flax fiber as natural reinforcements in unidirectional PBS matrix composites. PALF showed remarkable potential as a sustainable alternative to flax fiber, well known for its high mechanical properties. PALF’s ability to maintain length and integrity during mixing led to significant improvements in the flexural strength and modulus, particularly at 20 wt.% fiber content. Successful PALF dispersion in the matrix, along with fiber bundle disintegration, resulting in higher aspect ratio, further contributed to its superior performance. PALF offers valuable ecological benefits, with a lower carbon footprint and the utilization of agricultural waste. The study highlights PALF’s underexplored potential as a sustainable and high-performance natural reinforcement, paving the way for eco-friendly materials in various industries. PALF’s effective reinforcement and ecological advantages suggest that it is a promising candidate for developing sustainable and eco-friendly materials.

Author Contributions

Conceptualization, T.A. and K.M.; methodology, S.D., T.A. and K.L.G.; validation and data curation, S.D.; writing—original draft preparation, S.D. and T.A.; writing—review and editing, T.A., K.L.G. and K.M.; funding acquisition, T.A. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Mahidol University (Basic Research Fund: fiscal year 2022; Grant no. BRF1-046/2565).

Institutional Review Board Statement

Not applicable.

Data Availability Statement

Not applicable.

Acknowledgments

This research project is supported by Mahidol University (Basic Research Fund: fiscal year 2022; Grant no. BRF1-046/2565). We thank Mahidol University Frontier Research Facility (MU-FRF) for instrument support and the MU-FRF scientists, Nawapol Udpuay, Chawalit Takoon and Suwilai Chaveanghong, for their kind assistance in the operations of SEM and XRD.

Conflicts of Interest

T.A. declares a conflict of interest related to this research article: As a University Professor at Mahidol University, I have been engaged in developing an innovative method for extracting pineapple leaf fiber. This endeavor led to the establishment of TEAnity Team Co. Ltd., where I hold the position of Chief Technology Officer (CTO). While this research was conducted independently and supported solely by university funding, I acknowledge the potential for a conflict due to my dual roles. I affirm that the research and findings presented in the article remain unbiased and have not been influenced by any financial interests or affiliations with TEAnity Team Co. Ltd. The remaining authors declare no conflicts of interest.

References

  1. Hong, W.Y. A techno-economic review on carbon capture, utilisation and storage systems for achieving a net-zero CO2 emissions future. Carbon Capture Sci. Technol. 2022, 3, 100044. [Google Scholar] [CrossRef]
  2. Liu, E.; Lu, X.; Wang, D. A Systematic Review of Carbon Capture, Utilization and Storage: Status, Progress and Challenges. Energies 2023, 16, 2865. [Google Scholar] [CrossRef]
  3. George, J.; Ivens, J.; Verpoest, I. Mechanical properties of flax fibre reinforced epoxy composites. Angew. Makromol. Chem. 1999, 272, 41–45. [Google Scholar] [CrossRef]
  4. Kalia, S.; Kaith, B.S.; Kaur, I. Pretreatments of Natural Fibers and their Application as Reinforcing Material in Polymer Composites—A Review. Polym. Eng. Sci. 2009, 49, 1253–1272. [Google Scholar] [CrossRef]
  5. Baley, C.; Gomina, M.; Breard, J.; Bourmaud, A.; Davies, P. Variability of mechanical properties of flax fibres for composite reinforcement. A review. Ind. Crop Prod. 2020, 145, 111984. [Google Scholar] [CrossRef]
  6. Joshi, S.V.; Drzal, L.T.; Mohanty, A.K.; Arora, S. Are natural fiber composites environmentally superior to glass fiber reinforced composites? Compos. Part A Appl. Sci. Manuf. 2004, 35, 371–376. [Google Scholar] [CrossRef]
  7. Nabi Saheb, D.; Jog, J.P. Natural fiber polymer composites: A review. Adv. Polym. Technol. 1999, 18, 351–363. [Google Scholar] [CrossRef]
  8. Biagiotti, J.; Puglia, D.; Kenny, J.M. A review on natural fibre-based composites—Part I: Structure, processing and properties of vegetable fibres. J. Nat. Fibers 2004, 1, 37–68. [Google Scholar] [CrossRef]
  9. Puglia, D.; Biagiotti, J.; Kenny, J.M. A review on natural fibre-based composites—Part II: Application of natural reinforcements in composite materials for automotive industry. J. Nat. Fibers 2004, 1, 23–65. [Google Scholar] [CrossRef]
  10. Li, X.; Tabil, L.G.; Panigrahi, S. Chemical treatments of natural fiber for use in natural fiber-reinforced composites: A review. J. Polym. Environ. 2007, 15, 25–33. [Google Scholar] [CrossRef]
  11. Pil, L.; Bensadoun, F.; Pariset, J.; Verpoest, I. Why are designers fascinated by flax and hemp fibre composites? Compos. Part A Appl. 2016, 83, 193–205. [Google Scholar] [CrossRef]
  12. Baley, C.; Bourmaud, A.; Davies, P. Eighty years of composites reinforced by flax fibres: A historical review. Compos. Part A Appl. Sci. Manuf. 2021, 144, 106333. [Google Scholar] [CrossRef]
  13. Yan, L.; Chouw, N.; Jayaraman, K. Flax fibre and its composites—A review. Compos. B Eng. 2014, 56, 296–317. [Google Scholar] [CrossRef]
  14. Baley, C.; Le Duigou, A.; Morvan, C.; Bourmaud, A. Tensile properties of flax fibers. In Handbook of Properties of Textile and Technical Fibres, 2nd ed.; Bunsell, A.R., Ed.; Elsevier: Kidlington, UK, 2018; pp. 275–300. [Google Scholar]
  15. Mishra, S.; Mohanty, A.K.; Drzal, L.T.; Misra, M.; Hinrichsen, G. A review on pineapple leaf fibers, sisal fibers and their biocomposites. Macromol. Mater. Eng. 2004, 289, 955–974. [Google Scholar] [CrossRef]
  16. Arib, R.M.N.; Sapuan, S.M.; Hamdan, M.A.M.M.; Paridah, M.T.; Zaman, H.M.D.K. A literature review of pineapple fibre reinforced polymer composites. Polym. Polym. Compos. 2004, 12, 341–348. [Google Scholar] [CrossRef]
  17. Kengkhetkit, N.; Amornsakchai, T. Utilisation of pineapple leaf waste for plastic reinforcement: 1. A novel extraction method for short pineapple leaf fiber. Ind. Crops. Prod. 2012, 40, 55–61. [Google Scholar] [CrossRef]
  18. Asim, M.; Abdan, K.; Jawaid, M.; Nasir, M.; Dashtizadeh, Z.; Ishak, M.R.; Hoque, M.E.; Deng, Y. A review on pineapple leaves fibre and its composites. Inter. J. Polym. Sci. 2015, 2015, 950567. [Google Scholar] [CrossRef]
  19. Todkar, S.S.; Patil, S.A. Review on mechanical properties evaluation of pineapple leaf fibre (PALF) reinforced polymer composites. Compos. B. Eng. 2019, 174, 106927. [Google Scholar] [CrossRef]
  20. Nopparut, A.; Amornsakchai, T. Influence of pineapple leaf fiber and it’s surface treatment on molecular orientation in, and mechanical properties of, injection molded nylon composites. Polym. Test. 2016, 52, 141–149. [Google Scholar] [CrossRef]
  21. Kalapakdee, A.; Amornsakchai, T. Mechanical properties of preferentially aligned short pineapple leaf fiber reinforced thermoplastic elastomer: Effects of fiber content and matrix orientation. Polym. Test. 2014, 37, 36–44. [Google Scholar] [CrossRef]
  22. Surajarusarn, B.; Hajjar-Garreau, S.; Schrodj, G.; Mougin, K.; Amornsakchai, T. Comparative study of pineapple leaf microfiber and aramid fiber reinforced natural rubbers using dynamic mechanical analysis. Polym. Test. 2020, 82, 106289. [Google Scholar] [CrossRef]
  23. Surajarusarn, B.; Traiperm, P.; Amornsakchai, T. Revisiting the morphology, microstructure, and properties of cellulose fiber from pineapple leaf so as to expand its utilization. Sains Malays. 2019, 48, 145–154. [Google Scholar] [CrossRef]
  24. Straumit, I.; Vandepitte, D.; Wevers, M.; Lomov, S.V. Identification of the flax fibre modulus based on an impregnated quasi-unidirectional fibre bundle test and X-ray computed tomography. Compos. Sci. Technol. 2017, 151, 124–130. [Google Scholar] [CrossRef]
  25. Rafiqah, S.A.; Khalina, A.; Harmaen, A.S.; Tawakkal, I.A.; Zaman, K.; Asim, M.; Nurrazi, M.N.; Lee, C.H. A Review on Properties and Application of Bio-Based Poly(Butylene Succinate). Polymers 2021, 13, 1436. [Google Scholar] [CrossRef] [PubMed]
  26. Mochane, M.J.; Magagula, S.I.; Sefadi, J.S.; Mokhena, T.C. A Review on Green Composites Based on Natural Fiber-Reinforced Polybutylene Succinate (PBS). Polymers 2021, 13, 1200. [Google Scholar] [CrossRef] [PubMed]
  27. New High Biocontent Biopolymers. Available online: https://plasticsengineering.wordpress.com/2015/09/03/new-high-biocontent-biopolymers (accessed on 8 August 2023).
  28. Bianchi, S.; Marchese, P.; Vannini, M.; Sisti, L.; Tassoni, A.; Ferri, M.; Mallegni, N.; Cinelli, P.; Celli, A. Evaluation of the activity of natural phenolic antioxidants, extracted from industrial coffee residues, on the stability of poly(1,4-butylene succinate) formulations. J. Appl. Polym. Sci. 2023, 140, e53878. [Google Scholar] [CrossRef]
  29. European Flax: Environmentally Responsible. Available online: https://allianceflaxlinenhemp.eu/en/european-flax-environmentally-responsible (accessed on 24 August 2023).
  30. Lintex. Available online: http://www.dehondtcomposites.com/en/products/lintex/ (accessed on 24 August 2023).
  31. Kengkhetkit, N.; Amornsakchai, T. Effect of matrix orientation and fiber content on the properties of uniaxial pineapple leaf fiber—Polypropylene composites. KGK-Kaut. Gummi. Kunst. 2020, 73, 44–50. [Google Scholar]
  32. Updegraff, D.M. Semimicro determination of cellulose inbiological materials. Anal. Biochem. 1969, 32, 420–424. [Google Scholar] [CrossRef]
  33. Wise, L.E.; Murphy, M.; Adieco, A.A.D. A chlorite holocellulose, its fractionation and bearing on summative wood analysis and studies on the hemicelluloses. Pap. Trade J. 1946, 122, 35–43. [Google Scholar]
  34. TAPPI UM 250. Acid-Soluble Lignin in Wood and Pulp; Technical Association of the Pulp and Paper Industry: Atlanta, GA, USA, 1991. [Google Scholar]
  35. TAPPI T 222. Acid-Insoluble Lignin in Wood and Pulp; Technical Association of the Pulp and Paper Industry: Atlanta, GA, USA, 2002. [Google Scholar]
  36. Deng, Y.; Thomas, N.L. Blending Poly(butylene succinate) with Poly(lactic acid): Ductility and Phase Inversion Effects. Eur. Polym. J. 2015, 71, 534–546. [Google Scholar] [CrossRef]
  37. Huda, M.S.; Drzal, L.T.; Mohanty, A.K.; Misra, M. Effect of chemical modifications of the pineapple leaf fiber surfaces on the interfacial and mechanical properties of laminated biocomposites. Compos. Interfaces 2008, 15, 169–191. [Google Scholar] [CrossRef]
  38. Gaba, E.W.; Asimeng, B.O.; Kaufmann, E.E.; Katu, S.K.; Foster, E.J.; Tiburu, E.K. Mechanical and Structural Characterization of Pineapple Leaf Fiber. Fibers 2021, 9, 51. [Google Scholar] [CrossRef]
  39. Tanpichai, S.; Witayakran, S. All-cellulose composite laminates prepared from pineapple leaf fibers treated with steam explosion and alkaline treatment. J. Reinf. Plast. Compos. 2017, 36, 073168441770492. [Google Scholar] [CrossRef]
  40. French, A.D. Idealized powder diffraction patterns for cellulose polymorphs. Cellulose 2014, 21, 885–896. [Google Scholar] [CrossRef]
  41. Tantatherdtam, R.; Tran, T.; Chotineeranat, S.; Lee, B.H.; Sriroth, K.; Kim, H.J. Preparation and Characterization of Cassava Fiber-Based Polypropylene and Polybutylene Succinate Composites. Agric. Nat. Resour. 2009, 43, 245–251. [Google Scholar]
  42. Then, Y.Y.; Ibrahim, N.; Zainuddin, N.; Ariffin, H.; Yunus, W. Oil Palm Mesocarp Fiber as New Lignocellulosic Material for Fabrication of Polymer/Fiber Biocomposites. Int. J. Polym. Sci. 2013, 2013, 797452. [Google Scholar] [CrossRef]
  43. Frackowiak, S.; Ludwiczak, J.; Leluk, K. Man-Made and Natural Fibres as a Reinforcement in Fully Biodegradable Polymer Composites: A Concise Study. J. Polym. Environ. 2018, 26, 4360–4368. [Google Scholar] [CrossRef]
  44. Muthuraj, R.; Misra, M.; Mohanty, A. Injection Molded Sustainable Biocomposites From Poly(butylene succinate) Bioplastic and Perennial Grass. ACS Sustain. Chem. Eng. 2015, 3, 2767–2776. [Google Scholar] [CrossRef]
  45. Nanni, A.; Cancelli, U.; Montevecchi, G.; Masino, F.; Messori, M.; Antonelli, A. Functionalization and use of grape stalks as poly(butylene succinate) (PBS) reinforcing fillers. Waste Manag. 2021, 126, 538–548. [Google Scholar] [CrossRef]
  46. Goh, K.L. Physical Properties of Fibres and Matrix. In Discontinuous-Fibre Reinforced Composites: Fundamentals of Stress Transfer and Fracture Mechanics; Springer: London, UK, 2017; pp. 21–74. [Google Scholar]
  47. Cosquer, R.; Pruvost, S.; Gouanvé, F. Improvement of Barrier Properties of Biodegradable Polybutylene Succinate/Graphene Nanoplatelets Nanocomposites Prepared by Melt Process. Membranes 2021, 11, 151. [Google Scholar] [CrossRef]
  48. Ihn, K.J.; Yoo, E.S.; Im, S.S. Structure and Morphology of Poly(tetramethylene succinate) Crystals. Macromolecules 1995, 28, 2460–2464. [Google Scholar] [CrossRef]
  49. Tanguy, M.; Bourmaud, A.; Beaugrand, J.; Gaudry, T.; Baley, C. Polypropylene reinforcement with flax or jute fibre; Influence of microstructure and constituents properties on the performance of composite. Compos. B Eng. 2018, 139, 64–74. [Google Scholar] [CrossRef]
  50. Berzin, F.; Amornsakchai, T.; Lemaitre, A.; Di Giuseppe, E.; Vergnes, B. Processing and properties of pineapple leaf fibers-polypropylene composites prepared by twin-screw extrusion. Polym. Compos. 2018, 39, 4115–4122. [Google Scholar] [CrossRef]
  51. Lee, J.M.; Mohd Ishak, Z.A.; Mat Taib, R.; Law, T.T.; Ahmad Thirmizir, M.Z. Mechanical, Thermal and Water Absorption Properties of Kenaf-Fiber-Based Polypropylene and Poly(Butylene Succinate) Composites. J. Polym. Environ. 2013, 21, 293–302. [Google Scholar] [CrossRef]
  52. Hao, X.; Zhou, H.; Mu, B.; Chen, L.; Guo, Q.; Yi, X.; Sun, L.; Wang, Q.; Ou, R. Effects of fiber geometry and orientation distribution on the anisotropy of mechanical properties, creep behavior, and thermal expansion of natural fiber/HDPE composites. Compos. B Eng. 2020, 185, 107778. [Google Scholar] [CrossRef]
  53. Goh, K.L. Appendix A: Convergence to Continuous-Fibre Composites. In Discontinuous-Fibre Reinforced Composites: Fundamentals of Stress Transfer and Fracture Mechanics; Springer: London, UK, 2017; pp. 185–186. [Google Scholar]
  54. Surajarusarn, B.; Thaiwattananon, S.; Thanawan, S.; Mougin, K.; Amornsakchai, T. Realising the Potential of Pineapple Leaf Fiber as Green and High-performance Reinforcement for Natural Rubber Composite with Liquid Functionalized Rubber. Fibers Polym. 2021, 22, 2543–2551. [Google Scholar] [CrossRef]
  55. Albrecht, K.; Osswald, T.; Baur, E.; Meier, T.; Wartzack, S.; Müssig, J. Fibre Length Reduction in Natural Fibre-Reinforced Polymers during Compounding and Injection Moulding—Experiments Versus Numerical Prediction of Fibre Breakage. J. Compos. Sci. 2018, 2, 20. [Google Scholar] [CrossRef]
Polymers 15 03691 g001
Figure 1. Photographs of (a) PALF and (b) Flax fibers.
Figure 1. Photographs of (a) PALF and (b) Flax fibers.
Polymers 15 03691 g001
Polymers 15 03691 g002
Figure 2. Fiber alignment on a two-roll mill during the uniaxial composite prepreg preparation.
Figure 2. Fiber alignment on a two-roll mill during the uniaxial composite prepreg preparation.
Polymers 15 03691 g002
Polymers 15 03691 g003
Figure 3. ATR-FTIR spectra (a) and XRD patterns (b) of PALF and flax fibers.
Figure 3. ATR-FTIR spectra (a) and XRD patterns (b) of PALF and flax fibers.
Polymers 15 03691 g003
Polymers 15 03691 g004
Figure 4. SEM micrographs of (a) PALF and (b) flax fibers.
Figure 4. SEM micrographs of (a) PALF and (b) flax fibers.
Polymers 15 03691 g004
Polymers 15 03691 g005
Figure 5. Optical images of composite prepregs: (a) PALF/PBS and (b) flax/PBS. Images (c) and (d) depict magnified views of the regions of interest indicated by squares in images (a) and (b), respectively. The red elongated circles highlight the alignment of fibers. Machine direction is vertical.
Figure 5. Optical images of composite prepregs: (a) PALF/PBS and (b) flax/PBS. Images (c) and (d) depict magnified views of the regions of interest indicated by squares in images (a) and (b), respectively. The red elongated circles highlight the alignment of fibers. Machine direction is vertical.
Polymers 15 03691 g005
Polymers 15 03691 g006
Figure 6. Representative flexural stress–strain curves of PALF/PBS and flax/PBS composites containing different fiber contents.
Figure 6. Representative flexural stress–strain curves of PALF/PBS and flax/PBS composites containing different fiber contents.
Polymers 15 03691 g006
Polymers 15 03691 g007
Figure 7. Flexural properties of PALF/PBS and flax/PBS composites containing different fiber contents, (a) flexural strength and (b) flexural modulus at 1% strain. Gray bar represents neat PBS.
Figure 7. Flexural properties of PALF/PBS and flax/PBS composites containing different fiber contents, (a) flexural strength and (b) flexural modulus at 1% strain. Gray bar represents neat PBS.
Polymers 15 03691 g007
Polymers 15 03691 g008
Figure 8. Impact properties of PALF/PBS and flax/PBS composites containing different fiber contents. Gray bar represents neat PBS.
Figure 8. Impact properties of PALF/PBS and flax/PBS composites containing different fiber contents. Gray bar represents neat PBS.
Polymers 15 03691 g008
Polymers 15 03691 g009
Figure 9. HDT of PALF and flax composites containing different fiber contents. Gray bar represents neat PBS.
Figure 9. HDT of PALF and flax composites containing different fiber contents. Gray bar represents neat PBS.
Polymers 15 03691 g009
Polymers 15 03691 g010
Figure 10. Impact fracture surfaces of PALF/PBS and flax/PBS composites containing different fiber contents.
Figure 10. Impact fracture surfaces of PALF/PBS and flax/PBS composites containing different fiber contents.
Polymers 15 03691 g010
Polymers 15 03691 g011
Figure 11. (a) XRD patterns of composite prepregs and sheets; (b) X-ray pole figures for (110) plane of PALF/PBS and flax/PBS composite prepregs and sheets compressed at 140 °C.
Figure 11. (a) XRD patterns of composite prepregs and sheets; (b) X-ray pole figures for (110) plane of PALF/PBS and flax/PBS composite prepregs and sheets compressed at 140 °C.
Polymers 15 03691 g011
Polymers 15 03691 g012
Figure 12. Low magnification optical micrographs of (a) PALF and (b) flax fibers after solvent extraction from their respective 20 wt.% composite prepregs.
Figure 12. Low magnification optical micrographs of (a) PALF and (b) flax fibers after solvent extraction from their respective 20 wt.% composite prepregs.
Polymers 15 03691 g012
Table 1. Chemical composition of PALF and flax fibers.
Table 1. Chemical composition of PALF and flax fibers.
Chemical Constituent (%)PALFFlax
Cellulose (%)57.267.2
Holocellulose (%)85.582.6
Lignin (acid soluble)2.60.9
Lignin (acid insoluble)7.86.5
Table 2. Thermal properties of PBS/PALF and PBS/flax composites.
Table 2. Thermal properties of PBS/PALF and PBS/flax composites.
SampleFirst HeatingCoolingSecond Heating
Tm (°C)Xc (%)Tc (°C)Tm (°C)Xc (%)
PBS115.075.484.4114.472.6
10PALF114.278.981.4114.275.7
20PALF114.479.082.8114.075.5
10Flax114.876.281.0114.872.9
20Flax115.076.481.8115.372.6
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Amornsakchai, T.; Duangsuwan, S.; Mougin, K.; Goh, K.L. Comparative Study of Flax and Pineapple Leaf Fiber Reinforced Poly(butylene succinate): Effect of Fiber Content on Mechanical Properties. Polymers 2023, 15, 3691. https://doi.org/10.3390/polym15183691

AMA Style

Amornsakchai T, Duangsuwan S, Mougin K, Goh KL. Comparative Study of Flax and Pineapple Leaf Fiber Reinforced Poly(butylene succinate): Effect of Fiber Content on Mechanical Properties. Polymers. 2023; 15(18):3691. https://doi.org/10.3390/polym15183691

Chicago/Turabian Style

Amornsakchai, Taweechai, Sorn Duangsuwan, Karine Mougin, and Kheng Lim Goh. 2023. "Comparative Study of Flax and Pineapple Leaf Fiber Reinforced Poly(butylene succinate): Effect of Fiber Content on Mechanical Properties" Polymers 15, no. 18: 3691. https://doi.org/10.3390/polym15183691

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop