Crystals 2014, 4(3), 296-305;

Preparation and Characterization of Lead-Free (K0.5Na0.5)NbO3-LiNbO3 and (K0.5Na0.5)NbO3-LiTaO3 Ferroelectric Single Crystals

Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou 350002, China
Department of Chemistry and 4D LABS, Simon Fraser University, Burnaby, BC V5A1S6, Canada
Author to whom correspondence should be addressed.
Received: 20 April 2014 / Revised: 9 June 2014 / Accepted: 2 July 2014 / Published: 16 July 2014
(This article belongs to the Special Issue Piezoelectric Crystals)
Full-Text   |   PDF [12884 KB, uploaded 16 July 2014]   |  


Lead-free (K0.5Na0.5)NbO3-LiNbO3 (KNN-LN) and (K0.5Na0.5)NbO3-LiTaO3 (KNN-LT) ferroelectric single crystals, with the dimensions of 11 ´ 11 ´ 5 mm3 and 5 ´ 5 ´ 3 mm3, were grown successfully using the top-seeded solution growth (TSSG) method, respectively. The crystal structures were analyzed by means of X-ray diffraction, showing orthorhombic symmetry for KNN-LN single crystals and coexistence of orthorhombic and tetragonal symmetry for KNN-LT single crystals at room temperature. The orthorhombic-tetragonal (TO-T) and tetragonal-cubic (TC) phase transition temperatures are 195 °C and 420 °C for the KNN-LN single crystals, and 130 °C and 280 °C for KNN-LT single crystals, respectively. The remnant polarization (Pr) is 27.8 μC/cm2 with a coercive field (Ec) of 17 kV/cm for KNN-LT single crystals. The two single crystals showed 90° domains with layers in (parallel) straight lines, while KNN-LT single crystals have a larger domain region. The actual stoichiometry deviates easily from the original composition in the process of crystal growth, thus, an appropriate nominal composition and optimized crystal growth method is desired to get high-quality crystals in the future. View Full-Text
Keywords: crystal growth; lead-free ferroelectric materials; single crystals; domain crystal growth; lead-free ferroelectric materials; single crystals; domain

Graphical abstract

This is an open access article distributed under the Creative Commons Attribution License (CC BY 3.0).

Share & Cite This Article

MDPI and ACS Style

Chu, T.; He, C.; Tailor, H.; Long, X. Preparation and Characterization of Lead-Free (K0.5Na0.5)NbO3-LiNbO3 and (K0.5Na0.5)NbO3-LiTaO3 Ferroelectric Single Crystals. Crystals 2014, 4, 296-305.

Show more citation formats Show less citations formats

Related Articles

Article Metrics

Article Access Statistics



[Return to top]
Crystals EISSN 2073-4352 Published by MDPI AG, Basel, Switzerland RSS E-Mail Table of Contents Alert
Back to Top