Next Article in Journal
Topology of WC/Co Interfaces in Cemented Carbides
Previous Article in Journal
Research and Development of Self-Waterproofing Concrete for Tunnel Lining Structure and Its Impermeability and Crack Resistance Characteristics
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 16
Issue 16
10.3390/ma16165559
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Effects of Oxygen Flow during Fabrication by Magnetron Sputtering on Structure and Performance of Zr-Doped HfO2 Thin Films

by
Yingxue Xi
*,
Lei Liu
,
Jiwu Zhao
,
Xinhui Qin
,
Jin Zhang
,
Changming Zhang
and
Weiguo Liu
School of Optoelectronic Engineering, Xi’an Technological University, Xi’an 710021, China
*
Author to whom correspondence should be addressed.
Materials 2023, 16(16), 5559; https://doi.org/10.3390/ma16165559
Submission received: 29 June 2023 / Revised: 6 August 2023 / Accepted: 7 August 2023 / Published: 10 August 2023
(This article belongs to the Special Issue Advances in Ferroelectric Materials and Devices)
Browse Figures
Versions Notes

Abstract

:
Oxygen defects in Hafnium Oxide (HfO2)-based ferroelectric thin films not only are related to the cause of ferroelectricity but also affect the ferroelectric properties of the thin films. This paper, therefore, focuses on the fabrication of Zr:HfO2 thin films by RF (Radio Frequency) magnetron sputtering with Zr-doped HfO2 as the target and examines how oxygen flow impacts the oxygen vacancies and electrical properties thereof. Additionally, TiN thin-film electrodes were prepared by direct current (DC) magnetron reactive sputtering using nitrogen as the reaction gas, the influences of the substrate temperature on the film deposition rate and crystal phase structure were investigated, and the resultant thin-film electrodes with the lowest resistivity were obtained. Furthermore, the ferroelectric hysteresis loop and leakage current density of metal–insulator–metal (MIM) ferroelectric capacitors formed by annealing the 30 nm thick deposited Zr:HfO2 sandwiched between the top and bottom TiN electrodes were measured. The results demonstrate that varying oxygen flow has a considerable effect on oxygen vacancies and the Zr doping concentration of deposited Zr:HfO2 ferroelectric thin films. When the oxygen flow is set to 40 sccm (standard cubic centimeters per minute) and an external electric field strength of 2 mV/cm is applied, the remnant polarization reaches 18 μC/cm2, with a decrease in the leakage current density of 105–6 orders of magnitude.

1. Introduction

Due to its low optical loss, high refractive index, high laser damage threshold, and good chemical and mechanical properties, Hafnium Oxide (HfO2) has become a major alternative material for the fabrication of optoelectronic thin films [1,2,3]. Featuring a high dielectric constant, wide band gap, low electron tunneling effect, and excellent CMOS (Complementary Metal–Oxide Semiconductor) compatibility, HfO2 can substitute for silicon oxide as the next-generation oxide gate dielectric material, hence finding wide applications in various memory devices, such as airplanes, medical electronics, smart meters, or cell phone chips [4,5,6]. In 2011, Müller et al. [7] revealed dielectric anomalies in doped HfO2 thin films, verifying their impressive ferroelectric properties. Given that HfO2 ferroelectric thin films can surmount the key problem of compatibility between traditional ferroelectric materials and the CMOS process and have the potential for miniaturization to enhance integration and storage capacity, doped HfO2 thin films should be highly promising for non-volatile memory (NVM) applications [8].
HfO2 thin films can be fabricated by Atomic Layer Deposition (ALD) [9], Physical Vapor Deposition (PVD) [10,11,12,13], Chemical Vapor Deposition (CVD) [14], or Pulsed Laser Deposition (PLD) [15]. Compared to other fabrication techniques, PVD-derived HfO2 thin films offer higher purity and superior performance [16,17], which can be achieved through the adjustment of parameters such as working pressure, sputtering power, gas flow ratio, and substrate temperature. Furthermore, Physical Vapor Deposition (PVD) techniques, such as magnetron sputtering, find wide use in industrial production for their superior automation and high output [18].
Doped HfO2 thin films can modify their lattice orientation, thus favoring the formation of an orthogonal phase featuring ferroelectricity. To date, laboratory experiments have managed to prepare ferroelectric HfO2 thin films doped with Zr [8], Y [17,19], Si [20], Al [21], and La [22]. Both ZrO2 and HfO2 are highly sought-after materials with similar physicochemical properties employed in the making of advanced metal–oxide–semiconductor field-effect transistors (MOSFETs) and high-K materials. In this regard, Mueller et al. [23] first reported the ferroelectric (FE) properties of Hf0.5Zr0.5O2 deposited by ALD. Moreover, Hf1-xZrxO2 materials drew wide attention in that they could crystallize into films at lower temperatures ranging from 400 to 600 °C [24], with the remnant polarization, dielectric constant, and content of the monoclinic phase in the films modulated by integrated components. The ferroelectric properties of Hf1-xZrxO2 thin films deposited by ALD were limited by the performance of such films, revealing a maximum thickness of 20 nm [25]. Magnetron sputtering, a coating technique widely used in industry, allows precise control over film components to achieve industrial production, although it is difficult to control the thickness at the atomic level. Oxygen defects in HfO2-based ferroelectric thin films bear relevance to the cause of ferroelectricity [26,27,28] and affect their ferroelectric properties as well. Zhou et al. [29] revealed that HfO2 ferroelectricity and wake-up and fatigue effects could be attributed to oxygen vacancies through first-principles calculations and that oxygen vacancies could stabilize the ferroelectric Polarization-Orthogonal (PO) phase through numerous experiments. Mitmann et al. [26] discovered that oxygen vacancies, when at an appropriate concentration, can positively impact the ferroelectric properties of HZO thin films. Baumgarten et al. [28] further confirmed the influences of oxygen flow on the number of oxygen vacancies in HfO2 thin films prepared through magnetron sputtering. In this paper, Zr-doped HfO2 thin films were fabricated by Radio Frequency (RF) magnetron sputtering by using a single zirconium-doped hafnium metal target under constant working air pressure, and the impact of oxygen flow on the film components was analyzed. A three-layer heterojunction consisting of TiN/X-HfO2/TiN was deposited onto a Si substrate, with TiN thin films deposited via DC magnetron sputtering as the electrode; subsequently, the components and electrical properties of the annealed HZO were examined.

2. Film Preparation and Characterization

Doped HfO2 thin films were fabricated via RF magnetron sputtering on a P-type (100) single-crystal silicon substrate. The substrate was subjected to an ultrasonic cleaning procedure using acetone and anhydrous ethanol solution for 20 min prior to being coated, followed by rinsing with deionized water and blow-drying with nitrogen. In the fabrication of doped HfO2-based thin films by magnetron sputtering, a double-target co-sputtering approach is typically adopted [17,30,31,32,33]. As shown in Figure 1, a Zr-doped Hf target was employed in this study.
A Hf target with a size of Φ 60 mm × 5 mm and 99.99% purity was used as the magnetron sputtering cathode. Symmetrical circular holes of Φ 10 mm × 3 mm were cut at the magnetic field of the racetrack on the cathode target surface, where circular plates of Φ 10 mm × 3 mm made of doped Zr with purity ≥ 99.9% were uniformly installed. By using this method, uniformly doped HfO2 thin films were obtained. Moreover, the doping concentration could be modulated by controlling the number of circular element-doped plates in the magnetic field of the racetrack. The element-doped concentration could be characterized and calculated in line with the measurements of X-ray photoelectron spectroscopy (XPS). In this study, Thermo Scientific K-Alpha XPS (Waltham, MA, USA) was employed to analyze the components of the samples.
The coating process was conducted under conditions wherein the background vacuum was 2.0 × 10−3 Pa, with high-purity argon (≥99.99%) as the working gas and a target-to-substrate distance of 60 mm. In addition, prior to the coating process, the working pressure was set to 1 Pa, and a pre-sputtering process was performed for 15 min. Then, the coating experiment started. In fabricating TiN electrodes, pure nitrogen was introduced as the reaction gas, with an argon-flow-to-nitrogen-flow ratio of 10:1, wherein the argon flow was 30 sccm (standard cubic centimeter per minute, sccm), while the nitrogen flow was 3 sccm; the sputtering power was set to 140 W, and the working vacuum remained at 0.5 Pa by regulating the insert valve. The film thickness was regulated by appropriately adjusting the coating time to 20 min; this ensured an electrode thickness range between 30 nm and 40 nm. The resistivity of TiN films was calculated as a product of the thickness and sheet resistance measured by a four-point probe method. During the process of preparing doped HfO2 thin films, the target-to-substrate distance remained unchanged, with the sputtering power set to 100 W and the argon flow rate at 40 sccm; pure oxygen (≥99.99%) was introduced as the reaction gas, and the working vacuum was adjusted to 0.7 Pa without heating the substrate.
To investigate the electrical properties of doped HfO2 thin films, TiN electrodes were required to be coated on the top and bottom of the thin films. The preparation process and final samples are illustrated in Figure 2.
By using this method, a TiN/HfO2/TiN/Si heterojunction was formed through the deposition of a bottom TiN electrode, doped HfO2, and a top TiN electrode on a single-crystal silicon substrate. According to the competitive growth mechanism, the conductivity of TiN thin films is related to their lattice orientation, which can be controlled by tweaking the substrate temperature during the coating process.
Figure 3 displays the sheet resistance and resistivity of TiN thin films deposited by DC magnetron sputtering at various substrate temperatures (100 °C, 200 °C, 300 °C, 400 °C, and 500 °C), with the latter obtained from the product of sheet resistance and film thickness.
As the substrate temperature varied from 100 °C to 500 °C, the film thickness was found to be 35.6 nm, 37.8 nm, 36.4 nm, 35.3 nm, and 34.8 nm, accordingly. As illustrated in the figure, the sheet resistance and resistivity of the TiN thin film drop and then rise with the substrate temperature. At a substrate temperature of 300 °C, the sheet resistance is 8.3 Ω/□, which corresponds to a film resistivity of 30.2 µΩ·cm, slightly higher than that of the TiN block. This trend in the resistivity of TiN thin films may be attributable to their crystal structure. Figure 4 illustrates the grazing incidence scanning spectra of TiN thin films deposited at varying substrate temperatures with the Bruker D8 grazing incidence X-ray diffractometer.
Specifically, CuKα was used as the X-ray source, with a scan range from 10° to 80° and a grazing incidence angle of 1° at a scan rate of 2°/min. The analysis of the figure reveals that the preferred orientation of the crystal phase of TiN thin films transitions from (111) at 100 °C to (200) at 300 °C with increasing substrate temperature. As the substrate temperature continues to rise, each crystal phase of the thin films can obtain sufficient energy for competitive growth, eventually resulting in the polymorphism of the thin films. It has been established that thin films growing along (200) possess lower resistivity [34]. Thus, 300 °C was selected as the substrate temperature to fabricate TiN electrodes in this study.
At room temperature, the crystal phase of crystalline HfO2 is monoclinic [33], whereas high-temperature annealing is known to stimulate its transition from a monoclinic phase to a tetragonal phase, with its subsequent stabilization in a cubic phase. When HfO2 thin films are doped with other cations, the number of monoclinic phases in the films declines while that of tetragonal phases begins to rise, which indicates that the presence of tetragonal phases ultimately leads to the ferroelectricity of HfO2 thin films. The samples in this study were annealed in an RTP 500 rapid furnace for 40 s in a nitrogen atmosphere at 700 °C, with the heat treatment applied at a ramp-up rate of 35 °C/s, followed by a cooldown conducted in the furnace.

3. Results and Discussion

3.1. Variations in Deposition Rate and Components of Zr-Doped HfO2 Thin Films at Various Oxygen Flow Rates

As illustrated in Figure 5, the variation curve of the deposition rate of HZO at various oxygen flow rates was obtained from the Zr-doped HfO2 thin film (HZO) experiment using RF magnetron sputtering, wherein the oxygen flow was set to 10 sccm, 20 sccm, 30 sccm, 40 sccm, and 50 sccm, with other process and conditions remaining the same.
Specifically, the inset shows the film thicknesses measured with a non-contact 3D surface profiler from ZYGO when film steps were obtained by masking at an oxygen flow rate of 40 sccm.
As shown in Figure 5, the deposition rate of thin films does not fluctuate with the rise in oxygen flow but remains unchanged when the oxygen flow is increased from 10 sccm to 50 sccm in a given process range with a fixed working air pressure. Among all the elements that affect the deposition rate, the target power, working air pressure, and oxygen flow take the top three places in terms of importance [35]. In principle, at a lower oxygen flow rate, thin films are deposited in the metallic mode at an accelerated pace. As shown in the figure, the deposition rate of the doped metal film reaches 12.8 nm/min in the oxygen-free mode, which is far greater than that of the film in the reactive mode in the oxygen condition. However, an excessively high concentration of oxygen leads to target poisoning, subsequently resulting in a lower deposition rate. In this paper, it is evident that the deposition rate remained unaffected by alterations in oxygen flow, suggesting that the conditions chosen for the deposition of the thin films were well suited.
The Zr-doped HfO2 thin films obtained at various oxygen flow rates were tested with X-ray photoelectron spectroscopy (XPS) after a 40 s Ar+-etching procedure was performed on the surfaces of the films to remove contaminants on them. Subsequently, XPS results were analyzed using the Avantage software, and the O1s fine spectrum fitting graphs of the Zr-doped HfO2 thin films were successfully fitted, as shown in Figure 6.
Figure 6a presents the O1s fine spectrum fitting graphs of the thin films deposited at an oxygen flow rate of 10 sccm. The main peak of the binding energy, 529.37 eV, falling within the O1s (529.00~530.00 eV) binding energy range of metal oxide compounds, corresponds to Zr-O and Hf-O bonds [36], whereas the minor peak at 531.63 eV corresponds to the oxygen vacancies present within the films [17,37]. Figure 6b–e illustrate the fitting results of O1s fine spectra obtained at oxygen flow rates of 20 sccm, 30 sccm, 40 sccm, and 50 sccm, respectively. It can be observed that the main peaks characterizing Zr-O and Hf-O bonds and minor peaks characterizing oxygen vacancies arise in all spectra. The minor peak area is reduced correspondingly as the oxygen flow increases, suggesting that oxygen vacancies drop in number with increasing oxygen flow.
Figure 7 illustrates the fine scanning spectra of photoelectron spectroscopy of Hf-4f and Zr-3d peaks of Zr-doped HfO2 thin films deposited at varying oxygen flow rates.
By means of Gaussian Peak Fitting of Hf-4f, the spin–orbit-splitting-induced Hf-4f7/2 and Hf-4f5/2 peaks are identified, respectively, at 16.1 eV and 17.8 eV. The splitting energy is 1.7 eV, which is in agreement with the findings reported in the literature that characterizes the Hf-O bond in HfO2 thin films [37], implying that Hf exists in the form of Hf+4. Although the binding energy of the Hf 4f peak of HfOx<2 has not yet been reported, it is plausible that the binding energy of the Hf-4f peak shifts closer to the Hf atom as oxygen defects in the films grow. In contrast, the HfO2 spectrum measured in the figure is characterized by a bimodal binding energy of Hf-4f, which shifts toward the Hf peak as the oxygen flow increases. This is because the air pressure remained constant during the preparation. Consequently, as the oxygen flow rises, a concomitant rise in the vacuum pumping rate is required to maintain constant air pressure. A plausible explanation is that neutral oxygen vacancies formed during the process of film deposition are almost completely replaced by two electrons from the Hf atom [38]. This novel double-site occupancy defect state would promote a shift in the Fermi energy level [39], thereby leading to the augmentation of the binding energy of the Hf-4f peak. Further experiments and theoretical investigations are necessary to expound on this phenomenon. According to the figure, increased oxygen flow caused a progressive reduction in oxygen vacancies in the films and, consequently, resulted in a steady fall in the binding energy of the Hf-4f peak. However, when the oxygen flow rate was 50 sccm, the defects and vacancies in the deposited films increased, resulting in the Hf-4f peak binding energy no longer declining. In fact, research [29,40] has confirmed that oxygen vacancies are the primary driver of the ferroelectric phase of Hf-based thin films in a metastable state, and thus, the effective regulation of these vacancies in thin films is essential in forming the ferroelectric phase.
A similar phenomenon to the Hf-4f peak was also observed in the Zr-3d peak, where the binding energy was affected by the transfer of nearby O2 charges. As depicted in Figure 7b, the Zr-3d peak splits into two peaks corresponding to spin–orbit-splitting-induced Zr-3d5/2 and Zr-3d3/2 at 184.62 eV and 184.62 eV [41], respectively, implying the presence of Zr-O bonds in the films. As illustrated in Figure 7b, the bonding energy of the two peaks of Zr-3d declines with increasing oxygen flow below 40 sccm, yet it marginally rises at the oxygen flow rate of 50 sccm. By taking account of the ratio of the peak area of Hf-4f to that of Zr-3d, the content of Zr can be calculated at the different oxygen flow rates as follows: 12 mol.%, 14 mol.%, 15 mol.%, 15.3 mol.%, and 18 mol.%. It can be seen that both the Hf-4f peak and Zr-3d peak shift toward a lower binding energy position when the oxygen flow is augmented. This implies that oxygen vacancies within the films decrease with the increase in oxygen flow, and the difference in their shift magnitudes signifies that some of the Hf-O bonds are substituted by Zr-O bonds.
Figure 8 shows the X-ray energy dispersion spectrum and AFM pattern of Zr-HfO2 thin films prepared at an oxygen flow rate of 40 sccm. As shown in the figure, the Hf, O2, and Zr elements in the film are randomly and uniformly distributed without segregation, which proves that the elemental distribution of the film deposited by reactive sputtering using a zirconium-doped hafnium target is uniform. The AFM pattern shows that the deposited film is uniform, and the grain size is between 10 and 20 nm. Root-mean-square (RMS) surface roughness is 7.03 nm.

3.2. HZO-Based Heterojunction I–V Test and Polarization Curve Measurement

Figure 9 shows the I–V characteristic curves of the TiN/HZO/TiN heterojunction fabricated at various oxygen flow rates. It is evident from the figure that the heterojunction features a low leakage current. Such a feature can help reduce the loss of the device and improve its reliability and durability [42]. The asymmetry of the leakage current curves is due to the electrostatic potential barriers generated between the TiN electrode material and HZO thin film, and the presence of oxygen vacancies gives the curves a bulged shape. An analysis of the I-E curve reveals that, when an external electric field of 2 MV/cm is applied, the leakage current in the heterojunction decreases gradually as the oxygen flow increases from 10 sccm to 40 sccm; at an oxygen flow rate of 40 sccm, a minimum leakage current of approximately 10−5.6 A/cm2 is achieved; however, an increase in the oxygen flow to 50 sccm results in a further increase in the leakage current. When the oxygen flow rises, the vacuum pumping rate increases automatically to maintain the stable working pressure, leading to an increase in oxygen partial pressure and a drop in argon partial pressure at the working pressure. Eventually, the deposition rate of thin films declines slightly at an oxygen flow rate of 50 sccm (as exhibited in Figure 5). However, an unwanted increase in oxygen can lead to more defects in the films and, thus, a higher energy leakage in capacitors.
Using a ferroelectric analyzer, a polarization-intensity–external electric field (P-E) test was conducted on a Zr-doped HfO2-based heterojunction. Figure 10 displays the results of the P-E ferroelectric hysteresis loop.
At an oxygen flow rate of 10 sccm, the capacitor exhibits a linear orientation instead of a hysteresis curve, represented as paraelectricity. As the oxygen flow increases, the capacitor demonstrates obvious ferroelectricity characteristics, reaching a maximum remnant polarization of approximately 18 µC/cm2 and a coercive electric field of 2 MV/cm when the oxygen flow gradually increases to 40 sccm. However, with the oxygen flow increasing to 50 sccm, both the remnant polarization intensity and coercive electric field begin to decrease, possibly resulting from the excessive oxygen flow, which may have led to an increment in defects in the fabricated Zr-doped HfO2 thin films. In this study, Zr:HfO2 thin films showed good ferroelectricity and a maximum Zr doping amount of up to 20% mol. Moreover, its ferroelectric properties correlated with oxygen vacancies. Compared to the thin films fabricated by Atomic Layer Deposition (ALD), the films prepared herein remained unaffected by size effects, with a thickness of up to 30 nm. Additionally, the Zr:HfO2 heterojunction possessed an enhanced remnant polarization intensity and band gap, making it thermally stable and compatible with Complementary Metal–Oxide Semiconductors (CMOSs) and thus capable of being fabricated by 3D integration technology.

4. Conclusions

In this study, a Zr-doped TiN/HfO2/TiN heterojunction was fabricated on the Si substrate by RF magnetron sputtering. The study focused on the analysis of the chemical components and oxygen vacancies in Zr:HfO2 thin films prepared at varying oxygen flow rates and their impacts on the ferroelectric characteristics of the heterojunction. According to XPS analysis results, an increase in oxygen flow led to a diminishing number of oxygen vacancies in the films, and these vacancies were regarded as what caused the ferroelectricity of the films. Conversely, when the oxygen flow reached 50 sccm, a surplus of oxygen led to the heightening of defects in films. This result had a considerable effect on the electrical properties of the films, wherein the leakage current of the Zr-doped HfO2-based heterojunction fluctuated as the oxygen flow increased from 10 sccm to 50 sccm, with the small remnant polarization getting larger and then smaller. At the appropriate oxygen flow rate of 40 sccm, the remnant polarization intensity (Pr) attained a maximum of 18 µC/cm2, with the coercive electric field (Ec) amounting to approximately 2 MV/cm and the Zr-doped thin films reaching a thickness of 30 nm.

Author Contributions

Methodology, Y.X. and W.L.; Validation, X.Q.; Investigation, Y.X., L.L. and J.Z. (Jiwu Zhao); Resources, C.Z. and W.L.; Data curation, L.L.; Writing—original draft, Y.X., L.L. and J.Z. (Jiwu Zhao); Writing—review & editing, Y.X. and J.Z. (Jin Zhang); Supervision, Y.X.; Project administration, Y.X.; Funding acquisition, Y.X. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ahmad, Z.; Cheng, X.; Shahid, T.; Anwar, M.; Zhenlun, S. Effects of O2 Flux on Structure, Optical Properties and Hydrophobicity of Highly Emissive Antireflective HfO2 Thin Films by Magnetron Sputtering. Vacuum 2022, 197, 110824. [Google Scholar]
  2. Khan, S.B.; Wu, H.; Ma, L.; Hou, M.; Zhang, Z. HfO2 Nanorod Array as High-Performance and High-Temperature Antireflective Coating. Adv. Mater. Interfaces 2017, 4, 1600892. [Google Scholar] [CrossRef]
  3. Lin, S. Optical properties of HfO2 nanoceramic films as a function of N–Bi co-doping. Ceram. Int. 2014, 40, 5707–5713. [Google Scholar] [CrossRef]
  4. Buckley, J.; De Salvo, B.; Ghibaudo, G.; Gely, M.; Damlencourt, J.F.; Martin, F.; Nicotra, G.; Deleonibus, S. Investigation of SiO2/HfO2 gate stacks for application to non-volatile memory devices. Solid State Electron. 2005, 49, 1833–1840. [Google Scholar] [CrossRef]
  5. Fan, Y.; Ovchinnikov, I.V.; Jiang, W.; Schwartz, R.N.; Wang, K.L. Fluctuations in nanoscale magnetoelectronics devices. J. Appl. Phys. 2012, 112, 114–174. [Google Scholar] [CrossRef] [Green Version]
  6. Boscke, T.S.; Muller, J.; Brauhaus, D.; Schroder, U.; Bottger, U. Ferroelectricity in hafnium oxide thin films. Appl. Phys. Lett. 2011, 99, 112903. [Google Scholar] [CrossRef]
  7. Jena, S.; Tokas, R.B.; Misal, J.S.; Rao, K.D.; Udupa, D.V.; Thakur, S.; Sahoo, N.K. Effect of O2/Ar gas flow ratio on the optical properties and mechanical stress of sputtered HfO2 thin films. Thin Solid Film. 2015, 592, 135–142. [Google Scholar] [CrossRef]
  8. Min, H.P.; Han, J.K.; Yu, J.K.; Moon, T.; Kim, K.D.; Hwang, C.S. Thin HfxZr1-xO2 films: A new lead-free system for electrostatic supercapacitors with large energy storage density and robust thermal stability. Adv. Energy Mater. 2014, 16, 1400610. [Google Scholar]
  9. Aarik, J.; Mändar, H.; Kirm, M.; Pung, L. Optical characterization of HfO2 thin films grown by atomic layer deposition. Thin Solid Film. 2004, 466, 41–47. [Google Scholar] [CrossRef]
  10. Dave, V.; Dubey, P.; Gupta, H.O.; Chandra, R. Influence of sputtering pressure on the structural, optical and hydrophobic properties of sputtered deposited HfO2 coatings. Thin Solid Film. 2013, 549, 2–7. [Google Scholar] [CrossRef]
  11. Tan, R.; Azuma, Y.; Kojima, I. Suppression of interfacial diffusion by a predeposited Hf metal layer on SiO2/Si. Appl. Surf. Sci. 2004, 22, 346–350. [Google Scholar] [CrossRef]
  12. Aygun, G.; Yildiz, I. Interfacial and structural properties of sputtered HfO2 layers. J. Appl. Phys. 2009, 106, 014312. [Google Scholar] [CrossRef] [Green Version]
  13. Lehan, J.; Mao, Y.; Bovard, B.G.; Macleod, H.A. Optical and microstructural properties of hafnium dioxide thin films. Thin Solid Film. 1991, 203, 227–250. [Google Scholar] [CrossRef]
  14. Smirnova, T.P.; Yakovkina, L.V.; Kitchai, V.N.; Kaichev, V.; Shubin, Y.; Morozova, N.; Zherikova, K. Chemical vapor deposition and characterization of hafnium oxide films. J. Phys. Chem. Solids 2008, 69, 685–687. [Google Scholar] [CrossRef]
  15. Zhu, J.; Liu, Z.G.; Feng, Y. Thermal stability and electrical properties of pulsed laser-deposited Hf-silicate thin films for high-k gate dielectric applications. J. Phys. D Appl. Phys. 2003, 36, 3051–3056. [Google Scholar] [CrossRef]
  16. Mittmann, T.; Materano, M.; Lomenzo, P.D.; Park, M.H.; Stolichnov, I.; Cavalieri, M.; Zhou, C.; Chung, C.-C.; Jones, J.L.; Szyjka, T.; et al. Origin of Ferroelectric Phase in Undoped HfO2 Films Deposited by Sputtering. Adv. Mater. Interfaces 2019, 6, 1900042. [Google Scholar] [CrossRef] [Green Version]
  17. Zhang, W.; Zhou, D.; Sun, N.; Wang, J.; Li, S. Effect of Bias Voltage on Substrate for the Structure and Electrical Properties of Y:HfO2 Thin Films Deposited by Reactive Magnetron Co-Sputtering. Adv. Electron. Mater. 2021, 7, 2100488. [Google Scholar] [CrossRef]
  18. Musil, J.; Baroch, P.; Vlček, J.; Nam, K.H.; Han, J.G. Reactive magnetron sputtering of thin films: Present status and trends. Thin Solid Film. 2005, 475, 208–218. [Google Scholar] [CrossRef]
  19. Mimura, T.; Shimizu, T.; Funakubo, H. Ferroelectricity in YO1.5-HfO2 films around 1 μm in thickness. Appl. Phys. Lett. 2019, 115, 032901. [Google Scholar] [CrossRef]
  20. Böescke, T.S.; Teichert, S.; Bräuhaus, D.; Müller, J.; Schröder, U.; Böttger, U.; Mikolajick, T. Phase transitions in ferroelectric Silicon doped Hafnium oxide. Appl. Phys. Lett. 2011, 99, 112904. [Google Scholar] [CrossRef]
  21. Mueller, S.; Mueller, J.; Singh, A.; Riedel, S.; Sundqvist, J.; Schroeder, U. Mikolajick.Incipient ferroelectricity in Al-doped HfO2 thin films. Adv. Funct. Mater. 2014, 22, 2412–2417. [Google Scholar] [CrossRef]
  22. Schroeder, U.; Richter, C.; Park, M.H.; Schenk, T.; Pešić, M.; Hoffmann, M.; Fengler, F.; Pohl, D.; Rellinghaus, B.; Zhou, C.; et al. Lanthanum-Doped Hafnium Oxide: A Robust Ferroelectric Material. Appl. Phys. Lett. 2018, 57, 2752–2765. [Google Scholar] [CrossRef] [PubMed]
  23. Mueller, J.; Boescke, T.S.; Schroeder, U.; Mueller, S.; Braeuhaus, D.; Boettger, U.; Frey, L.; Mikolajick, T. Ferroelectricity in simple binary ZrO2 and HfO2. Nano Lett. 2012, 12, 4318–4323. [Google Scholar] [CrossRef]
  24. Park, M.H.; Kim, H.J.; Kim, Y.J.J.; Moon, T.; Kim, K.D.; Hwang, C.S. Toward a multifunctional monolithic device based on pyroelectricity and the electrocaloric effect of thin antiferroelectric HfxZr1-xO2 films. Nano Energy 2015, 12, 131–140. [Google Scholar] [CrossRef]
  25. Park, M.H.; Kim, H.J.; Kim, Y.J.; Lee, W.; Moon, T.; Hwang, C.S. Evolution of phases and ferroelectric properties of thin Hf0.5Zr0.5O2 films according to the thickness and annealing temperature. Appl. Phys. Lett. 2013, 102, 242905. [Google Scholar] [CrossRef]
  26. Mittmann, T.; Materano, M.; Chang, S.-C.; Karpov, I.; Mikolajick, T.; Schroeder, U. Impact of oxygen vacancy content in ferroelectric HZO films on the device performance. In Proceedings of the 2020 IEEE International Electron Devices Meeting (IEDM), San Francisco, CA, USA, 12–18 December 2020; pp. 18.4.1–18.4.4. [Google Scholar]
  27. Islamov, D.R.; Zalyalov, T.M.; Orlov, O.M.; Gritsenko, V.A.; Krasnikov, G.Y. Impact of oxygen vacancy on the ferroelectric properties of lanthanum-doped hafnium oxide. Appl. Phys. Lett. 2020, 117, 162901. [Google Scholar] [CrossRef]
  28. Baumgarten, L.; Szyjka, T.; Mittmann, T.; Materano, M.; Schlueter, C.; Schroeder, U.; Müller, M. Impact of vacancies and impurities on ferroelectricity in PVD- and ALD- grown HfO2 films. Appl. Phys. Lett. 2020, 118, 032903. [Google Scholar] [CrossRef]
  29. Zhou, Y.; Zhang, Y.K.; Yang, Q.; Jiang, J.; Fan, P.; Liao, M.; Zhou, Y.C. The effects of oxygen vacancies on ferroelectric phase transition of HfO2-based thin film from first-principle. Comput. Mater. Sci. 2019, 167, 143–150. [Google Scholar] [CrossRef]
  30. Akkaya, A.; Kahveci, O.; Şahin, B.; Ayyıldız, E. Simultaneously-doping of HfO2 thin films by Ni with sputtering technique and effect of post annealing on structural and electrical properties. Phys. B Condens. Matter 2023, 665, 415034. [Google Scholar] [CrossRef]
  31. Olsen, T.; Schröder, U.; Müller, S.; Krause, A.; Martin, D.; Singh, A.; Müller, J.; Geidel, M.; Mikolajick, T. Co-sputtering yttrium into hafnium oxide thin films to produce ferroelectric properties. Appl. Phys. Lett. 2012, 101, 082905. [Google Scholar] [CrossRef]
  32. Xu, L.; Shibayama, S.; Izukashi, K.; Nishimura, T.; Yajima, T.; Migita, S.; Toriumi, A. General relationship for cation and anion doping effects on ferroelectric HfO2 formation. In Proceedings of the 2016 IEEE International Electron Devices Meeting (IEDM), San Francisco, CA, USA, 3–7 December 2016; pp. 25.2.1–25.2.4. [Google Scholar]
  33. Xu, L.; Nishimura, T.; Shibayama, S.; Yajima, T.; Migita, S.; Toriumi, A. Kinetic pathway of the ferroelectric phase formation in doped HfO2 films. J. Appl. Phys. 2017, 122, 124104. [Google Scholar] [CrossRef]
  34. Sun, N.; Xu, J.; Zhou, D.; Zhao, P.; Li, S.; Wang, J.; Chu, S.; Ali, F. DC reactively sputtered TiNx thin films for capacitor electrodes. J. Mater. Sci. Mater. Electron. 2018, 29, 10170–10176. [Google Scholar] [CrossRef]
  35. Stutzin, G.C.; Rózsa, K.; Gallagher, A. Deposition rates in direct current diode sputtering. J. Vaccuum Sci. Technol. A 1993, 11, 647–656. [Google Scholar] [CrossRef]
  36. Heo, S.; Tahir, D.; Chung, J.G.; Lee, J.C.; Kim, K.; Lee, J.; Lee, H.; Park, G.S.; Oh, S.K.; Kang, H.J.; et al. Band alignment of atomic layer deposited (HfZrO4)1-x(SiO2)x gate dielectrics on Si(100). Appl. Phys. Lett. 2015, 107, 182101. [Google Scholar] [CrossRef]
  37. Ganapathi, K.L.; Bhat, N.; Mohan, S. Influence of O2 flow rate on HfO2 gate dielectrics for back-gated graphene transistors. Semicond. Sci. Technol. 2014, 29, 055007. [Google Scholar] [CrossRef]
  38. Foster, A.S.; Gejo, F.L.; Shluger, A.L.; Nieminen, R.M. Vacancy and interstitial defects in hafnia. Phys. Rev. B 2006, 65, 174117. [Google Scholar] [CrossRef] [Green Version]
  39. Cho, D.; Oh, S.-J.; Chang, Y.J.; Noh, T.W.; Jung, R.; Lee, J.-C. Role of oxygen vacancy in HfO2/SiO2/Si(100) interfaces. Appl. Phys. Lett. 2006, 88, 193502. [Google Scholar] [CrossRef]
  40. Rushchanskii, K.Z.; Blügel, S.; Ležaić, M. Ordering of oxygen vacancies and related ferroelectric Properties in HfO2-δ. Phys. Rev. Lett. 2021, 127, 087602. [Google Scholar] [CrossRef]
  41. Basahel, S.N.; Ali, T.T.; Mokhtar, M.; Narasimharao, K. Influence of crystal structure of nanosized ZrO2 on photocatalytic degradation of methyl orange. Nanoscale Res. Lett. 2015, 10, 73. [Google Scholar] [CrossRef] [Green Version]
  42. Park, M.H.; Lee, Y.H.; Kim, H.J.; Moon, T.; Kim, K.D.; Müller, J.; Kersch, A.; Schroeder, U.; Mikolajick, T.; Hwang, C.S. Ferroelectricity and antiferroelectricity of doped thin HfO2-based films. Adv. Mater. 2015, 27, 1811–1831. [Google Scholar] [CrossRef]
Materials 16 05559 g001
Figure 1. Schematic of Zr-doped hafnium magnetron sputtering cathode.
Figure 1. Schematic of Zr-doped hafnium magnetron sputtering cathode.
Materials 16 05559 g001
Materials 16 05559 g002
Figure 2. Fabrication flow of TiN/HZO/TiN/Si capacitor structure and photograph (see above right) of capacitor. The capacitor is fabricated through the deposition of Zr:HfO2 on a P-type silicon substrate by RF magnetron sputtering (top and bottom electrodes are TiN thin films deposited by DC magnetron sputtering), followed by annealing in a nitrogen atmosphere.
Figure 2. Fabrication flow of TiN/HZO/TiN/Si capacitor structure and photograph (see above right) of capacitor. The capacitor is fabricated through the deposition of Zr:HfO2 on a P-type silicon substrate by RF magnetron sputtering (top and bottom electrodes are TiN thin films deposited by DC magnetron sputtering), followed by annealing in a nitrogen atmosphere.
Materials 16 05559 g002
Materials 16 05559 g003
Figure 3. Sheet resistance (measured) and electrical resistivity (calculated) of TiN thin films deposited using magnetron sputtering at various substrate temperatures.
Figure 3. Sheet resistance (measured) and electrical resistivity (calculated) of TiN thin films deposited using magnetron sputtering at various substrate temperatures.
Materials 16 05559 g003
Materials 16 05559 g004
Figure 4. XRD patterns of TiN thin films deposited using magnetron sputtering at various substrate temperatures.
Figure 4. XRD patterns of TiN thin films deposited using magnetron sputtering at various substrate temperatures.
Materials 16 05559 g004
Materials 16 05559 g005
Figure 5. Graph of deposition rate of Zr-doped HfO2 thin films as function of oxygen flow rate ranging from 10 to 50 sccm. The thickness of Zr-doped HfO2 films prepared at an oxygen flow of 40 sccm was measured with a white-light interferometer (see the inset).
Figure 5. Graph of deposition rate of Zr-doped HfO2 thin films as function of oxygen flow rate ranging from 10 to 50 sccm. The thickness of Zr-doped HfO2 films prepared at an oxygen flow of 40 sccm was measured with a white-light interferometer (see the inset).
Materials 16 05559 g005
Materials 16 05559 g006
Figure 6. XPS O1s fine spectra of Zr-doped HfO2 thin films deposited at various oxygen flow rates.
Figure 6. XPS O1s fine spectra of Zr-doped HfO2 thin films deposited at various oxygen flow rates.
Materials 16 05559 g006
Materials 16 05559 g007
Figure 7. XPS fine spectra of Hf-4f (a) and Zr-3d (b) of Zr-doped HfO2 thin films deposited at varying oxygen flow rates.
Figure 7. XPS fine spectra of Hf-4f (a) and Zr-3d (b) of Zr-doped HfO2 thin films deposited at varying oxygen flow rates.
Materials 16 05559 g007
Materials 16 05559 g008
Figure 8. EDS spectra and AFM of Zr-doped HfO2 thin films deposited at an oxygen flow of 40 sccm. (a) Oxygen element, (b) hafnium element, (c) zirconium element (d) AFM.
Figure 8. EDS spectra and AFM of Zr-doped HfO2 thin films deposited at an oxygen flow of 40 sccm. (a) Oxygen element, (b) hafnium element, (c) zirconium element (d) AFM.
Materials 16 05559 g008
Materials 16 05559 g009
Figure 9. I–V curves of Zr-doped HfO2 thin films deposited at different oxygen flow rates.
Figure 9. I–V curves of Zr-doped HfO2 thin films deposited at different oxygen flow rates.
Materials 16 05559 g009
Materials 16 05559 g010
Figure 10. P–E curves of Zr-doped HfO2 thin films deposited at various oxygen flow rates.
Figure 10. P–E curves of Zr-doped HfO2 thin films deposited at various oxygen flow rates.
Materials 16 05559 g010
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Xi, Y.; Liu, L.; Zhao, J.; Qin, X.; Zhang, J.; Zhang, C.; Liu, W. Effects of Oxygen Flow during Fabrication by Magnetron Sputtering on Structure and Performance of Zr-Doped HfO2 Thin Films. Materials 2023, 16, 5559. https://doi.org/10.3390/ma16165559

AMA Style

Xi Y, Liu L, Zhao J, Qin X, Zhang J, Zhang C, Liu W. Effects of Oxygen Flow during Fabrication by Magnetron Sputtering on Structure and Performance of Zr-Doped HfO2 Thin Films. Materials. 2023; 16(16):5559. https://doi.org/10.3390/ma16165559

Chicago/Turabian Style

Xi, Yingxue, Lei Liu, Jiwu Zhao, Xinhui Qin, Jin Zhang, Changming Zhang, and Weiguo Liu. 2023. "Effects of Oxygen Flow during Fabrication by Magnetron Sputtering on Structure and Performance of Zr-Doped HfO2 Thin Films" Materials 16, no. 16: 5559. https://doi.org/10.3390/ma16165559

APA Style

Xi, Y., Liu, L., Zhao, J., Qin, X., Zhang, J., Zhang, C., & Liu, W. (2023). Effects of Oxygen Flow during Fabrication by Magnetron Sputtering on Structure and Performance of Zr-Doped HfO2 Thin Films. Materials, 16(16), 5559. https://doi.org/10.3390/ma16165559

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.