Next Article in Journal
Formation of Twin Boundaries in Rapidly Solidified Metals through Deformation Twinning
Next Article in Special Issue
Acceleration of Near-IR Emission through Efficient Surface Passivation in Cd3P2 Quantum Dots
Previous Article in Journal
Synthesis of Mesoporous and Hollow SiO2@ Eu(TTA)3phen with Enhanced Fluorescence Properties
Previous Article in Special Issue
Upconversion Emission Studies in Er3+/Yb3+ Doped/Co-Doped NaGdF4 Phosphor Particles for Intense Cathodoluminescence and Wide Temperature-Sensing Applications
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Scintillation Properties of Ba3RE(PO4)3 Single Crystals (RE = Y, La, Lu)

1
Division of Materials Science, Nara Institute of Science and Technology (NAIST), Nara 630-0192, Japan
2
Research Institute of Electronics, Shizuoka University, Shizuoka 432-8011, Japan
*
Author to whom correspondence should be addressed.
Materials 2023, 16(13), 4502; https://doi.org/10.3390/ma16134502
Submission received: 19 May 2023 / Revised: 13 June 2023 / Accepted: 20 June 2023 / Published: 21 June 2023
(This article belongs to the Special Issue Advances in Luminescent Materials)

Abstract

:
Eulytite-type Ba3RE(PO4)3 (RE = Y, La, and Lu) single crystals were synthesized by the floating zone method, and their scintillation properties were investigated. The powder X-ray diffraction measurement revealed that the single phase of Ba3RE(PO4)3 samples were successfully synthesized. The samples exhibited a luminescence peak due to self-trapped exciton at around 400 nm under vacuum ultraviolet and X-ray irradiation. The X-ray-induced scintillation decay time constants of the samples were several microseconds at room temperature. In the 241Am α-ray irradiated pulse height spectra, all the samples showed a clear full energy peak, and the absolute light yields of the Ba3Y(PO4)3, Ba3La(PO4)3, and Ba3Lu(PO4)3 single crystals were estimated to be 960, 1160, and 1220 ph/5.5 MeV-α, with a typical error of ±10%, respectively. The scintillation light yields of the Ba3RE(PO4)3 have been quantitatively clarified for the first time.

1. Introduction

Scintillators have a function to convert high-energy ionizing radiation to low-energy photons and are applied in many fields such as medical [1], security [2], well logging [3], and high energy physics [4]. When the scintillator absorbs ionizing radiation, an energetic primary electron is generated from an inner shell. Then, a lot of secondary electrons are produced by Coulomb scattering. The scintillation photons are emitted by electrons recombining at luminescence center. Scintillators are utilized as scintillation detectors by combining with photodetectors. Generally, a scintillator requires several properties, including high scintillation light yield (LY); high energy resolution; low afterglow level (Af); suitable emission wavelength, which coincides with the spectral sensitivity of the photodetector (e.g., PMT: photomultiplier tube); short decay time; and no deliquescence. Up to now, many researchers have studied novel scintillators [5,6,7,8,9,10,11]. However, there are no scintillators that have all the above requirements, and the development of new scintillators has been still ongoing.
Ba3RE(PO4)3 (BREPO, RE = rare earth) has attracted extensive attention as a luminescent material [12,13,14,15,16,17]. BREPO has high chemical stability, a large band gap, and the ability to accept trivalent lanthanide activators without charge compensation [18,19]. As BREPO belongs to eulytite compounds as well as Bi4Ge3O12 (BGO), which is one of the most popular scintillators [20,21,22,23,24], this material is expected to be a good scintillator. Actually, Shi et al. reported that Ce-doped Ba3La(PO4)3 (BLaPO) powder showed a luminescence intensity of 34% of BGO under X-ray irradiation [25]; as far as we know, this is the only study of the scintillation properties of BREPO. However, the intensity was acquired from a qualitative measurement. Thus, there is room for further investigation of the scintillation properties of BREPO. In addition, as ionizing radiation has higher penetrating power than ultraviolet-visible photons, single crystalline materials having higher transparencies than ceramics or powders are preferable in the scintillator field. However, the investigation of BREPO single crystals were limited in any field thus far [17,26]. If the scintillator had a low transparency at a luminescence wavelength, the number of scintillation photons reaching the photodetector decreases depending on the distance between the emitting point and the photodetector. As a result, the LY and the energy resolution of the scintillator are reduced.
In this study, we synthesized Ba3Y(PO4)3 (BYPO), BLaPO, and Ba3Lu(PO4)3 (BLuPO) single crystals. The photoluminescence (PL) and scintillation properties of them were investigated with a quantitative measurement of the scintillation LYs as the main purpose. Today, doping of impurity ions to the host material is a common method to develop the novel phosphors, and some researchers neglect the investigation of the properties of the host material itself. However, understanding the properties of the host material is inherently important. For example, the interaction probability between the radiation, materials, and energy migration efficiency basically depends on the host material. Actually, BREPO can accept rare earths other than Y, La, and Lu as well. However, other rare earths act as luminescence centers themselves, and the properties of the materials are often strongly affected by the rare earths. Therefore, we focused on undoped materials containing Y, La, and Lu that had no function as luminescence centers as a start.

2. Materials and Methods

The BREPO single crystalline samples were grown by the floating zone (FZ) method. The Y2O3 (4 N, Furuuchi Chemical, Tokyo Japan), La2O3 (4 N, Rare Metallic, Tokyo Japan), Lu2O3 (5 N, Noppon Yttrium, Tokyo Japan), BaCO3 (4 N, Rare Metallic), and H6NO4P (4 N, Sigma Aldrich, St. Louis, MO, USA) powders were used as raw materials. The 10% excess of H6NO4P was added from stoichiometric ratio to compensate for P evaporation during the crystal growth. The powders were mixed homogeneously by an agate mortar and an agate pestle. The powders were calcined by an electric furnace at 1100 °C, 8 h in air after mixing. Then, the powders were filled into a balloon and hardened by hydrostatic pressure to form into a cylindrical rod. The rods were sintered by an electric furnace at 1200 °C, 8 h in air. The sintering rods were used for the crystal growth by an FZ furnace (Crystal Systems Corporation, FZ-T-12000-X-VPO-PC-YH, Salem, MA, USA). The pulling down and rotation speeds during the crystal growth were 10 mm/h and 10 rpm, respectively. After the crystal growth, a part of the synthesized crystalline rod was cut and mechanically polished by a polishing machine (Byehler, MetaServ 250, Lake Bluff, IL, USA) for measurements, and the remaining parts were crushed into powder for the powder X-ray diffraction (XRD) measurement. A diffractometer (Rigaku, MiniFlex600, Tokyo Japan) with a bias voltage of 40 kV and a tube current of 15 mA was used to measure the powder XRD patterns. The measurement range was from 10 to 80° in 0.02° steps.
A spectrometer (Shimadzu, SolidSpec-3700, Kyoto, Japan) was used for the diffuse transmission spectra measurement. The measurement range was from 200 to 850 nm in 0.5 nm steps. The photoluminescence (PL) excitation and emission spectra were investigated under vacuum ultraviolet (VUV) irradiation by BL-7B beamline in the Ultra Violet Synchrotron Orbital Radiation (UVSOR) synchrotron facility at the Institute of Molecular Science (IMS), Japan. The synchrotron radiation was monochromatized using a 3 m normal-incidence monochromator. The tested wavelength ranges were from 50 to 200 nm in 2 nm steps for the excitation spectra and from 200 to 700 nm in 0.4 nm steps for the emission spectra.
The X-ray-induced scintillation spectra were acquired by our original setup. The sample was attached to the tip of an optical fiber and covered with a Teflon tape, and the sample was irradiated with X-rays. An X-ray generator (Spellman, XRB80N100/CB, Hauppauge, NY, USA) with a tungsten anode target and a beryllium window was used as a radiation source. The bias voltage and the tube current were set to 40 kV and 1.2 mA, respectively. The emitted photons were guided to a spectrometer (Andor, DU-420-BU2 CCD with Shamrock SR 163 monochromator, Belfast England) through the optical fiber. To avoid thermal noise, the CCD was cooled to 188 K by a Peltier module. The X-ray-induced scintillation decay time profiles and the afterglow profiles were studied by an afterglow characterization system. The pulsed LD (for the decay time profiles) or LED (for the afterglow profiles) light sources were the excitation roots. The pulsed width and the repetition frequency were tuned by a digital delay generator (Stanford Research Systems, DG645, Sunnyvale, CA, USA). Visible photons from the LD or LED hit a multi-alkali photocathode (S-20, Sb-Na-K-Cs) of the X-ray tube (Hamamatsu, N5084, Shizuoka, Japan) to convert to electrons. The high voltage bias of 30 kV, supplied by Matsusada HAR-40P0.75 (Shiga Japan), accelerated and led the photoelectrons to a tungsten target to generate bremsstrahlung X-rays. The X-rays were irradiated to the samples through a beryllium window. Emitted photons from the samples were detected by PMT (Hamamatsu, R7400P-06). Once scintillation photons were detected by the PMT, the signal was fed into the photon-counting unit (Hamamatsu, C5594) and then to a PCI-type counting board (Hamamatsu, TSCPC) in a personal computer. The trigger signal was also generated by DG645 and fed into TSCPC. In the case of the afterglow profiles measurement, C5594 and TSCPC were replaced to C9744 and M9003-01, respectively. In order to obtain the scintillation decay time constants, the least-square fitting with two exponential decay functions was utilized. The pulse height spectra with 241Am α-ray exposure were measured by below setup. The sample was mounted on the window of the PMT (Hamamatsu, R7600-200) with a silicon grease (OKEN, 6262A, Tokyo Japan) and covered by several layers of Teflon tape to guide emitted photons to the photocathode of the PMT. The scintillation light signal was converted to an electrical signal, and the signal was processed by a pre-amplifier (ORTEC, 113, Oak Ridge, TN, USA), shaping amplifier (ORTEC, 570), and a multichannel analyzer (Amptek, Pocket MCA 8000A, Bedford, MA, USA). To obtain the absolute scintillation LYs, a commercial BGO scintillator under 137Cs γ-ray irradiation (8000 ph/MeV) was used as a reference. The shaping times were set to 10 and 2 μs for the synthesized BREPO samples and the BGO reference, respectively.

3. Results and Discussion

Figure 1 shows the photo of the synthesized BREPO samples after cutting and polishing. The size of samples was about 8 mm long × 3 mm wide × 1 mm thick. The colorless transparent crystalline samples were obtained although a part of the samples was opaque and cracked.
Figure 2a shows the XRD patterns of the BREPO samples and a reference pattern of BLaPO (ICDD 85-2448), and Figure 2b indicates the expansion around 27°. All the samples showed identical peak pattern of BREPO without impurity phase. The results indicated the samples shown in Figure 1 were single phase of BREPO. From Figure 2b, the peak shift due to the differences of RE3+ site was observed. The BREPO compounds belonged to a cubic crystal structure with space group of I 4 ¯ 3d. The unit cells were composed of an isolated PO4 tetrahedron and an edge-shared RE/Ba octahedron. The diagrams of the lattice structure of BREPO were reported by previous studies [26,27]. The ionic radii of the Y3+, La3+, and Lu3+ ions were 0.900, 1.390, and 0.861 Å, respectively [28]; therefore, the peak shift was consistent with the difference in the ionic radii.
Figure 3 shows the diffuse transmission spectra of the BREPO samples. All the samples indicated high transmittance, around 80%, in the visible region. The BLaPO sample showed slightly lower transparency than BYPO and BLuPO samples; it was due to the cracks in the sample. The transmittance gradually decreased from 350 nm; however, the absorption edges of the samples were beyond the measurement limit of the apparatus (200 nm). Therefore, the optical band gaps of the BREPO samples were confirmed to be above 6.2 eV.
Figure 4 shows the VUV-irradiated PL (a) excitation and (b) emission spectra of the BREPO samples. The samples showed an excitation peak at 180 nm with a shoulder peak around 150 nm when the monitoring wavelength was set to 400 nm. Similar peaks have been observed in some orthophosphate materials, and the origin of the excitation peak was attributed to the absorption due to PO43− [25,29,30,31]. Under excitation at 180 nm, all the samples showed a broad emission peak around 400 nm. The features of the emission such as emission wavelength, large stokes shift, and broad band width were matched the features of self-trapped exciton (STE) [32], and some phosphates also exhibited luminescence due to excitons at similar wavelengths [33,34,35]. Therefore, the luminescence origin of the BREPO samples was considered to be due to STE.
Figure 5 shows the X-ray-induced scintillation spectra of the BREPO samples. All the samples exhibited a broad emission band around 400 nm. The emission wavelength and the spectral shape coincided with the luminescence observed in PL emission spectra under VUV irradiation. Therefore, the luminescence origin was ascribed to STE. The luminescence wavelength around 400 nm was suitable for detection by using the typical photodetectors.
Figure 6 shows the X-ray-induced scintillation decay time profiles of the BREPO samples. Note that the measurement was taken at room temperature. The decay curves of the samples were expressed by the sum of two exponential decay functions. The fast and slow decay time constants were several hundreds of milliseconds and several microseconds, respectively. The fast decay time constant was due to the instrumental response’s function. The slow decay time constant was consistent with that of STE, which was previously reported in some materials at room temperature [36,37]. This result supported that the luminescence observed in Figure 5 was due to STE. However, the accurate measurement of the scintillation decay time profiles was difficult because of low luminescence intensities and high Af values (described later) of the samples. Therefore, the discussion about relation or influence of the difference of RE site on scintillation decay time constants was difficult in this time.
Figure 7 shows the afterglow profiles of the BREPO samples. The obtained Afs were summarized in Table 1. The Af was calculated following formula,
Af (%) = 100 × (I2IBG)/(I1IBG).
Here, IBG, I1, and I2 are the background signal intensity, the signal intensity during X-ray irradiation, and the signal intensity obtained 20 ms after the irradiation was cut off, respectively. The obtained Afs were 1.01, 1.06, and 1.20% for the BYPO, BLaPO, and BLuPO samples, respectively. These Afs were quite higher than those of the oxide-based eulytite compounds BGO (10.1 ppm) and Bi4Si3O12 (192.3 ppm) measured by same setup [38,39].
Figure 8 shows the 241Am α-ray-irradiated pulse height spectra of the BREPO samples. The obtained LYs were summarized in Table 1, as with the Afs. All the samples exhibited full energy peaks. The absolute LYs of the BYPO, BLaPO, and BLuPO samples were estimated to be 960, 1160, and 1220 ph/5.5 MeV-α, with a typical error of ±10%. The LYs of the samples were lower than those of the BGO scintillator. One of the reasons for the low LYs was due to the high Afs. Afterglow is a type of storage-type luminescence caused by electron captures at some defect centers and re-excitations by weak thermal energy derived from room temperature. A high Af means a large number of electrons captured at defect centers; in other words, the energy migration efficiency in the scintillation process is low [40]. As the synthesized BREPO samples had opaque and cracked parts, the amounts of defect centers were considered to be high. Improving crystal quality and reducing defects are required for lower Afs and higher LYs. In addition, the scintillation decay time constants of several microseconds for the BREPO samples were too long for the pulse height measurement, with a shaping time of 10 μs. This discrepancy led to the underestimation of the LYs. Therefore, doping some impurity ions such as the Ce3+ ion is interesting to achieve faster decay time constants and higher LYs. On the other hand, there was a correlation between Afs and LYs among the BREPO samples. LY depends on not only energy migration efficiency but also quantum efficiency at luminescence centers [41]. Hence, this result implies that the sample containing heavier element possibly had a higher quantum yield of STE. The investigation of quantum yield under VUV excitation is an intriguing topic to further elucidate the scintillation mechanism.

4. Conclusions

Eulytite-type BREPO (RE = Y, La, and Lu) single crystals were synthesized by the FZ method, and their optical and scintillation properties were evaluated. The XRD measurement revealed that the synthesized samples were in a single phase of BREPO, although the samples included opaque and cracked parts. All the samples had high transmittances, approximately 80% in the visible region. Under VUV irradiation, the samples showed excitation peaks at 180 nm, with a shoulder peak around 150 nm and an emission peak around 400 nm. The excitation peak was ascribed to the host-related absorption specific to the orthophosphate materials, and the origins of the emission peaks were considered to be due to STE. The luminescence due to STE was also observed in the X-ray-induced scintillation spectra. The luminescence wavelength at around 400 nm was advantageous from the viewpoint of compatibility with the spectral sensitivity of the general photodetectors. The X-ray-induced scintillation decay time constants of the BREPO samples were several microseconds at room temperature. In the pulse height spectra under 241Am α-ray irradiation, the LYs of the BYPO, BLaPO, and BLuPO samples were estimated to be 960, 1160, and 1220 ph/5.5 MeV-α, with a typical error of ±10%, respectively. The absolute LY of BREPO was quantitatively revealed for the first time, although the LYs were lower than those of BGO, which also belongs to the eulytite compounds. For further improvement, crystals with fewer amounts of defects are desirable. In addition, the doping of some activators, such as Ce3+ ions, is interesting to enhance the LYs.

Author Contributions

Y.T.: Conceptualization, Investigation, Writing—original draft preparation. M.K.: Investigation, Supervision, Validation. K.I.: Investigation. T.K.: Supervision, Validation. D.N.: Supervision, Validation. N.K.: Supervision, Validation. T.Y.: Supervision, Validation. All authors have read and agreed to the published version of the manuscript.

Funding

This work was supported by Grants-in-Aid for Scientific A (22H00309), Grants-in-Aid for Scientific B (22H03872, 22H02939, 21H03733, and 21H03736), and Challenging Exploratory Research (22K18997) from Japan Society for the Promotion of Science.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Data will be made available on request.

Acknowledgments

This work was supported by the Cooperative Research Project of Research Center for Biomedical Engineering, A-STEP (JPMJTM22DM) from JST, Konica Minolta Science and Technology Foundation, Nakatani Foundation, and Kazuchika Okura Memorial Foundation.

Conflicts of Interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper’s conceptualization, investigation, or writing—original draft preparation.

References

  1. van Eijk, C.W.E. Inorganic Scintillators in Medical Imaging Detectors. Nucl. Instrum. Methods Phys. Res. Sect. A 2003, 509, 17–25. [Google Scholar] [CrossRef]
  2. Glodo, J.; Wang, Y.; Shawgo, R.; Brecher, C.; Hawrami, R.H.; Tower, J.; Shah, K.S. New Developments in Scintillators for Security Applications. Phys. Procedia 2017, 90, 285–290. [Google Scholar] [CrossRef]
  3. Melcher, C.L.; Schweitzer, J.S.; Manente, R.A.; Peterson, C.A. Applications of Single Crystals in Oil Well Logging. J. Cryst. Growth 1991, 109, 37–42. [Google Scholar] [CrossRef]
  4. Mao, R.; Zhang, L.; Zhu, R.-Y. Optical and Scintillation Properties of Inorganic Scintillators in High Energy Physics. IEEE Trans. Nucl. Sci. 2008, 55, 2425–2431. [Google Scholar] [CrossRef] [Green Version]
  5. Eijk, C.W.E. van Inorganic Scintillators in Medical Imaging. Phys. Med. Biol. 2002, 47, R85–R106. [Google Scholar] [CrossRef]
  6. Birowosuto, M.D.; Dorenbos, P. Novel γ- and X-Ray Scintillator Research: On the Emission Wavelength, Light Yield and Time Response of Ce3+ Doped Halide Scintillators. Phys. Status Solidi 2009, 206, 9–20. [Google Scholar] [CrossRef]
  7. Melcher, C.L.; Schweitzer, J.S. Cerium-Doped Lutetium Oxyorthosilicate: A Fast, Efficient New Scintillator. IEEE Trans. Nucl. Sci. 1992, 39, 502–505. [Google Scholar] [CrossRef]
  8. Takebuchi, Y.; Shiratori, D.; Kato, T.; Nakauchi, D.; Kawaguchi, N.; Yanagida, T. Synthesis of Lu2O3-Ga2O3-SiO2 Glass as a New Glass Scintillator. Sens. Mater. 2023, 35, 507. [Google Scholar] [CrossRef]
  9. Koshimizu, M.; Fujimoto, Y.; Asai, K. Development of Ce-Doped Gd3Al5−yGayO12 Nanoparticle Scintillators. Sens. Mater. 2023, 35, 521. [Google Scholar] [CrossRef]
  10. Nakamori, R.; Kawano, N.; Takaku, A.; Onoda, D.; Takebuchi, Y.; Fukushima, H.; Kato, T.; Shinozaki, K.; Yanagida, T. Radiation Response Characteristics of Pr3+-Activated SrO-Al2O3-TeO2 Glasses. Sens. Mater. 2022, 34, 707. [Google Scholar] [CrossRef]
  11. Matsumoto, S.; Watanabe, T.; Ito, A. Photo- and Radioluminescence Properties of Eu3+-Doped Y2O3 Thick Film Phosphor Prepared via Chemical Vapor Deposition. Sens. Mater. 2022, 34, 669. [Google Scholar] [CrossRef]
  12. Yu, R.; Noh, H.M.; Moon, B.K.; Choi, B.C.; Jeong, J.H.; Jang, K.; Yi, S.S.; Jang, J.K. Synthesis and Luminescence Properties of a Novel Red-Emitting Phosphor Ba3La(PO4)3:Eu3+ for Solid-State Lighting. J. Alloys Compd. 2013, 576, 236–241. [Google Scholar] [CrossRef]
  13. Liu, Q.; Liu, Y.; Ding, Y.; Peng, Z.; Tian, X.; Yu, Q.; Dong, G. A White Light Emitting Luminescent Material Ba3Y(PO4)3:Dy3+. Ceram. Int. 2014, 40, 10125–10129. [Google Scholar] [CrossRef]
  14. Ivanovskikh, K.; Meijerink, A.; Ronda, C.; Piccinelli, F.; Speghini, A.; Bettinelli, M. Fast UV Luminescence in Pr3+-Doped Eulytite Double Phosphates. Opt. Mater. 2011, 34, 419–423. [Google Scholar] [CrossRef] [Green Version]
  15. Yu, R.; Mi Noh, H.; Kee Moon, B.; Chun Choi, B.; Hyun Jeong, J.; Sueb Lee, H.; Jang, K.; Soo Yi, S. Photoluminescence Characteristics of Sm3+ Doped Ba3La(PO4)3 as New Orange-Red Emitting Phosphors. J. Lumin. 2014, 145, 717–722. [Google Scholar] [CrossRef]
  16. Li, T.; Li, P.; Wang, Z.; Xu, S.; Bai, Q.; Yang, Z. Substituting Different Cations in Tuning of the Photoluminescence in Ba3Ce(PO4)3. Inorg. Chem. 2016, 55, 8758–8769. [Google Scholar] [CrossRef]
  17. Chen, H.; Loiseau, P.; Aka, G.; Kränkel, C. Optical Spectroscopic Investigation of Ba3Tb(PO4)3 Single Crystals for Visible Laser Applications. J. Alloys Compd. 2018, 740, 1133–1139. [Google Scholar] [CrossRef]
  18. Blasse, G. New Compounds with Eulytine Structure: Crystal Chemistry and Luminescence. J. Solid State Chem. 1970, 2, 27–30. [Google Scholar] [CrossRef]
  19. Barbier, J. Structural Refinements of Eulytite-Type Ca3Bi(PO4)3 and Ba3La(PO4)3. J. Solid State Chem. 1992, 101, 249–256. [Google Scholar] [CrossRef]
  20. Holl, I.; Lorenz, E.; Mageras, G. A Measurement of the Light Yield of Common Inorganic Scintillators. IEEE Trans. Nucl. Sci. 1988, 35, 105–109. [Google Scholar] [CrossRef]
  21. Mares, J.A.; Beitlerova, A.; Nikl, M.; Solovieva, N.; D’Ambrosio, C.; Blazek, K.; Maly, P.; Nejezchleb, K.; de Notaristefani, F. Scintillation Response of Ce-Doped or Intrinsic Scintillating Crystals in the Range up to 1MeV. Radiat. Meas. 2004, 38, 353–357. [Google Scholar] [CrossRef]
  22. Moszynski, M.; Kapusta, M.; Mayhugh, M.; Wolski, D.; Flyckt, S.O. Absolute Light Output of Scintillators. IEEE Trans. Nucl. Sci. 1997, 44, 1052–1061. [Google Scholar] [CrossRef] [Green Version]
  23. Weber, M.; Derenzo, S.; Moses, W. Measurements of Ultrafast Scintillation Rise Times: Evidence of Energy Transfer Mechanisms. J. Lumin. 2000, 87–89, 830–832. [Google Scholar] [CrossRef]
  24. Rogemond, F.; Pedrini, C.; Moine, B.; Boulon, G. Fluorescence Properties of Bi4Ge3O12(BGO) Single Crystals under Laser Excitation: Excited State Dynamics and Saturation Effects. J. Lumin. 1985, 33, 455–486. [Google Scholar] [CrossRef]
  25. Shi, Q.; Huang, Y.; Ivanovskikh, K.V.; Pustovarov, V.A.; Wang, L.; Cui, C.; Huang, P. Luminescence Properties and Host Sensitization Study of Ba3La(PO4)3:Ce3+ with (V)UV and X-Ray Excitation. J. Alloys Compd. 2020, 817, 152704. [Google Scholar] [CrossRef]
  26. Wu, G.; Fan, M.; Jiang, C.; Chen, F.; Yu, F.; Cheng, X.; Zhao, X. Noncentrosymmetric Orthophosphate YM3(PO4)3 (M = Sr, Ba) Crystals: Single Crystal Growth, Structure, and Properties. Cryst. Growth Des. 2020, 20, 2390–2397. [Google Scholar] [CrossRef]
  27. Sharova, N.; Fjellvåg, H.; Norby, T. Structure, Defect Chemistry, and Proton Conductivity in Nominally Sr-Doped Ba3La(PO4)3. Solid State Ion. 2009, 180, 338–342. [Google Scholar] [CrossRef]
  28. Shannon, R.D. Revised Effective Ionic Radii and Systematic Studies of Interatomic Distances in Halides and Chalcogenides. Acta Crystallogr. Sect. A 1976, 32, 751–767. [Google Scholar] [CrossRef]
  29. Dorenbos, P.; Pierron, L.; Dinca, L.; van Eijk, C.W.E.; Kahn-Harari, A.; Viana, B. 4f-5d Spectroscopy of Ce3+ in CaBPO5, LiCaPO4 and Li2CaSiO4. J. Phys. Condens. Matter 2003, 15, 511–520. [Google Scholar] [CrossRef]
  30. Di, W.; Wang, X.; Chen, B.; Lai, H.; Zhao, X. Preparation, Characterization and VUV Luminescence Property of YPO4:Tb Phosphor for a PDP. Opt. Mater. 2005, 27, 1386–1390. [Google Scholar] [CrossRef]
  31. Yuan, J.-L.; Zhang, H.; Zhao, J.-T.; Chen, H.-H.; Yang, X.-X.; Zhang, G.-B. Synthesis, Structure and Luminescent Properties of Lu(PO3)3. Opt. Mater. 2008, 30, 1369–1374. [Google Scholar] [CrossRef]
  32. Williams, R.T.; Song, K.S. The Self-Trapped Exciton. J. Phys. Chem. Solids 1990, 51, 679–716. [Google Scholar] [CrossRef]
  33. Takebuchi, Y.; Koshimizu, M.; Shiratori, D.; Kato, T.; Nakauchi, D.; Kawaguchi, N.; Yanagida, T. Evaluation of Radiation-Induced Luminescence Properties of Tb-Doped LiCaPO4. Radiat. Phys. Chem. 2022, 197, 110180. [Google Scholar] [CrossRef]
  34. Lecointre, A.; Bessière, A.; Viana, B.; Aït Benhamou, R.; Gourier, D. Thermally Stimulated Luminescence of Ca3(PO4)2 and Ca9Ln(PO4)7 (Ln = Pr, Eu, Tb, Dy, Ho, Er, Lu). Radiat. Meas. 2010, 45, 273–276. [Google Scholar] [CrossRef]
  35. Makhov, V.; Kirikova, N.Y.; Kirm, M.; Krupa, J.; Liblik, P.; Lushchik, A.; Lushchik, C.; Negodin, E.; Zimmerer, G. Luminescence Properties of YPO4:Nd3+: A Promising VUV Scintillator Material. Nucl. Instrum. Methods Phys. Res. Sect. A 2002, 486, 437–442. [Google Scholar] [CrossRef]
  36. Zhang, J.; Liang, H.; Su, Q. Luminescence of Ce3+-Doped Sr10(PO4)6S Phosphors. J. Phys. D Appl. Phys. 2009, 42, 105110. [Google Scholar] [CrossRef]
  37. van Loef, E.V.D.; Dorenbos, P.; van Eijk, C.W.E. The Scintillation Mechanism in LaCl3:Ce3+. J. Phys. Condens. Matter 2003, 15, 1367–1375. [Google Scholar] [CrossRef]
  38. Nakauchi, D.; Kato, T.; Kawaguchi, N.; Yanagida, T. Characterization of Eu-Doped Ba2SiO4, a High Light Yield Scintillator. Appl. Phys. Express 2020, 13, 122001. [Google Scholar] [CrossRef]
  39. Ichiba, K.; Okazaki, K.; Takebuchi, Y.; Kato, T.; Nakauchi, D.; Kawaguchi, N.; Yanagida, T. X-Ray-Induced Scintillation Properties of Nd-Doped Bi4Si3O12 Crystals in Visible and Near-Infrared Regions. Materials 2022, 15, 8784. [Google Scholar] [CrossRef]
  40. Yanagida, T. Inorganic Scintillating Materials and Scintillation Detectors. Proc. Jpn. Acad. Ser. B 2018, 94, 75–97. [Google Scholar] [CrossRef] [Green Version]
  41. Robbins, D.J. On Predicting the Maximum Efficiency of Phosphor Systems Excited by Ionizing Radiation. J. Electrochem. Soc. 1980, 127, 2694–2702. [Google Scholar] [CrossRef]
Figure 1. Photo of synthesized BREPO samples after polishing.
Figure 1. Photo of synthesized BREPO samples after polishing.
Materials 16 04502 g001
Figure 2. (a) XRD patterns of BREPO samples and reference pattern of BLaPO. (b) indicates the expansion around 27°.
Figure 2. (a) XRD patterns of BREPO samples and reference pattern of BLaPO. (b) indicates the expansion around 27°.
Materials 16 04502 g002
Figure 3. Diffuse transmission spectra of BREPO samples.
Figure 3. Diffuse transmission spectra of BREPO samples.
Materials 16 04502 g003
Figure 4. VUV irradiated PL (a) excitation and (b) emission spectra of BREPO samples.
Figure 4. VUV irradiated PL (a) excitation and (b) emission spectra of BREPO samples.
Materials 16 04502 g004
Figure 5. X-ray-induced scintillation spectra of BREPO samples.
Figure 5. X-ray-induced scintillation spectra of BREPO samples.
Materials 16 04502 g005
Figure 6. X-ray-induced scintillation decay curves of BREPO samples.
Figure 6. X-ray-induced scintillation decay curves of BREPO samples.
Materials 16 04502 g006
Figure 7. Afterglow profiles of BREPO samples.
Figure 7. Afterglow profiles of BREPO samples.
Materials 16 04502 g007
Figure 8. 241Am α-ray-irradiated pulse height spectra of BREPO samples.
Figure 8. 241Am α-ray-irradiated pulse height spectra of BREPO samples.
Materials 16 04502 g008
Table 1. Afs and LYs of BREPO samples.
Table 1. Afs and LYs of BREPO samples.
SampleAf (%)LY (ph/5.5 MeV-𝛼)
BYPO1.01960
BLaPO1.061160
BLuPO1.201220
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

Takebuchi, Y.; Koshimizu, M.; Ichiba, K.; Kato, T.; Nakauchi, D.; Kawaguchi, N.; Yanagida, T. Scintillation Properties of Ba3RE(PO4)3 Single Crystals (RE = Y, La, Lu). Materials 2023, 16, 4502. https://doi.org/10.3390/ma16134502

AMA Style

Takebuchi Y, Koshimizu M, Ichiba K, Kato T, Nakauchi D, Kawaguchi N, Yanagida T. Scintillation Properties of Ba3RE(PO4)3 Single Crystals (RE = Y, La, Lu). Materials. 2023; 16(13):4502. https://doi.org/10.3390/ma16134502

Chicago/Turabian Style

Takebuchi, Yuma, Masanori Koshimizu, Kensei Ichiba, Takumi Kato, Daisuke Nakauchi, Noriaki Kawaguchi, and Takayuki Yanagida. 2023. "Scintillation Properties of Ba3RE(PO4)3 Single Crystals (RE = Y, La, Lu)" Materials 16, no. 13: 4502. https://doi.org/10.3390/ma16134502

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop