Next Article in Journal
Feasibility of a Three-Dimensional Porous Uncalcined and Unsintered Hydroxyapatite/poly-d/l-lactide Composite as a Regenerative Biomaterial in Maxillofacial Surgery
Previous Article in Journal
Ultra-Wideband and Wide-Angle Microwave Metamaterial Absorber
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 11
Issue 10
10.3390/ma11102046
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Microstructure and Mechanical Properties of ZrB2–HfC Ceramics Influenced by HfC Addition

by
Yi Jing
1,2,*,
Hongbing Yuan
1,2 and
Zisheng Lian
1,2
1
College of Mechanical Engineering, Taiyuan University of Technology, Taiyuan 030024, China
2
Shanxi Key Laboratory of Fully Mechanized Coal Mining Equipment, Taiyuan 030024, China
*
Author to whom correspondence should be addressed.
Materials 2018, 11(10), 2046; https://doi.org/10.3390/ma11102046
Submission received: 9 July 2018 / Revised: 28 September 2018 / Accepted: 18 October 2018 / Published: 20 October 2018
(This article belongs to the Section Advanced Composites)
Browse Figures
Versions Notes

Abstract

:
ZrB2–HfC ceramics have been fabricated using the liquid phase sintering technique at a sintering temperature as low as 1750 °C through the addition of Ni. The effects of HfC addition on the microstructure and mechanical properties of ZrB2–based ceramics have been investigated. These ceramics were composed of ZrB2, HfC, Ni, and a small amount of possible (Zr, Hf)B2 solid solution. Small HfC grains were distributed among ZrB2 grain boundaries. These small grains could improve the density of ZrB2–based ceramics and play a pinning role. With HfC content increasing from 10 wt % to 30 wt %, more HfC grains were distributed among ZrB2 grain boundaries, leading to weaker interface bonding among HfC grains; the relative density and Vickers hardness increased, and flexural strength and fracture toughness decreased. The weak interface bonding for 20 and 30 wt % HfC contents was the main cause of the decrease in both flexural strength and fracture toughness.

1. Introduction

TheZrB2 ceramic is an ultrahigh-temperature ceramic with a high melting point (above 3300 °C), high electrical and thermal conductivity, high refractoriness, corrosion resistance, wear resistance, and ablation resistance [1,2,3]. Its physical and chemical properties make it a promising candidate for industrial applications in a harsh environment. However, the strength and fracture toughness of monolithic ZrB2 are very low, which limits its extensive applications. In order to expand its applications, ceramic additives such as SiC [4], ZrSi2 [5], (Ti, W)C [6], Co–WC [7], WSi2 [8], and ZrO2 fiber [9] have been employed into the ZrB2 matrix to overcome these defects.
The HfC ceramic also is an ultrahigh-temperature ceramic with a high melting point (about 3900 °C), high hardness, high electrical conductivity, and high elastic modulus and chemical stability [10,11,12]. HfC is a potential candidate material for aerospace applications, owing to its high melting point and low self-diffusion coefficient. These applications include scramjet components and rocket nozzles serviced at above 3000 °C [13,14,15]. Recently, it has emerged as a reinforcement phase to improve microstructure and mechanical properties for different ceramic matrix materials. HfC added into TiCN–based, TiB2–based, and ZrO2–based ceramics can form HfC particle dispersion that not only improves their microstructures, but also enhances their mechanical properties [16,17,18]. These reports provide a new approach to improve microstructure and mechanical properties of other ceramics through adding HfC. Over the years, numerous studies on the influence of Co–WC [7], WSi2 [8], ZrO2 fiber [9], MoSi2 [19], B4C [20], and SiC [21] additives on properties of ZrB2–based ceramic have been reported, whereas few studies on the effects of the HfC additive on properties of ZrB2–based ceramic have been undertaken.
ZrB2–based ceramics are commonly fabricated using the powder metallurgy technique. This technique mainly includes the solid phase sintering technique and liquid phase sintering technique. Compared to liquid phase sintering, solid phase sintering requires a higher sintering temperature. For solid phase sintering used in fabricating ZrB2–based ceramics, sintering temperature is usually about 2000 °C, such as 2200 °C for sintering ZrB2–TiB2 ceramics [22], 2150–2250 °C for sintering ZrB2–B4C ceramics [23], and 2000 °C for sintering ZrB2–SiC ceramics [24], to obtain complete densification. Simultaneously, such high sintering temperatures can promote ZrB2 grain growth that results in the reduction of flexural strength [25]. In order to obtain full densification of ZrB2–based ceramics and to lower the sintering temperatures, a hot pressing sintering process and metal sintering aids are usually employed in fabricating these ceramics. The addition of Fe to a ZrB2–SiC mixture makes it possible to decrease the sintering temperature from 2000 to 1600 °C [26,27]. Monteverde et al. pointed out that Ni can lower sintering temperature and promote densification of ZrB2–TiB2 and ZrB2–B4C ceramics during hot-pressed sintering [28]. Moreover, many studies show that the content of metal sintering aids is generally in the range of 4~10 wt % in the liquid phase sintering process of ceramics; too little metal content cannot promote the complete liquid phase sintering of ceramics; excessive metal content will lower the hardness of ceramics [29,30,31].
In this article, we apply the liquid phase sintering technique to prepare ZrB2–HfC ceramics at a lower sintering temperature through adding 8 wt % Ni. The effects of HfC addition on microstructure and mechanical properties at room temperature of ZrB2–based ceramics will be investigated.

2. Experimental Procedure

Commercially available ZrB2 powder (purity ≥ 99.8 wt %, C < 0.15 wt %, Fe < 0.09 wt %, Co < 0.011 wt %) with a median particle size of 1 μm from Northwest Institute for Non-ferrous Metal Research, Xi’an, China was employed. HfC powder (purity ≥ 99.9 wt %, O < 0.17 wt %, Fe < 0.08 wt %) with a median particle size of 0.8 μm from Shanghai Chaowei Nanomaterials Co., Ltd., Shanghai, China was used as secondary phase. Ni powder (purity ≥ 99.8 wt %, O < 0.06 wt %, C < 0.14 wt %, Fe < 0.06 wt %) with a median particle size of 1 μm from Qinhuangdao ENO High-Tech Material Development Co., Ltd., Qinhuangdao, China was used as a sintering aid. ZrB2–10 wt % HfC–8 wt % Ni (ZH10N), ZrB2–20 wt % HfC–8 wt % Ni (ZH20N), and ZrB2–30 wt % HfC–8 wt % Ni (ZH30N) were hot pressed at 1750 °C for 1 h under 30 MPa in a vacuum (3 × 10−3 Pa).
Before hot pressing, powders were mixed and milled for 72 h in a polyethylene jar with zirconia balls and alcohol as medium. Then, the mixed slurry was dried in vacuum and sieved by a 200-mesh sieve. After hot pressing, sintered samples were cut into test bars using the electrical discharge wire cutting method and the surfaces of the test bars were polished using diamond slurries. The dimension of the test bar was 3 mm × 4 mm × 50 mm. These test bars were cleaned by ultrasonication in absolute ethyl alcohol as a medium. After ultrasonic cleaning, these bars were dried for different tests. Ten test bars were tested for each experimental condition.
Flexural strength was measured at a span of 30 mm and across head speed of 0.5 mm/min using the three-point bending test method on an electron universal tester, according to Chinese National Standards GB/T 6569-2006/ISO 14704: 2000 [32]. Vickers hardness was measured on polished surfaces using a diamond pyramid indenter under a load of 196 N for 15 s by HV-120, based on Chinese National Standards GB/T 16534-2009 [33]. Fracture toughness (KIC) was measured via the direct indentation method [18]; the indentation was obtained through the Vickers hardness test. The density of each ceramic was measured using Archimedes’ method, with distilled water as a medium. Theoretical density was calculated according to the rule of mixtures, based on the following densities: 6.10, 12.7, and 8.90 g/cm3 for ZrB2, HfC, and Ni, respectively. Relative density was the ratio of the measured density to the theoretical density. An X-ray diffraction (XRD, EMPYREAN, PANalytical B.V., Almelo, The Netherlands) and energy dispersive spectrometer (EDS, ACT-350, Oxford Instruments, Oxford, UK) were used to analyze the compositions of the ceramics. A scanning electron microscope in back scattered electron mode (SEM and BSE, Supra-55, Carl Zeiss AG, Oberkochen, Germany) was used to observe the polished surface and fractured surface morphologies.

3. Results and Discussion

3.1. Effects of HfC Addition on Microstructure of ZrB2–HfC Ceramics

Figure 1 shows the X-ray diffraction patterns of ZrB2–HfC ceramics. The main crystalline phases were ZrB2, HfC, and Ni, which was consistent with the compositions of the raw powders. This indicated that no reaction occurred during the sintering process. It can be seen that as HfC content increased, the peak of HfC increased accordingly.
Figure 2 exhibits SEM–BSE micrographs of polished surfaces of ZrB2–HfC ceramics with different HfC content. Obviously, ZrB2–HfC ceramics had three phases: A white phase, a black phase, and a grey phase. In order to determine their compositions, they were separately subjected to EDS analysis. Figure 3 displays EDS results of points A, B, and C in Figure 2 for these three phases. In Figure 3a, the sum of mass fraction of the Hf and C elements was 94.68% higher than that of the other elements; moreover, the ratio of the Hf and C atomic fraction was 43.5:45.92 near to 1:1; according to XRD analysis results. Therefore, the white phase in Figure 2 was HfC. In Figure 3b, the black phase consisted of 66.33 wt % Zr and 16.41 wt % B, their total mass fraction was 82.74% higher than that of the others, and the ratio of their atomic fraction was 29.44:61.46 near to 1:2. Thus, based on XRD analysis results, the black phase in Figure 2 was ZrB2. In Figure 3c, the grey phase contained 50.96 wt % Zr, 12.4 wt % B, 26.52 wt % Hf, 1.93 wt % C, and 8.2 wt % Ni, indicating that the grey phase consisted of a mixture of all compounds. In fabricating ZrB2–SiC–HfB2 ceramics, Balak et al. pointed out that Hf and Zr diffused each other in a way that resulted in the formation of a (Zr, Hf)B2 solid solution [34]. Generally, when a new solid solution forms, twin peaks appear next to the standard XRD [35,36]. However, the peak position of ZrB2 and HfC in Figure 1 was in line with their respective peak position in the standard XRD card. According to the above analysis, the grey phase was probably a mixture of ZrB2 HfC, Ni, and a small amount of possible (Zr, Hf)B2 solid solution. Furthermore, there were some pores (marked in Figure 2) in ZrB2–HfC ceramics. These pores mainly derived from the sintering process and from grain pull-out during the procedure of grinding and polishing. Accordingly, the area of the white phase increased gradually with HfC content increasing in Figure 2.
Figure 4 exhibits fracture morphologies of ZrB2–HfC ceramics with different HfC content. As can be seen, large ZrB2 and small HfC grains coexisted in these ceramics. The difference in the average ZrB2 grain size of these ceramics was very small. For each ceramic in Figure 4, the average grain size of ZrB2 was about 5 μm and of HfC was about 1 μm. These HfC grains were distributed among ZrB2 grain boundaries. In fabricating a ZrB2–SiC composite, Debnath et al. found that fine SiC particles distributed around ZrB2 grains could inhibit ZrB2 grain growth [27]. However, for ZrB2–HfC ceramics, these small HfC showed a small effect on ZrB2 grain growth. Generally, sintering temperature, additive content, and holding time are factors that determine the grain growth of the matrix phase. In the ZrB2–HfC–Ni system, the sintering temperature of 1750 °C perhaps had more significant effects on ZrB2 grain growth than HfC content and holding time; this resulted in just a small difference in the ZrB2 grain size. Moreover, compared to the size of raw powders, ZrB2 grain growth was obvious, from 1 to 5 um, while HfC grain growth was not obvious, from 0.8 to about 1 um, which also indicated that 1750 °C was more suitable for ZrB2 grain growth than for HfC. In HfC–SiC ceramics sintered at 2300 °C, Liu et al. pointed out that oxygen impurity can induce the growth of the HfC grain [37]. In this investigation, in order to reduce the introduced impurity, the mixed powders were milled in a polyethylene jar with zirconia balls and alcohol as mediums; then, the mixed slurry was dried in vacuum; after that, they were sintered in a vacuum (3 × 10−3 Pa). Therefore, in the fabrication processing, it was hard to introduce oxygen impurity to ZrB2–HfC–Ni ceramics, except the original oxygen impurity in raw powders. Compared to 1.7 wt % for the total content of oxygen impurity in HfC–SiC ceramics [37], 0.23 wt % for the total content of the oxygen impurity in ZrB2–HfC–Ni ceramics was considerably less; moreover, the sintering temperature of 1750 °C for fabricating ZrB2–HfC ceramics was lower than 2300 °C for fabricating HfC–SiC ceramics [37]; therefore, the unobvious HfC grain growth was ascribed to less oxygen impurity and lower sintering temperature in ZrB2–HfC–Ni ceramics. In addition, in Figure 4, there were a few coarse ZrB2 grains (as shown by circles) in each ceramic. These coarse grains were formed upon coalescence of small ZrB2 grains.
With HfC content increasing from 10 wt % to 30 wt %, more and more small HfC grains were located among ZrB2 grain boundaries. When HfC content was 10 wt %, many small HfC grains (as indicated by the red arrows in Figure 4a) were directly pinned into ZrB2 grains. These small HfC grains could play a pinning role to keep the material from fracturing during fracturing. This pinning effect of HfC grains on the ZrO2 grain boundaries was also discovered by Song et al. in ZrO2–HfC ceramics [18]. However, when the HfC content was 20 wt % and 30 wt %, some HfC grains (as indicated by the yellow arrows in Figure 4b,c) were distributed among the pinned HfC grains; these HfC hardly played the direct pinning effect on ZrB2; moreover, weak grain boundary strength may have been formed among these HfC grains due to the shortage of metal Ni to completely wet each of these HfC grains. Therefore, ZH10N would have stronger grain boundary strength than the other two ceramics.

3.2. Effects of HfC Content on Relative Density and Mechanical Properties of ZrB2–HfC Ceramics

Figure 5 presents the relative density and mechanical properties of ZrB2–HfC ceramics with different HfC content. In Figure 5a, with increasing HfC content from 10 wt % to 30 wt %, the relative density gradually increased from (99.12 ± 0.03)% to (99.55 ± 0.05)%. During the liquid phase sintering, when HfC content was 10 wt %, the liquid metal Ni played a leading role in improving densification. The reason was that the liquid metal Ni would fill in gaps among grains. When HfC content was 20 wt % and 30 wt %, densification mainly depended on the increase of small HfC grains to fill in pores among grains. In precipitating, pores among grains would form because of big wetting angles of about 65° for ZrB2 and Ni, and about 50° for HfC and Ni [38]. With HfC content increasing, these small HfC grains would fill in these pores to improve the densification of ZrB2–HfC ceramics. Small particles or grains like SiC could also improve the densification of ZrB2–SiC ceramics, as reported by Debnath et al. [27]. The lowest relative density of the ZH10N ceramic ((99.12 ± 0.03)%) was higher than that of the monolithic ZrB2 ceramic (80.1%) sintered at 1750 °C, as reported by Sonber et al. [8].
Similarly, Vickers hardness slightly varied from about 15 to 16 GPa in Figure 5b. Numerous investigations [36,39,40] showed that, for ceramics, their Vickers hardness had a close relationship with their density: Generally, their Vickers hardness increased with their density increasing. ZrB2–HfC ceramics were no exception. In addition, the hardness of HfC (about 26 GPa) is higher than that of ZrB2 (about 22 GPa), which also promoted the improvement of its Vickers hardness with HfC content increasing. The Vickers hardness of the ZH30N ceramic (16.14 ± 0.22 GPa) was slightly lower than that of the ZrB2–MoSi2 ceramics (16.2 ± 0.5 GPa), as reported by Andrea et al. [41].
In Figure 5c, with HfC content increasing, their flexural strength gradually decreased from 624.72 ± 21 MPa to 518.58 ± 22 MPa. Generally, big grains resulted in the low flexural strength. However, the difference between the ZrB2 grain size of these three ceramics was very small, indicating that with HfC content increasing, there was another reason for the decrease in flexural strength. The reason was that with HfC content increasing from 10 wt % to 30 wt %, weak grain boundary strength formed among more HfC grains. Diffused weak grain boundary strength led to low flexural strength. The ZH10N ceramic had the highest flexural strength, owing to stronger grain boundary strength. The flexural strength of the ZH10N ceramic (624.72 ± 21 MPa) was higher than that of the ZrB2–MoSi2 ceramics (531 ± 46 MPa), as reported by Sciti et al. [42].
In Figure 5d, with HfC content increasing, fracture toughness gradually decreased from 6.08 ± 0.18 MPa·m1/2 to 4.79 ± 0.15 MPa·m1/2. In fabricating ZrB2–MoSi2 ceramics, through comparing the fracture toughness (2.3 ± 0.2 MPa·m1/2) of ZrB2–MoSi2 ceramics with that (2.8 MPa·m1/2) of monolithic ZrB2, Sciti et al. claimed that the addition of MoSi2 particles did not activate any toughening mechanisms, owing to the small difference in the coefficients of the thermal expansion between ZrB2 and MoSi2 (8.4 × 10−6/K) [42]. Moreover, in the ZrB2–SiC–TaSi2 system, Wang et al. assumed that with an increase in TaSi2 content, the weaker interface bonding between ZrB2 and TaSi2 caused by the different coefficients of thermal expansion between the ZrB2 (6.7 × 10−6/K) and TaSi2 (14 × 10−6/K) resulted in the improvement of fracture toughness [2]. However, compared to the toughening mechanisms of ZrB2–SiC–TaSi2 and ZrB2–MoSi2 ceramics, ZrB2–HfC had a different toughening mechanism. In this investigation, although the difference in coefficients of the thermal expansion between ZrB2 and HfC (6.6 × 10−6/K [18]) is very small, the lowest fracture toughness of ZrB2–HfC ceramics (4.79 ± 0.15 MPa·m1/2) was higher than that of monolithic ZrB2 (2.8 MPa·m1/2), which indicated that HfC addition played a toughening role. Additionally, the fracture toughness of ZH20N and ZH30N ceramics was lower than that of the ZH10N ceramic, which indicated that weak interface bonding cannot result in the improvement of fracture toughness. This weak interface easily caused the crack to propagate to produce a long crack that resulted in low fracture toughness. The fracture toughness of ZrB2–HfC ceramics mainly depended on the pinning effect of HfC on ZrB2 grains and the interface bonding strength among HfC grains.

4. Conclusions

ZrB2–HfC–Ni ceramics with 10–30 wt % HfC content were sintered at 1750 °C by hot pressing. The effects of HfC content on the microstructure and mechanical properties were investigated. The conclusions were as follow:
(1)
ZrB2–HfC–Ni ceramics were mainly composed of ZrB2, HfC, and Ni. There were three phases: A white phase, a black phase, and a grey phase. The white phase was HfC, the black phase was ZrB2, and the grey phase was a mixture of ZrB2, HfC, and Ni with a small amount of possible (Zr, Hf)B2 solid solution.
(2)
Small HfC grains were distributed among the ZrB2 grain boundaries. These small grains could improve the density of ZrB2–based ceramics and play the pinning role in these ceramics. ZrB2 grain growth influenced by HfC addition was not significant.
(3)
With HfC content increasing from 10 wt % to 30 wt %, more HfC grains were distributed among ZrB2 grain boundaries, leading to weak interface bonding among HfC grains; the relative density and Vickers hardness increased and flexural strength and fracture toughness decreased. The weak interface bonding in ZH20N and ZH30N ceramics accounted for lowering the flexural strength and fracture toughness of these ceramics.

Author Contributions

Z.L. and Y.J. conceived and designed the experiments; Y.J. performed the experiments and analyzed the data; Z.L. and H.Y. contributed reagents/materials/analysis tools; Y.J. and H.Y. wrote the paper.

Funding

This work was funded by the Natural Science Foundation of Shanxi Province of China grant number 201701D221139 and 2012011024-3.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Sun, X.; Han, W.B.; Liu, Q.; Hu, P.; Hong, C.Q. ZrB2–ceramic toughened by refractory metal Nb prepared by hot-pressing. Mater. Des. 2010, 31, 4427–4431. [Google Scholar] [CrossRef]
  2. Wang, S.B.; Xu, C.; Ding, Y.B.; Zhang, X.H. Thermal shock behavior of ZrB2–SiC composite ceramics with added TaSi2. Int. J. Refract. Met. Hard Mater. 2013, 41, 507–516. [Google Scholar] [CrossRef]
  3. Zapata-Solvas, E.; Jayaseelan, D.D.; Brown, P.M.; Lee, W.E. Effect of oxidation on room temperature strength of ZrB2– and HfB2–based ultrahigh temperature ceramics. Adv. Appl. Ceram. 2015, 114, 407–417. [Google Scholar] [CrossRef]
  4. Han, J.C.; Hu, P.; Zhang, X.H.; Meng, S.H.; Han, W.B. Oxidation-resistant ZrB2–SiC composites at 2200 °C. Compos. Sci. Technol. 2008, 68, 799–806. [Google Scholar] [CrossRef]
  5. Wang, M.F.; Wang, C.A.; Zhang, X.H. Effects of SiC platelet and ZrSi2 additive on sintering and mechanical properties of ZrB2–based ceramics by hot-pressing. Mater. Des. 2012, 34, 293–297. [Google Scholar] [CrossRef]
  6. Li, B.; Wang, H. Prediction and analysis of microstructural effects on fabrication of ZrB2/(Ti,W)C composites. Int. J. Refract. Met. Hard Mater. 2013, 36, 167–173. [Google Scholar] [CrossRef]
  7. Choi, S.K.; Ui, S.W.; Choi, I.S.; Choi, S.C. Densification behavior of ZrB2 with Co–WC as additives. J. Ceram. Soc. Jpn. 2014, 122, 198–203. [Google Scholar] [CrossRef]
  8. Sonber, J.K.; Murthy, T.S.R.C.; Subramanian, C.; Hubli, R.C.; Fotedar, R.K.; Suri, A.K. Effect of WSi2 addition on densification and properties of ZrB2. Adv. Appl. Ceram. 2014, 113, 114–119. [Google Scholar] [CrossRef]
  9. Lin, J.; Huang, Y.; Zhang, H.A.; Yang, Y.H.; Zhao, T.Y. Densification and properties of ZrO2 fiber toughed ZrB2–SiC ceramics via spark plasma sintering. Mat. Sci. Eng. A 2015, 644, 204–209. [Google Scholar] [CrossRef]
  10. Diletta, S.; Stefano, G. Densification and mechanical behavior of HfC and HfB2 fabricated by spark plasma sintering. J. Am. Ceram. Soc. 2008, 91, 1433–1440. [Google Scholar]
  11. Xiang, L.Y.; Cheng, L.F.; Shi, L.; Yin, X.W.; Zhang, L.T. Laminated HfC–SiC ceramics produced by aqueous tape casting and hot pressing. Ceram. Int. 2015, 41, 14406–14411. [Google Scholar] [CrossRef]
  12. Ludovic, C.; Marianne, B.P.; Sans, J.L.; Diletta, S.; Laura, S. Effect of high temperature oxidation on the radiative properties of HfC–based ceramics. Corros. Sci. 2017, 126, 255–264. [Google Scholar]
  13. Pienti, L.; Sciti, D.; Silvestroni, L.; Cecere, A.; Savino, R. Ablation tests on HfC– and TaC–based ceramics for aeropropulsive applications. J. Eur. Ceram. Soc. 2015, 35, 1401–1411. [Google Scholar] [CrossRef]
  14. Omar, C.B.; Salvatore, G.; Nasrin, A.N.; Daniel, D.J.; Michael, J.R.; William, E.L. Sintering behaviour, solid solution formation and characterisation of TaC, HfC and TaC–HfC fabricated by spark plasma sintering. J. Eur. Ceram. Soc. 2016, 36, 1539–1548. [Google Scholar]
  15. Cai, T.; Liu, D.; Qiu, W.F.; Han, W.J.; Zhao, T. Polymer precursor-derived HfC–SiC ultrahigh-temperature ceramic nanocomposites. J. Am. Ceram. Soc. 2018, 101, 20–24. [Google Scholar] [CrossRef]
  16. Gao, J.J.; Song, J.P.; Liang, G.X.; An, J.; Cao, L.; Xie, J.C.; Lv, M. Effects of HfC addition on microstructures and mechanical properties of TiC0.7N0.3–based and TiC0.5N0.5–based ceramic tool materials. Ceram. Int. 2017, 43, 14945–14950. [Google Scholar] [CrossRef]
  17. Song, J.P.; Jiang, L.K.; Liang, G.X.; Gao, J.J.; An, J.; Cao, L.; Xie, J.C.; Wang, S.Y.; Lv, M. Strengthening and toughening of TiN–based and TiB2–based ceramic tool materials with HfC additive. Ceram. Int. 2017, 43, 8202–8207. [Google Scholar] [CrossRef]
  18. Song, J.P.; Cao, L.; Jiang, L.K.; Liang, G.X.; Gao, J.J.; Li, D.X.; Wang, S.Y.; Lv, M. Effect of HfN, HfC and HfB2 additives on phase transformation, microstructure and mechanical properties of ZrO2–based ceramics. Ceram. Int. 2018, 44, 5371–5377. [Google Scholar] [CrossRef]
  19. Wang, R.Z.; Li, W.G. Effects of microstructures and flaw evolution on the fracture strength of ZrB2–MoSi2 composites under high temperatures. J. Alloy Compd. 2015, 644, 582–588. [Google Scholar] [CrossRef]
  20. Chakraborty, S.; Debnath, D.; Mallick, A.R.; Das, P.K. Mechanical, tribological, and thermal properties of hot-pressed ZrB2–B4C composite. Int. J. Appl. Ceram. Technol. 2015, 12, 568–576. [Google Scholar] [CrossRef]
  21. He, J.B.; Cao, Y.J.; Zhang, Y.X.; Wang, Y.G. Mechanical properties of ZrB2–SiC ceramics prepared by polymeric precursor route. Ceram. Int. 2018, 44, 6520–6526. [Google Scholar] [CrossRef]
  22. Chakraborty, S.; Debnath, D.; Mallick, A.R.; Das, P.K. Mechanical and thermal properties of hot pressed ZrB2 system with TiB2. Int. J. Refract. Met. Hard Mater. 2014, 46, 35–42. [Google Scholar] [CrossRef]
  23. Ma, H.B.; Liu, H.L.; Zhao, J.; Xu, F.F.; Zhang, G.J. Pressureless sintering, mechanical properties and oxidation behavior of ZrB2 ceramics doped with B4C. J. Eur. Ceram. Soc. 2015, 35, 2699–2705. [Google Scholar] [CrossRef]
  24. Jin, X.X.; Dong, L.M.; Xu, H.Y.; Liu, L.Z.; Li, N.; Zhang, X.H.; Han, J.C. Effects of porosity and pore size on mechanical and thermal properties as well as thermal shock fracture resistance of porous ZrB2–SiC ceramics. Ceram. Int. 2016, 42, 9051–9057. [Google Scholar] [CrossRef]
  25. Alireza, R.; William, G.F.; Gregory, E.H. Effect of hot pressing time and temperature on the microstructure and mechanical properties of ZrB2–SiC. J. Mater. Sci. 2007, 42, 2735–2744. [Google Scholar]
  26. Zhang, X.; Liu, R.T.; Zhang, X.Y.; Zhu, Y.Y.; Sun, W.; Xiong, X. Densification and ablation behavior of ZrB2 ceramic with SiC and / or Fe additives fabricated at 1600 and 1800 °C. Ceram. Int. 2016, 42, 17074–17080. [Google Scholar] [CrossRef]
  27. Debnath, D.; Chakraborty, S.; Mallick, A.R.; Gupta, R.K.; Ranjan, A.; Das, P.K. Mechanical, tribological and thermal properties of hot pressed ZrB2–SiC composite with SiC of different morphology. Adv. Appl. Ceram. 2015, 114, 45–54. [Google Scholar] [CrossRef]
  28. Monteverde, F.; Fabbriche, D.D.; Bellosi, A. Zirconium diboride–based composites. Key Eng. Mater. 2002, 206–213, 961–964. [Google Scholar] [CrossRef]
  29. Mousavi, M.J.; Zakeri, M.; Rahimipour, M.R.; Amini, E. Effect of Ni and C additives on pressureless sintering and mechanical properties of ZrB2. Adv. Appl. Ceram. 2015, 114, 261–266. [Google Scholar] [CrossRef]
  30. Zhao, G.L.; Huang, C.Z.; Liu, H.L.; Zou, B.; Zhu, H.T.; Wang, J. Microstructure and mechanical properties of TiB2–SiC ceramic composites by Reactive Hot Pressing. Int. J. Refract. Met. Hard Mater. 2014, 42, 36–41. [Google Scholar] [CrossRef]
  31. Yue, X.Y.; Cai, Z.X.; Lv, X.H.; Wang, J.J.; Ru, H.Q. Effect of Ni content on microstructures and mechanical properties of hot-pressed TiC–TiB2–Ni composite. Mat. Sci. Eng. A 2016, 668, 208–214. [Google Scholar] [CrossRef]
  32. GB/T 6569-2006/ISO 14704: 2000. Fine Ceramics (Advanced Ceramics, Advanced Technical Ceramics)—Test Method for Flexural Strength of Monolithic Ceramics at Room Temperature; Chinese Standard Publishing House: Beijing, China, 2006; Available online: www.spc.org.cn (accessed on 22 February 2006). (In Chinese)
  33. GB/T 16534-2009. Fine Ceramics (Advanced Ceramics, Advanced Technical Ceramics)—Test Method for Hardness of Monolithic Ceramics at Room Temperature; Chinese Standard Publishing House: Beijing, China, 2009; Available online: www.spc.org.cn (accessed on 13 May 2009). (In Chinese)
  34. Balak, Z.; Zakeri, M. Effect of HfB2 on microstructure and mechanical properties of ZrB2–SiC–based composites. Int. J. Refract. Met. Hard Mater. 2016, 54, 127–137. [Google Scholar] [CrossRef]
  35. An, J.; Song, J.P.; Liang, G.X.; Gao, J.J.; Xie, J.X.; Cao, L.; Wang, S.Y.; Lv, M. Effects of HfB2 and HfN additions on the microstructures and mechanical properties of TiB2–based ceramic tool materials. Materials 2017, 10, 461. [Google Scholar] [CrossRef] [PubMed]
  36. Song, J.P.; Cao, L.; Gao, J.J.; Liang, G.X.; Wang, S.Y.; Lv, M. Effects of HfN content and metallic additives on the microstructure and mechanical properties of TiC0.7N0.3–based ceramic tool materials. J. Alloy Compd. 2018, 753, 85–92. [Google Scholar] [CrossRef]
  37. Liu, J.X.; Huang, X.; Zhang, G.J. Pressureless Sintering of Hafnium Carbide–Silicon Carbide Ceramics. J. Am. Ceram. Soc. 2013, 96, 1751–1756. [Google Scholar] [CrossRef]
  38. Li, R.J. Ceramic—Metal Composite Materials, 2nd ed.; Metallurgical Industry Press: Beijing, China, 2004. (In Chinese) [Google Scholar]
  39. Yin, Z.B.; Yan, S.Y.; Xu, W.W.; Yuan, J.T. Microwave sintering of Ti(C, N)–based cermet cutting tool material. Ceram. Int. 2018, 44, 1034–1040. [Google Scholar] [CrossRef]
  40. Zhao, G.L.; Huang, C.Z.; He, N.; Liu, H.L.; Zou, B. Microstructural development and mechanical properties of reactive hot pressed nickel-aided TiB2–SiC ceramics. Int. J. Refract. Met. Hard Mater. 2016, 61, 13–21. [Google Scholar] [CrossRef]
  41. Andrea, B.; Diletta, S. Spark plasma sintering and hot pressing of ZrB2–MoSi2 ultra-high-temperature ceramics. Mat. Sci. Eng. A 2008, 475, 108–112. [Google Scholar]
  42. Diletta, S.; Stefano, G.; Alida, B. Properties of a pressureless-sintered ZrB2–MoSi2 ceramic composite. J. Am. Ceram. Soc. 2006, 89, 2320–2322. [Google Scholar]
Materials 11 02046 g001 550
Figure 1. X-ray diffraction (XRD) patterns of ZrB2–HfC ceramics.
Figure 1. X-ray diffraction (XRD) patterns of ZrB2–HfC ceramics.
Materials 11 02046 g001
Materials 11 02046 g002 550
Figure 2. Scanning electron microscope in back scattered electron mode (SEM–BSE) micrographs of polished surfaces of ZrB2–HfC ceramics with different HfC content: (a) ZrB2–10 wt % HfC (ZH10N), (b) ZrB2–20 wt % HfC (ZH20N), and (c) ZrB2–30 wt % HfC (ZH30N).
Figure 2. Scanning electron microscope in back scattered electron mode (SEM–BSE) micrographs of polished surfaces of ZrB2–HfC ceramics with different HfC content: (a) ZrB2–10 wt % HfC (ZH10N), (b) ZrB2–20 wt % HfC (ZH20N), and (c) ZrB2–30 wt % HfC (ZH30N).
Materials 11 02046 g002
Materials 11 02046 g003 550
Figure 3. Energy dispersive spectrometer (EDS) measured at 30 kV of the phases in ZrB2–HfC ceramics: (a) EDS of point A for the white phase, (b) EDS of point B for the black phase, and (c) EDS of point C for the grey phase defined in Figure 2.
Figure 3. Energy dispersive spectrometer (EDS) measured at 30 kV of the phases in ZrB2–HfC ceramics: (a) EDS of point A for the white phase, (b) EDS of point B for the black phase, and (c) EDS of point C for the grey phase defined in Figure 2.
Materials 11 02046 g003
Materials 11 02046 g004 550
Figure 4. Fracture morphologies of the fracture surface of ZrB2–HfC ceramics with different HfC content: (a) ZrB2–10 wt % HfC (ZH10N), (b) ZrB2–20 wt % HfC (ZH20N), and (c) ZrB2–30 wt % HfC (ZH30N).
Figure 4. Fracture morphologies of the fracture surface of ZrB2–HfC ceramics with different HfC content: (a) ZrB2–10 wt % HfC (ZH10N), (b) ZrB2–20 wt % HfC (ZH20N), and (c) ZrB2–30 wt % HfC (ZH30N).
Materials 11 02046 g004
Materials 11 02046 g005 550
Figure 5. Relative density and mechanical properties of ZrB2–HfC ceramics with different HfC content: (a) Relative density, (b) Vickers hardness, (c) Flexural strength, and (d) Fracture toughness.
Figure 5. Relative density and mechanical properties of ZrB2–HfC ceramics with different HfC content: (a) Relative density, (b) Vickers hardness, (c) Flexural strength, and (d) Fracture toughness.
Materials 11 02046 g005

Share and Cite

MDPI and ACS Style

Jing, Y.; Yuan, H.; Lian, Z. Microstructure and Mechanical Properties of ZrB2–HfC Ceramics Influenced by HfC Addition. Materials 2018, 11, 2046. https://doi.org/10.3390/ma11102046

AMA Style

Jing Y, Yuan H, Lian Z. Microstructure and Mechanical Properties of ZrB2–HfC Ceramics Influenced by HfC Addition. Materials. 2018; 11(10):2046. https://doi.org/10.3390/ma11102046

Chicago/Turabian Style

Jing, Yi, Hongbing Yuan, and Zisheng Lian. 2018. "Microstructure and Mechanical Properties of ZrB2–HfC Ceramics Influenced by HfC Addition" Materials 11, no. 10: 2046. https://doi.org/10.3390/ma11102046

APA Style

Jing, Y., Yuan, H., & Lian, Z. (2018). Microstructure and Mechanical Properties of ZrB2–HfC Ceramics Influenced by HfC Addition. Materials, 11(10), 2046. https://doi.org/10.3390/ma11102046

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop