1. Introduction
π-conjugated small molecules and polymers are extensively used in organic electronics because of their low-cost manufacturing, light weight, good processability and good ability to be deposited on flexible substrates [
1,
2] in comparison with conventional inorganic semiconductors [
3,
4]. In order to efficiently tune the charge transport abilities and electronic performances of π-conjugated materials in (opto)electronic devices, an in-depth understanding of their molecular structures, supramolecular organization and film morphology are required. Among the most extensively investigated electron accepting organic materials, naphthalenediimides (NDI) [
5,
6,
7] and perylenediimides (PDI) [
1,
8] stand out because of their good electron-withdrawing abilities and their low-lying LUMO levels, which properly stabilize multiple negative charges. On the other hand, thiophene-based π-conjugated oligomers and polymers are efficient electron-donor systems with tunable HOMO levels, suitable to stabilize multiple positive charges.
For these reasons, donor-acceptor assemblies based on oligothiophene and naphthalimide moieties have received a great deal of attention in organic electronics [
1,
4,
9]. In this framework, during the last few years, we have been active in the syntheses of oligothiophene–naphthalimide assemblies in which the donor and acceptor electroactive units are connected through rigid heterocycles. The connection of flat and rigid donor and acceptor moieties through rigid heterocyclic spacers is an efficient strategy to minimize skeletal distortions, allowing closer intermolecular π–π stacking and extended intramolecular π conjugation. Furthermore, through the suitable functionalization of these innovative organic semiconductors, they can be designed to exhibit a good film forming ability and low reorganization energies for both electron and hole transports.
Therefore, in this feature article, we summarize our contribution to the development of synthetic strategies toward several families of ambipolar organic electronic materials based on oligothiophene and 1,8-naphthalimide units connected via different rigid heterocyclic linkers. We highlight the principles of design of the different families of oligothiophene–naphthalimide assemblies and rationalize how the synthetic modifications affect the molecular geometry, the frontier energy levels, the thin-film microstructures and their performances in organic field-effect transistors (OFETs).
To evaluate the charge-transport characteristics of all the systems reviewed in this work, top-contact/bottom-gate thin-film transistors were fabricated by either vapor or solution deposition of the semiconducting films onto octadecyltrichlorosilane (OTS)-functionalized Si/SiO
2 substrates and/or onto hexamethyldisilazane (HMDS)-treated Si/SiO
2 substrates, followed by gold deposition through a shadow mask to define source and drain electrodes, with different channel lengths and widths. The performance parameters were extracted from the I-V response plots, in the saturation regime, by using the assumptions of conventional transistor formalism, Equation (1):
where
is the drain current in the saturation regime,
W the channel width,
L the channel length,
C the capacitance per unit area of the insulator layer and
VG the gate voltage.
Thus, the linear fitting of the ID1/2 versus VG plot, in the saturation regime, allowed mobility, µ, and threshold voltage, VT, values estimation.
2. Amidine-Based Oligothiophene–Rylenimide Semiconductors
As it has been already mentioned, naphthalene and perylene diimide derivatives have been widely used as electron transport materials in a variety of device architectures [
1,
8]. The connection of electron donor oligothiophene units to the rylene skeleton provides an enhancement of the
p-type behavior of the novel rylene derivative formed, thus enabling ambipolar transport. Our first approach in this direction involves the syntheses of a series of semiconductors based on thiophene-fused rylenimide derivatives via imidazole linkers (
Figure 1). This family of oligothiophene–imidazole–rylenimide assemblies was designed with the aim to study the influence of different variables in OFET devices: (i) the effect of the length of the oligothiophene fragment on the charge transport characteristics, (ii) the effect of the replacement of some thiophene units by weaker electron donor benzene moieties and (iii) the effect of the lateral extension of the π-conjugated systems via naphthalene diimide vs. perylene diimide core interchange.
This first-generation of organic semiconductors based on rylenimide-fused oligothiophene units was obtained by condensation between suitable diaminooligothiophene unit
2 and the corresponding monoanhydride monoimide derivative
1 or
3 as it is depicted in
Scheme 1 [
10,
11,
12]. An analogue of
NDI-3T in which the central thiophene unit is replaced by a benzene moiety,
NDI-Ph-T-Ph (
Figure 2) was also obtained by following a similar synthetic procedure. Different alkyl chains were introduced at the imide nitrogen of the NDI and PDI derivatives in order to tune the processability of these semiconductors without significantly modifying their photo- and electrochemical properties [
13,
14,
15].
The molecular geometries of the oligothiophene–naphthalimide assemblies were optimized by DFT calculations at the B3LYP/6–31G** level. For
NDI-3T,
PDI-3T and
NDI-T-Ph-T, it is observed that the end-capped thiophenes close to the keto groups are severely twisted with dihedral angles above 50° with respect to the molecular plane because of the repulsive interactions between the sulfur atom of the heterocycle unit and the neighboring carbonyl group [
12]. Single crystals of
NDI-T-Ph-T were grown by slow vapor diffusion of hexane into a chloroform solution, and the molecular structure obtained by X-ray diffraction analyses confirms the twist of the thiophene unit close to the carbonyl group (
Figure 2). On the other hand, the systems with a single thiophene unit,
NDI-1T and
PDI-1T, resulted completely planar because of the absence of nonbonded electronic repulsions.
The UV–vis absorption spectrum of
NDI-3T presents three well-defined bands in the 300–600 nm region, highlighting the broad absorption band around 583 nm which is ascribed to an intramolecular charge-transfer excitation (ICT) from the HOMO, mainly located into the oligothiophene fragment, to the LUMO, delocalized over the naphthalimide moiety [
11]. The perylenimide-based analogue,
PDI-3T, shows an enhanced absorption cross section throughout the whole UV–vis spectrum with a strong ICT band at 610 nm extending up to 800 nm [
10]. It is also worth mentioning that the characteristic fluorescence of rylenimides [
5,
16] is absent in both
NDI-3T and
PDI-3T due to the strong charge transfer component.
Electrochemical characterization of these assemblies was carried out by using cyclic voltammetry measurements. Both reduction and oxidation processes were observed in all the naphthalene and peryleneimide derivatives (
Table 1). From these data, LUMO and HOMO energies could be estimated using standard approximations (
Figure 3 and
Table 1) [
17,
18], being −3.79/−5.83 eV for
NDI-1T and −3.87/−5.55 eV for the
NDI-3T analogue. A slight stabilization of the LUMO and a remarkable destabilization of the HOMO energy level around 0.3 eV is observed when the oligothiophene fragment is extended. This electrochemical band gap reduction is consistent with the band gap compression observed in the UV–vis spectra. Further reduction of the electrochemical band gap can be achieved by extending the π-system of the rylenimide unit through replacement of the naphthalimide moiety by the larger perylenimide analogue. Thus, LUMO/HOMO energies were estimated to be −3.88/−5.76 eV for
PDI-1T and −3.89/−5.55 eV for
PDI-3T. The extension of the oligothiophene moiety does not significantly alter the LUMO level, while it produces a destabilization of the HOMO level.
In order to evaluate the electrical performances of this first generation of oligothiophene–rylenimide semiconductors, films were grown and used to build top-contact-bottom gate (TC/BG) field-effect transistors. The films were obtained either by vapor deposition or solution processed onto Si/SiO2 substrates pretreated with HDMS or OTS. The best degree of crystallinity was found for NDI-1T because of the formation of cofacial π-conjugated planes aligned to the Si/SiO2 surface with a calculated tilt angle of 61.2°. In contrast, NDI-3T thin films resulted in an amorphous material, probably due to the lack of planarity caused by a sulfur–oxygen repulsion interaction which forces the disruption of the oligothiophene planarity. Although they are less crystalline than NDI-1T, the presence of sharp Bragg reflections in the X-ray diffractograms of PDI-1T and PDI-3T evidenced the existence of a certain degree of crystallinity in the perylene derivatives.
AFM analyses of the morphology and microstructure for the semiconductors in thin films reveal large planar terraces ascribed to polycrystalline surfaces for
NDI-1T (
Figure 4) [
12]. For the
NDI-3T derivative, the catenation of the thiophene backbone is translated in the loss of crystalline grain size, phenomena related to the amorphous profile in XRD. The replacement of the thiophene central ring by phenylene units has a remarkable effect in the microstructure, increasing the grain size. Finally, the introduction of perylenimide units in the semiconductor structure of
PDI-1T and
PDI-3T leads to well-connected crystallites but with smaller sizes than those observed for
NDI-1T.
TC/BG field-effect transistor properties were evaluated in terms of charge carrier mobility (μ), current on-off ratio (I
ON/I
OFF) and threshold voltage (
VT) (
Table 2). The best charge transport characteristics were found for
NDI-1T when vapor-deposited films were grown at 110 °C on Si/SiO
2 surfaces treated with HMDS, with electron mobilities reaching values of 0.35 cm
2 V
−1 s
−1. These good results regarding
NDI-1T could be explained in terms of high crystallinity and good molecular packing in well-connected grains, as observed in XRD and AFM analyses. The smaller grain sizes and lower crystallinity observed for
PDI-1T with a more extended π-conjugated system accounts for the slightly lower electron mobility of 0.1 cm
2 V
−1 s
−1 measured for this system. Regarding naphthalimide-based assemblies, the introduction of the phenylene moiety in
NDI-T-Ph-T enhanced the crystallinity and the presence of well-defined and well-connected smaller grains, allowing mobilities of around 0.1 cm
2 V
−1 s
−1 for electron transport. Finally, the introduction of catenated thiophene units in both
NDI-3T and
PDI-3T decreases their performances in the devices by around two orders of magnitude in agreement with the analyses of AFM images and XRD patterns. In contrast with the analogue with one thiophene unit (
NDI-1T), the introduction of additional thiophene moieties in
NDI-3T produces a twist in the oligothiophene backbone, thus hindering an efficient packing and therefore causing a decrease in the crystallinity of the films. As a result, electron mobilities of only 10
−4 cm
2 V
−1 s
−1 can be measured for these assemblies. In comparison with the naphthalimide containing assembly
NDI-3T, films made from the perylenimide-containing analogue,
PDI-3T, are more crystalline, having larger grains allowing for better charge carrier mobilities up to 10
−3 cm
2 V
−1 s
−1. Solution-processed OTFT transistors were also fabricated, and their morphologies and crystal structures were evaluated. The results obtained for these semiconductors were in good agreement with the new morphologies obtained for each one and, in the case of
PDI-3T, an electrical enhancement was found in comparison with the vapor-deposited thin-film transistors [
12].
It is also worth pointing out that the terthiophene–naphthalimide assemblies (
NDI-3T and
PDI-3T) are suitable for electropolymerization (
Scheme 2) [
10,
19]. Thus, electropolymerization of
PDI-3T generates a functionalized polythiophene with a UV–vis spectrum covering the whole UV–vis region. The polymer has a band gap of 0.9 eV and exhibits ambipolar characteristics, showing high electroactivity in both the
p- and the
n-doping processes [
10]. On the other hand,
NDI-3T can be also electropolymerized to yield a polymer which can store specific charges of 13 mAh g
−1 for polymer oxidation and 38 mA g
−1 for its reduction, which is interesting for fast charge/discharge batteries [
19].
Motivated by the above results [
12], a novel family of naphthalimide–oligothiophene assemblies [
20] (second-generation
NDI-nT) was designed with the aim to avoid the above-described skeletal distortion (
Figure 5).
In order to obtain this second generation of oligothiophene–naphthalimide assemblies, a linear synthetic approach was followed (
Scheme 3) instead of the convergent one used previously [
10,
11,
12]. Thus, a monobrominated thiophene–naphthalimide derivative (
NDI-1T-Br,
Scheme 3) was used as starting material. Stille cross-coupling reactions between
NDI-1T-Br and the corresponding monostannane derivatives
4,
5 and
6 were carried out in order to obtain the target molecules
NDI-2T,
NDI-3Tp and
NDI-4T in good yields [
20]. As depicted in
Scheme 3, the steric repulsion between the oxygen and sulfur heteroatoms is absent in these new organic semiconductors, thus preventing the skeletal distortions. Additionally,
NDI-5T (
Scheme 3) was synthesized for comparison purposes, given that it combines a fragment with the extended π-conjugated structure of
NDI-3Tp and also a fragment with the steric hindrance of
NDI-3T.
NDI-5T was obtained by a Suzuki cross-coupling reaction between
NDI-1T-2Br and the 2,2′−Bithiophene-5-boronic acid pinacol ester (
7).
The UV–vis absorption spectra of this second generation of oligothiophene–naphthalimide assemblies present broad absorption bands above 550 nm, with a significant charge-transfer character. The HOMO/LUMO energy levels for these
NDI-nT materials were estimated from the data collected by cyclic voltammetry [
17,
18]. The LUMO energy levels remain practically unaltered independent of the oligothiophene length, while the HOMO energy levels are more destabilized upon increasing the oligothiophene length. This behavior can be rationalized in terms of the LUMO and HOMO molecular topologies obtained by DFT/B3LYP/6-31G** theoretical calculations. The HOMOs are delocalized over the oligothiophene fragment while the LUMOs are located on the naphthalimide moiety (
Figure 6). The HOMO levels of
NDI-4T and
NDI-5T approach the Fermi level of Au, thus improving the hole injection in electronic devices. Thus, the molecular design used in this strategy allows for the optimization of the
p-type performance of the semiconductors without sacrificing the electron transport, due to the separation of the frontier molecular orbitals.
It is also worth noting that the band gap of the planar
NDI-3Tp (
Figure 5, right) is 0.1 eV smaller than that of the
NDI-3T analogue with a distorted structure (
Figure 5, left). This energy readjustment, in conjunction with other morphological and electronic factors, is probably the origin of the ambipolar behavior shown by
NDI-3Tp.
Thin films of these NDI-nT semiconducting materials were processed from solutions or by sublimation. X-ray analyses of the thin films show that crystallinity is much more pronounced in those films obtained by sublimation. However, solution processed films are also well textured. For all the laterally monosubstituted semiconductors, NDI-2T, NDI-3Tp and NDI-4T, the films obtained are crystalline, with at least three diffraction peaks. The AFM images of these films show small, well-interconnected crystallite domains. For comparison purposes, thin films of NDI-5T were also analyzed. These films exhibit noncrystalline microstructures which were also confirmed by AFM analysis in which only isolated domains were observed. The lack of crystallinity in the NDI-5T films can be ascribed to the presence of the oxygen–sulfur repulsive interaction, which leads to the loss of planarity in the skeleton structure and, from that, to poorly ordered packing.
The most remarkable characteristics of the FET performances of these semiconductors were investigated in TC/BG OFETs (
Table 3). The shortest derivative,
NDI-2T, only shows electron mobilities up to 2.6 × 10
−2 cm
2 V
−1 s
−1. The fact that
NDI-2T only exhibit
n-type mobility values is consistent with the similarity of its HOMO energy level and that of
NDI-1T. In contrast, ambipolarity was found for
NDI-3Tp and
NDI-4T. This ambipolar behavior could be related to: (1) the lack of skeletal distortions that allows close π–π stacking interactions and lower reorganization energies and (2) the presence of longer conjugated oligothiophene moieties with increased π conjugation lengths that allows a destabilization of the HOMO energy levels which approach the Fermi level of Au. For
NDI-3Tp and
NDI-4T, the best performances obtained for solution-processed films, annealed at 90 °C, were 2.01 × 10
−2 cm
2 V
−1 s
−1 and 6.79 × 10
−3 cm
2 V
−1 s
−1 for electrons and holes, respectively. On the other hand, mobilities of 3.15 × 10
−3 cm
2 V
−1 s
−1 and 3.15 × 10
−3 cm
2V
−1 s
−1, for electrons and holes, respectively, were obtained for vapor-deposited films. Interestingly, FETs fabricated using
NDI-5T exhibit ambipolar transport behavior with balanced electron and hole transport mobilities of approximately 10
−5 cm
2 V
−1 s
−1. The study demonstrates that the absence of ambipolarity is mainly due to the disruption in the π conjugation, while a decrease in the carrier mobility is induced by the skeletal distortions. Furthermore, there is a good correlation between the charge transport properties, the film microstructures and the ordered packing of nondistorted structures.
In line with these observations, we envisaged that the presence of an important dipole moment in these types of donor-acceptor assemblies may tend to pack them in an antiparallel way (
Figure 2d), which can prevent suitable HOMO–HOMO overlap between molecules [
12,
20,
21]. As the modulation of dipole moments has been shown to be a key parameter for tuning the electrical performance of organic semiconductors [
21,
22,
23], with the aim to efficiently tune the molecular packing of organic semiconducting materials, we combined our expertise in the syntheses of oligothiophene–naphthalimide assemblies with new strategies based on tuning dipole moments. Thus, we designed a third generation of bis-naphthalimides
2NDI-nT (
Scheme 4) based on a catenated oligothiophene bridge end-capped with
NDI-1T structures [
24]. We investigated the effect of combining two naphthalimide systems with one oligothiophene moiety in the molecular dipole moments and hence in the organic field-effect transistor performances.
Compounds
2NDI-3Ta,
2NDI-3Tb,
2NDI-4T and
2NDI-5T were obtained by Pd-catalyzed Stille cross-coupling reactions between
NDI-1T-1Br and the corresponding bis-stannanes
8,
9 and
10. In addition, dimer
2NDI-2T were synthesized by self-dimerization of
NDI-1T-1Br with bis(tributyltin) in the presence of Pd(PPh
3)
4 (
Scheme 4).
All naphthalimide dimers have similar absorption patterns with bathochromic shifts for the assemblies with longer oligothiophene fragments. As in the previous oligothiophene–naphthalimide assemblies, an intramolecular charge transfer band appears as a consequence of the segregated spatial location of the HOMO and LUMO molecular orbitals. Cyclic voltammetry measurements allow for the detection of tetraanion species due to the presence of two naphthalimide moieties. Moreover, in the case of
2NDI-5T, not only was the formation of tetraanion species observed but also the formation of stable radical dications [
24]. The estimation of the frontier molecular orbital energy levels from the electrochemical data (
Figure 7) shows that there is a destabilization of the HOMO energy level with the catenation. The presence of tetra and pentathiophene in the assemblies approaches the HOMO energy level to the Fermi level of Au, thus favoring the injection of holes and therefore enabling
p-type transport.
In order to analyze the influence of non-negligible molecular dipole moments in the molecular packing, computational studies were carried out. It was found that for 2NDI-2T and 2NDI-4T, with a pair number of thiophene units, the molecular dipolar moments are rather small, and there are negligible energetic differences between antiparallel and parallel dispositions. On the other hand, the semiconductors with an odd number of thiophene rings have non-negligible molecular dipolar moments and there is a stabilization of parallel stacking versus the antiparallel one.
Thin films of the 2NDI-nT semiconducting materials were fabricated by drop casting from chlorobenzene solutions. Wide-angle X-ray diffraction (WAXRD) analyses show that all these 2NDI-nT films are poorly crystalline, while tapping-mode AFM indicates remarkable differences upon annealing treatment. Thus, more favorable morphologies with rounded well-connected grains can be obtained with higher annealing temperatures.
In
Table 4, the most significant characteristics of the FET performances of these semiconductors in TC/BG OFETs are depicted.
2NDI-2T and
2NDI-3T exhibit comparable electron mobilities of 2.5 × 10
−4 cm
2 V
−1 s
−1 and 3.6 × 10
−4 cm
2 V
−1 s
−1, respectively. Regarding
2NDI-4T and
2NDI-5T, ambipolar properties were found. Well balanced hole and electron mobilities of 8.4 × 10
−3 cm
2 V
−1 s
−1 and 1.8 × 10
−3 cm
2 V
−1 s
−1 were found for
2NDI-5T. Interestingly,
2NDI-4T transports electrons more efficiently, while hole transport is more favored for
2NDI-5T. These results are in good agreement with the estimated HOMO and LUMO energy levels. Nevertheless, the changes in the molecular dipole moments could not be directly correlated with the charge carrier mobility values.
3. Inverted Amidine-Based Oligothiophene–Naphthalimide Semiconductors
The lessons learned from the first three series of oligothiophene–naphthalimide assemblies allowed us to conclude that ambipolar semiconductors with these kinds of systems can be obtained by (i) connecting the donor and acceptor moieties through conjugated rigid linkers, (ii) avoiding steric hindrance and skeletal distortions and (iii) extending the effective π-conjugated length of the oligothiophene moiety.
In the search for new low-bandgap materials in which facile hole and electron injection are possible from a single type of electrode, we designed a fourth generation of oligothiophene–naphthalimide assemblies, NAI derivatives (
Figure 8), that involves the inversion of the amidine linkage connections between the oligothiophenes and the naphthalimide in order to prevent steric interactions (
Figure 8) [
25].
As it is depicted in
Scheme 5, for the syntheses of the NAI derivatives, naphthalimide moieties endowed with amino functionalities (
11) and a thiophene derivative endowed with anhydride functionality (
12) were used as starting materials.
Through a condensation reaction between monomers
11 and
12, the dibrominated
NAI-1T-2Br derivative can be obtained. Further reaction of
NAI-1T-2Br by Stille cross-coupling reactions with the corresponding stannylated thiophene
13 or bithiophene
14 yield the target molecules
NAI-3T and
NAI-5T. In terms of the molecular structure, the inversion in the orientation of the carbonyl group in the imidazole unit provides more planar semiconductors, in which the O···S repulsive interaction is deliberately avoided in contrast with that observed in the first generation of oligothiophene–naphthalimide assemblies with noninverted amidine linkers [
12,
20].
The LUMO and HOMO molecular topologies of
NAI-3T and
NAI-5T could be also obtained by DFT/B3LYP/6-31G** theoretical calculations (
Figure 9). It is worth pointing out that, in contrast with the parent
NDI-3T and
NDI-5T derivatives, in the derivatives with the inverted amidine linkers, the HOMO is not localized solely on the oligothiophene fragment, and it is spread over the molecular skeleton. Additionally, in contrast with the NDI derivatives, for
NAI-3T and
NAI-5T, the LUMO orbital is delocalized not only on the naphthalimide moiety but also in the oligothiophene fragment.
Therefore, there is not a clear separation between the location of the HOMO and LUMO orbitals in NAI derivatives and, given this, the HOMO–LUMO transition does not involve a charge-transfer character in contrast with that observed for the parent NDI analogues. Furthermore, the λmax in the UV–vis absorption spectrum for the NAI derivatives displays hyperchromic and hypsochromic shifts in comparison with that of the parent NDI analogues.
Cyclic voltammetry measurements for both
NAI-3T and
NAI-5T present oxidation and reduction processes. From these values, the HOMO and LUMO energy levels could be estimated (
Figure 9).
The LUMO energy levels estimated for the NAI derivatives are significantly destabilized in comparison with those of the NDI analogues, while the HOMO energy levels of both
NAI-3T and
NAI-5T are more stabilized than those corresponding to their NDI counterparts [
12,
20,
24]. The molecular dipole moment is enhanced by about 4.5 times for the NAI derivatives in comparison with that of the NDI analogues, and smaller hole reorganization energies were obtained for the inverted amidines, which is a good indicator of facile charge accommodation.
Finally, in order to evaluate the electrical properties of these new semiconductors, TC/BG field-effect transistors were fabricated by vapor deposition. The
NAI-based films were characterized by WAXRD and AFM. Referring to the crystal packaging, the introduction of inverted amidine in the assemblies leads to more crystalline films in comparison with the amorphous films obtained for the NDI analogues. The high molecular dipole moments of the NAI derivatives reveals a significant tendency for packing with antiparallel orientations [
20,
24]. The AFM images and the X-ray diffractograms of films prepared from
NAI-3T and
NAI-5T show evidence of a high dependence of the morphology and crystallinity of the films with the temperature of deposition. Films obtained by sublimation onto OTS-treated surfaces at 110 °C show larger rod-like crystallites in the case of
NAI-3T, while
NAI-5T shows regular and small interconnected grains, both in good agreement with the diffraction patterns.
The OFET performance obtained for the vapor-deposited films is summed up in
Table 5. In this semiconductor series,
p-type and ambipolar transport properties were found for
NAI-5T and
NAI-3T, respectively. In the shorter member of the series, the electron mobilities are similar to that of the NDI analogues, around 1.9 × 10
−4 cm
2 V
−1 s
−1, with interesting balanced values for hole mobilities of 2.0 × 10
−4 cm
2 V
−1 s
−1 at 25 and 110 °C. Although the outputs for
NAI-5T show clear ambipolarity, only hole-charge transport values of 5.75 × 10
−5 cm
2 V
−1 s
−1 were ultimately measured. The better hole mobility values obtained for
NAI-5T in comparison with the parent
NDI-5T could be related to the HOMO delocalization over the whole molecule, which allows better orbital overlapping between molecules.
The implementation of these D-A semiconductors into polymeric structures [
26] were carried out as depicted in
Figure 10. Due to the avoided O···S repulsive interaction in NAI derivatives, we envisioned more planar structures in the polymers based on this structural moiety. For comparison purposes, we also synthesized NDI-based polymeric analogues where the O···S repulsive interaction is still present.
The polymers could be obtained by Stille cross-coupling reactions between
NAI-1T-2Br (
Scheme 5) or
NDI-1T-2Br (
Scheme 3) and the corresponding thiophene or bithiophene bisstanannes. Due to the low solubility of
poly(NDI-3T) and
poly(NAI-3T) derivatives, alkyl chains were introduced in the bithiophene comonomer to obtain more processable materials, designated as
poly(NDI-8C-3T) and
poly(NAI-8C-3T) (
Figure 10).
The DFT theoretical calculations (
Figure 11) carried out for
poly(NAI-nT) polymers show the lack of significant O···S repulsive interaction, thus yielding to the planarization of the polythiophene backbone in NAI-based polymers. In contrast, in the
poly(NDI-nT) polymers, O···S repulsive interactions are present, disrupting to a certain extent the effective conjugation of the polythiophene backbone.
In the absorption spectra, both poly(NAI-nT) and poly(NDI-nT) derivatives show bathochromic shifts in comparison with the respective molecular analogues due to the extension of the π-conjugated polymer backbones. Absorption in the whole UV–vis spectrum can be observed, extending even to the near infrared region. Cyclic voltammetry measurements of polymers of the NDI series show well-defined redox processes which contrast with the broad waves exhibited by the analogues of the NAI series. This may be due to the rotational torsion of the NDI-based polythiophene backbones due to the O···S repulsive interaction, leading to reduced p orbital overlap. This interruption of the conjugation produces a sequence of oligothiophene–naphthalimide assemblies connected through nonefficiently conjugated regions. This structural motif accounts for the defined redox processes which are characteristic of molecular systems. In contrast, polymers of the NAI series do not have these O···S repulsive interactions, and therefore the polymer backbone can be considered as a conjugated polymer chain with more extended delocalization, thus presenting broad waves which are characteristics of highly delocalized conjugated polymers. The relative nonprocessable nature of the polymers has prevented, until now, the achievement of significant charge carrier mobilities in OFET devices.
4. Pyrazine-Based Oligothiophene–Rylenimide Semiconductors
As it was previously shown, avoiding steric hindrance and skeletal distortions in naphthalimide–oligothiophene assemblies plays a crucial role in the search for ambipolarity. For that reason, we designed a fifth generation of naphthalimide–oligothiophene assemblies in which flat and rigid pyrazine units are used as conjugated linkers (
Figure 12).
Pyrazine-based materials can be obtained by condensation reactions between naphthalene (
NID) or peryleneimides (
PID) endowed with 1,2-diketone functionalities and the corresponding diaminothiophene derivatives (
Scheme 6) [
27,
28].
The molecular geometry of the pyrazine-based derivatives was optimized by DFT/B3LYP/6-31G** theoretical calculations, showing completely planar structures (
Figure 13) [
28,
29]. In
NIP-3T and
PIP-3T, the absence of steric repulsions and the presence of stabilizing S···N interactions favored the coplanarity of the oligothiophene–ryleneimide assemblies. DFT theoretical calculations show that the LUMO is mainly localized over the rylenimide core, as in the amidine-based analogues [
12,
20,
24,
25]. On the other hand, the HOMO distribution depends on the electron-donor fragment catenation, being located over the conjugated thienopyrazine fragment for the
NIP-1T and
PIP-1T semiconductor and spread over the whole oligothiophene fragment in the extended oligothiophene derivatives
NIP-3T and
PIP-3T. As previously mentioned, internal reorganization energies (λ) are related to the capability to stabilize injected charges in the system. The obtained values regarding electron and hole charges revealed that λ
e for NIP derivatives were comparable to those obtained for NDI. Lower values were obtained in terms of intramolecular reorganization energies for hole charge carriers for NIP derivatives (0.43 eV of
NDI-3T vs. 0.25 eV of
NIP-3T), being especially remarkable in the case of
NIP-1Ta, where λ
h was 0.16 eV as a result of the completely planar structure [
29]. The extension of the π-conjugated system provides even lower internal reorganization energies for both electron and hole transport, highlighting the case of
PIP-1Ta with λ
e and λ
h of 0.25 and 0.11 eV, respectively [
28].
The absorption spectra of
NIP-3T show two absorption bands, in which the lowest energy absorption is centered at 570 nm and can be ascribed to an ICT excitation, similar to that found for most of the above generations of oligothiophene–naphthalimide assemblies [
12,
20,
24,
25,
29]. This one-electron HOMO–LUMO excitation was also observed in
PIP-3T as a broad absorption band centered at 668 nm with an onset value above 900 nm. Moreover, the characteristic absorption pattern for the perylenimide core is found at 507 and 545 nm, corresponding, respectively, to 0–0 and 0–1 vibronic bands of the S0–S1 transition, and at 476 nm for the S0–S2 transition. The observed differences in the UV–vis spectra were related to the different π-extended structures of the rylenimide-fused thienopyrazine derivatives. Furthermore, the introduction of different alkyl or phenylene chains at the imide group has no significant effect on their optical properties [
28].
In order to study the electrochemical properties of these planar pyrazine-based assemblies, cyclic voltammetry experiments were carried out, and from the obtained electrochemical values, frontier molecular orbital energies could be estimated. As we previously described, oligothiophene chain catenation had an important effect on the HOMO energy, showing destabilized values as the oligothiophene grows, whereas LUMO energies were barely altered [
20,
24]. The lowest unoccupied molecular orbital energy levels depend on the extension of the rylenimide units. Thus, the estimated LUMO values for
NIP-1T and
PIP-1T are −3.40 eV and −3.49 eV, respectively. Regarding the oligothiophene counterpart, an increment in the number of the thiophenes has a negligible effect in the LUMO level, while this chemical modification clearly affects the HOMO energy levels, and therefore the optical band gap. The HOMO energy level estimated for
PIP-1T (−5.34 eV) is significantly stabilized in comparison to that estimated for
PIP-3T (−4.75 eV). The destabilization of the HOMO observed for
PIP-3T is in good agreement with the extension of the thiophene backbone and with the absorption spectra. Therefore, in these pyrazine-based semiconductors, tuning the HOMO–LUMO bandgap can be achieved by two approximations: (i) by extending the rylenimide core without modifying the donor moiety and (ii) through the increment in the length of the oligothiophene backbone. Comparison between the HOMO and LUMO energy levels of the NIP and PIP semiconductors and those of the NDI and PDI analogues reveals that the replacement of the imidazole linker by a rigid pyrazine heterocycle is reflected in more destabilized HOMO and LUMO orbitals, as well as in the enlargement of the band gap (
Table 6) [
28,
29].
As a common evaluation of the electrical properties for these pyrazine-based oligothiophene–rylenimide derivatives, the fabrication of TC/BG thin-film organic field-effect transistors was accomplished. Moreover, the thin films obtained for all the semiconductors measured were also studied by AFM and XRD analyses. AFM analysis of
NIP-1T,
NIP-3T,
PIP-1T and
PIP-3T (
Figure 14) reveals a strong dependence of the deposition temperature on the microstructure domains, doubling the grain size in the case of
NIP-1T when the temperature is increased from 25 °C. Interestingly, for
PIP-3T, large rod-like grain crystallites were observed, as was the case for the naphthalene analogue
NIP-3T. In addition, the effect of the imide substitution was evaluated by comparing the AFM images of
PIP-1Ta and
PIP-1Tb, which revealed that the presence of the phenyl units enhances the formation of well-rounded grains as a result of a better connectivity and order. The thin-film microstructures of
NIP-3T were compared with those of the amidine-based analogues,
NDI-3T and
NDI-3Tp, because of their structural similarities. By using wide-angle X-ray diffraction (WAXRD) techniques, we observed that films of
NDI-3Tp and
NIP-3T are relatively crystalline, while those of
NDI-3T were essentially amorphous. Nevertheless, the crystallinity of
NDI-3Tp is the highest, showing Bragg reflections up to the sixth order.
Concerning the charge transport ability of these thienopyrazine derivatives, all of them showed
n-type mobilities, with the best electron mobility value of 2.87 × 10
−4 cm
2 V
−1 s
−1 for
NIP-1T when it was deposited at 50 °C on HMDS-treated dielectric (
Table 7).
NIP-3T is the only thienopyrazine derivative that showed ambipolar behavior, with good balanced values for both hole and electron charge carriers. This effect is related to the high planar structure and low internal reorganization energies, enabling both electron and hole transport processes. The same behavior could be expected for
PIP-3T, but only discrete n-type mobility was observed (1.2 × 10
−4 cm
2 V
−1 s
−1). This result could be explained in terms of the formation of antiparallel π–π stackings among the molecules when they were vapor deposited over the dielectric, restricting the formation of the D and A domains necessary for the hole and electron transporting. This aggregation behavior is in good agreement with the predicted computational study for dimeric species [
28].
The above studies presented for the different generations of oligothiophene–naphthalimide assemblies show that there is an important effect of the crystalline structure as well as of the thin-film microdomains on the charge transport properties. In this regard, the tuning of the supramolecular packing has proven to be critical to obtain proper spatial arrangements of the donor-acceptor assemblies where heterojunctions are clearly segregated into donor and acceptor channels, promoting efficient charge transport. This strategy was firstly addresses by the introduction of hydrophilic or hydrophobic termini side chains in order to promote different self-assembled domains in the previously reported
NIP-3T core [
29,
30]. Thus, we envisaged that the formation of highly ordered aggregates is more probable for
NIP-3Tamphi bearing hydrophobic chains at the imide nitrogen and ethylene glycol hydrophilic chains on the oligothiophene moiety than in the case of the semiconductor with hydrophobic alkyl chains at both ends, namely
NIP-3Tlipo. As it is depicted in
Scheme 7, the syntheses of these new derivatives based on oligothiophene–naphthalimide assemblies were carried out following the convergent method previously described for these materials [
28,
29].
In order to study the (opto)electronic properties of these novel materials, cyclic voltammetry and UV–vis absorption measurements were carried out, and all values are summarized in
Table 8. The HOMO/LUMO energy levels estimated by the electrochemical measurements are practically identical in both assemblies, with similar values of the LUMO and negligible differences in the HOMO due to the presence of different termini-side chains on the oligothiophene moiety. Concerning the absorption properties, both materials have similar absorption profiles in comparison with the unfunctionalized
NIP-3Ta semiconductor. The UV–vis absorption spectra of both
NIP-3Tlipo and
NIP-3Tamphi show bathochromic shifts when the absorption is measured in thin films, thus indicating considerable aggregation behavior for both materials.
Interestingly, when the absorption measurements are carried out in THF/H
2O solvent mixtures, some differences were observed. When the THF/H
2O ratio varies from 100/0 to 60/40, the
NIP-3Tlipo absorption profile remains unaltered, while in the case of
NIP-3Tamphi, the lower energy absorption is redshifted and the spectra become similar to that obtained for the thin film, which suggests the formation of supramolecular aggregates. To further study the different tendency toward aggregation of these assemblies, hexane solutions were prepared for both
NIP-3Tamphi and
NIP-3Tlipo. Upon heating at 60 °C and subsequent cooling at 25 °C, a clear solution was obtained for
NIP-3Tlipo. In contrast, by performing the same thermal treatment, a suspension resulted for
NIP-3Tamphi. After drying the suspension, analysis by scanning electron microscopy (SEM) showed the formation of microfibers longer than 20 μm with a high aspect ratio (
Figure 15). By using good solvent/bad solvent mixtures it was also possible to grow micrometer-sized rods of
NIP-3Tlipo (
Figure 15). Analysis of the SEM images of both assemblies allows us to conclude that the microstructures formed are significantly different due to the different substitution pattern.
To rationalize the different nanostructure growth for these materials, DFT calculations at CAM-B3LYP level were used to predict the more stable dimeric aggregates for each semiconductor. This functional predicts that parallel disposition is the most stable of the two possible conformations for
NIP-3Tamphi, as it confirms the interaction energy values depicted in
Figure 16, due to the presence of attractive interactions between the ethylene glycol end moieties. On the contrary, the presence of aliphatic alkyl chains in the terthiophene moiety has less impact in the conformational stabilization, being only 1 kcal/mol more stabilized the antiparallel model, as it was previously described for other oligothiophene–naphthalimide assemblies [
12].
Finally, the charge carrier mobilities of
NIP-3Tamphi and
NIP-3Tlipo were analyzed using time of flight (TOF) techniques [
31,
32]. Remarkably, it was found that both materials show ambipolar characteristics as it was previously described for the
NIP-3T analogue. Interestingly, it can be observed that the introduction of self-assembled directors leads to higher electron and holes mobilities for
NIP-3Tamphi (4.3 × 10
−6 cm
2 V
−1 s
−1 and 2.1 × 10
−6 cm
2 V
−1 s
−1) in comparison with those measured for
NIP-3Tlipo (1.3 × 10
−7 cm
2 V
−1 s
−1 and 6.9 × 10
−8 cm
2 V
−1 s
−1).
To further explore the possibility of tuning the performance of this type of material in (opto)electronic devices, we designed a family of oligothiophene–naphthalimide assemblies based on pyrazine linkers in which end-capped units were introduced in order to promote good packing in the molecule while the HOMO/LUMO energy levels are still suitable for semiconducting applications [
33].
These new thienopyrazine-based semiconductors are endowed with different substituents in order to promote molecular ordering, better processability and tuning of the frontier molecular orbitals. These oligothiophene–naphthalimide assemblies can be divided into different groups depending on the nature of the end-capped units introduced: (i) substituents that promote intermolecular interactions and (ii) different electron acceptors in order to modulate the HOMO/LUMO energy levels. Thus, there are three end-capped derivatives functionalized with pyrene, triisopropilsilyl and diphenylamine with a donor-acceptor-donor (
D-A-D) structure (
Scheme 8). On the other hand, the introduction of electron acceptor substituents via Knoevenagel-like reactions led to obtaining
A2-D-A1-D-A2 semiconductors endowed with rhodanine and dicyanovinylene end groups (
Scheme 9).
The optimization of the most stable molecular structures for these thienopyrazine-based semiconductors shows completely planar structures for the central unit, as it was previously described for the
NIP-3T core [
28,
29]. When nonbulky electron-acceptor groups are introduced in the molecular structure, such as in
NIP-3T-Rd and
NIP-3T-DCV, the assemblies remain coplanar and fully conjugated. In contrast, when bulky structures are introduced into the terminal positions of the oligothiophene, such as in
NIP-3T-TA and
NIP-3T-Py, they adopt noncoplanar configurations. Furthermore, to study the effect of the different substituents at the alpha positions of the thiophene units, DFT calculations were carried out to predict the most favorable dimeric conformations for these new assemblies. In the abovementioned studies [
28,
29], we demonstrated that for the
NIP-3T core, the parallel and antiparallel dimeric conformations are quasi-isoenergetic. In contrast, when end-capped derivatives are introduced at the terminal positions, it can be observed that the most stable conformations are the parallel ones. In the case of
NIP-3T-Rd and
NIP-3T-DCV, this behavior is due to the dipole moments of these molecules. For
NIP-3T-Py, although the substituents are spatially out of the
NIP-3T plane, close and cooperative π–π interactions also promote the parallel stacking configuration (
Figure 17).
The optical and electrochemical properties of the D-A-D and A2-D-A1-D-A2 assemblies have been compared to those of the
NIP-3T building block (
Table 9 and
Table 10). For
NIP-3T-TA,
NIP-3T-TIPS and
NIP-3T-Py, the substitution with electron-rich units just redshifted the lowest energy band of the UV–vis absorption spectra. The decrease in the optical bad gap is mainly due to a destabilization of the HOMO levels, without significant modification of the LUMO energy level. In contrast, when the end-capped groups introduced at the terminal position of the oligothiophenes are strong electron acceptors, as in the case of
NIP-3T-Rd and
NIP-3T-DCV, the absorption spectra dramatically change. This substitution pattern allows for the formation of more extended π-conjugated systems, which is translated into an enhanced absorption cross section that extends through the whole visible range. Moreover, the topologies of the HOMO and LUMO levels of the A2-D-A1-D-A2 assemblies are different from those of the
NIP-3T core. Thus, for the A2-D-A1-D-A2 assemblies, frontier molecular orbitals are delocalized over the oligothiophene backbone (
Figure 18), being more stabilized than in the unsubstituted analogue.
The electrical characterization of these new semiconductors was carried out in organic field-effect transistors with TC/BG architectures. The thin films deposited by vapor deposition were also characterized by XRD and AFM techniques. As previously shown,
NIP-3Tb has ambipolar characteristics, with balanced holes and electron mobility values of 4 × 10
−5 cm
2 V
−1 s
−1. The introduction of lateral substituents modifies the polarity in the charge transport properties, as it was shown for
NIP-3T-TIPS, in which only
p-type characteristics were found. On the other hand, when pyrene moieties are introduced laterally in the
NIP-3T-Py derivative, electron mobilities of 10
−2 cm
2 V
−1 s
−1 were found, the best of all these semiconductors (
Table 11). In contrast, when electron-withdrawing groups are introduced, only n-type mobilities were observed, except in the case of
NIP-3T-Rdb in which ambipolarity is observed (
Table 11). The different behavior observed for the end-capped oligothiophene–naphthalimide semiconductors can be also related to the limited crystallinity observed in XRD and AFM images. It is worth pointing out that, given the suitable HOMO and LUMO energy levels, as well as good processability and full absorption range even in the NIR spectra of the oligothiophene–naphthalimide assemblies endowed with electron-acceptor units, they have also recently received some attention as nonfullerene acceptors in OSCs [
33].
As it was previously mentioned, the implementation of conjugated molecular assemblies into polymeric materials has proven to be an efficient strategy to develop new semiconductors for a wide variety of applications [
34,
35,
36,
37]. Among them, the development of metal-free, organic polymers as photocatalysts [
38] for the removal of hazardous contaminants [
39,
40] has been revealed as an emerging area in the last decade.
In this regard, molecular- and polymeric-conjugated assemblies with wide absorption cross-section characteristics are good candidates as photocatalysts. Moreover, it is known that materials which combine electron donor and electron acceptor units are also interesting in photocatalysis because fast recombination processes may be inhibited. The possibilities offered by the oligothiophene–naphthalimide assemblies to efficiently tune their optical and electronic properties as well as their suitability to be functionalized at the α positions of the oligothiophene moieties make these types of assemblies good candidates to be used as monomers for the syntheses of donor-acceptor polymeric materials suitable for the photocatalytic degradation of organic pollutants in water [
41].
As it is depicted in
Scheme 10, the synthesis of the poly(azomethine) network
NIP-3T-ANW is consummated by a Schiff-base condensation reaction between linear disubstituted oligothiophene–naphthalimide aldehyde
NIP-3T-CHOb [
33] with a trigonal monomer endowed with amine functional groups
TAPB [
42] under solvothermal reaction conditions [
43]. Interestingly, this polymeric material shows high thermal stability, without noticeable weight loss up to 450 °C, in contrast with the
NIP-3T molecular semiconductor in which the degradation starts at 200 °C. Regarding its optoelectronic properties, this material shows solid state absorption in the whole UV–vis spectrum, extending even up to 1200 nm in the NIR. In addition to its good light harvesting properties, an efficient electron-hole dissociation can be expected for
NIP-3T-ANW due to the presence of the donor-acceptor units. Furthermore, the material exhibits a good energy band alignment for the photodegradation of some organic pollutants, such as rhodamine B (
RhB). Due to the above characteristics, the potential of
NIP-3T-ANW as photocatalyst in the photodegradation of
RhB has been investigated. It is known that RhB is stable in aqueous solution under illumination in the absence of catalyst. In contrast, when
NIP-3T-ANW is added, after 120 min, almost a 90% of
RhB is degraded in the aqueous solution, and no stability problems in the catalyst are detected after four catalytic cycles. For comparison purposes, the photocatalytic activity of the analogue molecular component
NIP-3T has been also investigated, showing only a 55% degradation of RhB in the same time period. Thus, the incorporation of the D-A unit into the polymeric network dramatically increases its activity and allows for its recyclability without losing efficiency, as shown in
Figure 19.