Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 12
Issue 15
10.3390/nano12152717
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Photocatalytic Hydrogen Production from Aqueous Solutions of Glucose and Xylose over Layered Perovskite-like Oxides HCa2Nb3O10, H2La2Ti3O10 and Their Inorganic-Organic Derivatives

by
Sergei A. Kurnosenko
,
Vladimir V. Voytovich
,
Oleg I. Silyukov
*,
Ivan A. Rodionov
and
Irina A. Zvereva
Department of Chemical Thermodynamics and Kinetics, Institute of Chemistry, Saint Petersburg State University, 199034 Saint Petersburg, Russia
*
Author to whom correspondence should be addressed.
Nanomaterials 2022, 12(15), 2717; https://doi.org/10.3390/nano12152717
Submission received: 14 July 2022 / Revised: 3 August 2022 / Accepted: 6 August 2022 / Published: 7 August 2022
(This article belongs to the Special Issue Heterogeneous Photocatalysts Based on Nanocomposites)
Browse Figures
Versions Notes

Abstract

:
Nowadays, the efficient conversion of plant biomass components (alcohols, carbohydrates, etc.) into more energy-intensive fuels, such as hydrogen, is one of the urgent scientific and technological problems. The present study is the first one focused on the photoinduced hydrogen evolution from aqueous D-glucose and D-xylose using layered perovskite-like oxides HCa2Nb3O10, H2La2Ti3O10, and their organically modified derivatives that have previously proven themselves as highly active photocatalysts. The photocatalytic performance was investigated for the bare compounds and products of their surface modification with a 1 mass. % Pt cocatalyst. The photocatalytic experiments followed an innovative scheme including dark stages as well as the control of the reaction suspension’s pH and composition. The study has revealed that the inorganic−organic derivatives of the layered perovskite-like oxides can provide efficient conversion of carbohydrates into hydrogen fuel, being up to 8.3 times more active than the unmodified materials and reaching apparent quantum efficiency of 8.8%. Based on new and previously obtained data, it was shown that the oxides’ interlayer space functions as an additional reaction zone in the photocatalytic hydrogen production and the contribution of this zone to the overall activity is dependent on the steric characteristics of the sacrificial agent used.

1. Introduction

Plant biomass is one of the oldest and widely used sources of renewable energy. The latter is accumulated during photosynthesis, when plants convert the solar radiation into the energy of chemical bonds in organic compounds. Thus, targeted cultivation of plants for biomass can be considered a form of solar energy storage. Nevertheless, direct combustion of the plant biomass or its processing products does not appear to be sufficiently expedient because of their relatively low calorific value [1] and the release of carbon dioxide. With that said, there is particular interest in the biomass reforming to obtain more energy-intensive and environmentally friendly fuels such as hydrogen [2,3].
Currently, heterogeneous photocatalysis is being actively explored as a promising energy-saving method for hydrogen production from various sorts of organic raw [4]. In particular, the widely used sacrificial agents are primary alcohols (first of all, methanol) and amino alcohols (triethanolamine) [5,6]. However, these substances are not the only products of plant biomass processing. The other compounds to be reformed are carbohydrates, but significantly less attention is paid to their conversion into hydrogen fuel.
Nowadays, typical heterogeneous photocatalysts for carbohydrates reforming are composite materials on the basis of wide-gap semiconductor oxides (predominantly, TiO2 [7,8,9,10,11] as well as perovskites LaFeO3 [12,13]), sulfides (Zn1−xCdxS [14], CdS/MoS2 [15,16]), tungstates (BiWO6 [17]), and metal-free compounds (g-C3N4 [18,19,20]). They were tested in relation to light-driven hydrogen production from glucose [21], xylose [22], fructose [23], sucrose [24], cellulose [25,26], and lignocellulose [27]. Further optimization of the hydrogen production conditions [28] as well as the creation of hybrid reactors, combining the hydrolysis of polysaccharides and their photocatalytic reforming [29], allowed making significant progress in this field. However, the photocatalytic activity, sufficient for the wide industrial use, has not been achieved yet, which justifies the development of new, more efficient materials.
A promising class of heterogeneous photocatalysts for hydrogen production is represented by ion-exchangeable layered perovskite-like oxides. Their crystal structure is formed by negatively charged perovskite layers of BO6 octahedra, alternating regularly with interlayer spaces occupied by cations. Ion-exchangeable layered perovskites are classified into two structural types: the Dion−Jacobson phases A′[An−1BnO3n+1] and the Ruddlesden-Popper ones A′2[An−1BnO3n+1], where A′ is the interlayer alkali cation, A is the alkaline earth or transition cation, and B is Ti, Nb, etc.) [30,31,32]. Outstanding photocatalytic properties of these oxides and their protonated forms (A′ = H) appear to be due to the unique structure of the perovskite octahedron BO6, providing efficient separation of photogenerated charge carriers, and active involvement of the interlayer space in intercalation and ion exchange reactions [33,34,35,36,37,38,39,40,41,42], including probable penetration of reactant molecules into this zone during photocatalytic processes [43,44]. The main approaches to the further improvement of layered perovskites’ photocatalytic performance are known to be partial ionic substitution (doping) in the perovskite octahedra [45,46,47,48,49], preparation of composites with solid cocatalysts and photosensitizers [50,51,52,53,54,55,56,57], creation of Z-schemes [58,59,60,61,62], sensitization with organic dyes [63], as well as exfoliation into separate nanolayers [64].
One of the key features of protonated layered perovskite-like oxides is their pronounced reactivity with respect to some organic compounds. This allows forming hybrid inorganic−organic derivatives, consisting of the layered inorganic matrix and organic modifiers, chemically anchored to the interlayer space via oxygen vertices of the perovskite octahedra [65,66,67]. Two key approaches to the synthesis of such hybrid materials are intercalation of organic bases [68,69,70] and esterification-like grafting of alcohols [71,72,73], carbohydrates [74], alkoxysilanes [75], and organophosphorus acids [76]. Despite the wide range of inorganic−organic derivatives synthesized, until recently, any data on their photocatalytic activity towards hydrogen production have been practically absent due to probable concerns about their stability under operating conditions [77]. However, our recent studies [78,79,80,81] have shown that oxides HCa2Nb3O10 and H2Ln2Ti3O10 (Ln = La, Nd), preliminarily modified by interlayer n-alkylamines and n-alkoxy groups, demonstrate outstanding photocatalytic performance with regard to light-driven hydrogen evolution from aqueous methanol in the near-ultraviolet range. Particularly, these inorganic−organic derivatives were found to be up to 117 times more active than the unmodified oxides and provide apparent quantum efficiency of more than 40% after additional surface platinization. Despite the fact that the interlayer organic modifiers experienced partial or, in some cases, even complete degradation upon photocatalysis, the activity of the samples was maintained throughout the whole measurement time, and hydrogen was proven to evolve from the reaction solution, not from the sample material. With that said, the photocatalytic behavior of organically modified layered perovskites appears to be an interesting and promising research direction. Particularly, of special interest is the applicability of these materials to hydrogen production from other biomass components, such as carbohydrates.
This paper presents the results of the investigation of layered perovskites HCa2Nb3O10, H2La2Ti3O10, and their organically modified derivatives as photocatalysts for the conversion of aqueous D-glucose and D-xylose into hydrogen for the first time. The choice of particular inorganic−organic derivatives for photocatalytic tests was based on the results of our previous studies [78,79,80,81]: for each oxide, we selected one n-alkylamine and one n-alkoxy derivative that demonstrated the highest efficiency of hydrogen evolution from aqueous methanol with a Pt cocatalyst (n-butylamine and ethoxy derivatives of HCa2Nb3O10, ethylamine and ethoxy ones of H2La2Ti3O10). This study also pays special attention to the influence of Pt reduction conditions on the photocatalytic activity as well as to the role of the oxides’ interlayer space in the hydrogen generation reactions.

2. Materials and Methods

2.1. Synthesis of Initial Protonated Oxides

Alkaline layered perovskite-like oxides KCa2Nb3O10 (KCN3) and K2La2Ti3O10 (KLT3) were synthesized in accordance with the conventional ceramic method using preliminarily calcined Nb2O5, CaO, TiO2, La2O3, and K2CO3 as reactants (Vekton, Saint Petersburg, Russia). The oxides were weighed in stoichiometric amounts, and potassium carbonate was taken with a 30% excess to compensate for the loss during calcination. To prepare the reaction mixture, the reactants were placed into a grinding bowl with silicon nitride balls and ground under an n-heptane layer in a Fritsch Pulverisette 7 planetary micro mill (Fritsch, Idar-Oberstein, Germany) at a rotation speed of 600 rpm, using a program of 10 repetitions of 10 min each separated by 5 min intervals. The mixture obtained was dried and pelletized into ~2 g tablets at a pressure of 50 bar using an Omec PI 88.00 hydraulic press (Omec, Certaldo, Italy). Then, the tablets were placed into corundum crucibles with lids, calcined in a Nabertherm L-011K2RN muffle furnace (Nabertherm GmbH, Lilienthal, Germany) and, after cooling down, ground in an agate mortar. The temperature program of KCN3 synthesis consisted of two stages (800 °C for 12 h and 1100 °C for 24 h) with intermediate grinding and re-pelletizing. KLT3 was prepared via one-stage heating (1100 °C for 12 h).
To obtain the protonated niobate HCa2Nb3O10∙yH2O (HCN3), the KCN3 powder was treated with 12 M nitric acid at a ratio of 100 mL per 5 g of the sample at 25 °C for 1 day. After this, the product was centrifuged, thoroughly rinsed with water to remove acid residues and dried under ambient pressure. To avoid dehydration, HCN3 was further stored in an atmosphere of humid air. To prepare the protonated titanate H2La2Ti3O10 (HLT3), the KLT3 powder was kept in the atmosphere of humid air for 1 day. The hydrated alkaline titanate obtained was then treated with water at a ratio of 200 mL per 1 g of the sample for 1 h, centrifuged and stirred in 0.1 M hydrochloric acid, taken at the same ratio, for 1 day. Then, the final product was separated via centrifugation in a laboratory centrifuge ELMI CM-6MT (ELMI, Riga, Latvia) and dried in a desiccator over CaO for 2 days.

2.2. Synthesis of Inorganic−Organic Derivatives

The organic modification of the protonated oxides was performed in accordance with the methods developed and optimized in our previous reports [79,80,81].
To prepare the n-butylamine derivative HCN3×BuNH2 of the niobate, 0.25 g of HCN3, 9 mL of n-butylamine (Chemical line, Saint Petersburg, Russia), and 1 mL of distilled water were mixed in a sealed tube and stirred at 25 °C for 1 day. The ethoxy derivative HCN3×EtOH was synthesized under solvothermal conditions. For this, 1 g of HCN3 was mixed with 35 mL of a 96% azeotropic aqueous ethanol solution in a sealed PTFE vessel that than was inserted into a steel laboratory autoclave and, after intense shaking, kept at 100 °C for 7 days.
Ethylamine HLT3×EtNH2 and ethoxy HLT3×EtOH derivatives of the titanate were synthesized according to the strategy of successive replacement of some organic modifiers by others, since direct synthesis of the required samples in a pure single-phase state did not appear possible. HLT3×EtNH2 was prepared using the methylamine derivative HLT3×MeNH2 as a precursor, which, in turn, was obtained from the protonated titanate. For this, 1 g of the protonated sample was placed into a glass tube with 30 mL of 38% aqueous methylamine (Chemical line, Saint Petersburg, Russia), whereupon the mixture was sonicated on an ultrasonic homogenizer Hielscher UP200St (Hielscher, Teltow, Germany) at a half power for 5 min. Then, the tube was sealed, and the suspension was stirred at 60 °C for 10 days. The methylamine precursor was filtered, mixed with 30 mL of 70% aqueous ethylamine (Merck, Darmstadt, Germany) and stirred 25 °C for 1 day to obtain the target ethylamine derivative HLT3×EtNH2. The ethoxy derivative HLT3×EtOH was prepared on the basis of the n-butylamine precursor HLT3×BuNH2, which, in turn, was synthesized via a 1 day stirring of 1 g of the methylamine one in a 90% aqueous n-butylamine solution at 25 °C. One gram of the n-butylamine sample was mixed with 35 mL of a 96% azeotropic aqueous ethanol solution in a sealed polytetrafluoroethylene (PTFE) vessel that then was inserted into a steel laboratory autoclave and, after intense shaking, kept at 180 °C for 7 days.
All the final products were filtered and rinsed with acetone to remove residual organic reactants adsorbed on the surface. The synthesis conditions described are summarized in Table 1.

2.3. Investigation of Photocatalytic Activity

Photocatalytic activity was studied with respect to light-driven hydrogen production from 1 mol. % solutions of D-glucose and D-xylose in water for both bare samples and products of their modification with a 1% Pt cocatalyst under near-ultraviolet irradiation. The measurements were performed on the laboratory photocatalytic setting used in our previous reports [78,79,80,81] and described in detailes in Supporting Information Figure S1. The hydrogen formation rate ω, apparent quantum efficiency ϕ, and multiplicity of increase in the rate after Pt loading (platinization increase factor kPt) were chosen as quantitative indicators of the photocatalytic performance. The method for calculation ϕ is presented in Supporting Information Figure S2. Before the photocatalytic tests, the direct photolysis of the aqueous carbohydrates was investigated via their irradiation through a light filter in the absence of a catalyst and the detection of hydrogen evolved.

2.3.1. Testing the Activity of Bare Samples (No Cocatalyst)

To prepare the reaction suspension, 0.03 g of the sample were placed in a round-bottom flask containing 60 mL of 1 mol. % aqueous D-glucose or D-xylose. The flask was sealed, shaken and sonicated in an Elmasonic S10H bath (Elma, Singen, Germany) for 10 min. After this, 54 mL of the suspension obtained were pumped into the reaction compartment of the cell followed by turning on a magnetic stirrer, a light filter, a lamp, and an argon flow through the suspension. After 15 min, 4 mL of the suspension was taken from the cell to establish an actual volume concentration of the sample and pH of the medium before the photocatalytic measurement (c1, pH1). After 15 min, an argon purging of the reaction compartment was turned off, and the photocatalytic measurement, consisting in chromatographic analysis of the gaseous phase every 15 min, was conducted for 2 h. Afterwards, the lamp was turned off to organize a 45 min dark stage and monitor the potential activity of the sample in the absence of irradiation. Thereafter, 4 mL of the suspension were sampled to determine the volume concentration of the sample and pH of the medium at the end of the photocatalytic measurement (c2, pH2). After this, 30 mL of the residual suspension were centrifuged at a separation factor F = 1000 for 1 h to precipitate bulk particles and analyze the liquid phase composition (pH3).

2.3.2. Testing the Activity of Pt-Loaded Samples

Two ways of surface platinization were investigated: in situ Pt reduction in a 1 mol. % aqueous carbohydrate and preliminary reduction in 1 mol. % aqueous methanol. In the first case, 53 mL of the initial suspension in a carbohydrate were pumped into the reaction compartment. Fifteen minutes after turning on the stirrer, the light filter, the lamp, and argon, 1.1 mL of the 2.56 mM H2PtCl6 aqueous solution were injected into the reaction suspension to perform the photocatalytic platinization of the sample’s surface. The solution volume was calculated to provide the mass fraction of Pt in the photocatalyst of 1% assuming its full reduction. In the second case, the sample was initially dispersed in 53 mL of 1 mol. % aqueous methanol, platinized as described above, separated via filtering and then redispersed in a 1 mol. % carbohydrate.
The products of the direct in situ platinization were further designated as “sample/Pt” and those of the platinization in methanol as “sample/Pt(MeOH)”. In the study of all the platinized samples, the gas phase was analyzed every 5 min, and the dark stage duration was 20 min. Other experimental conditions and procedures were the same.

2.4. Instrumentation

2.4.1. XRD

Powder X-ray diffraction (XRD) analysis of the samples was performed on a Rigaku Miniflex II benchtop diffractometer (Rigaku, Tokyo, Japan) using CuKα radiation, an angle range of 2θ = 3°–60°, a scanning rate of 10°/min, and a step of 0.02°. The lattice parameters in the tetragonal system were calculated on the basis of all the diffraction peaks observed using the DiffracPlus Topas 4.2 software (Bruker, Karlsruhe, Germany).

2.4.2. Spectrophotometry

Spectrophotometric analyses of the photocatalytic suspensions were performed on a Thermo Scientific Genesys 10S UV–Vis spectrophotometer (Thermo Fisher Scientific, Waltham, MA, USA). Measurements were conducted in the range of optical density A of <2 using 1 mol. % aqueous D-glucose or D-xylose for dilution and baseline recording. Actual volume concentrations of the samples (c1, c2) were calculated by means of previously built calibration plots (Supporting Information Figure S3).

2.4.3. pH Measurement

The pH values of a reaction suspensions’ medium were determined using a laboratory pH-meter Toledo SevenCompact S220 (Mettler-Toledo GmbH, Greifensee, Switzerland) equipped with an InLab Expert Pro-ISM electrode.

2.4.4. Other Methods of Analysis

The comprehensive characterization of the samples in question by means of Raman spectroscopy, 13C nuclear magnetic resonance (13C NMR), diffuse reflectance spectroscopy (DRS), thermogravimetry (TG), elemental CHN analysis, scanning electron microscopy (SEM), and Brunauer–Emmett–Teller method (BET) is presented in our previous reports [78,79,80,81].

3. Results and Discussion

3.1. Characterization of the Protonated Oxides and Their Inorganic−Organic Derivatives

The initial protonated oxides HCN3 and HLT3 as well as their alkylamine and alkoxy derivatives were identified by means of powder XRD analysis (Figure 1). The indexing of the patterns has revealed the successful synthesis of all the target compounds in a pure form without perceptible by-phases. Although the organic modification proceeded as a topochemical reaction (occurring with the preservation of the layered perovskite structure in general), the derivatives obtained were new individual crystalline phases, which caused the differences in the XRD patterns as compared to the initial materials. The main transformations observed from the XRD data were the expansion of the interlayer space by the organic components being inserted and change in the conformation (relative arrangement) of adjacent perovskite slabs during the formation of some derivatives. The aforementioned expansion of the layered structure along the c crystallographic axis is seen from the low-angle shift of the (00x) reflections and the corresponding increase in the c lattice parameter and interlayer distance d (Table 2), which is measured between the centers of adjacent perovskite layers. The perovskite conformation change may be predicted based on the different relation between c and d values in the initial oxide and its derivative. For instance, HCN3, HCN3×BuNH2, and HLT3×EtNH2 appeared to exist in an eclipsed conformation (without a relative shift of adjacent perovskite slabs, c = d), whilst HLT3, HLT3×EtOH, and HCN3×EtOH were probably stacked in a staggered conformation (with a relative shift of the slabs along lateral axes by a/2, c = 2d). Thus, the relative arrangement of adjacent perovskite slabs, apparently, changed in the course of ethanol grafting into the niobate and ethylamine intercalation into the titanate. At the same time, positions of some reflections, such as (110), (010), and (020), and the a lattice parameter hardly experienced perceptible changes upon the organic modification pointing to the preservation of the perovskite layer structure.
As shown in our previous reports [78,79,80,81], the alkylamine derivatives synthesized represented inorganic−organic intercalates with alkylammonium cations, associated with interlayer oxygen anions, and the alkoxy ones were those with organic chains grafted covalently to the perovskite matrix. In addition to the organic modifier, all the derivatives also contained some amounts of interlayer water (Table 2). Despite the aforementioned interlayer expansion, the bandgap energy of the inorganic−organic samples hardly differed much from that of the initial protonated oxides, since energy bands of the materials in question are known to be formed by the atoms of perovskite octahedra [82]. Thus, the operation ranges of both protonated and organically modified oxides were near ultraviolet. Taking into account the DRT-125 lamp spectrum (Supporting Information Figure S4), the differences in the long-wavelength absorption edge of HLT3, HCN3, HCN3×BuNH2, and HCN3×EtOH samples (Table 2) cannot be a weighty reason for those in their photocatalytic performance, since the lamp did not have emission bands in the range of 343–360 nm. The red absorption edges of HLT3×EtNH2 (366 nm) and HLT3×EtOH (364 nm) were located near an intense lamp peak at 365 nm, which could cause a higher photocatalytic activity of these samples due to a greater amount of available light. However, since the 365 nm emission peak coincided with the optical absorption edge of the samples, the quantum yield of the photocatalytic reaction at this wavelength was scarcely high. With that said, the possible absorption at 365 nm was not taken into account, while calculating the quantum efficiency ϕ and, consequently, its value for inorganic−organic derivatives of HLT3 may be overestimated.
The specific surface areas of the samples (Table 2) were relatively low by the standards of heterogeneous photocatalysts, which is predominantly due to the ceramic synthesis of the alkaline precursors, providing a high crystallinity but strong intergrowth of the polycrystals. Nevertheless, the inorganic−organic derivatives in question have demonstrated impressive photocatalytic performance with respect to hydrogen production from aqueous alcohols, probably due to the unique layered structure and active involvement of the interlayer space in promoting the target reaction [78,79,80,81].

3.2. Photocatalytic Activity with Respect to Carbohydrates Reforming

The photocatalytic measurements were aimed at studying the kinetics of hydrogen evolution from 1 mol. % solutions of D-glucose and D-xylose in water, the influence of the platinization method on the catalytic performance, the stability of the reaction suspensions, and changes in their composition during photocatalysis. Dark stages organized at the end of each experiment (Figure 2 and Supporting Information Figures S5–S7) proved the photocatalytic nature of the hydrogen evolution reactions, since the reaction rate became zero as soon as the radiation source was switched off.
Preliminary experiments on the ultraviolet irradiation (λ > 220 nm) of the aqueous carbohydrates in the absence of a catalyst revealed that D-glucose and D-xylose underwent direct photolysis, accompanied by hydrogen formation at rates of 2.7 and 3.2 μmol/h, respectively (Supporting Information Figure S5). The use of bare protonated oxides HCN3 and HLT3 as photocatalysts allowed one to improve the hydrogen generation rate up to 5.1 times under the same irradiation conditions, achieving apparent quantum efficiencies of ϕ = 0.2% for HCN3 and ϕ = 0.1% for HLT3 (Table 3). As in methanol [80,81], the photocatalytic performance of the niobate in D-glucose turns out to be much greater than that of the titanate. A potential reason for this difference is high hydratability of the HCN3’s interlayer space (HCN3·1.5H2O), which is not typical of HLT3. The intercalated water may serve as a source of reactive hydroxyl radicals, involved in the oxidation of a sacrificial agent along with photogenerated holes and additionally increasing the photocatalytic reaction rate. The photocatalytic in situ platinization of the protonated niobate and titanate allowed increasing the rate of D-glucose conversion into hydrogen by approximately 7 and 17 times, respectively (Table 3). Photoreduced Pt nanoparticles function as a cocatalyst, facilitating surface charge separation and creating active sites for hydrogen evolution [83]. Meanwhile, the in situ Pt reduction was found not to be an optimal method for the platinization of the protonated oxides. The latter, previously platinized in aqueous methanol, exhibited a 1.5–1.8 times greater performance in the reaction of D-glucose reforming (Table 3), which pointed to a better reducing ability of relatively small methanol in comparison with that of the bulky carbohydrate.
All the inorganic−organic derivatives obtained showed an enhanced photocatalytic activity in both carbohydrates as compared with in the initial protonated oxides (Figure 2). The most active sample among bare ones tested in D-glucose was the ethoxy derivative HLT3×EtOH (ϕ = 0.50%) being superior to the protonated titanate HLT3 by 8.3 times. After in situ platinization, the greatest activity values were exhibited by the n-butylamine derivative of the niobate HCN3×BuNH2/Pt (ϕ = 7.5% in D-glucose and ϕ = 8.8% in D-xylose). Thus, the organically modified samples represent promising photocatalytic materials for hydrogen production, not only from methanol solutions but also from those of carbohydrates.
The rigorous evaluation of the photocatalytic activity achieved in relation to the results reported earlier was complicated by the fact that different research groups tested the samples’ performance under unequal conditions (light source, catalyst and carbohydrate concentrations, cocatalyst loading, etc.), which made it impossible to compare directly hydrogen evolution rates in the absence of quantum efficiency data. In general, the activity of organically modified and platinized samples towards hydrogen production from D-glucose and D-xylose (Table 3) exceeded that demonstrated by TiO2-based photocatalysts (TiO2/Pt and TiO2/RuO2/Pt) under similar experimental conditions or had a comparable value [7,21]. At the same time, it is important to keep in mind that widely used TiO2 P25 Degussa and its derivatives have an order of magnitude greater specific surface area than layered perovskite-like oxides presented in this study. As a consequence, the latter have the advantage of the activity normalized per unit area, even if the gross activity of a TiO2-based material proves to be higher.
The available experimental data still did not allow interpreting strictly the derivatives’ increased photocatalytic performance. However, taking into account structural features of these compounds and the hypothesis about their interlayer space as an additional reaction zone in photocatalysis, we can associate the aforementioned activity increase with the greater accessibility of the organically modified interlayer space for reactants. It has been shown on different photocatalytic materials [84,85,86] that the dissociative adsorption of alcohols yielding grafted alkoxy groups is an important step of their photooxidation. In our case, this process is likely to occur in the interlayer space of the modified oxide, which is supported by the very fact of the successful synthesis of grafted derivatives. Despite the partial or, in some cases, even complete decomposition of inserted organic components during photocatalysis [79,80,81], the interlayer reaction zone appeared to remain expanded and continue functioning at least as long as the sample was in the reaction medium, which accounted for the increased activity. Moreover, the enlarged interlayer distance d of the inorganic−organic derivatives could facilitate the penetration and reduction of H2PtCl6 within the interlayer zone forming there new active sites of hydrogen evolution.
Unlike the protonated oxides, all the inorganic−organic samples platinized in situ demonstrated greater activity than those decorated with Pt previously in aqueous methanol (Table 3). In view of the above, a reason for this difference may be the aforementioned degradation of interlayer organic modifiers during irradiation in aqueous methanol followed by the irreversible interlayer space contraction upon the sample separation and drying. In this case, the interlayer distance, apparently, was restored, which limited the supply of reactants into the interlayer zone and thereby decreased the activity.
No matter whether the interlayer organic modifiers decomposed or not, the hydrogen was formed from the carbohydrate solution, not from the sample itself, which was confirmed by the following calculations. For instance, the ethoxy derivative HLT3×EtOH/Pt tested in D-glucose gave 745 μmol H2 throughout the 2 h photocatalytic experiment, which exceeded 8.6 times the H2 amount that could have been formed potentially in the course of the complete decomposition of the grafted ethoxy groups, contained in 25 mg of the sample (86.5 μmol H2), while the activity was maintained. Thus, the reaction of hydrogen production indeed can be considered catalytic.
Another evidence of the participation of the inorganic−organic derivatives’ interlayer space in photocatalytic reactions is a strong correlation of their activity with the reactant molecules’ size (Figure 3). For the example of the HLT3-based inorganic−organic samples, it was clearly seen that the quantum efficiency of hydrogen production increased by 5–7 times when going from aqueous carbohydrates to aqueous methanol. At the same time, the performance of the unmodified protonated titanate increased no more than 1.5 times and thereby depended on the specific sacrificial agent’s size rather weakly. These experimental facts indicated that the interlayer space indeed functions as an additional reaction zone but the contribution of this zone in total photocatalytic performance is expressly dependent on the steric characteristics of reactants (at close values of redox potentials). For instance, relatively small methanol molecules readily penetrate the interlayer space and undergo oxidation while bulky D-glucose ones react predominantly at the boundary of the interlayer space with the reaction medium and on the external crystal surface (Figure 4).
According to the data on the analysis of the photocatalytic suspensions (Supporting Information Figures S8 and S9), the inorganic−organic derivatives (especially alkylamine ones) demonstrated good dispersibility in aqueous carbohydrates and provided noticeably greater volume concentrations than the initial protonated oxides taken in the same amount. However, HCN3-based samples formed more stable suspensions than HLT3-based ones: the latter precipitated more intensely on the cell walls despite the continuous stirring, because of which the actual volume concentrations decrease during the photocatalytic measurement by two or more times. This can explain deviations of some kinetic curves from a linear course.
Most of the studied samples provided weakly acidic pH values of the reaction medium (Supporting Information Figure S8), which should have a beneficial effect on the hydrogen production rate. Unlike aqueous methanol [79,80,81], solutions of carbohydrates appeared to suppress the deintercalation of amines from the alkylamine derivatives, since the latter gave suspensions with subacidic or at least neutral pH.
Generally, pH values of the reaction medium decreased during photocatalytic hydrogen generation (Supporting Information Figure S8). In addition, the final reaction solutions analyzed after centrifugation (Figure 5) showed pronounced absorption bands in the near ultraviolet region, which were not associated with residual suspended particles since the solutions did not exhibit the Tyndall effect being illuminated by a laser. Moreover, the peak intensities generally correlated with the photocatalytic performance of the corresponding samples. The aforementioned pH reduction and appearance of the spectra indicated that the aldonic acids were one (but apparently not the only) of the liquid-phase products of the carbohydrates reforming [87].

4. Conclusions

The present study has shown that organically modified layered perovskite-like oxides HCN3 and HLT3 can be used for the efficient photocatalytic conversion of aqueous carbohydrates into hydrogen fuel. The derivatives were superior in the photocatalytic activity to the unmodified oxides up to 8.3 times and, after surface platinization, exhibited apparent quantum efficiency up to 8.8%. However, the in situ platinization of the organically modified samples provided greater catalytic performance than that preliminarily conducted in aqueous methanol. Experimental data indicated that the interlayer space of the organically modified photocatalysts functions as an additional reaction zone in the photocatalytic hydrogen production and the contribution of this zone to the overall activity is dependent on the steric characteristics of the sacrificial agent used.

Supplementary Materials

The following supporting information can be downloaded at https://www.mdpi.com/article/10.3390/nano12152717/s1, Figure S1: Scheme and operation principle of photocatalytic setting, Figure S2: Spectrophotometric calibrations for the express measurement of reaction suspensions’ concentrations, Figure S3: Emission spectrum of the DRT-125 mercury lamp measured through the employed light filter solution compared with the absorption regions of the photocatalysts under study, Figure S4: Kinetic curves of photolytic hydrogen evolution from 1 mol. % aqueous carbohydrates under ultraviolet irradiation, Figure S5: Kinetic curves of photocatalytic hydrogen generation from 1 mol. % aqueous D-glucose over HCN3- and HLT3-based samples previously platinized in aqueous methanol, Figure S6: Kinetic curves of photocatalytic hydrogen generation from 1 mol. % aqueous D-xylose over HCN3- and HLT3-based samples platinized in situ, Table S1: Actual volume concentrations of the samples in suspensions and pH of the reaction medium, Figure S7: Comparison of the actual concentrations of the samples in the reaction suspensions at the beginning and the end of the photocatalytic measurement.

Author Contributions

Conceptualization, O.I.S., I.A.R. and I.A.Z.; methodology, O.I.S. and I.A.R.; investigation, S.A.K. and V.V.V.; data curation, O.I.S.; writing—original draft preparation, S.A.K. and V.V.V.; writing—review and editing, S.A.K., V.V.V., O.I.S., I.A.R. and I.A.Z.; visualization, S.A.K. and V.V.V.; supervision, I.A.Z. and O.I.S.; funding acquisition, I.A.Z. and O.I.S. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Russian Science Foundation (project No. 20-73-00027—synthesis of the samples; project No. 19-13-00184—investigation of the photocatalytic activity and characterization of the samples).

Data Availability Statement

The data presented in this study are available in the article body and Supplementary Materials.

Acknowledgments

The study was conducted using the equipment of the Saint Petersburg State University Research Park: Centre for X-ray Diffraction Studies, Centre for Optical and Laser Research, Centre for Magnetic Resonance, Centre for Chemical Analysis and Materials Research, Centre for Thermal Analysis and Calorimetry, Interdisciplinary Centre for Nanotechnology, and Centre for Innovative Technologies of Composite Nanomaterials.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Davis, K.A.; Yoo, S.; Shuler, E.W.; Sherman, B.D.; Lee, S.; Leem, G. Photocatalytic hydrogen evolution from biomass conversion. Nano Converg. 2021, 8, 6. [Google Scholar] [CrossRef] [PubMed]
  2. Omri, M.; Sauvage, F.; Golonu, S.; Wadouachi, A.; Pourceau, G. Photocatalyzed transformation of free carbohydrates. Catalysts 2018, 8, 672. [Google Scholar] [CrossRef] [Green Version]
  3. Yao, Y.; Gao, X.; Li, Z.; Meng, X. Photocatalytic reforming for hydrogen evolution: A review. Catalysts 2020, 10, 335. [Google Scholar] [CrossRef] [Green Version]
  4. Kennedy, J.; Bahruji, H.; Bowker, M.; Davies, P.R.; Bouleghlimat, E.; Issarapanacheewin, S. Hydrogen generation by photocatalytic reforming of potential biofuels: Polyols, cyclic alcohols, and saccharides. J. Photochem. Photobiol. A Chem. 2018, 356, 451–456. [Google Scholar] [CrossRef]
  5. Rodionov, I.A.; Zvereva, I.A. Photocatalytic activity of layered perovskite-like oxides in practically valuable chemical reactions. Russ. Chem. Rev. 2016, 85, 248–279. [Google Scholar] [CrossRef]
  6. Wang, S.; Zhang, J.; Li, B.; Sun, H.; Wang, S. Engineered Graphitic Carbon Nitride-Based Photocatalysts for Visible-Light-Driven Water Splitting: A Review. Energy Fuels 2021, 35, 6504–6526. [Google Scholar] [CrossRef]
  7. Bellardita, M.; García-López, E.I.; Marcì, G.; Palmisano, L. Photocatalytic formation of H2 and value-added chemicals in aqueous glucose (Pt)-TiO2 suspension. Int. J. Hydrog. Energy 2016, 41, 5934–5947. [Google Scholar] [CrossRef]
  8. Zhou, M.; Li, Y.; Peng, S.; Lu, G.; Li, S. Effect of epimerization of D-glucose on photocatalytic hydrogen generation over Pt/TiO2. Catal. Commun. 2012, 18, 21–25. [Google Scholar] [CrossRef]
  9. Bahadori, E.; Ramis, G.; Zanardo, D.; Menegazzo, F.; Signoretto, M.; Gazzoli, D.; Pietrogiacomi, D.; Michele, A.D. Photoreforming of Glucose over CuO/TiO2. Catalysts 2020, 10, 477. [Google Scholar] [CrossRef]
  10. Bellardita, M.; García-López, E.I.; Marcì, G.; Nasillo, G.; Palmisano, L. Photocatalytic Solar Light H2 Production by Aqueous Glucose Reforming. Eur. J. Inorg. Chem. 2018, 2018, 4522–4532. [Google Scholar] [CrossRef] [Green Version]
  11. Iervolino, G.; Vaiano, V.; Murcia, J.J.; Rizzo, L.; Ventre, G.; Pepe, G.; Campiglia, P.; Hidalgo, M.C.; Navío, J.A.; Sannino, D. Photocatalytic hydrogen production from degradation of glucose over fluorinated and platinized TiO2 catalysts. J. Catal. 2016, 339, 47–56. [Google Scholar] [CrossRef]
  12. Iervolino, G.; Vaiano, V.; Sannino, D.; Rizzo, L.; Ciambelli, P. Production of hydrogen from glucose by LaFeO3 based photocatalytic process during water treatment. Int. J. Hydrog. Energy 2016, 41, 959–966. [Google Scholar] [CrossRef]
  13. Iervolino, G.; Vaiano, V.; Sannino, D.; Rizzo, L.; Galluzzi, A.; Polichetti, M.; Pepe, G.; Campiglia, P. Hydrogen production from glucose degradation in water and wastewater treated by Ru-LaFeO3/Fe2O3 magnetic particles photocatalysis and heterogeneous photo-Fenton. Int. J. Hydrog. Energy 2018, 43, 2184–2196. [Google Scholar] [CrossRef]
  14. Zhao, H.; Li, C.F.; Yong, X.; Kumar, P.; Palma, B.; Hu, Z.Y.; van Tendeloo, G.; Siahrostami, S.; Larter, S.; Zheng, D.; et al. Coproduction of hydrogen and lactic acid from glucose photocatalysis on band-engineered Zn1-xCdxS homojunction. iScience 2021, 24, 102109. [Google Scholar] [CrossRef]
  15. Li, C.; Wang, H.; Ming, J.; Liu, M.; Fang, P. Hydrogen generation by photocatalytic reforming of glucose with heterostructured CdS/MoS2 composites under visible light irradiation. Int. J. Hydrog. Energy 2017, 42, 16968–16978. [Google Scholar] [CrossRef]
  16. Zheng, X.; Wang, X.; Liu, J.; Fu, X.; Yang, Y.; Han, H.; Fan, Y.; Zhang, S.; Meng, S.; Chen, S. Construction of NiPx/MoS2/NiS/CdS composite to promote photocatalytic H2 production from glucose solution. J. Am. Ceram. Soc. 2021, 104, 5307–5316. [Google Scholar] [CrossRef]
  17. Madriz, L.; Tatá, J.; Carvajal, D.; Núñez, O.; Scharifker, B.R.; Mostany, J.; Borrás, C.; Cabrerizo, F.M.; Vargas, R. Photocatalysis and photoelectrochemical glucose oxidation on Bi2WO6: Conditions for the concomitant H2 production. Renew. Energy 2020, 152, 974–983. [Google Scholar] [CrossRef]
  18. Speltini, A.; Scalabrini, A.; Maraschi, F.; Sturini, M.; Pisanu, A.; Malavasi, L.; Profumo, A. Improved photocatalytic H2 production assisted by aqueous glucose biomass by oxidized g-C3N4. Int. J. Hydrog. Energy 2018, 43, 14925–14933. [Google Scholar] [CrossRef]
  19. Bai, X.; Hou, Q.; Qian, H.; Nie, Y.; Xia, T.; Lai, R.; Yu, G.; Laiq Ur Rehman, M.; Xie, H.; Ju, M. Selective oxidation of glucose to gluconic acid and glucaric acid with chlorin e6 modified carbon nitride as metal-free photocatalyst. Appl. Catal. B Environ. 2022, 303, 120895. [Google Scholar] [CrossRef]
  20. Speltini, A.; Romani, L.; Dondi, D.; Malavasi, L.; Profumo, A. Carbon nitride-perovskite composites: Evaluation and optimization of photocatalytic hydrogen evolution in saccharides aqueous solution. Catalysts 2020, 10, 1259. [Google Scholar] [CrossRef]
  21. Kawai, T.; Sakata, T. Conversion of carbohydrate into hydrogen fuel by a photocatalytic process. Nature 1980, 286, 474–476. [Google Scholar] [CrossRef]
  22. Kurenkova, A.Y.; Markovskaya, D.V.; Gerasimov, E.Y.; Prosvirin, I.P.; Cherepanova, S.V.; Kozlova, E.A. New insights into the mechanism of photocatalytic hydrogen evolution from aqueous solutions of saccharides over CdS-based photocatalysts under visible light. Int. J. Hydrog. Energy 2020, 45, 30165–30177. [Google Scholar] [CrossRef]
  23. Kondarides, D.I.; Patsoura, A.; Verykios, X.E. Anaerobic photocatalytic oxidation of carbohydrates in aqueous Pt/TiO2 Suspensions with simultaneous production of hydrogen. J. Adv. Oxid. Technol. 2010, 13, 116–123. [Google Scholar] [CrossRef]
  24. Beasley, C.; Gnanamani, M.K.; Qian, D.; Hopps, S.D. Photocatalytic Reforming of Sucrose and Dextrose for Hydrogen Production on Pd/TiO2. ChemistrySelect 2021, 6, 6512–6524. [Google Scholar] [CrossRef]
  25. Caravaca, A.; Jones, W.; Hardacre, C.; Bowker, M. H2 production by the photocatalytic reforming of cellulose and raw biomass using Ni, Pd, Pt and Au on titania. Proc. R. Soc. Math. Phys. Eng. Sci. 2016, 472, 20160054. [Google Scholar] [CrossRef] [Green Version]
  26. Chang, C.; Skillen, N.; Nagarajan, S.; Ralphs, K.; Irvine, J.T.S.; Lawton, L.; Robertson, P.K.J. Using cellulose polymorphs for enhanced hydrogen production from photocatalytic reforming. Sustain. Energy Fuels 2019, 3, 1971–1975. [Google Scholar] [CrossRef]
  27. Kuehnel, M.F.; Reisner, E. Solar Hydrogen Generation from Lignocellulose. Angew. Chem. Int. Ed. 2018, 57, 3290–3296. [Google Scholar] [CrossRef]
  28. Ramis, G.; Bahadori, E.; Rossetti, I. Design of efficient photocatalytic processes for the production of hydrogen from biomass derived substrates. Int. J. Hydrog. Energy 2020, 46, 12105–12116. [Google Scholar] [CrossRef]
  29. Zou, J.; Zhang, G.; Xu, X. One-pot photoreforming of cellulosic biomass waste to hydrogen by merging photocatalysis with acid hydrolysis. Appl. Catal. A Gen. 2018, 563, 73–79. [Google Scholar] [CrossRef]
  30. Schaak, R.E.; Mallouk, T.E. Perovskites by Design: A Toolbox of Solid-State Reactions. Chem. Mater. 2002, 14, 1455–1471. [Google Scholar] [CrossRef]
  31. Uppuluri, R.; Sen Gupta, A.; Rosas, A.S.; Mallouk, T.E. Soft chemistry of ion-exchangeable layered metal oxides. Chem. Soc. Rev. 2018, 47, 2401–2430. [Google Scholar] [CrossRef] [PubMed]
  32. Tani, S.; Komori, Y.; Hayashi, S.; Sugahara, Y. Local environments and dynamics of hydrogen atoms in protonated forms of ion-exchangeable layered perovskites estimated by solid-state 1H NMR. J. Solid State Chem. 2006, 179, 3357–3364. [Google Scholar] [CrossRef]
  33. Silyukov, O.; Chislov, M.; Burovikhina, A.; Utkina, T.; Zvereva, I. Thermogravimetry study of ion exchange and hydration in layered oxide materials. J. Therm. Anal. Calorim. 2012, 110, 187–192. [Google Scholar] [CrossRef]
  34. Silyukov, O.I.; Kurnosenko, S.A.; Zvereva, I.A. Intercalation of Methylamine into the Protonated Forms of Layered Perovskite-Like Oxides HLnTiO4 (Ln = La and Nd). Glas. Phys. Chem. 2018, 44, 428–432. [Google Scholar] [CrossRef]
  35. Kurnosenko, S.A.; Silyukov, O.I.; Mazur, A.S.; Zvereva, I.A. Synthesis and thermal stability of new inorganic-organic perovskite-like hybrids based on layered titanates HLnTiO4 (Ln = La, Nd). Ceram. Int. 2020, 46, 5058–5068. [Google Scholar] [CrossRef]
  36. Shelyapina, M.G.; Lushpinskaya, I.P.; Kurnosenko, S.A.; Silyukov, O.I.; Zvereva, I.A. Identification of Intercalates and Grafted Organic Derivatives of H2La2Ti3O10 by Multinuclear NMR. Russ. J. Gen. Chem. 2020, 90, 760–761. [Google Scholar] [CrossRef]
  37. Kurnosenko, S.A.; Silyukov, O.I.; Minich, I.A.; Zvereva, I.A. Exfoliation of Methylamine and n-Butylamine Derivatives of Layered Perovskite-Like Oxides HLnTiO4 and H2Ln2Ti3O10 (Ln = La, Nd) into Nanolayers. Glas. Phys. Chem. 2021, 47, 372–381. [Google Scholar] [CrossRef]
  38. Silyukov, O.I.; Minich, I.A.; Zvereva, I.A. Synthesis of Protonated Derivatives of Layered Perovskite-Like Bismuth Titanates. Glas. Phys. Chem. 2018, 44, 115–119. [Google Scholar] [CrossRef]
  39. Minich, I.A.; Silyukov, O.I.; Gak, V.V.; Borisov, E.V.; Zvereva, I.A. Synthesis of Organic–Inorganic Hybrids Based on Perovskite-like Bismuth Titanate H2K0.5Bi2.5Ti4O13·H2O and n-Alkylamines. ACS Omega 2020, 8, 8158. [Google Scholar] [CrossRef] [Green Version]
  40. Shelyapina, M.G.; Silyukov, O.I.; Lushpinskaia, I.P.; Kurnosenko, S.A.; Mazur, A.S.; Shenderovich, I.G.; Zvereva, I.A. NMR Study of Intercalates and Grafted Organic Derivatives of H2La2Ti3O10. Molecules 2020, 25, 5229. [Google Scholar] [CrossRef]
  41. Silyukov, O.I.; Kurnosenko, S.A.; Minich, I.A.; Rodionov, I.A.; Zvereva, I.A. Protonated Forms of Layered Perovskite-Like Titanate NaNdTiO4: Neutron and X-ray Diffraction Structural Analysis. Solids 2021, 2, 265–277. [Google Scholar] [CrossRef]
  42. Shelyapina, M.G.; Silyukov, O.I.; Andronova, E.A.; Nefedov, D.Y.; Antonenko, A.O.; Missyul, A.; Kurnosenko, S.A.; Zvereva, I.A. 1H NMR Study of the HCa2Nb3O10 Photocatalyst with Different Hydration Levels. Molecules 2021, 26, 5943. [Google Scholar] [CrossRef] [PubMed]
  43. Rodionov, I.A.; Silyukov, O.I.; Utkina, T.D.; Chislov, M.V.; Sokolova, Y.P.; Zvereva, I.A. Photocatalytic properties and hydration of perovskite-type layered titanates A2Ln2Ti3O10 (A = Li, Na, K; Ln = La, Nd). Russ. J. Gen. Chem. 2012, 82, 1191–1196. [Google Scholar] [CrossRef]
  44. Takata, T.; Furumi, Y.; Shinohara, K.; Tanaka, A.; Hara, M.; Kondo, J.N.; Domen, K. Photocatalytic Decomposition of Water on Spontaneously Hydrated Layered Perovskites. Chem. Mater. 1997, 9, 1063–1064. [Google Scholar] [CrossRef]
  45. Zou, Z.; Ye, J.; Arakawa, H. Substitution effects of In3+ by Fe3+ on photocatalytic and structural properties of Bi2InNbO7 photocatalysts. J. Mol. Catal. 2001, 168, 289–297. [Google Scholar] [CrossRef]
  46. Reddy, V.; Hwang, D.; Lee, J. Effect of Zr substitution for Ti in KLaTiO4 for photocatalytic water splitting. Catal. Lett. 2003, 90, 39–44. [Google Scholar] [CrossRef]
  47. Kumar, V.; Govind; Uma, S. Investigation of cation (Sn2+) and anion (N3-) substitution in favor of visible light photocatalytic activity in the layered perovskite K2La2Ti3O10. J. Hazard. Mater. 2011, 189, 502–508. [Google Scholar] [CrossRef]
  48. Zhou, Y.; Wen, T.; Guo, Y.; Yang, B.; Wang, Y. Controllable doping of nitrogen and tetravalent niobium affords yellow and black calcium niobate nanosheets for enhanced photocatalytic hydrogen evolution. RSC Adv. 2016, 6, 64930–64936. [Google Scholar] [CrossRef]
  49. Kawashima, K.; Hojamberdiev, M.; Chen, S.; Yubuta, K.; Wagata, H.; Domen, K.; Teshima, K. Understanding the effect of partial N3−-to-O2− substitution and H+-to-K+ exchange on photocatalytic water reduction activity of Ruddlesden–Popper layered perovskite KLaTiO4. Mol. Catal. 2017, 432, 250–258. [Google Scholar] [CrossRef]
  50. Huang, Y.; Li, J.; Wei, Y.; Li, Y.; Lin, J.; Wu, J. Fabrication and photocatalytic property of Pt-intercalated layered perovskite niobates H1−xLaNb2−xMoxO7 (x = 0–0.15). J. Hazard. Mater. 2009, 166, 103–108. [Google Scholar] [CrossRef]
  51. Huang, Y.; Li, Y.; Wei, Y.; Huang, M.; Wu, J. Photocatalytic property of partially substituted Pt-intercalated layered perovskite, ASr2TaxNb3−xO10 (A = K, H; x = 0, 1, 1.5, 2 and 3). Sol. Energy Mater. Sol. Cells 2011, 95, 1019–1027. [Google Scholar] [CrossRef]
  52. Oshima, T.; Wang, Y.; Lu, D.; Yokoi, T.; Maeda, K. Photocatalytic overall water splitting on Pt nanocluster-intercalated, restacked KCa2Nb3O10 nanosheets: The promotional effect of co-existing ions. Nanoscale Adv. 2019, 1, 189–194. [Google Scholar] [CrossRef] [Green Version]
  53. Cui, W.; Qi, Y.; Liu, L.; Rana, D.; Hu, J.; Liang, Y. Synthesis of PbS–K2La2Ti3O10 composite and its photocatalytic activity for hydrogen production. Prog. Nat. Sci. Mater. Int. 2012, 22, 120–125. [Google Scholar] [CrossRef] [Green Version]
  54. Cui, W.; Liu, L.; Ma, S.; Liang, Y.; Zhang, Z. CdS-sensitized K2La2Ti3O10 composite: A new photocatalyst for hydrogen evolution under visible light irradiation. Catal. Today 2013, 207, 44–49. [Google Scholar] [CrossRef]
  55. Cui, W.; Guo, D.; Liu, L.; Hu, J.; Rana, D.; Liang, Y. Preparation of ZnIn2S4/K2La2Ti3O10 composites and their photocatalytic H2 evolution from aqueous Na2S/Na2SO3 under visible light irradiation. Catal. Commun. 2014, 48, 55–59. [Google Scholar] [CrossRef]
  56. Saito, K.; Kozeni, M.; Sohmiya, M.; Komaguchi, K.; Ogawa, M.; Sugahara, Y.; Ide, Y. Unprecedentedly enhanced solar photocatalytic activity of a layered titanate simply integrated with TiO2 nanoparticles. Phys. Chem. Chem. Phys. 2016, 18, 30920–30925. [Google Scholar] [CrossRef] [PubMed]
  57. Liu, Y.; Zhou, Y.; Lv, C.; Zhang, C.; Jin, X.; Meng, Q.; Chen, G. Construction of 2D-composite HCa2Nb3O10 /CaNb2O6 heterostructured photocatalysts with enhanced hydrogen production performance. New J. Chem. 2018, 42, 681–687. [Google Scholar] [CrossRef]
  58. Chen, X.; Shen, S.; Guo, L.; Mao, S.S. Semiconductor-based photocatalytic hydrogen generation. Chem. Rev. 2010, 110, 6503–6570. [Google Scholar] [CrossRef]
  59. Zhang, L.; Wong, K.H.; Chen, Z.; Yu, J.C.; Zhao, J.; Hu, C.; Chan, C.Y.; Wong, P.K. AgBr-Ag-Bi2WO6 nanojunction system: A novel and efficient photocatalyst with double visible-light active components. Appl. Catal. A Gen. 2009, 363, 221–229. [Google Scholar] [CrossRef]
  60. Kim, H.G.; Jeong, E.D.; Borse, P.H.; Jeon, S.; Yong, K.; Lee, J.S.; Li, W.; Oh, S.H. Photocatalytic Ohmic layered nanocomposite for efficient utilization of visible light photons. Appl. Phys. Lett. 2006, 89, 2012–2015. [Google Scholar] [CrossRef] [Green Version]
  61. Kim, H.G.; Borse, P.H.; Choi, W.; Lee, J.S. Photocatalytic Nanodiodes for Visible-Light Photocatalysis. Angew. Chem. 2005, 117, 4661–4665. [Google Scholar] [CrossRef]
  62. Zhang, L.; Wang, G.; Xiong, Z.; Tang, H.; Jiang, C. Fabrication of flower-like direct Z-scheme β-Bi2O3/g-C3N4 photocatalyst with enhanced visible light photoactivity for Rhodamine B degradation. Appl. Surf. Sci. 2018, 436, 162–171. [Google Scholar] [CrossRef]
  63. Youngblood, W.J.; Anna Lee, S.H.; Maeda, K.; Mallouk, T.E. Visible light water splitting using dye-sensitized oxide semiconductors. Acc. Chem. Res. 2009, 42, 1966–1973. [Google Scholar] [CrossRef] [Green Version]
  64. Maeda, K.; Mallouk, T.E. Two-Dimensional Metal Oxide Nanosheets as Building Blocks for Artificial Photosynthetic Assemblies. Bull. Chem. Soc. Jpn. 2018, 92, 38–54. [Google Scholar] [CrossRef]
  65. Sanchez, P.G.-R. and C. Functional Hybrid Materials; Wiley-VCH Verlag GmbH & Co. KGaA: Weinheim, Germany, 2006; ISBN 3527303596. [Google Scholar]
  66. Kickelbick, G. Hybrid Materials: Synthesis, Characterization, and Applications; Wiley-VCH Verlag GmbH & Co. KGaA: Weinheim, Germany, 2007; ISBN 9783527312993. [Google Scholar]
  67. Mir, S.H.; Nagahara, L.A.; Thundat, T.; Mokarian-Tabari, P.; Furukawa, H.; Khosla, A. Review—Organic-Inorganic Hybrid Functional Materials: An Integrated Platform for Applied Technologies. J. Electrochem. Soc. 2018, 165, B3137–B3156. [Google Scholar] [CrossRef]
  68. Constantino, V.R.L.; Barbosa, C.A.S.; Bizeto, M.A.; Dias, P.M. Intercalation compounds involving inorganic layered structures. An. Acad. Bras. Cienc. 2000, 72, 45–50. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  69. Jacobson, A.J.; Johnson, J.W.; Lewandowski, J. Intercalation of the layered solid acid HCa2Nb3O10 by organic amines. Mater. Res. Bull. 1987, 22, 45–51. [Google Scholar] [CrossRef]
  70. Minich, I.A.; Silyukov, O.I.; Kurnosenko, S.A.; Gak, V.V.; Kalganov, V.D.; Kolonitskiy, P.D.; Zvereva, I.A. Physical–Chemical Exfoliation of n-Alkylamine Derivatives of Layered Perovskite-like Oxide H2K0.5Bi2.5Ti4O13 into Nanosheets. Nanomaterials 2021, 11, 2708. [Google Scholar] [CrossRef]
  71. Tahara, S.; Sugahara, Y. Interlayer Surface Modification of the Protonated Triple-Layered Perovskite HCa2Nb3O10·xH2O with n-Alcohols. Langmuir 2003, 19, 9473–9478. [Google Scholar] [CrossRef]
  72. Tahara, S.; Ichikawa, T.; Kajiwara, G.; Sugahara, Y. Reactivity of the Ruddlesden−Popper Phase H2La2Ti3O10 with Organic Compounds: Intercalation and Grafting Reactions. Chem. Mater. 2007, 19, 2352–2358. [Google Scholar] [CrossRef]
  73. Kurnosenko, S.A.; Voytovich, V.V.; Silyukov, O.I.; Minich, I.A.; Malygina, E.N.; Zvereva, I.A. Inorganic-organic derivatives of layered perovskite-like titanates HLnTiO4 (Ln = La, Nd) with n-amines and n-alcohols: Synthesis, thermal, vacuum and hydrolytic stability. Ceram. Int. 2021, 48, 7240–7252. [Google Scholar] [CrossRef]
  74. Wang, C.; Tang, K.; Wang, D.; Liu, Z.; Wang, L.; Zhu, Y.; Qian, Y. A new carbon intercalated compound of Dion–Jacobson phase HLaNb2O7. J. Mater. Chem. 2012, 22, 11086. [Google Scholar] [CrossRef]
  75. Aznar, A.J.; Sanz, J.; Ruiz-Hitzky, E. Mechanism of the grafting of organosilanes on mineral surfaces. IV. Phenylderivatives of sepiolite and poly(organosiloxanes). Colloid Polym. Sci. 1992, 270, 165–176. [Google Scholar] [CrossRef]
  76. Shimada, A.; Yoneyama, Y.; Tahara, S.; Mutin, P.H.; Sugahara, Y. Interlayer surface modification of the protonated ion-exchangeable layered perovskite HLaNb2O7xH2O with organophosphonic acids. Chem. Mater. 2009, 21, 4155–4162. [Google Scholar] [CrossRef]
  77. Machida, M.; Mitsuyama, T.; Ikeue, K.; Matsushima, S.; Arai, M. Photocatalytic property and electronic structure of triple-layered perovskite tantalates, MCa2Ta3O10 (M = Cs, Na, H, and C6H13NH3). J. Phys. Chem. B 2005, 109, 7801–7806. [Google Scholar] [CrossRef]
  78. Rodionov, I.A.; Maksimova, E.A.; Pozhidaev, A.Y.; Kurnosenko, S.A.; Silyukov, O.I.; Zvereva, I.A. Layered Titanate H2Nd2Ti3O10 Intercalated With n-Butylamine: A New Highly Efficient Hybrid Photocatalyst for Hydrogen Production From Aqueous Solutions of Alcohols. Front. Chem. 2019, 7, 1–13. [Google Scholar] [CrossRef]
  79. Voytovich, V.V.; Kurnosenko, S.A.; Silyukov, O.I.; Rodionov, I.A.; Minich, I.A.; Zvereva, I.A. Study of n-alkylamine Intercalated Layered Perovskite-Like Niobates HCa2Nb3O10 as Photocatalysts for Hydrogen Production From an Aqueous Solution of Methanol. Front. Chem. 2020, 8, 300. [Google Scholar] [CrossRef]
  80. Voytovich, V.V.; Kurnosenko, S.A.; Silyukov, O.I.; Rodionov, I.A.; Bugrov, A.N.; Minich, I.A.; Malygina, E.N.; Zvereva, I.A. Synthesis of n-Alkoxy Derivatives of Layered Perovskite-Like Niobate HCa2Nb3O10 and Study of Their Photocatalytic Activity for Hydrogen Production from an Aqueous Solution of Methanol. Catalysts 2021, 11, 897. [Google Scholar] [CrossRef]
  81. Kurnosenko, S.A.; Voytovich, V.V.; Silyukov, O.I.; Rodionov, I.A.; Kirichenko, S.O.; Minich, I.A.; Malygina, E.N.; Khramova, A.D.; Zvereva, I.A. Photocatalytic Activity of n-Alkylamine and n-Alkoxy Derivatives of Layered Perovskite-like Titanates H2Ln2Ti3O10 (Ln = La, Nd) in the Reaction of Hydrogen Production from an Aqueous Solution of Methanol. Catalysts 2021, 11, 1279. [Google Scholar] [CrossRef]
  82. Asahi, R.; Morikawa, T.; Ohwaki, T.; Aoki, K.; Taga, Y. Visible-light photocatalysis in nitrogen-doped titanium oxides. Science 2001, 293, 269–271. [Google Scholar] [CrossRef]
  83. Al-Azri, Z.H.N.; Chen, W.T.; Chan, A.; Jovic, V.; Ina, T.; Idriss, H.; Waterhouse, G.I.N. The roles of metal co-catalysts and reaction media in photocatalytic hydrogen production: Performance evaluation of M/TiO2 photocatalysts (M = Pd, Pt, Au) in different alcohol-water mixtures. J. Catal. 2015, 329, 355–367. [Google Scholar] [CrossRef]
  84. Zhao, G.; Busser, G.W.; Froese, C.; Hu, B.; Bonke, S.A.; Schnegg, A.; Ai, Y.; Wei, D.; Wang, X.; Peng, B.; et al. Anaerobic Alcohol Conversion to Carbonyl Compounds over Nanoscaled Rh-Doped SrTiO3 under Visible Light. J. Phys. Chem. Lett. 2019, 10, 2075–2080. [Google Scholar] [CrossRef] [PubMed]
  85. Shen, Z.; Hu, Y.; Li, B.; Zou, Y.; Li, S.; Wilma Busser, G.; Wang, X.; Zhao, G.; Muhler, M. State-of-the-art progress in the selective photo-oxidation of alcohols. J. Energy Chem. 2021, 62, 338–350. [Google Scholar] [CrossRef]
  86. Li, B.; Hong, J.; Ai, Y.; Hu, Y.; Shen, Z.; Li, S.; Zou, Y.; Zhang, S.; Wang, X.; Zhao, G.; et al. Visible-near-infrared-light-driven selective oxidation of alcohols over nanostructured Cu doped SrTiO3 in water under mild condition. J. Catal. 2021, 399, 142–149. [Google Scholar] [CrossRef]
  87. Wads, I. Photodegradation of Carbohydrates. Part IV. Direct Photolysis of D-Glucose in Aqueous Solution. Acta Chem. Scand. 1962, 16, 487–494. [Google Scholar]
Nanomaterials 12 02717 g001 550
Figure 1. XRD patterns of the samples obtained via the protonation of initial oxides (HLT3 and HCN3), subsequent intercalation of amines (HCN3×RNH2 and HLT3×RNH2), and grafting of alcohols (HCN3×ROH and HLT3×ROH).
Figure 1. XRD patterns of the samples obtained via the protonation of initial oxides (HLT3 and HCN3), subsequent intercalation of amines (HCN3×RNH2 and HLT3×RNH2), and grafting of alcohols (HCN3×ROH and HLT3×ROH).
Nanomaterials 12 02717 g001
Nanomaterials 12 02717 g002 550
Figure 2. Kinetic curves of hydrogen generation from 1 mol. % aqueous D-glucose over the protonated oxides, inorganic−organic derivatives, and products of their in situ platinization under near ultraviolet irradiation.
Figure 2. Kinetic curves of hydrogen generation from 1 mol. % aqueous D-glucose over the protonated oxides, inorganic−organic derivatives, and products of their in situ platinization under near ultraviolet irradiation.
Nanomaterials 12 02717 g002
Nanomaterials 12 02717 g003 550
Figure 3. Comparison of the apparent quantum efficiency of hydrogen evolution from aqueous solutions of carbohydrates and methanol over platinized HLT3-based photocatalysts.
Figure 3. Comparison of the apparent quantum efficiency of hydrogen evolution from aqueous solutions of carbohydrates and methanol over platinized HLT3-based photocatalysts.
Nanomaterials 12 02717 g003
Nanomaterials 12 02717 g004 550
Figure 4. Interlayer space as an additional reaction zone in photocatalytic hydrogen generation.
Figure 4. Interlayer space as an additional reaction zone in photocatalytic hydrogen generation.
Nanomaterials 12 02717 g004
Nanomaterials 12 02717 g005 550
Figure 5. Ultraviolet absorption spectra of the reaction solutions after photocatalytic experiments (5× dilution; solid samples were separated via centrifugation).
Figure 5. Ultraviolet absorption spectra of the reaction solutions after photocatalytic experiments (5× dilution; solid samples were separated via centrifugation).
Nanomaterials 12 02717 g005
Table
Table 1. Conditions for the synthesis of the inorganic−organic derivatives.
Table 1. Conditions for the synthesis of the inorganic−organic derivatives.
SamplePrecursorOrganic Content in the
Reaction Mixture
(vol. %)		Temperature (°C)Duration (d)
HCN3×BuNH2HCN3 90251
HCN3×EtOHHCN3961007
HLT3×EtNH2HLT3×MeNH270251
HLT3×EtOHHLT3×BuNH2961807
Table
Table 2. Lattice parameters in the tetragonal system, interlayer distances d, quantitative compositions (interlayer organic x and water y content per formula unit), light absorption edge, and specific surface areas of the samples.
Table 2. Lattice parameters in the tetragonal system, interlayer distances d, quantitative compositions (interlayer organic x and water y content per formula unit), light absorption edge, and specific surface areas of the samples.
Samplea (Å)c (Å)d (Å)xyEg (eV)λmax (nm)S (m2/g)
HCN33.8216.016.0−1.503.503547.6
HCN3×BuNH23.8625.425.41.000.453.623435.0
HCN3×EtOH3.8635.817.90.900.453.503543.9
HLT33.7927.213.6−0.153.443603.2
HLT3×EtNH23.8220.220.20.700.353.39366− *
HLT3×EtOH3.8339.519.80.850.403.41364− *
* not measured.
Table
Table 3. Photocatalytic activity of the protonated oxides and inorganic−organic derivatives.
Table 3. Photocatalytic activity of the protonated oxides and inorganic−organic derivatives.
Sampleω (μmol/h)ϕ (%)kPt
D-glucoseHCN3140.2−
HCN3/Pt951.67
HCN3/Pt(MeOH)1402.410
HCN3×BuNH2210.4−
HCN3×BuNH2/Pt4507.521
HCN3×BuNH2/Pt(MeOH)4106.820
HCN3×EtOH200.3−
HCN3×EtOH/Pt2003.310
HCN3×EtOH/Pt(MeOH)1702.89
HLT340.1−
HLT3/Pt611.015
HLT3/Pt(MeOH)1101.828
HLT3×EtNH2100.2−
HLT3×EtNH2/Pt2704.527
HLT3×EtNH2/Pt(MeOH)2404.024
HLT3×EtOH300.5−
HLT3×EtOH/Pt3606.012
HLT3×EtOH/Pt(MeOH)1202.04
D-xyloseHCN3/Pt881.5−
HCN3×BuNH2/Pt5308.8−
HCN3×EtOH/Pt1402.3−
HLT3/Pt480.80−
HLT3×EtNH2/Pt3806.3−
HLT3×EtOH/Pt4207.0−
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Kurnosenko, S.A.; Voytovich, V.V.; Silyukov, O.I.; Rodionov, I.A.; Zvereva, I.A. Photocatalytic Hydrogen Production from Aqueous Solutions of Glucose and Xylose over Layered Perovskite-like Oxides HCa2Nb3O10, H2La2Ti3O10 and Their Inorganic-Organic Derivatives. Nanomaterials 2022, 12, 2717. https://doi.org/10.3390/nano12152717

AMA Style

Kurnosenko SA, Voytovich VV, Silyukov OI, Rodionov IA, Zvereva IA. Photocatalytic Hydrogen Production from Aqueous Solutions of Glucose and Xylose over Layered Perovskite-like Oxides HCa2Nb3O10, H2La2Ti3O10 and Their Inorganic-Organic Derivatives. Nanomaterials. 2022; 12(15):2717. https://doi.org/10.3390/nano12152717

Chicago/Turabian Style

Kurnosenko, Sergei A., Vladimir V. Voytovich, Oleg I. Silyukov, Ivan A. Rodionov, and Irina A. Zvereva. 2022. "Photocatalytic Hydrogen Production from Aqueous Solutions of Glucose and Xylose over Layered Perovskite-like Oxides HCa2Nb3O10, H2La2Ti3O10 and Their Inorganic-Organic Derivatives" Nanomaterials 12, no. 15: 2717. https://doi.org/10.3390/nano12152717

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop