Investigation of the Leachate Effect on Permeability and Geotechnical Characteristics of Fine-Grained Soil Modified Using Nanoclay–Nanofiber Composites
Next Article in Special Issue
Predictive Model Based on K-Nearest Neighbor Coupled with the Gray Wolf Optimizer Algorithm (KNN_GWO) for Estimating the Amount of Phenol Adsorption on Powdered Activated Carbon
Previous Article in Journal
Flocculation Patterns Related to Intra-Annual Hydrodynamics Variability in the Lower Grijalva-Usumacinta System
Previous Article in Special Issue
Enhanced Removal of Sb (III) by Hydroxy-Iron/Acid–Base-Modified Sepiolite: Surface Structure and Adsorption Mechanism
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:

Efficient Uptake of Angiotensin-Converting Enzyme II Inhibitor Employing Graphene Oxide-Based Magnetic Nanoadsorbents

Miguel Pereira de Oliveira
Carlos Schnorr
Theodoro da Rosa Salles
Franciele da Silva Bruckmann
Luiza Baumann
Edson Irineu Muller
Wagner Jesus da Silva Garcia
Artur Harres de Oliveira
Luis F. O. Silva
2 and
Cristiano Rodrigo Bohn Rhoden
Laboratório de Materiais Magnéticos Nanoestruturados—LaMMaN, Universidade Franciscana, Santa Maria 97010-030, Brazil
Department of Civil and Environmental, Universidad de la Costa, CUC, Calle 58 # 55–66, Barranquilla 080002, Colombia
Programa de Pós-graduação em Química, Universidade Federal de Santa Maria—UFSM, Santa Maria 97105-900, Brazil
Departamento de Desenho Industrial, Universidade Federal de Santa Maria—UFSM, Santa Maria 97105-900, Brazil
Departamento de Física, Universidade Federal de Santa Maria—UFSM, Santa Maria 97105-900, Brazil
Programa de Pós-graduação em Nanociências, Universidade Franciscana—UFN, Santa Maria 97010-030, Brazil
Author to whom correspondence should be addressed.
Water 2023, 15(2), 293;
Submission received: 13 December 2022 / Revised: 5 January 2023 / Accepted: 6 January 2023 / Published: 10 January 2023
(This article belongs to the Special Issue Adsorption Technology for Water and Wastewater Treatments)


This paper reports a high efficiency uptake of captopril (CPT), employing magnetic graphene oxide (MGO) as the adsorbent. The graphene oxide (GO) was produced through an oxidation and exfoliation method, and the magnetization technique by the co-precipitation method. The nanomaterials were characterized by FTIR, XRD, SEM, Raman, and VSM analysis. The optimal condition was reached by employing GO·Fe3O4 at pH 3.0 (50 mg of adsorbent and 50 mg L−1 of CPT), presenting values of removal percentage and maximum adsorption capacity of 99.43% and 100.41 mg g−1, respectively. The CPT adsorption was dependent on adsorbent dosage, initial concentration of adsorbate, pH, and ionic strength. Sips and Elovich models showed the best adjustment for experimental data, suggesting that adsorption occurs in a heterogeneous surface. Thermodynamic parameters reveal a favorable, exothermic, involving a chemisorption process. The magnetic carbon nanomaterial exhibited a high efficiency after five adsorption/desorption cycles. Finally, the GO·Fe3O4 showed an excellent performance in CPT removal, allowing future application in waste management.

1. Introduction

Water contamination by emerging pollutants (EPs) has become an important problem around the world [1]. Amongst these, drugs and personal care products are widely found in water bodies, due to their intrinsic characteristics and incomplete removal by current methods [2]. Additionally, due to their unique properties and xenobiotic-like character, these compounds present a high tendency to bioaccumulation, which leads to the development of diverse damages to human health, animals, and the environment [3]. In addition, high consumption, inadequate disposal, and incomplete metabolism are associated with the high and constant generation of waste. Due to low concentration and traces in water, the conventional systems are not able to remove these compounds, resulting in a secondary source of exposition and contamination [4].
Captopril (CPT) (1-(3-mercapto-2-D-methyl-1-oxopropyl)-L proline is a hydrophilic drug used to inhibit angiotensin-converting enzyme II (ACE II) and is one of the most commonly prescribed medicines for the treatment of high blood pressure and heart failure [5,6]. Although this medicine is effective for control of diseases, around 50% of CPT is excreted by kidneys in unchanged form, contributing to water contamination [7]. Additionally, this pharmaceutical compound may cause diverse side effects and toxicity to organisms [8,9].
In this scenario, diverse methods have been explored for EPs removal from aqueous medium, such as Fenton [10], photocatalyst [11], ozonation [12], and adsorption [13,14]. The adsorption technique is characterized by the capture of contaminant (adsorbate) using a solid surface (adsorbent). This method presents advantages compared with other processes, such as low energy requirements and easy operation, without byproducts and generation of sludge [15]. Regarding the uptake of captopril, recent studies reported its removal using alternative materials from the biomass and lignocellulosic waste [9,16]. Considering the high consumption of captopril and the potential damage to health, and the limited studies that report its removal from the aquatic environment, it is necessary to use and design alternative and novel adsorbents. Additionally, nanotechnology is an excellent tool to enhance the process, using adsorbents at nanoscale, improving the properties and characteristics of conventional adsorbents, as well as the adsorption efficiency [17,18].
Among these, carbon nanomaterials, such as graphene oxide (GO) can be used in the adsorption process, due to the high specific surface area, reactivity, and presence of oxygenated groups [19]. Nonetheless, the unique properties of GO allow combination with other nanoparticles, as magnetic nanoparticles (MNPs), conferring new properties as well as avoiding the filtration and centrifugation steps. Recently, Li et al. [20] synthesized a magnetic nanocomposite with GO and hydroxyapatite for Pb (II) removal from water. The results demonstrate that nanomaterials exhibited a high adsorption capacity and maintained efficiency after several cycles of adsorption/desorption.
This work reports captopril adsorption using magnetic graphene oxide (GO·Fe3O4), synthesized through a straightforward method, using only Fe2+ as the iron source [21]. The adsorption behavior was evaluated using different experimental variables. The isotherm and kinetic models were used to understand the adsorption equilibrium and kinetic profile. Additionally, the adsorbent regeneration was investigated to determine the lifetime and efficiency after diverse adsorption/desorption processes. The mechanistical hypotheses for captopril adsorption onto graphene oxide-based magnetic adsorbent are also proposed, based on chemical species and magnetite incorporation on the GO surface.

2. Materials and Methods

2.1. Synthesis of Graphene Oxide and Graphene Oxide-Based Magnetic Nanoadsorbent

Graphene oxide was synthesized following Salles et al. [22]. 1 g of graphite in flakes (Sigma-Aldrich®, St. Louis, MO, USA) was added to a flask with 60 mL of H2SO4 98% (Synth®) under magnetic stirring for 10 min at room temperature. Sequentially, 6 g of KMnO4 99% (Synth®) was slowly added over 20 min. The solution was heated at 40 °C and stirred continuously for 5 h. Afterward, 180 mL of distilled H2O was slowly added and stirring for 12 h at room temperature. Sequentially, the reaction was heated at 40 °C for 2 h. Finally, 300 mL of distilled H2O and 10 mL of H2O2 29% (Synth®) was added into the solution. The yellow solution was washed until pH 5.0 and dried in an oven (DeLeo) at 50 °C for 24 h.
The magnetic graphene oxide was produced by the co-precipitation method [21]. In a 250 mL round-bottom flask containing 120 mL of ultrapure water, 100 mg of GO were added to 1000 mg of FeCl2 ≥ 99% (Sigma-Aldrich®). Afterwards, ammonium hydroxide (Synth®) was added to reach pH 9.0. Sequentially, the mixture was submitted to ultrasonic radiation (Elma, power 150 W) for 90 min at room temperature. Finally, the product was purified with distilled water and acetone (Synth®), and dried in an oven (DeLeo) at 50 °C for total solvents evaporation.

2.2. Adsorbent Characterization

Graphene oxide and magnetic graphene oxide were characterized by several different techniques. The functional groups were determined through the Fourier Transform spectroscopy (Perkin-Elmer, model Spectro One). The crystallinity was determined by X-ray diffraction (Bruker diffractometer, model D2 Phaser), and Raman Spectroscopy (Renishaw inVia spectrometer system). The morphological characteristics were evaluated using a scanning electron microscopic (Zeiss Sigma 300 VP). The magnetic properties were evaluated with a vibrating sample magnetometer (Stanford Research Systems Model SR830 DSP lock-in amplifier, coupled to a Stanford Research Systems low-noise pre-amplifier model SR560, including a Kepco bipolar operation power supply).
The zero point of charge (pHZPC) of MGO was evaluated by the following procedure. 10 mg of adsorbent was added to a 100 mL flask containing 50 mL of ultrapure water (Milli-Q®, Darmstadt, Germany) and pH adjusted in the range of (2.0–12.0) using NaOH (0.01 mol L−1) and HCl (0.01 mol L−1). Sequentially, the samples were maintained under stirring (120 rpm) for 24 h at room temperature. Subsequentially, the final pH was measured with a potentiometer (Digimed).

2.3. Adsorption Procedure and Mathematical Modeling

The captopril adsorption was performed in a batch system. The influence of magnetite was initially evaluated employing GO and GO·Fe3O4 to determine the effect of iron nanoparticles in GO surface on the adsorption efficiency. The adsorption equilibrium study was evaluated using 50 mg of GO·Fe3O4 and 50 mg L−1 of initial concentration of captopril, pH 3.0, and different temperatures (20 °C, 30 °C, and 40 °C). The adsorption kinetic was performed employing different concentrations of CPT ≥ 98% (10–200 mg L−1), 50 mg of adsorbent, at room temperature, and pH 3.0. Thermodynamic parameters were evaluated under the same conditions of the equilibrium study. Besides, this the influence of pH was verified in a pH range between 2.0 and 10.0, using HCl and NaOH solutions (0.1 mol L−1) for adjustment of the pH of the solution. The effect of ionic strength was performed employing a gradual NaCl concentration (0.01–1 mol L−1). Following this, the effect of initial concentration and adsorbent dosage were performed using 10–200 mg L−1 of CPT and 12.5–50 mg of GO·Fe3O4, respectively. The adsorbent regeneration was carried out employing NaOH (0.25 mol L−1) as the desorbing agent at room temperature for 1 h and 150 rpm. The residual concentration of CPT was measured using a UV-vis spectrophotometer (Shimadzu-1650PC) at λ = 217 nm. The removal percentage and adsorption capacity at equilibrium are shown in Table 1 [23].
Isotherms models were employed to understand the relationship between the adsorbate and adsorbent molecules. The Langmuir, Freundlich, and Sips models were used to fit the experimental results, and the equations are shown in Table 1 [24].
The kinetic study is useful to explain the mass transfer phenomenon and the effect of contact time on the adsorption rate. The models used in this work were Pseudo-first-order (PFO), Pseudo-second-order (PSO), and Elovich. Thermodynamic parameters were calculated by Van ‘t Hoff equation (Equation (10)) to determine the adsorption behavior [25,26]. The equilibrium and kinetic data were estimated through non-linear regression, using the Statistical 10 software (StatSoft, Tulsa, OK, USA). The coefficient of determination (R2), adjusted coefficient of determination (R2adj), sum of squared errors (SSE), and average relative error (ARE) were used to verify the validity of models, and mean square error (MSE) are shown in Table 1 [27].
The mathematical modeling used to calculate the adjustment parameters are shown in Table 1.

3. Results and Discussion

3.1. Fourier Transform Infrared Spectroscopy (FTIR)

The presence of functional groups was evaluated by FTIR analysis (Figure 1). According to the results, it was possible to observe an intense signal around 3405 cm−1, corresponding to the stretching vibration of OH groups in GO composition [28]. The bands at 1734, 1651, 1342, and 1048 cm−1 are related to the C=O stretch vibration, C=C bonds, C-OH vibration, and C-O bonds, respectively [29]. Besides this, for the GO·Fe3O4, it was possible to verify the appearance of band around 617 cm−1 characteristics of Fe-O, which suggests the presence of magnetite into GO surface [30,31].

3.2. X-ray Diffraction (XRD)

The XRD results of graphene oxide and magnetic graphene oxide are shown in Figure 2. The GO diffraction shows the characteristic signal around 2θ ≈ 10.5°, corresponding to the (001) plane, and the absence of a peak at 2θ ≈ 26° indicate the complete oxidation of graphite (precursor material) [32]. The peak at 2θ ≈ 44.2° (100) suggests a small distance between GO layers. For the GO with iron oxide nanoparticles, it was possible to verify the appearance of peaks around 2θ ≈ 30.3°, 35.2°, 43.5°, 57.02°, and 63.3°, corresponding to the indices (220), (311), (400), (511) and (440), typical of magnetite [33]. The position and intensity of all peaks are compatible with Fe3O4 (ICDD card no:88-0315). The absence of GO signal in the GO·Fe3O4 diffractogram is attributed to the surface coated by iron nanoparticles, which is possible to observe in SEM results (Figure 3) [21].

3.3. Scanning Electron Microscopy (SEM)

The morphology of GO and GO·Fe3O4 was determined by scanning electron microscopy (SEM) and is shown in Figure 3. For the GO (Figure 3a), it was possible to verify a wrinkles sheet, which is characteristic of a nanomaterial with few layers [34]. In Figure 3b, for the magnetic graphene oxide, the GO surface was covered by magnetite. The high amount of FeCl2 employed in the magnetization process results in a magnetic nanocomposite with high magnetic nanoparticle content [21].

3.4. Raman Spectroscopy

The Raman spectroscopy results are shown in Figure 4. The three bands can be observed for GO andgraphene oxide-based magnetic nanoadsorbent (GO∙Fe3O4). For both materials, it was possibile to observe the bands at 1366, 1580, and 2698 cm1 that represent the bands D (defects and disorder of graphite structure), G (sp2 vibration by carbon atoms), and 2D (second order of the D band), which is characteristic of graphene materials [21]. Additionally, the ID/IG ratio increased after the magnetization procedure, showing values of 0.96 and 1.22 for GO and GO·Fe3O4. The increases are related to the involvement of carbon atoms in partial Fe3+ reduction [35].
Nonetheless, the co-precipitation method is widely used to synthesize magnetic nanoparticles, due to the low energy requirements, low temperature, and high-quality products. In this work, the magnetization process increased the ID/IG ratio; however, the low values showed that the MGO was not significantly affected by the procedure. Alongside this, using ammonium hydroxide as a precipitant agent, the graphene structure was preserved, resulting in excellent magnetic graphene oxide surface and low values for ID/IG ratio [21]. Zhang et al. [36] synthesized a magnetic nanocomposite, employing a microwave absorbing method with a mixture of Fe2+ and Fe3+ (1:2 molar ratio). The results of ID/IG ratio showed a high disorder in the nanocomposite structure. Nevertheless, Hatel et al. [37] developed GO/Fe3O4 nanorods using ultrasonic radiation and NaOH as the precipitating agent. Raman spectroscopy results demonstrated a nanocomposite with a low crystallinity degree when compared to the GO sample.

3.5. Vibrating Sample Magnetometer (VSM)

Figure 5 shows the magnetization profile of magnetic graphene oxide at room temperature. According to the graph, it was possible to verify that GO·Fe3O4 presented a ferromagnetic behavior; magnetization saturation (MS), remanent magnetization (MR), and MR/MS ratio values were 45 emu g−1, 3.44 emu g−1, and 0.076, respectively. Similarly, Ghosh et al. [38] developed a magnetic GO functionalized with nitrogen groups, and the materials showed a ferromagnetic behavior.

3.6. Captopril Adsorption

3.6.1. Effect of Magnetite Incorporation onto Graphene Oxide Surface

The synthesis of nanocomposites is an important tool for the design of adsorbent materials with different characteristics and properties. In this study, the effect of the magnetite incorporation on the GO surface on the captopril adsorption behavior was evaluated (Figure 6).
According to Figure 6, it was possible to verify that both adsorbents exhibited excellent performance when removing the emerging pollutant. However, the graphene oxide-based magnetic adsorbent presented the highest adsorption capacity and removal percentage values compared to the pristine carbon nanomaterial. The GO and GO∙Fe3O4 display removal values of 91.42 and 99.43% and adsorption capacities of 91.84 and 99.41 mg g−1, respectively. The development of composite materials not only improve the physicochemical stability, but also can enhance their efficiency as an adsorbent. Recently, diverse studies have reported the effects of magnetite on the GO surface in terms of the adsorption performance [21,39,40].

3.6.2. Effect of Initial Concentration of CPT and Adsorbent Dosage

The initial adsorbate concentration and the adsorbent dosage play an important role in the adsorption efficiency, due to the higher ability to overcome the mass transfer resistance phenomenon and the more available surface area, respectively. Here, the effect of the initial concentration of CPT and GO∙Fe3O4 was investigated in the range of 10–200 mg L−1 and 0.125–1.0 g L−1, respectively.
The influence of CPT concentration is shown in Figure 7. Remarkably, the adsorption capacity values improved with the gradual increase in the initial concentration of CPT (e.g., the qe value raised from 14.68 to 390.31 mg g−1 when the CPT concentration was changed from 10 to 200 mg L−1), thus implying that CPT adsorption is favored at higher concentrations. However, the removal percentage displayed a slight decrease with rising concentration. The removal value reduced by around 23% from the lowest to the highest concentration. The improvement in the adsorption performance can be attributed to the higher concentration gradient, impelling the motions of the adsorbate to the boundary layer, favoring the interaction between the liquid phase and the solid phase (surface of the adsorbent) and, therefore, the mass transfer phenomenon [41,42].
Regarding the effect of adsorbent dosage (Figure 8), it was observed that an initial increase in the GO∙Fe3O4 mass lead to an improvement in the removal percentage values. However, at the highest dosages (0.75 and 1.0 g L−1), a slight reduction was verified (the removal value decreased from 99.43 to 88.71% when the adsorbent dosage changed from 0.5 to 1.0 g L−1). On the other hand, the adsorption capacity decreased inversely with the gradual rise in the adsorbent quantity. This is related to the imbalance between available adsorption sites and absorbate molecules, which is caused bt higher adsorbent dosages [43,44].

3.6.3. Effect of pH and Adsorption Mechanisms

The pH of the solution is an important experimental parameter, due to its influence on chemical speciation and adsorbent surface charge. The effect of pH on CPT adsorption was evaluated in the range of 2–9, keeping other parameters constant. At the same time, the zero potential of charge (pHZPC) was estimated by the typical 11-point experiment.
From the results presented in Figure 9, it was possible to observe that the pH had a significant effect on the adsorption capacity and removal percentage values. The adsorption was reached at pH 3.0 (qe = 99.41 mg g−1 and R% = 99.43). Captopril is a drug used for arterial hypertension that contains an ionizable group (-COOH, pKa = 3.7), i.e., it has an anionic character in this pH condition [45]. Under acidic conditions, the GO∙Fe3O4 presents a positive surface charge (pHZPC = 7.41), which allows the occurrence of electrostatic interactions between the adsorbent and adsorbate (pH 3.0). In contrast, in the range between 4–7, the adsorbent and captopril have a cationic characteristic, decreasing the affinity of adsorbate by binding sites. At the same time, in acidic media, the H+ ions can compete for the available active sites, justifying the considerable reduction in the adsorption performance. In addition, under alkaline conditions, the adsorbent material exhibits an anionic surface, also affecting the interaction between the systems [21].
Adsorption mechanisms are closely related to the chemical structure of the adsorbate, such as functional groups, aromaticity, hydrophilicity, and pH sensitivity (ionizable groups). Additionally, the interaction depends on the charge and specific surface area of the adsorbent material. Thus, some hypotheses regarding the CPT adsorption onto GO∙Fe3O4 were proposed (Figure 10). Considering the influence of pH solution on the chemical speciation of adsorbate and the adsorbent surface charge, this suggests that the captopril adsorption phenomenon is mainly governed by electrostatic interactions (optimal condition was reached at pH 3.0) [45,46]. Although attraction forces can act on the CPT removal, the abundance of oxygenated functional groups in nanoadsorbent structure and carboxylic acids on the captopril molecule also allows the occurrence of other interactions, such as hydrogen bonds (Yoshida H-bonding and dipole-dipole hydrogen bonding) [44,47].

3.6.4. Effect of Ionic Strength

The evaluation of the effect from diverse experimental conditions is an important requirement considering the potential application in wastewater treatment systems. In this study, the influence of ionic strength on CPT adsorption was performed using different concentrations of sodium chloride (0.01–1.0 mol L−1), keeping other parameters constant. As shown in Figure 11, it was possible to observe that an increase in NaCl molarity caused a considerable reduction in the adsorption capacity value. For instance, the system without NaCl presents a qe of 99.41 mg g−1, while, at a concentration of 1.0 mol L−1, the adsorption capacity was 32.38 mg g−1. The Na+ and Cl¯ ions can hamper the binding between the adsorbate and adsorbent due to the competition by adsorption sites. Additionally, the presence of inorganic salts may decrease the specific surface area, as well as reduce the solubility of the adsorbate [44,48,49].

3.6.5. Kinetic Modeling

Kinetic models are valuable mathematical expressions, widely used to understand the adsorption behavior in relation to the experimental time. In this work, three models were employed: pseudo-first-model, pseudo-second-order, and Elovich to construct the kinetic profile and calculate the adjustment parameters for captopril adsorption onto GO·Fe3O4. The kinetic study was conducted at room temperature using different concentrations of adsorbate. Table 2 shows the adjust of experimental data to nonlinear kinetic models.
According to the results presented in Table 2, it was possible to assume that the captopril adsorption onto graphene oxide-based magnetic nanoadsorbent was well-described by the Elovich model in all concentrations tested. This because the model exhibited high values for coefficient of determination (R2 ≥ 0.994) and low values for error functions (ARE, MSE and SSE). Additionally, the Elovich parameters related to sorption rate (α) and surface coverage (β), respectively, indicated that the adsorption occurs in the heterogeneous surface, i.e., the adsorbent exhibits adsorption sites with different energy levels [24,50].
The kinetic profile of captopril adsorption is shown in Figure 12. As demonstrated by kinetic curves, it was possible to verify that the adsorption presents a characteristic behavior of fast kinetic, with three different stages. In the first minutes, a high amount of adsorbate is removed, followed by a stationary phase (plateau) and, finally, equilibrium is achieved. In addition, the adsorption capacity at equilibrium is proportional to the initial concentration of the contaminant. The increase in adsorption efficiency can be attributed to greater ease when overcoming of the mass transfer phenomenon and effective occupation of binding sites [51].

3.6.6. Adsorption Equilibrium Isotherms and Thermodynamic Study

The isotherm models are useful mathematical expressions that help us to understand the interaction between adsorbate and adsorbent; they are also used to verify the influence of temperature in the adsorption equilibrium. In this present work, Langmuir, Freundlich, and Sips isotherm models were used to predict the best adjustment of equilibrium data at different temperatures. As shown in Table 3, it was possible to determine that the Sips isotherm was the best model to describe the CPT adsorption onto GO∙Fe3O4. Concerning values for coefficients of determination (R2) and error functions (ARE and SSE), the descending order of fit of the models is as follows:
Sips < Freundlich < Langmuir
The Sips model is a combined equation of the Langmuir and Freundlich isotherms, used to predict the adsorption on the heterogenous surface [52]. Regarding the Sips constant associated to the heterogeneity (ns), it is remarkable that the heterogeneity of the system increased with the temperature (ns = 2.26 at 20 °C and ns = 7.88 at 40 °C). Additionally, the maximum adsorption capacity estimated by this model decreased with the rise in the temperature, indicating that adsorption is an exothermic process (in agreement with the thermodynamic study) [45]. On the other hand, in the Sips constant related to equilibrium (Ks), a considerable decrease was observed with the gradual increase in temperature, i.e., suggesting that the process is disadvantaged at high temperatures [53].
Figure 13 shows the Sips isotherms curves. According to the results, it is possible to observe a characteristic “L-shape” type for 20 and 30 °C, indicating an adsorbent surface with a high presence of binding sites [54]. However, for 40 °C, the isotherm showed an “S-shape” suggesting a solute–solute attraction and/or an adsorption site competition [55].
To understand adsorption behavior under the influence of temperature, this study was performed at different conditions (293.15, 313.15, and 333.15 K). The thermodynamic equilibrium constant (Ke) was calculated using the KSips (best adjustment for isotherm model), and the captopril molecular weight (217.29 g mol−1) [16,56,57,58,59] Thermodynamic parameters for CPT adsorption onto GO·Fe3O4 were calculated by the Van ’t Hoff equation and are shown in Table 4. From the values for Gibbs free energy variation (ΔG0), it was possible to assume that the captopril adsorption was a thermodynamically favorable process [56]. Furthermore, the negative value for enthalpy change (ΔH0) indicated exothermic adsorption [47]. Additionally, the magnitude (−64.19 kJ mol−1) suggests that the adsorption phenomenon is mainly governed by chemical interactions [60]. Regarding the entropy change (ΔS0), the negative value is related to a decrease in the randomness of the system.
The adsorption performance was compared to previous studies employing different adsorbents and experimental conditions. It is possible to observe, in Table 5, that all the materials employed in CPT removal showed a removal percentage. Karperiski et al. [16] synthesized an activated carbon with ZnCl2 from Caesalpina ferrea (CFAC) and obtained a qmax of 535.5 mg g−1. The results showed that the best adsorbent performance was reached by CFCAC.1.5 and the process was spontaneous and favorable for removal of 97.67% of CPT from the aqueous solution. Cunha et al. [9] developed an activated carbon derivate from Butia catarinensis (ABc) with a high surface area (1267 m2 g−1) and with high efficiency removal (up to 99%). The maximum adsorption capacity was dependent on the temperature, rising with the temperature. In this work, magnetic graphene oxide removed up to 99.0% of the drug, with a high adsorption capacity (100.41 mg g−1) at pH 3.0. Therefore, the magnetite functionalization improved the adsorption process, allowing easy adsorbent regeneration and reusability and avoiding centrifugation/filtration steps.

3.6.7. Regeneration and Reuse

The study of the regeneration of adsorbents is a crucial step in the adsorption processes, aiming at the development and application of materials with high performance and cost-effectiveness. In this work, the regeneration of GO∙Fe3O4 was performed using a solution of sodium hydroxide (0.25 mol L−1), stirring at room temperature for 60 min. Thus, five consecutive adsorption-desorption cycles were conducted to estimate the efficiency for several experiments. According to Figure 14, it was possible to observe that the nanoadsorbent exhibits high efficiency, even after diverse cycles of regeneration and reuse. The percentage removal value displayed a slight decrease over time, which can be attributed to incomplete desorption and mass loss during the adsorbent recovery step [26,47].

4. Conclusions

The magnetic graphene oxide was synthesized employing a straightforward method with low energy requirements and easy operation. The FTIR, XRD, Raman, SEM, and VSM techniques demonstrated that the nanocomposite was successfully obtained, exhibiting excellent properties (crystalline structure with low defects) and high value for saturation magnetization (Ms = 45 emu g−1). The graphene oxide-based magnetic nanoadsorbent exhibits higher performance when compared with the pristine carbon nanomaterial. The maximum adsorption capacity and removal percentage (99.43% and 100.41 mg g−1) was reached at pH 3.0, using 50 mg of adsorbent, 50 mg L−1 of CPT, and 293.15 K. These results can be attributed to the synergic effect between graphene oxide and iron oxide nanoparticles. The pH dependence and influence of the adsorbent type suggested that the CPT adsorption onto GO∙Fe3O4 is mainly driven by electrostatic interactions and hydrogen bonds. Sips and Elovich models were well-suited to describe the equilibrium and adsorption kinetics data, assuming a process on a heterogeneous surface. The thermodynamic study inferred that the adsorption was spontaneous, exothermic, and occurred predominantly by chemical mechanisms. Additionally, the GO∙Fe3O4 demonstrated high efficiency after five adsorption/desorption cycles. From the experimental results, it can be concluded that the magnetic adsorbent is a promising material for wastewater management, especially regarding emerging pollutants like captopril.

Author Contributions

M.P.d.O., C.S.: Methodology, Investigation. T.d.R.S., F.d.S.B., L.B.: Investigation, Writing—Original Draft. E.I.M., W.J.d.S.G.: Visualization, Data Curation. A.H.d.O., L.F.O.S.: Visualization, Writing—Review & Editing. C.R.B.R.: Conceptualization, Writing—Review & Editing, Supervision ([email protected]). All authors have read and agreed to the published version of the manuscript.


This research received no external funding.

Data Availability Statement

Not applicable.


The authors thank Laboratório de Materiais Magnéticos Nanoestruturados—LaMMaN, Laboratório de Magnetismo e Materiais Magnéticos—LMMM, UFSM, and CAPES, CNPq, FAPERGS (TO 22/2551-0000609-4) for their support.

Conflicts of Interest

The authors declare no conflict of interest.


  1. Duarte, E.D.V.; Oliveira, M.G.; Spaolonzi, M.P.; Costa, H.P.S.; da Silva, T.L.; da Silva, M.G.C.; Vieira, M.G.A. Adsorption of Pharmaceutical Products from Aqueous Solutions on Functionalized Carbon Nanotubes by Conventional and Green Methods: A Critical Review. J. Clean. Prod. 2022, 372, 133743. [Google Scholar] [CrossRef]
  2. Ramos, S.; Homem, V.; Alves, A.; Santos, L. A Review of Organic UV-Filters in Wastewater Treatment Plants. Environ. Int. 2016, 86, 24–44. [Google Scholar] [CrossRef] [PubMed]
  3. Gavrilescu, M.; Demnerová, K.; Aamand, J.; Agathos, S.; Fava, F. Emerging Pollutants in the Environment: Present and Future Challenges in Biomonitoring, Ecological Risks and Bioremediation. N. Biotechnol. 2015, 32, 147–156. [Google Scholar] [CrossRef] [PubMed]
  4. Wang, L.; Chen, G.; Shu, H.; Cui, X.; Luo, Z.; Chang, C.; Zeng, A.; Zhang, J.; Fu, Q. Facile Covalent Preparation of Carbon Nanotubes / Amine-Functionalized Fe3O4 Nanocomposites for Selective Extraction of Estradiol in Pharmaceutical Industry Wastewater. J. Chromatogr. A 2021, 1638, 461889. [Google Scholar] [CrossRef]
  5. Xi, L.; Zhang, X.; Chen, Y.; Peng, J.; Liu, M.; Huo, D.; Li, G.; He, H. A Fluorescence Turn-on Strategy to Achieve Detection of Captopril Based on Ag Nanoclusters. Chem. Phys. Lett. 2022, 807, 140085. [Google Scholar] [CrossRef]
  6. Qu, F.; Zhu, G.; Huang, S.; Li, S.; Qiu, S. Effective controlled release of captopril by silylation of mesoporous MCM-41. ChemPhysChem 2006, 7, 400–406. [Google Scholar] [CrossRef]
  7. Mahmoud, W.M.M.; Kümmerer, K. Captopril and Its Dimer Captopril Disulfide: Photodegradation, Aerobic Biodegradation and Identification of Transformation Products by HPLC-UV and LC-Ion Trap-MS(n). Chemosphere 2012, 88, 1170–1177. [Google Scholar] [CrossRef]
  8. Da Silva, D.M.; Carneiro da Cunha Areias, M. Voltammetric Detection of Captopril in a Commercial Drug Using a Gold-Copper Metal-organic Framework Nanocomposite Modified Electrode. Electroanalysis 2021, 33, 1255–1263. [Google Scholar] [CrossRef]
  9. Cunha, M.R.; Lima, E.C.; Lima, D.R.; Da Silva, R.S.; Thue, P.S.; Seliem, M.K.; Sheir, F.; Dos Reis, G.S.; Larsson, S.H. Removal of captopril pharmaceutical from synthetic pharmaceutical-industry wastewaters: Use of activated carbon derived from Butia catarinensis. J. Environ. Chem. Eng. 2020, 8, 104506. [Google Scholar] [CrossRef]
  10. Alayli, A.; Nadaroglu, H.; Turgut, E. Nanobiocatalyst beds with Fenton process for removal of methylene blue. Appl. Water Sci. 2021, 11, 32. [Google Scholar] [CrossRef]
  11. Oviedo, L.R.; Muraro, P.C.L.; Pavoski, G.; Espinosa, D.C.R.; Ruiz, Y.P.M.; Galembeck, A.; Rhoden, C.R.B.; da Silva, W.L. Synthesis and Characterization of Nanozeolite from (Agro)Industrial Waste for Application in Heterogeneous Photocatalysis. Environ. Sci. Pollut. Res. Int. 2022, 29, 3794–3807. [Google Scholar] [CrossRef] [PubMed]
  12. Sani, O.N.; Yazdani, M.; Taghavi, M. Catalytic ozonation of ciprofloxacin using γ-Al2O3 nanoparticles in synthetic and real wastewaters. J. Water Process Eng. 2019, 32, 100894. [Google Scholar] [CrossRef]
  13. Erdem, S.; Öztekin, M.; Açıkel, Y.S. Investigation of tetracycline removal from aqueous solutions using halloysite/chitosan nano-composites and halloysite nanotubes/alginate hydrogel beads. Environ. Nanotechnol. Monit. Manag. 2021, 16, 100576. [Google Scholar]
  14. Ciğeroğlu, Z.; Kazan-Kaya, E.S.; El Messaoudi, N.; Fernine, Y.; Américo-Pinheiro, J.H.P.; Jada, A. Remediation of tetracycline from aqueous solution through adsorption on g-C3N4-ZnO-BaTiO3 nanocomposite: Optimization, modeling, and theoretical calculation. J. Mol. Liq. 2022, 369, 120866. [Google Scholar] [CrossRef]
  15. Silveira, C.C.; Botega, C.S.; Rhoden, C.R.B.; Nunes, M.R.S.; Braga, A.L.; Lenardão, E.J. A Facile Synthesis of α-Phenylchalcogeno(S, Se) α,β-Unsaturated Esters from Ethyl α-Bromo-α-Phenylchalcogeno Acetates. Synth. Commun. 1998, 28, 3371–3380. [Google Scholar] [CrossRef]
  16. Kasperiski, F.M.; Lima, E.C.; Umpierres, C.S.; Dos Reis, G.S.; Thue, P.S.; Lima, D.R.; Dias, S.L.P.; Saucier, C.; Da Costa, J.B. Production of porous activated carbons from Caesalpinia ferrea seed pod wastes: Highly efficient removal of captopril from aqueous solutions. J. Clean. Prod. 2018, 197, 919–929. [Google Scholar] [CrossRef]
  17. Singh, S.; Kumar, V.; Anil, A.G.; Kapoor, D.; Khasnabis, S.; Shekar, S.; Pavithra, N.; Samuel, J.; Subramanian, S.; Singh, J.; et al. Adsorption and Detoxification of Pharmaceutical Compounds from Wastewater Using Nanomaterials: A Review on Mechanism, Kinetics, Valorization and Circular Economy. J. Environ. Manag. 2021, 300, 113569. [Google Scholar] [CrossRef]
  18. El Messaoudi, N.; El Mouden, A.; Fernine, Y.; El Khomri, M.; Bouich, A.; Faska, N.; Ciğeroğlu, Z.; Américo-Pinheiro, J.H.P.; Jada, A.; Lacherai, A. Green synthesis of Ag2O nanoparticles using Punica granatum leaf extract for sulfamethoxazole antibiotic adsorption: Characterization, experimental study, modeling, and DFT calculation. Environ. Sci. Pollut. Res. 2022, 29, 1–18. [Google Scholar] [CrossRef]
  19. Singh, S.; Anil, A.G.; Khasnabis, S.; Kumar, V.; Nath, B.; Adiga, V.; Kumar Naik, T.S.S.; Subramanian, S.; Kumar, V.; Singh, J.; et al. Sustainable Removal of Cr(VI) Using Graphene Oxide-Zinc Oxide Nanohybrid: Adsorption Kinetics, Isotherms and Thermodynamics. Environ. Res. 2022, 203, 111891. [Google Scholar] [CrossRef]
  20. Li, R.; Liu, Y.; Lan, G.; Qiu, H.; Xu, B.; Xu, Q.; Sun, N.; Zhang, L. Pb(II) Adsorption Characteristics of Magnetic GO-Hydroxyapatite and the Contribution of GO to Enhance Its Acid Resistance. J. Environ. Chem. Eng. 2021, 9, 105310. [Google Scholar] [CrossRef]
  21. Rhoden, C.R.B.; Bruckmann, F.d.S.; Salles, T.d.R.; Kaufmann Junior, C.G.; Mortari, S.R. Study from the Influence of Magnetite onto Removal of Hydrochlorothiazide from Aqueous Solutions Applying Magnetic Graphene Oxide. J. Water Proc. Eng. 2021, 43, 102262. [Google Scholar] [CrossRef]
  22. Salles, T.d.R.; Rodrigues, H.d.B.; Bruckmann, F.d.S.; Alves, L.C.S.; Mortari, S.R.; Rhoden, C.R.B. Graphene Oxide Optimization Synthesis for Application on Laboratory of Universidade Franciscana. Discip. Sci. 2020, 21, 15–26. [Google Scholar] [CrossRef]
  23. Bruckmann, F.d.S.; Zuchetto, T.; Ledur, C.M.; dos Santos, C.L.; da Silva, W.L.; Binotto Fagan, S.; Zanella da Silva, I.; Bohn Rhoden, C.R. Methylphenidate Adsorption onto Graphene Derivatives: Theory and Experiment. New J. Chem. 2022, 46, 4283–4291. [Google Scholar] [CrossRef]
  24. Bruckmann, F.S.; Schnorr, C.; Oviedo, L.R.; Knani, S.; Silva, L.F.O.; Silva, W.L.; Dotto, G.L.; Bohn Rhoden, C.R. Adsorption and Photocatalytic Degradation of Pesticides into Nanocomposites: A Review. Molecules 2022, 27, 6261. [Google Scholar] [CrossRef]
  25. Tran, H.N.; You, S.-J.; Chao, H.-P. Thermodynamic Parameters of Cadmium Adsorption onto Orange Peel Calculated from Various Methods: A Comparison Study. J. Environ. Chem. Eng. 2016, 4, 2671–2682. [Google Scholar] [CrossRef]
  26. Da Rosa Salles, T.; Da Silva Bruckamann, F.; Viana, A.R.; Krause, L.M.F.; Mortari, S.R.; Rhoden, C.R.B. Magnetic nanocrystalline cellulose: Azithromycin adsorption and in vitro biological activity against melanoma cells. J. Polym. Environ. 2022, 30, 2695–2713. [Google Scholar] [CrossRef]
  27. Cimirro, F.N.; Lima, C.E.; Cunha, M.R.; Dias, S.L.; Thue, P.S.; Mazzocato, A.C.; Dotto, G.L.; Gelesky, M.A.; Pavan, F.A. Removal of pharmaceutical compounds from aqueous solution by novel activated carbon synthesized from lovegrass (Poaceae). Environ. Sci. Pollut. Res. 2020, 27, 21442–21454. [Google Scholar] [CrossRef]
  28. Kanta, U.-A.; Thongpool, V.; Sangkhun, W.; Wongyao, N.; Wootthikanokkhan, J. Preparations, Characterizations, and a Comparative Study on Photovoltaic Performance of Two Different Types of Graphene/TiO2 Nanocomposites Photoelectrodes. J. Nanomater. 2017, 2017, 2758294. [Google Scholar] [CrossRef] [Green Version]
  29. Ossonon, B.D.; Bélanger, D. Synthesis and Characterization of Sulfophenyl-Functionalized Reduced Graphene Oxide Sheets. RSC Adv. 2017, 7, 27224–27234. [Google Scholar] [CrossRef] [Green Version]
  30. Da Silva Bruckmann, F.; Viana, A.R.; Lopes, L.Q.S.; Santos, R.C.V.; Muller, E.I.; Mortari, S.R.; Rhoden, C.R.B. Synthesis, Characterization, and Biological Activity Evaluation of Magnetite-Functionalized Eugenol. J. Inorg. Organomet. Polym. Mater. 2022, 32, 1459–1472. [Google Scholar] [CrossRef]
  31. Bruckmann, F.d.S.; Pimentel, A.C.; Viana, A.R.; Salles, T.d.R.; Krause, L.M.F.; Mortari, S.R.; da Silva, I.Z.; Rhoden, C.R.B. Synthesis, Characterization and Cytotoxicity Evaluation of Magnetic Nanosilica in L929 Cell Line. Discip. Sci. 2020, 21, 1–14. [Google Scholar] [CrossRef]
  32. Ain, Q.T.; Haq, S.H.; Alshammari, A.; Al-Mutlaq, M.A.; Anjum, M.N. The Systemic Effect of PEG-NGO-Induced Oxidative Stress in Vivo in a Rodent Model. Beilstein J. Nanotechnol. 2019, 10, 901–911. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  33. Liu, J.; Xu, D.; Chen, P.; Yu, Q.; Qiu, H.; Xiong, X. Solvothermal Synthesis of Porous Superparamagnetic RGO@Fe3O4 Nanocomposites for Microwave Absorption. J. Mater. Sci. Mater. Electron. 2019, 30, 17106–17118. [Google Scholar] [CrossRef]
  34. Kellici, S.; Acord, J.; Ball, J.; Reehal, H.S.; Morgan, D.; Saha, B. A Single Rapid Route for the Synthesis of Reduced Graphene Oxide with Antibacterial Activities. RSC Adv. 2014, 4, 14858–14861. [Google Scholar] [CrossRef]
  35. Côa, F.; Strauss, M.; Clemente, Z.; Rodrigues Neto, L.L.; Lopes, J.R.; Alencar, R.S.; Souza Filho, A.G.; Alves, O.L.; Castro, V.L.S.S.; Barbieri, E.; et al. Coating Carbon Nanotubes with Humic Acid Using an Eco-Friendly Mechanochemical Method: Application for Cu(II) Ions Removal from Water and Aquatic Ecotoxicity. Sci. Total Environ. 2017, 607–608, 1479–1486. [Google Scholar] [CrossRef] [PubMed]
  36. Zhang, K.; Zhang, Q.; Gao, X.; Chen, X.; Wang, Y.; Li, W.; Wu, J. Effect of absorbers’ composition on the microwave absorbing performance of hollow Fe3O4 nanoparticles decorated CNTs/graphene/C composites. J. Alloys Compd. 2018, 748, 70–716. [Google Scholar] [CrossRef]
  37. Hatel, R.; Majdoub, S.E.; Bakour, A.; Khenfouch, M.; Baitoul, M. Graphene Oxide/Fe3O4 Nanorods Composite: Structural and Raman Investigation. J. Phys. Conf. Ser. 2018, 1081, 012006. [Google Scholar] [CrossRef] [Green Version]
  38. Ghosh, B.; Sarma, S.; Pontsho, M.; Ray, S.C. Tuning of Magnetic Behaviour in Nitrogenated Graphene Oxide Functionalized with Iron Oxide. Diam. Relat. Mater. 2018, 89, 35–42. [Google Scholar] [CrossRef]
  39. Da Silva Bruckmann, F.; Mafra Ledur, C.; Zanella da Silva, I.; Luiz Dotto, G.; Rodrigo Bohn Rhoden, C. A DFT Theoretical and Experimental Study about Tetracycline Adsorption onto Magnetic Graphene Oxide. J. Mol. Liq. 2022, 353, 118837. [Google Scholar] [CrossRef]
  40. Cheng, Y.; Yang, S.; Tao, E. Magnetic graphene oxide prepared via ammonia coprecipitation method: The effects of preserved functional groups on adsorption property. Inorg. Chem. Commun. 2021, 128, 108603. [Google Scholar] [CrossRef]
  41. Zeng, K.; Hachem, K.; Kuznetsova, M.; Chupradit, S.; Su, C.H.; Nguyen, H.C.; El-Shafay, A.S. Molecular dynamic simulation and artificial intelligence of lead ions removal from aqueous solution using magnetic-ash-graphene oxide nanocomposite. J. Mol. Liq. 2022, 347, 118290. [Google Scholar] [CrossRef]
  42. Nuengmatcha, P.; Mahachai, R.; Chanthai, S. Thermodynamic and kinetic study of the intrinsic adsorption capacity of graphene oxide for malachite green removal from aqueous solution. Orient. J. Chem. 2014, 30, 1463. [Google Scholar] [CrossRef] [Green Version]
  43. Nasiri, A.; Rajabi, S.; Amiri, A.; Fattahizade, M.; Hasani, O.; Lalehzari, A.; Hashemi, M. Adsorption of tetracycline using CuCoFe2O4@ Chitosan as a new and green magnetic nanohybrid adsorbent from aqueous solutions: Isotherm, kinetic and thermodynamic study. Arab. J. Chem. 2022, 15, 104014. [Google Scholar] [CrossRef]
  44. Da Silva Bruckmann, F.; Schnorr, C.E.; Da Rosa Salles, T.; Nunes, F.B.; Baumann, L.; Müller, E.I.; Silva, L.F.O.; Dotto, G.L.; Bohn Rhoden, C.R. Highly Efficient Adsorption of Tetracycline Using Chitosan-Based Magnetic Adsorbent. Polymers 2022, 14, 4854. [Google Scholar] [CrossRef]
  45. Pereira, A.V.; Garabeli, A.A.; Schunemann, G.D.; Borck, P.C. Determination of dissociation constant (Ka) of captopril and nimesulide: Analytical chemistry experiments for undergraduate pharmacy. Quim Nova 2011, 34, 1656–1660. [Google Scholar] [CrossRef] [Green Version]
  46. Zhu, H.; Chen, T.; Liu, J.; Li, D. Adsorption of tetracycline antibiotics from an aqueous solution onto graphene oxide/calcium alginate composite fibers. RSC Adv. 2018, 8, 2616–2621. [Google Scholar] [CrossRef] [Green Version]
  47. Bruckmann, F.S.; Rossato Viana, A.; Tonel, M.Z.; Fagan, S.B.; Garcia, W.J.D.S.; Oliveira, A.H.D.; Dorneles, L.S.; Mortari, S.R.; Da Silva, W.L.; Da Silva, I.Z.; et al. Influence of magnetite incorporation into chitosan on the adsorption of the methotrexate and in vitro cytotoxicity. Environ. Sci. Pollut. Res. 2022, 29, 70413–70434. [Google Scholar] [CrossRef]
  48. Ji, L.; Chen, W.; Bi, J.; Zheng, S.; Xu, Z.; Zhu, D.; Alvarez, P.J. Adsorption of tetracycline on single-walled and multi-walled carbon nanotubes as affected by aqueous solution chemistry. Environ. Toxicol. Chem. 2010, 29, 2713–2719. [Google Scholar] [CrossRef]
  49. Liang, J.; Fang, Y.; Luo, Y.; Zeng, G.; Deng, J.; Tan, X.; Tang, N.; Li, X.; He, X.; Feng, C.; et al. Magnetic nanoferromanganese oxides modified biochar derived from pine sawdust for adsorption of tetracycline hydrochloride. Environ. Sci. Pollut. Res. 2019, 26, 5892–5903. [Google Scholar] [CrossRef]
  50. Agarry, S.E.; Aworanti, O.A. Kinetics, Isothermal and Thermodynamic Modelling Studies of Hexavalent Chromium Ions Adsorption from Simulated Wastewater onto Parkia biglobosa-Sawdust Derived Acid-Steam Activated Carbon. Appl. J. Envir. Eng. Sci. 2017, 3, 58–76. [Google Scholar]
  51. De Souza, F.M.; Dos Santos, O.A.A.; Vieira, M.G.A. Adsorption of herbicide 2,4-D from aqueous solution using organo-modified bentonite clay. Environ. Sci. Pollut. Res. 2019, 26, 18329–18342. [Google Scholar] [CrossRef] [PubMed]
  52. Nunes, F.B.; Da Silva Bruckmann, F.; Da Rosa Salles, T.; Rhoden, C.B.R. Study of phenobarbital removal from the aqueous solutions employing magnetite-functionalized chitosan. Environ. Sci. Pollut. Res. 2022, 29, 1–14. [Google Scholar] [CrossRef] [PubMed]
  53. Carvajal-Bernal, A.M.; Gomez-Granados, F.; Giraldo, L.; Moreno-Pirajan, J.C. Application of the Sips model to the calculation of maximum adsorption capacity and immersion enthalpy of phenol aqueous solutions on activated carbons. Eur. J. Chem. 2017, 8, 112–118. [Google Scholar] [CrossRef] [Green Version]
  54. Kalam, S.; Abu-Khamsin, S.A.; Kamal, M.S.; Patil, S. Surfactant Adsorption Isotherms: A Review. ACS Omega 2021, 6, 32342–32348. [Google Scholar] [CrossRef]
  55. Gago, D.; Chagas, R.; Ferreira, L.M.; Velizarov, S.; Coelhoso, I. A Novel Cellulose-Based Polymer for Efficient Removal of Methylene Blue. Membranes 2020, 10, 13. [Google Scholar] [CrossRef] [Green Version]
  56. Salvstrini, S.; Ambrosone, L.; Kopinke, F.D. Some mistakes and misinterpretations in the analysis of thermodynamic adsorption data. J. Mol. Liq. 2022, 352, 118762. [Google Scholar] [CrossRef]
  57. Tran, H.N. Improper Estimation of Thermodynamic Parameters in Adsorption Studies with Distribution Coefficient KD (Qe/Ce) or Freundlich Constant (KF): Considerations from the Derivation of Dimensionless Thermodynamic Equilibrium Constant and Suggestions. Adsorp. Sci. Technol. 2022, 2022, 5553212. [Google Scholar] [CrossRef]
  58. Lima, E.C.; Hosseini-Bandegharaei, A.; Moreno-Piraján, J.C.; Anastopoulos, I. A Critical Review of the Estimation of the Thermodynamic Parameters on Adsorption Equilibria. Wrong Use of Equilibrium Constant in the Van’t Hoof Equation for Calculation of Thermodynamic Parameters of Adsorption. J. Mol. Liq. 2019, 273, 425–434. [Google Scholar] [CrossRef]
  59. Tran, H.N.; Lima, E.C.; Juang, R.-S.; Bollinger, J.-C.; Chao, H.-P. Thermodynamic Parameters of Liquid–Phase Adsorption Process Calculated from Different Equilibrium Constants Related to Adsorption Isotherms: A Comparison Study. J. Environ. Chem. Eng. 2021, 9, 106674. [Google Scholar] [CrossRef]
  60. Dotto, G.L.; Moura, J.M.D.; Cadaval, T.R.S.; Pinto, L.A.D.A. Application of chitosan films for the removal of food dyes from aqueous solutions by adsorption. Chem. Eng. J. 2013, 214, 8–16. [Google Scholar] [CrossRef]
  61. Li, Z.; Wu, D.; Liang, Y.; Xu, F.; Fu, R. Facile Fabrication of Novel Highly Microporous Carbons with Superior Size-Selective Adsorption and Supercapacitance Properties. Nanoscale 2013, 5, 10824–10828. [Google Scholar] [CrossRef] [PubMed]
Figure 1. FTIR of GO and GO·Fe3O4.
Figure 1. FTIR of GO and GO·Fe3O4.
Water 15 00293 g001
Figure 2. XRD of (a) GO and (b) GO·Fe3O4.
Figure 2. XRD of (a) GO and (b) GO·Fe3O4.
Water 15 00293 g002
Figure 3. SEM of (a) GO and (b) GO·Fe3O4.
Figure 3. SEM of (a) GO and (b) GO·Fe3O4.
Water 15 00293 g003
Figure 4. Raman spectroscopy of GO and GO·Fe3O4.
Figure 4. Raman spectroscopy of GO and GO·Fe3O4.
Water 15 00293 g004
Figure 5. VSM of GO·Fe3O4.
Figure 5. VSM of GO·Fe3O4.
Water 15 00293 g005
Figure 6. Effect of magnetite incorporation onto the graphene oxide surface. Adsorbent dosage (0.5 g L−1), initial concentration of CPT (50 mg L−1), pH 3.0, and 293.15 K.
Figure 6. Effect of magnetite incorporation onto the graphene oxide surface. Adsorbent dosage (0.5 g L−1), initial concentration of CPT (50 mg L−1), pH 3.0, and 293.15 K.
Water 15 00293 g006
Figure 7. Effect of the initial concentration of CPT (GO·Fe3O4 dosage (0.5 g L−1), C0 = 10−200 mg L−1, pH 3.0, and 293.15 K).
Figure 7. Effect of the initial concentration of CPT (GO·Fe3O4 dosage (0.5 g L−1), C0 = 10−200 mg L−1, pH 3.0, and 293.15 K).
Water 15 00293 g007
Figure 8. Effect of the adsorbent dosage on CPT adsorption (GO·Fe3O4 dosage (0.125–1.0 g L−1), initial concentration of CPT (50 mg L−1), pH 3.0, and 293.15 K).
Figure 8. Effect of the adsorbent dosage on CPT adsorption (GO·Fe3O4 dosage (0.125–1.0 g L−1), initial concentration of CPT (50 mg L−1), pH 3.0, and 293.15 K).
Water 15 00293 g008
Figure 9. (a) Effect of pH on CPT adsorption (C0 = 50 mg L−1, pH = 2–9, adsorbent dosage = 0.5 g L−1, V = 100 mL, and 293.15 K) and (b) Zero point of charge of GO∙Fe3O4.
Figure 9. (a) Effect of pH on CPT adsorption (C0 = 50 mg L−1, pH = 2–9, adsorbent dosage = 0.5 g L−1, V = 100 mL, and 293.15 K) and (b) Zero point of charge of GO∙Fe3O4.
Water 15 00293 g009
Figure 10. Hypotheses of the captopril adsorption mechanism.
Figure 10. Hypotheses of the captopril adsorption mechanism.
Water 15 00293 g010
Figure 11. Effect of ionic strenght on CPT adsorption (C0 = 50 mg L−1, pH = 3.0, adsorbent dosage = 0.5 g L−1, NaCl concentration (0.01–1.0 mol L−1), V = 100 mL, and 293.15 K).
Figure 11. Effect of ionic strenght on CPT adsorption (C0 = 50 mg L−1, pH = 3.0, adsorbent dosage = 0.5 g L−1, NaCl concentration (0.01–1.0 mol L−1), V = 100 mL, and 293.15 K).
Water 15 00293 g011
Figure 12. Kinetic curves for CPT adsorption onto GO·Fe3O4.
Figure 12. Kinetic curves for CPT adsorption onto GO·Fe3O4.
Water 15 00293 g012
Figure 13. Sips model for CPT adsorption onto GO·Fe3O4.
Figure 13. Sips model for CPT adsorption onto GO·Fe3O4.
Water 15 00293 g013
Figure 14. GO·Fe3O4 performance after several adsorption cycles.
Figure 14. GO·Fe3O4 performance after several adsorption cycles.
Water 15 00293 g014
Table 1. Equations of removal percentage, adsorption capacity, adsorption isotherms, kinetics, thermodynamics models, and mathematical modelling.
Table 1. Equations of removal percentage, adsorption capacity, adsorption isotherms, kinetics, thermodynamics models, and mathematical modelling.
Removal Percentage and Adsorption CapacityMathematical ExpressionParameters
Removal percentage R % = C 0 C e C 0   ×   100 (1)C0 is the initial concentration of CPT (mg L−1); Ce is the concentration of CPT at equilibrium (mg L−1), qe is the adsorption capacity at equilibrium; V is the volume (L); m is the mass of adsorbent material (g)
Adsorption capacity q e = C 0 C e   V m (2)
Isotherm modelsMathematical expressionParameters
Langmuir q e = q m a x   K L . C e 1 + K L   C e (3)qmax- maximum amount adsorbed (mg g−1); KL- is the Langmuir isotherm constant (L g−1)
Freundlich q e = K F ·   C e 1 / n (4)KF- Freundlich constant ((mg g−1) (L mg−1)−1/n); n- heterogeneity factor
Sips q e = q S i p s K S i p s C e n S i p s 1 + K S i p s C e n S i p s (5)KSips- Sips isotherm constant (L mg−1); qSips- maximum amount adsorbed (mg g−1); nSips- heterogeneity factor
Kinetic modelsMathematical expressionParameters
Pseudo-first-order q t = q 1 1 e k 1 · t (6)k1- pseudo-first-order kinetic constant (min−1)
Pseudo-second-order q t = t 1 k 2 · q 2 2 + t q 2 (7)k2- pseudo-second-order kinetic constant (mg g−1 min−1)
Elovich q e = 1 β   ln α β t + 1 (8)α- initial adsorption rate (mg g−1 min−1); β- desorption constant (g mg−1)
ThermodynamicMathematical expressionParameters
Gibbs free energy variation (ΔG0) Δ G ° = R T   l n K e   (9)R- gas constant (8.314 J mol−1 K−1); T- absolute temperature (K); Kd- thermodynamic equilibrium constant
van’t Hoff l n K e = Δ S ° R + Δ H ° R T (10)
Relationship of Gibbs free energy(ΔG0), Enthalpy (ΔH0) and entropy (ΔS0) variation         Δ G ° = Δ H ° T Δ S ° (11)
Mathematical modelingMathematical expressionParameters
Adjusted coefficient of determination (R2adj) R a d j 2 = 1 1 R 2 n 1 n k 1 (12)qe,exp and qe,pred are the adsorbed amounts obtained from the experiment and the isotherm and kinetic model, respectively; n is the amount of data; k is the number of parameters in the model
Sum squares error (SSE) S S E = 1 n i = 1 n q e ,   e x p q e ,   p r e d 2 (13)
Average relative error (ARE) A R E = 100 n i = 1 n q e ,   e x p q e ,   p r e d q e ,   e x p (14)
Mean square error (MSE) MSE = 1 n p i = 1 n q e , exp q e , pred 2 (15)qe,exp is the experimental value; qe,pred is the predicted value; n is the number of experimental values; p is the number of parameters according to the model.
Table 2. Kinetic parameters for captopril adsorption onto GO·Fe3O4.
Table 2. Kinetic parameters for captopril adsorption onto GO·Fe3O4.
Concentration (mg L−1)102550100200
Pseudo-first-order model (PFO)
q1 (mg g−1)13.44 ± 0.34 a45.69 ± 0.9796.06 ± 0.91186.32 ± 1.81386.58 ± 0.60
k1 (min−1)0.375 ± 0.110.205 ± 0.040.606 ± 0.150.403 ± 0.050.804 ± 0.05
ARE (%)5.674.282.091.960.25
MSE (mg g−1)21.339.699.0638.173.94
Pseudo-second-order model (PSO)
q2 (mg g−1)13.59 ± 0.3547.99 ± 0.6297.03 ± 0.87190.11 ± 1.21387.53 ± 0.48
k2 (g mg−1 min−1)0.049 ± 0.020.007 ± 0.0010.025 ± 0.010.005 ± 0.0010.023 ± 0.004
ARE (%)5.041.971.821.112.59
MSE (mg g−1)20.833.366.1711.259.98
Elovich model
α (mg g−1 min−1)10.48 ± 0.2115.35 ± 0.5916.62 ± 1.024.57 ± 0.973.95 ± 1.02
β (g mg−1)0.997 ± 0.010.222 ± 0.050.273 ± 0.0260.118 ± 0.020.066 ± 0.002
ARE (%)2.532.881.020.620.19
MSE (mg g−1)
a (Mean ± standard deviation).
Table 3. Equilibrium parameters for CPT adsorption onto GO·Fe3O4.
Table 3. Equilibrium parameters for CPT adsorption onto GO·Fe3O4.
Temperature20 °C30 °C40 °C
qmax (mg g−1)101.93 ± 1.76 a101.49 ± 3.3599.28 ± 5.96
KL (L mg−1)0.771 ± 0.460.43 ± 0.0550.057 ± 0.97
ARE (%)3.825.694.92
MSE (mg g−1)216.3817.4219.55
KF ((mg g−1) (L−1)−1/n74.51 ± 2.215.01 ± 3.322.61 ± 1.97
n10.95 ± 3.2945.85 ± 2.0516.54 ± 1.44
ARE (%)3.841.991.01
MSE (mg g−1)29.775.6715.43
qs (mg g−1)100.41 ± 0.9790.47 ± 1.1970.72 ± 2.56
Ks (L mg−1)0.444 ± 0.140.255 ± 0.650.082 ± 0.001
ns2.26 ± 1.153.91 ± 1.747.88 ± 0.68
ARE (%)1.241.840.09
MSE (mg g−1)23.412.483.01
a (Mean ± standard deviation).
Table 4. Thermodynamic parameters for CPT adsorption onto GO·Fe3O4.
Table 4. Thermodynamic parameters for CPT adsorption onto GO·Fe3O4.
T(K)KeΔG0 (kJ mol−1)ΔH0 (kJ mol−1)ΔS0 (kJ mol−1 K−1)
Table 5. Removal percentage of different adsorbents of CPT.
Table 5. Removal percentage of different adsorbents of CPT.
AdsorbentspHRemoval (%)Reference
Activated carbon functionalized with ZnCl27.097.67[16]
Activated carbon derivate from Butia catarinensis7.0<99.0[9]
Microporous carbonsNot informed97.0[61]
Magnetic graphene oxide3.0<99This work
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.

Share and Cite

MDPI and ACS Style

de Oliveira, M.P.; Schnorr, C.; da Rosa Salles, T.; da Silva Bruckmann, F.; Baumann, L.; Muller, E.I.; da Silva Garcia, W.J.; de Oliveira, A.H.; Silva, L.F.O.; Rhoden, C.R.B. Efficient Uptake of Angiotensin-Converting Enzyme II Inhibitor Employing Graphene Oxide-Based Magnetic Nanoadsorbents. Water 2023, 15, 293.

AMA Style

de Oliveira MP, Schnorr C, da Rosa Salles T, da Silva Bruckmann F, Baumann L, Muller EI, da Silva Garcia WJ, de Oliveira AH, Silva LFO, Rhoden CRB. Efficient Uptake of Angiotensin-Converting Enzyme II Inhibitor Employing Graphene Oxide-Based Magnetic Nanoadsorbents. Water. 2023; 15(2):293.

Chicago/Turabian Style

de Oliveira, Miguel Pereira, Carlos Schnorr, Theodoro da Rosa Salles, Franciele da Silva Bruckmann, Luiza Baumann, Edson Irineu Muller, Wagner Jesus da Silva Garcia, Artur Harres de Oliveira, Luis F. O. Silva, and Cristiano Rodrigo Bohn Rhoden. 2023. "Efficient Uptake of Angiotensin-Converting Enzyme II Inhibitor Employing Graphene Oxide-Based Magnetic Nanoadsorbents" Water 15, no. 2: 293.

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop