Next Article in Journal
Boronic Acid Esters and Anhydrates as Dynamic Cross-Links in Vitrimers
Next Article in Special Issue
Optimizing the Surface Structural and Morphological Properties of Silk Thin Films via Ultra-Short Laser Texturing for Creation of Muscle Cell Matrix Model
Previous Article in Journal
Effectiveness and Productivity Improvement of Conventional Pultrusion Processes
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Antibiotic-Loaded Polymeric Barrier Membranes for Guided Bone/Tissue Regeneration: A Mini-Review

by
Manuel Toledano-Osorio
1,
Cristina Vallecillo
1,
Marta Vallecillo-Rivas
1,
Francisco-Javier Manzano-Moreno
1,2,3,* and
Raquel Osorio
1
1
Faculty of Dentistry, Colegio Máximo de Cartuja s/n, University of Granada, 18071 Granada, Spain
2
Biomedical Group (BIO277), Department of Stomatology, Facultad de Odontología, University of Granada, 18071 Granada, Spain
3
Instituto Investigación Biosanitaria ibs.GRANADA, University of Granada, C/Doctor Azpitarte 4, Planta, 18012 Granada, Spain
*
Author to whom correspondence should be addressed.
Polymers 2022, 14(4), 840; https://doi.org/10.3390/polym14040840
Submission received: 31 January 2022 / Revised: 14 February 2022 / Accepted: 17 February 2022 / Published: 21 February 2022
(This article belongs to the Special Issue Synthesis of Polymer Membranes and Their Applications)

Abstract

:
Polymeric membranes are frequently used for bone regeneration in oral and periodontal surgery. Polymers provide adequate mechanical properties (i.e., Young’s modulus) to support oral function and also pose some porosity with interconnectivity to permit for cell proliferation and migration. Bacterial contamination of the membrane is an event that may lead to infection at the bone site, hindering the clinical outcomes of the regeneration procedure. Therefore, polymeric membranes have been proposed as carriers for local antibiotic therapy. A literature search was performed for papers, including peer-reviewed publications. Among the different membranes, collagen is the most employed biomaterial. Collagen membranes and expanded polytetrafluoroethylene loaded with tetracyclines, and polycaprolactone with metronidazole are the combinations that have been assayed the most. Antibiotic liberation is produced in two phases. A first burst release is sometimes followed by a sustained liberation lasting from 7 to 28 days. All tested combinations of membranes and antibiotics provoke an antibacterial effect, but most of the time, they were measured against single bacteria cultures and usually non-specific pathogenic bacteria were employed, limiting the clinical relevance of the attained results. The majority of the studies on animal models state a beneficial effect of these antibiotic functionalized membranes, but human clinical assays are scarce and controversial.

1. Introduction

In 1982, Nyman et al. [1] proposed the possibility of producing periodontal tissue regeneration in humans by using a barrier membrane. This barrier membrane should avoid soft tissue cell invasion of the regenerating area, maintaining the space and facilitating the periodontal ligament derived cells or bone cells to grow into the defective area. These principles have also been employed to promote guide bone regeneration at those sites where an intraoral bone defect or insufficient bone exists, mainly caused by teeth loss, trauma, tumoral pathology or infections [2]. Currently, these guided tissue regeneration and guided bone regeneration techniques are widely accepted and are often used for clinical applications [3,4].
These occlusive membranes must fulfill several criteria, including space maintaining capacity, mechanical properties, osteoconductivity/osteoinductivity, and biocompatibility [5,6]. Currently, it seems that natural and artificial polymers are the best candidate materials to comply with most of these prerequisites [6]. However, it should be taken into account that in many cases, periodontal guided tissue and bone regeneration are hindered due to contamination and infection of the healing site. It seems that the placement of barrier membranes at the oral cavity creates a favorable ecological niche that facilitates the growth of some periodontal pathogens [3,4].
In order to improve the barrier membrane function, the incorporation of antibacterials has been suggested to try to inhibit bacterial contamination at the surgical intervention or during the healing period if membrane exposure to the oral cavity occurs (Figure 1) [4,7]. If bacterial colonization and subsequent infection is produced in the early stages of wound healing, the clinical outcomes of the complete procedure will be jeopardized [7,8]. Controlling the membrane’s colonization of bacteria and reducing the possibility of infection in the early healing stage increases the predictability of the clinical outcomes [9]. It should be taken into account that some issues discourage the use of systemic antibiotic therapy due to risk of toxicity, acquired bacterial resistance, difficulty in penetrating some areas, and insufficient concentration levels at the infected site to efficiently inhibit the target microorganisms, among others [10]. Therefore, the use of local drug administration is recommended to potentially reduce the drug resistance of the bacteria by lowering the dosage of used antibiotics. The combination of polymeric barrier membranes and antibacterials are preferred in order to facilitate, accelerate, and enhance the effect of guided tissue and guided bone regeneration procedures [4,7].
The estimated healing period in bone regeneration is more than 6 months, and for periodontal regeneration, 4 to 6 weeks are necessary [11]. Antibacterials have shorter lifespans and rapid local clearances at bone healing sites. To overcome these points, a polymeric carrier system may play a key role in determining antibacterial activity. In recent years, there has been a strong increase in research focused on appropriate antibacterials and carrying materials for controlled and optimal release. Polymeric-based membranes have been proposed as key biomaterials capable of securing sustained release of antibacterials over a period of time and of affording acceptable release kinetics [4].
The purpose of this study was to review the existing literature on the main findings on antibiotic-loaded polymeric barrier membranes, covering design, manufacturing, loading and release kinetic, antibacterial efficacy, and usefulness for guided bone and tissue regeneration.

2. Methods

Using the National Library of Medicine (MEDLINE by PubMed), The Cochrane Oral Health Group Trials Register, EMBASE, and Web of Science (WOS) a literature search was performed for papers, including peer-reviewed publications from 1963 up to January 2022.
Combinations of several search terms were applied to create a search strategy including the following word combinations: (“Guided Tissue Regeneration” OR “GTR” OR “Guided Bone Regeneration” OR “GBR” OR “Bone Regeneration” OR “Periodontal Regeneration” OR “Bone Tissue Regeneration” OR “Bone formation” OR “Osteogenesis” OR “Osteogenic regeneration”) AND (“Barrier Membrane” OR “Membrane” OR “Barrier” OR “Collagen Membrane” OR “Chitosan-Collagen Membrane” OR “Natural Membrane” OR “Bovine Membrane” OR “Porcine Membrane” OR “Pericardium Membrane” OR “Dermis Membrane”) AND ((ions[MeSH Terms]) OR antibiotics[MeSH Terms] OR (antibacterial agents[MeSH Terms]) OR (agents, antimicrobial[MeSH Terms]) OR tetracycline OR doxycycline OR metronidazole OR minocycline OR roxithromycin OR moxifloxacin OR ciprofloxacin)). Bibliographies of eligible articles were also manually searched for missing papers after the electronic searching.

3. Results and Discussion

3.1. Polymeric Materials for Antibacterial-Loaded Membranes

Several polymers have been used as antibacterial carriers for bone regeneration barrier membranes. They can roughly be classified as natural or synthetic, resorbable or non-resorbable [3,6]. The previously-employed polymers for the mentioned medical application are presented in Table 1.
Among all the polymeric biomaterials, the natural collagen membrane is the most widely used as an antibacterial carrier in bone regeneration [5,12,13,14,15,16,17,18,19,20,21]. Several factors may explain this finding: (1) among the degradable membranes, collagen-based ones are the most commonly employed in dentistry because of their bioactivity, biocompatibility, and mechanical properties [3,7,22]; (2) they have been found to have many options for loading [23]. It should be considered that the chemical structure of collagen offers versatility, as it contains carboxyl and amino terminals, permitting not only adsorption, but also covalent binding of a great variety of different chemical groups [24]; (3) collagen degradability permits effective antibacterial liberation even if the antimicrobial substance is covalently linked to collagen [23,24].
Other synthetic polymers that have also been used as antibacterial carriers are: poly(lactic acid) (PLA) [25,26,27,28], poly(glycolic acid) (PGA) [16,19,29,30,31,32], polycaprolactone (PCL) [33,34,35,36,37,38], or combinations between them [10,39,40,41,42,43]. All these abovementioned polymers are also resorbable. PCL is a slow resorbing polymer as it degrades via an erosion mechanism, hence avoiding the rapid release of acidic byproducts, which may be detrimental to surrounding tissues. PGA and PLA are aliphatic polyesters with a fast degrading behavior [29].
Among the non-resorbable polymers, two are used as antibacterial carriers. One of them is expanded polytetrafluoroethylene (ePTFE) [8,16,19,44,45] and the second is a novel polymer based on hydroxyethyl methacrylate–methyl methacrylate (HEMA–MMA) copolymers that is still in the experimental phase [46,47].

3.2. Manufacturing Procedure for Polymeric Antibacterial-Loaded Membranes

The most frequently employed manufacturing technique for synthetic polymeric membranes is electrospinning [5,25,29,30,31,33,34,35,36,37,38,41,42,47,48,51,52,60,61]. This production method permits the adjusting of the most relevant characteristics of the manufactured membranes. It enables the creation of membranes with desired mechanical properties such as flexibility or elasticity. Fiber diameter may also be adjusted from micro to nanosized. Pore size, which imparts occlusive properties and an interconnected porous network resembling the bone collagen network, which is favorable for long term tissue infiltration and integration [29,47,48], can be controlled. Processing variables for each electrospinning method are different between the evaluated studies and include different voltages, needle to collector distances, and flow rates. These variables, together with the polymeric solution parameters such as surface tension, viscosity, and electrical conductivity of the solution, control the morphology of the electrospun fiber mats [5].
Antibacterials can be loaded in the electrospun nanofiber through: (1) blending, which is a passive loading of the antibacterial into the nanofibers (adding it in the polymeric solution prior to electrospinning) [25,30,31,33,34,36,37,41,51]; (2) coaxial electrospinning, where the antibacterials are embedded inside the electrospun nanofibers in order to improve some different aspects such as release outline (extending the period of drug delivery), drug safety, or drug-loading efficiency of non-soluble substances [37,38,42,55]; and (3) solvent evaporation or immersion techniques after fiber production, which permit physical absorption and chemical bonding of the antibacterials onto the polymers [37,47,48]. The simple electrospinning technique has gained widespread interest in the area of tissue engineering and drug delivery due to its relative ease of use and versatility [62]. Meanwhile, co-axial electrospinning is less employed, as it is a more difficult technique requiring more than a single nozzle [5]. One of the major advantages of electrospun fiber mats is the inherently high surface-to-volume-ratio of formed scaffolds. Not only does this help to enhance drug loading and to accomplish sustained and controlled local drug delivery, but it also improves cell attachment [62].
Collagen, PLA, PLGA, PCL, and other polymeric resorbable membranes have been fabricated through the casting method, by solvent evaporation, or as dried films [10,12,20,39,43,50,55]. In these cases, they are less porous and do not have a fibrous micro or nanostructure resembling collagen. These membranes were loaded by incorporation of the antibacterial in the polymer blend solution [10,12,13,32,39,49,51,55] or by immersion or solvent evaporation techniques after membrane production [14,15,16,17,18,19,20,43,50].
When using non-resorbable synthetic membranes, antibacterials are coated on the outer polymer surface through adsorption [8,16,44,59], direct covalent binding of the drug onto the membrane surface [47,48], or by grafting (using intermediary compounds in order to provoke a crosslinking reaction between the antibacterial and the polymeric membrane) [59].
Other manufacturing techniques as supercritical CO2-assisted processes, 3D printing, porogen leaching, gas foaming, phase separation, or any possible combination between these may also be employed for polymeric membrane preparation [63,64]. Among these techniques, the phase separation process is easy to execute and does not require sophisticated equipment. It is based on the principle that a homogeneous solution of a polymer dissolved in a good solvent can undergo a phase separation, causing solution saturation that will lead to polymer precipitation, followed by a microcellular foam polymer structuration [65]. It is beneficial since it may offer good control of the scaffold structure, particularly in terms of porosity and interconnectivity [63]. These properties play a significant role in tissue regeneration, affecting several cell processes such as adhesion, migration, proliferation, and differentiation [65].

3.3. Loaded Antibacterials for Bone Regeneration in Dentistry

The most frequently loaded antibiotics in bone regeneration membranes are tetracyclines [8,12,13,14,16,17,18,27,28,29,30,32,39,40,43,47,48,49,50,51,56,57,59]; which are broad-spectrum antibiotics that have been shown to be useful in fighting against most of the bacteria responsible for periodontitis [66]. The most frequently employed tetracyclines have been minocycline [12,13,49] and doxycycline [14,28,30,47,48,50,56,59]. Tetracyclines work by inhibiting protein synthesis in bacteria [67] and have been shown to have a prolonged lifespan and anticollagenase properties, and are well absorbed by bone due to a calcium quelating effect [59].
The second most frequently employed antibiotics are metronidazole [5,10,15,20,21,25,33,38,42,52,55,58] and other nitroimidazoles such as ornidazole [31], niridazole, and tinidazole [21]. These are antibiotics with antibacterial activity for Gram-negative and anaerobic bacteria [25], and they are specific against most of the subgingival [10] and periodontopathic biofilms [21]. Metronidazole’s mechanism of action is based on the alteration of nucleic acid synthesis in bacteria [67].
Other encountered, but less used antibiotics for loading membranes were amoxycillin [15,16,19], vancomycin [41] or azithromycin [29]. Amoxycillin and vancomycin are antibiotics targeting the bacterial cell wall [67]. Azithromycin is a macrolide antibiotic extensively recommended for a wide range of anaerobic infections. It mainly acts by altering protein synthesis. However, its main disadvantage is low bio-availability as a result of its poor water solubility, probably limiting its proposed clinical application [29].

3.4. Antibiotic Release Kinetics

Antibiotic release kinetics is not evaluated in all the reviewed studies. When ascertained, it was usually done in vitro. The supernatants are measured at specific time-points after immersion of the loaded membranes in a solution (normally deionized water or phosphate buffered saline). High performance liquid chromatography [31,33,34,37,38,41], inductively coupled plasma atomic emission spectrometry [53], UV-vis spectrophotometry [10,12,13,21,30,50,58,59], and fluorescence [36] are the most used techniques to determine the released concentration of the loaded antibiotics. Loading efficiency, when determined, was usually high, ranging between 30 and 85% [29,52].
Antibiotic release from polymeric membranes is in all cases characterized by two different phases. The first is an initial burst release, which can be described as the liberation produced between 7 and 10 h [37,55,68], or between 12 and 48 h [10,13,29,31,32,33,34,36,39,42,49,50,52,54,58,59]. This rapid release is followed by a slower and sustained liberation that may last from 35 h to 10 days [10,13,21,32,34,37,38,39,48,52,57,59,65], or in some cases much longer, up to 28 days [12,25,30,33,36,49,53,58]. These described liberation kinetics indicate that some of the antibiotic is always retained by absorption and is rapidly liberated after immersion. The slow and relatively sustained posterior release probably corresponds to the antibiotic that is ionically or covalently linked to the membranes, or to the antibiotic that is liberated at the same time that the membrane degrades. Therefore, the procedures used to load the antibiotic and the type of membrane may be considered as determinant factors affecting antibiotic release. The loading of antibiotics on polymers through chemical conjugation may have a more controlled kinetic release than those processed through physical adsorption [69]. However, it is also necessary to investigate the antibacterial activity of the released antibiotics, since liberation does not always imply biological activity.

3.5. Antibacterial Efficacy of Antibiotic-Loaded Membranes

Most studies investigated antibiotic loaded membrane efficacy using in vitro antibacterial cell assays [12,15,16,19,29,30,31,33,34,38,41,42,44,48,49,53,56,58,65] and/or in vivo animal models when surgically treating contaminated bone defects [14,36,41]. The efficacy of the membrane as an antibiotic delivery carrier was always confirmed.
Of the antibacterial cell assays, the most employed was the agar disk diffusion test [12,15,29,30,31,33,34,38,41,42,49,56,58,65]. Other techniques such as the plate-counting method [53], determination of bacterial penetration through membranes [19], bacterial colonization on membranes [44], scanning electron microscopy evaluation of membranes colonization [16,48,53], or number of cells determination by more precise techniques such as quantitative polymerase chain reaction [48] were rarely executed.
It is also worth mentioning that sometimes non-clinically relevant or unspecific bacteria were used for these studies, as in the case of Peptostreptococcus anaerobius [31], Staphylococcus aureus [12,30,33,36,41,53,56], Pseudomonas aeruginosa [33], Echerichia coli [30,53,56], Helicobacter pilori [37], or Streptococcus mutans [16,19,49]. Of periodontally-relevant bacteria Aggregatibacter actinomycetemcomitans [15,16], Porphyromonas gingivalis [13,14,15,49] and Fusobacterium nucleatum [13,31,34,38,42,68] have been tested. All these studies were based on single bacterial cultures; therefore, results should not be directly extrapolated to the clinical situation. It has to be taken into account that bacteria grow in biofilms, providing them with specific characteristics that make bacteria more resistant and tolerant to antibiotics than when in a planktonic state [70]. Only one recently published study was performed using a subgingival multispecies biofilm model with six different bacterial species [48].
The incorporation of antibacterial agents in membranes is a promising approach that may promote bone formation, especially for some challenging clinical situations when the characteristics of the defect make the site especially prone to membrane exposure and subsequent bacterial contamination and infection. However, despite the promising results encountered in vitro and in preclinical animal models, the value of incorporating antibacterials has not yet been evidenced clinically [4].
In animal models, when treating previously contaminated bone defects, the efficacy has been probed in terms of bone regeneration of doxycycline-loaded collagen membranes [14], vancomycin-loaded PCL-membranes [36], and vancomycin-loaded PGA membranes [41]. Tetracycline-loaded PGA membranes and minocycline-chitosan membranes also induced major regeneration in periodontal defects in beagle dogs [51] and rats [49], respectively.
None of the antibacterial-loaded membranes have been evaluated for efficacy in reducing microbial adhesion and infection in humans. Conversely, several antibiotic-loaded membranes were tested in humans evaluating clinical efficacy when compared to non-antibiotic-loaded membranes. Gain in periodontal attachment level and increases in bone formation were obtained when using tetracycline-loaded ePTFE membranes [44], doxycycline-loaded collagen membranes [18], and metronidazole-loaded collagen membranes [20]. However, in two clinical studies, doxycycline-loaded collagen membranes [28] and tetracycline-loaded ePTFE membranes [8] failed to enhance the periodontal regeneration outcomes when compared to non-antibiotic-loaded membranes. These controversial results may be due to the small sample size of the studies (around 10 to 25 patients) and to the lack of standardization of the employed antibiotic concentration and liberation, which was sometimes extremely low (i.e., 4 wt% [28]) or not reported [8].

3.6. Other Findings Associated with Antibiotics Loaded on Polymeric Membranes

The cytocompatibility of these membranes was sometimes evaluated using different cells lines as osteoblasts [13,37,42,53,60,61], fibroblasts [13,35,37,39,52], epithelial cells [59], and stem cells [5,25,30,32], always with favorable results.
It is relevant that in addition to their antimicrobial activity, doxycycline and minocycline have been shown to enhance osteoblast and/or stem cell proliferation, differentiation, and osteogenic activity [5,13,30,32,33,53,60,61]. Moreover, these antibiotics were shown to inhibit bone resorption and to promote bone formation when assayed in animals [13,29,33,40,43] and in humans [62].
Immunomodulatory effects have been proven for doxycycline-loaded membranes in both cells [71] and animals [47]. The same effect was also shown for metronidazole-loaded collagen membranes in cells [21] or azithromycin-loaded PGA membranes when tested in an animal model [29].
Tetracycline-loaded collagen membranes have also been reported to have slower degradation [17], which may be beneficial for bone regeneration in challenging bone defects.

4. Conclusions

It can be concluded that, taking into account the fact that infection can lead to the failure of the intended bone regeneration, polymeric membranes could be used as carriers for local antibiotic therapy. Due to antibiotic lifespans and the rapid clearance rate existing at the surgical sites, it is impossible for antibiotics to produce a long-term effect without the aid of a carrier facilitating a controlled liberation. The loading efficacy and the kinetic release will depend on the employed polymeric material. The polymeric carrier should ideally have a constant and slow degradation and should be ideally maintained through the complete healing period. Collagen or ePTFE loaded with tetracyclines, and PCL with metronidazole are the most frequently assayed combinations. Antibiotics present the advantage of possessing a wide therapeutic window, making it easier to obtain a beneficial effect whenever the liberation is effective. In the existing studies, even when antibacterial efficacy is often reported, most of the times it is not measured against specific subgingival pathogenic bacteria and it is usually measured using an agar disc diffusion method, which are two variables limiting the clinical relevance of the previously published results. It should be considered that the present literature review lacks of standardization in method; therefore, results need to be taken with caution.
It should also be taken into account that there is relatively scarce experimental evidence that a local antibacterial strategy could be useful in bone regeneration procedures. Apart from several studies on infected periodontal defects locally treated with antibiotics and polymeric membranes [8,18,20,28,44], no specific antimicrobial strategy has been yet clinically validated [4].
Future studies should be performed focusing on: (i) the standardization of adsorption/release abilities of the different polymeric carriers, (ii) antibacterial activity assays using specific and periodontal clinically-relevant biofilm models, and (iii) randomized clinical trials in order to finally determine the safety and efficacy of these novel and innovative procedures; thereby helping to eliminate the barriers limiting the extension of the experimental results to the clinical situation.

Author Contributions

Conceptualization, M.T.-O., C.V., M.V.-R., F.-J.M.-M. and R.O.; formal analysis, M.T.-O., C.V., M.V.-R., F.-J.M.-M. and R.O.; funding acquisition, M.T.-O. and R.O.; investigation, M.T.-O., C.V., M.V.-R., F.-J.M.-M. and R.O.; methodology, M.T.-O., C.V., M.V.-R., F.-J.M.-M. and R.O.; supervision, F.-J.M.-M. and R.O.; validation, M.T.-O. and R.O.; visualization, M.T.-O., F.-J.M.-M. and R.O.; writing—original draft, M.T.-O., C.V., M.V.-R., F.-J.M.-M. and R.O.; writing—review and editing, M.T.-O., C.V., M.V.-R., F.-J.M.-M. and R.O. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by the Ministry of Economy and Competitiveness (MINECO) and the European Regional Development Fund (FEDER), grant number (PID2020-114694RB-I00 MINECO/AEI/FEDER/UE). M. Toledano-Osorio holds a FPU fellowship from the Ministry of Universities (FPU20/00450) and this manuscript is part of his Ph.D. thesis.

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Nyman, S.; Lindhe, J.; Karring, T.; Rylander, H. New Attachment Following Surgical Treatment of Human Periodontal Disease. J. Clin. Periodontol. 1982, 9, 290–296. [Google Scholar] [CrossRef] [PubMed]
  2. Toledano-Osorio, M.; Toledano, M.; Manzano-Moreno, F.J.; Vallecillo, C.; Vallecillo-Rivas, M.; Rodriguez-Archilla, A.; Osorio, R. Alveolar Bone Ridge Augmentation Using Polymeric Membranes: A Systematic Review and Meta-Analysis. Polymers 2021, 13, 1172. [Google Scholar] [CrossRef] [PubMed]
  3. Sasaki, J.-I.; Abe, G.L.; Li, A.; Thongthai, P.; Tsuboi, R.; Kohno, T.; Imazato, S. Barrier Membranes for Tissue Regeneration in Dentistry. Biomater. Investig. Dent. 2021, 8, 54–63. [Google Scholar] [CrossRef] [PubMed]
  4. Omar, O.; Elgali, I.; Dahlin, C.; Thomsen, P. Barrier Membranes: More than the Barrier Effect? J. Clin. Periodontol. 2019, 46 (Suppl. 21), 103–123. [Google Scholar] [CrossRef] [Green Version]
  5. Ghavimi, M.A.; Bani Shahabadi, A.; Jarolmasjed, S.; Memar, M.Y.; Maleki Dizaj, S.; Sharifi, S. Nanofibrous Asymmetric Collagen/Curcumin Membrane Containing Aspirin-Loaded PLGA Nanoparticles for Guided Bone Regeneration. Sci. Rep. 2020, 10, 18200. [Google Scholar] [CrossRef]
  6. Sanz, M.; Dahlin, C.; Apatzidou, D.; Artzi, Z.; Bozic, D.; Calciolari, E.; De Bruyn, H.; Dommisch, H.; Donos, N.; Eickholz, P.; et al. Biomaterials and Regenerative Technologies Used in Bone Regeneration in the Craniomaxillofacial Region: Consensus Report of Group 2 of the 15th European Workshop on Periodontology on Bone Regeneration. J. Clin. Periodontol. 2019, 46 (Suppl. 21), 82–91. [Google Scholar] [CrossRef]
  7. Rudolf, J.-L.; Moser, C.; Sculean, A.; Eick, S. In-Vitro Antibiofilm Activity of Chlorhexidine Digluconate on Polylactide-Based and Collagen-Based Membranes. BMC Oral Health 2019, 19, 291. [Google Scholar] [CrossRef] [Green Version]
  8. Sipos, P.M.; Loos, B.G.; Abbas, F.; Timmerman, M.F.; van der Velden, U. The Combined Use of Enamel Matrix Proteins and a Tetracycline-Coated Expanded Polytetrafluoroethylene Barrier Membrane in the Treatment of Intra-Osseous Defects. J. Clin. Periodontol. 2005, 32, 765–772. [Google Scholar] [CrossRef] [Green Version]
  9. Zucchelli, G.; Pollini, F.; Clauser, C.; De Sanctis, M. The Effect of Chlorhexidine Mouthrinses on Early Bacterial Colonization of Guided Tissue Regeneration Membranes. An in Vivo Study. J. Periodontol. 2000, 71, 263–271. [Google Scholar] [CrossRef]
  10. Kurtiş, B.; Unsal, B.; Cetiner, D.; Gültekin, E.; Ozcan, G.; Celebi, N.; Ocak, O. Effect of Polylactide/Glycolide (PLGA) Membranes Loaded with Metronidazole on Periodontal Regeneration Following Guided Tissue Regeneration in Dogs. J. Periodontol. 2002, 73, 694–700. [Google Scholar] [CrossRef]
  11. Vallecillo-Rivas, M.; Toledano-Osorio, M.; Vallecillo, C.; Toledano, M.; Osorio, R. The Collagen Origin Influences the Degradation Kinetics of Guided Bone Regeneration Membranes. Polymers 2021, 13, 3007. [Google Scholar] [CrossRef] [PubMed]
  12. Wu, L.; Morrow, B.R.; Jefferson, M.M.; Li, F.; Hong, L. Antibacterial Collagen Composite Membranes Containing Minocycline. J. Pharm. Sci. 2021, 110, 2177–2184. [Google Scholar] [CrossRef] [PubMed]
  13. Ma, S.; Adayi, A.; Liu, Z.; Li, M.; Wu, M.; Xiao, L.; Sun, Y.; Cai, Q.; Yang, X.; Zhang, X.; et al. Asymmetric Collagen/Chitosan Membrane Containing Minocycline-Loaded Chitosan Nanoparticles for Guided Bone Regeneration. Sci. Rep. 2016, 6, 31822. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  14. Kütan, E.; Duygu-Çapar, G.; Özçakir-Tomruk, C.; Dilek, O.C.; Özen, F.; Erdoğan, Ö.; Özdemir, I.; Korachi, M.; Gürel, A. Efficacy of Doxycycline Release Collagen Membrane on Surgically Created and Contaminated Defects in Rat Tibiae: A Histopathological and Microbiological Study. Arch. Oral Biol. 2016, 63, 15–21. [Google Scholar] [CrossRef]
  15. Mehrotra, N.; Reddy Palle, A.; Kumar Gedela, R.; Vasudevan, S. Efficacy of Natural and Allopathic Antimicrobial Agents Incorporated onto Guided Tissue Regeneration Membrane Against Periodontal Pathogens: An in Vitro Study. J. Clin. Diagn Res. 2017, 11, ZC84–ZC87. [Google Scholar] [CrossRef]
  16. Cheng, C.-F.; Wu, K.-M.; Chen, Y.-T.; Hung, S.-L. Bacterial Adhesion to Antibiotic-Loaded Guided Tissue Regeneration Membranes-a Scanning Electron Microscopy Study. J. Formos. Med. Assoc. 2015, 114, 35–45. [Google Scholar] [CrossRef] [Green Version]
  17. Moses, O.; Frenkel, T.; Tal, H.; Weinreb, M.; Bornstein, M.M.; Nemcovsky, C.E. Effect of Systemic Tetracycline on the Degradation of Tetracycline-Impregnated Bilayered Collagen Membranes: An Animal Study. Clin. Implant. Dent. Relat. Res. 2010, 12, 331–337. [Google Scholar] [CrossRef]
  18. Chaturvedi, R.; Gill, A.S.; Sikri, P. Evaluation of the Regenerative Potential of 25% Doxycycline-Loaded Biodegradable Membrane vs Biodegradable Membrane Alone in the Treatment of Human Periodontal Infrabony Defects: A Clinical and Radiological Study. Indian J. Dent. Res. 2008, 19, 116–123. [Google Scholar] [CrossRef]
  19. Cheng, C.-F.; Lee, Y.-Y.; Chi, L.-Y.; Chen, Y.-T.; Hung, S.-L.; Ling, L.-J. Bacterial Penetration through Antibiotic-Loaded Guided Tissue Regeneration Membranes. J. Periodontol. 2009, 80, 1471–1478. [Google Scholar] [CrossRef]
  20. Dowell, P.; al-Arrayed, F.; Adam, S.; Moran, J. A Comparative Clinical Study: The Use of Human Type I Collagen with and without the Addition of Metronidazole in the GTR Method of Treatment of Periodontal Disease. J. Clin. Periodontol. 1995, 22, 543–549. [Google Scholar] [CrossRef]
  21. Al-Arrayed, F.; Thomas, S.; Moran, J. Effect of Addition of Antimicrobial Drugs to Human Collagen Membrane. Clin. Mater. 1993, 12, 169–179. [Google Scholar] [CrossRef]
  22. Caballé-Serrano, J.; Abdeslam-Mohamed, Y.; Munar-Frau, A.; Fujioka-Kobayashi, M.; Hernández-Alfaro, F.; Miron, R. Adsorption and Release Kinetics of Growth Factors on Barrier Membranes for Guided Tissue/Bone Regeneration: A Systematic Review. Arch. Oral Biol. 2019, 100, 57–68. [Google Scholar] [CrossRef]
  23. Friess, W. Collagen--Biomaterial for Drug Delivery. Eur. J. Pharm. Biopharm. 1998, 45, 113–136. [Google Scholar] [CrossRef]
  24. Sbricoli, L.; Guazzo, R.; Annunziata, M.; Gobbato, L.; Bressan, E.; Nastri, L. Selection of Collagen Membranes for Bone Regeneration: A Literature Review. Materials 2020, 13, 786. [Google Scholar] [CrossRef] [Green Version]
  25. Ho, M.-H.; Chang, H.-C.; Chang, Y.-C.; Claudia, J.; Lin, T.-C.; Chang, P.-C. PDGF-Metronidazole-Encapsulated Nanofibrous Functional Layers on Collagen Membrane Promote Alveolar Ridge Regeneration. Int. J. Nanomedicine 2017, 12, 5525–5535. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  26. Saarani, N.N.; Jamuna-Thevi, K.; Shahab, N.; Hermawan, H.; Saidin, S. Antibacterial Efficacy of Triple-Layered Poly(Lactic-Co-Glycolic Acid)/Nanoapatite/Lauric Acid Guided Bone Regeneration Membrane on Periodontal Bacteria. Dent. Mater. J. 2017, 36, 260–265. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  27. Nublat, C.; Braud, C.; Garreau, H.; Vert, M. Ammonium Bicarbonate as Porogen to Make Tetracycline-Loaded Porous Bioresorbable Membranes for Dental Guided Tissue Regeneration: Failure Due to Tetracycline Instability. J. Biomater. Sci. Polym. Ed. 2006, 17, 1333–1346. [Google Scholar] [CrossRef] [PubMed]
  28. Lyons, L.C.; Weltman, R.L.; Moretti, A.J.; Trejo, P.M. Regeneration of Degree Ii Furcation Defects with a 4% Doxycycline Hyclate Bioabsorbable Barrier. J. Periodontol. 2008, 79, 72–79. [Google Scholar] [CrossRef] [PubMed]
  29. Mathew, A.; Vaquette, C.; Hashimi, S.; Rathnayake, I.; Huygens, F.; Hutmacher, D.W.; Ivanovski, S. Antimicrobial and Immunomodulatory Surface-Functionalized Electrospun Membranes for Bone Regeneration. Adv. Healthc. Mater. 2017, 6, 1601345. [Google Scholar] [CrossRef]
  30. Lian, M.; Sun, B.; Qiao, Z.; Zhao, K.; Zhou, X.; Zhang, Q.; Zou, D.; He, C.; Zhang, X. Bi-Layered Electrospun Nanofibrous Membrane with Osteogenic and Antibacterial Properties for Guided Bone Regeneration. Colloids Surf. B Biointerfaces 2019, 176, 219–229. [Google Scholar] [CrossRef]
  31. Zhang, H.; Ma, H.; Zhang, R.; Wang, K.; Liu, J. Construction and Characterization of Antibacterial PLGA/Wool Keratin/Ornidazole Composite Membranes for Periodontal Guided Tissue Regeneration. J. Biomater. Appl. 2020, 34, 1267–1281. [Google Scholar] [CrossRef] [PubMed]
  32. Jin, S.-H.; Kweon, H.; Park, J.-B.; Kim, C.-H. The Effects of Tetracycline-Loaded Silk Fibroin Membrane on Proliferation and Osteogenic Potential of Mesenchymal Stem Cells. J. Surg. Res. 2014, 192, e1–e9. [Google Scholar] [CrossRef] [PubMed]
  33. Shi, R.; Gong, M.; Chi, C.; Huang, Y.; Li, W.; Li, G.; Ye, J.; Liao, M.; Zhang, L.; Tian, W. Nano Twin-Fiber Membrane with Osteogenic and Antibacterial Dual Functions as Artificial Periosteum for Long Bone Repairing. J. Biomed. Nanotechnol. 2019, 15, 272–287. [Google Scholar] [CrossRef]
  34. Xue, J.; He, M.; Liang, Y.; Crawford, A.; Coates, P.; Chen, D.; Shi, R.; Zhang, L. Fabrication and Evaluation of Electrospun PCL-Gelatin Micro-/Nanofiber Membranes for Anti-Infective GTR Implants. J. Mater. Chem. B 2014, 2, 6867–6877. [Google Scholar] [CrossRef] [PubMed]
  35. Figueira, D.R.; Miguel, S.P.; de Sá, K.D.; Correia, I.J. Production and Characterization of Polycaprolactone- Hyaluronic Acid/Chitosan- Zein Electrospun Bilayer Nanofibrous Membrane for Tissue Regeneration. Int. J. Biol. Macromol. 2016, 93, 1100–1110. [Google Scholar] [CrossRef] [PubMed]
  36. Wei, S.; Jian, C.; Xu, F.; Bao, T.; Lan, S.; Wu, G.; Qi, B.; Bai, Z.; Yu, A. Vancomycin-Impregnated Electrospun Polycaprolactone (PCL) Membrane for the Treatment of Infected Bone Defects: An Animal Study. J. Biomater. Appl. 2018, 32, 1187–1196. [Google Scholar] [CrossRef]
  37. Shi, R.; Ye, J.; Li, W.; Zhang, J.; Li, J.; Wu, C.; Xue, J.; Zhang, L. Infection-Responsive Electrospun Nanofiber Mat for Antibacterial Guided Tissue Regeneration Membrane. Mater. Sci. Eng. C Mater. Biol. Appl. 2019, 100, 523–534. [Google Scholar] [CrossRef]
  38. He, M.; Jiang, H.; Wang, R.; Xie, Y.; Zhao, C. Fabrication of Metronidazole Loaded Poly (ε-Caprolactone)/Zein Core/Shell Nanofiber Membranes via Coaxial Electrospinning for Guided Tissue Regeneration. J. Colloid Interface Sci. 2017, 490, 270–278. [Google Scholar] [CrossRef]
  39. Owen, G.R.; Jackson, J.K.; Chehroudi, B.; Brunette, D.M.; Burt, H.M. An in Vitro Study of Plasticized Poly(Lactic-Co-Glycolic Acid) Films as Possible Guided Tissue Regeneration Membranes: Material Properties and Drug Release Kinetics. J. Biomed. Mater. Res. Part A 2010, 95, 857–869. [Google Scholar] [CrossRef]
  40. Park, Y.J.; Lee, Y.M.; Park, S.N.; Lee, J.Y.; Ku, Y.; Chung, C.P.; Lee, S.J. Enhanced Guided Bone Regeneration by Controlled Tetracycline Release from Poly(L-Lactide) Barrier Membranes. J. Biomed. Mater. Res. 2000, 51, 391–397. [Google Scholar] [CrossRef]
  41. Gao, J.; Huang, G.; Liu, G.; Liu, Y.; Chen, Q.; Ren, L.; Chen, C.; Ding, Z. A Biodegradable Antibiotic-Eluting PLGA Nanofiber-Loaded Deproteinized Bone for Treatment of Infected Rabbit Bone Defects. J. Biomater. Appl. 2016, 31, 241–249. [Google Scholar] [CrossRef] [PubMed]
  42. He, P.; Li, Y.; Huang, Z.; Guo, Z.-Z.; Luo, B.; Zhou, C.-R.; Li, H. A Multifunctional Coaxial Fiber Membrane Loaded with Dual Drugs for Guided Tissue Regeneration. J. Biomater. Appl. 2020, 34, 1041–1051. [Google Scholar] [CrossRef] [PubMed]
  43. Chang, C.Y.; Yamada, S. Evaluation of the Regenerative Effect of a 25% Doxycycline-Loaded Biodegradable Membrane for Guided Tissue Regeneration. J. Periodontol. 2000, 71, 1086–1093. [Google Scholar] [CrossRef] [PubMed]
  44. Zarkesh, N.; Nowzari, H.; Morrison, J.L.; Slots, J. Tetracycline-Coated Polytetrafluoroethylene Barrier Membranes in the Treatment of Intraosseous Periodontal Lesions. J. Periodontol. 1999, 70, 1008–1016. [Google Scholar] [CrossRef]
  45. Chen, Y.-T.; Hung, S.-L.; Lin, L.-W.; Chi, L.-Y.; Ling, L.-J. Attachment of Periodontal Ligament Cells to Chlorhexidine-Loaded Guided Tissue Regeneration Membranes. J. Periodontol. 2003, 74, 1652–1659. [Google Scholar] [CrossRef]
  46. Yin, I.X.; Zhang, J.; Zhao, I.S.; Mei, M.L.; Li, Q.; Chu, C.H. The Antibacterial Mechanism of Silver Nanoparticles and Its Application in Dentistry. Int. J. Nanomedicine 2020, 15, 2555–2562. [Google Scholar] [CrossRef] [Green Version]
  47. Toledano, M.; Toledano-Osorio, M.; Osorio, R.; Carrasco-Carmona, Á.; Gutiérrez-Pérez, J.-L.; Gutiérrez-Corrales, A.; Serrera-Figallo, M.-A.; Lynch, C.D.; Torres-Lagares, D. Doxycycline and Zinc Loaded Silica-Nanofibrous Polymers as Biomaterials for Bone Regeneration. Polymers 2020, 12, 1201. [Google Scholar] [CrossRef]
  48. Bueno, J.; Sánchez, M.C.; Toledano-Osorio, M.; Figuero, E.; Toledano, M.; Medina-Castillo, A.L.; Osorio, R.; Herrera, D.; Sanz, M. Antimicrobial Effect of Nanostructured Membranes for Guided Tissue Regeneration: An in Vitro Study. Dent. Mater. 2020, 36, 1566–1577. [Google Scholar] [CrossRef]
  49. Li, N.; Jiang, L.; Jin, H.; Wu, Y.; Liu, Y.; Huang, W.; Wei, L.; Zhou, Q.; Chen, F.; Gao, Y.; et al. An Enzyme-Responsive Membrane for Antibiotic Drug Release and Local Periodontal Treatment. Colloids Surf. B Biointerfaces 2019, 183, 110454. [Google Scholar] [CrossRef]
  50. Qasim, S.S.B.; Nogueria, L.P.; Fawzy, A.S.; Daood, U. The Effect of Cross-Linking Efficiency of Drug-Loaded Novel Freeze Gelated Chitosan Templates for Periodontal Tissue Regeneration. AAPS PharmSciTech 2020, 21, 173. [Google Scholar] [CrossRef]
  51. Kim, I.-Y.; Jung, U.-W.; Kim, C.-S.; Lee, Y.-K.; Cho, K.-S.; Chai, J.-K.; Kim, C.-K.; Choi, S.-H. Effects of a Tetracycline Blended Polylactic and Polyglycolic Acid Membrane on the Healing of One-Wall Intrabony Defects in Beagle Dogs. Biomed. Mater. 2007, 2, S106–S110. [Google Scholar] [CrossRef] [PubMed]
  52. Xue, J.; Niu, Y.; Gong, M.; Shi, R.; Chen, D.; Zhang, L.; Lvov, Y. Electrospun Microfiber Membranes Embedded with Drug-Loaded Clay Nanotubes for Sustained Antimicrobial Protection. ACS Nano 2015, 9, 1600–1612. [Google Scholar] [CrossRef] [PubMed]
  53. Yan, J.; Zhou, W.; Jia, Z.; Xiong, P.; Li, Y.; Wang, P.; Li, Q.; Cheng, Y.; Zheng, Y. Endowing Polyetheretherketone with Synergistic Bactericidal Effects and Improved Osteogenic Ability. Acta Biomater. 2018, 79, 216–229. [Google Scholar] [CrossRef] [PubMed]
  54. Chang, K.-C.; Chen, W.-C.; Chen, C.-H.; Ko, C.-L.; Liu, S.-M.; Chen, J.-C. Chemical Cross-Linking on Gelatin-Hyaluronan Loaded with Hinokitiol for the Preparation of Guided Tissue Regeneration Hydrogel Membranes with Antibacterial and Biocompatible Properties. Mater. Sci. Eng. C Mater. Biol. Appl. 2021, 119, 111576. [Google Scholar] [CrossRef] [PubMed]
  55. Murgia, D.; Angellotti, G.; Conigliaro, A.; Carfi Pavia, F.; D’Agostino, F.; Contardi, M.; Mauceri, R.; Alessandro, R.; Campisi, G.; De Caro, V. Development of a Multifunctional Bioerodible Nanocomposite Containing Metronidazole and Curcumin to Apply on L-PRF Clot to Promote Tissue Regeneration in Dentistry. Biomedicines 2020, 8, 425. [Google Scholar] [CrossRef]
  56. Marques, M.S.; Zepon, K.M.; Petronilho, F.C.; Soldi, V.; Kanis, L.A. Characterization of Membranes Based on Cellulose Acetate Butyrate/Poly(Caprolactone)Triol/Doxycycline and Their Potential for Guided Bone Regeneration Application. Mater. Sci. Eng. C Mater. Biol. Appl. 2017, 76, 365–373. [Google Scholar] [CrossRef]
  57. Markman, C.; Fracalanzza, S.E.; Novaes, A.B.; Novaes, A.B. Slow Release of Tetracycline Hydrochloride from a Cellulose Membrane Used in Guided Tissue Regeneration. J. Periodontol. 1995, 66, 978–983. [Google Scholar] [CrossRef]
  58. da Silva, M.A.C.; Oliveira, R.N.; Mendonça, R.H.; Lourenço, T.G.B.; Colombo, A.P.V.; Tanaka, M.N.; Tude, E.M.O.; da Costa, M.F.; Thiré, R.M.S.M. Evaluation of Metronidazole-Loaded Poly(3-Hydroxybutyrate) Membranes to Potential Application in Periodontitis Treatment. J. Biomed. Mater. Res. B Appl. Biomater. 2016, 104, 106–115. [Google Scholar] [CrossRef]
  59. Boschin, F.; Blanchemain, N.; Bria, M.; Delcourt-Debruyne, E.; Morcellet, M.; Hildebrand, H.F.; Martel, B. Improved Drug Delivery Properties of PVDF Membranes Functionalized with Beta-Cyclodextrin--Application to Guided Tissue Regeneration in Periodontology. J. Biomed. Mater. Res. Part A 2006, 79, 78–85. [Google Scholar] [CrossRef]
  60. Qian, Y.; Zhou, X.; Sun, H.; Yang, J.; Chen, Y.; Li, C.; Wang, H.; Xing, T.; Zhang, F.; Gu, N. Biomimetic Domain-Active Electrospun Scaffolds Facilitating Bone Regeneration Synergistically with Antibacterial Efficacy for Bone Defects. ACS Appl. Mater. Interfaces 2018, 10, 3248–3259. [Google Scholar] [CrossRef]
  61. Toledano-Osorio, M.; Manzano-Moreno, F.J.; Toledano, M.; Osorio, R.; Medina-Castillo, A.L.; Costela-Ruiz, V.J.; Ruiz, C. Doxycycline-Doped Membranes Induced Osteogenic Gene Expression on Osteoblastic Cells. J. Dent. 2021, 109, 103676. [Google Scholar] [CrossRef] [PubMed]
  62. Ma, Y.; Song, J.; Almassri, H.N.S.; Zhang, D.; Zhang, T.; Cheng, Y.; Wu, X. Minocycline-Loaded PLGA Electrospun Membrane Prevents Alveolar Bone Loss in Experimental Peridontitis. Drug Deliv. 2020, 27, 151–160. [Google Scholar] [CrossRef] [PubMed]
  63. Baldino, L.; Aragón, J.; Mendoza, G.; Irusta, S.; Cardea, S.; Reverchon, E. Production, characterization and testing of antibacterial PVA membranes loaded with HA-Ag3PO4 nanoparticles, produced by SC-CO2 phase inversion. J. Chem. Technol. Biotechnol. 2018, 94, 98–108. [Google Scholar] [CrossRef] [Green Version]
  64. Prihandana, G.S.; Sriani, T.; Muthi’ah, A.D.; Machmudah, A.; Mahardika, M.; Miki, N. Study Effect of NAg Particle Size on the Properties and Antibacterial Characteristics of Polysulfone Membranes. Nanomaterials 2022, 12, 388. [Google Scholar] [CrossRef] [PubMed]
  65. Gay, S.; Lefebvre, G.; Bonnin, M.; Nottelet, B.; Boury, F.; Gibaud, A.; Calvignac, B. PLA Scaffolds Production from Thermally Induced Phase Separation: Effect of Process Parameters and Development of an Environmentally Improved Route Assisted by Supercritical Carbon Dioxide. J. Supercrit. Fluids 2018, 136, 123–135. [Google Scholar] [CrossRef]
  66. de Oliveira, L.F.; Jorge, A.O.C.; Dos Santos, S.S.F. In Vitro Minocycline Activity on Superinfecting Microorganisms Isolated from Chronic Periodontitis Patients. Braz. Oral Res. 2006, 20, 202–206. [Google Scholar] [CrossRef]
  67. Kapoor, G.; Saigal, S.; Elongavan, A. Action and Resistance Mechanisms of Antibiotics: A Guide for Clinicians. J. Anaesthesiol. Clin. Pharmacol. 2017, 33, 300–305. [Google Scholar] [CrossRef]
  68. Xue, J.; Shi, R.; Niu, Y.; Gong, M.; Coates, P.; Crawford, A.; Chen, D.; Tian, W.; Zhang, L. Fabrication of Drug-Loaded Anti-Infective Guided Tissue Regeneration Membrane with Adjustable Biodegradation Property. Colloids Surf. B Biointerfaces 2015, 135, 846–854. [Google Scholar] [CrossRef]
  69. Kim, J.-E.; Lee, E.-J.; Kim, H.-E.; Koh, Y.-H.; Jang, J.-H. The Impact of Immobilization of BMP-2 on PDO Membrane for Bone Regeneration. J. Biomed. Mater. Res. Part A 2012, 100, 1488–1493. [Google Scholar] [CrossRef]
  70. Garrett, T.R.; Bhakoo, M.; Zhang, Z. Bacterial Adhesion and Biofilms on Surfaces. Prog. Nat. Sci. 2008, 18, 1049–1056. [Google Scholar] [CrossRef]
  71. Toledano-Osorio, M.; Manzano-Moreno, F.J.; Toledano, M.; Medina-Castillo, A.L.; Costela-Ruiz, V.J.; Ruiz, C.; Osorio, R. Doxycycline-Doped Polymeric Membranes Induced Growth, Differentiation and Expression of Antigenic Phenotype Markers of Osteoblasts. Polymers 2021, 13, 1063. [Google Scholar] [CrossRef] [PubMed]
Figure 1. A barrier membrane employed to avoid soft tissue cell invasion, enhancing space maintenance of the regenerating area. The incorporation of antibacterials in the membrane has been suggested to inhibit bacterial contamination during the surgical intervention or the healing period if membrane exposure to the oral cavity occurs, improving the performance of the bone regeneration procedure.
Figure 1. A barrier membrane employed to avoid soft tissue cell invasion, enhancing space maintenance of the regenerating area. The incorporation of antibacterials in the membrane has been suggested to inhibit bacterial contamination during the surgical intervention or the healing period if membrane exposure to the oral cavity occurs, improving the performance of the bone regeneration procedure.
Polymers 14 00840 g001
Table 1. Combinations of previously-employed polymers and antibiotics in the designing of barrier membranes for guided bone/tissue regeneration.
Table 1. Combinations of previously-employed polymers and antibiotics in the designing of barrier membranes for guided bone/tissue regeneration.
Polymeric MaterialOriginResorbableLoaded AntibioticReferences
Expanded Polytetrafluoroethylene-ePTFE-SyntheticNoTetracycline[8,16,19,44]
Amoxicillin[16,19]
(MMA)1-co-(HEMA)1/(MA)3-co-(HEA)2SyntheticNoDoxycycline[47,48]
CollagenNatural or
Synthetic
YesMinocycline[12]
Doxycycline[14]
Tetracycline[16,17,18,19]
Amoxicillin[15,16,19]
Metronidazole[15,20,21]
Niridazole[21]
Tinidazole[21]
Chitosan YesMinocycline[49]
Doxycycline[50]
Collagen-Chitosan YesMinocycline[13]
Poly(lactic acid)
-PLA-
SyntheticYesMetronidazole[25]
Doxycycline[28]
Tetracycline[27]
Poly(glycolic acid)
-PGA-
SyntheticYesAzithromycin[29]
Doxycycline[30]
Tetracycline[16,19,51]
Amoxicillin[16,19]
Ornidazole[31]
Polycaprolactone-PCL-SyntheticYesMoxifloxacin[33]
Metronidazole[34,37,38,52]
Vancomycin[36]
Salicylic acid[35]
PGA-PLASyntheticYesTetracycline[39,40,43]
Vancomycin[41]
Metronidazole[10,42]
PolyetheretherketoneSyntheticNoGentamicin[53]
Hyaluronic acidSyntheticYesHinokitiol[54]
Metronidazole[55]
CelluloseSyntheticYesDoxycycline[56]
Tetracycline[57]
HydroxybutyrateSyntheticYesMetronidazole[58]
Silk fibroinSyntheticYesTetracycline[32]
Polyvinylidene difluoride-PVDF-SyntheticNoDoxycycline[59]
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Toledano-Osorio, M.; Vallecillo, C.; Vallecillo-Rivas, M.; Manzano-Moreno, F.-J.; Osorio, R. Antibiotic-Loaded Polymeric Barrier Membranes for Guided Bone/Tissue Regeneration: A Mini-Review. Polymers 2022, 14, 840. https://doi.org/10.3390/polym14040840

AMA Style

Toledano-Osorio M, Vallecillo C, Vallecillo-Rivas M, Manzano-Moreno F-J, Osorio R. Antibiotic-Loaded Polymeric Barrier Membranes for Guided Bone/Tissue Regeneration: A Mini-Review. Polymers. 2022; 14(4):840. https://doi.org/10.3390/polym14040840

Chicago/Turabian Style

Toledano-Osorio, Manuel, Cristina Vallecillo, Marta Vallecillo-Rivas, Francisco-Javier Manzano-Moreno, and Raquel Osorio. 2022. "Antibiotic-Loaded Polymeric Barrier Membranes for Guided Bone/Tissue Regeneration: A Mini-Review" Polymers 14, no. 4: 840. https://doi.org/10.3390/polym14040840

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop