The sodium-treated sepiolite (NaSep)-supported rare earth oxide (RE/NaSep; RE = La, Eu, Dy, and Tm) samples were prepared using the rotary evaporation method. Physicochemical properties of these materials were characterized by XRD, SEM, BET, FTIR, XPS, H₂–TPR, NH₃–TPD, and in situ DRIFTS, and their catalytic activities for formaldehyde (HCHO) (2000 ppm) oxidation were evaluated. The results show that loading of the rare earth oxide on NaSep improved its catalytic performance. Among all the samples, Eu/NaSep performed the best, and complete HCHO conversion was achieved at a temperature of 150 °C and a gas hourly space velocity of 240,000 mL/(g h); a good catalytic activity was still maintained after 45 h of stability test. The catalytic oxidation mechanism of HCHO was studied using the in situ DRIFTS technique. As a result, the effective and stable catalytic performance of the Eu/NaSep sample was mainly due to the presence of hydroxyl groups on the sepiolite surface and the doped rare earth oxides, which contributed to its high performance. HCHO oxidation underwent via the steps of HCHO + O₂ → HCOO⁻ + OH⁻ → H₂O + CO₂. It is concluded that the optimal catalytic activity of Eu/NaSep was associated with the highest O_ads/O_latt atomic ratio, the largest amount of hydroxyl groups, the highest acidity, and the best reducibility. The present work may provide new insights into the application in the removal of high-concentration HCHO over the rare earth oxides supported on natural low-cost clays. Full article

New iron-oxide-based anodes are prepared by an environmentally-friendly and low-cost route. The analysis of the composition, structure, and microstructure of the samples reveals the presence of a major hematite phase, which is accompanied by a certain concentration of an oxyhydroxide phase, which can act as a “lithium-reservoir”. By using sodium alginate as a binder, the synthesized anodes display superior electrochemical response, i.e., high specific capacity values and high stability, not only versus Li but also versus a high voltage cathode in a full cell. From these bare materials, clay-supported anodes are further obtained using sepiolite and bentonite natural silicates. The electrochemical performance of such composites is improved, especially for the sepiolite-containing one treated at 400 °C. The thermal treatment at this temperature provides the optimal conditions for a synergic nano-architecture to develop between the clay and the hematite nanoparticles. High capacity values of ~2500 mA h g⁻¹ after 30 cycles at 1 A g⁻¹ and retentions close to 92% are obtained. Moreover, after 450 cycles at 2 A g⁻¹ current rate, this composite electrode displays values as high as ~700 mA h g⁻¹. These results are interpreted taking into account the interactions between the iron oxide nanoparticles and the sepiolite surface through hydrogen bonds. The electrochemical performance is not only dependent on the oxidation state and particle morphology, but the composition is revealed as a key feature. Full article