Search Results (5)

Multifunctional road marking coatings with the functions of high-temperature stability, degradation of exhaust gas, and self-cleaning are of great significance for the safe operation and environmental protection of tunnels. This article uses active acrylic resin and an organosilicon hydrophobic agent as the base material, selects expanded vermiculite and glass microspheres as insulation fillers, and uses ammonium polyphosphate, pentaerythritol, melamine, and aluminum hydroxide as high-thermal-stability systems to prepare a two-component road marking coating base material. Then, nano SiO₂ and modified nano TiO₂ are added as modifiers to prepare a multifunctional road marking coating for tunnels. The physical and chemical properties of multifunctional road marking coatings are evaluating based on laboratory tests including thermogravimetry and derivative thermogravimetry, differential scanning calorimetry, infrared spectroscopy, scanning electron microscopy, exhaust degradation, and contact angle tests. The results indicate that the developed multifunctional road marking coating effectively reduces the thermal conductivity of the carbon layer through physical changes in the flame retardant system and the heat resistance formed by the high breaking bond energy of nano SiO₂ during the combustion process. It forms a ceramic-like structure of titanium pyrophosphate with nano TiO₂ that is beneficial for improving flame retardancy without generating harmful volatile gases and has good flame retardant properties. N–V co-doping reduces the bandgap of TiO₂, broadens the absorption range of visible light by nano TiO₂, improves the catalytic efficiency of visible light, and achieves the degradation efficiency of the four harmful components NO_x, HC, CO, and CO₂ in automotive exhaust by 23.4%, 8.3%, 2.5%, and 2.9%, respectively. The solid–liquid phase separation in the multifunctional road marking coating in the tunnel causes the formation and accumulation of nano SiO₂ and TiO₂ particles on the coating surface, resulting in a microstructure similar to the “micro–nano micro-convex” on the lotus leaf surface and making a water droplet contact angle of 134.2° on the coating surface. Full article

Melamine-resin microspheres were synthesized at a pH of 4.0 for 20 min and used as silver nanoparticle (AgNP) carriers for surface enhanced resonant Raman scattering (SERRS) detection. An acetic acid–treatment reaction was introduced into the fabrication of the final substrate. The SERRS performance of the substrate was effectively optimized by regulating excess formaldehyde and experimental parameters, such as acidity, number of treatments and reaction temperature in the acid-treatment reaction. Based on the SERRS detection, it was declared that a trace amount of oligomers with a certain degree of polymerization is necessary for the construction of SERRS hotspots. In addition, it is important to remove excess oligomers with reference to the synthetic reaction of the polymer materials, given the special role of oligomers and the wide application of polymer materials in SERRS detection. Full article

In this article, the intumescent flame-retardant microsphere (KC-IFR) was prepared by inverse emulsion polymerizations, with the use of k-carrageenan (KC) as carbon source, ammonium polyphosphate (APP) as acid source, and melamine (MEL) as gas source. Meanwhile, benzoic acid functionalized graphene (BFG) was synthetized as a synergist. A “four-source flame-retardant system” (KC-IFR/BFG) was constructed with KC-IFR and BFG. KC-IFR/BFG was blended with waterborne epoxy resin (EP) to prepare flame-retardant coatings. The effects of different ratios of KC-IFR and BFG on the flame-retardant properties of EP were investigated. The results showed that the limiting oxygen index (LOI) values increased from 19.7% for the waterborne epoxy resin to 28.7% for the EP1 with 20 wt% KC-IFR. The addition of BFG further improved the LOI values of the composites. The LOI value reached 29.8% for the EP5 sample with 18 wt% KC-IFR and 2 wt% BFG and meanwhile, UL-94 test reached the V-0 level. In addition, the peak heat release (pHRR) and smoke release rate (SPR) of EP5 decreased by 63.5% and 65.4% comparing with EP0, respectively. This indicated the good flame-retardant and smoke suppression property of EP composites coating. Full article

In order to improve the general problem of irregular coating morphology and low mechanical strength of the coating layer in existing coating desensitization technology, nano-cyclotrimethylene trinitramine/melamine-urea-formaldehyde (RDX/MUF) composite energetic microspheres were prepared by an improved emulsion polymerization, taking the MUF as the binder and RDX as the main explosive. In order to judge whether RDX/MUF possessed good stability, the combination of differential scanning calorimetry (DSC) and molecular dynamics (MD) simulation was used to determine the level of binding binding energy between urea-formaldehyde resin binder (UF) and RDX. In addition, to investigate the optimal reaction temperature for the preparation of MUF/RDX, the binding energy between UF and RDX at different temperatures was simulated. And then the morphology and thermal properties of the as-prepared composite energetic microspheres were analyzed by scanning electron microscopy (SEM) and DSC, the impact sensitivity and friction sensitivity of the resultant samples were tested as well. Moreover, RDX/MUF with the same MUF content was prepared by physical mixing for comparative analysis. MD simulation demonstrated that UF and RDX possessed good binding ability at 298 K. The DSC method indicatec that UF and RDX had good compatibility, and the comprehensive performance of RDX after coating was not significantly deteriorated; The optimal binding temperature between UF and RDX was 60~70 °C which is consistent with the experimental results. The experimental results showed that the optimum process conditions for the preparation of RDX/MUF could be listed as follows: the temperature for preparing RDX/MUF composite energetic microspheres by the improved emulsion polymerization was 70 °C the optimal pH value of the urea-formaldehyde resin prepolymer solution was 3, and the optimal melamine-urea molar ratio was 0.4. Full article

Influence of the excess monomer within the synthetic reaction solution of melamine resin microspheres (MFMSs) on the surface-enhanced Raman spectroscopy (SERS) enhancement from Rhodamine 6G (R6G) was investigated, where the R6G was adsorbed on the silver nanoparticles (AgNPs) that were loaded on the MFMSs. Surface characteristics of the MFMSs were modified by the excess monomer (i.e., the excessive melamine or formaldehyde) through its terminal overreaction, which can be simply controlled by some of the synthetic reaction conditions, thus further allowing us to optimize the assembly of the loaded AgNPs for the SERS detection. These SERS substrates incorporating the optimized MFMSs with the excess formaldehyde can also be used for tracing analyses of more environmental and food contaminants. Full article