The main objective of this study is the synthesis, use, and reuse of magnetic copper ferrite nanospheres (CFNS) for extra-heavy oil viscosity reduction. The CFNS were synthesized using a solvothermal method resulting in mean particle size of 150 nm. Interactions of CFNS with the crude oil were evaluated through asphaltene adsorption isotherms, as well as static and dynamic rheology measurements for two cycles at 25 °C. Adsorption and desorption experiments corroborated that most of the asphaltenes adsorbed can be removed for nanoparticle reuse. During the rheology tests, nanoparticles were evaluated in the first cycle at different concentrations from 300 to 1500 mg/L, leading to the highest degree of viscosity reduction of 18% at 500 mg/L. SiO₂ nanoparticles were evaluated for comparison issues, obtaining similar results regarding the viscosity reduction. After measurements, the CFNS were removed with a magnet, washed with toluene, and further dried for the second cycle of viscosity reduction. Rheology tests were performed for a second time at a fixed concentration of 500 mg/L, and slight differences were observed regarding the first cycle. Finally, changes in the extra-heavy oil microstructure upon CFNS addition were observed according to the significant decrease in elastic and viscous moduli. Full article

Copper ferrites containing Cu⁺ ions can be highly active heterogeneous Fenton catalysts due to synergic effects between Fe and Cu ions. Therefore, a method of copper ferrite nanosphere (CFNS) synthesis was selected that also permits the formation of cuprite, obtaining a CFNS composite that was subsequently calcined up to 400 °C. Composites were tested as Fenton catalysts in the mineralization of phenol (PHE), p-nitrophenol (PNP) and p-aminophenol (PAP). Catalysts were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS) and magnetic measurements. Degradation of all phenols was practically complete at 95% total organic carbon (TOC) removal. Catalytic activity increased in the order PHE < PNP < PAP and decreased when the calcination temperature was raised; this order depended on the electronic effects of the substituents of phenols. The as-prepared CFNS showed the highest catalytic activity due to the presence of cubic copper ferrite and cuprite. The Cu⁺ surface concentration decreased after calcination at 200 °C, diminishing the catalytic activity. Cuprite alone showed a lower activity than the CFNS composite and the homogeneous Fenton reaction had almost no influence on its overall activity. CFNS activity decreased with its reutilization due to the disappearance of the cuprite phase. Degradation pathways are proposed for the phenols. Full article