Search Results (4)

Manganese slag (MS) containing a certain amount of active hydration substances may be used as a kind of cementitious material. In the present study, we measured the mass, the relative dynamic modulus of elasticity (RDME), and the flexural and compressive strengths of MS high-performance concrete (MS-HPC) with added basalt fibers exposed to NaCl freeze–thaw cycles (N-FCs), NaCl dry–wet alternations (N-DAs), and Na₂SO₄ dry–wet alternations (NS-DAs). Scanning electron microscope energy-dispersive spectrometer (SEM-EDS) spectra, thermogravimetric analysis (TG) curves, and X-ray diffraction spectroscopy (XRD) curves were obtained. The mass ratio of MS ranged from 0% to 40%. The volume ratio of basalt fibers varied from 0% to 2%. We found that, as a result of salt action, the mass loss rate (MLR) exhibited linear functions which were inversely correlated with the mass ratio of MS and the volume ratio of basalt fibers. After salt action, MLR increased by rates of 0~56.3%, but this increase was attenuated by the addition of MS and basalt fibers. Corresponding increases in RDME exhibited a linear function which was positively correlated with MS mass ratios in a range of 0~55.1%. The addition of MS and basalt fibers also led to decreased attenuation of mechanical strength, while the addition of MS led to increased levels of flocculent hydration products and the elements Mn, Mg, and Fe. CaClOH and CaSO₄ crystals were observed in XRD curves after N-DA and NS-DA actions, respectively. Finally, the addition of MS resulted in increased variation in TG values. However, the opposite result was obtained when dry–wet actions were exerted. Full article

Steel pipes are commonly used to strengthen the concrete’s load-bearing capacity. However, they are prone to corrosion in salt erosion environments. In this study, the influence of Na₂MoO₄ and benzotriazole on concrete-filled steel tubes’ corrosion performance is investigated. The steel pipes’ mass loss rates (MRs), ultrasonic velocity, electrical resistance, and the AC impedance spectrum and Tafel curves of concrete-filled steel tubes were used to characterize the degree of corrosion in the steel pipes. Scanning electron microscopy–energy-dispersive spectrometry and X-ray diffraction were used for studying the composition of steel pipe rust. The research results revealed that the NaCl freeze–thaw cycles (F-C) and NaCl dry–wet alternation (D-A) actions had a reducing effect on the mass and ultrasonic velocity of the concrete-filled steel tubes. After 300 NaCl F-C and 30 NaCl D-A, the MRs were 0%~0.00470% and 0%~0.00666%. The corresponding ultrasonic velocities were 0%~21.1% and 0%~23.6%. When a rust inhibitor was added, the results were the opposite. The MRs decreased by 0%~80.3% and 0%~81.6% with the added Na₂MoO₄ and benzotriazole. Meanwhile, the corresponding ultrasonic velocities were 0%~8.1% and 0%~8.3%. The steel tubes were corroded after 300 NaCl F-C and 30 NaCl D-A. The addition of rust inhibitors improved the corrosion resistance of the concrete-filled steel tubes by increasing the electrical resistance before NaCl erosion. The corrosion area rate decreased by using the rust inhibitors. The corrosion resistance effect of benzotriazole was higher than that of Na₂MoO₄. The concrete-filled steel tube with an assembly unit comprising 5 kg/m³ of Na₂MoO₄ and 15 kg/m³ of benzotriazole had the best corrosion resistance under the erosion induced by NaCl F-C and D-A. Rust inhibitors reduced the content of iron-containing crystals and iron elements. The specimens with 5 kg/m³ Na₂MoO₄ and 15 kg/m³ benzotriazole had the lowest concentration of iron-containing crystals and iron elements. Full article

In recent years, promising developments in the hydrothermal carbonization (HTC) of sewage sludge, as well as the potential to reclaim phosphorus and nitrogen, have emerged. In this study, the HTC of digested sewage sludge (DSS) was investigated for the downstream production of heavy metal (HM)-free fertilizer and the use of freeze concentration (FC) as a novel technology for process water treatment. To obtain clean fertilizer, phosphatic acid extracts were first treated with ion-exchange resins to remove dissolved HM, as well as phosphorus precipitating agents (i.e., aluminum and iron). Over 98% of the aluminum (Al) and 97% of the iron (Fe) could be removed in a single treatment step. The purified extract was then used for the precipitation of HM-free struvite crystals, with P-recovery rates exceeding 89%. Process water (PW) makes up the largest share of the two main HTC-products (i.e., hydrochar and PW) and is very rich in organic compounds. Compared to evaporation or membrane separation, FC is a promising technology for concentrating solutes from PW. Separation experiments resulted in the recovery of over 90% of the dissolved compounds in the concentrate. In our study, the concentrate was later utilized as an ammonium source for struvite precipitation, and the subsequent aerobic digestion of the remaining ice water resulted in an 85% reduction in chemical oxygen demand (COD) in 15 days. Full article

In the present work, freeze crystallization studies, as a novel concentration method for aqueous 1,5-diazabicyclo[4.3.0]non-5-enium acetate ([DBNH][OAc]) ionic liquid solution, were conducted. In order to find the appropriate temperature and composition range for freeze crystallization, the solid–liquid equilibrium of a binary [DBNH][OAc]–water compound system was investigated with differential scanning calorimetry (DSC). Results of this analysis showed that the melting temperature of the pure ionic liquid was 58 ℃, whereas the eutectic temperature of the binary compound system was found to be −73 ℃. The activity coefficient of water was determined based on the freezing point depression data obtained in this study. In this study, the lowest freezing point was −1.28 ℃ for the aqueous 6 wt.% [DBNH][OAc] solution. Ice crystal yield and distribution coefficient were obtained for two types of aqueous solutions (3 wt.% and 6 wt.% [DBNH][OAc]), and two freezing times (40 min and 60 min) were used as the main parameters to compare the two melt crystallization methods: static layer freeze and suspension freeze crystallization. Single-step suspension freeze crystallization resulted in higher ice crystal yields and higher ice purities when compared with the single-step static layer freeze crystallization. The distribution coefficient values obtained showed that the impurity ratios in ice and in the initial solution for suspension freeze crystallization were between 0.11 and 0.36, whereas for static layer freeze crystallization these were between 0.28 and 0.46. Consequently, suspension freeze crystallization is a more efficient low-energy separation method than layer freeze crystallization for the aqueous-ionic liquid solutions studied and, therefore, this technique can be applied as a concentration method for aqueous-ionic liquid solutions. Full article