Next Article in Journal
Functionalization and Antibacterial Applications of Cellulose-Based Composite Hydrogels
Next Article in Special Issue
Recent Progress and Potential Biomedical Applications of Electrospun Nanofibers in Regeneration of Tissues and Organs
Previous Article in Journal
Mastering of Filled Rubber Strength beyond WLF: Competition of Temperature, Time, Crack Deflection and Bond Breaking
Previous Article in Special Issue
Metronidazole Topically Immobilized Electrospun Nanofibrous Scaffold: Novel Secondary Intention Wound Healing Accelerator
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 14
Issue 4
10.3390/polym14040766
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Phyto-Assisted Assembly of Metal Nanoparticles in Chitosan Matrix Using S. argel Leaf Extract and Its Application for Catalytic Oxidation of Benzyl Alcohol

by
Amel Taha
1 and
Enshirah Da’na
2,*
1
Department of Chemistry, College of Science, King Faisal University, P.O. Box 400, Al-Ahsa 31982, Saudi Arabia
2
Department of Biomedical Engineering, College of Engineering, King Faisal University, P.O. Box 400, Al-Ahsa 31982, Saudi Arabia
*
Author to whom correspondence should be addressed.
Polymers 2022, 14(4), 766; https://doi.org/10.3390/polym14040766
Submission received: 1 February 2022 / Revised: 11 February 2022 / Accepted: 13 February 2022 / Published: 16 February 2022
(This article belongs to the Special Issue Biopolymers-Based Nanocomposites: Preparation, Properties and Applications)
Browse Figures
Versions Notes

Abstract

:
The design and synthesis of eco-friendly solid-supported metal nanoparticles with remarkable stability and catalytic performance have gained much attention for both industrial and environmental applications. This study provides a novel, low-cost, simple, and eco-friendly approach for decorating cross-linked chitosan with gold nanoparticles (AuNPs), greenly prepared with Solenostemma argel (S. argel) leaf extract under mild conditions. Glutaraldehyde-modified chitosan beads were used to coordinate with Au(III) ions and act as stabilizing agents, and S. argel leaf extract was used as a cost-effective phyto-reducing agent to reduce gold ions to elemental Au nanoparticles. The successful cross-linking of chitosan with glutaraldehyde, the coordination of Au(III) ions into the chitosan matrix, and the phytochemical reduction of Au(III) to Au nanoparticles were investigated via FT-IR spectroscopy. The obtained Au nanoparticles have a uniform spherical shape and size <10 nm, as confirmed by both X-ray diffraction (XRD) (~8.8 nm) and TEM (6.0 ± 3 nm). The uniformity of the AuNPs’ size was confirmed by Scanning Electron Microscopy (SEM) and Transition Electron Microscopy (TEM). The powder X-ray diffraction technique showed crystalline AuNPs with a face-centered cubic structure. The elemental analysis and the Energy Dispersive Spectroscopy (EDS) analysis both confirmed the successful integration of Au nanoparticles with the chitosan network. The catalytic activity of this highly stable nanocomposite was systematically investigated via the selective oxidation of benzyl alcohol to benzaldehyde. Results showed a remarkable conversion (97%) and excellent selectivity (99%) in the formation of benzaldehyde over other side products.

Graphical Abstract

1. Introduction

Nowadays, the design and synthesis of inorganic/organic hybrid materials (metal nanoparticles/polymer) have attracted much attention, due to their important applications in biomedical [1,2], sensor [3,4,5], semiconductor [6], catalysis [7,8,9,10], solar cell [11], and many other fields [12]. This wide range of applications is mainly due to the fact that these hybrid nanocomposites have attractive electrical [13], optical [13,14,15], and magnetic [16,17,18] characteristics compared to those of pure polymers or inorganic particles. Many polymers, such as poly (amidoamine) (PAMAM) [19,20,21,22] and PPV [11], have been utilized as stabilizing agents or support for different metal nanoparticles, such as copper [23], gold [24], silver [25], and platinum [26].
One of the most abundant biopolymers is chitosan, which is derived from the distillation of chitin that occurs naturally in the exoskeletons of insects, crustacean shells, and fungi cellular walls [27]. Both chitin and chitosan are biocompatible, biodegradable, and non-toxic, with antimicrobial and hydrating effects [27,28]. However, chitosan is preferred, because of its higher solubility [27]. Chitosan-based hybrid materials are considered effective bio-sorbents, since they are relatively cheap and their surfaces are rich in amino and hydroxyl groups [29,30]. They were reported to significantly capture many pollutants, such as p-nitrophenol [31] and heavy metal ions [27]. Furthermore, they have a high chelating affinity towards metal ions, which is related to the high content of nitrogen (6.89%) [29]. Accordingly, chitosan can function as the ideal support for many different species, such as ions and molecules [28,29,32,33]. However, the main challenge to the application of this biological support is its high solubility in most organic acids and dilute mineral solutions. This drawback can be overcome by chemical or physical modification via cross-linking agents, such as ethylene glycol diglycidyl ether, glutaraldehyde (GLA), epichlorohydrin, genipin, or triphosphate [31,34,35]. Among these agents, GLA is the most attractive, since it does not alter the adsorption capacity of chitosan [31]. In addition to enhancing chemical stability, this cross-linking can improve both the mechanical and thermal stability of the chitosan [34,35].
Many synthesis routes have been reported in the literature for AuNPs supported on chitosan derivatives [36,37,38,39,40]. However, there is still serious concern about these routes, mainly related to harsh synthesis conditions, high cost, complexity, the need for toxic chemicals, and metal leaching problems. Furthermore, these approaches are not attractive for biological applications, since they may be toxic and non-biocompatible. Thus, there is a need to develop eco-friendly and green techniques without the need for any toxic chemicals or harsh conditions. So far, many biological species, such as bacteria, viruses, fungi, and plant extracts, have been utilized for the synthesis of AuNPs [41,42,43]. Among all of these facilitating species, plant extract has many attractive features, such as scalability, economic feasibility, simplicity, availability, and non-toxicity [41,44,45]. Carlo et al. (2012) reported a green synthesis route to combine gold nanoparticles with chitosan network via using different organic acids to control the rate of reduction of AuIII into AuNPs and the morphology of the resulting nanoparticles [30].
Solenostemma argel (Apocynaceae) is a North African, naturally grown desert plant that is widely available in Libya, Sudan, Egypt, Algeria, and Saudi Arabia [46]. It is widely used to traditionally treat many diseases [47,48]. The chemical composition of S. argel leaves have been reported in the literature [49]. El-Zayat et al. reported the presence of antifungal, antioxidant, and antibacterial components in the leaf extract [48]. Another chromatographic investigation of S. argel leaves revealed the presence of many chemical components, such as flavonoids and alkaloids, which are known to have excellent reduction and capping effects [50].
Based on this, it is expected that S. argel leaf extract can function as a green reducing agent. Thus, combining it with cross-linked chitosan may enhance the phytochemical assembly of metal nanoparticles within the organic matrix. Accordingly, this current work reports a novel green phytochemical route for the bioreduction of Au(III) ions to elemental Au atoms with the aid of S. argel leaf extract, instead of a chemical reducing agent, for the synthesis of gold nanoparticles within the chitosan matrix under very mild conditions. To the best of our knowledge, the utilization of cross-linked chitosan and leaf extract in green preparation of metal nanoparticles has never been reported. Furthermore, the structural properties of the resulted hybrid nanocomposite and its catalytic performance towards the degradation of alcohol were investigated.

2. Experimental

2.1. Materials

All chemicals and solvents were used as received without further purification. Hydrogen tetrachloroaurate trihydrate (HAuCl4.3H2O) was obtained from Merck (Kenilworth, NJ, USA); chitosan flakes, glutaraldehyde 50%, benzyl alcohol, and 4-nitrophenol were purchased from Sigma Aldrich (Missouri, MS, USA). All aqueous solutions were made using deionized water. S. argel leaves were purchased from the local market of Hofuf City, Eastern Province, Kingdom of Saudi Arabia.

2.2. Methods

2.2.1. Preparation of S. argel Leaf Extract

To prepare the S. argel leaf extract, 20 g of the dried and ground leaf was mixed with 100 mL of deionized water in a 500 mL round flask for one hour. After that, the mixture was boiled for 20 min and filtered under a vacuum, then collected and stored at 4 °C.

2.2.2. Cross-Linked Chitosan Preparation

The chitosan solution was prepared by mixing 2 g of chitosan flakes with 60 mL of acetic acid solution (5% v/v) and stirring for 18 h. Then, the remaining acid within the chitosan gel was neutralized to coagulate the chitosan gel into uniform spherical beads. This was achieved by dropwise precipitation of the mixture into 250 mL of a 0.5M NaOH bath under magnetic stirring at 100 rpm. After that, the beads were thoroughly rinsed with distilled water until neutral pH was reached, dried under ambient conditions, ground, and sieved through a mesh size <200 µm. A suspension was then prepared by mixing a specific mass of the chitosan beads with a similar mass of 2.5% GLA solution for 24 h at 100 rpm and 20 °C. The chitosan-GLA beads were then separated by filtration and thoroughly rinsed with hot distilled water followed by cold distilled water. Finally, the beads were dried, ground, and sieved as before. During the synthesis process, different colors were noticed, indicating some chemical changes taking place during each step.

2.2.3. Preparation of Chitosan-GLA/AuNPs Hybrid Nanocomposite

A specific mass of the synthesized chitosan-GLA beads (0.5 g) was mixed with 30 mL of 0.3 mM HAuCl4 aqueous solutions and stirred for a few minutes to allow the adsorption of Au(III) ions on the chitosan-GLA beads; then, it was filtered, thoroughly washed with deionized water, and dried. To reduce Au(III) into Au nanoparticles, 30 mL of S. argel leaf extract was mixed with 0.5 g of chitosan-GLA beads loaded with Au(III) ions and stirred for 18 h. Finally, the Au-chitosan-GLA beads were filtered, washed with deionized water, dried in a vacuum, and then stored in a dry place.

2.2.4. Characterization Methods

FT-IR spectra of chitosan beads after each step of synthesis were recorded with a Cary 630 FT-IR spectrophotometer within the range of 400 to 4000 cm−1. UV–vis absorption spectroscopy analysis was performed in a Shimadzu UV-1800 spectrophotometer (Kyoto, Japan) using quartz cuvettes. Spectra were collected within the range of 200–800 nm. The crystalline nature of the Au particles in chitosan matrix was analyzed by X-ray diffraction on an XRD Bruker (Billerica, MA, USA) D8 advanced diffractometer with Cu Kα as the radiation source (λ = 1.5418 Å, kV = 40, mA = 40) in the 2θ range of 10–90°. The morphology of AuNPs formed in the biopolymer matrix was explored through field emission scanning electron microscopy (FESEM) using a Philips XL30 (Amsterdam, Netherlands) with accelerating voltage 30 kV and 3.0 mm working distance in the secondary electron imaging mode. Furthermore, energy dispersive X-ray spectrometry (EDX) and transmission electron microscopy (TEM, JEOL JEM-1011-instrument) (Tokyo, Japan) were performed. The thermal stability of the samples was tested with the TGA analysis using a Mettler Toledo (Columbus, OH, USA) TGA/SDTA851E instrument by heating the samples at a ramp of 10 °C min−1 in the range 50–1000 °C under nitrogen atmosphere. The nitrogen adsorption–desorption isotherms at 77 K were performed using a NOVA 4200e (Quantachrome Instruments, FL, USA). The specific surface area was calculated using the Brunauer–Emmett–Teller (BET) equation.

2.3. Catalytic Evaluation of Chitosan-GLA/AuNPs Hybrid Nanocomposite

The catalytic activity of chitosan-GLA/AuNPs nanocomposite was evaluated through the oxidation of benzyl alcohol to its relevant carbonyl compounds, with H2O2 as an oxidant. The oxidation reaction of alcohol was carried out in a magnetically stirred glass beaker (50 mL). Typically, 1 mmol alcohol substrate, 1.2 mmol H2O2, and 8.6 mg catalyst were added into 5 mL water. The suspension was then heated up to 80 °C and stirred for 6 h. After completion of the reaction (monitored by TLC), the catalyst was separated from the reaction mixture by centrifuge. The products were analyzed by GC (Perkin Elmer Clarus 500) (Waltham, MA, USA) equipped with a FID detector and identified by comparison with known standards. The recovered catalyst was washed with deionized water and ethanol, dried, and kept in a desiccator.

3. Result and Discussion

3.1. FT-IR

The successful cross-linking modification of chitosan and subsequent coordination of Au(III) ions into biopolymer matrix and phytochemical reduction can be partially investigated via FT-IR spectroscopy, as shown in Figure 1. The spectrum of chitosan flakes (Figure 1a) shows a strong, broad vibration at around 3425 cm−1 assigned to the stretching vibration of O–H and N–H groups, while the peak at 1650 cm−1 is attributed to the N–H bending vibration of primary amine (–NH2 in chitosan flakes). After the cross-linking with GLA, this bending band disappeared, due to the participation of –NH2 of chitosan in the cross-linking with GLA (Figure 1b). In contrast, the intensity of absorption peaks in the region 2800–3000 cm−1, corresponding to the –CH2 and –CH3 groups of chitosan and GLA, remarkably increased. In addition, a significant new peak in Figure 1b, which appeared at 1662 cm−1, is presumably the characteristic band of Schiff base, that is, strong stretching vibration of imine (C=N), confirming the successful cross-linking modification of the chitosan. In addition, the absence of any peak at 1720 cm−1 indicated that there was no unreacted pendant aldehyde group and cross-linking was almost completed.
Due to their excellent chelating capacity, the modified chitosan-GLA beads are considered an attractive adsorbent to coordinate with metal ions. This is mainly because of the large number of hydroxyl functional groups and Schiff-base structure. After adding chitosan-GLA beads to the aqueous solution of HAuCl4, the color of the beads gradually changed from orange to dark red as a result of adsorbing Au(III) ions onto the biopolymer matrix. Finally, after mixing these beads with an aqueous solution of S. argel leaf extract, the color changed from dark red to black. This is due to the complete reduction of coordinated Au(III) ions to elemental Au and the assembly of AuNPs in the biopolymer matrix. This mechanism was confirmed by the FT-IR and UV–vis spectroscopies analysis. The FT-IR spectrum of chitosan-GLA/AuNPs beads is shown in Figure 1c. The significant difference in FT-IR spectra of the chitosan-GLA and chitosan-GLA/AuNPs beads (curves b and c) was a shift of C=N stretching frequencies from 1662 to 1637 cm−1, which is indicative of the back-bonding metal–ligand coordination. The presence of a shoulder at 1550 cm−1 is related to the amide II band that may contribute to the amine –NH2 group, which was specific for chitosan cross-linking with glutaraldehyde [51,52]. Additionally, the intensity of the O–H stretching band at 3445 cm−1 from the hydroxyl groups of chitosan rings decreased when Au loaded to the chitosan chains, suggesting the chelation of Au with both imine and hydroxyl groups of modified chitosan, as shown in Figure 1c. For chitosan-gold beads, the broadening in the region of 2800–3600 cm−1 indicates that NH2 and OH are involved in the stabilization of AuNPs [36,53]. This result confirms the existence of a chemical bond between the chitosan-GLA matrix and Au nanoparticles.

3.2. UV–vis

In addition to the FT-IR evidence, the UV–vis analysis of chitosan flakes and chitosan-GLA/AuNPs beads was helpful to prove the successful assembly of small AuNPs in the polymer matrix. As seen, while the spectrum of chitosan flakes had no absorbance in the region of 400–800 nm, there was a remarkable maximum absorbance (λmax) for Au-loaded chitosan at ~530 nm. It has already been shown that the absorbance around ~530 nm is the main characteristic of the gold nanoparticles with core sizes of 2–10 nm in diameter [30,54]. Accordingly, Figure 2 qualitatively indicated the embedment of AuNPs 2–10 nm in the chitosan matrix. It is worth mentioning that a UV–vis analysis of the solution after mixing the chitosan-GLA beads with the aqueous solution of HAuCl4 was performed, and no Au nanoparticle peaks were detected at this stage, confirming that the reduction was caused by the plant extract.

3.3. Elemental Analysis

The elemental analysis of the samples showed that, following the cross-linking modification of chitosan flakes, the N content of samples decreased from 7.80 to 6.95% (Table 1, entries 1 and 2), while an increase in the contents of C and H was observed. This is in good agreement with the attachment of the cross-linking agent (GLA), with several carbon and hydrogen atoms, to the chitosan matrix. In addition, the Au contents of chitosan-GLA/Au(III) and chitosan-GLA/AuNPs beads, estimated by atomic absorption spectroscopy, were 0.1032 and 0.10280 mmol g−1, respectively (Table 1, entries 3 and 4). This indicated that ~99% of the coordinated Au(III) ions were phytochemically reduced to elemental gold with S. argel leaf extract to form small AuNPs incorporated in the biopolymer matrix.

3.4. XRD

The growth of AuNPs in the matrix of chitosan-GLA beads under phytochemical reduction of Au(III) ions with S. argel leaf extract was also confirmed by XRD analysis. Figure 3a shows the powder XRD patterns for the chitosan flakes and illustrates the presence of two broad peaks observed in the 2θ range of 12° to 26° which are assigned to the crystallinity of the original chitosan flakes. As seen in Figure 3b, these peaks are still preserved after the cross-linking process. The characteristic peaks at 38.2°, 44.6°, and 64.6°, attributed to the classical planes of face-centered cubic lattices of AuNPs in chitosan matrix, are also evidenced (Figure 3c), indicating that the embedment of AuNPs in biopolymer networks does not change their crystalline structure. Since the content of AuNPs in the Au–chitosan composite was very low, the diffraction intensities of the gold were weak in the pattern of the composite. According to the full width at half-maximum (FWHM) of the diffraction peak from a crystalline plane (111), the average size of AuNPs in the composite was estimated from the Scherrer equation to be ~8.8 nm. The results were consistent with the electron micrograph observations to be discussed later. Furthermore, the XRD pattern of the samples was used to estimate the degree of crystallinity for each sample using Origin 2020 software. The results of crystallinity are recorded in Table 2, which shows that chitosan-GLA/AuNPs beads have the highest degree of crystallinity of 64.21%.

3.5. FESEM

Figure 4 shows the FESEM images of the chitosan-GLA (a) and chitosan-GLA/AuNPs (b). As seen, some spherical Au particles were detected on the surface of the chitosan (surrounded by red circles in Figure 4b). However, most of the AuNPs are mostly encapsulated within the chitosan polymeric matrix, due to the cross-linking modification process. Figure 4c,d shows the EDS analysis, which confirms that chitosan-GLA beads contain no Au atom, while the chitosan-GLA/AuNP nanocomposite contains about 31.49 wt.% Au (2.93 atom%), 48.65 wt.% carbon (74.30 atom%), and 19.86 wt.% oxygen (22.77 atom%), as shown in the insert of Figure 4c,d. Since no other capping or reducing agents were used during synthesis, these results thus clearly demonstrated that S. argel leaf extract acted as a reducing agent. On the other hand, the chitosan-GLA beads acted as a sorbent to coordinate with Au(III) ions and a dispersant to trap the initially formed gold seeds and prevent them from further growth and aggregation in the synthesis process of AuNPs. The appearance of some Pt traces in the chitosan-GLA beads analysis (Figure 4c) is related to the platinum grid used as a sample holder.

3.6. TGA

The thermal stability of the prepared nanocomposites was explored by the thermogravimetric analysis (TGA) of chitosan, chitosan-GLA, and chitosan-GLA/AuNPs. Figure 5 shows the three stages of mass loss for chitosan. The first loss is attributed to the loosely bonded moisture (~5%) in the range 50–100 °C. The chitosan mass was then stable until the beginning of the second stage at 240 °C. The second weight loss (~41%) occurred in the range of 240–330 °C, due to the decomposition of polymer chains. The third stage is slower than the second and is extended in the temperature range 330–900 °C, with a loss of ~27% related to the continuous decomposition of the polymer chain. The total chitosan loss for the entire temperature range was 73%. The chitosan-GLA/AuNPs and the chitosan-GLA follow the same profile for the first stage in the temperature range 50–195 °C, with a mass loss of ~10%, which may be related to the loss of moisture attached to the surface. After 195 °C, the mass loss of chitosan-GLA was slower than that of chitosan-GLA/AuNPs until 430 °C, with a total loss of 54% for the three samples. The loss in this stage could be attributed to the decomposition of chitosan and GLA chains in addition to S. argel leaf extract coated on AuNPs for chitosan-GLA/AuNP. The third stage is in the range 430–900 °C, with mass losses of 12%, 19%, and 19% for chitosan-GLA/Au, chitosan-GLA, and chitosan-GLA, respectively, which may be related to the decomposition of chitosan, GLA, and S. argel leaf extract. The total mass loss of chitosan-GLA/Au (65%) was lower than that of chitosan and chitosan-GLA (73%), due to the strengthening effect of the embedded AuNPs, which is believed to play a key role in composite stability. It is assumed that AuNPs with higher surface energy simply combine with the oxygen or water in the air and increase the possibility for interfacial hydrogen-bonding formation. In consequence, this could reduce the mobility of chitosan chains in the composite. The chain mobility reduction could in turn suppress the chain transfer reaction and slow the degradation process of the biopolymer, and so its decomposition could take place at higher temperatures. These results demonstrated that the thermal stability of chitosan remarkably improved when modified with GLA and doped with AuNPs.

3.7. TEM

The transmission electron microscopy imaging provided further insight into the morphology and mean size of the AuNPs loaded in the chitosan matrix. A representative TEM image recorded from chitosan-GLA/AuNPs beads synthesized using S. argel leaf extract is shown in Figure 6a. As seen in the image, the spherical AuNPs with diameters no more than 10 nm are well separated and reasonably dispersed. Figure 6b shows single-crystal AuNPs with a lattice d-spacing of 2.36°A in the (1 1 1) plane, which is related to face-centered cubic (f c c) structure. Additionally, to understand the role of chitosan in the phytochemical-assisted formation of AuNPs, in a control experiment the possibility of the formation of AuNPs using S. argel leaf extract without cross-linked chitosan was tested. The TEM image of the product (Figure 6c) showed that there was a wide range of sizes and different morphologies and shapes of the AuNPs (spherical, triangle, cubic, and oval), and various sizes were observed. This revealed that, even though the S. argel leaf extract is capable of reducing the Au(III) ions to elemental Au, using cross-linked chitosan is necessary to have better control over the shape and size. Huang et al. (2007) prepared triangular and spherical gold nanoparticles by reacting Cinnamomum camphora leaf extract with aqueous gold precursors. They attributed the controlled shape of the gold nanoparticles to the protective and reductive biomolecules used [55]. Dwivedi et al. (2010) used Chenopodium album leaf extract for the green synthesis of gold nanoparticles and reported 10–30 nm spherical nanoparticles [43]. Sugunan et al. (2005) prepared spherical gold nanoparticles with an average size of 20 nm supported on chitosan [56]. This controlling effect of chitosan on morphology and size of the AuNPs is due to the lowering of the growth rate of initially formed small spherical Au seeds, which are trapped in a polymeric matrix (Figure 6a), show no tendency to aggregate, and are stable for one year. The image in Figure 6d was used in Figure 6e about the particle size distribution histogram. Accordingly, the average particle size of AuNPs was found to be around 6.0 ± 3 nm, which is consistent with the results obtained by XRD (8.8 nm).
Altogether, the aforementioned spectroscopic and microscopic observations confirmed the phyto-inspired assembly of Au atoms in the matrix of cross-linked chitosan with the aid of S. argel leaf extract, resulting in the feasible formation of highly stable spherical AuNPs smaller than 10 nm. All processes occurred at room temperature and were completed in a few minutes through a green and cost-effective route without using any organic solvent or chemical toxic reducing/stabilizing agents.

3.8. Specific Surface Area (BET)

BET surface area for the chitosan at different stages of modification was measured and recorded in Table 2. The BET surface area of the chitosan-GLA/AuNPs beads is 4.90 m2g−1, which is better than many other modified chitosans reported in the literature [57]. This relatively high specific surface area for the chitosan-GLA/AuNPs beads is useful for the catalytic oxidation activity of this catalyst. It is apparent in Table 2 that the sample with the highest surface area resulted in the highest oxidation activity. The BET results strongly support the fact that the chitosan-GLA/AuNPs have a porous structure, as indicated by SEM [57].

3.9. Catalytic Activity Studies

The catalytic activity of the AuNPs loaded in the chitosan matrix was quantitatively determined for the oxidation of benzyl alcohol (BnOH) by H2O2 to its relevant carbonyl compounds. This process is a very important intermediate in the production of various biologically and industrially important substances. It was observed that in the presence of a specific amount of chitosan-GLA/AuNPs beads, with Au content of 0.102 mmol, stirring of the reaction medium containing an aqueous solution of BnOH and H2O2 led to the desired benzaldehyde compounds as final products. For instance, it was found that a combination of 1 mmol of BnOH, 1.25 mmol of H2O2, and 8.6 mg of chitosan-GLA/AuNPs beads and stirring the mixture for 6 h at 80 °C could result in the remarkable conversion (97%) and excellent selectivity (99%) in the formation of benzaldehyde over the other possible products.
It is worth mentioning that, while in the positive control experiment, in the absence of a catalyst, only 10% conversion of BnOH was observed (Table 2, entry 2), in the negative control experiment with chitosan-GLA/AuNPs catalyst, in the absence of H2O2, the solution remained unchanged. Meanwhile, using S. argel leaf extract, chitosan flakes, chitosan-GLA beads, and chitosan-GLA/Au3+ beads as catalysts showed very low to moderate conversions (Table 2, entries 3–6). As shown, none of these added compounds could efficiently catalyze the oxidation reaction. The moderate conversion observed using chitosan-GLA/Au3+ beads was due to Au3+-promoted oxidation of BnOH. Altogether, these simple control experiments confirmed the efficient catalytic role of chitosan-GLA/AuNPs composite in BnOH oxidation with excellent conversion. In addition, the Au-chitosan hybrid nanocatalyst was found to be reusable at least for four runs (Table 2, entries 7–9), and during the reuse experiments, no deformation, agglomeration, or Au leaching was observed.

4. Conclusions

In summary, a novel, green, and cost-effective combination of cross-linked chitosan and biological leaf extract of a plant (S. argel) has been utilized towards the assembly of stable AuNPs in the matrix of a biopolymer. The cross-linking of chitosan with glutaraldehyde provided a thermally stable framework for loading of Au(III) ions and their reduction to elemental Au by S. argel leaf extract, instead of any other toxic chemical reducing agent. The processes in this study provided a method for the preparation of well-controlled size and morphology of gold nanoparticles and may find significant industrial importance in solid-supported metal nanoparticles preparation. The Au particles were spherical and monodispersed (<10 nm). In addition, the catalytic performance of the obtained Au-chitosan hybrid nanocomposite was evaluated. The resultant nanocomposite showed remarkable performance of catalytic activity towards the oxidation reaction of benzyl alcohol to its relevant carbonyl compounds with excellent conversion and selectivity, using hydrogen peroxide as an oxidant. Moreover, the recyclability features of this nanocomposite make it a good candidate to be considered as a green catalyst in bioorganic synthetic routes to drugs and pro-drugs.

Author Contributions

A.T.: conceptualization, investigation, methodology, data curation, formal analysis, writing—original draft preparation, funding acquisition. E.D.: visualization, formal analysis, writing—reviewing and editing, funding acquisition. All authors have read and agreed to the published version of the manuscript.

Funding

This research was funded by Deanship of Scientific Research at King Faisal University, grant number AN000439 and the APC was funded by Deanship of Scientific Research at King Faisal University.

Institutional Review Board Statement

Not applicable.

Data Availability Statement

The data presented in this study are available on request from the corresponding author.

Acknowledgments

The authors extend their appreciation to the Deanship of Scientific Research at King Faisal University for funding this research through project number AN000439.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Park, W.; Shin, H.; Choi, B.; Rhim, W.-K.; Na, K.; Han, D.K. Advanced hybrid nanomaterials for biomedical applications. Prog. Mater. Sci. 2020, 114, 100686. [Google Scholar] [CrossRef]
  2. Liu, Y.; Ji, X.; He, Z. Organic–inorganic nanoflowers: From design strategy to biomedical applications. Nanoscale 2019, 11, 17179–17194. [Google Scholar] [CrossRef]
  3. Yu, M.-R.; Suyambrakasam, G.; Wu, R.-J.; Chavali, M. Preparation of organic–inorganic (SWCNT/TWEEN–TEOS) nano hybrids and their NO gas sensing properties. Sens. Actuators B Chem. 2012, 161, 938–947. [Google Scholar] [CrossRef]
  4. Wang, C.; Wang, H.; Zhang, M.; Zeng, B.; Zhao, F. Molecularly imprinted photoelectrochemical sensor for aflatoxin B1 detection based on organic/inorganic hybrid nanorod arrays. Sens. Actuators B Chem. 2021, 339, 129900. [Google Scholar] [CrossRef]
  5. Huang, G.; Zhou, H.; Wang, C.; Kashi, C.; Ye, X.; Li, W.; Wang, G.-E.; Xu, G. A new 1D inorganic–organic hybrid perovskite-like semiconductor with high stability and humidity response. Inorg. Chem. Commun. 2021, 128, 108581. [Google Scholar] [CrossRef]
  6. Kanaujia, P.K.; Dehury, K.M.; Adnan, M.; Prakash, G.V. Alternative fabrication methodologies for two-dimensional self-assembled Inorganic-Organic hybrid semiconductors. Opt. Mater. 2020, 110, 110511. [Google Scholar] [CrossRef]
  7. Salvo, A.M.P.; Giacalone, F.; Gruttadauria, M. Advances in Organic and Organic-Inorganic Hybrid Polymeric Supports for Catalytic Applications. Molecules 2016, 21, 1288. [Google Scholar] [CrossRef] [Green Version]
  8. Berijani, K.; Morsali, A. The role of metal–organic porous frameworks in dual catalysis. Inorg. Chem. Front. 2021, 8, 3618–3658. [Google Scholar] [CrossRef]
  9. Varadwaj, G.B.B.; Parida, K.; Nyamori, V.O. Transforming inorganic layered montmorillonite into inorganic–organic hybrid materials for various applications: A brief overview. Inorg. Chem. Front. 2016, 3, 1100–1111. [Google Scholar] [CrossRef]
  10. Budroni, G.; Corma, A. Gold–Organic–Inorganic High-Surface-Area Materials as Precursors of Highly Active Catalysts. Angew. Chem. Int. Ed. 2006, 45, 3328–3331. [Google Scholar] [CrossRef]
  11. Choi, Y.-J.; Park, H.-H.; Golledge, S.; Johnson, D.C. A study on the incorporation of ZnO nanoparticles into MEH-PPV based organic–inorganic hybrid solar cells. Ceram. Int. 2012, 38, S525–S528. [Google Scholar] [CrossRef]
  12. Gómez-Romero, P.; Ayyad, O.; Suárez-Guevara, J.; Muñoz-Rojas, D. Hybrid organic–inorganic materials: From child’s play to energy applications. J. Solid State Electrochem. 2010, 14, 1939–1945. [Google Scholar] [CrossRef]
  13. Fu, H.; Jiang, C.; Luo, C.; Lin, H.; Peng, H. A Quasi-Two-Dimensional Copper Based Organic-Inorganic Hybrid Perovskite with Reversible Thermochromism and Ferromagnetism. Eur. J. Inorg. Chem. 2021, 2021, 4984–4989. [Google Scholar] [CrossRef]
  14. Cai, P.; Wang, S.; Xu, T.; Tang, Y.; Yuan, X.; Wan, M.; Ai, Q.; Si, J.; Yao, X.; Cao, Y.; et al. Mn4+ doped zero-dimensional organic-inorganic hybrid material with narrow-red emission. J. Lumin. 2020, 228, 117661. [Google Scholar] [CrossRef]
  15. Wang, G.-E.; Sun, C.; Wang, M.-S.; Guo, G.-C. Semiconducting crystalline inorganic–organic hybrid metal halide nanochains. Nanoscale 2020, 12, 4771–4789. [Google Scholar] [CrossRef] [PubMed]
  16. Zhou, B.; Chi, Q.; Dong, Y.; Liu, L.; Zhang, Y.; Chang, L.; Pan, Y.; He, A.; Li, J.; Wang, X. Effects of annealing on the magnetic properties of Fe-based amorphous powder cores with inorganic-organic hybrid insulating layer. J. Magn. Magn. Mater. 2020, 494, 165827. [Google Scholar] [CrossRef]
  17. Zhao, H.; Fu, H.; Hu, Z.; Fu, Q.; Tao, H.; Weng, J.; Xiong, L.; Cheng, Z. Magnetic hybrid organic–inorganic perovskite (CH3NH3)2XCl4 (X = Mn, Cu, Co) crystals. CrystEngComm 2021, 23, 5208–5213. [Google Scholar] [CrossRef]
  18. Liu, D.-D.; Chen, Y.-G. Coordination polymers of lanthanide elements and metatungstate: Syntheses, structure and magnetic property. Inorg. Chim. Acta 2013, 401, 70–75. [Google Scholar] [CrossRef]
  19. Lin, S.; Zhang, X.; Luo, M. A novel inorganic–organic hybrid compound constructed from copper(II)-monosubstituted polyoxometalates and poly(amidoamine). J. Solid State Electrochem. 2008, 13, 1585–1589. [Google Scholar] [CrossRef]
  20. Vasylyev, M.V.; Gatard, S.; Bar-Nahum, I.; Konstantinovski, L.; Wachtel, E.J.; Neumann, R. Synthesis and Characterization of Polyoxometalate–Polyamino Dendritic Hybrid Compounds. J. Clust. Sci. 2006, 17, 235–243. [Google Scholar] [CrossRef]
  21. Li, H.; Zheng, Z.; Cao, M.; Cao, R. Stable gold nanoparticle encapsulated in silica-dendrimers organic–inorganic hybrid composite as recyclable catalyst for oxidation of alcohol. Microporous Mesoporous Mater. 2010, 136, 42–49. [Google Scholar] [CrossRef]
  22. Naka, K.; Chujo, Y. Effect of anionic dendrimers on the crystallization of calcium carbonate in aqueous solution. Comptes Rendus. Chim. 2003, 6, 1193–1200. [Google Scholar] [CrossRef]
  23. Gil, M.; Kim, H.; Bae, J.; Cha, S.-H.; Lee, K.J. Preparation of metal-ion containing polymers: Synthesis and characterization of methacryliccopolymers containing copper ion. Polymer 2015, 77, 297–304. [Google Scholar] [CrossRef]
  24. Zhang, R.-C.; Sun, D.; Zhang, R.; Lin, W.-F.; Macias-Montero, M.; Patel, J.; Askari, S.; McDonald, C.; Mariotti, D.; Maguire, P. Gold nanoparticle-polymer nanocomposites synthesized by room temperature atmospheric pressure plasma and their potential for fuel cell electrocatalytic application. Sci. Rep. 2017, 7, 46682. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  25. Tolstov, A.L. Preparation, Structure, and Properties of Hybrid Polymer Composites Containing Silver Clusters and Nanoparticles. Theor. Exp. Chem. 2015, 51, 74–95. [Google Scholar] [CrossRef]
  26. Sharon, M.; Nandgavkar, I.; Sharon, M. Platinum nanocomposites and its applications: A review. Adv. Mater. Res. 2017, 2, 129–153. [Google Scholar]
  27. Negm, N.A.; Hefni, H.; Abd-Elaal, A.A.; Badr, E.A.; Kana, M.T.A. Advancement on modification of chitosan biopolymer and its potential applications. Int. J. Biol. Macromol. 2020, 152, 681–702. [Google Scholar] [CrossRef] [PubMed]
  28. Verma, M.L.; Kumar, S.; Das, A.; Randhawa, J.S.; Chamundeeswari, M. Chitin and chitosan-based support materials for enzyme immobilization and biotechnological applications. Environ. Chem. Lett. 2019, 18, 315–323. [Google Scholar] [CrossRef]
  29. Wang, X.; Du, Y.; Fan, L.; Liu, H.; Hu, Y. Chitosan- metal complexes as antimicrobial agent: Synthesis, characterization and Structure-activity study. Polym. Bull. 2005, 55, 105–113. [Google Scholar] [CrossRef]
  30. Di Carlo, G.; Curulli, A.; Toro, R.G.; Bianchini, C.; De Caro, T.; Padeletti, G.; Zane, D.; Ingo, G.M. Green Synthesis of Gold–Chitosan Nanocomposites for Caffeic Acid Sensing. Langmuir 2012, 28, 5471–5479. [Google Scholar] [CrossRef]
  31. Ngah, W.W.; Fatinathan, S. Chitosan flakes and chitosan–GLA beads for adsorption of p-nitrophenol in aqueous solution. Colloids Surf. A Physicochem. Eng. Asp. 2006, 277, 214–222. [Google Scholar] [CrossRef]
  32. Geçer, A.; Yıldız, N.; Çalımlı, A.; Turan, B. Trimethyl chitosan nanoparticles enhances dissolution of the poorly water soluble drug Candesartan-Cilexetil. Macromol. Res. 2010, 18, 986–991. [Google Scholar] [CrossRef]
  33. Xu, X.; Liu, P.; Li, S.-H.; Zhang, P.; Wang, X.-Y. Chitosan-supported imine palladacycle complex and its catalytic performance for heck reaction. React. Kinet. Catal. Lett. 2006, 88, 217–223. [Google Scholar] [CrossRef]
  34. Francis, A.O.; Zaini, M.A.A.; Muhammad, I.M.; Abdulsalam, S.; El-Nafaty, U.A. Physicochemical modification of chitosan adsorbent: A perspective. Biomass Convers. Biorefinery 2021. [Google Scholar] [CrossRef]
  35. Mourya, V.; Inamdar, N.N. Chitosan-modifications and applications: Opportunities galore. React. Funct. Polym. 2008, 68, 1013–1051. [Google Scholar] [CrossRef]
  36. Cárdenas-Triviño, G.; Cruzat-Contreras, C. Study of Aggregation of Gold Nanoparticles in Chitosan. J. Clust. Sci. 2018, 29, 1081–1088. [Google Scholar] [CrossRef] [Green Version]
  37. Keshipour, S.; Mirmasoudi, S.S. Cross-linked chitosan aerogel modified with Au: Synthesis, characterization and catalytic application. Carbohydr. Polym. 2018, 196, 494–500. [Google Scholar] [CrossRef] [PubMed]
  38. Zahedifar, M.; Es-Haghi, A.; Zhiani, R.; Sadeghzadeh, S.M. Synthesis of benzimidazolones by immobilized gold nanoparticles on chitosan extracted from shrimp shells supported on fibrous phosphosilicate. RSC Adv. 2019, 9, 6494–6501. [Google Scholar] [CrossRef] [Green Version]
  39. Khan, S.A.; Bakhsh, E.M.; Asiri, A.M.; Khan, S.B. Synthesis of zero-valent Au nanoparticles on chitosan coated NiAl layered double hydroxide microspheres for the discoloration of dyes in aqueous medium. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 2020, 250, 119370. [Google Scholar] [CrossRef] [PubMed]
  40. da Silva, A.B.; Rufato, K.B.; de Oliveira, A.C.; Souza, P.R.; da Silva, E.P.; Muniz, E.C.; Vilsinski, B.H.; Martins, A.F. Composite materials based on chitosan/gold nanoparticles: From synthesis to biomedical applications. Int. J. Biol. Macromol. 2020, 161, 977–998. [Google Scholar] [CrossRef]
  41. Jadoun, S.; Arif, R.; Jangid, N.K.; Meena, R.K. Green synthesis of nanoparticles using plant extracts: A review. Environ. Chem. Lett. 2020, 19, 355–374. [Google Scholar] [CrossRef]
  42. Nadeem, M.; Abbasi, B.H.; Younas, M.; Ahmad, W.; Khan, T. A review of the green syntheses and anti-microbial applications of gold nanoparticles. Green Chem. Lett. Rev. 2017, 10, 216–227. [Google Scholar] [CrossRef] [Green Version]
  43. Dwivedi, A.D.; Gopal, K. Biosynthesis of silver and gold nanoparticles using Chenopodium album leaf extract. Colloids Surf. A Physicochem. Eng. Asp. 2010, 369, 27–33. [Google Scholar] [CrossRef]
  44. Annamalai, A.; Christina, V.; Sudha, D.; Kalpana, M.; Lakshmi, P. Green synthesis, characterization and antimicrobial activity of Au NPs using Euphorbia hirta L. leaf extract. Colloids Surf. B Biointerfaces 2013, 108, 60–65. [Google Scholar] [CrossRef] [PubMed]
  45. Mukundan, D.; Mohankumar, R.; Vasanthakumari, R. Comparative study of synthesized silver and gold nanoparticles using leaves extract of Bauhinia tomentosa Linn and their anticancer efficacy. Bull. Mater. Sci. 2017, 40, 335–344. [Google Scholar] [CrossRef]
  46. Hamed, A.I. New steroids from Solenostemma argel leaves. Fitoterapia 2001, 72, 747–755. [Google Scholar] [CrossRef]
  47. El-Shiekh, R.; Al-Mahdy, D.; Hifnawy, M.; Abdel-Sattar, E. In-vitro screening of selected traditional medicinal plants for their anti-obesity and anti-oxidant activities. S. Afr. J. Bot. 2019, 123, 43–50. [Google Scholar] [CrossRef]
  48. El-Zayat, M.M.; Eraqi, M.M.; Alfaiz, F.A.; Elshaer, M.M. Antibacterial and antioxidant potential of some Egyptian medicinal plants used in traditional medicine. J. King Saud Univ.-Sci. 2021, 33, 101466. [Google Scholar] [CrossRef]
  49. Plaza, A.; Perrone, A.; Balestrieri, C.; Balestrieri, M.L.; Bifulco, G.; Carbone, V.; Hamed, A.; Pizza, C.; Piacente, S. New antiproliferative 14,15-secopregnane glycosides from Solenostemma argel. Tetrahedron 2005, 61, 7470–7480. [Google Scholar] [CrossRef]
  50. Adel, R.; Saty, A.; Yousof, S.; Alhuseen, O.; Mohammed, H.; Alamin, A. Phytochemical Screening of Solenostemma argel & Extraction & Separation of Its Flavonoid. Ph.D. Thesis, Sudan University of Science and Technology, Khartoum State, Sudan, 2016. [Google Scholar]
  51. Pinto, R.V.; Gomes, P.S.; Fernandes, M.H.; Costa, M.E.; Almeida, M. Glutaraldehyde-crosslinking chitosan scaffolds reinforced with calcium phosphate spray-dried granules for bone tissue applications. Mater. Sci. Eng. C 2019, 109, 110557. [Google Scholar] [CrossRef] [PubMed]
  52. Li, B.; Shan, C.-L.; Zhou, Q.; Fang, Y.; Wang, Y.-L.; Xu, F.; Han, L.-R.; Ibrahim, M.; Guo, L.-B.; Xie, G.-L.; et al. Synthesis, Characterization, and Antibacterial Activity of Cross-Linked Chitosan-Glutaraldehyde. Mar. Drugs 2013, 11, 1534–1552. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  53. Sun, L.; Pu, S.; Li, J.; Cai, J.; Zhou, B.; Ren, G.; Ma, Q.; Zhong, L. Size controllable one step synthesis of gold nanoparticles using carboxymethyl chitosan. Int. J. Biol. Macromol. 2018, 122, 770–783. [Google Scholar] [CrossRef]
  54. Da’Na, E.; Sayari, A. Optimization of copper removal efficiency by adsorption on amine-modified SBA-15: Experimental design methodology. Chem. Eng. J. 2011, 167, 91–98. [Google Scholar] [CrossRef]
  55. Huang, J.; Li, Q.; Sun, D.; Lu, Y.; Su, Y.; Yang, X.; Wang, H.; Wang, Y.; Shao, W.; He, N.; et al. Biosynthesis of silver and gold nanoparticles by novel sundried Cinnamomum camphora leaf. Nanotechnology 2007, 18, 105104. [Google Scholar] [CrossRef]
  56. Sugunan, A.; Thanachayanont, C.; Dutta, J.; Hilborn, J. Heavy-metal ion sensors using chitosan-capped gold nanoparticles. Sci. Technol. Adv. Mater. 2005, 6, 335–340. [Google Scholar] [CrossRef]
  57. Luo, W.; Bai, Z.; Zhu, Y. Fast removal of Co(ii) from aqueous solution using porous carboxymethyl chitosan beads and its adsorption mechanism. RSC Adv. 2018, 8, 13370–13387. [Google Scholar] [CrossRef] [Green Version]
Polymers 14 00766 g001 550
Figure 1. FT-IR of (a) chitosan flakes, (b) chitosan-GLA beads, and (c) chitosan-GLA/AuNPs beads.
Figure 1. FT-IR of (a) chitosan flakes, (b) chitosan-GLA beads, and (c) chitosan-GLA/AuNPs beads.
Polymers 14 00766 g001
Polymers 14 00766 g002 550
Figure 2. UV–vis absorption spectra of chitosan flakes and chitosan-GLA/AuNPs beads prepared with an aqueous solution of S. argel leaf extract.
Figure 2. UV–vis absorption spectra of chitosan flakes and chitosan-GLA/AuNPs beads prepared with an aqueous solution of S. argel leaf extract.
Polymers 14 00766 g002
Polymers 14 00766 g003 550
Figure 3. XRD patterns of (a) chitosan flakes, (b) chitosan-GLA, and (c) chitosan-GLA/AuNPs beads.
Figure 3. XRD patterns of (a) chitosan flakes, (b) chitosan-GLA, and (c) chitosan-GLA/AuNPs beads.
Polymers 14 00766 g003
Polymers 14 00766 g004a 550Polymers 14 00766 g004b 550Polymers 14 00766 g004c 550
Figure 4. FESEM images (a,b) and EDS (c,d) of chitosan-GLA and chitosan-GLA/AuNPs beads, respectively.
Figure 4. FESEM images (a,b) and EDS (c,d) of chitosan-GLA and chitosan-GLA/AuNPs beads, respectively.
Polymers 14 00766 g004aPolymers 14 00766 g004bPolymers 14 00766 g004c
Polymers 14 00766 g005 550
Figure 5. TGA thermograms of chitosan, chitosan-GLA, and chitosan-GLA/AuNPs composites.
Figure 5. TGA thermograms of chitosan, chitosan-GLA, and chitosan-GLA/AuNPs composites.
Polymers 14 00766 g005
Polymers 14 00766 g006a 550Polymers 14 00766 g006b 550Polymers 14 00766 g006c 550
Figure 6. HRTEM images of chitosan-GLA/AuNPs nanocomposite (a); the lattice fringes in the (1 1 1) plane of the particles and measured lattice d-spacing (b); TEM image of AuNPs prepared with S. argel leaf extract without using cross-linked chitosan (c); TEM image of AuNPs prepared with S. argel leaf extract using cross-linked chitosan (d); and the particle size distributions of AuNPs within the chitosan-GLA/AuNPs nanocomposite (e).
Figure 6. HRTEM images of chitosan-GLA/AuNPs nanocomposite (a); the lattice fringes in the (1 1 1) plane of the particles and measured lattice d-spacing (b); TEM image of AuNPs prepared with S. argel leaf extract without using cross-linked chitosan (c); TEM image of AuNPs prepared with S. argel leaf extract using cross-linked chitosan (d); and the particle size distributions of AuNPs within the chitosan-GLA/AuNPs nanocomposite (e).
Polymers 14 00766 g006aPolymers 14 00766 g006bPolymers 14 00766 g006c
Table
Table 1. Elemental analysis of chitosan flakes and modified chitosan with GLA, Au3+, and AuNPs.
Table 1. Elemental analysis of chitosan flakes and modified chitosan with GLA, Au3+, and AuNPs.
EntrySamples Elements
C%%H%NAu
% atommmol g−1
1Chitosan 40.917.547.80--
2Chitosan-GLA 43.587.816.95--
3Chitosan-GLA/Au3+51.598.815.522.0330.103
4Chitosan-GLA/AuNPs51.638.835.502.0240.102
Table
Table 2. BET specific surface area, degree of crystallinity, and the catalytic oxidation of benzyl alcohol with H2O2 in the presence of various compounds.
Table 2. BET specific surface area, degree of crystallinity, and the catalytic oxidation of benzyl alcohol with H2O2 in the presence of various compounds.
EntryCatalystBET (m2g−1)Crystallinity (%)Conversion % a
1chitosan-GLA/AuNPs beads4.9064.2197.5
2No catalyst--10.0
3S. argel leaf extract--12.8
4chitosan flakes3.2562.034.3
5chitosan-GLA beads4.7363.1814.9
6chitosan-GLA/Au3+ beads--42.3
7chitosan-GLA/AuNPs beads 95.1 b
8chitosan-GLA/AuNPs beads 91.3 c
9chitosan-GLA/AuNPs beads 70.0 d
a Determined by GC. b–d 2nd, 3rd, and 4th run, respectively.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Taha, A.; Da’na, E. Phyto-Assisted Assembly of Metal Nanoparticles in Chitosan Matrix Using S. argel Leaf Extract and Its Application for Catalytic Oxidation of Benzyl Alcohol. Polymers 2022, 14, 766. https://doi.org/10.3390/polym14040766

AMA Style

Taha A, Da’na E. Phyto-Assisted Assembly of Metal Nanoparticles in Chitosan Matrix Using S. argel Leaf Extract and Its Application for Catalytic Oxidation of Benzyl Alcohol. Polymers. 2022; 14(4):766. https://doi.org/10.3390/polym14040766

Chicago/Turabian Style

Taha, Amel, and Enshirah Da’na. 2022. "Phyto-Assisted Assembly of Metal Nanoparticles in Chitosan Matrix Using S. argel Leaf Extract and Its Application for Catalytic Oxidation of Benzyl Alcohol" Polymers 14, no. 4: 766. https://doi.org/10.3390/polym14040766

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop