Next Article in Journal
Fabrication and Characteristics of PCL Membranes Containing Strontium-Substituted Hydroxyapatite Nanofibers for Guided Bone Regeneration
Next Article in Special Issue
Magnetite Nanoparticles Coated with PEG 3350-Tween 80: In Vitro Characterization Using Primary Cell Cultures
Previous Article in Journal
Electrohydrodynamic-Jet (EHD)-Printed Diketopyrrolopyroole-Based Copolymer for OFETs and Circuit Applications
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Polymers
Volume 11
Issue 11
10.3390/polym11111760
polymers-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Non-Chloride in Situ Preparation of Nano-Cuprous Oxide and Its Effect on Heat Resistance and Combustion Properties of Calcium Alginate

by
Peiyuan Shao
1,
Peng Xu
1,
Lei Zhang
1,2,
Yun Xue
1,
Xihui Zhao
1,
Zichao Li
1,2,* and
Qun Li
1,3,*
1
College of Chemistry and Chemical Engineering, Qingdao University, Qingdao 266071, China
2
College of Life Sciences, Institute of Advanced Cross-Field Science, Qingdao University, Qingdao 266071, China
3
Shandong Collaborative Innovation Center of Marine Biobased Fibers and Ecological Textiles, Qingdao University, Qingdao 266071, China
*
Authors to whom correspondence should be addressed.
Polymers 2019, 11(11), 1760; https://doi.org/10.3390/polym11111760
Submission received: 11 October 2019 / Revised: 22 October 2019 / Accepted: 24 October 2019 / Published: 27 October 2019
(This article belongs to the Special Issue Metal Nanoparticles-Polymer Hybrid Materials)
Browse Figures
Versions Notes

Abstract

:
With Cu2+ complexes as precursors, nano-cuprous oxide was prepared on a sodium alginate template excluded of Cl− and based on which the calcium alginate/nano-cuprous oxide hybrid materials were prepared by a Ca2+ crosslinking and freeze-drying process. The thermal degradation and combustion behavior of the materials were studied by related characterization techniques using pure calcium alginate as a comparison. The results show that the weight loss rate, heat release rate, peak heat release rate, total heat release rate and specific extinction area of the hybrid materials were remarkably lower than pure calcium alginate, and the flame-retardant performance was significantly improved. The experimental data indicates that nano-cuprous oxide formed a dense protective layer of copper oxide, calcium carbonate and carbon by lowering the initial degradation temperature of the polysaccharide chain during thermal degradation and catalytically dehydrating to char in the combustion process, and thereby can isolate combustible gases, increase carbon residual rates, and notably reduce heat release and smoke evacuation.

Graphical Abstract

1. Introduction

Nano-cuprous oxide is a typical p-type semiconductor material with active electron holes, which exhibits effective catalytic activity, strong adsorption and low-temperature paramagnetic properties [1]. It has potential applications in organic synthesis, photoelectric conversion, new energy, water decomposition, sterilization, superconductivity, and others, and has become one of the most widely studied inorganic nanomaterials in the past decade [2,3,4,5,6,7,8,9,10].
Due to their low cost and sustainability, marine biomaterials from renewable resources have attracted attention today as fossil energy is depleting. Alginate is a linear, binary-block copolymer with special structures and properties [11,12]. It has served as a template for the preparation of new functional hybrid materials in recent years [13,14,15,16,17]. In particular, sodium alginate can form a strong and stable “egg box” model (Figure 1) [12,18,19] structure of water-insoluble materials by crosslinking with divalent or trivalent metal ions, which is not only widely used in food and medicine [20,21,22], but also as an eco-friendly flame-retardant material [23,24,25,26,27].
It is well known that the goal of developing hybrid materials is to improve the functionality of the hybrid material by creating a synergistic effect through the interaction between two phases [13,28,29,30], and the flame-retardant properties of the inherently flame-retardant calcium alginate can be further improved by adding inorganic nanoparticles [31,32,33,34,35]. In order to overcome the defects caused by the agglomeration of inorganic nanoparticles due to the mechanical addition method [34], previous research on preparing calcium alginate-based hybrid materials by in situ methods have been reported [31,32,33]. Herein, a new multifunctional material employing nano-cuprous oxide to improve the antibacterial and catalytic properties of calcium alginate is presented. However, to the best of our knowledge, no such report has been well documented so far. Note that copper alginate shows no flame retardancy [36]; thus, the effect of nano-cuprous oxide on the flame-retardant properties of calcium alginate is worth exploring.
Generally, calcium chloride has been used as a crosslinking agent to prepare calcium alginate. However, since copper ions, cuprous ions, and chloride ions have complicated chemical reactions, it is difficult to prepare calcium alginate/nano-cuprous oxide hybrid materials by such a method based on the attempts in our laboratory for over a year. Therefore, we propose a novel “non-chlorine in situ” preparation method, aiming for the facile preparation of calcium alginate/nano-cuprous oxide hybrid materials by the in situ method in the absence of chloride ions. Our study found an improved limiting oxygen index of 54.0 for the hybrid material compared to pure calcium alginate. Although the role of inorganic nanoparticles in hybrid material has been reported so far, there has been no literature on the effects of nano-cuprous oxide on the flame-retardant properties of calcium alginate or its mechanism. The results here show that the peak heat release rate of calcium alginate can be reduced by 15% with only 1 wt % nano-cuprous oxide addition, and the flame-retardant mechanism was slightly different from the traditional mechanism [5,7]. In summary, the calcium alginate/nano-cuprous oxide hybrid materials prepared by the “non-chlorine in situ” method is a multi-functional material with important potential applications and flame-retardant, antibacterial, and catalytic properties. The effect and mechanism of cuprous oxide on the material is essential to the design of the material.

2. Materials and Methods

2.1. Materials

Sodium alginate (NaAlg) was purchased from the Guangfu Fine Chemical Research Institute (Tianjin, China). Pentahydrate copper sulfate (CuSO4·5H2O) was obtained from the Guangcheng Chemical Reagent Co., Ltd. (Tianjin, China). Both ammonia water (NH3·H2O) and sodium hydroxide (NaOH) were supplied by the fine chemical plant of the Laiyang Economic and Technological Development Zone (Yantai, China). Calcium acetate and ascorbic acid were purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). All the chemicals were of analytical grade and not further purified, and all the solutions were prepared using deionized water.

2.2. Preparation of Nano-Cu2O In Situ

The preparation process of the nano-Cu2O is shown schematically in Scheme 1. CuSO4·5H2O (3.9 g) was dissolved in a predetermined amount of deionized water, followed by the addition of 13 mL NH3·H2O (12 mol/L). Then, 20 g of NaAlg was added and the whole volume of the mixture solution was maintained at 500 mL. The solution was heated at a constant temperature of 55 °C for 6 h until a uniform and stable blue solution was formed. Subsequently, 11.4 g of ascorbic acid was added into the solution and was slowly stirred until the color entirely changed to yellow. Consequently, the nano-Cu2O was prepared on the NaAlg template.

2.3. Preparation of Calcium Alginate/Nano-Cuprous Oxide Hybrid Materials

NaOH (1 mol/L) was slowly dropped into the 3 wt % calcium acetate solution (2 L) until the pH reached 10. The as-prepared solution containing 4 wt % NaAlg was poured into molds of various shapes and then placed in the calcium acetate solution for 24 h, obtaining the crosslinked hybrid material (CaAlg/nano-Cu2O). Finally, the product was washed several times with deionized water and dried in a freeze-dryer for 24 h. It is found by calculation that the content of Cu2O in the hybrid material prepared by the in situ method was equivalent to the mechanical process of adding of 1 wt % Cu2O. As a comparison, pure calcium alginate (CaAlg) was prepared in a similar procedure only without the addition of the reagents related to the preparation of Cu2O.

2.4. Measurements and Characterizations

For the characterization of the calcined residue, the samples were heated to a target temperature (250, 450, and 750 °C) at a heating rate of 5 °C/min in air, and then kept for 2 h.

2.4.1. Density

The quality and dimension of CaAlg and CaAlg/nano-Cu2O hybrid material were measured using an electronic balance (PL303 Precision Balance, Mettler-Toledo, Tokyo, Japan) and digital calipers, and then the densities were calculated based on the data.

2.4.2. X-ray Diffraction (XRD)

An X-ray diffractometer (Ultima IV, Rigaku, Tokyo, Japan) was employed to investigate the samples and calcined residue under Cu Kα radiation (λ = 0.15418 nm), with a scan rate (2θ) of 5°/min in an angular range of 15–80 in continuous mode (operating voltage: 40 kV, current: 30 mA).

2.4.3. Field Emission Scanning Electron Microscopy (FESEM)

The morphology and microstructure of the materials and their calcined residues were observed by a field emission scanning electron microscope (Sigma 500/VP, Carl Zeiss AG, Jena, Germany) at a beam voltage of 10 kV. Prior to SEM imaging, all the sample surfaces were sprayed with thin layers of gold to avoid charging under the electron beam. The distribution of Cu on the surface of the CaAlg/nano-Cu2O hybrid material was plotted using an energy dispersive X-ray spectrometer (EDX) attachment.

2.4.4. Synchronous Thermal Analyzer (STA)

A synchronous thermal analyzer (TGA/DSC1 1600, Mettler Toledo, Columbus, OH, USA) was employed to analyze the materials under a nitrogen atmosphere. Samples of 4–6 mg were placed in an aluminum crucible and heated from room temperature to 1000 °C at a heating rate of 10 °C/min and a gas flow rate of 50 mL/min.

2.4.5. Cone Calorimeter (CONE)

The combustion behavior of the samples was studied with a cone calorimeter (FTT-0007, Fire Testing Technology, East Grinstead, UK) under an external heat flux of 50 kW/m2 with horizontal orientation in air according to standard ISO 5660-1. The dimensions of all the samples were 100 mm × 100 mm × 8 mm.

2.4.6. Limiting Oxygen Index (LOI)

The LOI values were determined using a M606B type instrument (Shanfang Instrument Co., Ltd., Qingdao, China). Samples of dimensions 80 mm × 10 mm × 8 mm were used for all the tests while CaAlg/nano-Cu2O was compressed to ensure that it was substantially the same quality as CaAlg. The samples were placed in a standard laboratory, at a temperature of 23 ± 2 °C and a relative humidity of 50 ± 5%, for at least 24 h before testing.

2.4.7. Vertical Burning (UL-94)

Vertical burning tests were performed on a CZF-2 test instrument (Jiangning Analytical Instrument Factory, Nanjing, China) according to the standard American Society for Testing and Materials (ASTM) D3801. The size of both samples was 130 mm × 13 mm × 8 mm.

2.4.8. Microscale Combustion Calorimeter (MCC)

A microscale combustion calorimeter (MCC-2, Govmark, Farmingdale, NY, USA) was used to investigate the flammability behavior of the test samples. Samples of 5 ± 0.05 mg were heated from room temperature to 750 °C (heating rate of 1 °C/s) in a stream of nitrogen flowing at 80 cm3/min. Before entering a 900 °C combustion furnace, the thermal degradation products were mixed with a 20 cm3/min steam, consisting of 20% oxygen and 80% nitrogen.

3. Results and Discussion

3.1. Morphology of Materials

In Figure 2a, the digital photo shows that the two materials exhibited similar porous structures with notably different colors. The difference in color can be attributed to the fact that nano-Cu2O changed the optical properties of the material itself, which was dependent on the structure, size, and dispersion of the particles [13]. The freeze-drying condensed the moisture in the material into ice, and the “ice matrix” left after the sublimation of the ice was the essence of its macroscopic appearance as a porous structure [37,38].
The two materials were analyzed by XRD and the results are shown in Figure 2b. Comparing the obtained diffraction peak with the pure phase Cu2O (cuprite, JCPDS-#99-0041), it was found that the four peaks with different diffraction values of two materials (at 36.4°, 42.3°, 61.4° and 73.5°) were identical with the crystal planes of Cu2O at (111), (200), (220), and (311), respectively. This confirms the existence of Cu2O and also the formation of hybrid materials.
It is noteworthy that the density of CaAlg was 0.19 g/cm3 while that of CaAlg/nano-Cu2O hybrid material was only 0.08 g/cm3. FESEM was used to study the morphology of the two materials in order to explain the difference in density. The results of electron microscopic characterization are shown in Figure 3. It can be seen from the analysis and comparison of the SEM images that CaAlg showed a lamellar structure with a smooth, uniform surface and a few nodules. CaAlg/nano-Cu2O was a three-dimensional network structure, and some spherical Cu2O particles with an average diameter below 100 nm were adhered to the CaAlg framework interface through a strong interaction, while the others were embedded in the framework of CaAlg.
It can be noticed from the microstructure that there were differing densities between the two materials and the three-dimensional network structure clearly exhibited a relatively lower density. The formation of this type of structure is due to the fact that NaAlg itself is rich in hydroxyl and carboxyl groups and can form intermolecular hydrogen bonds with Cu2O in situ [39,40]. The continuous network structure formed at the same time affected the mass transfer process of the solid–liquid phases in subsequent crosslinking, which led to the presence of a similar three-dimensional network structure in the final hybrid materials. This structure can effectively prevent the movement of polymer molecular chains during combustion with a lower thermal conductivity, and thus can provide better thermal stability of the materials [11,41].

3.2. Thermal Stability

The thermal stability of CaAlg and CaAlg/nano-Cu2O was investigated by simultaneous thermal analysis (TG-DSC) and the comparison curves are displayed in Figure 4. The studied samples followed the same degradation trend and tended to be stable after three stages of decline. The decomposition process of CaAlg was similar to that of previous studies [31,42], and the three stages of its decomposition included: the desorption process of water at 50–140 °C, the thermal destruction of glycosidic bonds and the elimination process of adjacent hydroxyl groups at 240–400 °C; and a process took place in which the glycosidic bond was further destroyed to form an intermediate substance at 400–520 °C.
Comparing the two materials, the thermal stability of CaAlg/nano-Cu2O was obviously better than that of CaAlg, and the rate of weight loss was reduced by about 15%. In the desorption stage of water, the weight loss rate of CaAlg/nano-Cu2O was significantly lower than that of CaAlg, which can be attributed to the low thermal conductivity for the three-dimensional network structure of the hybrid material. As a biogenic polymer, CaAlg is rich in hydroxyl and carboxyl groups and can easily absorb water, while for hybrid materials, Cu2O can form multi-hydrogen bonds with the hydroxyl and carboxyl groups in CaAlg, so that the composites had a better thermal stability at low temperature.
As shown in Figure 4, more notable differences occurred at around 400 °C, in which CaAlg/nano-Cu2O was the first to re-decompose the glycosidic bonds at 360 °C, almost 40 °C less than CaAlg. This was mainly due to the fact that Cu2O in the hybrid material catalyzed the thermal decomposition of CaAlg and reduced the energy required for the reaction [43]. Comparing the DSC curves, it was found that although the decomposition reaction of CaAlg/nano-Cu2O proceeded in advance, the peak exotherm was significantly lower than that of CaAlg (namely 38.8%). The decrease in peak heat release indicated improvement in the thermal stability of the material.
In addition, there were two other noticeable observations in the curves shown in Figure 4. The slight weight loss of CaAlg/nano-Cu2O at 600 °C led to a weak change in the heat flux, which may be due to the decomposition of CaCO3 in the thermal cracking products of CaAlg catalyzed by CuO. It can be observed from the DSC curves that the two materials exhibited exothermic peaks at 700 °C without causing mass loss, which can be attributed to the phase transition process of the intermediate produced by the thermal decomposition of CaAlg at high temperature.
The XRD analysis of the calcined residue of the two prepared materials was carried out and the results are shown in Figure 5. It can be seen that CaAlg/nano-Cu2O showed a diffraction peak of Cu2O (cuprite, JCPDS-#99-0041) only in the calcination residue at 250 °C. However, in the calcination residue under the three temperature conditions, clear CuO (copper oxide, JCPDS-#89-5898) diffraction peaks can be observed, which were formed by the oxidation of Cu2O in the material. Except for Cu2O and CuO, the components of the calcined residue of the two materials were basically the same.
Among them, one category of product was CaCO3 of different crystal phases at 250 °C, including calcite (calcite, JCPDS-#99-0022), aragonite (aragonite, JCPDS-#71-2392) and vaterite (vaterite, JCPDS-#74-1867), while the product was at a single calcite phase of CaCO3 at 450 °C. With the decomposition of CaCO3 at 750 °C, not only CaCO3 but also CaO and Ca(OH)2 were generated.
Through the morphological study of the residue after calcination of the two materials, the stability of the materials was analyzed from a microscopic point of view. The relevant characterization results are shown in Figure 6.
As shown in Figure 6a, CaCO3 particles of different sizes were distributed on the surface of the CaAlg calcination residue at 250 °C. However, for CaAlg/nano-Cu2O, the framework of CaAlg collapsed as the temperature rose and Cu2O particles with a higher surface energy were rapidly deposited on the surface of the material, which was oxidized to CuO. As seen in Figure 6b, Cu2O catalyzed the decomposition reaction of the outer layer of CaAlg, in which the release of gas carried off most of the heat and the remaining solid residue formed a dense barrier on the outer layer. The formation of the barrier layer can prevent heat and combustible gas from diffusing into the internal layer [44], greatly reducing the heat release rate and significantly improving the flame retardancy.
It can be observed from Figure 6c that dense polyhedral particles covered the surface of the CaAlg calcination residue at 750 °C, demonstrating the flame-retardant properties of the material. However, the most obvious morphological change in the calcination residue of CaAlg/nano-Cu2O was the inflation of the residue particles [45], as displayed in Figure 6d, which directly formed denser particle distribution and smaller surface voids. This can further improve the flame retardancy of the material. The morphological difference was related to the carbonized layer formation of the CuO-promoted material at high temperature [11,28].

3.3. Combustion Behavior

The experimental data of cone calorimetry are listed in Table 1. As seen, the heat release rate (HRR), peak heat release rate (PHRR), and total heat of release (THR) of CaAlg/nano-Cu2O were significantly lower than those of CaAlg. However, the quality of the samples used in this test was quite different due to the various structures, making the comparison of data inconclusive. At present, there is no known study on the influence of sample differences on cone calorimetry data and the degree of the relevant influence. Thus, the subsequent data were reanalyzed using an MCC experiment.
There are two quality-independent parameters in the CONE test—effective heat of combustion (EHC) and mean specific extinction area (mean SEA)—which are reliable results worthy of attention. EHC represents the ratio of HRR to mass loss rate, reflecting the degree of combustion of volatile gases in the gas phase flame. By comparison, it can be found that CaAlg/nano-Cu2O had a lower EHC value than that of CaAlg, indicating that the overall response of the former was lower than that of the latter, which indirectly proved that the hybrid material had better thermal stability. SEA is defined as the ability of a sample to decompose volatiles produced by flammable masses of combustibles. By comparing the mean SEA of the two materials, it can be clearly seen that CaAlg/nano-Cu2O exhibited better prominent smoke suppression ability than CaAlg.
Table 2 shows the results of the LOI and UL-94 tests for the two materials. In the UL-94 test, both materials were classified as V-0 based on the fact that both of them exhibited smoldering and maintained their original shape without melt dripping. For the limiting oxygen experiment, the materials are considered to be flame retardant when the LOI value surpasses 27.0. The LOI value of CaAlg was 49.2, which can be already recognized as well flame-retardant. Comparatively, the LOI value of CaAlg/nano-Cu2O reached 54.0, reflecting a successful improvement by introducing the nano-Cu2O particles to CaAlg.
MCC, also known as pyrolysis combustion flow calorimetry, is a standard ASTM test method (ASTM 7309) for the analysis of solid materials. It can dynamically measure the HRR and other relevant data based on the oxygen consumed during the experiment [24]. The material can be tested and analyzed at milligram sizes, which can effectively avoid the influence caused by differences in sample preparation [46].
As seen in Table 2, the MCC results are consistent with the phenomenon of the flame experiments. CaAlg had a HRC of 18 J/g/K, a PHRR of 16.19 W/g, and a THR of 4.3 kJ/g, all of which were at lower levels. The fabrication of CaAlg/nano-Cu2O further improved the flame retardancy of CaAlg, and the values of several parameters declined, especially for the PHRR, which was decreased by nearly 15%. At the same time, the 5% increase in residual carbon confirmed the effect of the nanoparticles on the catalytic carbon formation of CaAlg/nano-Cu2O as well. It is clear that nano-Cu2O showed positive influence on the flame retardancy of the hybrid materials.

3.4. Flame-Retardant Mechanism

Scheme 2 shows the flame-retardant mechanism of nano-Cu2O on the CaAlg/nano-Cu2O hybrid material in detail. Due to the presence of inorganic nanoparticles, the hybrid materials formed a three-dimensional network structure with low thermal conductivity, which showed superior thermal stability at the initial stage of combustion.
At 40–400 °C, the skeleton of CaAlg gradually collapsed and disintegrated with the increase of temperature. The nano-Cu2O attached to the skeleton had a high surface energy and rapidly migrated and deposited on the surface of CaAlg/nano-Cu2O. Since Cu2O catalyzed the thermal decomposition reaction of CaAlg, the outermost CaAlg is the first to be decomposed at a relatively low temperature. Vapor and CO2 generated by dehydration and decarboxylation in the CaAlg thermal decomposition process carried away most of the heat, while the remaining solid residue, including CuO oxidized from Cu2O, formed a dense carbon barrier in the outermost layer of CaAlg/nano-Cu2O. The barrier layer prevented heat and flammable gas from diffusing into the inner layer, while the release of the incombustible gas lowered the concentration of the flammable gas at both the inner and outer contact surfaces, suppressing the overall thermal decomposition reaction to a lower degree and greatly reducing the HRR.
Above 400 °C, the thermal decomposition product CaCO3 began to shift to CaO. As the temperature increased further, char formation began. At this time, the CuO in the calcination residue of CaAlg/nano-Cu2O became a catalyst for the char formation reaction. A large amount of the carbonaceous carbon produced was coated on the surface of CaAlg/nano-Cu2O and appeared to be an expansion of the calcination residue. It promoted a denser barrier layer and a narrower surface void that both shielded the diffusion of flammable gases and blocked heat and heat radiation. The heat feedback of the material was reduced, and thereby the progress of the combustion reaction was suppressed. This further improved the flame retardancy of the hybrid materials.

4. Conclusions

In this study, nano-cuprous oxide was prepared by employing Cu2+ complexes as precursors via a non-chloride in situ method rather than the widely used direct crosslinking of the sodium alginate solution template. Then, the composites based on the calcium alginate/cuprous oxide nanoparticles were fabricated by a simple green crosslinking and freeze-drying process. Measurements and characterizations show that CaAlg/nano-Cu2O displayed a completely different three-dimensional network structure from CaAlg, with a LOI value up to 54.0. The addition of a mere 1 wt % nano-Cu2O reduced the PHHR by 15% and increased the residual carbon rate by 5%, which contributed to the improvement for the flame retardancy of CaAlg/nano-Cu2O. Moreover, it can be inferred from the supposed working and flame-retardant mechanism of nano-Cu2O on CaAlg that the carbon layer that formed at low temperature due to catalysis protected the internal material, reduced the HRR, THR, PHRR and EHC, and suppressed the release of smoke of the hybrid materials. The char formation was reinforced by CuO catalysis to reduce combustion performance and improve the flame-retardant properties of the material. CaAlg/nano-Cu2O not only has potential development prospects in the field of antibacterial and catalytic materials, but also a green material with lower heat release and smoke release, and improved flame-retardant properties compared to CaAlg.

Author Contributions

Conceptualization, Z.L. and Q.L.; Data curation, P.S.; Investigation, P.S., P.X. and L.Z.; Resources, Y.X. and X.Z.; Writing—original draft, P.S.; Writing—review and editing, Z.L.

Funding

This work was supported by the National Natural Science Foundation of China (grant number 51773102).

Acknowledgments

The authors wish to thank Tingting Zhang from Biology Experimental Teaching Center of College of Life Sciences in Qingdao University for the use of some instruments and assistance with the measurements.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Sun, S.; Zhang, X.; Yang, Q.; Liang, S.; Zhang, X.; Yang, Z. Cuprous oxide (Cu2O) crystals with tailored architectures: A comprehensive review on synthesis, fundamental properties, functional modifications and applications. Prog. Mater. Sci. 2018, 96, 111–173. [Google Scholar] [CrossRef]
  2. Qiu, S.L.; Xing, W.Y.; Feng, X.M.; Yu, B.; Mu, X.W.; Yuen, R.K.K.; Hu, Y. Self-standing cuprous oxide nanoparticles on silica@polyphosphazene nanospheres: 3D nanostructure for enhancing the flame retardancy and toxic effluents elimination of epoxy resins via synergistic catalytic effect. Chem. Eng. J. 2017, 309, 802–814. [Google Scholar] [CrossRef]
  3. Aguilar, M.S.; Rosas, G. A new synthesis of Cu2O spherical particles for the degradation of methylene blue dye. Environ. Nanotechnol. Monit. Manag. 2019, 11, 100195. [Google Scholar] [CrossRef]
  4. Su, R.; Li, Q.; Chen, Y.; Gao, B.; Yue, Q.; Zhou, W. One-step synthesis of Cu2O@carbon nanocapsules composites using sodium alginate as template and characterization of their visible light photocatalytic properties. J. Clean. Prod. 2019, 209, 20–29. [Google Scholar] [CrossRef]
  5. Kumar, S.; Ojha, A.K.; Bhorolua, D.; Das, J.; Kumar, A.; Hazarika, A. Facile synthesis of CuO nanowires and Cu2O nanospheres grown on rGO surface and exploiting its photocatalytic, antibacterial and supercapacitive properties. Phys. B 2019, 558, 74–81. [Google Scholar] [CrossRef]
  6. Kociolek-Balawejder, E.; Stanislawska, E.; Dworniczek, E.; Seniuk, A.; Jacukowicz-Sobala, I.; Winiarska, K. Cu2O doped gel-type anion exchanger obtained by reduction of brochantite deposit and its antimicrobial activity. React. Funct. Polym. 2019, 141, 42–49. [Google Scholar] [CrossRef]
  7. Yang, Z.; Hao, X.; Chen, S.; Ma, Z.; Wang, W.; Wang, C.; Yue, L.; Sun, H.; Shao, Q.; Murugadoss, V.; et al. Long-term antibacterial stable reduced graphene oxide nanocomposites loaded with cuprous oxide nanoparticles. J. Colloid Interface Sci. 2019, 533, 13–23. [Google Scholar] [CrossRef]
  8. Wang, D.; Kan, Y.; Yu, X.; Liu, J.; Song, L.; Hu, Y. In situ loading ultra-small Cu2O nanoparticles on 2D hierarchical TiO2-graphene oxide dual-nanosheets: Towards reducing fire hazards of unsaturated polyester resin. J. Hazard. Mater. 2016, 320, 504–512. [Google Scholar] [CrossRef]
  9. Guo, Y.; Dai, M.M.; Zhu, Z.X.; Chen, Y.Q.; He, H.; Qin, T.H. Chitosan modified Cu2O nanoparticles with high catalytic activity for p-nitrophenol reduction. Appl. Surf. Sci. 2019, 480, 601–610. [Google Scholar] [CrossRef]
  10. Jing, G.J.; Zhang, X.J.; Zhang, A.A.; Li, M.; Zeng, S.H.; Xu, C.J.; Su, H.Q. CeO2-CuO/Cu2O/ Cu monolithic catalysts with three-kind morphologies Cu2O layers for preferential CO oxidation. Appl. Surf. Sci. 2018, 434, 445–451. [Google Scholar] [CrossRef]
  11. Shang, K.; Liao, W.; Wang, J.; Wang, Y.T.; Wang, Y.Z.; Schiraldi, D.A. Nonflammable alginate nanocomposite aerogels prepared by a simple freeze-drying and post-cross-linking method. ACS Appl. Mater. Interfaces 2016, 8, 643–650. [Google Scholar] [CrossRef] [PubMed]
  12. Lee, K.Y.; Mooney, D.J. Alginate: Properties and biomedical applications. Prog. Polym. Sci. 2012, 37, 106–126. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  13. Aime, C.; Coradin, T. Nanocomposites from biopolymer hydrogels: Blueprints for white biotechnology and green materials chemistry. J. Polym. Sci. Part B Polym. Phys. 2012, 50, 669–680. [Google Scholar] [CrossRef]
  14. Chen, H.B.; Shen, P.; Chen, M.J.; Zhao, H.B.; Schiraldi, D.A. Highly efficient flame retardant polyurethane foam with alginate/clay aerogel coating. ACS Appl. Mater. Interfaces 2016, 8, 32557–32564. [Google Scholar] [CrossRef]
  15. Safaei, M.; Taran, M.; Imani, M.M. Preparation, structural characterization, thermal properties and antifungal activity of alginate-CuO bionanocomposite. Mater. Sci. Eng. C 2019, 101, 323–329. [Google Scholar] [CrossRef]
  16. Zhai, Z.; Ren, B.; Xu, Y.; Wang, S.; Zhang, L.; Liu, Z. Green and facile fabrication of Cu-doped carbon aerogels from sodium alginate for supercapacitors. Org. Electron. 2019, 70, 246–251. [Google Scholar] [CrossRef]
  17. Carneiro-Da-Cunha, M.G.; Cerqueira, M.A.; Souza, B.W.S.; Carvalhoc, S.; Quintas, M.A.C.; Teixeira, J.A.; Vicente, A.A. Physical and thermal properties of a chitosan/alginate nanolayered PET film. Carbohydr. Polym. 2010, 82, 153–159. [Google Scholar] [CrossRef]
  18. Grant, G.T.; Morris, E.R.; Rees, D.A.; Smith, P.J.C.; Thom, D. Biological interactions between polysaccharides and divalent cations: The egg-box model. FEBS Lett. 1973, 32, 195–198. [Google Scholar] [CrossRef] [Green Version]
  19. Serrano-Aroca, A.; Ruiz-Pividal, J.F.; Llorens-Gamez, M. Enhancement of water diffusion and compression performance of crosslinked alginate films with a minuscule amount of graphene oxide. Sci. Rep. 2017, 7, 11684. [Google Scholar] [CrossRef]
  20. Das, D.; Bang, S.; Zhang, S.M.; Noh, I. Bioactive Molecules release and cellular responses of alginate-tricalcium phosphate particles hybrid gel. Nanomaterials 2017, 7, 389. [Google Scholar] [CrossRef]
  21. Matricardi, P.; Pontoriero, M.; Coviello, T.; Casadei, M.A.; Alhaique, F. In situ cross-linkable novel alginate-dextran methacrylate IPN hydrogels for biomedical applications: Mechanical characterization and drug delivery properties. Biomacromolecules 2008, 9, 2014–2020. [Google Scholar] [CrossRef] [PubMed]
  22. Siqueira, P.; Siqueira, E.; de Lima, A.E.; Siqueira, G.; Pinzon-Garcia, A.D.; Lopes, A.P.; Segura, M.E.C.; Isaac, A.; Pereira, F.V.; Botaro, V.R. Three-dimensional stable alginate-nanocellulose gels for biomedical applications: Towards tunable mechanical properties and cell growing. Nanomaterials 2019, 9, 78. [Google Scholar] [CrossRef] [PubMed]
  23. Liu, Y.; Zhao, X.R.; Peng, Y.L.; Wang, D.; Yang, L.W.; Peng, H.; Zhu, P.; Wang, D.Y. Effect of reactive time on flame retardancy and thermal degradation behavior of bio-based zinc alginate film. Polym. Degrad. Stab. 2016, 127, 20–31. [Google Scholar] [CrossRef]
  24. Liu, Y.; Zhang, C.J.; Zhao, J.C.; Guo, Y.; Zhu, P.; Wang, D.Y. Bio-based barium alginate film: Preparation, flame retardancy and thermal degradation behavior. Carbohydr. Polym. 2016, 139, 106–144. [Google Scholar] [CrossRef] [PubMed]
  25. Zhang, J.; Ji, Q.; Wang, F.; Tan, L.; Xia, Y. Effects of divalent metal ions on the flame retardancy and pyrolysis products of alginate fibers. Polym. Degrad. Stab. 2012, 97, 1034–1040. [Google Scholar] [CrossRef]
  26. Liu, Y.; Li, Z.F.; Wang, J.S.; Zhu, P.; Zhao, J.C.; Zhang, C.J.; Guo, Y.; Jin, X. Thermal degradation and pyrolysis behavior of aluminum alginate investigated by TG-FTIR-MS and Py-GC-MS. Polym. Degrad. Stab. 2015, 118, 59–68. [Google Scholar] [CrossRef]
  27. Ma, X.M.; Li, R.; Zhao, X.H.; Ji, Q.; Xing, Y.C.; Sunarso, J.; Xia, Y.Z. Biopolymer composite fibres composed of calcium alginate reinforced with nanocrystalline cellulose. Compos. Part A Appl. Sci. Manuf. 2017, 96, 155–163. [Google Scholar] [CrossRef]
  28. Liu, Z.Q.; Li, Z.; Yang, Y.X.; Zhang, Y.L.; Wen, X.; Li, N.; Fu, C.; Jian, R.K.; Li, L.J.; Wang, D.Y. A geometry effect of carbon nanomaterials on flame retardancy and mechanical properties of ethylene-vinyl acetate/magnesium hydroxide composites. Polymers 2018, 10, 1028. [Google Scholar] [CrossRef]
  29. Wu, N.J.; Niu, F.K.; Lang, W.C.; Xia, M.F. Highly efficient flame-retardant and low-smoke-toxicity poly (vinyl alcohol)/alginate/montmorillonite composite aerogels by two-step crosslinking strategy. Carbohydr. Polym. 2019, 221, 221–230. [Google Scholar] [CrossRef]
  30. Lewin, M. Some comments on the modes of action of nanocomposites in the flame retardancy of polymers. Fire Mater. 2003, 27, 1–7. [Google Scholar] [CrossRef]
  31. Li, J.; Li, Z.; Zhao, X.; Deng, Y.; Xue, Y.; Li, Q. Flame retardancy and thermal degradation mechanism of calcium alginate/CaCO3 composites prepared via in situ method. J. Therm. Anal. Calorim. 2017, 131, 2167–2177. [Google Scholar] [CrossRef]
  32. Liu, Z.; Li, Z.; Zhao, X.; Zhang, L.; Li, Q. Highly efficient flame retardant hybrid composites based on calcium alginate/nano-calcium borate. Polymers 2018, 10, 625. [Google Scholar] [CrossRef] [PubMed]
  33. Xu, P.; Shao, P.Y.; Zhang, Q.; Cheng, W.; Li, Z.C.; Li, Q. A novel inherently flame-retardant composite based on zinc alginate/nano-Cu2O. Polymers 2019, 11, 1575. [Google Scholar] [CrossRef] [PubMed]
  34. Zhao, W.; Qi, Y.; Wang, Y.; Xue, Y.; Xu, P.; Li, Z.; Li, Q. Morphology and thermal properties of calcium alginate/reduced graphere oxide composites. Polymers 2018, 10, 990. [Google Scholar] [CrossRef] [PubMed]
  35. Liu, Z.; Li, J.; Zhao, X.; Li, Z.; Li, Q. Surface coating for flame retardancy and pyrolysis behavior of polyester fabric based on calcium alginate nanocomposites. Nanomaterials 2018, 8, 875. [Google Scholar] [CrossRef]
  36. Zhang, C.J.; Liu, Y.H.; Wang, L.; Zhu, P. Properties of Cu2+ modified calcium alginate fiber. Text. Aux. 2011, 1, 4. [Google Scholar]
  37. Zhang, H.Y.; Liu, C.J.; Chen, L.; Dai, B. Control of ice crystal growth and its effect on porous structure of chitosan cryogels. Chem. Eng. Sci. 2019, 201, 50–57. [Google Scholar] [CrossRef]
  38. Yang, J.R.; Li, Y.Q.; Liu, Y.B.; Li, D.X.; Zhang, L.; Wang, Q.G.; Xiao, Y.M.; Zhang, X.D. Influence of hydrogel network microstructures on mesenchymal stem cell chondrogenesis in vitro and in vivo. Acta Biomater. 2019, 91, 159–172. [Google Scholar] [CrossRef]
  39. Hou, X.; Xue, Z.; Xia, Y.; Qin, Y.; Zhang, G.; Liu, H.; Li, K. Effect of SiO2 nanoparticle on the physical and chemical properties of eco-friendly agar/sodium alginate nanocomposite film. Int. J. Biol. Macromol. 2019, 125, 1289–1298. [Google Scholar] [CrossRef]
  40. Hou, X.B.; Xue, Z.X.; Xia, Y.Z. Preparation of a novel agar/sodium alginate fire-retardancy film. Mater. Lett. 2018, 233, 274–277. [Google Scholar] [CrossRef]
  41. Kashiwagi, T.; Du, F.M.; Douglas, J.F.; Winey, K.I.; Harris, R.H.; Shields, J.R. Nanoparticle networks reduce the flammability of polymer nanocomposites. Nat. Mater. 2005, 4, 928–933. [Google Scholar] [CrossRef] [PubMed]
  42. Papageorgiou, S.K.; Kouvelos, E.P.; Favvas, E.P.; Sapalidis, A.A.; Romanos, G.E.; Katsaros, F.K. Metal-carboxylate interactions in metal-alginate complexes studied with FTIR spectroscopy. Carbohydr. Res. 2010, 345, 469–473. [Google Scholar] [CrossRef] [PubMed]
  43. Ramdani, Y.; Liu, Q.; Huiquan, G.; Liu, P.; Zegaoui, A.; Wang, J. Synthesis and thermal behavior of Cu2O flower-like, Cu2O-C60 and Al/Cu2O-C60 as catalysts on the thermal decomposition of ammonium perchlorate. Vacuum 2018, 153, 277–290. [Google Scholar] [CrossRef]
  44. Shi, R.; Tan, L.; Zong, L.; Ji, Q.; Li, X.; Zhang, K.; Cheng, L.; Xia, Y. Influence of Na (+) and Ca (+) on flame retardancy, thermal degradation, and pyrolysis behavior of cellulose fibers. Carbohydr. Polym. 2017, 157, 1594–1603. [Google Scholar] [CrossRef]
  45. Dong, Q.X.; Liu, M.M.; Ding, Y.F.; Wang, F.; Gao, C.; Liu, P.; Wen, B.; Zhang, S.M.; Yang, M.S. Synergistic effect of DOPO immobilized silica nanoparticles in the intumescent flame retarded polypropylene composites. Polym. Adv. Technol. 2013, 24, 732–739. [Google Scholar] [CrossRef]
  46. Yang, C.Q.; He, Q.L.; Lyon, R.E.; Hu, Y. Investigation of the flammability of different textile fabrics using micro-scale combustion calorimetry. Polym. Degrad. Stab. 2010, 95, 108–115. [Google Scholar] [CrossRef]
Polymers 11 01760 g001 550
Figure 1. The crosslinking of sodium alginate—the “egg box” structure.
Figure 1. The crosslinking of sodium alginate—the “egg box” structure.
Polymers 11 01760 g001
Polymers 11 01760 sch001 550
Scheme 1. Schematic of nano-Cu2O preparation in situ.
Scheme 1. Schematic of nano-Cu2O preparation in situ.
Polymers 11 01760 sch001
Polymers 11 01760 g002 550
Figure 2. Digital photos (a) and X-ray diffraction (XRD) patterns (b) of CaAlg and CaAlg/nano-Cu2O.
Figure 2. Digital photos (a) and X-ray diffraction (XRD) patterns (b) of CaAlg and CaAlg/nano-Cu2O.
Polymers 11 01760 g002
Polymers 11 01760 g003 550
Figure 3. Scanning electron microscopy (SEM) images of (a) CaAlg and (b) CaAlg/nano-Cu2O. The inset in (b) is the magnified image.
Figure 3. Scanning electron microscopy (SEM) images of (a) CaAlg and (b) CaAlg/nano-Cu2O. The inset in (b) is the magnified image.
Polymers 11 01760 g003
Polymers 11 01760 g004 550
Figure 4. Weight loss, DTG, and DSC curves of CaAlg and CaAlg/nano-Cu2O under N2.
Figure 4. Weight loss, DTG, and DSC curves of CaAlg and CaAlg/nano-Cu2O under N2.
Polymers 11 01760 g004
Polymers 11 01760 g005 550
Figure 5. XRD patterns of calcined residue at different temperatures: (a) CaAlg and (b) CaAlg/nano-Cu2O hybrid material.
Figure 5. XRD patterns of calcined residue at different temperatures: (a) CaAlg and (b) CaAlg/nano-Cu2O hybrid material.
Polymers 11 01760 g005
Polymers 11 01760 g006 550
Figure 6. SEM images of calcined residue: (a) CaAlg heated to 250 °C; (b) CaAlg/nano-Cu2O heated to 250 °C; (c) CaAlg heated to 750 °C; (d) CaAlg/nano-Cu2O heated to 750 °C.
Figure 6. SEM images of calcined residue: (a) CaAlg heated to 250 °C; (b) CaAlg/nano-Cu2O heated to 250 °C; (c) CaAlg heated to 750 °C; (d) CaAlg/nano-Cu2O heated to 750 °C.
Polymers 11 01760 g006
Polymers 11 01760 sch002 550
Scheme 2. Flame-retardant mechanism of nano-Cu2O on the hybrid materials.
Scheme 2. Flame-retardant mechanism of nano-Cu2O on the hybrid materials.
Polymers 11 01760 sch002
Table
Table 1. CONE test results of CaAlg and CaAlg/nano-Cu2O. HRR = heat release rate; THR = total heat of release; PHRR = peak heat release rate; EHC = effective heat of combustion; SEA = specific extinction area.
Table 1. CONE test results of CaAlg and CaAlg/nano-Cu2O. HRR = heat release rate; THR = total heat of release; PHRR = peak heat release rate; EHC = effective heat of combustion; SEA = specific extinction area.
SamplesTTI (s)HRR (kW/m2)THR (MJ/m2)PHRR (kW/m2)EHC (MJ/kg)Mean SEA (m2/kg)
CaAlg1139.736.4093.5910.8741.46
CaAlg/nano-Cu2O616.092.0267.309.1421.43
Table
Table 2. Limiting oxygen index (LOI) test, UL-94 test and MCC test results of CaAlg and CaAlg/nano-Cu2O.
Table 2. Limiting oxygen index (LOI) test, UL-94 test and MCC test results of CaAlg and CaAlg/nano-Cu2O.
SamplesLOI (%)UL-94HRC (J/g/K)PHRR (W/g)THR (kJ/g)Residues (%)
CaAlg49.2V-01816.194.355.65
CaAlg/nano-Cu2O54.0V-01614.01460.55

Share and Cite

MDPI and ACS Style

Shao, P.; Xu, P.; Zhang, L.; Xue, Y.; Zhao, X.; Li, Z.; Li, Q. Non-Chloride in Situ Preparation of Nano-Cuprous Oxide and Its Effect on Heat Resistance and Combustion Properties of Calcium Alginate. Polymers 2019, 11, 1760. https://doi.org/10.3390/polym11111760

AMA Style

Shao P, Xu P, Zhang L, Xue Y, Zhao X, Li Z, Li Q. Non-Chloride in Situ Preparation of Nano-Cuprous Oxide and Its Effect on Heat Resistance and Combustion Properties of Calcium Alginate. Polymers. 2019; 11(11):1760. https://doi.org/10.3390/polym11111760

Chicago/Turabian Style

Shao, Peiyuan, Peng Xu, Lei Zhang, Yun Xue, Xihui Zhao, Zichao Li, and Qun Li. 2019. "Non-Chloride in Situ Preparation of Nano-Cuprous Oxide and Its Effect on Heat Resistance and Combustion Properties of Calcium Alginate" Polymers 11, no. 11: 1760. https://doi.org/10.3390/polym11111760

APA Style

Shao, P., Xu, P., Zhang, L., Xue, Y., Zhao, X., Li, Z., & Li, Q. (2019). Non-Chloride in Situ Preparation of Nano-Cuprous Oxide and Its Effect on Heat Resistance and Combustion Properties of Calcium Alginate. Polymers, 11(11), 1760. https://doi.org/10.3390/polym11111760

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.