Next Article in Journal
Self-Catalyzed CdTe Wires
Next Article in Special Issue
Cyclodextrin-Grafted TiO2 Nanoparticles: Synthesis, Complexation Capacity, and Dispersion in Polymeric Matrices
Previous Article in Journal
Effect of Laminating Pressure on Polymeric Multilayer Nanofibrous Membranes for Liquid Filtration
Previous Article in Special Issue
Supramolecular Control over the Interparticle Distance in Gold Nanoparticle Arrays by Cyclodextrin Polyrotaxanes
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Nanomaterials
Volume 8
Issue 5
10.3390/nano8050273
nanomaterials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Cucurbit[n]uril (n = 6, 7) Based Carbon-Gold Hybrids with Peroxidase-Like Activity

by
Liangfeng Zhang
,
Yan Zeng
,
Simin Liu
and
Feng Liang
*
The State Key Laboratory of Refractories and Metallurgy, Coal Conversion and New Carbon Materials Hubei Key Laboratory, School of Chemistry & Chemical Engineering, Wuhan University of Science and Technology, Wuhan 430081, China
*
Author to whom correspondence should be addressed.
Nanomaterials 2018, 8(5), 273; https://doi.org/10.3390/nano8050273
Submission received: 4 April 2018 / Revised: 17 April 2018 / Accepted: 20 April 2018 / Published: 24 April 2018
(This article belongs to the Special Issue Supramolecular Nano-architectures)
Browse Figures
Versions Notes

Abstract

:
Despite the combination of molecular recognition and local electric field enhancement endowing cucurbit[n]uril-capped metallic nanoparticles, indicating great potential in a variety of areas, prior work has paid little attention to carbonizing cucurbit[n]uril on the surface of gold nanoparticles, which may propose new carbon-gold hybrid materials with interesting applications. In this work, we developed a simple and cost-effective method to prepare carbon-gold hybrids by carbonizing cucurbit[n]uril modified gold nanoparticles. The as-prepared cucurbit[n]uril based carbon and carbon-gold hybrid materials have shown to possess peroxidase-like activity. All cucurbit[n]uril based nanomaterials exhibited high catalytic activity over a pH range 2–6 and more tolerant to high temperature (up to 60 °C) when compared to natural horseradish peroxidase.

Graphical Abstract

1. Introduction

The cucurbit[n]uril (CB[n]) family, which bears a rigid hydrophobic cavity and two identical carbonyl fringed portals, is one of the most important macrocyclic containers in host-guest chemistry. The carbonyl oxygen atoms of the cucurbit[n]uril can coordinate directly to a variety of metal ions and lead to complicated nanoscale frameworks and architectures [1]. Since Li and colleagues unraveled the direct interactions between surface of gold nanoparticles and the electron-rich carbonyl rims of CB[n] for the first time [2], CB[n] has been commonly used in capping gold and other metallic nanoparticles with applications, such as in catalysis, drug delivery, electrochemical analysis and surface-enhanced Raman spectroscopy (SERS) [3,4]. In spite of this, there are very few reports of carbonization of CB[n] on the surface of gold nanoparticles, which may be expected to bring new carbon-gold hybrid materials with interesting applications. Previous studies have shown that carbon-gold nanocomposites have excellent biocompatibility, electric conductivity, and physical and chemical stability [5,6,7,8,9,10].
The long-term goal of our group is to construct carbon, metal and carbon-metal hybrid nanomaterials for emerging catalytic, sensing and biological applications [11,12,13,14,15,16,17]. In our previous work, we developed carbon nanomaterials decorated with metal nanoparticles by ion implantation and chemical deposition [18,19,20], in which the metal particles adhered poorly to the carbon material. Recently, we developed a sonicationand solvothermal method to prepare carbon nanomaterials [21,22,23] that can degrade hydrogen peroxide to produce hydroxyl radicals, and thus possess intrinsic peroxidase-like activity [22]. Herein, we demonstrate a simple and cost-effective method to prepare carbon-gold hybrids by carbonizing cucurbit[n]uril modified gold nanoparticles, as illustrated in Scheme 1. The prepared materials exhibited high catalytic activity over a pH range 2~6 and were more tolerant to high temperature when compared to natural horseradish peroxidase (HRP).

2. Materials and Methods

2.1. Chemicals

Sodium hydroxide, hydrogen peroxide, disodium hydrogen phosphate dodecahydrate, sodium chloride and 3,3′,5,5′-tetramethylbenzidine (TMB) were purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China). Horseradish peroxidase was purchased from Hubei Xinxin Belle Biotechnology Co., Ltd. (Wuhan, China). Potassium tetrachloroaurate (III) was purchased from Sahn Chemical Technology Co., Ltd. (Shanghai, China). Cucurbit[6]uril and cucurbit[7]uril were synthesized by our group [14,17].

2.2. Cucurbit[n]uril Directed Synthesis of Gold Nanoparticles (AuNPs)

The aqueous solution of CB[6] (5 mmol, 25 mL) and CB[7] (5 mmol, 25 mL) was prepared with the assistance of sodium chloride (29 mg) because CB[6] partially dissolved in double distilled water. After that, one equivalent amount of aqueous KAuCl4 (5 mmol, 25 mL) was mixed with CB[6] or CB[7] solution at room temperature. A yellow precipitate was immediately obtained, then an aqueous solution of NaOH (40 mmol, 50 mL) was added. The yellow precipitate disappeared, and a clear solution was obtained; then, a wine-red colored solution formed after 48 h, indicating the formation of the AuNPs.

2.3. Preparation of Cucurbit[n]uril Based Carbon-Gold and Carbon Nanomaterials

Initially, the resulting wine red AuNPs was washed three times with double distilled water by means of centrifugation. After that, AuNPs solution was sealed in Teflon-lined stainless-steel autoclave (100 mL) and reacted at 180 °C for 24 h by using Vacuum oven DZF-6020 (Shanghai Jinghong, Shanghai, China). After the autoclave was cooled down to the room temperature, the pre-carbonized materials were collected by means of centrifugation. The obtained khaki powder was dried in vacuum at 40 °C, then carbonized in quartz crucible up to 700 °C under a nitrogen atmosphere at a heating rate of 5 °C/min, and then held at that temperature for 1 h by using a vacuum tube furnace, OTF-1200X. Carbon nanomaterials were directly prepared from CB[6] and CB[7] in a quartz crucible by heating up to 700 °C under a nitrogen atmosphere at a rate of 5 °C/min, and then held at that temperature for 1 h.

2.4. Materials Characterization

The UV-vis absorption spectra were recorded on Shimadzu UV-vis-NIR spectrophotometer (Shimadzu, Tokyo, Japan). Transmission electron microscopy (TEM) was performed by using JEM-2100UHR STEM (JEOL, Tokyo, Japan). Energy-dispersive X-ray spectroscopy (EDS) measurements were performed with a spectrometer attached to PHILIPS XL30 TMP field-emission scanning electron microscopy (SEM) system (Philips, Hillsboro, OR, USA). The X-ray powder diffraction (XRD) pattern was tested on a X’Pert PRO MPD diffractometer (Panalytical B.V., Amsterdam, Holland) with nickel-filtered Cu Kαradiation. A thermal gravimetric analyzer (TGA) STA449 (Nai Chi Scientific Instruments, Shanghai, China)was used for the investigation of the thermal properties of the samples.

2.5. Peroxidase-Like Activity

To investigate the peroxidase-like activity of carbon-gold and carbon nanomaterials, catalytic oxidation of the colorimetric substrate TMB in the presence of H2O2 was performed. In a typical experiment [22], the mixture of TMB (8 mM, 100 µL), carbon-gold (40 µL) or carbon nanomaterials (1 mg/mL), phosphate buffer (25 mM, 810 µL, pH = 4), together with H2O2 (1 M, 50 µL) are incubated at 35 °C for standard curve measurement. Under the above-mentioned condition, the catalytic reaction was incubated in the buffer solution under different pH (1.0–12.0) to investigate the pH effect on the tested reaction. Similarly, the reaction was incubated in the buffer solution under different temperature from 25 °C to 60 °C to examine the effect of temperature. HRP was investigated under the same conditions as the control.
Under optimum conditions, the steady-state kinetic parameters of carbon-gold (CCB[n]/AuNPs) and carbon nanomaterials (CCB[n]) as catalysts were determined by using H2O2 and TMB as substrates. In the presence of H2O2 and TMB, the reaction was carried out at 35 °C in a 1 mL of a tube containing prepared nanomaterials or HRP in phosphate buffer solution (25 mM, pH = 4). The assays were carried out by varying concentration of TMB at a fixed concentration of H2O2 or varying concentration of H2O2 at a fixed concentration of TMB. The reaction kinetics measurements were performed by recording the absorbance reading at 652nm in the time scan mode.

3. Results and Discussion

3.1. Characterization of Prepared Nanomaterials

As illustrated in Scheme 1, KAuCl4 in CB[n] solution produced CB[n] capped AuNPs under a specific set of conditions [24,25,26,27]. The CB[n] plays the role of both reducing and protecting agents. The particles obtained were spherical in shape and had good dispensability as shown in Figure 1. UV-vis spectroscopy of AuNPs are shown in Figure 1a, the characteristic surface plasmon resonance band of these two kinds of AuNPs centered at 547 nm and 540 nm, respectively. The size of AuNPs was investigated by transmission electron microscopy (TEM), as shown in Figure 1b,c, and the mean diameter of the CB[n] capped AuNPs, CB[6]/AuNPs and CB[7]/AuNPs were 8.0 ± 1.5 nm and 10.0 ± 1.1 nm.
In order to confirm the morphology of the annealed CB[6]/AuNPs and CB[7]/AuNPs hybrid materials (CCB[6]/AuNPs and CCB[7]/AuNPs), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were applied to study the prepared materials. The SEM images in Figure 2a,e show that these hybrid materials have three-dimensional porous structures.EDS spectroscopy was further used to confirm the hybrid nanomaterials. As shown in Figure 2b,f, EDS only detected gold and carbon in the composites, suggesting that these hybrids are composed of gold and carbon elements. Moreover, X-ray diffraction patterns were utilized to detect the crystal structures of two hybrids. The diffraction peaks observed from the blue line of Figure 2d,h at 38.2°, 44.4°, 64.7° 77.7° and 81.8° could be ascribed to the (111), (200), (220), (311) and (222) planes of the Au crystals, and a broad peak at 20°–30° related to the amorphous carbon of cucurbit[n]uril [28,29], which further confirms that the hybrid materials are composites of gold and carbon. In addition, the black strip of Au is embedded in the carbon film irregularly, as evidenced by the TEM images in Figure 2c,g.
Thermal gravimetric analysis (TGA) was used to investigate the weight loss of CB[6] and CB[7]. As shown in Figure 3, there are two steps to weight loss. The slight weight loss from the first stage could be attributed to the release of physically absorbed water, and the other loss is from the pyrogenation of cucurbit[n]urils [17]. The annealed cucurbit[7]uril (CCB[7]) is multilayer stacking of porous structures (the pore size is around 0.56 ± 0.13 μm), while the annealed cucurbit[6]uril (CCB[6]) is the layer by layer stacking structure, with no obvious pores detected. The thickness of CCB[7] sheet (1.47 ± 0.29 μm) is thicker than that of CCB[6] (0.97 ± 0.32 μm).

3.2. Peroxidase-Like Activity

The catalytic performance of as-prepared carbon-gold and carbon nanomaterials were tested by using the peroxidase substrate TMB. Upon the addition of H2O2, the catalytic reaction can be monitored by detecting TMB absorbance change at 652 nm [22,30,31]. As shown in Figure 4, no obvious absorbance peak at 652 nm could be detected in the mixed solution of TMB and prepared materials of TMB and H2O2. After the addition of H2O2, the absorption peak at 652 nm was significantly enhanced in the presence of prepared nanomaterials over the same period. These results clearly demonstrated that prepared hybrids and carbon nanomaterials in this work possessed intrinsic peroxidase-like activity. As shown in Figure S1, with the increasing concentration of TMB, the absorbance at 652 nm changed quickly, suggesting that more TMB was oxidized. Furthermore, TMB can be detected by the prepared materials as low as 1 × 10−4 mol/L, which is similar to HRP [32,33,34,35].
Similar to other peroxidase mimics as well as the natural peroxidase HRP, the catalytic activity of hybrids and carbon nanomaterials is also dependent on pH and temperature [32,33]. It is well known that pH is an important parameter for a catalytic reaction. The pH dependent experiments were performed in the buffer solution with different pH values range from 1.0 to 12.0. Similar to the natural peroxidase HRP, the optimal pH is 4. In addition, hybrids and carbon nanomaterials are much more stable over a relatively wide pH range. As shown in Figure 5a–d, when the pH of the buffer solution is 5, the peroxidase-like activity of hybrids and carbon nanomaterials remained 80%, while the HRP almost drifted to inactive performance. Moreover, the influence of temperature on the TMB oxidation reaction catalyzed by the as-prepared nanomaterials and HRP were investigated by varying the reaction temperature from 25 °C to 60 °C, as illustrated in Figure 5e,f. Due to the sensitivity of HRP to temperature, the natural enzyme easily becomes denatured, while the catalytic activity of hybrids and carbon nanomaterials increased gradually with increasing experimental temperatures. However, the catalytic activity of hybrids and CCB[6] dramatically decreased at a temperature higher than 55 °C, except for CCB[7], which continuously increased with the higher temperature. This might be attributed to the honeycomb-like porous structure and larger pore volume of CCB[7] as shown in Figure 3. Although it has been reported that Fe3O4@C nanoparticles [33] and CeO2 nanoparticles [34] exhibited temperature-dependent catalytic activity, the exact mechanism underlying such activity is still unclear. The evolution of oxidation of TMB under H2O2 as a function of pH and temperature was conducted. As shown in Figure S2, H2O2 could be more efficient in oxidizing TMB at higher temperatures under acidic conditions. Increasing the temperature could accelerate the decomposition of H2O2 to produce oxygen and benefit the oxidation of TMB.
For further analyzing the catalytic mechanism of hybrids and carbon nanomaterials, steady-state kinetics with TMB and H2O2 as substrates were investigated. A series of experiments were performed by varying the concentration of one substrate while fixing another as constant. Typical Michaelis-Menten curves (Figure 6) were received in a certain concentration of H2O2 or TMB. Maximum initial velocity (Vmax) and Michaelis-Menten constant (Km) were obtained using Lineweaver-Burk plot and were presented in Table 1. Typically, the lower Km represents a higher enzyme-like affinity between the catalyst and the substrate [32,35]. The Km value of hybrids with TMB was lower than that of carbon nanomaterials and higher than that of CB[n] capped AuNPs (Figure S3). This suggests higher binding affinity of hybrids to TMB than that of carbon nanomaterials, and lower binding affinity of hybrids to TMB than that of CB[n] capped AuNPs. Similarly, the Km value of hybrids with H2O2 is slightly lower than that of carbon nanomaterials and higher than that of CB[n] capped AuNPs. The results can be attributed to the synergistic effect of gold and carbon, so hybrids with gold could absorb TMB and H2O2 more efficiently than carbon materials. However, the Vmax of carbon nanomaterials is higher than that of hybrids. This is possible as the dispersion of hybrids in water is worse than that of carbon nanomaterials.
Similar to previous studies [36,37], the unsupported CB[n] capped AuNPs could catalyze the oxidation of TMB in the presence of H2O2. Typically, AuNPs could absorb H2O2 [38] and CB[n] on the gold tend to attract amino groups of TMB electrostatically [3,39], which likely to result in stronger affinity to reaction substrates (Table 1). After carbonization, the unique porous carbon architecture was produced, and the gold was embedded in the porous carbon aggregates, which possibly could benefit electron transfer [40]. Thus far, the hybrids in our case exhibited comparable peroxidase-like activity with Fe3O4, Pt, Pd and CuS nanoparticles, and much better binding affinity towards H2O2 (Table 1). There is still great potential to improve their ability as nano-enzymes by tuning compositions.

4. Conclusions

In the present work, we prepared well-dispersed AuNPs using cucurbit[n]uril (n = 6, 7) as reducing and protecting agents according to a facile and eco-friendly one-step synthesis. CB[n] based carbon-gold hybrids and carbon nanomaterials were then successfully prepared by carbonization, which is a simple, cost-effective, quick and practical approach. All CB[n]based nanomaterials possess intrinsic peroxidase-like activity, and the hybrids could absorb substrates more efficiently with the incorporated gold. This method guided constructing novel and enhanced carbon-gold multifunctional nanomaterials. Once guest molecules containing nitrogen, oxygen and other heteroatoms are included in the cavity of CB[n] on metallic nanoparticles, heteroatom-doped carbon-metal hybrids can be prepared.

Supplementary Materials

The following are available online at https://www.mdpi.com/2079-4991/8/5/273/s1, Figure S1: The time-dependent absorbance changes at 652 nm under different TMB concentration; Figure S2: (a) Temperature and (b) pH dependence for TMB and H2O2 system in the absence of nanomaterials; Figure S3: UV-vis spectra of different TMB system with (a) CB[6]/AuNPs and (b) CB[7]/AuNPs, and steady-state kinetic curves of (c) CB[6]/AuNPs and (d) CB[7]/AuNPs.

Author Contributions

S.L. and F.L. conceived and designed the experiments; L.Z. performed the experiments; L.Z., Y.Z. and F.L. analyzed the data; L.Z. and F.L. wrote the paper.

Acknowledgments

We acknowledge the financial support from National Natural Science Foundation of China (21372183, 21472143), Thousand Youth Talents Program of China, and Program for Innovative Teams of Outstanding Young and Middle-aged Researchers in the Higher Education Institutions of Hubei Province (T201702).

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Ni, X.L.; Xiao, X.; Cong, H.; Liang, L.L.; Cheng, K.; Cheng, X.J.; Ji, N.N.; Zhu, Q.J.; Xue, S.F.; Tao, Z. Cucurbit[n]uril-based coordination chemistry: From simple coordination complexes to novel poly-dimensional coordination polymers. Chem. Soc. Rev. 2013, 42, 9480–9508. [Google Scholar] [CrossRef] [PubMed]
  2. An, Q.; Li, G.; Tao, C.; Li, Y.; Wu, Y.; Zhang, W. A general and efficient method to form self-assembled cucurbit[n]uril monolayers on gold surfaces. Chem. Commun. 2008, 0, 1989–1991. [Google Scholar] [CrossRef] [PubMed]
  3. Barrow, S.J.; Kasera, S.; Rowland, M.J.; del Barrio, J.; Scherman, O.A. Cucurbituril-Based Molecular Recognition. Chem. Rev. 2015, 115, 12320–12406. [Google Scholar] [CrossRef] [PubMed]
  4. Gurbuz, S.; Idris, M.; Tuncel, D. Cucurbituril-based supramolecular engineered nanostructured materials. Org. Biomol. Chem. 2015, 13, 330–347. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  5. Cui, H.; Hong, C.; Ying, A.; Yang, X.; Ren, S. Ultrathin gold nanowire-functionalized carbon nanotubes for hybrid molecular sensing. ACS Nano 2013, 7, 7805–7811. [Google Scholar] [CrossRef] [PubMed]
  6. Yao, A.; Fu, Q.; Xu, L.; Xu, Y.; Jiang, W.; Wang, D. Synthesis of pH-responsive nanocomposites of gold nanoparticles and graphene oxide and their applications in SERS and catalysis. RSC Adv. 2017, 7, 56519–56527. [Google Scholar] [CrossRef]
  7. Khalil, I.; Julkapli, N.M.; Yehye, W.A.; Basirun, W.J.; Bhargava, S.K. Graphene-gold nanoparticles hybrid-synthesis, functionalization, and application in a electrochemical and surface-enhanced raman scattering biosensor. Materials 2016, 9, 406. [Google Scholar] [CrossRef] [PubMed]
  8. Ondera, T.J.; Hamme, A.T. Gold nanopopcorn attached single-walled carbon nanotube hybrid for rapid detection and killing of bacteria. J. Mater. Chem. B 2014, 2, 7534–7543. [Google Scholar] [CrossRef] [PubMed]
  9. Yang, W.; Qu, L.; Zheng, R.; Liu, Z.; Ratinac, K.R.; Shen, L.; Yu, D.; Yang, L.J.; Barrow, C.; Ringer, S.P.; et al. Self-Assembly of gold nanowires along carbon nanotubes for ultrahigh-aspect-ratio hybrids. Chem. Mater. 2011, 23, 2760–2765. [Google Scholar] [CrossRef]
  10. Song, J.; Wang, F.; Yang, X.; Ning, B.; Harp, M.G.; Culp, S.H.; Hu, S.; Huang, P.; Nie, L.; Chen, J.; et al. Gold nanoparticle coated carbon nanotube ring with enhanced raman scattering and photothermal conversion property for theranostic applications. J. Am. Chem. Soc. 2016, 138, 7005–7015. [Google Scholar] [CrossRef] [PubMed]
  11. Zhou, X.; Liang, F. Application of graphene/graphene oxide in biomedicine and biotechnology. Curr. Med. Chem. 2014, 21, 855–869. [Google Scholar] [CrossRef] [PubMed]
  12. Liang, F.; Chen, R. Emerging assay platforms based on nanostructures. Curr. Nanosci. 2015, 11, 684. [Google Scholar] [CrossRef]
  13. Ma, T.; Liang, F.; Chen, R.; Liu, S.; Zhang, H. Synthesis of Au-Pd bimetallic nanoflowers for catalytic reduction of 4-nitrophenol. Nanomaterials 2017, 7, 239. [Google Scholar] [CrossRef] [PubMed]
  14. Ma, T.; Yang, W.; Liu, S.; Zhang, H.; Liang, F. A comparison reduction of 4-nitrophenol by gold nanospheres and gold nanostars. Catalysts 2017, 7, 38. [Google Scholar] [CrossRef]
  15. Shu, T.; Su, L.; Wang, J.; Lu, X.; Liang, F.; Li, C.; Zhang, X. Value of the debris of reduction sculpture: Thiol etching of Au nanoclusters for preparing water-soluble and aggregation-induced emission-active Au(I) complexes as phosphorescent copper ion sensor. Anal. Chem. 2016, 88, 6071–6077. [Google Scholar] [CrossRef] [PubMed]
  16. Lu, X.; Wang, T.; Shu, T.; Qu, X.; Zhang, X.; Liang, F.; Su, L. Combination of chemical etching of gold nanoclusters with aggregation-induced emission for preparation of new phosphors for the development of UV-driven phosphor-converted white light-emitting diodes. J. Mater. Chem. C 2016, 4, 11482–11487. [Google Scholar] [CrossRef]
  17. Han, Y.; Yang, X.; Liu, Y.; Ai, Q.; Liu, S.; Sun, C.; Liang, F. Supramolecular controlled cargo release via near infrared tunable cucurbit[7]uril-gold nanostars. Sci. Rep. 2016, 6, 22239. [Google Scholar] [CrossRef] [PubMed]
  18. Liu, Y.; Hu, Y.; Chen, R.; Zhan, W.; Ni, H.; Zhang, P.; Liang, F. Antibacterial properties of multi-walled carbon nanotubes decorated with silver nanoparticles. Curr. Nanosci. 2016, 12, 411–415. [Google Scholar] [CrossRef]
  19. Liu, Y.; Liu, S.; Chen, R.; Zhan, W.; Ni, H.; Liang, F. An antibacterial nonenzymatic glucose sensor composed of carbon nanotubes decorated with silver nanoparticles. Electroanalysis 2015, 27, 1138–1143. [Google Scholar] [CrossRef]
  20. Liu, Y.; Han, Y.; Chen, R.; Zhang, H.; Liu, S.; Liang, F. In situimmobilization of copper nanoparticles on polydopamine coated graphene oxide for H2O2 determination. PLoS ONE 2016, 11, e0157926. [Google Scholar]
  21. Zhou, Y.; Liu, L.; Shen, Y.; Wu, L.; Yu, L.; Liang, F.; Xi, J. Carbon dots promoted vanadium flow batteries for all-climate energy storage. Chem. Commun. 2017, 53, 7565–7568. [Google Scholar] [CrossRef] [PubMed]
  22. Zeng, Y.; Miao, F.; Zhao, Z.; Zhu, Y.; Liu, T.; Chen, R.; Liu, S.; Lv, Z.; Liang, F. Low-cost nanocarbon-based peroxidases from graphite and carbon fibers. Appl. Sci. 2017, 7, 924. [Google Scholar]
  23. Liu, Y.; Shen, Y.; Yu, L.; Liu, L.; Liang, F.; Qiu, X.; Xi, J. Holey-engineered electrodes for advanced vanadium flow batteries. Nano Energy 2018, 43, 55–62. [Google Scholar] [CrossRef]
  24. Lee, T.C.; Scherman, O.A. A facile synthesis of dynamic supramolecular aggregates of cucurbit[n]uril (n = 5–8) capped with gold nanoparticles in aqueous media. Chem. Eur. J. 2012, 18, 1628–1633. [Google Scholar] [CrossRef] [PubMed]
  25. Lee, T.C.; Scherman, O.A. Formation of dynamic aggregates in water by cucurbit[5]uril capped with gold nanoparticles. Chem. Commun. 2010, 46, 2438–2440. [Google Scholar] [CrossRef] [PubMed]
  26. Lanterna, A.; Pino, E.; Domenech-Carbo, A.; Gonzalez-Bejar, M.; Perez-Prieto, J. Enhanced catalytic electrochemical reduction of dissolved oxygen with ultraclean cucurbituril[7]-capped gold nanoparticles. Nanoscale 2014, 6, 9550–9553. [Google Scholar] [CrossRef] [PubMed]
  27. Blanco, E.; Esteve-Adell, I.; Atienzar, P.; Casas, J.A.; Hernández, P.; Quintana, C. Cucurbit[7]uril-stabilized gold nanoparticles as catalysts of the nitro compound reduction reaction. RSC Adv. 2016, 6, 86309–86315. [Google Scholar] [CrossRef]
  28. Jose, M.V.; Marx, S.; Murata, H.; Koepsel, R.R.; Russell, A.J. Direct electron transfer in a mediator-free glucose oxidase-based carbon nanotube-coated biosensor. Carbon 2012, 50, 4010–4020. [Google Scholar] [CrossRef]
  29. Cui, R.; Liu, C.; Shen, J.; Gao, D.; Zhu, J.-J.; Chen, H.-Y. Gold nanoparticle-colloidal carbon nanosphere hybrid material: Preparation, characterization, and application for an amplified electrochemical immunoassay. Adv. Funct. Mater. 2008, 18, 2197–2204. [Google Scholar] [CrossRef]
  30. Gao, L.; Zhuang, J.; Nie, L.; Zhang, J.; Zhang, Y.; Gu, N.; Wang, T.; Feng, J.; Yang, D.; Perrett, S.; et al. Intrinsic peroxidase-like activity of ferromagnetic nanoparticles. Nat. Nanotechnol. 2007, 2, 577–583. [Google Scholar] [CrossRef] [PubMed]
  31. Shi, W.; Wang, Q.; Long, Y.; Cheng, Z.; Chen, S.; Zheng, H.; Huang, Y. Carbon nanodots as peroxidase mimetics and their applications to glucose detection. Chem. Commun. 2011, 47, 6695–6697. [Google Scholar] [CrossRef] [PubMed]
  32. Tao, Y.; Lin, Y.; Huang, Z.; Ren, J.; Qu, X. Incorporating graphene oxide and gold nanoclusters: A synergistic catalyst with surprisingly high peroxidase-like activity over a broad pH range and its application for cancer cell detection. Adv. Mater. 2013, 25, 2594–2599. [Google Scholar] [CrossRef] [PubMed]
  33. Lu, N.; Zhang, M.; Ding, L.; Zheng, J.; Zeng, C.; Wen, Y.; Liu, G.; Aldalbahi, A.; Shi, J.; Song, S.; et al. Yolk-shell nanostructured Fe3O4@C magnetic nanoparticles with enhanced peroxidase-like activity for label-free colorimetric detection of H2O2 and glucose. Nanoscale 2017, 9, 4508–4515. [Google Scholar] [CrossRef] [PubMed]
  34. Liu, Q.; Yang, Y.; Lv, X.; Ding, Y.; Zhang, Y.; Jing, J.; Xu, C. One-step synthesis of uniform nanoparticles of porphyrinfunctionalized ceria with promising peroxidase mimetics for H2O2and glucose colorimetric detection. Sens. Actuators. B Chem. 2017, 240, 726–734. [Google Scholar] [CrossRef]
  35. Song, Y.; Qu, K.; Zhao, C.; Ren, J.; Qu, X. Graphene oxide: Intrinsic peroxidase catalytic activity and its application to glucose detection. Adv. Mater. 2010, 22, 2206–2210. [Google Scholar] [CrossRef] [PubMed]
  36. Jv, Y.; Li, B.; Cao, R. Positively-charged gold nanoparticles as peroxidiase mimic and their application in hydrogen peroxide and glucose detection. Chem. Commun. 2010, 46, 8017–8019. [Google Scholar] [CrossRef] [PubMed]
  37. Wang, S.; Chen, W.; Liu, A.L.; Hong, L.; Deng, H.H.; Lin, X.H. Comparison of the peroxidase-like activity of unmodified, amino-modified, and citrate-capped gold nanoparticles. ChemPhysChem 2012, 13, 1199–1204. [Google Scholar] [CrossRef] [PubMed]
  38. Cui, H.; Zhang, Z.F.; Shi, M.J.; Xu, Y.; Wu, Y.L. Light emission of gold nanoparticles induced by the reaction of bis(2,4,6-trichlorophenyl) oxalate and hydrogen peroxide. Anal. Chem. 2005, 77, 6402–6406. [Google Scholar] [CrossRef] [PubMed]
  39. Yu, F.; Huang, Y.; Cole, A.J.; Yang, V.C. The artificial peroxidase activity of magnetic iron oxide nanoparticles and its application to glucose detection. Biomaterials 2009, 30, 4716–4722. [Google Scholar] [CrossRef] [PubMed]
  40. Zhang, D.; Zhao, H.; Fan, Z.; Li, M.; Du, P.; Liu, C.; Li, Y.; Li, H.; Cao, H. A highly sensitive and selective hydrogen peroxide biosensor based on gold nanoparticles and three-dimensional porous carbonized chicken eggshell membrane. PLoS ONE 2015, 10, e0130156. [Google Scholar] [CrossRef] [PubMed]
  41. Fu, Y.; Zhang, H.; Dai, S.; Zhi, X.; Zhang, J.; Li, W. Glutathione-stabilized palladium nanozyme for colorimetric assay of silver(I) ions. Analyst 2015, 140, 6676–6683. [Google Scholar] [CrossRef] [PubMed]
  42. Li, W.; Zhang, H.; Zhang, J.; Fu, Y. Synthesis and sensing application of glutathione-capped platinum nanoparticles. Anal. Methods 2015, 7, 4464–4471. [Google Scholar] [CrossRef]
  43. Zhang, L.; Chen, M.; Jiang, Y.; Chen, M.; Ding, Y.; Liu, Q. A facile preparation of montmorillonite-supported copper sulfide nanocomposites and their application in the detection of H2O2. Sens. Actuators B Chem. 2017, 239, 28–35. [Google Scholar] [CrossRef]
Nanomaterials 08 00273 sch001 550
Scheme 1. Schematic illustration of preparation of cucurbit[n]uril based carbon-gold and carbon nanomaterials with peroxidase-like activity.
Scheme 1. Schematic illustration of preparation of cucurbit[n]uril based carbon-gold and carbon nanomaterials with peroxidase-like activity.
Nanomaterials 08 00273 sch001
Nanomaterials 08 00273 g001 550
Figure 1. (a) UV-vis spectra of the prepared AuNPs. TEM micrographs and their corresponding histograms of (b) CB[6]/AuNPs and (c) CB[7]/AuNPs.
Figure 1. (a) UV-vis spectra of the prepared AuNPs. TEM micrographs and their corresponding histograms of (b) CB[6]/AuNPs and (c) CB[7]/AuNPs.
Nanomaterials 08 00273 g001
Nanomaterials 08 00273 g002 550
Figure 2. (a) Secondary electron SEM image of CCB[6]/AuNPs; (b) EDS pattern of CCB[6]/AuNPs; (c) TEM image of CCB[6]/AuNPs; (d) XRD pattern of CB[6] and corresponding materials; (e) Secondary electron SEM image of CCB[7]/AuNPs; (f) EDS pattern of CCB[7]/AuNPs; (g) TEM image of CCB[7]/AuNPs; (h) XRD pattern of CB[7] and corresponding materials.
Figure 2. (a) Secondary electron SEM image of CCB[6]/AuNPs; (b) EDS pattern of CCB[6]/AuNPs; (c) TEM image of CCB[6]/AuNPs; (d) XRD pattern of CB[6] and corresponding materials; (e) Secondary electron SEM image of CCB[7]/AuNPs; (f) EDS pattern of CCB[7]/AuNPs; (g) TEM image of CCB[7]/AuNPs; (h) XRD pattern of CB[7] and corresponding materials.
Nanomaterials 08 00273 g002
Nanomaterials 08 00273 g003 550
Figure 3. TGA curves of (a) CB[6] and (d) CB[7]; Secondary electron SEM images of CCB[6]: (b,c); Secondary electron SEM images of CCB[7]: (e,f).
Figure 3. TGA curves of (a) CB[6] and (d) CB[7]; Secondary electron SEM images of CCB[6]: (b,c); Secondary electron SEM images of CCB[7]: (e,f).
Nanomaterials 08 00273 g003
Nanomaterials 08 00273 g004 550
Figure 4. UV-vis spectra of different TMB system with (a) CCB[6]; (b)CCB[7]; (c) CCB[6]/AuNPs; (d) CCB[7]/AuNPs.
Figure 4. UV-vis spectra of different TMB system with (a) CCB[6]; (b)CCB[7]; (c) CCB[6]/AuNPs; (d) CCB[7]/AuNPs.
Nanomaterials 08 00273 g004
Nanomaterials 08 00273 g005 550
Figure 5. pH dependent response curves of different materials in this work and HRP: (a) CCB[6]/AuNPs; (b) CCB[7]/AuNPs; (c) CCB[6]; (d) CCB[7]. Temperature dependent response curves of different materials in this work and HRP: (e) CCB[6]/AuNPs; (f) CCB[7]/AuNPs; (g) CCB[6]; (h) CCB[7].
Figure 5. pH dependent response curves of different materials in this work and HRP: (a) CCB[6]/AuNPs; (b) CCB[7]/AuNPs; (c) CCB[6]; (d) CCB[7]. Temperature dependent response curves of different materials in this work and HRP: (e) CCB[6]/AuNPs; (f) CCB[7]/AuNPs; (g) CCB[6]; (h) CCB[7].
Nanomaterials 08 00273 g005
Nanomaterials 08 00273 g006 550
Figure 6. Steady-state kinetic curves of different materials in this work and HRP: (a) CCB[6]/AuNPs; (b) CCB[7]/AuNPs; (c) CCB[6]; (d) CCB[7]; (e) HRP.
Figure 6. Steady-state kinetic curves of different materials in this work and HRP: (a) CCB[6]/AuNPs; (b) CCB[7]/AuNPs; (c) CCB[6]; (d) CCB[7]; (e) HRP.
Nanomaterials 08 00273 g006
Table
Table 1. Michaelis-Menten constant (Km) and maximum reaction rate (Vmax) of different nanomaterials in this work and HRP.
Table 1. Michaelis-Menten constant (Km) and maximum reaction rate (Vmax) of different nanomaterials in this work and HRP.
CatalystSubstrateKm (mM)Vmax (10−9 M/s)
CCB[6]TMB2.4 ± 0.198.2 ± 3.8
H2O22.2 ± 0.216.4 ± 1.8
CCB[7]TMB2.5 ± 0.134.7 ± 2.9
H2O21.4 ± 0.15.2 ± 0.8
CB[6]/AuNPsTMB0.098 ± 0.00810.1 ± 0.8
H2O20.2 ± 0.073.0 ± 0.2
CB[7]/AuNPsTMB0.038 ± 0.00310.2 ± 0.2
H2O20.097 ± 0.023.9 ± 0.1
CCB[6]/AuNPsTMB1.9 ± 0.211.4 ± 1.2
H2O21.3 ± 0.210.8 ± 1.5
CCB[7]/AuNPsTMB0.63 ± 0.126.4 ± 1.0
H2O20.74 ± 0.081.7 ± 1.1
HRPTMB0.81 ± 0.1147.6 ± 2.3
H2O29.8 ± 0.0487.6 ± 2.0
Fe3O4 magnetic nanoparticles [30]TMB0.09834.4
H2O215497.8
Glutathione-capped Pd nanoparticles [41]TMB0.068315
H2O2156408
Glutathione-capped Pt nanoparticles [42]TMB0.079328
H2O273.6302
Montmorillonite-supported CuS nanoparticles [43]TMB0.0212.8
H2O22.30.97

Share and Cite

MDPI and ACS Style

Zhang, L.; Zeng, Y.; Liu, S.; Liang, F. Cucurbit[n]uril (n = 6, 7) Based Carbon-Gold Hybrids with Peroxidase-Like Activity. Nanomaterials 2018, 8, 273. https://doi.org/10.3390/nano8050273

AMA Style

Zhang L, Zeng Y, Liu S, Liang F. Cucurbit[n]uril (n = 6, 7) Based Carbon-Gold Hybrids with Peroxidase-Like Activity. Nanomaterials. 2018; 8(5):273. https://doi.org/10.3390/nano8050273

Chicago/Turabian Style

Zhang, Liangfeng, Yan Zeng, Simin Liu, and Feng Liang. 2018. "Cucurbit[n]uril (n = 6, 7) Based Carbon-Gold Hybrids with Peroxidase-Like Activity" Nanomaterials 8, no. 5: 273. https://doi.org/10.3390/nano8050273

Note that from the first issue of 2016, this journal uses article numbers instead of page numbers. See further details here.

Article Metrics

Back to TopTop