Next Article in Journal
RutheniumII Complexes bearing Fused Polycyclic Ligands: From Fundamental Aspects to Potential Applications
Next Article in Special Issue
Magnetic Pycnoporus sanguineus-Loaded Alginate Composite Beads for Removing Dye from Aqueous Solutions
Previous Article in Journal
Surface-Functionalized Hyperbranched Poly(Amido Acid) Magnetic Nanocarriers for Covalent Immobilization of a Bacterial γ-Glutamyltranspeptidase
Previous Article in Special Issue
Beads-Based Electrochemical Assay for the Detection of Influenza Hemagglutinin Labeled with CdTe Quantum Dots
 
 
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Biocompatible Fe3O4 Increases the Efficacy of Amoxicillin Delivery against Gram-Positive and Gram-Negative Bacteria

by
Alexandru Mihai Grumezescu
1,
Monica Cartelle Gestal
2,*,
Alina Maria Holban
3,
Valentina Grumezescu
1,
Bogdan Ștefan Vasile
1,
Laurențiu Mogoantă
4,
Florin Iordache
5,
Coralia Bleotu
6 and
George Dan Mogoșanu
7
1
Department of Science and Engineering of Oxide Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, Politehnica University of Bucharest, Polizu Street no 1-7, 011061 Bucharest, Romania
2
School of Medicine, Faculty of Public Health, SENESCYT 9 de Octubre N22-64 y Ramírez Dávalos - Casa Patrimonial, 170517 Quito, Ecuador
3
Microbiology Immunology Department, Faculty of Biology, University of Bucharest, Aleea Portocalelor no 1-3, 060101 Bucharest, Romania
4
Research Center for Microscopic Morphology and Immunology, University of Medicine and Pharmacy of Craiova, 2 Petru Rareş Street, 200349 Craiova, Romania
5
Institute of Cellular Biology and Pathology of Romanian Academy, "Nicolae Simionescu", Department of Fetal and Adult Stem Cell Therapy, 8, B.P. Hasdeu, 050568 Bucharest, Romania
6
Stefan S. Nicolau Institute of Virology, 285 Mihai Bravu, 030304 Bucharest, Romania
7
Department of Pharmacognosy & Phytotherapy, Faculty of Pharmacy, University of Medicine and Pharmacy of Craiova, 2 Petru Rareş Street, 200349 Craiova, Romania
*
Author to whom correspondence should be addressed.
Molecules 2014, 19(4), 5013-5027; https://doi.org/10.3390/molecules19045013
Submission received: 5 March 2014 / Revised: 9 April 2014 / Accepted: 14 April 2014 / Published: 22 April 2014
(This article belongs to the Special Issue Bio and Nanomaterials Based on Fe3O4)

Abstract

:
This paper reports the synthesis and characterization of amoxicillin- functionalized magnetite nanostructures (Fe3O4@AMO), revealing and discussing several biomedical applications of these nanomaterials. Our results proved that 10 nm Fe3O4@AMO nanoparticles does not alter the normal cell cycle progression of cultured diploid cells, and an in vivo murine model confirms that the nanostructures disperse through the host body and tend to localize in particular sites and organs. The nanoparticles were found clustered especially in the lungs, kidneys and spleen, next to the blood vessels at this level, while being totally absent in the brain and liver, suggesting that they are circulated through the blood flow and have low toxicity. Fe3O4@AMO has the ability to be easily circulated through the body and optimizations may be done so these nanostructures cluster to a specific target region. Functionalized magnetite nanostructures proved a great antimicrobial effect, being active against both the Gram positive pathogen S. aureus and the Gram negative pathogen E. coli. The fabricated nanostructures significantly reduced the minimum inhibitory concentration (MIC) of the active drug. This result has a great practical relevance, since the functionalized nanostructures may be used for decreasing the therapeutic doses which usually manifest great severe side effects, when administrated in high doses. Fe3O4@AMO represents also a suitable approach for the development of new alternative strategies for improving the activity of therapeutic agents by targeted delivery and controlled release.

Graphical Abstract

1. Introduction

The rate of development of bacterial resistance to current antibiotics is significantly higher than the rate at which researchers are producing novel antibiotics [1,2,3]. The most frequently encountered nosocomial pathogen exhibiting resistance and multi drug resistance (MDR) patterns is Staphylococcus aureus. This pathogen may be encountered on normal human skin and mucosa and has a great adaptability to antibiotic pressure [4]. Methicillin-resistant S. aureus (MRSA) represents one of the major etiology of severe hospital acquired infections and increased mortality in these patients [5].
Another commensal bacterium of humans and animals whose pathogenic variants may cause severe infections, including gastroenteritis, urinary tract infection, meningitis, peritonitis, and septicemia is Escherichia coli [6,7]. Surveillance data show that resistance in E. coli is consistently high for antimicrobial agents that have been in use for a long time in human and veterinary medicine, but also in food industry [8].
Some pathogens, such as the versatile Pseudomonas aeruginosa and Mycobacterium tuberculosis also possess a high level of intrinsic resistance, which is attributable to a concerted action of multidrug efflux pumps with chromosomally encoded antibiotic resistance genes and the low permeability of the bacterial cellular envelope [9,10].
Since the development of novel antimicrobial drugs is a very elaborate and costly process, research has focused on alternative methods for fighting infections. Using natural products and compounds may be an efficient approach in combating infections [11,12,13], but our current knowledge fails to ensure the success of a therapy based on these compounds in many conditions. This is because the lack of scientific evidence of the intimate mechanisms of action and their effect and distribution within the host. Another potentially efficient strategy relies on using magnetite nanosystems to improve the efficiency of current antimicrobials with proved effect [14,15,16,17,18,19,20,21,22,23,24,25].
The aim of this study was to synthesize, characterize and test the antimicrobial potentiating effect of a biocompatible Fe3O4-amoxicillin nanosystem, using both a Gram negative and a Gram positive bacteria model.

2. Results and Discussion

The crystalline properties of the prepared nanostructure (Fe3O4@AMO) were investigated by X-Ray diffraction (XRD). The XRD pattern of sample are shown in Figure 1 and all detectable peaks can be assigned to a pure cubic structured Fe3O4 (JCPDS no. 65-3107) [26]. No additional peaks have been observed indicating the formation of pure and single crystalline phase.
Figure 1. XRD patterns of Fe3O4@AMO and control Fe3O4.
Figure 1. XRD patterns of Fe3O4@AMO and control Fe3O4.
Molecules 19 05013 g001
Transmission electron microscopy allows obtaining information about the sizes and shapes of the prepared nanostructures. Figure 2 present the TEM images of the Fe3O4@AMO particles from which it can be seen that the crystalline particles are coated with a non-crystalline layer. The size of prepared particles is about 10 nm. No aggregates have been observed, the Fe3O4@AMO maintaining their nanometric size. The SAED rings, exhibit the high polycrystalline nature of the magnetite without the presence of any other crystalline phases [27].
Figure 3a presents the size distribution histogram of Fe3O4@AMO. The size distribution at 25 °C showed a hydrodynamic particle size average at 52 nm. Fe3O4@AMO exhibited a positive zeta potential of about 70 mV (Figure 3b), with a higher colloidal stability, being favorable for the electrostatic interaction with the negatively charged bacterial wall. This fact allows a better release of antibiotics inside the bacterial cell [21].
Figure 2. TEM images (a,b), HR-TEM image (c) and SAED pattern (d) of magnetite nanoparticles coated with amoxicillin (Fe3O4@AMO).
Figure 2. TEM images (a,b), HR-TEM image (c) and SAED pattern (d) of magnetite nanoparticles coated with amoxicillin (Fe3O4@AMO).
Molecules 19 05013 g002
Figure 3. DLS histogram (a) and zeta potential distribution (b) of the Fe3O4@AMO nanoparticles.
Figure 3. DLS histogram (a) and zeta potential distribution (b) of the Fe3O4@AMO nanoparticles.
Molecules 19 05013 g003
The TG analysis of the Fe3O4@AMO was performed in order to estimate the percent of AMO entrapped on the surface of Fe3O4 by comparison with the control (Fe3O4). The results of TG analysis are shown in Figure 4. The weight loss between 25 and 600 °C refers to the evaporation of adsorbed water and due to the decomposition of the physisorption and the chemisorption of the therapeutic agent [28,29]. Therefore, the content of the amoxicillin from Fe3O4@AMO was about 1.37%.
Figure 4. Thermogravimetric curves for magnetite nanoparticles with and without amoxicillin.
Figure 4. Thermogravimetric curves for magnetite nanoparticles with and without amoxicillin.
Molecules 19 05013 g004
Flow cytometry analysis revealed that the tested nanostructures (Fe3O4@AMO) have a great biocompatibility in vitro, allowing the normal development of cultured eukaryotic cells. The results demonstrated that the Fe3O4@AMO does not alter the normal progression of the cell cycle in cultured human cells, the percentage of cells encountered in different stages of cell cycle being similar with those obtained for the untreated control (Figure 5).
Figure 5. Flow cytometry results revealing the cell cycle progression of HCT8 cultured cells after the treatment for 24 h with the Fe3O4@AMO nanostructures. K = control HCT8 culture (untreated), Fe3O4 = HCT8 cultures grown in the presence of 1 mg/mL Fe3O4; Fe3O4@AMO = HCT8 cultures grown in the presence of 1 mg/mL Fe3O4@AMO. p < 0.5, based on One Way ANOVA test.
Figure 5. Flow cytometry results revealing the cell cycle progression of HCT8 cultured cells after the treatment for 24 h with the Fe3O4@AMO nanostructures. K = control HCT8 culture (untreated), Fe3O4 = HCT8 cultures grown in the presence of 1 mg/mL Fe3O4; Fe3O4@AMO = HCT8 cultures grown in the presence of 1 mg/mL Fe3O4@AMO. p < 0.5, based on One Way ANOVA test.
Molecules 19 05013 g005
The flow cytometry results were confirmed by the MTT assay (Figure 6) and microscopy data (Figure 7), which proved that endothelial cells grown in the presence of Fe3O4@AMO for up to five days have normal behavior and aspect, being similar to untreated control cells.
Figure 6. Graphic representation of the MTT results obtained by analyzing endothelial cells grown in the presence of tested Fe3O4@AMO for 24, 48 and 72 h.
Figure 6. Graphic representation of the MTT results obtained by analyzing endothelial cells grown in the presence of tested Fe3O4@AMO for 24, 48 and 72 h.
Molecules 19 05013 g006
Figure 7. Fluorescence microscopy images of endothelial cells grown in the presence of Fe3O4@AMO (a) and in standard conditions (b) at 5 days of incubation.
Figure 7. Fluorescence microscopy images of endothelial cells grown in the presence of Fe3O4@AMO (a) and in standard conditions (b) at 5 days of incubation.
Molecules 19 05013 g007
Despite their low effect on eukaryote cells, functionalized magnetite materials proved a great antimicrobial effect, being active against both the Gram-positive pathogen S. aureus and the Gram-negative pathogen E. coli. The results demonstrate that the tested nanostructures are very efficient in inhibiting bacteria growth, revealing a very low MIC value. Furthermore, the obtained MIC value for the Fe3O4@AMO proved to be significantly lower than the one obtained for the plain antibiotic solution (Figure 8 and Figure 9). The fabricated nanomaterials proved to reduce the necessary MIC of amoxicillin to about 3-fold for S. aureus and about 4-fold for E. coli.
The antimicrobial assay results demonstrate that these nanostructures also impacts on bacteria adherence. A concentration equal or higher to 2.142 µg/mL proved to be sufficient to inhibit the adherence of S. aureus on the bottom of the plate; while the minimum concentration necessary for adherence inhibition in E. coli proved to be 0.556 µg/mL (Figure 10 and Figure 11).
Figure 8. MIC values obtained for the nanoparticles functionalized with antibiotics against S. aureus ATCC 29213, as compared with control MIC values, represented by plain antibiotic solutions, ** p < 0.05.
Figure 8. MIC values obtained for the nanoparticles functionalized with antibiotics against S. aureus ATCC 29213, as compared with control MIC values, represented by plain antibiotic solutions, ** p < 0.05.
Molecules 19 05013 g008
Figure 9. MIC values obtained for the nanoparticles functionalized with antibiotics against E. coli ATCC 25922, as compared with control MIC values, represented by plain antibiotic solutions. *** p < 0.01.
Figure 9. MIC values obtained for the nanoparticles functionalized with antibiotics against E. coli ATCC 25922, as compared with control MIC values, represented by plain antibiotic solutions. *** p < 0.01.
Molecules 19 05013 g009
Figure 10. The effect of Fe3O4@AMO on S. aureus adherence at the inert substrata after 24 h of incubation.
Figure 10. The effect of Fe3O4@AMO on S. aureus adherence at the inert substrata after 24 h of incubation.
Molecules 19 05013 g010
This result demonstrates that the nanostructures may be efficiently used as targeted delivery nanoshuttles, and have a great potentiating effect on antibiotics’ activity. The fact that these nanostructures reduce the necessary amount of antibiotic for reaching the MIC effects has a great practical relevance, since it may be used for decreasing the therapeutic doses which usually manifest considerable and severe side effects, when administrated in high amounts. Fe3O4@AMO also represents a suitable approach for the development of new alternative strategies for improving the activity of therapeutic agents by targeted delivery and controlled release. Therefore, our results contribute to the current knowledge on the field of novel bio-active nanostructured materials and bring new insights within the development of efficient therapeutic strategies by stabilizing and lowering the amount of active compounds used for therapy. This approach may impact on economical, ecological and medical fields because the use of lower amounts of active compounds for treating bacterial infections with the same efficiency lead to decreased costs, lower toxicity and side effects, as well as a lower chemical pollution rate.
Figure 11. The effect of Fe3O4@AMO on E. coli adherence at the inert substrata after 24 h of incubation.
Figure 11. The effect of Fe3O4@AMO on E. coli adherence at the inert substrata after 24 h of incubation.
Molecules 19 05013 g011
The low cytotoxicity effects proved in vitro were confirmed also in vivo on a murine model. The results demonstrated that the Fe3O4@AMO nanostructures disperse through the host body and tend to localize in particular sites and organs. After 48 h of treatment with these dispersible nanoparticles, they were found clustered especially in the lungs, kidneys and spleen, while totally lacking in the brain and liver. The distribution of these nanostructures within the blood irrigated areas of these organs, suggest that they are circulated through the blood flow. This hypothesis is supported by the organ sections images that reveal a preferential localization of tested nanoparticles along the blood vessels (Figure 12). This observation is very useful for the development of therapeutic approaches for systemic and localized infections, because these nanostructures have the ability to be easily circulated and optimizations may be done so these nanostructures cluster to a specific target region. The results also revealed that the analyzed organs tissues are not affected after the treatment with the fabricated nanostructures, they manifesting a normal aspect. However, in the lungs it can be noticed an increased percent of inflammatory cells (as appreciated by comparing treating and untreated mice samples), as neutrophils and macrophages, and many of the observed macrophages contain high amounts of intracellular nanoparticles. The occurrence of an inflammatory process is although normal when injecting a foreign suspension within the body. No lesion typical or suggestive for tubular necrosis and glomerulopathy were observed in the kidneys, as revealed by the analyzed microscopy images obtained from tissue sections (Figure 12D).
Figure 12. Transversal sections through different mice organs (A = brain, B = liver, C = lung, D = kidney, E = spleen) in untreated control (1) and after the treatment with the obtained magnetite nanoparticles for 48 h (2); ×400 magnification.
Figure 12. Transversal sections through different mice organs (A = brain, B = liver, C = lung, D = kidney, E = spleen) in untreated control (1) and after the treatment with the obtained magnetite nanoparticles for 48 h (2); ×400 magnification.
Molecules 19 05013 g012

3. Experimental Section

3.1. Synthesis of Magnetite Nanostructures

All chemicals used in the experiments were of analytical reagent grade and were used without further purification. The protocol developed by Grumezescu et al. was used as the basic synthesis method of magnetite nanostructures [30,31]. Briefly, amoxicillin (AMO, 100 mg) and NH4OH (4 mL, 25%) were mixed in deionized water (400 mL) in order to prepare the alkali solution. FeCl3 (0.65 g,) and FeSO4 × 7H2O (1 g) aqueous solution (100 mL) was added drop by drop into alkali solution (400 mL) under vigorous stirring for 30 min at the room temperature. The pH value was higher than 12. A dark suspension of Fe3O4@AMO was obtained. In order to purify the prepared nanostructures, Fe3O4@AMO was separated with a strong NdFeB permanent magnet (100 Kgf), repeatedly washed with deionized water and methanol, and finally dried at room temperature.

3.2. Characterization of Magnetite Nanostructures

3.2.1. X-ray Diffraction

X-ray diffraction analysis was performed on a Shimadzu XRD 6000 diffractometer at room temperature. In all the cases, Cu Kα radiation from a Cu X-ray tube (run at 15 mA and 30 kV) was used. The samples were scanned in the Bragg angle 2θ range of 10–80 degree.

3.2.2. Transmission Electron Microscopy

The transmission electron microscopy (TEM) images were obtained on finely powdered samples using a Tecnai™ G2 F30 S-TWIN high resolution transmission electron microscope from FEI Company (Hillsboro, OR, USA) equipped with SAED. The microscope operated in transmission mode at 300 kV with TEM point resolution of 2 Å and line resolution of 1 Å. The microspheres were dispersed into pure ethanol and ultrasonicated for 15 min. After that, diluted sample was poured onto a holey carbon-coated copper grid and left to dry before TEM analysis.

3.2.3. Dynamic Light Scattering (DLS)

Particles size analysis was performed using intensity distribution by dynamic light scattering technique (Zetasizer Nano ZS, Malvern Instruments Ltd., Malvern, UK), at scattering angles of 90° and 25 °C. The average diameters (based on Stokes–Einstein equation) were calculated from three individual measurements. The zeta potential was measured using the Zetasizer Nano ZS.

3.2.4. Thermogravimetric Analysis

The thermogravimetric (TG) analysis of the biocomposite was assessed with a Shimadzu DTG-TA-50H instrument. Samples were screened to 200 mesh prior to analysis, were placed in alumina crucible, and heated with 10 K·min−1 from room temperature to 800 °C, under the flow of 20 mL·min−1 dried synthetic air (80% N2 and 20% O2).

3.2.5. Cell Cycle

HCT8 (ECAC90032006) line was cultivated in RPMI 1640 (Gibco, New York, NY, USA) supplemented with 10% heat-inactivated bovine serum and penicillin/streptomycin at 37 °C with 5% CO2. HCT8 cell line was treated with 100 µg/mL of the tested nanoparticles suspension, and maintained for 24 h at 37 °C, in 5% CO2 and humid atmosphere. After the incubation time, cells were harvested, washed with phosphate buffered saline (PBS) (pH 7.5), fixed in 70% cold ethanol and maintained overnight at −20 °C. Each sample was washed in PBS, treated with 100 µg/mL RNase A for 15 min and stained with 10 µg/mL propidium iodide by incubation at 37 °C for 1 h, following a protocol adapted from [32]. After propidium iodide staining of the cells, the events acquisition was done using an Epics Beckman Coulter flow cytometer. The obtained data were analysed using FlowJo software and expressed as fractions of cells in different cell cycle phases.

3.2.6. Cell Viability

Human endothelial cells (EAhy926 cell line, ATCC, Manassas, VA, USA) were grown in DMEM culture medium containing 10% FBS, and 1% penicillin and neomycin (Sigma Aldrich, St. Louis, MO, USA). For cell proliferation and viability was used CellTiter96 Non-Radioactive Cell Proliferation Assay, (Promega, Madison, WI, USA). Endothelial cells were seeded in 96-well plate at a density of 5 × 103 cells/well, in DMEM medium, supplemented with 10% FBS and incubated with NMS materials for 72 h, while the controls were represented by endothelial cells grown in the same culture conditions, but on bare substrates. Cell proliferation assay was performed in triplicates, according to manufacturer’s guidelines, at different time intervals. Briefly, 15 µL of Promega Kit Solution I was added in each well and incubated for 4 h. Furthermore, 100 µL of Promega Kit Solution II was added in the 96-well plate and incubated for another hour and spectrophotometry mesurements were performed at 570 nm using a Mithras LB 940 spectrophotometer (Berthold Technology, Bad Wildbad, Germany).
RED CMTPX fluorophore (Life Technologies, Invitrogen, Carlsbad, CA, USA) is a cell tracker for long-term tracing of living cells. The RED CMTPX dye was added in the culture medium at a final concentration of 5 µM, incubated 30 min for the dye to penetrate through the cells. Furthermore, the cells were washed with PBS and visualized by fluorescent microscopy. The nuclei were counterstaining with DAPI (1 mg/mL). Living cells tracing in the presence of nanospheres was monitored for 5 days in culture. The micrographs were taken by a digital camera driven by the Axio-Vision 4.6 (Carl Zeiss, Munich, Germany) software.

3.2.7. In Vivo Biodistribution

The experimental protocol was applied according with the European Council Directive No. 86/609/24 November 1986, the European Convention on the Protection of Vertebrate Animals (2005) and the Romanian Government Ordinance No. 37/2 February 2002. The mice organs were collected under general anesthesia. Biological material was fixed, directly after the sampling, in 10% buffered neutral formalin, for 72 h, at room temperature, and then processed for routinely histological paraffin embedding technique. For the histological study of nanoparticles, 4-μm thick serial sections were cut on a MICROM HM355s rotary microtome (MICROM International GmbH, Walldorf, Germany) equipped with a waterfall based section transfer system (STS, MICROM). The cross-sections were placed on histological blades treated with poly-L-Lysine (Sigma-Aldrich, Munich, Germany). After Hematoxylin–Eosin classical staining, cross-sections were evaluated and photographed using a Nikon Eclipse 55i light microscope equipped with a Nikon DS–Fi1 CCD high definition video camera (Nikon Instruments, Apidrag, Bucharest, Romania). Images were captured, stored and analyzed using Image ProPlus 7 AMS software (Media Cybernetics Inc., Marlow, Buckinghamshire, UK) [33,34].

3.2.8. Antimicrobial and Anti-Adherence Assay

S. aureus ATCC 25923 and E. coli ATCC 25922 were purchased from the American Type Cell Culture (ATCC). For establishing the minimal inhibitory concentration (MIC) of the tested nanoparticles, two-fold microdilutions of nanoparticles suspensions prepared in sterile saline buffer were done in nutrient broth previously distributed in 96 multi-well plates. Each sample was inoculated with 10 μL from S. aureus or E. coli microbial suspensions of a density corresponding to 0.5 McFarland (~108 bacterial cells). Negative and positive controls were used. The plates were incubated for 24 h at 37 °C, in order to establish the influence of different concentrations of nanoparticles solutions on the planktonic cells growth. The MICs were considered as the last dilution of each tested compound which inhibited the microbial growth.
Microbial adherence in the presence of fabricated magnetite nanostructures was analyzed in 6 multi-well plates (Nunc, Invitrogen, Bucharest, Romania). Different dilutions of the tested suspension containing fabricated nanoparticles were distributed in 96 well plates. 200 µL of S. aureus or E. coli inoculum with standard density of 1–3 × 104 CFU/mL were added in each well. Samples were incubated for 24 h at 37 °C. Adherence ability was analyzed after 24 h by crystal violet assay [35] the absorbance of the stained samples after acetic acid release was measured at 490 nm using a spectrophotometer.

4. Conclusions

This paper reports the successful fabrication of a biocompatible Fe3O4@AMO nanosystem, with great antimicrobial activity. This bio-active nanosized material proved to enhance the efficacy of low doses of amoxicillin against both the Gram negative pathogen E. coli and the Gram positive S. aureus. Furthermore, the obtained functionalized magnetite was proved to be well circulated through the mammalian body, offering the perspective of being used as an efficient drug delivery and controlled release nanosystem for active drugs in different localized infections.

Acknowledgments

This paper is supported by the PN-II-PT-PCCA-2011-3.2-0284: “Novel nanostructured prosthetic tubular devices with antibacterial and antibiofilm properties induced by physicochemical and morphological changes” funded by the National University Research Council in Romania. This work has been funded by the Prometeo Program, Secretary of superior education of Science, Technology and innovation of the Ecuador Republic.

Author Contributions

AMG and AMH conceived the study; MCG provided the microbial strains, and drafted the manuscript together with AMH and AMG. AMG and BSV performed the synthesis and characterization of Fe3O4@AMO. LM, CB, MCG, FI and GDM performed the in vivo and in vitro experiments. AMG and MCG participated in the design of the study and coordination. All authors read and approved the final manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

  1. Centers for Disease Control and Prevention. Antibiotic Resistance Questions & Answers. In Get Smart: Know When Antibiotics Work Homepage. Available online: http://www.cdc.gov/getsmart/antibiotic-use/antibiotic-resistance-faqs.html (accessed on 6 June 2009. Retrieved December 2013).
  2. Cartelle, M.; Canle, D.; Llarena, F.J.; Molina, F.; Villanueva, R.; Bou, G. Characterisation of the first CTX-M-10-producing isolate of Salmonella enterica serotype Virchow. Clin. Microbiol. Infect. 2006, 12, 285–287. [Google Scholar] [CrossRef]
  3. Cartelle, M.; del Mar Tomas, M.; Molina, F.; Moure, R.; Villanueva, R.; Bou, G. High-level resistance to ceftazidime conferred by a novel enzyme, CTX-M-32, derived from CTX-M-1 through a single Asp240-Gly substitution. Antimicrob. Agents Chemother. 2004, 48, 2308–2313. [Google Scholar] [CrossRef]
  4. Xie, J.; Pierce, J.G.; James, R.C.; Okano, A.; Boger, D.L. A redesigned vancomycin engineered for dual D-Ala-D-Ala and D-Ala-D-Lac binding exhibits potent antimicrobial activity against vancomycin-resistant bacteria. J. Am. Chem. Soc. 2011, 133, 13946–13949. [Google Scholar] [CrossRef]
  5. Boyle-Vavra, S.; Daum, R.S. Community-acquired methicillin-resistant Staphylococcus aureus: The role of Panton-Valentine leukocidin. Lab. Investig. 2007, 87, 3–9. [Google Scholar] [CrossRef]
  6. Sodha, S.V.; Lynch, M.; Wannemuehler, K.; Leeper, M.; Malavet, M.; Schaffzin, J. Multistate outbreak of Escherichia coli O157:H7 infections associated with a national fast-food chain, 2006: A study incorporating epidemiological and food source traceback results. Epidemiol. Infect. 2011, 139, 309–316. [Google Scholar] [CrossRef]
  7. Bou, G.; Cartelle, M.; Tomas, M.; Canle, D.; Molina, F.; Moure, R.; Eiros, J.M.; Guerrero, A. Identification and broad dissemination of the CTX-M-14 beta-lactamase in different Escherichia coli strains in the northwest area of Spain. J. Clin. Microbiol. 2002, 40, 4030–4036. [Google Scholar] [CrossRef]
  8. Tadesse, D.A.; Zhao, S.; Tong, E.; Ayers, S.; Singh, A.; Bartholomew, M.J.; McDermott, P.F. Antimicrobial drug resistance in Escherichia coli from humans and food animals, United States. Emerg. Infect. Dis. 2012, 18, 741–749. [Google Scholar] [CrossRef]
  9. Poole, K. Efflux-mediated multiresistance in Gram-negative bacteria. Clin. Microbiol. Infect. 2004, 10, 12–26. [Google Scholar] [CrossRef]
  10. Louw, G.E.; Warren, R.M.; Gey van Pittius, N.C.; McEvoy, C.R.E.; van Helden, P.D.; Victor, T.C. A balancing act: Efflux/influx in mycobacterial drug resistance. Antimicrob. Agents Chemother. 2009, 53, 3181–3189. [Google Scholar] [CrossRef]
  11. Grumezescu, A.M.; Vasile, B.S.; Holban, A.M. Eugenol functionalized magnetite nanostructures used in anti-infectious therapy. Lett. Appl. NanoBioSci. 2013, 2, 120–123. [Google Scholar]
  12. Holban, A.M.; Grumezescu, A.M.; Andronescu, E.; Grumezescu, V.; Chifiriuc, C.M.; Radulescu, R. Magnetite-usnic acid nanostructured bioactive material with antimicrobial activity. Rom. J. Mater. 2013, 43, 402–407. [Google Scholar] [CrossRef]
  13. Holban, A.M.; Grumezescu, A.M.; Ficai, A.; Chifiriuc, C.M.; Lazar, V.; Radulescu, R. Fe3O4@C18-carvone to prevent Candida tropicalis biofilm development. Rom. J. Mater. 2013, 43, 300–350. [Google Scholar]
  14. Chifiriuc, M.C.; Grumezescu, A.M.; Andronescu, E.; Ficai, A.; Cotar, A.I.; Grumezescu, V.; Bezirtzoglou, E.; Lazar, V.; Radulescu, R. Water dispersible magnetite nanoparticles influence the efficacy of antibiotics agains planktonic and biofilm embedded Enterococcus faecalis cells. Anaerobe 2013, 22, 14–19. [Google Scholar] [CrossRef]
  15. Grumezescu, A.M.; Cotar, A.I.; Andronescu, E.; Ficai, A.; Ghitulica, C.D.; Grumezescu, V.; Vasile, B.S.; Chifiriuc, M.C. In vitro activity of the new water dispersible Fe3O4@usnic acid nanostructure against planktonic and sessile bacterial cells. J. Nanopart. Res. 2013, 15, 1766. [Google Scholar] [CrossRef]
  16. Cotar, A.I.; Grumezescu, A.M.; Huang, K.-S.; Chifiriuc, C.M.; Radulescu, R. Magnetite nanoparticles influence the efficacy of antibiotics against biofilm embedded Staphylococcus aureus cells. Biointerface Res. Appl. Chem. 2013, 3, 559–565. [Google Scholar]
  17. Cotar, A.I.; Grumezescu, A.M.; Andronescu, E.; Voicu, G.; Ficai, A.; Ou, K.-L.; Huang, K.-S.; Chifiriuc, M.C. Nanotechnological solution for improving the antibiotic efficiency against biofilms developed by gram-negative bacterial strains. Lett. Appl. NanoBioSci. 2013, 2, 97–104. [Google Scholar]
  18. Grumezescu, A.M.; Andronescu, E.; Grumezescu, V.; Bleotu, C.; Saviuc, C.; Mihaiescu, D.E.; Chifiriuc, C.M. Biocompatible magnetic hollow silica microspheres for drug delivery. Curr. Org. Chem. 2013, 17, 1029–1033. [Google Scholar] [CrossRef]
  19. Grumezescu, A.M.; Andronescu, E.; Ficai, A.; Ficai, D.; Huang, K.S.; Gheorghe, I.; Chifiriuc, M.C. Water soluble magnetic biocomposite with potential applications for the antimicrobial therapy. Biointerface Res. Appl. Chem. 2012, 2, 469–475. [Google Scholar]
  20. Grumezescu, A.M.; Holban, A.M.; Andronescu, E.; Ficai, A.; Bleotu, C.; Chifiriuc, M.C. Water dispersible metal oxide nanobiocomposite as a potentiator of the antimicrobial activity of kanamycin. Lett. Appl. NanoBioSci. 2012, 1, 77–82. [Google Scholar]
  21. Grumezescu, A.M.; Andronescu, E.; Holban, A.M.; Ficai, A.; Ficai, D.; Voicu, G.; Grumezescu, V.; Balaure, P.C.; Chifiriuc, C.M. Water dispersible cross-linked magnetic chitosan beads for increasing the antimicrobial efficiency of aminoglycoside antibiotics. Int. J. Pharm. 2013, 454, 233–240. [Google Scholar] [CrossRef]
  22. Philosof-Mazor, L.; Dakwar, G.R.; Popov, M.; Kolusheva, S.; Shames, A.; Linder, C.; Greenberg, S.; Heldman, E.; Stepensky, D.; Jelinek, R. Bolaamphiphilic vesicles encapsulating iron oxide nanoparticles: New vehicles for magnetically targeted drug delivery. Int. J. Pharm. 2013, 450, 241–249. [Google Scholar] [CrossRef]
  23. Ladj, R.; Bitar, A.; Eissa, M.M.; Fessi, H.; Mugnier, Y.; le Dantec, R.; Elaissari, A. Polymer encapsulation of inorganic nanoparticles for biomedical applications. Int. J. Pharm. 2013, 458, 230–241. [Google Scholar] [CrossRef]
  24. Grumezescu, A.M.; Andronescu, E.; Ficai, A.; Bleotu, C.; Mihaiescu, D.E.; Chifiriuc, M.C. Synthesis, characterization and in vitro assessment of the magnetic chitosan–carboxymethylcellulose biocomposite interactions with the prokaryotic and eukaryotic cells. Int. J. Pharm. 2012, 436, 771–777. [Google Scholar] [CrossRef]
  25. Chifiriuc, M.C.; Grumezescu, A.M.; Saviuc, C.; Croitoru, C.; Mihaiescu, D.E.; Lazar, V. Improved antibacterial activity of cephalosporins loaded in magnetic chitosan microspheres. Int. J. Pharm. 2012, 436, 201–205. [Google Scholar] [CrossRef]
  26. Li, Y.; Jiangn, R.; Liu, T.; Lv, H.; Zhang, X. Single-microemulsion-based solvothermal synthesis of magnetite microflowers. Ceram. Int. 2014, 40, 4791–4795. [Google Scholar] [CrossRef]
  27. Jiang, W.; Wu, Y.; He, B.; Zeng, X.; Lai, K.; Gu, Z. Effect of sodium oleate as a buffer on the synthesis of superparamagnetic magnetite colloids. J. Colloid Interface Sci. 2010, 347, 1–7. [Google Scholar] [CrossRef]
  28. Voicu, G.; Grumezescu, V.; Andronescu, E.; Grumezescu, A.M.; Ficai, A.; Ghitulica, C.D.; Gheorghe, I.; Chifiriuc, M.C. Caprolactam-silica network, a strong potentiator of the antimicrobial activity of kanamycin against Gram-positive and Gram-negative bacterial strains. Int. J. Pharm. 2013, 446, 63–69. [Google Scholar] [CrossRef]
  29. Qian, Z.; Zhang, Z.; Chen, Y. A novel preparation of surface-modified paramagnetic magnetite/polystyrene nanocomposite microspheres by radiation-induced miniemulsion polymerization. J. Colloid Interface Sci. 2008, 327, 354–361. [Google Scholar] [CrossRef]
  30. Grumezescu, A.M.; Andronescu, E.; Ficai, A.; Mihaiescu, D.E.; Vasile, B.S.; Bleotu, C. Syntehsis, characterization and biological evaluation of Fe3O4/C12 core/shell nanosystem. Lett. Appl. NanoBioSci. 2012, 1, 31–35. [Google Scholar]
  31. Grumezescu, A.M.; Saviuc, C.; Chifiriuc, C.M.; Hristu, R.; Mihaiescu, D.E.; Balaure, P.; Stanciu, G.; Lazar, V. Inhibitory activity of Fe3O4/oleic acid/usnic acid—core/shell/extra-shell nanofluid on S. aureus biofilm development. IEEE Trans. NanoBioSci. 2011, 10, 269–274. [Google Scholar] [CrossRef]
  32. Krishan, A. Rapid flow cytofluorometric analysis of mammalian cell cycle by propidium iodide staining. J. Cell Biol. 1975, 66, 188–193. [Google Scholar] [CrossRef]
  33. Mogoşanu, G.D.; Popescu, F.C.; Busuioc, C.J.; Pârvănescu, H.; Lascăr, I. Natural products locally modulators of the cellular response: Therapeutic perspectives in skin burns. Rom. J. Morphol. Embryol. 2012, 53, 249–262. [Google Scholar]
  34. Mogoşanu, G.D.; Popescu, F.C.; Busuioc, C.J.; Lascăr, I.; Mogoantă, L. Comparative study of microvascular density in experimental third-degree skin burns treated with topical preparations containing herbal extracts. Rom. J. Morphol. Embryol. 2013, 54, 107–113. [Google Scholar]
  35. Saviuc, C.; Grumezescu, A.M.; Chifiriuc, M.C.; Bleotu, C.; Stanciu, G.; Hristu, R.; Mihaiescu, D.; Lazăr, V. In vitro methods for the study of microbial biofilms. Biointerface Res. Appl. Chem. 2011, 1, 31–40. [Google Scholar]
  • Sample Availability: Samples of the nanostructures are available from the authors.

Share and Cite

MDPI and ACS Style

Grumezescu, A.M.; Gestal, M.C.; Holban, A.M.; Grumezescu, V.; Vasile, B.Ș.; Mogoantă, L.; Iordache, F.; Bleotu, C.; Mogoșanu, G.D. Biocompatible Fe3O4 Increases the Efficacy of Amoxicillin Delivery against Gram-Positive and Gram-Negative Bacteria. Molecules 2014, 19, 5013-5027. https://doi.org/10.3390/molecules19045013

AMA Style

Grumezescu AM, Gestal MC, Holban AM, Grumezescu V, Vasile BȘ, Mogoantă L, Iordache F, Bleotu C, Mogoșanu GD. Biocompatible Fe3O4 Increases the Efficacy of Amoxicillin Delivery against Gram-Positive and Gram-Negative Bacteria. Molecules. 2014; 19(4):5013-5027. https://doi.org/10.3390/molecules19045013

Chicago/Turabian Style

Grumezescu, Alexandru Mihai, Monica Cartelle Gestal, Alina Maria Holban, Valentina Grumezescu, Bogdan Ștefan Vasile, Laurențiu Mogoantă, Florin Iordache, Coralia Bleotu, and George Dan Mogoșanu. 2014. "Biocompatible Fe3O4 Increases the Efficacy of Amoxicillin Delivery against Gram-Positive and Gram-Negative Bacteria" Molecules 19, no. 4: 5013-5027. https://doi.org/10.3390/molecules19045013

Article Metrics

Back to TopTop