Magnetism of Tetragonal β-Fe3Se4 Nanoplates Controllably Synthesized by Thermal Decomposition of (β-Fe2Se3)4[Fe(tepa)] Hybrid

We report magnetism of tetragonal β-Fe3Se4 nanoplates controllably synthesized by thermal decomposition at 603 K of inorganic–organic (β-Fe2Se3)4[Fe(tepa)] hybrid nanoplates (tepa = tetraethylenepentamine). (β-Fe2Se3)4[Fe(tepa)] hybrid precursor and β-Fe3Se4 nanoplates are in single crystal features as characterized by selected area electron diffraction. Rietveld refinements reveal that ordered inorganic–organic (β-Fe2Se3)4[Fe(tepa)] hybrid nanoplates are in a tetragonal layered crystal structure with a space group of I4cm (108) and room-temperature lattice parameters are a = 8.642(0) Å and c = 19.40(3) Å, while the as-synthetic tetragonal β-Fe3Se4 nanoplates have a layered crystal structure with the P4/nmm space group, and room-temperature lattice parameters are a = 3.775(8) Å and c = 5.514(5) Å. Magnetic measurements show the weak ferrimagnetism for (β-Fe2Se3)4[Fe(tepa)] hybrid nanoplates at room temperature, while the assynthetic β-Fe3Se4 nanoplates are antiferromagnetic in a temperature range between 120 and 420 K but in a ferrimagnetic feature below ~120 K. The as-synthetic β-Fe3Se4 nanoplates are thermally instable, which are transformed to ferrimagnetic β-Fe3Se4 nanoplates by annealing at 623 K (a little higher than the synthetic temperature). There is an irreversible change from antiferromagnetism of the as-synthetic β-Fe3Se4 phase to the ferrimagnetism of the as-annealed β-Fe3Se4 phase in a temperature between 420 and 470 K. Above 470 K, the tetragonal β-Fe3Se4 phase transforms to monoclinic Fe3Se4 phase with a Curie temperature (TC) of ~330 K. This discovery highlights that crystal structure and magnetism of Fe-Se binary compounds are highly dependent on both their phase compositions and synthesis procedures.


Introduction
The synthesis and characterization of iron selenides are interesting topics in materials sciences, due to their outstanding electrical and magnetic properties, which are sensitively dependent on their phase compositions and crystal structures [1][2][3][4]. It is known that hexagonal Fe 7 Se 8 is in the ferrimagnetism with the Curie temperature (T C ) at~460 K and a spin-reorientation occurs around 130 K for Fe 7 Se 8 [5], while monoclinic Fe 3 Se 4 has a T C at~320-340 K [4,6]. Due to large uniaxial magnetocrystalline anisotropy constant (1 × 10 7 erg/cm 3 at 10 K), Fe 3 Se 4 nanostructures [7,8] and Cr-doped Fe 3 Se 4 compounds [9,10] have received attention owing to the realization of a large coercivity as potential rare-Earth-free permanent magnets. The ferrimagnetism of Fe 3 Se 4 and Fe 7 Se 8 originates from the ferromagnetically aligned spins within the c-plane and antiferromagnetically coupled adjacent Fe planes with ordered iron vacancies [11]. Tetragonal β-FeSe with a PbO structure is intriguing for the simplest layered crystal structure with the P4/nmm space group in the iron-based superconductors [2]. The superconductivity of β-FeSe is sensitively dependent on the crystal structure [12] and stoichiometry [13]. Theoretical studies show that tetragonal β-FeSe is nonmagnetic, but ferromagnetism is present in the hexagonal NiAs-type α-FeSe with the T C of 420 K [14]. Se-rich FeSe films exhibit a ferrimagnetic order with the T C~3 25 K [15], but ordered Fe vacancies lead to composition-dependent antiferromagnetic orders for some tetragonal β-Fe 1−x Se (0 < x < 0.2) superstructures, such as β-Fe 4 Se 5 , at low temperatures [13,16]. However, the effect of the composition x on the magnetism of β-Fe 1−x Se was not studied enough due to difficult synthesis for single phase β-Fe 1-x Se. β-Fe 3 Se 4 superstructures serve as components in the intercalated compound TlFe 1.5 Se 2 , which show two possible states, in which the square superstructure of √ 2 × √ 2 has lower energy than the rhombus ordered pattern ( √ 2 × 2 √ 2 ) [17]. Antiferromagnetic order of AFe 1.5 Se 2 (A = Tl, K, Rb, or Cs) is driven by the Se-bridged antiferromagnetic superexchange interactions between Fe moments [17]. The selected area electron diffraction (SAED) pattern of square β-Fe 3 Se 4 superstructure along the c-axis is similar to that of superconducting tetragonal β-FeSe, except that the absented (h00) and (0k0) with h odd and k odd are now visible due to Fe vacancy order [16]. A previous work reveals that FeSe 2 chains were used to coordinate with Fe-amine (amine = ethylenediamine (en), diethylenetriamine (dien) or tris(2-aminoethyl)amine (tren)) complexes for hybrid (FeSe 2 ) 2 [Fe(en) 2 ] [18], (FeSe 2 ) 2 [Fe(dien) 2 ] and (FeSe 2 ) 2 [Fe(tren)] [19]. More recently, we reported that tetragonal β-Fe 3 Se 4 superstructures can be used as inorganic building units to construct the room temperature ferrimagnetic (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] (teta = triethylenetetramine) [20]. Moreover, the FeSe x inorganic building units can be changed from FeSe 2 chains to β-Fe 2 Se 3 and β-Fe 3 Se 4 by tuning the stoichiometric ratio of Fe and Se precursors in the organic diethylenetriamine (dien) system [21]. However, the monoclinic phase of Fe 3 Se 4 but not tetragonal phase was obtained by direct thermal decomposition of the (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] and the Fe 3 Se 4 (dien) 2 hybrid materials at a temperature higher than their decomposition temperatures [20,21]. There was previously a rare report on the magnetic information of tetragonal β-Fe 3 Se 4 single phase [16].
Here, we design and synthesize a new ordered inorganic-organic (β-Fe 2 Se 3 ) 4 [Fe(tepa)] hybrid material. Tetragonal β-Fe 3 Se 4 nanoplates were synthesized by thermal decomposition of the hybrid precursor in a tepa solution at 603 K. Tetragonal β-Fe 3 Se 4 nanoplates show interesting magnetism due to tetragonal crystal structure and disordered distribution of iron vacancies, which is much different from that of monoclinic Fe 3 Se 4 . Our study provides guidance for future applications in such a chemical solution for controllable synthesis of tetragonal β-Fe 1−x Se functional materials in a wide composition range with varied crystal structure but the same composition.
In a typical reaction for a new ordered inorganic-organic (β-Fe 2 Se 3 ) 4 [Fe(tepa)] hybrid material, 2162.7 mg of Fe(acac) 3 and 888.3 mg of SeO 2 with the Fe/Se molar ratio of 6:8 were mixed in 80 mL of tepa in a 250 mL four-neck flask. Under a nitrogen flow, the mixture solution was heated to 393 K and kept for 1 h to remove moisture and oxygen. Then, the temperature was slowly raised to 573 K in a period time of 50 h and maintained for 3 h to obtain product with good crystallization. The solution was cooled to room temperature by removing the heating source. The precipitates were separated from reaction solution by centrifugation at 8000 rpm. A ThermoFisher inductively coupled plasma (ICP) spectroscopy gave a concentration of 0.0208 and 0.0715 mg mL −1 , respectively for Fe and Se ions left in the yellow transparent supernatant above the precipitates, suggesting that all the Fe and Se atoms in the starting materials have combined in the hybrid product. The precipitates were rewashed by 15 mL of acetone for four times.
For the synthesis of tetragonal Fe 3 Se 4 nanoplates, the hybrid precursor was dispersed in 80 mL of tepa in a 250 mL four-neck flask. Under a nitrogen flow, the mixture solution was heated to 573 K at a ramping rate of 10 K min −1 and kept for 3 h. Then, the temperature was raised to 603 K in a period time of 12 h and maintained for 3 h. Finally, the product was cooled to room temperature by removing the heating source. The resultant product was precipitated by centrifugation at 8000 rpm and washed with 15 mL of acetone for five times. Both the hybrid precursor and the thermal decomposed product were dried in vacuum at room temperature and store in a glovebox with an argon atmosphere for further characterization.
Powder X-ray diffraction (XRD) was performed on a D/Max-2400 diffractometer (Rigaku Inc., Tokyo, Japan) equipped with a Cu K α radiation source at room temperature. The program Rietica was used to refine the crystal structure of the products. The size and morphology of the products were examined by a JSM 6301F field-emission scanning electron microscope (FESEM) (JEOL Inc., Tokyo, Japan) system and a Tecnai G2 F20 transmission electron microscope (TEM) (FEI Inc., Hillsboro, OR, USA) at 200 kV. The Fourier transform infrared (FTIR) spectrum was recorded on a Nicolet iN10 MX & iS10 spectrometer using the KBr pellet technique (Thermo Fisher Inc., Waltham, MA, USA). Elemental compositions of the products were analyzed by an Oxford energy dispersive X-ray (EDX) spectroscopy. Thermal gravimetric analysis (TGA) was carried out on a STA6000 thermal analyzer (PerkinElmer Inc., Waltham, MA, USA) with heating rate of 10 K min −1 between 300 and 800 K. Temperature-dependent magnetization in the field-cooling (FC) and zerofield-cooling (ZFC) modes (H = 0.1 and 50 kOe) and static magnetic measurements of the products were performed using a vibrating sample magnetometer (VSM) standard option in a physical property measurement system (PPMS) (Quantum Design Inc., San Diego, CA, USA) equipped with a superconducting magnet with a maximum magnetic field of 140 kOe in a temperature range between 5 and 400 K. The magnetization versus temperature curves of the Fe 3 Se 4 nanoplates in a temperature range between 300 and 720 K were collected using the VSM with the oven option in a high vacuum state during the oven operation. Figure 1a) and TEM images ( Figure 1b) illustrate that the hybrid precursor possesses a square plate shape with a size of about 70-100 nm for thickness and 1-6 µm for length. Fourier transform infrared (FTIR) spectrum ( Figure 2) presents characteristic peaks of tepa featured by the vibration bands of -CH 2 -, -NH 2 , and -NH. The bands at 2915, 2860 and 1453 cm −1 are ascribed to the stretching vibration and C-H deformation of −CH 2 in the tepa chain. Two bands at 3436 and 3273 cm −1 are caused by asymmetric and symmetric bending vibrations of −NH 2 , while the band at 1110 cm −1 is due to C−N stretching vibration in tepa. The band of 1613 cm −1 in the hybrid nanoplates is attributed to the bending vibrations of N−H in tepa, which is larger than the value (1591 cm −1 ) for raw tepa solvent, indicating the complexation of tepa with iron ions and the elongation of N−H bonds. It reveals the presence of organic tepa in the hybrid material. The relative molar ratio of Fe to Se in the hybrid nanoplates was examined by EDX elemental analysis (the inset of Figure 1a). The presence of Fe and Se as the only heavy elements is observed in the EDX spectrum, and the Fe/Se average atomic ratio is determined to be 43.23/56.77 (3.04:4) in good agreement with the stoichiometric ratio of Fe and Se in the starting materials. TGA curve in Figure 3a shows a small weight loss (~2.8 wt%) from room temperature to~570 K due to a small amount of free tepa and other organic solvents absorbed on the surface of the hybrid nanoplates, and a sharp weight loss (13.1 wt%) between the onset temperature (T onset ) of~570 K and the end temperature (T end ) of 726 K for decomposition, due to the loss of the bonded tepa and a small amount of Se. Figure 3b represents that the product heated at 673 K consists of tetragonal β-Fe 3 Se 4 nanoplates and monoclinic Fe 3 Se 4 , while that heated at 723 K consists of tetragonal β-Fe 3 Se 4 nanoplates, monoclinic Fe 3 Se 4 and hexagonal Fe 7 Se 8 . Monoclinic Fe 3 Se 4 may be generated by a structural transition from the tetragonal β-Fe 3 Se 4 . Hexagonal Fe 7 Se 8 was produced by a little loss of Se from these Fe 3 Se 4 nanoplates. A phase transformation from monoclinic Fe 3 Se 4 (T C = 334 K) to hexagonal Fe 7 Se 8 (T C = 460 K) was observed in the thermal decomposition product of (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] due to loss of a slight Se [20]. According to Figure 3b, the thermal decomposition of hybrid precursor should be complete below 673 K and weight loss around 673 K was resulted from evaporation of tepa. The molar ratio of Fe 3 Se 4 to tepa in the hybrid precursor was suggested to be calculated by removing the influence of the small amount of Se on the weight loss. We suppose that below 685 K, only a little higher than 673 K, there was no Se loss from both the tetragonal Fe 3 Se 4 and the monoclinic Fe 3 Se 4 nanoplates. As a result, the TG analysis would give a molar ratio of 3:1 for Fe 3 Se 4 to tepa in the hybrid precursor. It suggests a chemical formula of (Fe 3 Se 4 ) 3 tepa for the present hybrid precursor. ature to ~570 K due to a small amount of free tepa and other organic solvents absorbed on the surface of the hybrid nanoplates, and a sharp weight loss (13.1 wt%) between the onset temperature (Tonset) of ~570 K and the end temperature (Tend) of 726 K for decomposition, due to the loss of the bonded tepa and a small amount of Se. Figure 3b represents that the product heated at 673 K consists of tetragonal β-Fe3Se4 nanoplates and monoclinic Fe3Se4, while that heated at 723 K consists of tetragonal β-Fe3Se4 nanoplates, monoclinic Fe3Se4 and hexagonal Fe7Se8. Monoclinic Fe3Se4 may be generated by a structural transition from the tetragonal β-Fe3Se4. Hexagonal Fe7Se8 was produced by a little loss of Se from these Fe3Se4 nanoplates. A phase transformation from monoclinic Fe3Se4 (TC = 334 K) to hexagonal Fe7Se8 (TC = 460 K) was observed in the thermal decomposition product of (β-Fe3Se4)4[Fe(teta)1.5] due to loss of a slight Se [20]. According to Figure 3b, the thermal decomposition of hybrid precursor should be complete below 673 K and weight loss around 673 K was resulted from evaporation of tepa. The molar ratio of Fe3Se4 to tepa in the hybrid precursor was suggested to be calculated by removing the influence of the small amount of Se on the weight loss. We suppose that below 685 K, only a little higher than 673 K, there was no Se loss from both the tetragonal Fe3Se4 and the monoclinic Fe3Se4 nanoplates. As a result, the TG analysis would give a molar ratio of 3:1 for Fe3Se4 to tepa in the hybrid precursor. It suggests a chemical formula of (Fe3Se4)3tepa for the present hybrid precursor.        A SAED image of a hybrid nanoplate in Figure 1c reveals periodic crystal structure along the thickness direction. Compared to the previous (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] [20], a little obscure diffraction points marked by red circles in the SAED image may be caused by more iron vacancies in the hybrid nanoplate. Powder XRD pattern of the hybrid material ( Figure 4a) reveals that all Bragg diffraction peaks can be refined and indexed by using the tetragonal structure with the space group I4cm (No. 108). The corresponding refinement process gave good R factors (R p = 6.046%, R wp = 9.609% and χ 2 = 1.732) and the crystal structure of the (Fe 3 Se 4 ) 3 tepa hybrid nanoplates is the same as that for previous (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] [20], in which two independent subsystems have been identified: β-Fe 3 Se 4 superstructure and Fe(teta) 1.5 complex. Refined room-temperature lattice parame-ters of the hybrid material are a = 8.642(0) Å and c = 19.40(3) Å, about 0.6% and 6.8% shrinkage along the a and c axes, respectively, compared with that of (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] [20]. The Fe/Se molar ratio in this hybrid material is 3:4, which deviates much from 3.25:4 for the (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ], demonstrating that the inorganic building units in the present hybrid material differ from the β-Fe 3 Se 4 superstructures. Based on the electron diffraction analysis on the tetragonal β-Fe 1−x Se (0.1 ≤ x ≤ 0.5) superstructures in the reference [16] and our previous works [20,21], the tetragonal β-Fe 2 Se 3 (x = 0.333) superstructure is the only possible fragment built in the present hybrid material. The SAED for β-Fe 2 Se 3 superstructure is different from that of β-Fe 3 Se 4 superstructures due to more ordered iron vacancies in β-Fe 2 Se 3 than in β-Fe 3 Se 4 . However, when a SAED was taken along the c axis or the thickness direction of the present layered hybrid nanoplate, Fe atoms in [Fe(tepa)] 2+ complexes that overlap on iron vacancies of tetragonal β-Fe 2 Se 3 superstructures could influence the observation of iron vacancy order of tetragonal β-Fe 2 Se 3 . As a result, Figure 1c represents a SAED image similar to that of β-Fe 3 Se 4 superstructure. With the consideration of the unit cell size, atom composition, inorganic/organic unit molar ratio and electrical neutrality principles, we suggest that the most possible coordination for this new hybrid material is  [21]. SEM image (Figure 1d) illustrates that the β-Fe 3 Se 4 nanoplates synthesized by thermal decomposition of hybrid nanoplates at 603 K are in a square shape with a varied particle size from several hundred nanometers to 3 µm. The thicknesses of some β-Fe 3 Se 4 nanoplates are obviously bigger than those of hybrid precursor, possibly due to thermal decomposition of several adjacent hybrid nanoplates to a β-Fe 3 Se 4 nanoplate. From the EDX spectrum (the inset of Figure 1d), the Fe/Se atomic ratio is determined in average to be 42.99/57.01 (3.01:4) for the synthetic β-Fe 3 Se 4 nanoplates, which is in good agreement with the stoichiometric ratio of Fe and Se in the hybrid precursor. The oxidation states of Fe and Se species have been evaluated by X-ray photoelectron spectroscopy (XPS) ( Figure 5). The binding energies of C 1s at about 285 and 285.5 eV in Figure 5a revealed the amorphous carbon and the C-N in tepa [22] absorbed on the surface of the as-synthetic β-Fe 3 Se 4 nanoplates. Based on the calibration of amorphous carbon at 285 eV, the Fe 2p and the Se 3d spectra were shown in Figure 5b,c, respectively. The Fe 2p spectrum (Figure 5b) contains two asymmetric peaks due to the spin-orbit splitting, which can be assigned to Fe 2p 3/2 at 711.0 eV and Fe 2p 1/2 at 724.7 eV. Both Fe 2p 3/2 and Fe 2p 1/2 peaks can be further deconvoluted into two sub-peaks Fe 2+ (2p 3/2 at 710.0 eV, 2p 1/2 at 723.6 eV) and Fe 3+ (2p 3/2 at 711.8 eV, 2p 1/2 at 725.4 eV) [23]. Satellite peaks can be detected at 715.9 and 719.5 eV for Fe 2+ 2p 3/2 and Fe 3+ 2p 3/2 , respectively. According to the fitting area for the Fe 2+ and Fe 3+ ions, the molar ratio of Fe 2+ /Fe 3+ in the as-synthetic β-Fe 3 Se 4 nanoplates was estimated to be 1:1.9, which is close to the Fe 2+ /Fe 3+ of 1:2 for β-Fe 3 Se 4 based on the electrical neutrality principles. Figure 5c shows the Se 3d peak at 55.1 eV, indicating the presence of Se-Fe-Se [24,25], which could be deconvoluted into Se 3d 5/2 at 54.7 eV and Se 3d 3/2 at 55.6 eV. For the β-Fe 3 Se 4 nanoplates annealed at 623 K, the C 1s (at 285 and 285.5 eV), Fe 2p with Fe 2+ (2p 3/2 at 710.2 eV, 2p 1/2 at 723.8 eV) and Fe 3+ (2p 3/2 at 711.8 eV and 2p 1/2 at 725.4 eV) and Se 3d (3d 5/2 at 55.1 eV and 3d 3/2 at 56.0 eV) spectra were also analyzed and presented in Figure 5d-f, which are similar to the results of the as-synthetic β-Fe 3 Se 4 nanoplates. Moreover, the satellite peaks can be detected at 715.2 and 719.7 eV for Fe 2+ 2p 3/2 and Fe 3+ 2p 3/2 in the annealed sample, respectively. TEM image (Figure 1e) and the corresponding SAED pattern (Figure 1f) reveal periodic crystal structure of a β-Fe 3 Se 4 nanoplate in the thickness direction along the c axis. Compared to the SAED pattern of the hybrid precursor (Figure 1c), the diffraction points for the β-Fe 3 Se 4 nanoplate become clear and distinguishable (Figure 1f). However, the SAED pattern is similar to the superconducting β-FeSe nanosheets reported previously [13], but much different from that of β-Fe 3 Se 4 superstructure with ordered iron vacancies in the (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] [20]. The formation of β-Fe 3 Se 4 nanoplates may follow a thermal decomposition reaction of (Fe 2 Se 3 ) 4 [Fe(tepa)] = 4Fe 2 Se 3 + Fe + tepa and a diffusion reaction of 4Fe 2 Se 3 + Fe = 3Fe 3 Se 4 . During the reactions, Fe atoms produced by thermal decomposition of [Fe(tepa)] 2+ complexes may randomly diffuse and fill in the iron vacancies of β-Fe 2 Se 3 , which would create a random distribution of iron vacancies in the as-synthetic β-Fe 3 Se 4 nanoplates. As a result, the absented (h00) and (0k0) with h odd and k odd originating from iron vacancy order are not visible again in the SAED of our as-synthetic β-Fe 3 Se 4 nanoplates recorded along the c direction, which is much different from that of previous β-Fe 3 Se 4 superstructure with iron vacancy order [20]. The XRD of the as-synthetic β-Fe 3 Se 4 nanoplates was refined in Figure 4b based on the model for the β-FeSe [2,13]. The corresponding refinement process gave good R factors (R p = 3.557%, R wp = 5.099% and χ 2 = 0.657) and refined lattice parameters at room temperature are a = 3.775(8) Å and c = 5.514(5) Å for the as-synthetic β-Fe 3 Se 4 nanoplates, about 0.28% expansion along the a and b axes due to Fe vacancies but almost the same along the c axis comparing with that of superconducting β-FeSe [13]. The disordered distributions of iron vacancies are currently under investigation. SEM image (Figure 1d) illustrates that the β-Fe3Se4 nanoplates synthesized by thermal decomposition of hybrid nanoplates at 603 K are in a square shape with a varied particle size from several hundred nanometers to 3 µm. The thicknesses of some β-Fe3Se4 nanoplates are obviously bigger than those of hybrid precursor, possibly due to thermal decomposition of several adjacent hybrid nanoplates to a β-Fe3Se4 nanoplate. From the EDX spectrum (the inset of Figure 1d), the Fe/Se atomic ratio is determined in average to be 42.99/57.01 (3.01:4) for the synthetic β-Fe3Se4 nanoplates, which is in good agreement

Magnetic Properties
Figure 6a presents isothermal field (H) dependence of magnetization (M) of the hybrid precursor, showing a weak ferromagnetic feature at a low magnetic field range. The small hysteresis loops of the hybrid material reveal the ferromagnetic characteristics in the temperature range between 10 K and 370 K. The coercivity (HC) and remanence magnetization are 297 Oe and 0.006 emu g −1 at 370 K, respectively, which increase to 309 Oe and 0.017 emu g −1 at 10 K. The magnetizations at a high magnetic field range increase linearly with increasing the magnetic field even up to the maximum magnetic field of 50 kOe. This linear field dependence of the magnetization at high field range is not contrary to the ferrimagnetic compounds, in which strong antiferromagnetic coupling between different magnetic sublattices prevents their full alignment by the magnetic field [20]. Figure 6b presents the temperature (T) dependence of magnetization of the hybrid material recorded from 10 and 370 K in the ZFC/FC processes under a magnetic field of 0.1 and 50 kOe, respectively. The ZFC/FC curves at a magnetic field of 0.1 kOe exhibit a divergence below ~250 K, while the divergence temperature decreases to ~60 K as the ZFC/FC curves were measured in a high magnetic field of 50 kOe. The FC curve shows a smooth decrease in magnetization with raising the temperature from 10 to 370 K. It suggests no magnetic transition of this hybrid precursor below 370 K, and its TC should be higher than 370 K. Such a room-temperature ferrimagnetic behavior is similar to those of our previous ordered inorganic-organic hybrid materials (β-Fe3Se4)4[Fe(teta)1.5] and the Fe3Se4(dien)2 [20,21].

Magnetic Properties
Figure 6a presents isothermal field (H) dependence of magnetization (M) of the hybrid precursor, showing a weak ferromagnetic feature at a low magnetic field range. The small hysteresis loops of the hybrid material reveal the ferromagnetic characteristics in the temperature range between 10 K and 370 K. The coercivity (H C ) and remanence magnetization are 297 Oe and 0.006 emu g −1 at 370 K, respectively, which increase to 309 Oe and 0.017 emu g −1 at 10 K. The magnetizations at a high magnetic field range increase linearly with increasing the magnetic field even up to the maximum magnetic field of 50 kOe. This linear field dependence of the magnetization at high field range is not contrary to the ferrimagnetic compounds, in which strong antiferromagnetic coupling between different magnetic sublattices prevents their full alignment by the magnetic field [20]. Figure 6b presents the temperature (T) dependence of magnetization of the hybrid material recorded from 10 and 370 K in the ZFC/FC processes under a magnetic field of 0.1 and 50 kOe, respectively. The ZFC/FC curves at a magnetic field of 0.1 kOe exhibit a divergence below 250 K, while the divergence temperature decreases to~60 K as the ZFC/FC curves were measured in a high magnetic field of 50 kOe. The FC curve shows a smooth decrease in magnetization with raising the temperature from 10 to 370 K. It suggests no magnetic transition of this hybrid precursor below 370 K, and its T C should be higher than 370 K. Such a room-temperature ferrimagnetic behavior is similar to those of our previous ordered inorganic-organic hybrid materials (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] and the Fe 3 Se 4 (dien) 2 [20,21].   Figure 7a shows that both ZFC and FC magnetizations recorded at a magnetic field of 50 kOe in a temperature range from 10 to 370 K decrease with increasing the temperature to about 140 and then increase to 370 K. Such a behavior is also observed in the FC magnetization curve in a magnetic field of 140 kOe with an inflection point temperature shifting to about 125 K High-temperature magnetization measurements in Figure 7b show reversible tempera ture dependence of magnetization below 420 K, which becomes irreversible above 420 K It indicates that the as-synthetic β-Fe3Se4 nanoplates are metastable at room temperature and their magnetism changes at a temperature higher than 420 K. Isothermal field de pendence of magnetization between −50 and 50 kOe in Figure 7c shows a weak S-shape in the MH curve recorded at 140 K and a small hysteresis loop at 10 K, suggesting a weak ferromagnetic feature of the as-synthetic β-Fe3Se4 nanoplates below 140 K. Above this temperature, a linear field dependence of magnetization was observed in the MH curves recorded at a temperature between 300 and 320 K (Figure 7c). The linear field depend ence of magnetization was also observed at 370 K and higher magnetic field ranges from −140 to 140 kOe (Figure 7d). Considering the increase in magnetization with increasing the temperature from 140 to 420 K (Figure 7a,b), the linear field dependence of magneti zation suggests an antiferromagnetism of the as-synthetic β-Fe3Se4 nanoplates. Hysteresis loop recorded after field-cooled from 370 to 10 K at 140 kOe shows an exchange bias ef fect with a coercivity of 7.83 kOe and an exchange bias field of 2.55 kOe (Figure 7d), fur ther revealing the presence of ferromagnetic and antiferromagnetic components in the as-synthetic β-Fe3Se4 nanoplates. The disordered distribution of iron vacancies in the as-synthetic β-Fe3Se4 nanoplates may be the reason that creates the different magnetic spin configurations. Besides a magnetic irreversibility (Figure 7b), temperature depend ence of magnetization in the process cooling from 470 to 300 K shows no magnetic tran   Figure 7a shows that both ZFC and FC magnetizations recorded at a magnetic field of 50 kOe in a temperature range from 10 to 370 K decrease with increasing the temperature to about 140 and then increase to 370 K. Such a behavior is also observed in the FC magnetization curve in a magnetic field of 140 kOe with an inflection point temperature shifting to about 125 K. High-temperature magnetization measurements in Figure 7b show reversible temperature dependence of magnetization below 420 K, which becomes irreversible above 420 K. It indicates that the as-synthetic β-Fe 3 Se 4 nanoplates are metastable at room temperature and their magnetism changes at a temperature higher than 420 K. Isothermal field dependence of magnetization between −50 and 50 kOe in Figure 7c shows a weak S-shape in the MH curve recorded at 140 K and a small hysteresis loop at 10 K, suggesting a weak ferromagnetic feature of the as-synthetic β-Fe 3 Se 4 nanoplates below 140 K. Above this temperature, a linear field dependence of magnetization was observed in the MH curves recorded at a temperature between 300 and 320 K (Figure 7c). The linear field dependence of magnetization was also observed at 370 K and higher magnetic field ranges from −140 to 140 kOe (Figure 7d). Considering the increase in magnetization with increasing the temperature from 140 to 420 K (Figure 7a,b), the linear field dependence of magnetization suggests an antiferromagnetism of the as-synthetic β-Fe 3 Se 4 nanoplates. Hysteresis loop recorded after field-cooled from 370 to 10 K at 140 kOe shows an exchange bias effect with a coercivity of 7.83 kOe and an exchange bias field of 2.55 kOe (Figure 7d), further revealing the presence of ferromagnetic and antiferromagnetic components in the assynthetic β-Fe 3 Se 4 nanoplates. The disordered distribution of iron vacancies in the assynthetic β-Fe 3 Se 4 nanoplates may be the reason that creates the different magnetic spin configurations. Besides a magnetic irreversibility (Figure 7b), temperature dependence of magnetization in the process cooling from 470 to 300 K shows no magnetic transition for the β-Fe 3 Se 4 sample. However, after the sample was heated to 600 K, a magnetic transition was observed at about 335 K in the cooling process from 600 to 300 K. Such a magnetic transition temperature is in good agreement with the T C for monoclinic Fe 3 Se 4 [8], suggesting that a crystal structure transition from tetragonal β-Fe 3 Se 4 to monoclinic Fe 3 Se 4 occurred in the high-temperature magnetic measurement.
Magnetism 2022, 1, FOR PEER REVIEW 11 transition was observed at about 335 K in the cooling process from 600 to 300 K. Such a magnetic transition temperature is in good agreement with the TC for monoclinic Fe3Se4 [8], suggesting that a crystal structure transition from tetragonal β-Fe3Se4 to monoclinic Fe3Se4 occurred in the high-temperature magnetic measurement.  Figure 7b shows a thermal instability of the as-synthetic β-Fe3Se4 nanoplates at a temperature higher than 420 K. To examine the magnetic irreversibility in the heating process from 300 to 470 K and in the cooling process from 470 to 300 K, we annealed the as-synthetic β-Fe3Se4 nanoplates in a sealed SiO2 tube in an argon atmosphere at 623 K (just a little higher than the synthetic temperature of 603 K) for 1 h. Figure 4c represents the XRD pattern of the annealed β-Fe3Se4 nanoplates. The corresponding refinement process gave good R factors (Rp = 5.098%, Rwp = 6.851% and χ 2 = 1.774) for the annealed sample. In the case of the annealed β-Fe3Se4 nanoplates, refined lattice parameters at room temperature are a = 3.779(3) Å and c = 5.513(8) Å, almost the same as those of the as-synthetic material. Both the XRD pattern ( Figure 4c) and the structure characteristics (Figure 1g-i) for the annealed sample are similar to those of the as-synthetic β-Fe3Se4 nanoplates, indicating few changes in the unit cell parameters. Figure 8a plots the tem-  Figure 7b shows a thermal instability of the as-synthetic β-Fe 3 Se 4 nanoplates at a temperature higher than 420 K. To examine the magnetic irreversibility in the heating process from 300 to 470 K and in the cooling process from 470 to 300 K, we annealed the as-synthetic β-Fe 3 Se 4 nanoplates in a sealed SiO 2 tube in an argon atmosphere at 623 K (just a little higher than the synthetic temperature of 603 K) for 1 h. Figure 4c represents the XRD pattern of the annealed β-Fe 3 Se 4 nanoplates. The corresponding refinement process gave good R factors (R p = 5.098%, R wp = 6.851% and χ 2 = 1.774) for the annealed sample. In the case of the annealed β-Fe 3 Se 4 nanoplates, refined lattice parameters at room temperature are a = 3.779(3) Å and c = 5.513(8) Å, almost the same as those of the as-synthetic material. Both the XRD pattern ( Figure 4c) and the structure characteristics (Figure 1g-i) for the annealed sample are similar to those of the as-synthetic β-Fe 3 Se 4 nanoplates, indicating few changes in the unit cell parameters. Figure 8a plots the temperature dependence of magnetization of the annealed β-Fe 3 Se 4 nanoplates recorded in the ZFC/FC curves between 10 and 370 K under a magnetic field of 0.1 and 50 kOe, respectively. The ZFC/FC curves under 0.1 kOe exhibit a divergence below~250 K, while the divergence temperature decreases to~60 K in 50 kOe. The FC curves show a smooth decrease in magnetization with raising the temperature from 10 to 370 K, suggesting a ferromagnetic feature of the annealed β-Fe 3 Se 4 nanoplates below 370 K. Therefore, the T C of the annealed β-Fe 3 Se 4 nanoplates should be higher than 370 K. The magnetization in Figure 8b shows a slight decrease with increasing temperature to about 470 K and then an increase with increasing temperature to 600 K, almost the same as the temperature dependence of magnetization for the β-Fe 3 Se 4 nanoplates experienced a heating process from 300 to 470 K as shown in Figure 7b. When the annealed sample was cooled down from 600 K, a magnetic transition at about 335 K corresponding to monoclinic β-Fe 3 Se 4 phase was also observed. It suggests that heat treatment at 623 K results in a magnetic change from the antiferromagnetism for the as-synthetic β-Fe 3 Se 4 nanoplates to the ferrimagnetism for the annealed β-Fe 3 Se 4 nanoplates. Hysteresis loops of the annealed β-Fe 3 Se 4 nanoplates in Figure 8c present the ferrimagnetism at a temperature range from 10 to 300 K. The saturation magnetization (M S ) and coercivity (H C ) for the annealed β-Fe 3 Se 4 nanoplates increase from 0.7 emu/g and 0.13 kOe at 300 K to 0.8 emu/g and 2.45 kOe at 10 K. Compared to monoclinic Fe 3 Se 4 , the reduced saturation magnetization for the annealed β-Fe 3 Se 4 nanoplates may be ascribed to different spin configurations of Fe atoms in this tetragonal phase. Moreover, the coercivity values of the annealed β-Fe 3 Se 4 nanoplates are much smaller than the previous results for the monoclinic Fe 3 Se 4 nanoplatelets with the H C of 40 and 4 kOe, respectively, at 10 and 300 K [4]. The different coercivity values may originate from the difference in grain sizes and stoichiometry. However, the unusually large coercivity for monoclinic Fe 3 Se 4 nanostructure significantly depends on its uniaxial magnetocrystalline anisotropy [7]. Figure 8 further reveals an effect of a heat-treatment at a temperature of 623 K, only a little higher than the synthetic temperature (603 K), on the magnetic properties of the annealed β-Fe 3 Se 4 nanoplates, which is much different from those of the as-synthetic β-Fe 3 Se 4 nanoplates. The change of the magnetic properties should be resulted from the varied spin configurations for these samples under a thermal excitation.
Moreover, Figure 8b shows a high magnetization of about 1 emu/g at a magnetic field of 50 kOe at 600 K, which is larger than the M S measured at 300 K. Such a high magnetization should be related to the annealed tetragonal β-Fe 3 Se 4 temperature, but not monoclinic Fe 3 Se 4 due to 600 K being much higher than the T C of the monoclinic phase. The XRD pattern of the product decomposed at 673 K indicates that the product consists of a main phase of tetragonal β-Fe 3 Se 4 and a minor phase of monoclinic Fe 3 Se 4 (Figure 3b). It suggests that the T C of the annealed tetragonal β-Fe 3 Se 4 is higher than 600 K. However, tetragonal β-Fe 3 Se 4 is metastable at a temperature higher than 470 K, which will transform to monoclinic Fe 3 Se 4 through a change of crystal symmetry and hexagonal Fe 7 Se 8 through loss of Se atoms. The phase evolution seriously relates to the annealing temperature and the annealing period. Although the Curie temperature is an important factor to a magnet, the T C of the annealed tetragonal β-Fe 3 Se 4 is not determined at present due to the absence of single phase tetragonal β-Fe 3 Se 4 nanoplates at higher temperatures. Moreover, Figure 8b shows a high magnetization of about 1 emu/g at a magnetic field of 50 kOe at 600 K, which is larger than the MS measured at 300 K. Such a high magnetization should be related to the annealed tetragonal β-Fe3Se4 temperature, but not monoclinic Fe3Se4 due to 600 K being much higher than the TC of the monoclinic phase. The XRD pattern of the product decomposed at 673 K indicates that the product consists of a main phase of tetragonal β-Fe3Se4 and a minor phase of monoclinic Fe3Se4 (Figure 3b). It suggests that the TC of the annealed tetragonal β-Fe3Se4 is higher than 600 K. However, tetragonal β-Fe3Se4 is metastable at a temperature higher than 470 K, which will transform to monoclinic Fe3Se4 through a change of crystal symmetry and hexagonal Fe7Se8 through loss of Se atoms. The phase evolution seriously relates to the annealing temperature and the annealing period. Although the Curie temperature is an important factor to The similarity and differences between tetragonal β-Fe 3 Se 4 and the more extensively investigated monoclinic Fe 3 Se 4 . Despite the same chemical stoichiometry, the as-synthetic tetragonal β-Fe 3 Se 4 is antiferromagnetic at room temperature, while the annealed tetragonal β-Fe 3 Se 4 and the monoclinic Fe 3 Se 4 are ferrimagnetic materials. The present tetragonal β-Fe 3 Se 4 nanoplates are much different from the components in the intercalated compounds AFe 1.5 Se 2 [17] and the inorganic building units in ordered inorganic-organic (β-Fe 3 Se 4 ) 4 [Fe(teta) 1.5 ] hybrid material [20]. Besides the strong 2D shape anisotropy of the nanoplates, the ferrimagnetic materials may have different magnetocrystalline anisotropies mainly due to different crystal symmetries. Previously, substitution of Se with Te in tetragonal FeSe results in an obvious enhancement of superconducting critical transition temperature [26]. Conversely, the Fe ions in monoclinic Fe 3 Se 4 can be easily substituted by other transition metals to form different monoclinic phases with varying magnetic properties [27]. For example, Fe 3-x Cr x Se 4 (0 ≤ x ≤ 2) are hard magnets with a maximum magnetocrystalline anisotropy of 1.2 × 10 6 erg/cm 3 at x = 0.5 [9,10]. This substitution of Fe with other transition-metal ions should be also possible within tetragonal β-Fe 3 Se 4 . Our investigations reveal the dependence of magnetism of tetragonal structure of β-Fe 3 Se 4 and monoclinic structure of Fe 3 Se 4 on their crystal structures, which may originate from the difference distributions of iron vacancies. Other interesting physical properties originating from the varied crystal symmetries and distributions of iron vacancies are currently under investigation.

Conclusions
In conclusion, we have developed a facile protocol for synthesizing tetragonal β-Fe 3 Se 4 nanoplates by thermal decomposition of a new ordered inorganic-organic (β-Fe 2 Se 3 ) 4 [Fe(tepa)] hybrid material in the high-temperature organic-solution-phase process. The ordered inorganic-organic (β-Fe 2 Se 3 ) 4 [Fe(tepa)] hybrid material is in a tetragonal crystal structure with a space group I4cm (108), while the as-synthetic tetragonal β-Fe 3 Se 4 nanoplates have the layered crystal structure with the P4/nmm space group. The assynthetic β-Fe 3 Se 4 nanoplates show the antiferromagnetism in a temperature between 120 and 420 K but a ferrimagnetism below~120 K. The as-synthetic β-Fe 3 Se 4 nanoplates are metastable, which experienced an irreversible magnetic transition at about 470 K. The annealed β-Fe 3 Se 4 nanoplates are in the ferrimagnetism between 10 and 470 K. Varied magnetic properties of tetragonal β-Fe 3 Se 4 nanoplates are ascribed to disordered distribution of iron vacancies. Moreover, different magnetic properties of tetragonal structure of Fe 3 Se 4 and monoclinic structure of Fe 3 Se 4 should be mainly created by the different crystal symmetries.