Preparation of Activated Carbon/TiO 2 Nanohybrids for Photodegradation of Reactive Red-35 Dye Using Sunlight

: Activated carbon/titanium dioxide (AC/TiO 2 ) nanohybrids were synthesized by a hydrothermal technique using various weight percent of commercial AC and were characterized by X-ray diffraction (XRD), ﬁeld emission scanning electron microscopy (FESEM), Fourier transform infrared (FTIR) and thermogravimetric analysis (TGA). The synthesized nanohybrids were applied to photodegradation of Reactive Red-35 (RR-35) dye in aqueous solution using sunlight. Due to the synergistic effect of adsorption and photodegradation activity, AC/TiO 2 nanohybrids were more efﬁcient in treating the aqueous dye solution than that of AC and TiO 2 The maximum (95%) RR-35 dye removal from the water was obtained with 20 wt% AC/TiO 2 within 30 min at natural pH of 5.6. The possible photodegradation mechanism of RR-35 dye with AC/TiO 2 was discussed from the scavenger test. Moreover, AC/TiO 2 was found to be suitable for long-term repeated applications through recyclability experiments. Therefore, AC/TiO 2 nanohybrid is a promising photocatalyst for treating azo dyes especially RR-35 from water.


Introduction
Adverse effects are being observed in the environment, especially, in water quality due to the rapid urbanization and industrialization in the world. Hazardous wastes along with untreated toxic chemicals are usually flushed into rivers and ponds or nearby water reservoirs [1]. The dyes are considered hazardous water pollutants due to their toxic effects on the environment and complexity in removal [2]. Textile dyes, especially azo dyes not only affect the aesthetic merit of surface water but also reduces light penetration that hampers aquatic lives [2]. Moreover, azo dyes are usually mutagenic and carcinogenic [2,3]. Reactive Red-35 (RR-35) is a typical toxic azo dye and has widely been used in textile industries because of its vibrant colors, water-fastness and energy-efficient application techniques [4].
Several techniques have been applied for wastewater treatment, especially in azo dye removal from water [2,5]. However, the traditional physical and biological water treatment processes have some drawbacks such as prolonged tendency, high cost and lower efficiency [2]. Moreover, some non-traditional processes such as ozonation, radiation and membrane processes have some drawbacks; for example, ozonation and radiation processes generate toxic byproducts, which could be difficult to remove [6,7]. Therefore, cost-effective and environment-friendly methods are desired for the removal of toxic dyes from the effluent streams.

Preparation of AC/TiO 2 Nanohybrids
In this study, the various proportions of AC/TiO 2 nanohybrids were successfully synthesized, according to the previous report with slight modification [23,24]. A 10 mL solution of TiCl 3 in 15% HCl was hydrolyzed using 20 mL deionized water and then a dropwise addition of aqueous NH 4 OH (20 mL) produced dark blue precipitate, which turned yellowish due to the addition of H 2 O 2 through constant stirring. After 30 min of vigorous stirring, the calculated amount of AC was added to the mixture. The obtained suspensions were left for 4 days for aging and then the precipitates were filtered, washed with distilled water followed by acetone and dried at 60 • C. Finally, calcination was done at 400 • C under air for 6 h to obtain desired AC/TiO 2 nanohybrids. For comparison, bare TiO 2 was also synthesized by a similar procedure without using AC.

Characterization of Studied Nanohybrids
An X-ray diffractometer (Ultima IV, Rigaku Corporation, Akishima, Japan) fitted with Cu Kα radiation (λ = 0.154 nm) was used to analyze the XRD patterns of the studied samples at room temperature (25 • C). The morphological features of the samples were examined by an analytical field emission scanning electron microscope (FESEM) (JEOL JSM-6490LA, Tokyo, Japan) operating at an accelerating voltage of 20 kV. The interaction between TiO 2 and AC was observed by recording transmission spectra on a Fourier transform infrared spectrometer (FTIR, Shimadzu IR Prestidge-21, Japan) in the wavenumber range of 4000-400 cm −1 with resolution 4 cm −1 and S/N ratio of over 40,000:1. The thermal stability of the samples was inspected by recording thermograms on a thermogravimetric analyzer (TG-00260, SHIMADZU Corp, Japan), which operated within 25-800 • C with 10 • C min −1 heating rate and 5 min hold time.

RR-35 Dye Removal Experiments
The dye removal performance of commercial AC, bare TiO 2 and AC/TiO 2 nanohybrids were carried out at various operating conditions such as pH, time and dye concentration using a standard solution of RR-35 (at 536 λ max nm [25]) under solar irradiation in openair. The remaining concentration of RR-35 after degradation at various conditions was measured by recording absorbance on a UV-1700 Spectrophotometer (Shimadzu, Japan). Batch experiments were performed under similar conditions on sunny days between 11:00 and 14:00 BST (Bangladesh standard time) for the investigation of the % removal of RR-35 using the studied photocatalysts (location coordinate: 23.7275 • N, 90.4019 • E; intensity of sunlight: 3.0 mW/cm 2 ; time of year: June to August). The intensity of light was measured by a UV radiometer with a sensor of 320-420 nm wavelength (UVR-400, Iuchi Co., Osaka, Japan). For adjusting the pH of the solutions before degradation experiments, dilute HCl (0.1 M) and NaOH (0.1 M) aqueous solutions were used. It should be noted that the natural solution pH of RR-35 was 5.6. Moreover, a reusability experiment was carried out to evaluate the potential of AC/TiO 2 for industrial application.

XRD Analysis
The XRD patterns of AC, TiO 2 and AC/TiO 2 nanohybrids are shown in Figure 1. As can be seen in Figure 1a, the XRD of AC shows two weak broad peaks at 25 • and 44 • corresponding to reflection in the (002) plane and the (100) plane, which indicates the existence of quartz phase at low concentration and two-dimensional reflections of disordered stacking of micrographites, respectively [26,27]. On the other hand, the XRD pattern of TiO 2 and AC/TiO 2 nanohybrids shows diffraction peaks at about 25.34 • , 37.76 • , 48.00 • , 53.81 • and 55.11 • (2θ values), which could be indexed as (101), (004), (200), (105) and (211) planes, respectively, of an anatase TiO 2 [28,29]. It suggests that the anatase TiO 2 is predominantly formed in the nanohybrids when calcined at 400 • C [24]. The sharp peaks of the XRD pattern of synthesized nanohybrids acknowledge that there were no impurities present in the nanohybrids. Therefore, the XRD analysis strongly supports the successful fabrication of the nanohybrids. Interestingly, it was observed that the diffraction peak intensity was decreased and slight peak broadening was occurred in nanohybrids with increasing AC content (Figure 1b), similar to the previous report [22,23]. Therefore, the crystallite size of nanohybrids was decreased with increasing AC content. Based on the XRD results, the crystal size of the nanohybrids is determined using the Scherrer formula for the peak at 2θ = 25.15 • . The crystal size of bare TiO 2 , 10 wt% AC/TiO 2 , 20 wt% AC/TiO 2 and 30 wt% AC/TiO 2 could be estimated as 26, 20, 16 and 15 nm, respectively. Notably, there was no characteristic peak that is observed in nanohybrids due to AC. The reason could be attributed to the fact that the main peak of AC might be shielded by the peak of anatase TiO 2 [30].

FESEM Analysis
The morphologies of the AC, TiO2 and AC/TiO2 nanohybrids are investigated by FESEM micrographs and shown in Figure 2. The external surface of the AC clusters is flat, rough and porous whereas the aggregation of TiO2 crystallites is significant in TiO2, with a size of 26 nm (based on the Scherrer equation). From FESEM images of AC/TiO2 nanohybrids, it is observed that the TiO2 particle with the nanosized dimension is uniformly deposited on the AC surface and in the bulk of the AC and the aggregate size of TiO2 particles strongly depended on the AC content. The FESEM images, shown in Figure 2, reveal that particle size of nanohybrids decreased with increasing AC content, which is also agreeable with the XRD results. Therefore, it is easily assumed that the nanohybrid had a relatively higher percentage of smaller particles than TiO2, which might be beneficial for photocatalytic activity [31].

FESEM Analysis
The morphologies of the AC, TiO 2 and AC/TiO 2 nanohybrids are investigated by FESEM micrographs and shown in Figure 2. The external surface of the AC clusters is flat, rough and porous whereas the aggregation of TiO 2 crystallites is significant in TiO 2 , with a size of 26 nm (based on the Scherrer equation). From FESEM images of AC/TiO 2 nanohybrids, it is observed that the TiO 2 particle with the nanosized dimension is uniformly deposited on the AC surface and in the bulk of the AC and the aggregate size of TiO 2 particles strongly depended on the AC content. The FESEM images, shown in Figure 2, reveal that particle size of nanohybrids decreased with increasing AC content, which is also agreeable with the XRD results. Therefore, it is easily assumed that the nanohybrid had a relatively higher percentage of smaller particles than TiO 2 , which might be beneficial for photocatalytic activity [31].

FESEM Analysis
The morphologies of the AC, TiO2 and AC/TiO2 nanohybrids are investigated by FESEM micrographs and shown in Figure 2. The external surface of the AC clusters is flat, rough and porous whereas the aggregation of TiO2 crystallites is significant in TiO2, with a size of 26 nm (based on the Scherrer equation). From FESEM images of AC/TiO2 nanohybrids, it is observed that the TiO2 particle with the nanosized dimension is uniformly deposited on the AC surface and in the bulk of the AC and the aggregate size of TiO2 particles strongly depended on the AC content. The FESEM images, shown in Figure 2, reveal that particle size of nanohybrids decreased with increasing AC content, which is also agreeable with the XRD results. Therefore, it is easily assumed that the nanohybrid had a relatively higher percentage of smaller particles than TiO2, which might be beneficial for photocatalytic activity [31].

FTIR Analysis
FTIR spectra of TiO 2 and AC/TiO 2 nanohybrids are shown together with AC in Figure 3. The main absorption peaks were located at 3430, 1058, 710 and 530 cm −1 . The bands observed in AC and synthesized nanohybrids, located at 3430 cm −1 were due to -OH stretching. Bare TiO 2 and nanohybrids revealed an intense peak contributing to the stretching vibrations of Ti-O bonds at 710 and 530 cm −1 , which is the characteristic peak of TiO 2 [28]. Interestingly, with the addition of AC, a new peak located at 1058 cm −1 appeared and the peak at 530 cm −1 shifted to lower wavenumbers, similar to the previous report [23]. Besides, with increasing AC content, the width and intensity of the peak at 1058 cm −1 was increased. Thus, it can be concluded that the appearance of this peak is related to AC in the AC/TiO 2 composites [23].
Photochem 2021, 1, FOR PEER REVIEW 5 observed in AC and synthesized nanohybrids, located at 3430 cm −1 were due to -OH stretching. Bare TiO2 and nanohybrids revealed an intense peak contributing to the stretching vibrations of Ti-O bonds at 710 and 530 cm −1 , which is the characteristic peak of TiO2 [28]. Interestingly, with the addition of AC, a new peak located at 1058 cm −1 appeared and the peak at 530 cm −1 shifted to lower wavenumbers, similar to the previous report [23]. Besides, with increasing AC content, the width and intensity of the peak at 1058 cm −1 was increased. Thus, it can be concluded that the appearance of this peak is related to AC in the AC/TiO2 composites [23].

TG Analysis
To investigate the amount of TiO2 in the AC/TiO2 composites synthesized at different ratios, thermogravimetric (TG) tests were carried out in a range of 25-800 °C under N2 flow. As shown in the TG curves (Figure 4), the gentle weight loss of commercial AC, TiO2 and AC/TiO2 nanohybrids at temperatures ranging from 20 to 200 °C is observed due to the desorption of physisorbed water. According to the TG curves, the weight loss of the nanohybrids increased with increasing AC content. The final weight loss was 15.6% for pure AC, which is agreeable with earlier reported results [32] and 6.6%, 4.3%, 2.4% and 0.60% for 30 wt % AC/TiO2, 20 wt % AC/TiO2, 10 wt % AC/TiO2 and TiO2.

TG Analysis
To investigate the amount of TiO 2 in the AC/TiO 2 composites synthesized at different ratios, thermogravimetric (TG) tests were carried out in a range of 25-800 • C under N 2 flow. As shown in the TG curves (Figure 4), the gentle weight loss of commercial AC, TiO 2 and AC/TiO 2 nanohybrids at temperatures ranging from 20 to 200 • C is observed due to the desorption of physisorbed water. According to the TG curves, the weight loss of the nanohybrids increased with increasing AC content. The final weight loss was 15.6% for pure AC, which is agreeable with earlier reported results [32] and 6.6%, 4.3%, 2.4% and 0.60% for 30 wt% AC/TiO 2 , 20 wt% AC/TiO 2 , 10 wt% AC/TiO 2 and TiO 2 .

Effect of AC Content
The effect of AC content in nanohybrids for the removal of RR-35 from water under dark and sunlight irradiation is depicted in Figure 5. To quantify the relative contributions of both adsorption and photodegradation towards the overall removal of RR-35, control experiments in dark were carried out for 30 min. As shown in Figure 5, the adsorption of RR-35 by AC, TiO 2 and 20% AC/TiO 2 under dark were calculated to be 42%, 9% and 34% respectively. The respective values for commercial AC and bare TiO 2 were 47% and 26% under sunlight irradiation within 30 min. The removal efficiency of AC in dark and under sunlight is nearly similar which indicates that the removal of RR-35 using AC was due to adsorption rather than photocatalysis. Additionally, the TiO 2 was not much effective for the degradation of RR-35 due to a large band gap, similar to the earlier report for the degradation of methyl orange dye [33]. Commercial AC showed better performance than TiO 2 , which might be due to the adsorption of RR-35 on AC. Additionally, it was noticed that the photocatalytic efficiency of nanohybrids was increased compared with commercial AC and TiO 2 because of the synergistic effect of both adsorption and photocatalysis due to a combination of AC and TiO 2 [34]. Among studied nanohybrids, 20 wt% AC/TiO 2 showed the best performance in RR-35 removal (95%) due to the formation of nanoparticles with good crystallinity [33]. Probably, all of the TiO 2 nanoparticles might take part in interaction with AC in the case of 20wt% AC/TiO 2 , which was important for maximum removal of RR-35 [33,35]. Therefore, further investigation was carried out using 20 wt% AC/TiO 2 as a photocatalyst for degradation of RR-35.

Effect of AC Content
The effect of AC content in nanohybrids for the removal of RR-35 from water under dark and sunlight irradiation is depicted in Figure 5. To quantify the relative contributions of both adsorption and photodegradation towards the overall removal of RR-35, control experiments in dark were carried out for 30 min. As shown in Figure 5, the adsorption of RR-35 by AC, TiO2 and 20% AC/TiO2 under dark were calculated to be 42%, 9% and 34% respectively. The respective values for commercial AC and bare TiO2 were 47% and 26% under sunlight irradiation within 30 min. The removal efficiency of AC in dark and under sunlight is nearly similar which indicates that the removal of RR-35 using AC was due to adsorption rather than photocatalysis. Additionally, the TiO2 was not much effective for the degradation of RR-35 due to a large band gap, similar to the earlier report for the degradation of methyl orange dye [33]. Commercial AC showed better performance than TiO2, which might be due to the adsorption of RR-35 on AC. Additionally, it was noticed that the photocatalytic efficiency of nanohybrids was increased compared with commercial AC and TiO2 because of the synergistic effect of both adsorption and photocatalysis due to a combination of AC and TiO2 [34]. Among studied nanohybrids, 20 wt % AC/TiO2 showed the best performance in RR-35 removal (95%) due to the formation of nanoparticles with good crystallinity [33]. Probably, all of the TiO2 nanoparticles might take part in interaction with AC in the case of 20 wt % AC/TiO2, which was important for maximum removal of RR-35 [33,35]. Therefore, further investigation was carried out using 20 wt % AC/TiO2 as a photocatalyst for degradation of RR-35.

Effect of pH
Solution pH strongly controls the surface charge of a nanohybrid and thus the photodegradation of dye is also greatly affected. The degradation of RR-35 by 20 wt % AC/TiO2 was recorded within a pH range of 2-10 and the results are displayed in Figure  6. The results revealed that the degradation of dye increased with solution pH up to a certain level (at pH 6.0) and then decreased with solution pH. The maximum removal of RR-35 at pH 6.0 was 99%, after 30 min of the sunlight irradiation. At natural pH 5.6, the RR-35 removal was observed 95%, which was almost similar to the percent of removal

Effect of pH
Solution pH strongly controls the surface charge of a nanohybrid and thus the photodegradation of dye is also greatly affected. The degradation of RR-35 by 20 wt% AC/TiO 2 was recorded within a pH range of 2-10 and the results are displayed in Figure 6. The results revealed that the degradation of dye increased with solution pH up to a certain level (at pH 6.0) and then decreased with solution pH. The maximum removal of RR-35 at pH 6.0 was 99%, after 30 min of the sunlight irradiation. At natural pH 5.6, the RR-35 removal was observed 95%, which was almost similar to the percent of removal obtained at pH 6.0. Therefore, further investigation such as the effect of time, dye concentration, scavenger test and reusability experiment was carried at natural solution pH (5.6) of RR-35. The point of zero charge value (pzc) of TiO 2 and AC/TiO 2 is reported as 6.8 and 7.6 respectively [25,36], which means that the surface of AC/TiO 2 becomes positive below this pH value (pH < 7.6) and negative above this pH value (pH > 7.6). RR-35 is an anionic dye in aqueous solution; therefore, at pH 5.6-7.0, the positively charged 20 wt% AC/TiO 2 surface could adsorb more dye molecules through electrostatic interaction. Due to the enhanced adsorption, more dye molecules are exposed to the active sites of the photocatalyst. The lower rate of photodegradation of RR-35 at alkaline media was found probably due to the presence of superfluous negative charge on the catalyst surface, which could repel the anionic dye molecules. Moreover, at a very low pH (from 2.0 to 4.0) the photodegradation of RR-35 decreased probably due to the protonation of dye molecules, which consequently reduced the adsorption of dye molecules on the AC/TiO 2 surface [36].

Effect of Time
The effect of irradiation time on photodegradation of RR-35 using 20 wt % AC/TiO2 was investigated by evaluating the percentage removal of RR-35 at different periods as shown in Figure 7. The result from Figure 7 revealed that 95% dye was removed by 5 mg of 20 wt % AC/TiO2 in 30 min at pH 5.6 under sunlight irradiation. It was evident that the rate of degradation was higher during the initial stage (up to 10 min). Afterward, the degradation rate started decreasing gradually and the degradation finally reached equilibrium after 30 min. It might be due to the gradual decline in the concentration of RR-35 and simultaneous formation of degradation products with irradiation time. As a result, maximum degradation (95%) of RR-35 was found after 30 min of sunlight irradiation.

Effect of Time
The effect of irradiation time on photodegradation of RR-35 using 20 wt% AC/TiO 2 was investigated by evaluating the percentage removal of RR-35 at different periods as shown in Figure 7. The result from Figure 7 revealed that 95% dye was removed by 5 mg of 20 wt% AC/TiO 2 in 30 min at pH 5.6 under sunlight irradiation. It was evident that the rate of degradation was higher during the initial stage (up to 10 min). Afterward, the degradation rate started decreasing gradually and the degradation finally reached equilibrium after 30 min. It might be due to the gradual decline in the concentration of RR-35 and simultaneous formation of degradation products with irradiation time. As a result, maximum degradation (95%) of RR-35 was found after 30 min of sunlight irradiation.
shown in Figure 7. The result from Figure 7 revealed that 95% dye was removed by 5 mg of 20 wt % AC/TiO2 in 30 min at pH 5.6 under sunlight irradiation. It was evident that the rate of degradation was higher during the initial stage (up to 10 min). Afterward, the degradation rate started decreasing gradually and the degradation finally reached equilibrium after 30 min. It might be due to the gradual decline in the concentration of RR-35 and simultaneous formation of degradation products with irradiation time. As a result, maximum degradation (95%) of RR-35 was found after 30 min of sunlight irradiation.

Effect of Initial Concentration of RR-35
It is necessary to study the dependence of the dye removal efficiency on the initial dye concentration given its practical application. The dye removal rate of different initial RR-35 concentrations with 20 wt% AC/TiO 2 is presented in Figure 8. From Figure 8 it was observed that the dye removal rate rises with the increase in initial dye concentration from 10 to 20 mg L −1 and a further increase in dye concentration leads to the decrease in removal rate [37]. Additionally, with increasing the initial dye concentration up to 40 mg L −1 , the degradation amounts of RR-35 increased gradually, and exceeding 40 mg L −1 , the degradation amounts of RR-35 were almost the same. The high concentration gradient provides an increase of driving force to move RR-35 from the bulk to the nanohybrid surface. This mass transfer process continued until the nanohybrid surface was saturated with RR-35 molecules [38]. It could be stated that saturation probably occurred at 40 mg L −1 RR-35 concentration. Besides, at a concentration above 40 mg L −1 , a significant amount of sunlight may be absorbed by the dye molecules itself, which could reduce the photodegradation efficiency of AC/TiO 2 [39]. In this study, 20 mg L −1 of RR-35 solution was selected to evaluate the photodegradation of dye for the following experiment owing to the concentration of real wastewater.

Role of Radical Scavenger
Radical scavenger experiments were carried out to determine the reactive species responsible for the photodegradation of RR-35 dye. In this study, iso-propanol (IP), ascorbic acid (AA) and oxalic acid (OA) were introduced to be the scavengers of hydroxyl radicals ( • OH), superoxide radical ( • O 2 − ) and holes (h + ), respectively [18,[40][41][42]. The three scavenging experiments were similar to the RR-35 dye removal process. The effect of the radical scavengers on the RR-35 photodegradation over 20 wt% AC/TiO 2 using sunlight is displayed in Figure 9. From the figure, 95% removal of RR-35 was found with no scavenger (NS), while 56% removal was found with IP, 78% with AA and 85% with OA, respectively. The results strongly indicated that both • OH and • O 2 − radicals played a significant role in the photodegradation of RR-35, whereas, h + showed a minor effect in the degradation process under sunlight.
surface. This mass transfer process continued until the nanohybrid surface was saturated with RR-35 molecules [38]. It could be stated that saturation probably occurred at 40 mg L −1 RR-35 concentration. Besides, at a concentration above 40 mg L −1 , a significant amount of sunlight may be absorbed by the dye molecules itself, which could reduce the photodegradation efficiency of AC/TiO2 [39]. In this study, 20 mg L −1 of RR-35 solution was selected to evaluate the photodegradation of dye for the following experiment owing to the concentration of real wastewater.

Role of Radical Scavenger
Radical scavenger experiments were carried out to determine the reactive species responsible for the photodegradation of RR-35 dye. In this study, iso-propanol (IP), ascorbic acid (AA) and oxalic acid (OA) were introduced to be the scavengers of hydroxyl radicals ( • OH), superoxide radical ( • O2 − ) and holes (h + ), respectively [18,[40][41][42]. The three scavenging experiments were similar to the RR-35 dye removal process. The effect of the radical scavengers on the RR-35 photodegradation over 20 wt % AC/TiO2 using sunlight is displayed in Figure 9. From the figure, 95% removal of RR-35 was found with no scavenger (NS), while 56% removal was found with IP, 78% with AA and 85% with OA, respectively. The results strongly indicated that both • OH and • O2 − radicals played a significant role in the photodegradation of RR-35, whereas, h + showed a minor effect in the degradation process under sunlight.

Photodegradation Mechanism
The fundamental mechanism of the AC/TiO2 nanohybrids exhibit dual functions such as absorption and photodegradation to remove the RR-35 dye from an aqueous solution [34]. The proposed schematic illustration of the photodegradation mechanism of RR-35 dye by 20 wt % AC/TiO2 using sunlight is presented in Figure 10. Under sunlight irradiation, the RR-35 removal process requires the dye to be adsorbed on the AC/TiO2 surface before immediate photodegradation [43]. The efficiency of photodegradation can be affected by the adsorption performance of substrate AC and the photocatalytic activity of TiO2 nanoparticles [34]. Moreover, the AC introduced to the composite structure acts as an electron sink, thereby decreasing the recombination of photogenerated charge carriers and finally enhancing the photocatalytic activity of the AC/TiO2 [44]. During the sunlight irradiation, the AC/TiO2 (considering the semiconductor of TiO2, 3.2 eV) can absorb the UV light energy to create the conduction band electrons (e ) and valence band holes (h ) [30,45]. Then, the photogenerated holes (h ) are responsible for the oxidation of RR-35 dyes and water (H2O) molecules adsorbed on the surface of the AC/TiO2 and the formation of hydroxyl radicals ( • OH) [44]. The photoexcited e attack the dissolved oxygen (O2) to generate superoxide radicals ( • O2 − ), which can act as a pre-

Photodegradation Mechanism
The fundamental mechanism of the AC/TiO 2 nanohybrids exhibit dual functions such as absorption and photodegradation to remove the RR-35 dye from an aqueous solution [34]. The proposed schematic illustration of the photodegradation mechanism of RR-35 dye by 20 wt% AC/TiO 2 using sunlight is presented in Figure 10. Under sunlight irradiation, the RR-35 removal process requires the dye to be adsorbed on the AC/TiO 2 surface before immediate photodegradation [43]. The efficiency of photodegradation can be affected by the adsorption performance of substrate AC and the photocatalytic activity of TiO 2 nanoparticles [34]. Moreover, the AC introduced to the composite structure acts as an electron sink, thereby decreasing the recombination of photogenerated charge carriers and finally enhancing the photocatalytic activity of the AC/TiO 2 [44]. During the sunlight irradiation, the AC/TiO 2 (considering the semiconductor of TiO 2 , 3.2 eV) can absorb the UV light energy to create the conduction band electrons (e − CB ) and valence band holes (h + VB ) [30,45]. Then, the photogenerated holes (h + VB ) are responsible for the oxidation of RR-35 dyes and water (H 2 O) molecules adsorbed on the surface of the AC/TiO 2 and the formation of hydroxyl radicals ( • OH) [44]. The photoexcited e − CB attack the dissolved oxygen (O 2 ) to generate superoxide radicals ( • O 2 − ), which can act as a precursor of many reactive species in photochemical reactions [46]. Moreover, • O 2 − is an important source of • OH radical and avoids the recombination of the electron/hole pair in the photocatalyst, thus improving the photodegradation process [47]. The photogenerated holes (h + VB ), photoexcited electrons (e − CB ), hydroxyl radicals ( • OH) and superoxide radical ions ( • O 2 − ) take part in heterogeneous-photocatalytic reactions. These species can lead to the photodegradation of RR-35 molecules to intermediates, and then go further degradation to CO 2 and H 2 O. Thus, the photodegradation of dye pollutants is one of the suitable processes because of its abundance advantages, such as breaking down pollutants and achieving complete mineralization to convert into non-toxic products [44]. Therefore, we expect the following photodegradation reactions of RR-35 dye by AC/TiO 2 under sunlight irradiation [45,47,48]: RR-35 dye + • OH/ • O2 − → Intermediates → CO2 + H2O (5) Figure 10. Schematic illustration of the photodegradation mechanism of RR-35 by 20 wt % AC/TiO2 using sunlight.

Reusability of AC/TiO2
Reusability is one of the most important characteristics of a material for removing pollutants from industrial effluents since it is related to the cost-effectiveness of the photocatalyst. The reusability of 20 wt % AC/TiO2 was evaluated up to four cycles by simple alkali (0.01 M NaOH) washing [34]. The alkali-treated nanohybrid was washed with distilled water and dried for the next cycle. The result of the reusability experiment is illustrated in Figure 11. The graph clearly illustrated that the performance of the recycled 20 wt % AC/TiO2 for RR-35 removal remained almost consistent. The removal activity of the nanohybrid gradually decreased up to four cycles due to the poisoning effect of degraded products and the blocking of sunlight irradiation [49]. Therefore, it can be concluded that the AC/TiO2 is suitable for long-term repeated use for the removal of

Reusability of AC/TiO 2
Reusability is one of the most important characteristics of a material for removing pollutants from industrial effluents since it is related to the cost-effectiveness of the photocatalyst. The reusability of 20 wt% AC/TiO 2 was evaluated up to four cycles by simple alkali (0.01 M NaOH) washing [34]. The alkali-treated nanohybrid was washed with distilled water and dried for the next cycle. The result of the reusability experiment is illustrated in Figure 11. The graph clearly illustrated that the performance of the recycled 20 wt% AC/TiO 2 for RR-35 removal remained almost consistent. The removal activity of the nanohybrid gradually decreased up to four cycles due to the poisoning effect of degraded products and the blocking of sunlight irradiation [49]. Therefore, it can be concluded that the AC/TiO 2 is suitable for long-term repeated use for the removal of RR-35 dye from the aqueous environment.

Conclusions
In this study, a cost-effective method has been reported for the preparation of AC/TiO2 nanohybrids. The best removal efficiency for RR-35 dye was obtained by 20 wt % AC/TiO2. The remarkable removal of RR-35 with AC/TiO2 can be explained by both the adsorption and photodegradation activity of nanohybrids. RR-35 dye photodegradation with AC/TiO2 using sunlight was mainly controlled by the • OH and • O2 − radicals whereas, the h + played a minor effect in the process. Moreover, AC/TiO2 nanohybrids can be regenerated by simple alkali washing. Therefore, AC/TiO2 can be suggested as an efficient photocatalyst for RR-35 dye removal from water based on the facile synthesis, very fast with nearly complete removal, and excellent reusability.

Conclusions
In this study, a cost-effective method has been reported for the preparation of AC/TiO 2 nanohybrids. The best removal efficiency for RR-35 dye was obtained by 20 wt% AC/TiO 2 . The remarkable removal of RR-35 with AC/TiO 2 can be explained by both the adsorption and photodegradation activity of nanohybrids. RR-35 dye photodegradation with AC/TiO 2 using sunlight was mainly controlled by the • OH and • O 2 − radicals whereas, the h + played a minor effect in the process. Moreover, AC/TiO 2 nanohybrids can be regenerated by simple alkali washing. Therefore, AC/TiO 2 can be suggested as an efficient photocatalyst for RR-35 dye removal from water based on the facile synthesis, very fast with nearly complete removal, and excellent reusability.