An Investigation of Antimicrobial Activity for Plant Pathogens by Green-Synthesized Silver Nanoparticles Using Azadirachta indica and Mangifera indica

: Photo-microbes are well known to demolish rice and fruits, as farmers use chemical pesticides to overcome agricultural problems and economic damage. The use of pesticides in agriculture fails to protect crops in lower concentrations and increases the intake of chemicals that cause many human ailments. The sophisticated nanotechnology approach used in agriculture for antimicrobial activities offers several advantages for growth and improves nutrient absorption in plants. We report the green synthesis of silver nanoparticles (AgNPs) using Azadirachta indica ( A. indica ) and Mangifera indica ( M. indica ) tree leaf extract that contains antioxidants to treat numerous diseases. AgNPs tested against three plant pathogens, fungi Alternaria alternata ( A. alternata ), Sclerotium rolfsii ( A. rolfsii ), and bacteria Xanthomonas oryzae ( X. oryzae ), which leads to agricultural problems. The experiment was performed with different concentrations of AgNPs in µ L/mL prepared using two other plants extract against fungi and bacteria during summer. The results expose the importance of plant extract in synthesizing silver nanoparticles (AgNPs) and their efﬁcacy for microbes. A compari-son among different concentrations of AgNPs (4 µ L/mL, 6 µ L/mL, and 10 µ L/mL) was performed for two fungi (tomato disease) and bacteria (rice leaf blight disease). A-AgNPs ( A. indica -AgNPs) demonstrate a greater zone of inhibition than M-AgNPs ( M. indica -AgNPs), further highlighting the dependence of plants. Under in vitro conditions, the results of the antifungal activity showed zones of inhibition of 21 mm against A. alternata and 17 mm against A. rolfsii , while antibacterial activity against X. oryzae bacteria showed a 15 mm zone of inhibition at 10 mg/mL for A-AgNPs , and less for M-AgNPs . For AgNPs, the antifungal activity was characterized bya more signiﬁcant area of inhibition than antibacterial activity was. The current study indicates that AgNPs with lower concentrations exhibitsuperior toxicity to microbes and may be able to manage diseases in rice and tomato, and increase plant growth.


Introduction
Due to their catalytic performance, affordability, and biocompatible environment, AgNPs are widely used in biomedical, food, physical, and chemical applications [1]. NPs can be synthesized using chemical, physical and biological methods. Their different shapes and sizes, controlled at the nanoscale level (1 < 10 nm), depend on time, concentration, and temperature [2]. Despite several methods being available, green synthesis remains apriority in the face of environmental issues, and the hazardous chemicals used in the

Pathogens
The antimicrobial activity of silver nanoparticles against two different fungus species (A. alternata) (A. rolfsii) and one bacterium (X. oryzae), provided by the IARI (Pusa Road, New Delhi, India), was studied. These pathogens spread a variety of diseases infectious to crops, vegetable plant, and humans.

Preparation of Plant Extract
Fresh tree leaves from two different plants were collected from the campus of the National Physical laboratory and washed twice thoroughly with distilled water, and then cleaned with tissue paper to remove dirt. The A. indica and M. indica leaves (15 g) were ground using a pestle and mortar and then mixed in deionized water (80 mL) before being boiled on a hot plate for 30 min at 70 • C in a beaker to obtain the extract. The extracts were further filtered with Whatman filter paper and stored in the freezer for further use.

Synthesis of Silver Nanoparticles
A total of 1 mM (millimolar) solution of AgNO 3 salt was dissolved in distilled water and added to leaf extract for reaction. The extract ratio would vary during the responses due to high phytochemicals. A total of 6 mL of extract from A. indica and M. indica leaves was added to 20 mL of 1 mM AgNO 3 solution to reduce the metal salt into metal nanoparticles. The reaction mixture was then heated at 60-70 • C for 15-20 min in a beaker, round bottom flask, or conical flask. The color of the NPs started changing from transparent to dark brown due to the formation of NPs, as shown in Figure 1. The synthesized AgNPs can be stored under 4 • C for one year to perform different characterizations [20].

Preparation of PDA Media
Potato dextrose media (PDA) wereprepared using 20 gm Agar, 20 gm dextrose, potato extract (200 mL), and deionized water (800 mL). PDA media were separated in a different flask and then autoclaved for 3 h at 115 • C when the temperature (room temperature) of the PDA reached 35-40 • C for further use, and allowed to settle down (15 min)

Preparation of PDA Media
Potato dextrose media (PDA) wereprepared using 20 gm Agar, 20 gm dextrose, potato extract (200 mL), and deionized water (800 mL). PDA media were separated in a different flask and then autoclaved for 3 h at 115 °C when the temperature (room temperature) of the PDA reached 35-40°C for further use, and allowed to settle down (15 min) slowly in a petri dish.

Isolation of Fungus and Bacteria
The samples of A. alternata and A. rolfsii fungus collected from the test tubes were isolated from fruits and plants. A small fungus sample and a pinch of Streptomycin were added to autoclaved PDA media at 35-40°C. The fungus-mediated PDA media were poured into a petri dish to rest in solidifying. The growth of A. alternata and A. rolfsii (fresh fungus) on PDA (potato dextrose agar) was observed after seven days of inoculation at a temperature of ±27 °C. X. oryzae bacteria were isolated from the infected rice leaves, which exhibited symptoms of bacterial leaf blight illnesses, in order to study the in vitro susceptibility to the AgNPs. The isolated bacterial suspension was obtained from the cultures grown in nutrient broth overnight and further carried out to study against AgNPs.

Mechanism of Silver Nanoparticles
The natural phytochemicals in plants reduce metal salt to metal nanoparticles by oxidation and reduction methods in water. The addition of silver nitrate(s) to deionized water was mixed well in an aqueous form; Equation (1): AgNO3 (s) ↔ Ag + (aq) + NO3 − (aq) (1) The aqueous silver nitrate was added to the plant extract to reduce silver cation (Ag + ) to silver nanoparticles. The transfer of electrons from phytochemicals to silver cations is shared in the form of radicals to each cation converting into nanoparticles (zero valences) and oxidizing itself. In Figure 2, gallic acid is used as an example, and is converted into 3, 4-didehydroshikimate, i.e., quinone, with the sequential process of the conversion of Ag + to Ag 0 NPs [21].

Isolation of Fungus and Bacteria
The samples of A. alternata and A. rolfsii fungus collected from the test tubes were isolated from fruits and plants. A small fungus sample and a pinch of Streptomycin were added to autoclaved PDA media at 35-40 • C. The fungus-mediated PDA media were poured into a petri dish to rest in solidifying. The growth of A. alternata and A. rolfsii (fresh fungus) on PDA (potato dextrose agar) was observed after seven days of inoculation at a temperature of ±27 • C. X. oryzae bacteria were isolated from the infected rice leaves, which exhibited symptoms of bacterial leaf blight illnesses, in order to study the in vitro susceptibility to the AgNPs. The isolated bacterial suspension was obtained from the cultures grown in nutrient broth overnight and further carried out to study against AgNPs.

Mechanism of Silver Nanoparticles
The natural phytochemicals in plants reduce metal salt to metal nanoparticles by oxidation and reduction methods in water. The addition of silver nitrate(s) to deionized water was mixed well in an aqueous form; Equation (1): The aqueous silver nitrate was added to the plant extract to reduce silver cation (Ag + ) to silver nanoparticles. The transfer of electrons from phytochemicals to silver cations is shared in the form of radicals to each cation converting into nanoparticles (zero valences) and oxidizing itself. In Figure 2, gallic acid is used as an example, and is converted into 3, 4-didehydroshikimate, i.e., quinone, with the sequential process of the conversion of Ag + to Ag 0 NPs [21]. The current mechanism in Figure 2 was explained using gallic acid with Ag + cation. The functional groups in plant extract, such as hydroxyls, enone in catechins, and flavonoids, havebeen well-defined in the literature. The major reducing agents in (Az. indica  The current mechanism in Figure 2 was explained using gallic acid with Ag + cation. The functional groups in plant extract, such as hydroxyls, enone in catechins, and flavonoids, havebeen well-defined in the literature. The major reducing agents in (Az. indica and Mg. indica) plant extracts are flavonoids, catechins, saponins, azadirachtins, phenols, gallic acid, and alkaloids, as also shown in Table 1 [22,23]. These antioxidants react with Ag + (cation) in the colloidal form and are reduced to Ag 0 NPs the moment plant extracts are added to the solution of silver nitrate at a certain temperature and concentration. This reaction is possible because of the presence of functional groups in the antioxidants that donate their electron to Ag + , oxidizing itself. After reduction, the atomic nuclei tend to assemble closely, initiating the process of NPs formation. The capping agent bound to the surface of the NPs when the NPs attain theirmaximum size stabilizes the surface energy [24]. Omidi et al. synthesized AgNPs using adiantum capillus-veneris L leaf extract and observed the presence of the phenolic group. The study demonstrated the reaction mechanism of flavonoids and polyphenols with Ag + to produce AgNPs by reacting with hydroxyl and converting them to a carbonyl group [25]. Similarly, Sharma et al. synthesized AgNPs using saponin seed extract (Madhuca longifolia seed extract) as a major constituent in the proposed mechanism to produce Ag + to Ag-NPs [26]. The presence of free radicals in DPPH produces a reaction with a hydrogen atom or electron provided by extract or silver nanoparticles modified by the fading of purple to a pale yellow color, as confirmed by UV-Vis spectrophotometer. A 0.2 mM volume of DPPH solution was mixed with A. indica, M. indica (plant extract), A-AgNPs, and M-AgNPs prepared at various concentrations: 50, 100, 150, 200, 250, 300, 350, 400, 450, and 500 mg/mL. Methanol was added to DPPH as a control. The mixture was vigorously swirled and incubated for 20 min at room temperature in the dark. A UV-Vis spectrophotometer was used to determine the solution's absorbance at 517 nm (Lambda 950). As it contained several antioxidants, ascorbic acid was employed as a standard. The following equation was utilized to estimate the free radical scavenging activity [27]; where, Sc = absorbance of DPPH radical control, Sa = absorbance of DPPH radical withsilver nanoparticles/ascorbic acid.

Phytochemical Presence in Different Plants
The several phytochemicals identified in the aqueous leaf extract of A. indica and M. indica tree leaves that cap and reduce silver salt to AgNPs have been the subject of substantial qualitative research. The studies show that phytochemical screening of A. indica and M. indica leaf extract suggest that they are a good source of activity against many diseases, including oral cancer [28], as well as providing anti-fungal, anti-bacterial, and anti-diabetes effects, and working against ulcers, as can be observed in Figure 3 [29] studied the A. indica leaf powder to remove 98% malachite green dye from the industrial waste. Aqueous A. indica and M. indica extracts also prevent lung fibrosis and coagulopathy with regular usage. A. indica leaf extracts contain azadirachtin, phenols, hasnimbin, quercetin, limonoids, and tannins, and M. indica extracts contain mangiferin, catechin, gallic acid, flavonoids, and hyperin [22,23]. These antioxidants react with Ag + (cation) in colloidal form and are reduced to Ag 0 NPs, the moment plant extracts are added to the silver nitrate solution at a certain temperature and concentration. The reaction is possible because of the presence of functional groups in the antioxidants to donate their electrons to Ag + and oxidize themselves. After reduction, the atomic nuclei tend to assemble closely, initiating the process of NPs formation. The capping agent bound to the surface of NPs when the NPs attained the maximum size, stabilizing the surface energy [24].

Characterization of the Synthesized AgNPs
The reduction of silver Metal (M + to M 0 NPs) was confirmedby measuring UV-Vis spectroscopy of the low ratio of nanoparticles following dilution in distilled ter. The color changed from transparent to brown following the completion of the r tions. A UV-Vis instrument (Shimadzu UV-3101) was used to measure the absorba between 300 nm and 800 nm [Duisburg, Germany].
GIXRD (Grazing Incidence X-ray diffraction) patterns were recorded usin high-precision PANalytical X'Pert PRO MRD [United Kingdom] high-resolution sys with Cu Kα with λ = 1.54059 A 0 radiation scanned in 2θ ranges from 20 to 80°. Scherrer equation was also used to analyze particle size (Equation (3)): where, ι = average size of ordered domains, λ = wavelength of radiation, k = dimens less shape factor (Scherrer constant), β = full width at half maximum in radians, and angle diffraction.
The nanoparticles' size and morphology were measured using a TEM (transmis electron microscopy) instrument from Jeol Ltd. [Tokyo, Japan], with an accelera voltage of 100 kV. The nanoparticles used for TEM analysis were ultra-sonicated fo min, and then the AgNPs were dropped onto a carbon-coated copper grid to let them in air. SEM (scanning electron microscopy) measurements (ZEISS instrument) [J Germany] of the nanoparticles were performed in order to study their morpholo

Characterization of the Synthesized AgNPs
The reduction of silver Metal (M + to M 0 NPs) was confirmedby measuring the UV-Vis spectroscopy of the low ratio of nanoparticles following dilution in distilled water. The color changed from transparent to brown following the completion of the reactions. A UV-Vis instrument (Shimadzu UV-3101) was used to measure the absorbance between 300 nm and 800 nm [Duisburg, Germany].
GIXRD (Grazing Incidence X-ray diffraction) patterns were recorded using a highprecision PANalytical X'Pert PRO MRD [United Kingdom] high-resolution system with Cu Kα with λ = 1.54059 A 0 radiation scanned in 2θ ranges from 20 to 80 • . The Scherrer equation was also used to analyze particle size (Equation (3)): where, ι = average size of ordered domains, λ = wavelength of radiation, k = dimensionless shape factor (Scherrer constant), β = full width at half maximum in radians, and θ = angle diffraction. The nanoparticles' size and morphology were measured using a TEM (transmission electron microscopy) instrument from Jeol Ltd. [Tokyo, Japan], with an accelerating voltage of 100 kV. The nanoparticles used for TEM analysis were ultra-sonicated for 15 min, and then the AgNPs were dropped onto a carbon-coated copper grid to let them dry in air. SEM (scanning electron microscopy) measurements (ZEISS instrument) [Jena, Germany] of the nanoparticles were performed in order to study their morphologies. SEM (scanning electron microscopy) was employed to determine the surface morphology of the AgNPs.
FTIR (Fourier-transform infrared) spectral analysis (Perkin Elmer FTIR spectrum BX-II) was performed to identify the presence of functional groups, measured in the range 400-4000 cm −1 , with maximum output being less than 1 mW with 64 scans, recorded in transmission mode [Germany]. The organic phytochemicals present in silver nanoparticles prepared in KBr salt were added to a small number of nanoparticles in order to prepare the pellet. The hydrodynamic diameter and stability of the nanoparticles were measured using a DLS (dynamic light scattering) instrument (Malvern Panalytical) [Austria]. The particle size was obtained using a Malvern (1062761) Zetasizer at 25 • C with a measurement position of 2 mm in an aqueous medium [Austria].

Anti-Fungal Activity
The standard disc diffusion method was performedwith the antifungal assays against A. alternata and A. rolfsii fungicide. A. alternata and A. rolfsii fungicides were added in a separate conical flask and mixed thoroughly by agitating slowly. The mixture was poured (10 mL) directly on auto-clave petri dishes. The autoclaved filter paper disc of 4 mm diameter soaked in AgNPs (varying concentration) was placed on each plate for antifungal resistance. The plates were incubated at 27 • C for four days until the growth of fungicides, and zone of inhibitions around the discs were noted and scaled.

Anti-Bacterial Activity
Martinus Beijerinck and Perez introduced the anti-bacterial activity method by disc diffusion method discovered in 1889 [30]. The A-AgNPs and M-AgNPs were examined against the X. Oryzae strain with respect to their anti-bacterial activity. The sterilized PDA (200 mL) was poured into various autoclaved Petri plates. Fresh inoculum of bacterial (150 mL) strains was spread onto multiple petri plates (with numbering) using a sanitized spreader to cultivate bacterial growth. The autoclaved 4 mm filter paper discs were pierced on PDA media infused with different concentrations of A-AgNPs and M-AgNPs (3.0, 6.0, and 10 µL/mL), and deionized water was used as control. Bacterial growth was observed following incubation for 48 h at 37 • C. The zone of inhibition was measured around the well, and the studies were conducted twice against each bacterium to verify the solidity and record the measurements. The correlation of the mean inhibitions of plant pathogen growth were analyzed using ANOVA (one-way analysis of variance), with significant differences in activity being determined using a t-test (p < 0.05).

Results
The green synthesis of AgNPs produced using different plant leaf extracts (A. indica and M. indica) occurs due to reduction of silver salt (precursor) to NPs by biomolecules. The change in the color of the reaction mixture from transparent to brown during synthesis has been reported in many studies [31]. The intensity of synthesized AgNPs was scrutinized using different parameters.

Optical Analysis
Optical analysis was performed by means of UV-Visible spectroscopy characterization for the peak spectrum of AgNPs at a concentration of 1 mM AgNO 3 . The absorption of plant-mediated AgNPs was measured using a UV-Vis spectroscopy instrument ranging from 350 to 600 nm. The absorbance peak, observed at 432 nm (A-AgNPs) and 442 nm (M-AgNPs), as shown in (Figure 4a,b), indicates the formation of AgNPs and the presence of free electrons on the surface of the nanoparticles, known as surface plasmon resonance Physchem 2023, 3 132 (SPR), which is produced by the vibration of the nanoparticles. The spectrum confirms asingle sharp peak for both plant-mediated AgNPs, without extra peaks, also confirming that the NPs are spherical in shape. The absorption spectra of the NPs were used to analyze the intra-band excitations of conduction electrons in the AgNPs, from lowest to highest energy state [32]. The formation of AgNPs occurs due to the enhancement of SPR band intensity, which shifts from red to blue, resulting in an increase in the size of the NPs. According to previous research, the surface plasmon resonance of AgNPs causes an absorption peak in the range between 420 and 450 nm [33]. Similar studies have been reported for AgNPs synthesized using Ocimum sanctum extract, for which SPR absorption takes place at 445 nm, with a sharp peak indicating the small size of the NPs [34]. The uniform shape of the SPR band demonstrates the spherical shape of the AgNPs. The surfaces of the AgNPs resemble plasmon due to their positively charged nuclei and unbound electrons in the conduction band [35]. Mangini et al., studied the interaction of ubiquity with AgNPs using the laser ablation method, showing the shifting of the SPR band to a higher wavelength, such that more extensive aggregation and distribution changes in the NPs could be observed [36]. Khannanov et al., first reported the magnetic properties of Cobalt nanoparticles using the hyper-branched polyester polyol to enhance the proteolytic enzymes. It was observed in their study that the SPR range indicates the formation of Cobalt nanoparticles in the range of 257-276 nm [37]. The higher concentration of phytochemicals (organic molecules present in extract), colloidal uniformity, particle size, and presence of delicate AgNPs are the factors responsible for the broad absorption peak [38]. The color change in the AgNO 3 salt and leaf extract from transparent to brown is dependent on temperature, concentration, and reaction time. The addition of plant extract at higher concentration decreases the chances of AgNPs formation. The growth of AgNPs from the reduction of metal salt follows the pattern of Ostwald ripening. The plasmon peak depends on the dielectric constant: where ε ∞ = high-frequency dielectric constant; ε m = surrounding medium; λ sp = plasmon peak position; and λ p = bulk plasmon frequency [39].
Physchem 2023, 3, FOR PEER REVIEW 9 uniform shape of the SPR band demonstrates the spherical shape of the AgNPs. The surfaces of the AgNPs resemble plasmon due to their positively charged nuclei and unbound electrons in the conduction band [35]. Mangini et al., studied the interaction of ubiquity with AgNPs using the laser ablation method, showing the shifting of the SPR band to a higher wavelength, such that more extensive aggregation and distribution changes in the NPs could be observed [36]. Khannanov et al., first reported the magnetic properties of Cobalt nanoparticles using the hyper-branched polyester polyol to enhance the proteolytic enzymes. It was observed in their study that the SPR range indicates the formation of Cobalt nanoparticles in the range of 257-276 nm [37]. The higher concentration of phytochemicals (organic molecules present in extract), colloidal uniformity, particle size, and presence of delicate AgNPs are the factors responsible for the broad absorption peak [38]. The color change in the AgNO3 salt and leaf extract from transparent to brown is dependent on temperature, concentration, and reaction time. The addition of plant extract at higher concentration decreases the chances of AgNPs formation. The growth of AgNPs from the reduction of metal salt follows the pattern of Ostwald ripening. The plasmon peak depends on the dielectric constant: where ε ∞ = high-frequency dielectric constant; εm = surrounding medium; λsp = plasmon peak position; and λp = bulk plasmon frequency [39].

GIXRD (Grazing Incidence X-ray Diffraction)
GIXRD was used to perform the structural analysis of green-synthesized AgNPs using A. indica and M. indica tree leaves. Four diffraction peaks were observed at 2θ = 38.12, 44.27, 64.54, and 77.29, as shown in (Figure 5a,b) at a scan range of 20 < 2θ < 80 • . The major peaks in the spectra correspond to the (111), (200), (220), and (311) planes, possessing an fcc (face-centered cubic) structure, and resembling JCPDS card no: 04-0783 [40]. The spectra of the AgNPs (A. Indica and M. Indica) were compared using the JCPDS Ag/Ag 2 O NPs range. No additional impurity peaks (oxides) were observed in the spectra, indicating the presence of AgNPs only [41]. Manikandan  where β denotes the broadening of diffraction lines, λ is the wavelength (0.1546 nm), and θ represents Bragg's diffraction angle.
The sharp peaks indicate the spherical shape and crystalline nature of the nanoparticles. As calculated by Debye Scherrer's formula, the average crystallite size for A-AgNPs and M-AgNPs are 9.4 nm and 9.8 nm. The small crystallite size increases the interior volume and surface area, causing nanoparticles lattice contraction [44]. The crystallite size coincides with the orderly coherent diffraction domain, which is always smaller than the TEM. The highest peak, which is at 38.12 in both spectra, describes the actual growth and purity of the AgNPs [45]. The sharpening of the peaks exhibits a size in the nano regime, and indicates the crystalline nature of the NPs [46].

TEM (Size and Shape)
TEM characterization was used to investigate the shape of A-AgNPs and M-AgNPs, and their precise size information. The colloidal solution of A-AgNPs and M-AgNPs was deposited on a carbon-coated grid and dried under normal conditions. The green-synthesized AgNPs were quasi-spherical (high surface area), grown thermodynamically, and anisotropic. The capping agents in phytochemicals enhance monodispersity and crystal growth [46]. The recorded images demonstrated the presence of mono-dispersed nanoparticles with a spherical shape. The size and shape of the nanoparticles are important factors in their antimicrobial activity; smaller particles can easily interact with the cell walls of micro-organisms (RNA and DNA) [47]. The green-synthesized AgNPs were spherical, with average particle sizes of 11.45 nm (A-AgNPs), as shown in Figure 6a-c, including a histogram of size distribution, and 22 nm (M-AgNPs), as shown in Figure 6d-f. The size calculated on the basis of TEM is always smaller than that calculated using DLS. The DLS was used to calculate the hydrodynamic diameter of AgNPs with their capping agents and reducing agents in the form of the phytochemicals present in the vicinity of NPs, whereas TEM directly provides size and structural information.
The aggregation of monodisperse AgNPs was recorded by TEM for the measurements. Previous studies reported by Consolo et al., presented spherical AgNPs with a similar size (5 and 18 nm), synthesized from a strain of Trichoderma harzianum fungus [48]. The crystallite size of the colloidal AgNPs was evaluated using Debye Scherrer's formula: where β denotes the broadening of diffraction lines, λ is the wavelength (0.1546 nm), and θ represents Bragg's diffraction angle. The sharp peaks indicate the spherical shape and crystalline nature of the nanoparticles. As calculated by Debye Scherrer's formula, the average crystallite size for A-AgNPs and M-AgNPs are 9.4 nm and 9.8 nm. The small crystallite size increases the interior volume and surface area, causing nanoparticles lattice contraction [44]. The crystallite size coincides with the orderly coherent diffraction domain, which is always smaller than the TEM. The highest peak, which is at 38.12 in both spectra, describes the actual growth and purity of the AgNPs [45].
The sharpening of the peaks exhibits a size in the nano regime, and indicates the crystalline nature of the NPs [46].

TEM (Size and Shape)
TEM characterization was used to investigate the shape of A-AgNPs and M-AgNPs, and their precise size information. The colloidal solution of A-AgNPs and M-AgNPs was deposited on a carbon-coated grid and dried under normal conditions. The greensynthesized AgNPs were quasi-spherical (high surface area), grown thermodynamically, and anisotropic. The capping agents in phytochemicals enhance monodispersity and crystal growth [46]. The recorded images demonstrated the presence of mono-dispersed nanoparticles with a spherical shape. The size and shape of the nanoparticles are important factors in their antimicrobial activity; smaller particles can easily interact with the cell walls of micro-organisms (RNA and DNA) [47]. The green-synthesized AgNPs were spherical, with average particle sizes of 11.45 nm (A-AgNPs), as shown in Figure 6a-c, including a histogram of size distribution, and 22 nm (M-AgNPs), as shown in Figure 6d-f. The size calculated on the basis of TEM is always smaller than that calculated using DLS. The DLS was used to calculate the hydrodynamic diameter of AgNPs with their capping agents and reducing agents in the form of the phytochemicals present in the vicinity of NPs, whereas TEM directly provides size and structural information. The anti-fungal activity of the AgNPs, presented zones of inhibition of 20 mm and 15 mm against Pyricularia oryzae and A. alternata, respectively [49].
Khatami et al., also described similar spherical AgNPs with an average size of 1-35 nm synthesized using Descurainia sophia, showing good anti-fungal activity. The size of the AgNPs was confirmed by studies suggesting good antimicrobial activity [50].

SEM (Morphology)
A. indica and M. indica tree leaf extracts were used to synthesize the AgNPs, and SEM images were obtained of the leaf extract. The images showed relatively spherical-shaped AgNPs when observed at a magnification of acceleration voltage of 21.84 KX with an angle of 54.00, as shown in Figure 7a at a magnification of 5.00 kV and at low magnification. The aggregation of monodisperse AgNPs was recorded by TEM for the measurements. Previous studies reported by Consolo et al., presented spherical AgNPs with a similar size (5 and 18 nm), synthesized from a strain of Trichoderma harzianum fungus [48].
The anti-fungal activity of the AgNPs, presented zones of inhibition of 20 mm and 15 mm against Pyricularia oryzae and A. alternata, respectively [49].
Khatami et al., also described similar spherical AgNPs with an average size of 1-35 nm synthesized using Descurainia sophia, showing good anti-fungal activity. The size of the AgNPs was confirmed by studies suggesting good antimicrobial activity [50].

SEM (Morphology)
A. indica and M. indica tree leaf extracts were used to synthesize the AgNPs, and SEM images were obtained of the leaf extract. The images showed relatively spherical-shaped AgNPs when observed at a magnification of acceleration voltage of 21.84 KX with an angle of 54.00, as shown in Figure 7a at a magnification of 5.00 kV and at low magnification.
For the multilayer deposition of diluted colloidal AgNPs (different NPs) coated on a silicon substrate, the surface morphologies of A-AgNPs and M-AgNPs synthesized using other plant extracts were spherical at both high and low magnification, with similar results being reported by Torres-Martinez et al., during the synthesis of AgNPs using Mentha spicata extract [51]. Comparable results were observed by Agnihotri et al., in immobilized AgNPs on a silica surface, which showed similar uniformly dispersed NPs in a spherical shape. The images of the AgNPs samples indicate their green synthesis, and the particles were spherical in shape, with agglomeration [52]. Similar results were reported by Kiran et al., who synthesized AgNPs using Eucalyptus tereticornis leaf extract, and tested them against the MCF-7 cancer cell line [53]. The phytochemicals were present on the surface of the AgNPs, affecting the size of the NPs. The synthesized A-AgNPs and M-AgNPs were aggregated in the colloidal solution due to the appropriate quality of phytochemicals attached to the AgNPs.

SEM (Morphology)
A. indica and M. indica tree leaf extracts were used to synthesize the AgNPs, and SEM images were obtained of the leaf extract. The images showed relatively spherical-shaped AgNPs when observed at a magnification of acceleration voltage of 21.84 KX with an angle of 54.00, as shown in Figure 7a at a magnification of 5.00 kV and at low magnification. For the multilayer deposition of diluted colloidal AgNPs (different NPs) coated on a silicon substrate, the surface morphologies of A-AgNPs and M-AgNPs synthesized using other plant extracts were spherical at both high and low magnification, with similar results being reported by Torres-Martinez et al., during the synthesis of AgNPs using Mentha spicata extract [51]. Comparable results were observed by Agnihotri et al., in immobilized AgNPs on a silica surface, which showed similar uniformly dispersed NPs in a spherical shape. The images of the AgNPs samples indicate their green synthesis, and the particles were spherical in shape, with agglomeration [52]. Similar results were reported by Kiran et al., who synthesized AgNPs using Eucalyptus tereticornis leaf extract, and tested them against the MCF-7 cancer cell line [53]. The phytochemicals were present on the surface of the AgNPs, affecting the size of the NPs. The synthesized A-AgNPs and M-AgNPs were aggregated in the colloidal solution due to the appropriate quality of phytochemicals attached to the AgNPs.

Particle Size Analysis
The hydrodynamic diameter of the green-synthesized spherical-shaped A-AgNPs and M-AgNPs was studied using the DLS technique. The surface-active molecules on the surface of the nanoparticles produced stable mono-dispersed colloidal AgNPs. The size of the nanoparticles when measured by DLS (i.e., with a larger size) is dependent on the surrounding metallic core and the thickness of the electrical double layer [54]. The morphology, surface area, composition, particle reactivity, and size distribution of the nanoparticles were observed to be in the range 90-1000 nm. Javed et al., 2020 reported that phytochemicals-capped AgNPs have a large surface area, which plays a vital role in destroying bacteria, fungi, and viruses [55]. As it can be observed from Figure 8a

Particle Size Analysis
The hydrodynamic diameter of the green-synthesized spherical-shaped A-AgNPs and M-AgNPs was studied using the DLS technique. The surface-active molecules on the surface of the nanoparticles produced stable mono-dispersed colloidal AgNPs. The size of the nanoparticles when measured by DLS (i.e., with a larger size) is dependent on the surrounding metallic core and the thickness of the electrical double layer [54]. The morphology, surface area, composition, particle reactivity, and size distribution of the nanoparticles were observed to be in the range 90-1000 nm. Javed et al., 2020 reported that phytochemicals-capped AgNPs have a large surface area, which plays a vital role in destroying bacteria, fungi, and viruses [55]. As it can be observed from Figure 8a Piper Chaba stem extracts and reported the hydrodynamic size to be 122 nm, with a PDI value of~0.221, indicating that the NPs were monodisperse [56]. The average size observed through DLS was greater than that observed via.TEM due to the capping of phytochemicals on the surface of nanoparticles. The shape and size of nanoparticles is dependent on the temperature, pH, reductant (extract), and precursor concentration [57]. The DLS pattern demonstrates the hydrodynamic diameter of synthesized AgNPs, which is influenced by the phytochemicals adsorbed ontothe surface of the NPs. The depth of the electrical double layer, and how it affects the size of the NPs is determined by the presence of AgNPs in colloidal form and on the surface of the NPs. As a result, DLS measurements inflate the size of spherical AgNPs compared to other macroscopic methods [58]. Physchem 2023, 3, FOR PEER REVIEW 13 measurements inflate the size of spherical AgNPs compared to other macroscopic methods [58]. The studies also reported Brownian fluctuations in intensity for smaller particles more than for larger particles [59]. The studies indicate that plant-synthesized NPs aggregate frequently compared to ionic liquids [60]. Similar studies have been published recently by Rana et al., who synthesized AgNPs with a hydrodynamic diameter of 250 nm and a zeta potential value of −13.9 mV [34].

Stability
The stability of AgNPs was also determined using a Zeta-potential instrument. It is essential to know the parameters of stabilized nanoparticles, as the optimal range for highly stable AgNPs is set to be greater than −30 mV and less than +30 mv. The negative zeta potential values of A-AgNPs and M-AgNPs were found at −19.07 mV and −17.   The studies also reported Brownian fluctuations in intensity for smaller particles more than for larger particles [59]. The studies indicate that plant-synthesized NPs aggregate frequently compared to ionic liquids [60]. Similar studies have been published recently by Rana et al., who synthesized AgNPs with a hydrodynamic diameter of 250 nm and a zeta potential value of −13.9 mV [34].

Stability
The stability of AgNPs was also determined using a Zeta-potential instrument. It is essential to know the parameters of stabilized nanoparticles, as the optimal range for highly stable AgNPs is set to be greater than −30 mV and less than +30 mv. The negative zeta potential values of A-AgNPs and M-AgNPs were found at −19.07 mV and −17.2 mV, indicating the stability of NPs Figure 9a,b. The colloidal form of AgNPs averts aggregation due to repulsion between NPs [61]. The zeta potential also depends on the dispersion of electrolytes and the pH of nanoparticles. The negative charge on the surface of the nanoparticles establishes repulsion between the particles, thus validating their stability. Phanjom et al., synthesized AgNPs and reported similar results for zeta potential, at −14.3 mV [62]. Anandalakshmi et al., reported the zeta potential of AgNPs (Pedalium murex leaf extract) as −7.66 mV, thus demonstrating nanoparticles stability [63]. The negative charge in the functional group of the phytochemicals stabilizes the nanoparticles and prevents them from clustering. Physchem 2023, 3, FOR PEER REVIEW 13 measurements inflate the size of spherical AgNPs compared to other macroscopic methods [58]. The studies also reported Brownian fluctuations in intensity for smaller particles more than for larger particles [59]. The studies indicate that plant-synthesized NPs aggregate frequently compared to ionic liquids [60]. Similar studies have been published recently by Rana et al., who synthesized AgNPs with a hydrodynamic diameter of 250 nm and a zeta potential value of −13.9 mV [34].

Stability
The stability of AgNPs was also determined using a Zeta-potential instrument. It is essential to know the parameters of stabilized nanoparticles, as the optimal range for highly stable AgNPs is set to be greater than −30 mV and less than +30 mv. The negative zeta potential values of A-AgNPs and M-AgNPs were found at −19.07 mV and −17.

FTIR Spectroscopy Analysis
A phytochemicals analysis was performed to identify the presence of azadirachtin, gallic acid, flavonoids, saponins, alkaloids, and Nimbins, as shown in Figure 10a,b. The peak observed in the FTIR spectrum due to the association between the functional group and absorption bands had the ability to enhance the antimicrobial activities of AgNPs synthesized using two different plants [64]. The shifting of FTIR bands in the spectrum demonstrates major and minor shifts that could be due to the stabilization, reduction and capping of AgNPs. The FTIR spectrum of A-AgNPs showed major absorption peaks at 3680, 3454, 3141, 2968, 2567, 1843, 1256, 1119, 868, 700, and 510 cm −1 , which also indicates the presence of phytochemicals (Figure 10a, red). The FTIR spectrum of A. indica leaf extract showed major absorption peaks at 3807, 3538, 3251, 2960, 2608, 1945, 1315, 925, 837, and 602 cm −1 (Figure 10a, black). Similarly, the FTIR spectrum for M-AgNPs showed major absorption peaks for phytochemicals at 3741, 3495, 3405, 3165, 3042, 2873, 2412, 1297, 1132, 809, 559 cm −1 (Figure 10b, red). The FTIR spectrum of M. indica leaf extract showed major absorption peaks at 3834, 3708, 3575, 3288, 3082, 2648, 2177, 1241, 1142, 984, and 810 cm −1 (Figure 10b, black). The peaks observed at 3807, 3741 and 3834 and 3708 cm −1 for the strong -OH band stretching vibrations were detected in both samples and plant extract (Figure 10a  The peaks observed at 3042 and 3082 cm −1 were assigned to CH stretching of the aromatic ring. The methyl group, cycloalkane and aliphatic C-H stretching, and carboxylic acid show a peak at 2567, 2608, 2648, 2873 and 2412 cm −1 . The carboxylic group in the anhydride functional group exhibits the absorption band at 1843, 1945 cm −1 . The peak at 1315, 1256, 1297, and 1241 cm −1 were assigned for C-O/C-H bending and alkyl ketone. The alkyl amine group and OH stretching were observed at 1119, 1132, and 1142 cm −1 and the band at 1012 cm −1 for tertiary alcohol. The ether group (C-O-C) observed the absorption peaks at 925, 984 cm −1 . The peaks were observed at 868, 837, 809, 810, and 700 cm −1 for C-O and C-S stretching in the aliphatic group. The peaks observed at 602 cm −1 are present due to the stretching of the aromatic group, whereas 510 and 559 cm −1 show the presence of the OH group of phenolic. The studies show that protein, polysaccharides, amide group, azadirachtin, phenols, alkaloids, carbohydrates, and fatty acids are required in the reduction of silver metal to silver nanoparticles [66]. The peaks from FTIR indicate the presence of phytochemical compounds that conclude the stability, interaction, and syn- The peaks observed at 3042 and 3082 cm −1 were assigned to CH stretching of the aromatic ring. The methyl group, cycloalkane and aliphatic C-H stretching, and carboxylic acid show a peak at 2567, 2608, 2648, 2873 and 2412 cm −1 . The carboxylic group in the anhydride functional group exhibits the absorption band at 1843, 1945 cm −1 . The peak at 1315, 1256, 1297, and 1241 cm −1 were assigned for C-O/C-H bending and alkyl ketone. The alkyl amine group and OH stretching were observed at 1119, 1132, and 1142 cm −1 and the band at 1012 cm −1 for tertiary alcohol. The ether group (C-O-C) observed the absorption peaks at 925, 984 cm −1 . The peaks were observed at 868, 837, 809, 810, and 700 cm −1 for C-O and C-S stretching in the aliphatic group. The peaks observed at 602 cm −1 are present due to the stretching of the aromatic group, whereas 510 and 559 cm −1 show the presence of the OH group of phenolic. The studies show that protein, polysaccharides, amide group, azadirachtin, phenols, alkaloids, carbohydrates, and fatty acids are required in the reduction of silver metal to silver nanoparticles [66]. The peaks from FTIR indicate the presence of phytochemical compounds that conclude the stability, interaction, and synthesis of AgNPs from A. indica and M. indica. The outcomes of the data do not sync up with the phytochemical testing done on A. indica and M. indica [65].

DPPH Scavenging
The aqueous extract of A. indica and M. indica and their synthesized AgNPs are able to donate electrons or radicals for the study of antioxidant activity by means of DPPH assay as a free radical scavenger.
The antioxidant activity is directly proportional to AgNPs and plant extract concentration. The presence of functional groups in the phytochemicals present in different plants results in natural antioxidants with high reducing capacity. However, our data indicate that the highest scavenging activity of DPPH was achieved at concentrations of 500 mg/mL, with A-AgNPs achieving 85% and M-AgNPs 76%, as demonstrated in Figure 11. The results show better antioxidant activity for AgNPs than standard ascorbic acid (72%). Similar results were produced by Menon et al., who determined the antioxidant activity of Ag-NPs synthesized using the medicinal plant Acalypha indica leaf extract [67]. The freshly prepared DPPH exhibited a purple color due to the donation of electrons from the extract and the nanoparticles, stabilizing the DPPH with a maximum absorbance at 517 nm. The mechanism of antioxidant activity of AgNPs was single electron transfer to the DPPH radical. AgNPs have free radical quenching ability due to the antioxidants in the NPs [68]. However, the antioxidant activity determined in the AgNPs was higher than in ascorbic acid. The higher antioxidant activity in the green-synthesized AgNPs decreased the chances of cancer when entering through the food chain, but they demonstrate cell toxicity to some extent [69].

DPPH Scavenging
The aqueous extract of A. indica and M. indica and their synthesized AgNPs are able to donate electrons or radicals for the study of antioxidant activity by means of DPPH assay as a free radical scavenger.
The antioxidant activity is directly proportional to AgNPs and plant extract concentration. The presence of functional groups in the phytochemicals present in different plants results in natural antioxidants with high reducing capacity. However, our data indicate that the highest scavenging activity of DPPH was achieved at concentrations of 500 mg/mL, with A-AgNPs achieving 85% and M-AgNPs 76%, as demonstrated in Figure  11. The results show better antioxidant activity for AgNPs than standard ascorbic acid (72%). Similar results were produced by Menon et al., who determined the antioxidant activity of AgNPs synthesized using the medicinal plant Acalypha indica leaf extract [67]. The freshly prepared DPPH exhibited a purple color due to the donation of electrons from the extract and the nanoparticles, stabilizing the DPPH with a maximum absorbance at 517 nm. The mechanism of antioxidant activity of AgNPs was single electron transfer to the DPPH radical. AgNPs have free radical quenching ability due to the antioxidants in the NPs [68]. However, the antioxidant activity determined in the AgNPs was higher than in ascorbic acid. The higher antioxidant activity in the green-synthesized AgNPs decreased the chances of cancer when entering through the food chain, but they demonstrate cell toxicity to some extent [69]. Antioxidants swiftly scavenge free radicals and gradually block their production, while antimicrobial agents interact with microbes. Both represent different properties; however, under inflammatory conditions, microbial infection highlights that there is a relationship between antioxidant and antimicrobial activities [70]. Compounds with high antioxidant activity may assist specific pathways that produce antimicrobial peptides inside the body. This could result in the inhibition of microbes. According to the study by Farag et al., phenolic compounds have strong antioxidant activities, thus showing the inhibition of microbes by attaching to the active site of an enzyme protein to stop the metabolic process [71]. Farahmandfar et al. reported the antioxidant and antimicrobial activities of Arum maculatum extracts, where the highest yield was obtained in ethanol and water (50:50). According to this research, there are phytochemicals like phenols, flavonoids, and tannins that may exchange electrons, and are thus added to foods to prevent peroxidation, rather than preserving them artificially. According to this research, Antioxidants swiftly scavenge free radicals and gradually block their production, while antimicrobial agents interact with microbes. Both represent different properties; however, under inflammatory conditions, microbial infection highlights that there is a relationship between antioxidant and antimicrobial activities [70]. Compounds with high antioxidant activity may assist specific pathways that produce antimicrobial peptides inside the body. This could result in the inhibition of microbes. According to the study by Farag et al., phenolic compounds have strong antioxidant activities, thus showing the inhibition of microbes by attaching to the active site of an enzyme protein to stop the metabolic process [71]. Farahmandfar et al. reported the antioxidant and antimicrobial activities of Arum maculatum extracts, where the highest yield was obtained in ethanol and water (50:50). According to this research, there are phytochemicals like phenols, flavonoids, and tannins that may exchange electrons, and are thus added to foods to prevent peroxidation, rather than preserving them artificially. According to this research, Gram-negative and Gram-positive bacteria are both resistant to the antimicrobial effects of plant extracts with high antioxidant content [72].  (Figure 12a-c). The A-AgNPs show larger zones of inhibition for A. alternata and A. rolfsii fungi than M-AgNPs; this could be due to the high degree of synergic antioxidant activity exhibited by A. indica. The negative controls (deionized water) did not show any hindrance effect on the growth of fungi. different plant fungi (A. alternata and A. rolfsii) pathogens. The diameter of the zone of inhibition with respect to the growth of A. alternata fungi was measured with A-AgNPs and M-AgNPs. The largest zones of inhibition against the A. alternata and A. rolfsii fungi were observed at a concentration of 10 μL/mL of A-AgNPs and M-AgNPs. The smallest zone of inhibition was recorded with a 3 mg/mL concentration of AgNPs. Higher antifungal activity against A. alternata and A. rolfsii fungi was observed with increasing concentrations of A-AgNPs. The average diameter of the zone of inhibition expanded with increasing concentrations of AgNPs. The A. alternata and A. rolfsii fungi were tested against A-AgNPs and M-AgNPs at concentrations of 4 μL/mL, 6 μL/mL, and 10 μL/mL (denotes as A1, B1, C1 and A2, B2, C2), respectively, for 48 h in (Figure 12a-c). The A-AgNPs show larger zones of inhibition for A. alternata and A. rolfsii fungi than M-AgNPs; this could be due to the high degree of synergic antioxidant activity exhibited by A. indica. The negative controls (deionized water) did not show any hindrance effect on the growth of fungi.

Anti-Bacterial Activity In Vitro Inhibitory Effect of A-AgNPs and M-AgNPs on the X. Oryzae Bacteria
These studies on the growth and inhibition of X. Oryzae strain demonstrate that A-AgNPs and M-AgNPs at different concentrations (6,8, and 10 µL/mL) inhibit the growth of the bacteria compared with untreated control deionized water. Higher anti-bacterial activity was observed for A-AgNPs than M-AgNPs against the rice pathogen. The zones of inhibition observed for AgNPs against the bacterium are presented in Figure 13a (1,2,3,4) for A-AgNPs and Figure 13b (5,6,7,8) for M-AgNPs. Figure 14 presents the mean of three replicates with the addition of an error bar. The studies were conducted against three different microbes, fungi and bacteria. However, the zone of inhibition was more prone to variance for fungi than for bacteria. A similar study was reported by Rizawan et al., who synthesized AgNPs using Trigonella foenum-graecum L. leaf extract, which were spherical in shape, with a size in the range of 9-37 nm and exhibited sharp absorbance peaks at 380 nm. Ampicillin was used as a standard antibiotic for bacterial studies, and Fluconazole and Carbendazim as standard antifungals against fungi tested at the same concentration as the AgNPs against the same microbes [73]. Physchem 2023, 3, FOR PEER REVIEW growth of the bacteria compared with untreated control deionized water. Higher ti-bacterial activity was observed for A-AgNPs than M-AgNPs against the rice patho The zones of inhibition observed for AgNPs against the bacterium are presented in ure 13a (1,2,3,4) for A-AgNPs and Figure 13b (5,6,7,8) for M-AgNPs.  Figure 14 presents the mean of three replicates with the addition of an error bar. studies were conducted against three different microbes, fungi and bacteria. Howe the zone of inhibition was more prone to variance for fungi than for bacteria. A sim study was reported by Rizawan et al., who synthesized AgNPs using Trigonella num-graecum L. leaf extract, which were spherical in shape, with a size in the range o 37 nm and exhibited sharp absorbance peaks at 380 nm. Ampicillin was used as a sta ard antibiotic for bacterial studies, and Fluconazole and Carbendazim as standard a fungals against fungi tested at the same concentration as the AgNPs against the s microbes [73]. The AgNPs were tested at three working concentrations, revealing that the low MIC (minimum inhibitory concentration) concentration, 6 μL/mL, was effective aga A. rolfsii, A. alternata and X. Oryzae microbes. Similar results were reported agains Aeruginosa with an MIC value of 0.5 μg/mL [74]. Parvekar et al. studied MIC of Ag against Staphylococcus aureus bacteria, obtaining an MIC value of 0.625 mg/mL [75]. et al. synthesized AgNPs using A. alternata fungi and evaluated them against Fusar   Figure 14 presents the mean of three replicates with the addition of an error bar. The studies were conducted against three different microbes, fungi and bacteria. However, the zone of inhibition was more prone to variance for fungi than for bacteria. A similar study was reported by Rizawan et al., who synthesized AgNPs using Trigonella foenum-graecum L. leaf extract, which were spherical in shape, with a size in the range of 9-37 nm and exhibited sharp absorbance peaks at 380 nm. Ampicillin was used as a standard antibiotic for bacterial studies, and Fluconazole and Carbendazim as standard antifungals against fungi tested at the same concentration as the AgNPs against the same microbes [73]. The AgNPs were tested at three working concentrations, revealing that the lowest MIC (minimum inhibitory concentration) concentration, 6 μL/mL, was effective against A. rolfsii, A. alternata and X. Oryzae microbes. Similar results were reported against P. Aeruginosa with an MIC value of 0.5 μg/mL [74]. Parvekar   The AgNPs were tested at three working concentrations, revealing that the lowest MIC (minimum inhibitory concentration) concentration, 6 µL/mL, was effective against A. rolfsii, A. alternata and X. Oryzae microbes. Similar results were reported against P. Aeruginosa with an MIC value of 0.5 µg/mL [74]. Parvekar

Discussion
Chemical fertilizers have been used for a long time to manage plant diseases, and as the demand for food increases due to the increasing population, farmers are under increasing pressure to increase crop growth. Excessive use of pesticides in agriculture causes several health issues, including severe allergies. Due to their large surface area and compact size, NPs have been used in agriculture to increase productivity. AgNPs synthesized using plant extract protect and increase the growth of crops. The antimicrobial mechanism of AgNPs is described in Figure 15.
the demand for food increases due to the increasing population, farmers are under increasing pressure to increase crop growth. Excessive use of pesticides in agriculture causes several health issues, including severe allergies. Due to their large surface area and compact size, NPs have been used in agriculture to increase productivity. AgNPs synthesized using plant extract protect and increase the growth of crops. The antimicrobial mechanism of AgNPs is described in Figure 15. Figure 15. AgNPs mechanism of action for antimicrobial activity. Ag + ions are released from AgNPs during the redox reaction by exchanging electrons and ROS free radicals to react with DNA, protein enzymes, and mitochondria.
The antimicrobial activity of AgNPs studied against plant pathogens disrupts the cell membrane, disrupts the respiration enzyme, and enhances toxicity in microbes by generating ROS, affecting their DNA and RNA and causing cell extinction [77]. The formation of Ag + ions causes the electrostatic interaction of AgNPs through oxidation, which reacts with the negative charge of the cell wall in microbes [78]. Insertion of AgNPs into microbe cells influences the transportation of phosphate ions and thiol groups present in cells for the growth and infection caused in plants and vegetable cells. DNA and RNA structures in cellular carrying cytosine, guanine, pyrimidine, and purine base linked to Ag + ions inhibit the replication of these nucleic acids due to changes in phase from the relaxed state to the condensed state, and also terminate their reproduction [79]. Additionally, free radical species generated by AgNPs when reacting with oxygen during mitochondria metabolism result in methylation breakdown, nitrogenous bases, and carbohydrates [80]. ROS produce hydroxyl, superoxide, hydrogen peroxide, and singlet oxygen, which disorganize the respiratory system of microbes. Sulfur and phosphorous atoms present inside the genome of microbes adhere to the surface of AgNPs, performing electron transfer, thus disturbing respiration and destroying microbes [81]. The mechanism itself explains the importance of plant-derived AgNPs in antimicrobial activities. Figure 15. AgNPs mechanism of action for antimicrobial activity. Ag + ions are released from AgNPs during the redox reaction by exchanging electrons and ROS free radicals to react with DNA, protein enzymes, and mitochondria.
The antimicrobial activity of AgNPs studied against plant pathogens disrupts the cell membrane, disrupts the respiration enzyme, and enhances toxicity in microbes by generating ROS, affecting their DNA and RNA and causing cell extinction [77]. The formation of Ag + ions causes the electrostatic interaction of AgNPs through oxidation, which reacts with the negative charge of the cell wall in microbes [78]. Insertion of AgNPs into microbe cells influences the transportation of phosphate ions and thiol groups present in cells for the growth and infection caused in plants and vegetable cells. DNA and RNA structures in cellular carrying cytosine, guanine, pyrimidine, and purine base linked to Ag + ions inhibit the replication of these nucleic acids due to changes in phase from the relaxed state to the condensed state, and also terminate their reproduction [79]. Additionally, free radical species generated by AgNPs when reacting with oxygen during mitochondria metabolism result in methylation breakdown, nitrogenous bases, and carbohydrates [80]. ROS produce hydroxyl, superoxide, hydrogen peroxide, and singlet oxygen, which disorganize the respiratory system of microbes. Sulfur and phosphorous atoms present inside the genome of microbes adhere to the surface of AgNPs, performing electron transfer, thus disturbing respiration and destroying microbes [81]. The mechanism itself explains the importance of plant-derived AgNPs in antimicrobial activities.
Marwah et al., performed similar studies, monitoring the toxicity of chemically synthesized AgNPs at concentrations of 50, 75, and 100 ppm against Stachybotrys chartarum fungi, which showed zones of inhibition of 21, 26, and 29 mm, respectively [82]. Previous studies have reported that the AgNPs synthesized using methanolic extract show a similar zone of inhibition when tested against human pathogens, which was recorded at 19.25 mm against B. cereus [83]. Recently, Amna et al., carried out similar studies on AgNPs that were 49 nm in size and cubic in shape, which were screened against Colletotricumfalcatum and Fusarium moniliforme fungi, achieving maximum zones of inhibition of 21 mm and 24 mm, respectively [84]. On the basis of the results obtained for both plants for scrutinizing the antimicrobial activity of AgNPs, it was observed that A-AgNPs achieved better results for plant pathogens, fungi, and bacteria. Vanti et al., performed a similar study on the activity of AgNPs synthesized using Solanum torvum against Ralstoniasolana cearum and Xanthomonas axonopodis pv. Punicae bacteria. The highest zones of inhibition were found at 18 mm and 11.4 mm for plant-caused bacteria [85]. Hossain et al. synthesized uniform spherical nanocrystals with a size of 20 to 100 nm for the production of AgNPs using the bacterium Pseudomonas rhodesiae, in order to determine their antibacterial activity against D. dadantii, where a maximum zone of inhibition of 22 nm was observed [86]. Ahmed et al., conducted similar studies on the X. Oryzae bacteria using AgNPs synthesized from the Bacillus cereus strain [87]. Similar work involving Catharanthus roseus plant extract was reported by Roy et al., synthesized iron nanoparticles that were resistant to E. coli and degraded methyl orange dye by 50% [88]. Salve et al., synthesized AgNPs with an average size of 20 nm using Madhuca longifolia leaf extract, which were studied with respect to their anti-inflammatory (protein denaturation) activity against E. coli bacteria and their anticancer activity [89]. The AgNPs were found to be spherically shaped, with a size in the range of 18-39 nm, and with respect to their antibacterial activity, showed a zone of inhibition of 25.11 nm. The studies carried out in this paper during the screening of AgNPs with plant pathogens in the absence of any antibiotic demonstrate higher anti-fungal activity than antibacterial activity.

Conclusions
This study concludes that green synthesis, which is essential for production of NPs, using A. indica and M. indica tree leaf extract is environmentally friendly and cost-effective, with natural capping and reducing agents. AgNPs synthesized from plant extract (A. indica and M. indica) possessed higher antioxidant activity in concentrations ranging from 50 to 500 mg/mL compared with standard ascorbic acid. The green-synthesized AgNPs showed good antimicrobial activity against plant pathogens. However, the A-AgNPs and M-AgNPs have not been compared together with A. alternata, A. rolfsii fungi and X. Oryzae bacteria. Due to variations in antioxidant and antibacterial levels, these plant extracts demonstrated varying zones of inhibition against microorganisms. A-AgNPs proved to possess higher anti-fungal activity than M-AgNPs, with a zone of inhibition of 21 and 16 mm, compared to anti-bacterial activity, where the zone of inhibition of 15 mm was highly influenced at a concentration of 6-10 µL/mL. The AgNPs exhibited greater antifungal activity after four days than antibacterial efficacy after two days. The free radical and cation of Ag + ions react with sulfur and phosphorous elements. The use of plant extract added many natural benefits to NPs, with less pollution and excellent efficiency in nanotechnology techniques. Therefore, synthesizing AgNPs from leaf extract is a cost-effective, time-saving, and reagent-free way of preparing phytoremediation products to restrict phytopathogen growth. The antimicrobial activity of AgNPs reduces the potency of pathogens, thus preserving the agricultural system.