Strength, Porosity and Permeability Properties of Porous Concrete Made from Recycled Concrete Aggregates

: Due to expansion in infrastructure and increased development of urbanization in Ethiopia, most of the places are covered either by impermeable cement concrete or bitumen that blocks the percolation of water from rainfall. A porous concrete made of zero ﬁne aggregates, creating a pore that permits the concrete to be water permeable, is highly desirable. Similarly, the demand for natural coarse aggregates remains high, while natural resources are being depleted. Therefore, this study aims to investigate the properties of porous concrete using recycled concrete aggregate as a partial replacement for natural coarse aggregate. Experimental tests were conducted on cement setting time, workability of concrete, compressive, split tensile, porosity, and permeability of porous concrete. The properties of porous concrete at different ratios—0, 15, 30, 45 and 60%—revealed that RCA is suitable for use as coarse aggregate. The optimum replacement percentage of recycled aggregate for porous concrete in terms of strength is 30%, with 28th-day compressive strength of 17.37 MPa. However, slight increments were observed in porosity and permeability coefﬁcient. Therefore, the concrete produced in this study is structural concrete, which is suitable for walkways and other concrete ﬂat works, whereby heavy vehicle trafﬁc loads do not exist.


Introduction
The production of concrete ingredients commonly implies high energy costs and causes environmental pollution. Therefore, producing sustainable and eco-friendly concrete is highly desirable for reducing the carbon footprint of concrete [1,2]. Additionally, natural resources are being consumed at an increasing rate in today's world due to rapid urbanization and increased demand [3]. This increased demand for natural resources leads to the depletion of virgin concrete ingredients, which is a critical issue for the construction industry, particularly in developing countries [1]. Moreover, environmentally friendly concrete that uses less energy and emits less carbon during its production than conventional concrete is called green concrete. This concrete is a good alternative to conventional concrete in terms of wise consumption of natural resources. Hence, replacing conventional concrete constituent materials with other alternative raw materials makes green concrete more environmentally friendly. As a result, it is often thought to be cheap to produce concrete with recycled aggregate to avoid extra charges for the disposal of waste, consume less energy, and achieve higher durability [4,5].
Several studies have reported that large quantities of waste are generated every year by the construction industry. The waste continues to instigate serious problems both locally and globally [6,7]. Hence, the trends in the last decade have been to increase the recycling Crushed stone gravel of natural basaltic origin conforming to ASTM C 33 was used as coarse aggregate [16]. According to the A.C.I. 522R (2010) committee report, the coarse aggregate size used for porous concrete is either of a single size or with gradings ranging from 19 mm to 9.5 mm. Therefore, aggregates with gradings between 20 mm and 4.75 mm, with a maximum size of 20 mm, were included. Additionally, corrective measures like blending of the aggregate to meet the grading requirements and washing it to make it free from impurities like silt, clay, dirt and inorganic matter were conducted before proceeding to the mix proportion. The particle size distribution of the aggregate was analyzed, and the obtained result fulfilled the ASTM C 33 standard specification of coarse aggregate for concrete production. This test method is mainly used to identify the classification of materials being used as aggregates. The results are shown in Figure 1. Constr. Mater. 2023, 4, FOR PEER REVIEW 3 and conforming to ISO-9001:2015, was used in the production of all concrete specimens. The cement class PPC 32.5 R is a versatile all-purpose cement with superior workability, reduced water demand, and superior cohesion, strength and low emissions; it is a rapidsetting cement and provides good early strength. It can also be used to produce lowstrength concrete, which is also suitable for porous concrete. The properties of the cement were tested as per ASTM C187, ASTM C191, ASTM C184 and ASTM C188, respectively, and summarized in Table 1. Crushed stone gravel of natural basaltic origin conforming to ASTM C 33 was used as coarse aggregate [16]. According to the A.C.I. 522R (2010) committee report, the coarse aggregate size used for porous concrete is either of a single size or with gradings ranging from 19 mm to 9.5 mm. Therefore, aggregates with gradings between 20 mm and 4.75 mm, with a maximum size of 20 mm, were included. Additionally, corrective measures like blending of the aggregate to meet the grading requirements and washing it to make it free from impurities like silt, clay, dirt and inorganic matter were conducted before proceeding to the mix proportion. The particle size distribution of the aggregate was analyzed, and the obtained result fulfilled the ASTM C 33 standard specification of coarse aggregate for concrete production. This test method is mainly used to identify the classification of materials being used as aggregates. The results are shown in Figure 1.

Recycled Concrete Aggregate (RCA)
As shown in Figure 2, recycled concrete aggregate obtained from a demolished concrete building at Jimma University's Hotel and Tourism project site and conforming to ASTM C 33 was used after crushing it to the specified grade, as shown in Table 2. During the recycling process, several impurities were eliminated by sorting the demolished concrete waste from the site before disposal, removing unnecessary attachments, crushing by jackhammer, loading and transporting it to the laboratory, resizing it by hammer to the

Recycled Concrete Aggregate (RCA)
As shown in Figure 2, recycled concrete aggregate obtained from a demolished concrete building at Jimma University's Hotel and Tourism project site and conforming to ASTM C 33 was used after crushing it to the specified grade, as shown in Table 2. During the recycling process, several impurities were eliminated by sorting the demolished concrete waste from the site before disposal, removing unnecessary attachments, crushing by jackhammer, loading and transporting it to the laboratory, resizing it by hammer to the desired size, and washing it to remove fine particles and some of the old mortar. The grain size distribution for recycled concrete aggregate also fulfilled the requirements of ASTM C 33, as shown in Figure 1. Constr. Mater. 2023, 4, FOR PEER REVIEW 4 desired size, and washing it to remove fine particles and some of the old mortar. The grain size distribution for recycled concrete aggregate also fulfilled the requirements of ASTM C 33, as shown in Figure 1.  Tap water supplied to the Jimma university construction laboratory from the Jimma town water and sewerage authority was utilized in the production, curing and soaking of the samples.

Methods
Engineering property tests were conducted on the materials to determine their suitability for concrete production. Mix design for the control concrete group and the recycled concrete aggregate replaced concrete group were determined per the A.C.I. 522R, 2010 design standard. Cube molds with dimensions of 150 mm × 150 mm × 150 mm and cylinder molds with dimensions of 200 mm × 100 mm were used to cast the specimen with partial replacement of 0, 15, 30, 45 and 60% normal coarse aggregate with recycled concrete aggregate. According to ACI 522R, (2010), the minimum and maximum compressive strength required for porous concrete made up of natural aggregate ranges between 2.8 and 28 MPa, respectively, with typical values of about 17 MPa, which is suitable for a wide range of applications, such as light-traffic roads, parking lots, residential streets, and pavement sidewalks. In order to obtain a proper mix of RCA, several concrete samples were cast at different mix ratios, and the compressive strength was tested; whereby it was observed that the compressive strength of the concrete decreased significantly when the ratio of RCA was more than 50%, even though it is within the range specified in ACI. Then, it was decided to analyze the effect of the replacement up to 60%. Therefore, a target compressive strength of 17.37 MPa at 30% replacement of RCA is suitable for the intended use. Therefore, 15 to 60% was chosen in order to find the optimum percentage of RCA required  Tap water supplied to the Jimma university construction laboratory from the Jimma town water and sewerage authority was utilized in the production, curing and soaking of the samples.

Methods
Engineering property tests were conducted on the materials to determine their suitability for concrete production. Mix design for the control concrete group and the recycled concrete aggregate replaced concrete group were determined per the A.C.I. 522R, 2010 design standard. Cube molds with dimensions of 150 mm × 150 mm × 150 mm and cylinder molds with dimensions of 200 mm × 100 mm were used to cast the specimen with partial replacement of 0, 15, 30, 45 and 60% normal coarse aggregate with recycled concrete aggregate. According to ACI 522R, (2010), the minimum and maximum compressive strength required for porous concrete made up of natural aggregate ranges between 2.8 and 28 MPa, respectively, with typical values of about 17 MPa, which is suitable for a wide range of applications, such as light-traffic roads, parking lots, residential streets, and pavement sidewalks. In order to obtain a proper mix of RCA, several concrete samples were cast at different mix ratios, and the compressive strength was tested; whereby it was observed that the compressive strength of the concrete decreased significantly when the ratio of RCA was more than 50%, even though it is within the range specified in ACI. Then, it was decided to analyze the effect of the replacement up to 60%. Therefore, a target compressive strength of 17.37 MPa at 30% replacement of RCA is suitable for the intended use. Therefore, 15 to 60% was chosen in order to find the optimum percentage of RCA required for porous concrete. The cast specimens were tested after 7, 14 and 28 days of curing. Destructive test like compressive strength and non-destructive tests like porosity and permeability tests were conducted.

Mix Proportion
Mix design for porous concrete with strengths ranging between 2.8 and 28 MPa, as per the A.C.I. 522R-2010 recommendations, were used. The mix proportions for normal porous concrete with replacement of various percentages with recycled concrete aggregate (RCA) porous concrete are given in Table 3. The quantity of cement for each experimental group was kept constant, and the water-cement ratio varied with increasing amount of recycled concrete aggregate, due to its higher water absorption capacity. For all tests, three samples were tested, and the mean values are reported.

Workability Test
Workability is the degree of mobility of the concrete and its easiness to work with [17]. Conventionally, it is checked by a vertically uplifting slump cone with a height of 300 mm, a diameter of 200 mm at the top, and a diameter of 100 mm at the bottom. However, this procedure is not appropriate for very wet or very dry concrete mixes. Hence, performing compacting factor tests or testing the density ratio of the weight of partially compacted concrete to the weight of fully compacted concrete is particularly useful for porous concrete mixes with very low Workability. The corresponding compacting factor result is calculated as shown in Equation (1)

Compressive Strength Test
Tests related to the compressive strength of the concrete were conducted at 7, 14, and 28 curing days, as shown in Figure 3. The strength was determined by dividing the maximum load attained for the cross-sectional area of the cube specimen, as shown in Equation (2) [18].

Porosity Test
Porosity is the ratio of voids in the concrete to the total volume (V) of the sample. The test was performed by dividing the difference between the oven-dry weight of the sample (Md) and the weight of the submerged sample in the water tank for a minimum of 30 min

Porosity Test
Porosity is the ratio of voids in the concrete to the total volume (V) of the sample. The test was performed by dividing the difference between the oven-dry weight of the sample (Md) and the weight of the submerged sample in the water tank for a minimum of 30 min (Mw) by the water density (δ w ) to determine porosity (P) using Equation (3) [19]. The test is shown in Figure 4.
where P = Porosity, Md = Mass of oven-dried sample, Mw = Mass of the submerged sample in the water tank for a minimum of 30 min, δ w = Density of water, V = Total volume of sample.

Porosity Test
Porosity is the ratio of voids in the concrete to the total volume (V) of the sample. The test was performed by dividing the difference between the oven-dry weight of the sample (Md) and the weight of the submerged sample in the water tank for a minimum of 30 min (Mw) by the water density (δw) to determine porosity (P) using Equation (3) [19]. The test is shown in Figure 4.

Permeability Test
The most important feature of the porous concrete is to allow the percolation of water passing through the porous medium. The test was conducted using a constant head method [20]. The coefficient of permeability was obtained using Darcy's law, as shown in Equation (4), which was preliminarily used as a falling head test to obtain its coefficient as per standard procedures [21].
where Q = Quantity of water discharged cm 3 , K = Coefficient of permeability (cm/s), L = Length of specimen (cm),

Permeability Test
The most important feature of the porous concrete is to allow the percolation of water passing through the porous medium. The test was conducted using a constant head method [20]. The coefficient of permeability was obtained using Darcy's law, as shown in Equation (4), which was preliminarily used as a falling head test to obtain its coefficient as per standard procedures [21].
where Q = Quantity of water discharged cm 3 , K = Coefficient of permeability (cm/s), L = Length of specimen (cm), t = Total time of discharge (s), A = Cross-section area of specimen (cm 2 ), h = Difference in head on manometer (cm).

Compaction Factor Test Results
Very dry and wet mixes do not enable the correct slump height to be achieved and are not suitable for use with the conventional compaction method. Hence, the compaction factor test was conducted to determine the degree of Workability by allowing the mix to fall through successive hoppers of standard height using a compaction factor test apparatus. This test is a suitable method for testing the compacting factor limits from very low to high Workability, with possible values of 0.78, 0.85, 0.92 and 0.95, which indicate very low, low, medium, and high Workability, respectively as in Table 4. The results confirmed that, with increasing percentage of recycled aggregate, (1) the water absorption from cement paste increases when the aggregate is dry, due to a the high void ratio; (2) water is released into the interfacial transition zone when the aggregate is moist; and (3) the cement materials penetrate into the pores, in contrast to natural coarse aggregate.
This work highlights the need for a roller compacting technique for a concrete mix that is characterized as harsh.

Compressive Strength Test Results
The average compressive strength results of cubes for both the natural aggregate mix and the mix with recycled concrete aggregate replacement were determined and evaluated on the 7th, 14th, and 28th curing days by crushing the samples using a Universal Testing Machine. The corresponding mean strength is presented in Figure 5.

Compaction Factor Test Results
Very dry and wet mixes do not enable the correct slump height to be achieved and are not suitable for use with the conventional compaction method. Hence, the compaction factor test was conducted to determine the degree of Workability by allowing the mix to fall through successive hoppers of standard height using a compaction factor test apparatus. This test is a suitable method for testing the compacting factor limits from very low to high Workability, with possible values of 0.78, 0.85, 0.92 and 0.95, which indicate very low, low, medium, and high Workability, respectively as in Table 4. The results confirmed that, with increasing percentage of recycled aggregate, (1) the water absorption from cement paste increases when the aggregate is dry, due to a the high void ratio; (2) water is released into the interfacial transition zone when the aggregate is moist; and (3) the cement materials penetrate into the pores, in contrast to natural coarse aggregate.
This work highlights the need for a roller compacting technique for a concrete mix that is characterized as harsh.

Compressive Strength Test Results
The average compressive strength results of cubes for both the natural aggregate mix and the mix with recycled concrete aggregate replacement were determined and evaluated on the 7th, 14th, and 28th curing days by crushing the samples using a Universal Testing Machine. The corresponding mean strength is presented in Figure 5.  As shown, with increasing percentage of recycled aggregates in the mixes, there is a decrease in the compressive strength of the cube. For the natural aggregate mix (0% RCA), the 28th-day compressive strength was 25.63 MPa. This mix is considered to be a reference (control) mix for the purpose of comparison with the RCA replaced mix.
As per the A.C.I. 522R 10 guidelines, the compressive strength of natural aggregate porous concrete ranges between 2.8 and 28 MPa, with typical average values of about 17 MPa, which is suitable for a wide range of applications, such as light traffic pavements, parking lots, residential streets, and pavement sidewalks. These experimental results show that for all RCA replacement levels, the compressive strength values fall within the range stipulated in the standard.
For the 45% and 60% RCA replacement levels, the compressive strength results after the 28th day were less than the typical average value of 17 MPa implemented in most required application areas. However, for the 15% and 30% RCA replacement levels, the results were higher than the typical average value of 17 MPa. From this study, the 30% replacement of recycled concrete aggregate was found to provide the optimum level of RCA replacement for porous concrete.
As shown in Figure 5, the compressive strength test results decrease with increasing percentage of recycled aggregate, which reduces the bond strength between cement paste and aggregates. In addition, this affects the strength development of the concrete at the microstructure level by forming different Interfacial Transition Zones (I.T.Z.) during the strength development stages of the concrete [19]. Therefore, the RCA should not have a rough surface structure (old mortar), which is the main drawback to the decreased strength of porous concrete with recycled aggregate replacement.

Porosity Test Results
The porosity test was performed as per the standard [20], by dividing the difference between the 24 h oven-dried weight of the sample (Md) and the weight of the sample submerged in a water tank for a minimum of 30 min (Mw) by the water density. The corresponding test results on the 28th day for RCA replacements of 0, 15, 30, 45 and 60% were approximately the same, as shown in Figure 6.
porous concrete ranges between 2.8 and 28 MPa, with typical average values of about 17 MPa, which is suitable for a wide range of applications, such as light traffic pavements, parking lots, residential streets, and pavement sidewalks. These experimental results show that for all RCA replacement levels, the compressive strength values fall within the range stipulated in the standard.
For the 45% and 60% RCA replacement levels, the compressive strength results after the 28th day were less than the typical average value of 17 MPa implemented in most required application areas. However, for the 15% and 30% RCA replacement levels, the results were higher than the typical average value of 17 MPa. From this study, the 30% replacement of recycled concrete aggregate was found to provide the optimum level of RCA replacement for porous concrete.
As shown in Figure 5, the compressive strength test results decrease with increasing percentage of recycled aggregate, which reduces the bond strength between cement paste and aggregates. In addition, this affects the strength development of the concrete at the microstructure level by forming different Interfacial Transition Zones (I.T.Z.) during the strength development stages of the concrete [19]. Therefore, the RCA should not have a rough surface structure (old mortar), which is the main drawback to the decreased strength of porous concrete with recycled aggregate replacement.

Porosity Test Results
The porosity test was performed as per the standard [20], by dividing the difference between the 24 h oven-dried weight of the sample (Md) and the weight of the sample submerged in a water tank for a minimum of 30 min (Mw) by the water density. The corresponding test results on the 28th day for RCA replacements of 0, 15, 30, 45 and 60% were approximately the same, as shown in Figure 6. For every 15% increase in the RCA replacement ratio in the concrete, the porosity ratio of the porous concrete increased. For example, the increment at 28 days with increasing recycled concrete aggregate was 8.45, 12.95, 14.94 and 16.26% for 15, 30, 45 and 60% of RCA, respectively, compared to the control mix. This increment was in the range of approximately 8 to 16% for RCA contents of 15 to 60%. This indicates that porous concrete with recycled aggregate contains not only virgin aggregate, but also hydrated cement For every 15% increase in the RCA replacement ratio in the concrete, the porosity ratio of the porous concrete increased. For example, the increment at 28 days with increasing recycled concrete aggregate was 8.45, 12.95, 14.94 and 16.26% for 15, 30, 45 and 60% of RCA, respectively, compared to the control mix. This increment was in the range of approximately 8 to 16% for RCA contents of 15 to 60%. This indicates that porous concrete with recycled aggregate contains not only virgin aggregate, but also hydrated cement paste, which reduces the specific gravity and increases porosity. Additionally, the void ratio of this concrete was beyond the acceptable range of 36-43%, which affects the Workability and strength of the concrete.

Permeability Test Results
The permeability of porous concrete is an important parameter for evaluating the suitability of using porous concrete for pavement sidewalks, residential streets, tennis courts, light traffic roads, and parking lots. It mainly depends on the size and pore structures of the concrete. The test was conducted by providing sufficient voids through which water could drain or pass safely into the sub-base or subgrade layers of the pavement. Researchers have argued that porous concrete generally has high permeability compared to normal dense concrete, and the permeability test method may not be suitable for testing porous concrete. Keeping this view in mind, a permeability test was conducted to estimate the permeability coefficient of porous concrete. The infiltration test for water to pass through pores of porous concrete was expressed in centimeters per second (cm/s), as per the ASTM-C1701 [21] standard, and the results are shown in Figure 7.
The permeability of porous concrete is an important parameter for evaluating the suitability of using porous concrete for pavement sidewalks, residential streets, tennis courts, light traffic roads, and parking lots. It mainly depends on the size and pore structures of the concrete. The test was conducted by providing sufficient voids through which water could drain or pass safely into the sub-base or subgrade layers of the pavement. Researchers have argued that porous concrete generally has high permeability compared to normal dense concrete, and the permeability test method may not be suitable for testing porous concrete. Keeping this view in mind, a permeability test was conducted to estimate the permeability coefficient of porous concrete. The infiltration test for water to pass through pores of porous concrete was expressed in centimeters per second (cm/s), as per the ASTM-C1701 [21] standard, and the results are shown in Figure 7. With increasing percentage of RCA in the mix, the permeability of the concrete increases due to the increasing void ratio or porosity of the concrete. This shows the direct relationship of porosity and permeability with the RCA replacement amount. Furthermore, Figure 7 shows that the coefficient of permeability (k) increases with every additional 15% inclusion of RCA by anywhere from 17.12 to 35.66%.

Relationship between the RCA, Strength, Porosity and Permeability Properties of the Concrete
The main challenges encountered during porous concrete mixture proportioning were determining aggregate size, aggregate cement ratio, and water-cement ratio, and the balance between acceptable values of compressive strength, porosity, and water percolation rate. The strength properties of porous concrete decrease with increasing aggregate size [22,23]. However, porosity has a direct relationship with permeability and RCA replacement percentage. Increasing the percentage of RCA increases the porosity, resulting in faster discharge of water through the concrete pores, and consequently, a decrease in With increasing percentage of RCA in the mix, the permeability of the concrete increases due to the increasing void ratio or porosity of the concrete. This shows the direct relationship of porosity and permeability with the RCA replacement amount. Furthermore, Figure 7 shows that the coefficient of permeability (k) increases with every additional 15% inclusion of RCA by anywhere from 17.12 to 35.66%.

Relationship between the RCA, Strength, Porosity and Permeability Properties of the Concrete
The main challenges encountered during porous concrete mixture proportioning were determining aggregate size, aggregate cement ratio, and water-cement ratio, and the balance between acceptable values of compressive strength, porosity, and water percolation rate. The strength properties of porous concrete decrease with increasing aggregate size [22,23]. However, porosity has a direct relationship with permeability and RCA replacement percentage. Increasing the percentage of RCA increases the porosity, resulting in faster discharge of water through the concrete pores, and consequently, a decrease in compressive strength. As shown on Figure 8, the mean compressive strength of concrete decreases as the percentage of RCA increases, while both porosity and permeability increase. Therefore, by combining all the sizes of coarse aggregates between 20 and 4.75 mm and 30% RCA by weight of natural coarse aggregate, the required compressive strength (17 MPa), sufficient porosity, and permeability requirements were achieved in this study.
compressive strength. As shown on Figure 8, the mean compressive strength of concrete decreases as the percentage of RCA increases, while both porosity and permeability increase. Therefore, by combining all the sizes of coarse aggregates between 20 and 4.75 mm and 30% RCA by weight of natural coarse aggregate, the required compressive strength (17 MPa), sufficient porosity, and permeability requirements were achieved in this study.

Discussion
The test results show that the degree of Workability of the concrete slightly decreased from medium to low with increasing amount of recycled concrete aggregate. A similar conclusion was formulated in [24]. For the recycled aggregate mixes, their 28th-day compressive strengths were 21.42, 17.37, 14.96 and 11.61 MPa for 15, 30, 45 and 60% recycled aggregates, respectively. Compared with the control mix, the compressive strengths decreased from 16.43 to 54.70% when the percentages of RCA in the mix was increased from 15 to 60%. The increased amount of RCA affected the strength development of the concrete due to the high void ratio and high water absorption capacity of the old mortars surrounding the RCA. This, in turn, affected the strength development of the concrete by reducing the bond between cement paste and aggregate, as well as the formation of different interfacial transition zones. This finding also confirms the findings reported in previous research [25,26], which concluded that the presence of adhered mortar on the surface of an overwhelmed concrete mixture usually degrades the quality of the recycled mixture, and therefore the fresh and hardened residences of concrete crafted from it compared to natural aggregates. Similar results were reported in [27] and [28], showing that compressive strength decreases with increasing recycled aggregate percentage and porosity.
As shown in Figure 7, the porosity of the concrete increases with increasing ratio of RCA. The cause of this extra porosity is the lack of fine aggregate (sand) and the uniformsized coarse aggregate in the design of the mix. This, in turn, affects the Workability of the fresh concrete due to the presence of old mortar pores, which absorb a high amount of water during mixing. Therefore, the high-water absorption of RCA results in a decrease in the Workability of fresh concrete and the bonding strength of hardened concrete due to the presence of old mortar on its surface.
This finding was independently confirmed in [29,30], where recycled aggregates were reported to have a higher porosity than natural aggregates, causing a decrease in the mechanical properties and durability of the concrete.
The maximum permeability value of 2.86 cm/s was measured for 60% replacement of RCA by weight of natural coarse aggregate to produce porous concrete. Minimum permeability requirements of 0.2 cm/s to 1.20 cm/s are reported in the standard [31]. The rate of permeability measured during the tests ranges from 1.84 to 2.86 cm/s, demonstrating that good permeability and infiltration capacity have been achieved.

Discussion
The test results show that the degree of Workability of the concrete slightly decreased from medium to low with increasing amount of recycled concrete aggregate. A similar conclusion was formulated in [24]. For the recycled aggregate mixes, their 28th-day compressive strengths were 21.42, 17.37, 14.96 and 11.61 MPa for 15, 30, 45 and 60% recycled aggregates, respectively. Compared with the control mix, the compressive strengths decreased from 16.43 to 54.70% when the percentages of RCA in the mix was increased from 15 to 60%. The increased amount of RCA affected the strength development of the concrete due to the high void ratio and high water absorption capacity of the old mortars surrounding the RCA. This, in turn, affected the strength development of the concrete by reducing the bond between cement paste and aggregate, as well as the formation of different interfacial transition zones. This finding also confirms the findings reported in previous research [25,26], which concluded that the presence of adhered mortar on the surface of an overwhelmed concrete mixture usually degrades the quality of the recycled mixture, and therefore the fresh and hardened residences of concrete crafted from it compared to natural aggregates. Similar results were reported in [27] and [28], showing that compressive strength decreases with increasing recycled aggregate percentage and porosity.
As shown in Figure 7, the porosity of the concrete increases with increasing ratio of RCA. The cause of this extra porosity is the lack of fine aggregate (sand) and the uniformsized coarse aggregate in the design of the mix. This, in turn, affects the Workability of the fresh concrete due to the presence of old mortar pores, which absorb a high amount of water during mixing. Therefore, the high-water absorption of RCA results in a decrease in the Workability of fresh concrete and the bonding strength of hardened concrete due to the presence of old mortar on its surface.
This finding was independently confirmed in [29,30], where recycled aggregates were reported to have a higher porosity than natural aggregates, causing a decrease in the mechanical properties and durability of the concrete.
The maximum permeability value of 2.86 cm/s was measured for 60% replacement of RCA by weight of natural coarse aggregate to produce porous concrete. Minimum permeability requirements of 0.2 cm/s to 1.20 cm/s are reported in the standard [31]. The rate of permeability measured during the tests ranges from 1.84 to 2.86 cm/s, demonstrating that good permeability and infiltration capacity have been achieved.
Research conducted on the effect of sand on pervious concrete by [32] argued that the porosity and permeability of pervious concrete decrease with the increase in sand content, but the mechanical properties (strength) of the concrete increase.

Conclusions
This research presented experimental studies on the effects of recycled concrete aggregate on the properties of porous concrete. Based on the findings of the study, the following conclusions were drawn: Increasing the percentage of recycled concrete aggregate decreases the degree of Workability of the porous concrete from medium to low.
The average compressive strength of the porous concrete decreased by between 16.43 and 54.70% for every 15% increase in RCA This is due to the presence of adhered mortar on the RCA, which absorbs the designated mixing water and reduces the amount of cement paste, reducing the bond strength between the cement paste and the coarse aggregate. The cube compressive strengths of 21.42 MPa and 17.37 MPa for 15 and 30% RCA replacement were higher than the typical value (17 MPa) used in non-structural construction applications.
The porosity of the concrete increases slightly with every 15% increase in RCA by an amount in the range of 8 to 16% due to the increased coarseness of aggregate in the mix and the lack of fine aggregates in the mix. This indicates that there is a direct relationship between RCA content and the void ratio of the produced porous concrete.
The permeability of porous concrete increases with increasing RCA content by between 17.12 and 35.66% due to the increased void ratio. The value ranges from 1.84 to 2.86 cm/s, which is high enough to be used as a drainage system. This shows that as the percentage of RCA increases in the mixes, the permeability of the concrete increases.
Increasing the percentage of recycled concrete aggregate increases porosity and permeability and decreases the compressive strength of the porous concrete.
Overall, recycled concrete aggregate has a significant effect on the properties of porous concrete. With increasing percentage of RCA, the higher the porosity, the faster the water permeability rate, and the lower the strength of the final concrete.