Developments in Mask-Free Singularly Addressable Nano-LED Lithography

: LED devices are increasingly gaining importance in lithography approaches due to the fact that they can be used flexibly for mask-less patterning. In this study, we briefly report on developments in mask-free lithography approaches based on nano-LED devices and summarize our current achievements in the different building blocks needed for its application. Individually addressable nano-LED structures can form the basis for an unprecedented fast and flexible patterning, on demand, in photo-chemically sensitive films. We introduce a driving scheme for nano-LEDs in arrays serving for a singularly addressable approach. Furthermore, we discuss the challenges facing nano-LED fabrication and possibilities to improve their performance. Additionally, we introduce LED structures based on a hybrid nanocrystal/nano-LED approach. Lastly, we provide an outlook how this approach could further develop for next generation lithography systems. This technique has a huge potential to revolutionize the field and to contribute significantly to energy and resources saving device nanomanufacturing.


Introduction
Although a large amount of work was carried out on the development of optical lithographical techniques during the last half century, there still is a lack of fast and cheap as well as energy and resources saving solutions.Therefore, next developments in this field will be focused on mask-free approaches, which can serve with an unprecedented flexibility in structure patterning on demand.Nevertheless, several "building blocks" are needed for a new generation mask-less approach, before this could be realized.First, the development of group III nitrides material and appropriate epitaxial techniques were successfully driven forward since the end of the 1980's [1][2][3][4][5][6][7].Additionally, advanced fabrication technologies are required in the micro-down to the nanoscale device processing.Indeed, sophisticated methods for the fabrication of efficient light emitter sources as well as several approaches to produce them down to the micro- [8][9][10][11][12] and to the nanoscale [13][14][15][16][17][18][19][20] were already achieved.With respect to singularly addressable light emitter sources, Orenstein and co-workers reached an important milestone in their pioneering work where matrix driven arrays with surface emitting laser diodes were developed [21][22][23][24] albeit for signal processing and optical communication.The further developments, which represent a significant step forward, were reported on the arrangement of LEDs in arrays [25][26][27][28][29][30][31] and the possibility to drive them preferably singularly (among others for displays) [32][33][34][35][36][37][38][39][40][41][42][43].Hence, if all of these "ingredients/building blocks" are available within a lithography system, in principle, next generation lithography can be carried out mask-free, allowing time and resources savings, flexible structure patterning on demand.Indeed J. N. Kurtin presented in 2005 an array of LED structures suitable for such individually addressable lithographical patterning [44].
Nanomanufacturing 2024, 4 100 The application of UV (microscale) LEDs to lithography was also reported [45][46][47][48][49][50][51][52].Alternative approaches were pursued such as amongst others plasmonic lithography [53].In 2012 and 2015 we presented a first proof of principle [54,55], where nano-LED devices with diameters ~100 nm arranged hexagonally in arrays were used in the lithographical exposure process for "hole" shaped structure fabrication.A "hole" structure size down to about 400 nm was achieved when the nano-LED sources emitted light with a central wavelength of ~405 nm.Finally, in 2020, we presented for the first time (to the best of our knowledge) nano-LED devices with metallic apertures for the lithographical process in the so-called "near-field" regime [56].Photochemical reactions initialized by those nano-emitter devices resulted in a space-lateral distribution of photo-induced reactions in the exposed regions of ~75 nm in diameter.This confirms that nano-LED devices with appropriate apertures for near-field applications can be potentially applied in mass-production successfully for nanomanufacturing.Nevertheless, the ultimate demonstration of single photon lithography was up to now/date not demonstrated.Since favorable photochemical reactions could be theoretically driven by single photons, with an appropriate energy in processes where-depending on the molecule cross-section-one or a couple of photons can alter one chemical bond, this technique would allow to enable the era of mass nanomanufacturing for, e.g., molecular electronics.However, in nowadays/conventional photoresists, a higher yield of incident photons is required for the photochemical reaction.Additionally, before this concept can be realized, suitable single photon sources operated at room temperature, and their industrial mass production, have to be developed.Besides other "light emitting" solutions, our previous studies reveal that III-nitride based nano-LEDs are very promising as multifunctional photon emitting devices, which can be used as hybrid photon emitting sources.In such hybrid device architectures, we presented single nano-LED structures driven electrically, and integrated with freestanding CdSe nanocrystals [57].Such hybrid architectures can serve as testing platforms for the investigation of plasmonic effects.This could be of benefit especially for the sake of field enhancement at the position of a light emitting nanoparticle.Further methods discussed for micro-LEDs with respect to localized surface plasmon enhancement for device improvement [58] and the improvement of light extraction and shaping using metamaterials could in the far future also be applied to nano-LEDs [59] and their employment for future mask-free singularly addressable lithography.Here, in this study, we deliver a short overview/roadmap of the most promising developments in this new arising nanomanufacturing field and present current achievements for (hybrid) nano-LED assisted mask-less lithography.

Materials and Methods
The singularly addressable nano-LEDs employed for the mask-free lithography approach were all based on the same parent structure.To this end 2 ′′ c-plane sapphire substrates were chosen and group III-nitride heterostructures were deposited by metalorganic vapor phase epitaxy (MOVPE).First, n-doped GaN 5 × 10 18 cm −3 was grown followed by a five-fold superlattice structure consisting of 16 nm GaN barriers and 2.5 nm In 0.16 Ga 0.84 N wells.At last, a 250 nm thick GaN layer p-doped to 5 × 10 17 cm −3 followed by 20 nm of p + -doped GaN (6 × 10 18 cm −3 ) were deposited.
In the next building block nano-LED devices positioned in arrays were defined by using e-beam lithography to pattern holes in the PMMA 600 K resist and subsequent developing in AR 600-55 developer.After the physical vapor deposition (PVD) of Ni and the lift-off process, 100 nm Ni caps were formed serving as the etching mask for the space definition/formation of nano-LEDs.In a first step, reactive ion etching was performed up to the bottom n-doped GaN contact layer in an Oxford Plasmalab 100 reactor with an inductively coupled plasma (ICP) 180 source at a pressure of 4 µbar, a sample temperature of 5 • C, a chlorine:argon gas mixture of 16:4, and an ICP power of 750 W [18,60].In the next step, n-doped GaN bottom contacts (word lines) were defined with the help of optical lithography.The photoresist AZ 5206 was chosen followed by developing in a standard developer (MIF 326).An Ar-ion beam etching process (Ar-IBE, Oxford Instruments, 200 V, Nanomanufacturing 2024, 4 101 20 mA) was carried out down to the sapphire substrate.The nano-LEDs were insulated from neighbors using hydrogen silsesquioxane (HSQ), which was spun onto the structured template to obtain a planar surface.The template was then annealed to induce the chemical reaction to the SiO 2 layer.At last, transparent top contacts (bit lines) were prepared using optical lithography and the same photoresist and developer mentioned above followed by deposition of the transparent Ni/Au (5 nm/5 nm) top-contact metallization and a subsequent conventional rapid thermal annealing process.The nano-LEDs were annealed locally with the laser micro-annealing (LMA) process presented earlier [60].Furthermore, it becomes possible to fabricate an array of hybrid nano-LEDs.A micropipette is used [57,61] to apply the polymer-nanocrystal suspension, the details and procedure of which will be published separately.
The structures were inspected with optical microscopy and scanning electron microscopy (SEM).Furthermore, micro-photoluminescence (µ-PL) and micro-electroluminescence spectroscopy (µ-EL) were carried out at room temperature to assess the fabrication procedure and to evaluate the long-term stability of the nano-LED performance.For both the LMA process as well as the µ-PL and µ-EL spectroscopy experiments, a confocal Raman and photoluminescence spectrometer (Renishaw inVia FSM REFLEX, New Mills, Gloucestershire, UK) was used which was equipped with a HeCd laser (325 nm) and a CCD detector [60].
The basic idea behind mask-free singularly addressable LED lithography is presented in Figure 1.In general, nano-LEDs are arranged in a crossbar geometry, allowing for their individual driving after the fabrication of "word" and "bit" lines.In such a way, different patterns can be "created" on demand flexibly.This lithographical approach has the potential to simplify and accelerate patterning significantly compared to conventional mask-based lithographical processes, since large areas of the photosensitive films/photoresists can be exposed at the same time.
Nanomanufacturing 2024, 4, FOR PEER REVIEW 3 next step, n-doped GaN bottom contacts (word lines) were defined with the help of optical lithography.The photoresist AZ 5206 was chosen followed by developing in a standard developer (MIF 326).An Ar-ion beam etching process (Ar-IBE, Oxford Instruments, 200 V, 20 mA) was carried out down to the sapphire substrate.The nano-LEDs were insulated from neighbors using hydrogen silsesquioxane (HSQ), which was spun onto the structured template to obtain a planar surface.The template was then annealed to induce the chemical reaction to the SiO2 layer.At last, transparent top contacts (bit lines) were prepared using optical lithography and the same photoresist and developer mentioned above followed by deposition of the transparent Ni/Au (5 nm/5 nm) top-contact metallization and a subsequent conventional rapid thermal annealing process.The nano-LEDs were annealed locally with the laser micro-annealing (LMA) process presented earlier [60].Furthermore, it becomes possible to fabricate an array of hybrid nano-LEDs.A micropipette is used [57,61] to apply the polymer-nanocrystal suspension, the details and procedure of which will be published separately.
The structures were inspected with optical microscopy and scanning electron microscopy (SEM).Furthermore, micro-photoluminescence (µ-PL) and microelectroluminescence spectroscopy (µ-EL) were carried out at room temperature to assess the fabrication procedure and to evaluate the long-term stability of the nano-LED performance.For both the LMA process as well as the µ-PL and µ-EL spectroscopy experiments, a confocal Raman and photoluminescence spectrometer (Renishaw inVia FSM REFLEX, New Mills, Gloucestershire, UK) was used which was equipped with a HeCd laser (325 nm) and a CCD detector [60].
The basic idea behind mask-free singularly addressable LED lithography is presented in Figure 1.In general, nano-LEDs are arranged in a crossbar geometry, allowing for their individual driving after the fabrication of "word" and "bit" lines.In such a way, different patterns can be "created" on demand flexibly.This lithographical approach has the potential to simplify and accelerate patterning significantly compared to conventional mask-based lithographical processes, since large areas of the photosensitive films/photoresists can be exposed at the same time.

Results
It is well known that conventional argon ion beam etching (IBE) as well as reactive ion etching (RIE) used for the spatial definition/formation of nano-LEDs leads to a degradation of the devices' optical properties which is manifested by a significant decrease in their electroluminescence [57,60,62].Here, in this study, SEM investigations (Figure 2) reveal inhomogeneous surface nano-LED morphology.This inhomogeneity is a result of the surface damage of the combined physical and chemical reactive ion etching processes.These physical and/or most probably chemical processes take place along the whole surface of the nano-LED.However, a physical damage up to 20 nm was observed only at the "top" of the nanostructure regions.This can be explained by the longer times that the tops of the nanostructures are exposed to the etching reactants during the RIE processes.Deeper regions close to the nano-LED's "base" are affected only by "shorter" etching times (i.e., a shorter exposure) which is manifested among others by "smoother" surface morphology.With respect to the morphology of the nano-LEDs it must be taken into account that the LED parent structure used as the basis for the etched nano-LEDs has a high defect density and defects themselves will most probably affect their morphology.Here it should be noted, that even though the SEM inspection over a large area reveals almost individual surface morphology (damage) for every nano-LED structure, nevertheless, the nano-LEDs all have the same average dimensions (e.g., top and bottom diameter, total height).Therefore, the SEM image in Figure 2 is only an example of such a nano-LED.A comprehensive analysis on the causes of the defects is in preparation and will be the subject of a future report.The photoluminescence measurements presented e.g in our earlier stuides [60,62] reveal the negative effect of RIE processes on the optical and electrical device characteristics.Hence, alternative technological steps are required to "heal" such "defect" structures.Previously, we presented such an approach-a local laser micro annealing (LMA) procedure [60], a next building block, which will be described in the following section.After the nano-LED's device definition/formation, n-GaN regions located at a depth of ~1 µm schematically shown in Figure 1, are defined by conventional photolithography and a subsequent Ar-IBE procedure.An example for nano-LED structures located on the "word line" is presented in Figure 3. Details of the structures presented in Figure 3B reveal that the etched regions do not reach the nano-LED structures themselves.The Ar-IBE etching process leads to a significant surface damage only in the n-GaN/sapphire interface region (Figure 3C) as well as in "deeper" regions where the n-GaN layer was already fully removed and the sapphire substrate was reached.Here it should be noted, as is evident in Figure 3B, the defined n-GaN layer regions, which later serve as a "word line", are not affected by the etching technology.An example for the large array of "buried" nano-LED structures with a diameter of ~100 nm is presented in Figure 4.All devices are encompassed in a SiO 2 layer as can be seen in detail in Figure 5.It serves on the one hand for electrical insulation and on the other hand as a planarization layer for the subsequent final top contact and bit line processing.These "buried" nano-LEDs arranged in large testing arrays were subsequently characterized by micro-photoluminescence (micro-PL) spectroscopy at room temperature.An example for a micro-PL mapping is presented in Figure 6.Details are discussed in the following section "Discussion".Furthermore, after top contact metallization, apertures are formed, which can take up the polymer-nanocrystal suspension.Figure 7a presents a "buried" single nano-LED structure with an aperture filled with polymer-nanocrystal suspension in detail and Figure 7b shows exemplarily a layout for hybrid nano-LEDs singularly addressable by the respective "word" (grey) and "bit" lines (gold).This device layout represents a first example for "combined" hybrid nano-LED structures.We demonstrated the nano-LEDs with a metallic aperture in our previous report [56].The fabrication process and characterization of hybrid nano-LED devices was reported in [57].The combination of both device architectures results in the structure presented in detail in Figure 7a.If the appropriate nanocrystals with different materials and/or diameters are locally injected in the targeted nano-LED´s aperture regions, such combined structures allow to create "multicolor" light emitter arrays suitable for a lithographical process where "mixtures" of photosensitive films or layer-stacks could be selectively photo-chemically altered.This would allow the processing of complex patterning architectures simultaneously in the future.
Nanomanufacturing 2024, 4, FOR PEER REVIEW 5 LED´s aperture regions, such combined structures allow to create "multicolor" light emitter arrays suitable for a lithographical process where "mixtures" of photosensitive films or layer-stacks could be selectively photo-chemically altered.This would allow the processing of complex patterning architectures simultaneously in the future.The n-GaN region serves as the bottom contact and the word line (as can be seen in Figure 7b).The "interface" region visible in the images is a product of material re-deposited during the etching process.LED´s aperture regions, such combined structures allow to create "multicolor" light emitter arrays suitable for a lithographical process where "mixtures" of photosensitive films or layer-stacks could be selectively photo-chemically altered.This would allow the processing of complex patterning architectures simultaneously in the future.The n-GaN region serves as the bottom contact and the word line (as can be seen in Figure 7b).The "interface" region visible in the images is a product of material re-deposited during the etching process.The n-GaN region serves as the bottom contact and the word line (as can be seen in Figure 7b).The "interface" region visible in the images is a product of material re-deposited during the etching process.The hybrid nano-LEDs are singularly addressable by the respective "word" (grey) and "bit" lines (gold).Please note that "word" and "bit" lines in this image are colored for the sake of increasing the respective struc-ture´s visibility.

Discussion
Developments in mask-free singularly addressable nano-LED lithography with respect to its future implementation are closely connected to a number of challenges such as the reproducibility and control of the fabrication process, its simplicity and efficiency as well as the long-term stability of the light emitter sources.Therefore, selected/critical steps involved are discussed and assessed in the following.As we already mentioned in the previous section, conventional reactive ion etching (RIE) is used for the spatial definition and/or structure formation of nano-LED devices.The optimization of the nanomanufacturing/etching procedure is key to obtaining nano-LEDs, that can be (singularly) adressable [18,55].The nano-LED/structure definition is carried out up to the n-doped GaN contact layer which should not degrade by the etching process.For the The hybrid nano-LEDs are singularly addressable by the respective "word" (grey) and "bit" lines (gold).Please note that "word" and "bit" lines in this image are colored for the sake of increasing the respective structure's visibility.

Discussion
Developments in mask-free singularly addressable nano-LED lithography with respect to its future implementation are closely connected to a number of challenges such as the reproducibility and control of the fabrication process, its simplicity and efficiency as well as the long-term stability of the light emitter sources.Therefore, selected/critical steps involved are discussed and assessed in the following.As we already mentioned in the previous section, conventional reactive ion etching (RIE) is used for the spatial definition and/or structure formation of nano-LED devices.The optimization of the nanomanufacturing/etching procedure is key to obtaining nano-LEDs, that can be (singularly) adressable [18,55].The nano-LED/structure definition is carried out up to the n-doped GaN contact layer which should not degrade by the etching process.For the preparation of the nano-LEDs into individual "word lines", etching in a further step must be carried out (Ar-IBE procedure) to define the respective contact layer.
Therefore the sapphire substrate has to be reached to ensure the insulation of the lines.The principle of this device architecture is presented in Figure 1.It needs to be taken into account that a redeposition of etched GaN takes place along the lines (Figure 3C in detail).In spite of careful etching optimization, the etching procedure nevertheless leads to a significant decrease in the nano-LEDs' electroluminescence intensity.Hence, alternative fast and efficient technological procedures need to be applied for device performance improvement.A number of technological approaches are available to heighton the efficiency of micrometer and nano-sized LED structures.One of these is the precise local laser micro annealing (LMA) procedure, a building block the full potential of which has still to be uncovered.As we already mentioned in Section 3 (Results) the etching process for the formation and fabrication of nano-LED devices leads to a degradation of their optical properties [60].Since various emerging applications such as "nano-LED singularly addressable lithography" introduced in this work and others require full control and/or tuning of the electroluminescence intensity of individual devices, a suitable technology needs to be developed.The application of the LMA process resulted in meeting the requirement and the expected optical properties can then be achieved.In our previous study [60], the simple model based on a defect layer depth described the direct correlation between the suppression of radiative recombination as a follow of the MQW's effective volume reduction after the etching procedure.As a result, the respective effective volume can be increased after the LMA procedure was applied locally for the individual nano-LED structures.This effect was confirmed by our photoluminescence studies and an about 70% decrease in the defect layer depth was evaluated [60].Hence, application of the LMA is advantageous also in the fabrication of the singularly addressable nano-LED architecture, since the precise control of the EL intensity of all the individual devices reduces along the way the overall device power consumption as well as increases their lifetime as it was reported previously [60].Nevertheless, LMA is not limited only to nano-LED devices, this technique can be applied also to transmistor based devices forming core components for optical computing [63,64].The conditioning of LED devices plays [60] an important role also in the development of novel correlative characterization techniques as we already presented in our previous studies [60,62].Unfortunately, the formation of nano-LED devices remains a crucial point in spite of all of these development efforts.This is demonstrated in Figure 2.
After SEM inspection of the fabricated nano-LEDs it was confirmed that the RIE procedure has to be further optimized in future-targeting the aim to prevent surface and/or detrimental damage especially in the region.In this "building" block, special attention has to be paid also to alternative gas mixtures for RIE, which could be used instead of the conventional one.As a consequence of the etching procedure and the damage related to the chemical and physical etching processes, the distribution of the photoluminescence differs strongly over the array as can be seen in Figure 6a.It presents an intensity mapping of the single nano-LEDs in the array at the individually measured points.The mapping consists of hundreds of PL-spectra, which were then evaluated for the map presentation.Where only GaN remains after etching, a high GaN band edge luminescence (denoted in blue) is observed.Defect luminescence (emission maxima in the PL spectra range of ~540-600 nm, denoted in green-red) is detected presumably at the circumference of the nano-LEDs and PL emission maxima (~440-445 nm) denoted in pink/violet color are attributed to the MQW luminescence of the nano-LEDs.The mapping discloses that radiative recombination is suppressed due to the damage induced by the etching process as was previously reported [60].Therefore, a further building block-the LMA technique-has to be applied in the nano-LED's device processing as well.A simple model showing the effect of the reduction of defect layer depth after laser micro annealing was introduced in our previous work [60].The subsequent micro photoluminescence studies disclosing an increased photoluminescence intensity indicated that the LMA process has a direct impact on the curing of etching related defects.These are deemed responsible for the suppression of radiative recombination in the nano-LED devices.Photoluminescence measurements on the nano-LED structures revealed [60] that by using the LMA procedure, the nano-LED properties were enhanced in comparison to their non-locally annealed counterparts.According to the simple model mentioned above, the integrated PL-intensity enhancement of the nano-LEDs observed can be explained by the reduction of the defect layer depth from ~17 nm to ~5 nm [60].Furthermore, the application of the LMA process to the nano-LEDs leads to a current increase up to ~3.7-fold at 5 V [60].Additionally, only a "moderate reduction" ~15% in electroluminescence intensity (during continuous wave long term operation for 5000 h) in comparison to its non-locally annealed counterpart (~50%), was demonstrated.Furthermore, micro-Raman thermography investigations performed on single nano-LED structures (after the LMA procedure) revealed an up to 60 K decrease in work temperature [60].This is advantageous, since lithographical processes, in general, are temperature "sensitive".One other important issue are the long-term "costs" for such lithographical techniques.They can be decreased significantly if the device lifetime, stability as well as reliability could be increased in comparison to/with existing "light/exposure" sources used for conventional lithography.Indeed, it has already been disclosed that the application of the LMA procedure for nano-LED devices could be of a large benefit.During up to 5000 h of operation, the electroluminescence of such nano-LEDs barely decreases (i.e., the optical properties do not degrade).This means that the nano-LED lifetime and reliability increase by local annealing with the LMA process.The performance of such locally annealed nano-LEDs renders them suitable for a future employment as a key component for on chip integrated electro-optic convertors [62].Additionally, they may achieve still unprecedented importance in the development of novel computing architectures based on transmistor/all optical switch units.

Conclusions
In this contribution, we discussed the technology of nano light emitting diodes (nano-LEDs) for future mask-free singularly addressable lithographical techniques.Our previous studies revealed that the nano-LEDs are suitable devices for the local initialization of photochemical reactions.Hence, advanced "LED-based" lithographical techniques such as for applications in the "near" field regime could potentially revolutionize the fabrication of nanodevices.Ultimately, if appropriate arrays of single photon sources could be developed and integrated into a singularly addressable approach, they could serve for future molecular lithographical/patterning techniques.In addition, inspired by the technology developed for color displays, "light" sources of different wavelengths can be applied principally in the future to "multi-color" singularly addressable nano-LED lithographical techniques.Nevertheless, the development of the LEDs' device nanomanufacturing technologies are not limited only to the in this study presented advanced lithographical techniques.They are also driven/motivated by strong technological needs and demand on highly efficient, energy and resources saving solutions as well.Highly resolved illumination microscopy and a large range of spectroscopic and diagnostic methods such as in security (e.g., gas and drugs monitoring) and/or where localized light sources attaining deeper insights into biological cells are needed, are just a selection of applications in which the nano-LEDs could gain importance.They could potentially represent key/basic components in sophisticated technological architectures necessary for future developments towards on chip optical communication, advanced data processing and storage for optical and/or neuromorphic computing as well.Finally, singularly addressable nano-LEDs introduced in a driving scheme for the lithographical approach in this work could also be of benefit in emerging optogenetic and neuronal stimulation applications.The key to their successful application will be, however, the development of such nanofabrication technologies as presented in this report.

Figure 1 .
Figure 1.Principle driving scheme for the nano-LEDs arranged in arrays allowing the fabrication of different patterns without a mask.The nano-LEDs are singularly addressable by the respective word and bit lines.

Figure 1 .
Figure 1.Principle driving scheme for the nano-LEDs arranged in arrays allowing the fabrication of different patterns without a mask.The nano-LEDs are singularly addressable by the respective word and bit lines.

Figure 2 .
Figure 2. Example for an SEM image of a single nano-LED structure directly after the reactive ion etching process.The Ni cap used as the etching mask is still visible.The morphology of the nano-LEDs is inhomogeneous: a shallower chemical/physical corrosion depth and lower roughness is observed near the base region of the nanostructure.The roughness and chemical/physical damage to the nano-LED structure were determined in the SEM.

Figure 3 .
Figure 3. (A) Scanning electron micrograph of single hybrid-nano-LED structures positioned on the "base" region formed by the Ar-IBE process, (B) in detail and (C) showing the GaN/sapphire interface region.The n-GaN region serves as the bottom contact and the word line (as can be seen in Figure7b).The "interface" region visible in the images is a product of material re-deposited during the etching process.

Figure 2 .
Figure 2. Example for an SEM image of a single nano-LED structure directly after the reactive ion etching process.The Ni cap used as the etching mask is still visible.The morphology of the nano-LEDs is inhomogeneous: a shallower chemical/physical corrosion depth and lower roughness is observed near the base region of the nanostructure.The roughness and chemical/physical damage to the nano-LED structure were determined in the SEM.

Figure 2 .
Figure 2. Example for an SEM image of a single nano-LED structure directly after the reactive ion etching process.The Ni cap used as the etching mask is still visible.The morphology of the nano-LEDs is inhomogeneous: a shallower chemical/physical corrosion depth and lower roughness is observed near the base region of the nanostructure.The roughness and chemical/physical damage to the nano-LED structure were determined in the SEM.

Figure 3 .
Figure 3. (A) Scanning electron micrograph of single hybrid-nano-LED structures positioned on the "base" region formed by the Ar-IBE process, (B) in detail and (C) showing the GaN/sapphire interface region.The n-GaN region serves as the bottom contact and the word line (as can be seen in Figure7b).The "interface" region visible in the images is a product of material re-deposited during the etching process.

Figure 3 .
Figure 3. (A) Scanning electron micrograph of single hybrid-nano-LED structures positioned on the "base" region formed by the Ar-IBE process, (B) in detail and (C) showing the GaN/sapphire interface region.The n-GaN region serves as the bottom contact and the word line (as can be seen in Figure7b).The "interface" region visible in the images is a product of material re-deposited during the etching process.

Figure 4 .
Figure 4. SEM image of the structured vertical hybrid nano-LED devices after the RIE etching procedure and encompassing the nanostructures in HSQ/SiO2 for device insulation.

Figure 5 .
Figure 5. Detail-SEM image of the structured vertical hybrid-nano-LED devices, in which a suspension of polymer-nanocrystals was applied to the apertures.

Figure 4 . 6 Figure 4 .
Figure 4. SEM image of the structured vertical hybrid nano-LED devices after the RIE etching procedure and encompassing the nanostructures in HSQ/SiO 2 for device insulation.

Figure 5 .
Figure 5. Detail-SEM image of the structured vertical hybrid-nano-LED devices, in which a suspension of polymer-nanocrystals was applied to the apertures.

Figure 5 .Figure 6 .
Figure 5. Detail-SEM image of the structured vertical hybrid-nano-LED devices, in which a suspension of polymer-nanocrystals was applied to the apertures.Nanomanufacturing 2024, 4, FOR PEER REVIEW 7

Figure 6 .
Figure 6.(a) Micro-PL mapping from the single nano-LEDs in the array.Three different luminescence bands/maxima were observed previously[60] and are presented here graphically in colors.They are attributed to GaN band edge luminescence (blue), radiative recombination from the multi quantum well region with the emission maxima in the PL spectra at ~440-445 nm (pink/violet color) and defect luminescence ~540-600 nm (green-red).The etching process is responsible for the suppression of radiative recombination from the MQW region.(b) Detail of micro PL mapping for a single nano-LED structure without the injected nanocrystal-polymer suspension.

Figure 6 .Figure 7 .
Figure6.(a) Micro-PL mapping from the single nano-LEDs in array.Three different luminescence bands/maxima were observed previously[60] and are presented here graphically in colors.They are attributed to GaN band edge luminescence (blue), radiative recombination from the multi quantum well region with the emission maxima in the PL spectra at ~ 440-445 nm (pink/violet color) and defect luminescence ~ 540-600 nm (green-red).The etching process is responsible for the suppression of radiative recombination from the MQW region.(b) Detail of micro PL mapping for a single nano-LED structure without the injected nanocrystal-polymer suspension.

Figure 7 .
Figure 7. (a) Detail-SEM image of the vertical hybrid-nano-LED device-aperture filled with injected polymer-nanocrystal suspension; (b) example for a hybrid nano-LED array.The hybrid nano-LEDs are singularly addressable by the respective "word" (grey) and "bit" lines (gold).Please note that "word" and "bit" lines in this image are colored for the sake of increasing the respective structure's visibility.