Bibliographical Synthesis on the Corrosion and Protection of Archaeological Iron by Green Inhibitors

: Iron is a widely used metal due to its low cost and availability, but it is susceptible to corrosion in many circumstances. This corrosion can result in economic and environmental losses, and negatively affect the physical and chemical properties of the metal. This chapter provides a background on iron corrosion in archaeology and introduces various inhibitors used for its protection. It starts with a general overview of corrosion and metallurgy of iron, followed by an in-depth explanation of the mechanisms of iron corrosion in water and air. The chapter concludes with a review of different corrosion inhibitors, focusing on those made from natural plant extracts.


Introduction
Corrosion is a major issue in industry, causing the loss of 100 million tons of steel per year, which is nearly 15% of the world's production. It is a complex phenomenon that depends on several factors such as the environment, composition of the metal, and its properties. Corrosion results in direct costs such as replacement of corroded structures and labor, and indirect costs such as production losses, efficiency loss, product contamination, and more, which add up to billions of dollars in losses annually. Due to the long-term nature of corrosion, it is often underestimated in the design of equipment and structures, leading to further losses [1,2].
Corrosion is an important issue to consider as it can cause significant damage to historical and cultural artifacts. The process of corrosion can cause a loss of important information and details about the artifact, and can also change its appearance. This can make it difficult for archaeologists and historians to understand and preserve the history of a particular site or artifact, making it an important issue to address [3].
Corrosion is a slow process that affects the structural safety of various industries, including transportation, chemical, petrochemical, and construction. The rate of corrosion depends on the environment, the metal's composition, and its properties. It is often underestimated in design and results in direct costs such as replacement and labor, as well as indirect costs including production loss and efficiency loss. In heritage conservation, corrosion leads to the disappearance of historical artifacts and alters archaeological history [4,5].

History of Iron and Metallurgy
Iron is a very abundant metal on the earth's crust, mostly in the form of oxides. The metallurgy of iron dates back to 1700-1500 BC in regions south of the Caucasus and spread to Europe via Greece and the Danube valley [6]. Iron working was developed in Europe around 800 BC with the Hallstatt civilization and spread to Switzerland and Gaul [7].
The production of iron was traditionally carried out using the direct method or "blast furnace" process, where iron ore was reduced in the presence of wood, coal, and oxygen.

Behavior of Iron in Aqueous Medium
The corrosion of iron in an aqueous environment is due to an irreversible oxidationreduction reaction between the metal and an oxidizing agent contained in the environment.
The oxidation of the metal involves the reduction of the oxidizing agent.
In the case of iron corrosion, for example, if we consider the overall oxidation-reduction Reaction (3), it can be broken down into a partial oxidation reaction or anodic Reaction (1) and a partial reduction reaction or cathodic Reaction (2): 2H + + 2e − → H 2 (2) Fe + 2H + → Fe 2+ + H 2 The anodic and cathodic partial reactions to be considered for iron corrosion in the presence of water are generally: Anodic partial reaction (oxidation): Cathodic partial reactions (reduction): -In an aerated environment (aerobic): -In a deaerated (anaerobic) environment: In the case of corrosion in aqueous media, aeration or de-aeration generally corresponds to the presence or absence of dissolved oxygen [10].

Thermodynamic Approach
The Nernst potential, acidity constants, and solubility products are used to predict the thermodynamics of iron corrosion reactions in aqueous media using Pourbaix diagrams [11]. These diagrams show the stability ranges of the chemical species involved, but do not provide information on the reaction kinetics. Figure 1 gives an example of an equilibrium diagram established by Descostes [12] based on data from Chivot [13,14]. Considering the following species: Fe, Fe 2+ , Fe 3+ , FeOH + , FeOH 2+ , Fe(OH) 2 + , HFeO 2 − , Fe(OH) 2 , Fe(OH) 3 − , Fe(OH) 3  The stability range of species can vary based on solid phases considered. Goethite has the broadest thermodynamic stability range, but similar diagrams can be created for different compositions of total iron and complexing ions in solution (carbonates, sulfates, etc.,) [15]. The stability range of species can vary based on solid phases considered. Goethite has the broadest thermodynamic stability range, but similar diagrams can be created for different compositions of total iron and complexing ions in solution (carbonates, sulfates, etc.,) [15].

Kinetic Approach
The thermodynamic approach can provide information about the likelihood of corrosion reactions, but it does not give information about the speed of the reaction. The speed of the reaction is primarily determined through electrochemical kinetics, which involves measuring corrosion potential, current, polarization resistance, etc. The rate of corrosion can be estimated based on these measurements and is often expressed as mass loss per unit area [10].
The rate of corrosion reaction depends on the rate of charge transfer and the rate of material transport. The slower of the two stages controls the overall rate of the reaction [16].
Accary et al. [17] were the pioneers in conducting studies on the kinetics of corrosion of ferrous alloys. In their 1983 study, they estimated the average rate of corrosion to be between 0.01 and 10 μm/year, based on the measurements of the thickness of corrosion on a collection of 20 ferrous objects. Another study by Soerensen et al. [18], determined the average rate of corrosion by measuring the ratio of the surface area of the corrosion products to that of the metal using X-rays. This study found average corrosion rates ranging from 0.025 to 1.2 μm/year.

Kinetic Approach
The thermodynamic approach can provide information about the likelihood of corrosion reactions, but it does not give information about the speed of the reaction. The speed of the reaction is primarily determined through electrochemical kinetics, which involves measuring corrosion potential, current, polarization resistance, etc. The rate of corrosion can be estimated based on these measurements and is often expressed as mass loss per unit area [10].
The rate of corrosion reaction depends on the rate of charge transfer and the rate of material transport. The slower of the two stages controls the overall rate of the reaction [16].
Accary et al. [17] were the pioneers in conducting studies on the kinetics of corrosion of ferrous alloys. In their 1983 study, they estimated the average rate of corrosion to be between 0.01 and 10 µm/year, based on the measurements of the thickness of corrosion on a collection of 20 ferrous objects. Another study by Soerensen et al. [18], determined the average rate of corrosion by measuring the ratio of the surface area of the corrosion products to that of the metal using X-rays. This study found average corrosion rates ranging from 0.025 to 1.2 µm/year. Johnson and Francis [19] conducted a study on the global estimate of the corrosion rate of archaeological objects. They found that the corrosion rate can range from a minimum of 0.1 mm per millennium to a maximum of 10 mm per year, depending on the burial conditions. However, the burial conditions are often not well understood, which leads to a wide range of possible corrosion rates [5].

Iron Corrosion Products in Aqueous Media
The layer of corrosion products formed on metal surfaces consists of multiple compounds, the composition of which is dependent on the pH of the environment, the composition of the medium, the concentration and transport conditions of oxygen, and other chemical species present such as chloride, carbonate, sulfate, etc. Factors such as convection and diffusion also play a role in determining the nature of the corrosion products [20].
In the case of corrosion in an aqueous environment with oxygen present, followed by corrosion in a deaerated (anaerobic) environment due to oxygen depletion (for example in storage), we can consider the following hypothetical equilibria between iron and its oxides or hydroxides. Iron/oxide equilibria are stable, while iron/hydroxide equilibria are unstable [10].
Oxidation of iron in the presence of oxygen, aerobic corrosion: 2Fe Reduction of the oxide or hydroxide surface: After consumption of oxygen, anaerobic corrosion: Based on these reactions, Misawa et al. and Cornell and Schwertmann [21,22] conducted studies on the formation of compounds resulting from oxidation. These studies established a relatively complex reaction scheme that governs the appearance and evolution of species in aqueous solution, starting from the formation of ferrous ions (Fe 2+ ) ( For this study, Misawa et al. and Cornell and Schwertmann found that the presence of ferrous ions in solution is dependent on the oxygen level and pH. When the oxygen level is high and the pH is below 6, ferrous ions remain in solution. However, if the pH is above 6, ferrous hydroxide (Fe (OH)2) precipitates and quickly transforms into Fe (OH)3 due to oxidation and hydrolysis.
The oxidation rate of green rusts (Fe (OH)2) determines the formation of lepidocrocite (γ-FeOOH) or magnetite (Fe3O4). Magnetite is a thermodynamically stable phase, but in For this study, Misawa et al. and Cornell and Schwertmann found that the presence of ferrous ions in solution is dependent on the oxygen level and pH. When the oxygen level is high and the pH is below 6, ferrous ions remain in solution. However, if the pH is above 6, ferrous hydroxide (Fe(OH) 2 ) precipitates and quickly transforms into Fe(OH) 3 due to oxidation and hydrolysis.
The oxidation rate of green rusts (Fe(OH) 2 ) determines the formation of lepidocrocite (γ-FeOOH) or magnetite (Fe 3 O 4 ). Magnetite is a thermodynamically stable phase, but in the presence of iron in an oxidation state between +II and +III, it can evolve into a similar structured phase, maghemite (γ-Fe 2 O 3 ), at a higher iron oxidation degree.
In the long term, Fe(OH) 3 can transform into goethite α-FeOOH through loss of water. If the oxygen level is low, ferrous ions can react directly with OH anions to form unstable compounds such as Fe(OH) 2 or Fe 2 (OH) 3 Cl in the presence of chlorine [15].

Atmospheric Corrosion of Iron
Metals are not only unstable when in contact with or immersed in corrosive solutions, there is another type of corrosion in contact with air, called atmospheric corrosion. This type of corrosion is due to the degradation of metal objects when exposed to air and its elements such as oxygen, humidity, and pollutants. The formation and disappearance of liquid films on metal surfaces contribute to this corrosion. The rate of atmospheric corrosion varies depending on the environment the metal is exposed to, with industrial environments being the most corrosive, followed by urban and rural environments. The difference in the rate of corrosion is due to the presence of pollutants in the atmosphere [10].
Most studies on atmospheric corrosion do not distinguish between outdoor and indoor atmospheric environments. Both environments can cause variations in relative humidity leading to moisture cycling on metal surfaces and result in corrosion. Outdoor atmospheric environments can also result in electrolyte run-off and the presence of a surface water film, while indoor atmospheric corrosion occurs under shelter. Nevertheless, the influence of relative humidity and moisture cycling remains significant in both environments [15].

Mechanisms of Atmospheric Corrosion of Iron
When iron is exposed to moist air, it reacts with the oxygen in the air and forms iron oxide (rust) through a process called atmospheric corrosion. This process is an electrochemical reaction, where electrons are transferred between the iron and oxygen atoms in the air. This reaction forms a protective layer of iron oxide on the surface, which helps prevent further corrosion. The accompanying Figure 3 provides a diagram of the atmospheric corrosion process, including the various steps involved in the process and the specific chemical reactions that take place.
The early studies in the 1930s showed that atmospheric corrosion of metals cannot be described by a simple oxidation reaction and that more complex mechanisms are involved. Researchers subsequently highlighted the role of moisture cycling in the corrosion process and demonstrated that the kinetics of electrochemical reactions play a crucial role in atmospheric corrosion [23]. This work expanded the understanding of atmospheric corrosion and showed that it is a multi-faceted process that involves a range of chemical, physical, and electrochemical phenomena. These findings have had a lasting impact on the field of corrosion science and continue to inform current research and understanding of atmospheric corrosion.
Schikorr [24] proposed the "acid regeneration" model, which suggests that iron oxides form in areas of acidic pH and that the presence of sulfur dioxide catalyzes the corrosion reactions through the formation of sulfuric acid, which is regenerated during moisture cycling. This model was later expanded upon by Evans and Taylor [25], who proposed the "electrochemical cycling" model based on electrochemical reactions. This model states that the corrosion process is controlled by a humidification-drying cycle and was experimentally verified by Stratmann et al. This work further advanced our understanding of atmospheric corrosion and showed the important role of electrochemical reactions in the process. The "electrochemical cycling" model is widely accepted today as a key mechanism that governs atmospheric corrosion [26,27].
door atmospheric environments. Both environments can cause variations in relative humidity leading to moisture cycling on metal surfaces and result in corrosion. Outdoor atmospheric environments can also result in electrolyte run-off and the presence of a surface water film, while indoor atmospheric corrosion occurs under shelter. Nevertheless, the influence of relative humidity and moisture cycling remains significant in both environments [15].

Mechanisms of Atmospheric Corrosion of Iron
When iron is exposed to moist air, it reacts with the oxygen in the air and forms iron oxide (rust) through a process called atmospheric corrosion. This process is an electrochemical reaction, where electrons are transferred between the iron and oxygen atoms in the air. This reaction forms a protective layer of iron oxide on the surface, which helps prevent further corrosion. The accompanying Figure 3 provides a diagram of the atmospheric corrosion process, including the various steps involved in the process and the specific chemical reactions that take place. The early studies in the 1930s showed that atmospheric corrosion of metals cannot be described by a simple oxidation reaction and that more complex mechanisms are involved. Researchers subsequently highlighted the role of moisture cycling in the corrosion process and demonstrated that the kinetics of electrochemical reactions play a crucial role in atmospheric corrosion [23]. This work expanded the understanding of atmospheric corrosion and showed that it is a multi-faceted process that involves a range of chemical, physical, and electrochemical phenomena. These findings have had a lasting impact on the field of corrosion science and continue to inform current research and understanding of atmospheric corrosion.
Schikorr [24] proposed the "acid regeneration" model, which suggests that iron oxides form in areas of acidic pH and that the presence of sulfur dioxide catalyzes the corrosion reactions through the formation of sulfuric acid, which is regenerated during moisture cycling. This model was later expanded upon by Evans and Taylor [25], who proposed the "electrochemical cycling" model based on electrochemical reactions. This model states that the corrosion process is controlled by a humidification-drying cycle and was experimentally verified by Stratmann et al. This work further advanced our understanding of atmospheric corrosion and showed the important role of electrochemical reactions in the process. The "electrochemical cycling" model is widely accepted today as a key mechanism that governs atmospheric corrosion [26,27]. The humidification-drying cycle in atmospheric corrosion ( Figure 4) is divided into three stages, each defined by the evolution of the thickness of the electrolyte film on the surface of the metal object. During the first stage, there is a wetting stage where the metal surface is initially wetted by moisture. The second stage is the wet period, during which the electrolyte film has a significant and constant thickness. The third stage is the drying stage, during which the moisture evaporates and the electrolyte film becomes thinner. These stages play an important role in the electrochemical reactions that take place during atmospheric corrosion, and the progression of the cycles is driven by the relative humidity and temperature conditions in the environment.
Electrochem 2023, 4, FOR PEER REVIEW 8 The humidification-drying cycle in atmospheric corrosion ( Figure 4) is divided into three stages, each defined by the evolution of the thickness of the electrolyte film on the surface of the metal object. During the first stage, there is a wetting stage where the metal surface is initially wetted by moisture. The second stage is the wet period, during which the electrolyte film has a significant and constant thickness. The third stage is the drying stage, during which the moisture evaporates and the electrolyte film becomes thinner. These stages play an important role in the electrochemical reactions that take place during atmospheric corrosion, and the progression of the cycles is driven by the relative humidity and temperature conditions in the environment.

Anchor Stage
During the humidification-drying cycle, the formation of an electrolyte film on the metal surface triggers the anodic dissolution of iron, and the electrons produced by the oxidation reaction must be consumed by a reduction reaction. During the wetting phase ( Figure 5), a strong dissolution kinetics of iron is observed due to the fact that the rust

Anchor Stage
During the humidification-drying cycle, the formation of an electrolyte film on the metal surface triggers the anodic dissolution of iron, and the electrons produced by the oxidation reaction must be consumed by a reduction reaction. During the wetting phase ( Figure 5), a strong dissolution kinetics of iron is observed due to the fact that the rust layer formed is not conductive and therefore oxygen cannot reduce on its surface. This leads to a reduction of the metal surface accessible through a network of tortuous and nanometric pores, which contributes to the overall corrosion process. This highlights the importance of the wetting stage in atmospheric corrosion and the complex interplay between electrochemical reactions, the thickness of the electrolyte film, and the physical and chemical conditions of the environment [3]. The corrosion product layer itself is responsible for the corrosion, and the anodic d solution of the metal is balanced by the reduction of a constituent of this layer [28]. R search by Matsushima [15] showed that the reaction of ferric species is dominant in t cathodic reaction on corroded iron in wet corrosion. This finding was later confirmed Evans and Taylor [25], and Stratmann, [29], further solidifying the importance of the w ting phase in atmospheric corrosion and the role of the corrosion product layer in t electrochemical reactions taking place. This work highlights the complex and multi-fa eted nature of atmospheric corrosion and the need for a comprehensive understanding the various processes involved to effectively prevent and mitigate the effects of corrosi in metal materials.
According to Anthony [30], the phases most likely to reduce during the wetting pha are lepidocrocite, ferrihydrite, and feroxyhyte. However, Monnier stated that lepid crocite is the most likely phase to reduce and that amorphous phases tend to reduce lower potentials [31]. As a result, electron consumption during the wetting step may co respond to the reduction of several phases, highlighting the complex nature of the ele trochemical reactions taking place during atmospheric corrosion. This work underscor the need for a comprehensive understanding of the various processes involved in atmo pheric corrosion, including the role of different phases of corrosion products in the ele trochemical reactions and the factors that influence their reduction potential [15].

Wet Stage
In the second stage of the wetting-drying cycle, the electrolyte thickness is assum to be constant and uniform on the surface of the sample, i.e., on the existing and partia reduced corrosion product layer. Figure 6 shows that the iron and dissolved oxygen co sumptions are equal, which indicates that the cathodic reaction is the reduction of d solved oxygen in the electrolyte and the anodic reaction is the oxidation of the metal su strate. This stage of the humidification-drying cycle highlights the key role that dissolv oxygen plays in atmospheric corrosion, as well as the importance of the corrosion produ layer in the overall corrosion process. Understanding the complex interplay between t metal substrate, electrolyte film, and dissolved oxygen is essential to effectively preve The corrosion product layer itself is responsible for the corrosion, and the anodic dissolution of the metal is balanced by the reduction of a constituent of this layer [28]. Research by Matsushima [15] showed that the reaction of ferric species is dominant in the cathodic reaction on corroded iron in wet corrosion. This finding was later confirmed by Evans and Taylor [25], and Stratmann, [29], further solidifying the importance of the wetting phase in atmospheric corrosion and the role of the corrosion product layer in the electrochemical reactions taking place. This work highlights the complex and multi-faceted nature of atmospheric corrosion and the need for a comprehensive understanding of the various processes involved to effectively prevent and mitigate the effects of corrosion in metal materials.
According to Anthony [30], the phases most likely to reduce during the wetting phase are lepidocrocite, ferrihydrite, and feroxyhyte. However, Monnier stated that lepidocrocite is the most likely phase to reduce and that amorphous phases tend to reduce at lower potentials [31]. As a result, electron consumption during the wetting step may correspond to the reduction of several phases, highlighting the complex nature of the electrochemical reactions taking place during atmospheric corrosion. This work underscores the need for a comprehensive understanding of the various processes involved in atmospheric corrosion, including the role of different phases of corrosion products in the electrochemical reactions and the factors that influence their reduction potential [15].

Wet Stage
In the second stage of the wetting-drying cycle, the electrolyte thickness is assumed to be constant and uniform on the surface of the sample, i.e., on the existing and partially reduced corrosion product layer. Figure 6 shows that the iron and dissolved oxygen consumptions are equal, which indicates that the cathodic reaction is the reduction of dissolved oxygen in the electrolyte and the anodic reaction is the oxidation of the metal substrate. This stage of the humidification-drying cycle highlights the key role that dissolved oxygen plays in atmospheric corrosion, as well as the importance of the corrosion product layer in the overall corrosion process. Understanding the complex interplay between the metal substrate, electrolyte film, and dissolved oxygen is essential to effectively prevent and mitigate the effects of atmospheric corrosion on metal materials [15].
Electrochem 2023, 4, FOR PEER REVIEW 10 oxidation reaction to be consumed by the reduction reaction, leading to a stable and uniform corrosion rate. On the other hand, the anodic reaction would take place at the bottom of the pores where the metal and the electrolyte are in direct contact, which leads to a decoupling of the anodic and cathodic zones. This separation of the anodic and cathodic zones creates conditions for the formation of local cells, leading to a non-uniform corrosion rate and a more complex overall corrosion process.

Drying Stage
The drying stage of the electrolyte process has two parts: first, as the thickness decreases, reaction speed increases due to improved oxygen diffusion and iron consumption. At a critical electrolyte thickness, there is a sudden drop in iron oxidation and oxygen reduction currents because of water film dislocation [15,25,32]. In the second part of the drying stage, an increase in dissolved species leads to precipitation and surface coverage, resulting in a weak oxygen reduction current and anodic control of the system [28].
During the drying stage (Figure 7), the high concentration of oxygen in the residual electrolyte film causes polarization of the corrosion layer at high potentials, leading to reoxidation of iron species and the formation of lepidocrocite and goethite [16].  In this stage of the wetting-drying cycle (Figure 6), the oxygen reduction reaction is believed to take place largely on the outer surface of the corrosion product layer, which consists of a conductive reduced phase produced during the wetting step and in contact with the iron meta [31]. This conductive layer allows the electrons produced by the oxidation reaction to be consumed by the reduction reaction, leading to a stable and uniform corrosion rate. On the other hand, the anodic reaction would take place at the bottom of the pores where the metal and the electrolyte are in direct contact, which leads to a decoupling of the anodic and cathodic zones. This separation of the anodic and cathodic zones creates conditions for the formation of local cells, leading to a non-uniform corrosion rate and a more complex overall corrosion process.

Drying Stage
The drying stage of the electrolyte process has two parts: first, as the thickness decreases, reaction speed increases due to improved oxygen diffusion and iron consumption. At a critical electrolyte thickness, there is a sudden drop in iron oxidation and oxygen reduction currents because of water film dislocation [15,25,32]. In the second part of the drying stage, an increase in dissolved species leads to precipitation and surface coverage, resulting in a weak oxygen reduction current and anodic control of the system [28].
During the drying stage (Figure 7), the high concentration of oxygen in the residual electrolyte film causes polarization of the corrosion layer at high potentials, leading to re-oxidation of iron species and the formation of lepidocrocite and goethite [16].
tion. At a critical electrolyte thickness, there is a sudden drop in iron oxidation and oxygen reduction currents because of water film dislocation [15,25,32]. In the second part of the drying stage, an increase in dissolved species leads to precipitation and surface coverage, resulting in a weak oxygen reduction current and anodic control of the system [28].
During the drying stage (Figure 7), the high concentration of oxygen in the residual electrolyte film causes polarization of the corrosion layer at high potentials, leading to reoxidation of iron species and the formation of lepidocrocite and goethite [16].

Products of Atmospheric Corrosion of Iron
Atmospheric corrosion refers to the corrosion of materials caused by the exposure to the atmosphere and its environmental conditions, such as humidity, temperature, presence of pollutants, and pH. The corrosion rate is influenced by the alternation of wet and dry periods, leading to the formation and disappearance of an electrolyte film on the surface. The corrosive power of the atmosphere can be determined by these factors, and the end result is usually a mixture of iron oxides and oxyhydroxides.
Magnetite and maghemite are the two most commonly encountered iron oxides that result from atmospheric corrosion. The corrosion products may also include polymorphic oxyhydroxides of iron, such as goethite (α-FeOOH), lepidocrocite (γ-FeOOH), feroxyhyte (δ-FeOOH), and sometimes akageneite (β-FeOOH) which contains chlorine. In addition, the corrosion layer may also contain ferrihydrite, which is a poorly crystallized and hydrated compound [3]. Table 1 displays the iron oxides and oxyhydroxides present in rust layers that are formed due to atmospheric corrosion. Table 1. Iron oxides and oxyhydroxides encountered in rust layers resulting from atmospheric corrosion [15,33,34].

Products of Atmospheric Corrosion of Iron
Atmospheric corrosion refers to the corrosion of materials caused by the exposure to the atmosphere and its environmental conditions, such as humidity, temperature, presence of pollutants, and pH. The corrosion rate is influenced by the alternation of wet and dry periods, leading to the formation and disappearance of an electrolyte film on the surface. The corrosive power of the atmosphere can be determined by these factors, and the end result is usually a mixture of iron oxides and oxyhydroxides.
Magnetite and maghemite are the two most commonly encountered iron oxides that result from atmospheric corrosion. The corrosion products may also include polymorphic oxyhydroxides of iron, such as goethite (α-FeOOH), lepidocrocite (γ-FeOOH), feroxyhyte (δ-FeOOH), and sometimes akageneite (β-FeOOH) which contains chlorine. In addition, the corrosion layer may also contain ferrihydrite, which is a poorly crystallized and hydrated compound [3]. Table 1 displays the iron oxides and oxyhydroxides present in rust layers that are formed due to atmospheric corrosion.

Products of Atmospheric Corrosion of Iron
Atmospheric corrosion refers to the corrosion of materials caused by the exposure to the atmosphere and its environmental conditions, such as humidity, temperature, presence of pollutants, and pH. The corrosion rate is influenced by the alternation of wet and dry periods, leading to the formation and disappearance of an electrolyte film on the surface. The corrosive power of the atmosphere can be determined by these factors, and the end result is usually a mixture of iron oxides and oxyhydroxides.
Magnetite and maghemite are the two most commonly encountered iron oxides that result from atmospheric corrosion. The corrosion products may also include polymorphic oxyhydroxides of iron, such as goethite (α-FeOOH), lepidocrocite (γ-FeOOH), feroxyhyte (δ-FeOOH), and sometimes akageneite (β-FeOOH) which contains chlorine. In addition, the corrosion layer may also contain ferrihydrite, which is a poorly crystallized and hydrated compound [3]. Table 1 displays the iron oxides and oxyhydroxides present in rust layers that are formed due to atmospheric corrosion. In general, the composition of the rust layer is primarily influenced by atmospheric conditions and the composition of the metal [35]. The rust layer may be relatively homogeneous in some cases [36], but in many cases, it is composed of two parts: an adhesive In general, the composition of the rust layer is primarily influenced by atmospheric conditions and the composition of the metal [35]. The rust layer may be relatively homogeneous in some cases [36], but in many cases, it is composed of two parts: an adhesive "sub-layer" containing magnetite and various amorphous oxyhydroxides such as goethite, akageneite, lepidocrocite, and feroxyhyte (δ-FeOOH), and an outer, more porous In general, the composition of the rust layer is primarily influenced by atmospheric conditions and the composition of the metal [35]. The rust layer may be relatively homogeneous in some cases [36], but in many cases, it is composed of two parts: an adhesive "sub-layer" containing magnetite and various amorphous oxyhydroxides such as goethite, akageneite, lepidocrocite, and feroxyhyte (δ-FeOOH), and an outer, more porous In general, the composition of the rust layer is primarily influenced by atmospheric conditions and the composition of the metal [35]. The rust layer may be relatively homo-geneous in some cases [36], but in many cases, it is composed of two parts: an adhesive "sub-layer" containing magnetite and various amorphous oxyhydroxides such as goethite, akageneite, lepidocrocite, and feroxyhyte (δ-FeOOH), and an outer, more porous and crystallized layer containing mainly goethite and lepidocrocite oxyhydroxides [37,38].
Iron (II) and (III) hydroxides can be identified using X-ray diffraction and are unstable in aerated media, undergoing transformation into a green rust-like intermediate before the formation of lepidocrocite or magnetite, which are considered thermodynamically stable phases [39][40][41]. Under atmospheric conditions, the rust layer can reach significant thicknesses (a few millimeters) over a very long period of time (more than 50 years) [16].
The work of J. Monnier [15] has confirmed that lepidocrocite is rarely connected to the metal and that highly reactive phases, such as feroxyhyte and ferrihydrite, are abundant in the corrosion product layers of objects that have undergone long-term corrosion. The reduction and re-oxidation of these phases can result in a mixture of maghemite and magnetite or lead to the reprecipitation of reducible phases such as lepidocrocite, ferrihydrite, and/or feroxyhyte.

Protection of Iron by Corrosion Inhibitors
The high cost of annual material degradation has prompted the use of protection methods to save materials and energy, and to meet new requirements, such as the use of non-toxic products.
The protection of materials from corrosive environments can be achieved through various actions at the metallurgical, structural, electrochemical, and environmental levels. Three degrees of action are identified [42]:

1.
Actions on the material, such as modifying its composition or microstructure or isolating it from its environment through a metallic or organic coating or anodization.

2.
Actions on the environment, such as incorporating corrosion inhibitors or avoiding moisture accumulation in the structure.

3.
Actions on the electrochemical corrosion process, such as cathodic protection.
The protection of metal heritage requires consideration of both preservation of surface information and protection against corrosion. Organic coatings, such as varnishes and waxes, can provide protection. Anodic, cathodic, and galvanic protection, as well as the use of inhibitors, are common and effective methods of protection.

Background
The Romans were aware of corrosion and its effects on metal objects. Pliny the Elder, a Roman naturalist and historian, mentioned in the first century A.D. the use of oil or bitumen for protecting bronze and pitch, gypsum or ceruse for iron from corrosion.
This shows that even in ancient times, people were aware of the need for protection against corrosion and sought methods to preserve their metal objects.
The study of corrosion has a long history, dating back to the 17th century. However, it was not until the 19th century that the means of protecting against corrosion were studied scientifically. The number of references dealing with corrosion inhibitors increased rapidly after 1945, with numerous articles written on the subject in various fields such as aviation, oil refining, and diesel engines. In recent years, there has been a significant increase in works on corrosion inhibition, reflecting technological advancements in the field [43].

Definition
A corrosion inhibitor is a substance added to a corrosion system to slow down the corrosion rate of a metal without significantly altering the concentration of corrosive agents in the environment. The definition used by the National Association of Corrosion Engineers (NACE) states that an inhibitor is a substance that retards corrosion in low concentration. The international standard ISO 8044 defines an inhibitor as a chemical substance added to the corrosion system in a chosen concentration to decrease the corrosion rate of the metal. The properties of an effective inhibitor include lowering the corrosion rate, stability in the presence of other constituents, stability at temperatures of use, effectiveness at low concentrations, compatibility with non-toxicity standards, and cost-effectiveness [44,45].

Classification
Inhibitors can be classified based on different criteria such as mechanism of inhibition, application, or chemical nature. This classification helps in better understanding the working of inhibitors and selecting the right inhibitor for a particular corrosion problem. The different classifications of inhibitors provide a comprehensive understanding of the different types of inhibitors and their uses in various corrosion scenarios [46].
The classification of inhibitors ( Figure 8) based on their field of application is a useful way to differentiate between inhibitors used in different environments. For example, inhibitors used in acidic media are mainly used to prevent electrochemical attack during pickling processes and in drilling fluids in the oil industry. Inhibitors for neutral media are mainly used to protect cooling circuits. In organic media, a large number of inhibitors are used in engine lubricants and gasoline to protect against corrosion caused by the presence of water and ionic species. This classification helps in selecting the appropriate inhibitor for a specific corrosion problem and ensures maximum protection against corrosion [47].
Electrochem 2023, 4, FOR PEER REVIEW 14 rate, stability in the presence of other constituents, stability at temperatures of use, effectiveness at low concentrations, compatibility with non-toxicity standards, and cost-effectiveness [44,45].

Classification
Inhibitors can be classified based on different criteria such as mechanism of inhibition, application, or chemical nature. This classification helps in better understanding the working of inhibitors and selecting the right inhibitor for a particular corrosion problem. The different classifications of inhibitors provide a comprehensive understanding of the different types of inhibitors and their uses in various corrosion scenarios [46].
The classification of inhibitors ( Figure 8) based on their field of application is a useful way to differentiate between inhibitors used in different environments. For example, inhibitors used in acidic media are mainly used to prevent electrochemical attack during pickling processes and in drilling fluids in the oil industry. Inhibitors for neutral media are mainly used to protect cooling circuits. In organic media, a large number of inhibitors are used in engine lubricants and gasoline to protect against corrosion caused by the presence of water and ionic species. This classification helps in selecting the appropriate inhibitor for a specific corrosion problem and ensures maximum protection against corrosion [47]. Inhibitors for paints and gas phases are used to temporarily protect various packaged objects from corrosion during transport and storage. Electrochemically, inhibitors are classified as anodic, cathodic, or mixed inhibitors, depending on their effect on the rate of oxidation and reduction reactions. Anodic inhibitors slow down the oxidation of the metal, cathodic inhibitors slow down the reduction of the oxidant, while mixed inhibitors affect both anodic and cathodic domains. The electrochemical effect of inhibitors on the surface can be explained by various physico-chemical mechanisms. In some cases, the inhibitor forms a physical barrier between the metal and the corrosive medium, as in the case of thick coatings such as waxes and varnishes. In other cases, the inhibitor operates through a pH or redox buffer effect, which can passivate the metal and reduce the Inhibitors for paints and gas phases are used to temporarily protect various packaged objects from corrosion during transport and storage. Electrochemically, inhibitors are classified as anodic, cathodic, or mixed inhibitors, depending on their effect on the rate of oxidation and reduction reactions. Anodic inhibitors slow down the oxidation of the metal, cathodic inhibitors slow down the reduction of the oxidant, while mixed inhibitors affect both anodic and cathodic domains. The electrochemical effect of inhibitors on the surface can be explained by various physico-chemical mechanisms. In some cases, the inhibitor forms a physical barrier between the metal and the corrosive medium, as in the case of thick coatings such as waxes and varnishes. In other cases, the inhibitor operates through a pH or redox buffer effect, which can passivate the metal and reduce the corrosion rate. The mode of action of an inhibitor can also involve the formation of surface films due to the precipitation of inorganic salts or poorly soluble organic complexes. These films reduce the accessibility of oxygen to the metal surface and partially block the anodic dissolution [48].
The technique of removing the corrosive agent from the medium is only applicable in closed systems, such as in the closed hot water circuits of thermal power stations. Additionally, it is important to note that many inhibitors act through multiple mechanisms simultaneously, which can increase their effectiveness in preventing corrosion [49].

Inhibitors Specific to Ferrous Metals in an Acid Medium
Different corrosion inhibitors can effectively protect ferrous metals from corrosion in acidic environments, either individually or in combination. The selection of the appropriate inhibitor depends on various factors such as the type of metal, environment, and specific conditions [50].

Synthetic Inhibitors
Organic inhibitors contain elements such as nitrogen, sulfur, and oxygen that can exchange electrons with the metal and protect it from corrosion. These inhibitors work through a chemical process called spontaneous adsorption and provide good results in inhibiting steel corrosion in acidic medium [51]. Organic inhibitors have several advantages over inorganic inhibitors, as they provide uniform passivation on the metal surface for maximum protection, while inorganic inhibitors form brittle and porous films that can lead to localized corrosion [52]. There is a large body of literature available discussing the use of organic compounds as corrosion inhibitors for ferrous metals in acidic media, as listed in Table 2. Table 2. Examples of inhibitors used for the protection of iron and its alloys in acidic media.

Compounds References
Nitrogenous Hexamethylenetetramine or methenamine [52] Diazoles: imidazole and its derivatives  [55][56][57] The addition of organic compounds to the acid solution generally reduces its aggressiveness, however, these compounds are toxic and harmful to the environment, leading to the need for alternative, eco-friendly, and efficient inhibitors. One such alternative is the use of natural substances, including vegetable oils [58].

Corrosion Inhibitors Based on Natural Substances
The use of natural substances such as vegetable oils is attractive due to their low cost and abundant availability as environmentally friendly and biodegradable compounds. The use of plant extracts as corrosion inhibitors dates back to 1930, with the use of Chelidonium majus and other plants in a pickling bath of H 2 SO 4 . The first patent on corrosion inhibition was granted to Baldwin, who used molasses and vegetable oils for pickling steel sheets in acidic media [59].
Currently, many research groups around the world are exploring the use of plant products as corrosion inhibitors for metals and alloys in various corrosive environments [60]. There is an increasing number of publications addressing this topic, as shown in Table 3, which details some of the main green inhibitors for the corrosion of ferrous metals in acidic medium.

Conclusions
Corrosion inhibitors are a cost-effective and practical solution for protecting metals and alloys against corrosion. The unique aspect of this method is that the anti-corrosion treatment is applied to the corrosive environment instead of directly to the metal, making it a convenient and inexpensive method in comparison to other corrosion control methods.
There are different types of inhibitors that work based on different mechanisms, leading to varying levels of effectiveness in different environments. Among the inhibitors, plant-based inhibitors have proven to be particularly effective and have gained widespread popularity, especially due to their low toxicity and eco-friendly nature. However, there are still some challenges and problems associated with the use of these inhibitors. Here are some perspectives on the problems of green corrosion inhibitors and future research directions in the field of iron protection [46-51]: 1.
Inhibitor effectiveness: the effectiveness of green corrosion inhibitors can be influenced by several factors, such as the type of metal, the corrosive environment, and the inhibitor concentration. Therefore, further research is needed to optimize the performance of these inhibitors under various conditions. 2.
Compatibility with other materials: green corrosion inhibitors may not be compatible with other materials used in the metal protection process, such as coatings or paints. Therefore, research efforts should focus on developing inhibitors that are compatible with other materials used in metal protection.

3.
Environmental impact: although green corrosion inhibitors are considered to be environmentally friendly, their impact on the environment should be carefully evaluated. For example, some natural inhibitors may cause eutrophication in water bodies or have other unintended consequences. Therefore, further research is needed to ensure that these inhibitors do not harm the environment.

4.
Cost: the cost of green corrosion inhibitors can be high, particularly for large-scale applications. Therefore, research efforts should focus on developing cost-effective inhibitors that can provide effective protection at a lower cost.
Overall, green corrosion inhibitors offer a promising solution for metal protection with reduced environmental impact. However, there are still some challenges that need to be addressed. Future research efforts should focus on developing eco-friendly and cost-effective inhibitors, optimizing their performance under various conditions, exploring new approaches to corrosion protection, and developing smart corrosion inhibitors that can respond to changes in the environment and adjust their effectiveness accordingly.