Full Factorial Design Synthesis of Silver Nanoparticles Using Origanum vulgare

: Green synthesis of silver nanoparticles (AgNPs) involves a reduction reaction of a metal salt solution mixed with a plant extract. The reaction yield can be controlled using several independent factors, such as extract and metal concentration, temperature, and incubation time. AgNPs from Origanum vulgare (oregano) were synthesized in the past. However, no investigations were performed on the combined effects of independent factors that affect the synthesis. In this work, silver nitrate, oregano extract, and sodium hydroxide (NaOH) concentrations were chosen as the independent factors, and full factorial design under Response Surface Methodology was employed. UV–Vis absorbance spectroscopy, X-ray Powder Diffraction (XRD), and Fourier Transform Infrared Spectroscopy (FTIR) were used to characterize the nanoparticles. A Voigt function was ﬁtted on the measured UV–Vis spectra. The ﬁtting parameters of the Voigt function, peak wavelength, area, and Full Width at Half Maximum, were used as the responses. A quadratic model was ﬁtted for the peak wavelength and area. The NaOH concentration proved to be the dominant factor in nanoparticle synthesis. UV–Vis absorbance showed a characteristic plasmon resonance of AgNPs at 409 nm. XRD veriﬁed the crystallinity of the nanoparticles and FTIR identiﬁed the ligands involved.


Introduction
Silver nanoparticles (AgNPs) have demonstrated excellent antimicrobial activities against a variety of microorganisms, which make them suitable for materials used in medical products [1].Nano-silver has also been used in textiles, coated water filters, for the treatment of mental illness, and other areas [2].
Among various synthesis methods, green synthesis of AgNPs has received attention due to its eco-friendliness, low cost, and capability to integrate microorganisms and biomolecules [3,4].Silver, gold, and other metallic nanoparticles can be synthesized using plant extracts obtained from dry or fresh leaves, fruits, and seeds [4].In a typical reaction, a metal salt solution is mixed with the extract, and a reduction in the metal ion occurs [4] with simultaneous capping of the formed nanoparticle [5].A range of factors control the reaction, such as metal salt and extract concentration, pH, incubation time, and temperature [5,6].
The effects of these different factors can be investigated either by varying 'one factor at a time' or by employing the response surface methodology (RSM) that allows studying the effect of several factors simultaneously [7,8].First-or second-order polynomial equations are adjusted in RSM based on experimental data obtained in an experimental design [8].Green synthesis of AgNPs based on Gallic Acid (GA) and investigation into the effects of AgNO 3 concentration, GA concentration, and pH were recently performed employing RSM [8].In another work, temperature, AgNO 3 , and the extract/AgNO 3 ratio were used as independent factors for nanoparticle synthesis using Punica granatum leaves [9].Two factors, namely AgNO 3 concentration and pH, were used under RSM for nanoparticle synthesis from the extract of desert truffle Ascocarps [10].Box-Behnken [11] and Plackett-Burman [12] designs under response surface methodology were also used.A full factorial design and a central composite design with four factors, namely incubation time, incubation temperature, dose of the extract, and AgNO 3 concentration under RSM using Eucalyptus globulus fruit were also reported [13].In contrast, 'one factor at a time' was used on AgNP synthesis by Mentha Iongifolia [14] Oregano (Origanum vulgare L.) is an aromatic herb rich in antioxidant compounds including phenolic acids, flavonoids, and essential oils such as thymol, and, as a result, have health benefits for the human body [15].Origanum-mediated synthesized AgNPs were proposed as alternative antibacterial agents [16,17].Silver nitrate (AgNO 3 ) aqueous solutions with concentrations ranging from 0.5 mM to 100 mM are reported [1,[17][18][19][20] to be used as the precursor for silver ions.The effects of reaction time and temperature were investigated [20].
In this work, the combined effects of incubation time, incubation temperature, metal salt concentration, extract concentration, and sodium hydroxide concentration were investigated using a full factorial design and response surface methodology.The UV-Vis absorption peak wavelength λ 0 , the area under the absorption curve (A), and the Full Width at Half Maximum (FWHM) were used as the responses.To our knowledge, this is the first time such work has been reported for AgNPs synthesized using oregano.

Chemicals-Oregano Extract
AgNO 3 aqueous solution (0.1 M) and sodium hydroxide (NaOH) pellets were purchased from Sigma-Aldrich (Steinheim, Germany).Dried oregano (grown on the island of Lemnos) leaves were purchased from a local herb store in Lemnos, Greece.
The oregano extract (OE) was prepared as follows: 3.76 g of dried oregano leaves were boiled in 100 mL distilled water for 10 min.The final extract was obtained with filtering using cheesecloth.The extract was stored at 4 • C for future experiments.

Silver Nanoparticle Synthesis
A final volume of 2.5 mL aqueous solution was used in all syntheses unless otherwise stated.AgNO 3 (C AgNO 3 ) (0.25-2 mM) was used as the precursor of silver ions [21].The reaction started by adding OE at a concentration ( C ext ) (0.8-20% v/v).NaOH (C NaOH ) (0-7.9 mM) was also added.In a typical synthesis procedure, a mixture of AgNO 3 , OE, and NaOH at specific concentrations was heated in a water bath at a temperature (incubation temperature) of 60 • C for 1 h (incubation time).All syntheses was performed in the dark without stirring.

Characterization Techniques
UV-Vis spectroscopy measurements were performed exploiting the Perkin Elmer-Lambda 25 UV-Vis spectrophotometer in the spectral range 340-700 nm, using 1 mL cuvettes with 1 cm path length.
X-ray Diffraction Patterns (XRD) and Fourier Transform Infrared (FTIR) experiments were carried out as described in a previous work [21].The AgNPs investigated with these techniques (XRD and FTIR) were prepared with the following conditions: AgNO 3 (1 mM), OE (2% v/v), and NaOH (2 mM) were mixed.The obtained nanoparticles were centrifuged at 20,000× g for 30 min at 4 • C prior to these measurements.

Statistical Analysis and Experimental Design
As in previous work [21], nanoparticle formation was observed using visual inspection for a color change in the reaction solution and measuring the UV-Vis absorbance of an aliquot.The UV-Vis spectra were fitted using a Voigt profile [22] with fitting pa-rameters [21]: the peak wavelength (λ 0 ) at maximum absorption, the Full Width at Half Maximum (FWHM), and the peak area under the UV-Vis curve (A).The best fit of the UV-Vis absorption spectra was found using the routine Peak Analyzer of the software Origin Pro (version 2020).The quality of fit was determined using the R square regression coefficient (R 2 ≥ 0.99), and the fit significance was examined using the ANalysis Of Variance (ANOVA) (p-value smaller than 0.05) [21].
Full Factorial Design (FFD) with three independent factors was applied to the measured UV-Vis spectra: OE concentration (X 1 ), AgNO 3 concentration (X 2 ), and NaOH concentration (X 3 ).The aim was to investigate the combined effects, if any, of the independent factors on the responses: the peak wavelength (λ 0 ), the FWHM, and the peak area (A).Response Surface Methodology (RSM) was employed.Three levels were used for each factor: (−1, 0, and 1).Each of the factors was coded using Equation [23] as follows: where X i and x i the coded and the actual value of independent factor i, x oi is the central value (level 0) of factor i, and ∆x i is the step change in x i corresponding to a unit change in the coded value [24].The central values for the experimental design were AgNO 3 (1 mM), OE (2% v/v), and NaOH (1 mM), with corresponding steps 0.5 mM, 1.2% v/v, and 1 mM, respectively.A total of 27 runs (Table 1) were conducted in the experiment and the runs were repeated three times each.These factors and their values were selected after preliminary experiments.
Table 1.FFD with three synthesis parameters (independent factors) with coded factor levels, actual values into parentheses, and measured three mean responses (wavelength at peak maximum λ 0 , peak area A, and FWHM) for AgNPs synthesis via OE.A second-order polynomial was obtained for each response as a function of the coded values (X i ) of the independent factors [6,21]: where β 0 denotes the regression coefficient, β i is the linear coefficient, β ii is the quadratic coefficients, β ij is the second-order interaction coefficients, and X i (i = 1, 2, 3) is the coded values of the three independent factors [21,25].Standard procedures were applied to assess the quality of the regression polynomials [23].ANOVA was applied to assess the significance and adequacy of the model, as well as the significance of the regression coefficients appearing in the derived polynomial [26].
The magnitude and sign of the regression coefficients and Pareto analysis [27] were used as a measure of the importance of the various independent factors and their interactions at a significance level of 5% (p-value < 0.05), unless otherwise stated.Not statistically significant terms were excluded from the polynomial models except for those required for a hierarchical mode [21].

UV-Vis Spectra Analysis
An absorption peak within the range of 400-450 nm is indicative of AgNP formation, which is attributed to a surface plasmon resonance [28][29][30].Color change in the reaction mixture also allows visual monitoring of AgNP formation [31].
In Figure 1, the combined effects of OE and NaOH concentrations on the UV-Vis spectra are plotted.A better absorption curve can be observed at the lowest extract concentration (OE 2% v/v Figure 1a) with the presence of NaOH.A Voigt profile was shown to fit adequately with UV-Vis spectra of AgNP solution in a previous study, providing a method of correlation between nanoparticle formation and synthesis parameters [21].This was the case in this work; however, it occurred only at the lowest extract concentration (OE 2% v/v).Agglomerated or ill-formed nanoparticles [32], their crystallinity [33,34], and charge transfer between nanoparticles can influence the observed UV-Vis spectrum [35].The addition of NaOH changes the pH of the solution.The pH of the reaction changes the chemical nature of the extract, which has an effect of changing its performance and rate of reduction and therefore nanoparticle synthesis [36].The size and shape of silver nanoparticles are affected by the pH of the reaction solution [37][38][39][40].This was investigated further with the addition of hydrochloric acid (HCl), which did not produce any nanoparticles (Figure 2).The addition of NaOH changes the pH of the solution.The pH of the reaction changes the chemical nature of the extract, which has an effect of changing its performance and rate of reduction and therefore nanoparticle synthesis [36].The size and shape of silver nanoparticles are affected by the pH of the reaction solution [37][38][39][40].This was investigated further with the addition of hydrochloric acid (HCl), which did not produce any nanoparticles (Figure 2).The addition of NaOH changes the pH of the solution.The pH of the reaction changes the chemical nature of the extract, which has an effect of changing its performance and rate of reduction and therefore nanoparticle synthesis [36].The size and shape of silver nanoparticles are affected by the pH of the reaction solution [37][38][39][40].This was investigated further with the addition of hydrochloric acid (HCl), which did not produce any nanoparticles (Figure 2).The fitting parameters used in the Voigt profile are related to nanoparticle size, shape, yield, and size distribution [21].It was an attempt to determine the appropriate conditions that produce the smallest peak wavelength with maximum peak area and narrowest FWHM.From the findings, the smallest peak was achieved at incubation temperature (60 The fitting parameters used in the Voigt profile are related to nanoparticle size, shape, yield, and size distribution [21].It was an attempt to determine the appropriate conditions that produce the smallest peak wavelength with maximum peak area and narrowest FWHM.From the findings, the smallest peak was achieved at incubation temperature (60 • C), incubation time 1 h, and NaOH (0-2 mM) (Supporting Information: Figures S1 and S3; Tables S1 and S2).
The corresponding ranges of OE and AgNO 3 concentrations were investigated in a similar manner as shown in Figure 3.The investigation (see Supporting Information: Table S3) determined a range (0.5-1.5 mM) for AgNO 3 and (0.8-3.2% v/v) for OE concentrations.S3; Tables S1 and S2).
The corresponding ranges of OE and AgNO3 concentrations were investigated in a similar manner as shown in Figure 3.The investigation (see Supporting Information: Table S3) determined a range (0.5-1.5 mM) for AgNO3 and (0.8-3.2% v/v) for OE concentrations.

Statistical Modeling of AgNP Synthesis
A quadratic regression model (Equation ( 2)) was applied for each response in order to better understand the effect of all independent factors as well as their interactions in the AgNPs synthesis.The ANOVA for each response is given in Tables 2-4.A p-value smaller than 0.001 can be observed for the quadratic model for both the peak wavelength at maximum λ 0 (Table 2) and the peak area A (Table 3), indicating that the quadratic model was suitable for both responses.This is further supported by the large value of the F statistic.In contrast, a pure model can be observed for the FWHM (Table 4) (p-value = 0.1435) and F = 1.56.The coefficient of determination (R 2 ) of the models for the peak wavelength was 93.92%, whereas for the peak area was 89.41%, which indicated a significant correlation between the observed and predicted values [6,23,41].The model adequacy was tested by applying standard diagnostic tools (see Supplementary Material) [23,26].
The regression coefficients for the wavelength at peak maximum λ 0 are given in Table 5.The wavelength is affected mainly by the NaOH concentration (X 3 ), followed by equal contribution from OE (X 1 ) and AgNO 3 (X 2 ) concentrations.A large contribution appears from the quadratic term of NaOH concentration.A small contribution also appears from the interaction term X 2 X 3 of AgNO 3 and NaOH concentrations.Terms where NaOH concentration appears contribute negatively to the peak wavelength.The response surface (peak wavelength) for AgNP synthesis therefore is provided by the following second-order polynomial: The regression coefficients for peak area A are given in Table 6.The area is affected almost equally by NaOH (X 3 ) and AgNO 3 (X 2 ) concentrations, followed by the OE (X 1 ) concentration.A large contribution appears from the interaction term X 2 X 3 of AgNO 3 and NaOH concentrations, followed by a smaller contribution from the interaction terms X 1 X 2 of OE and AgNO 3 concentrations, and the interaction X 1 X 3 with the negative sign of OE and NaOH concentrations.A large negative contribution appears for the quadratic terms of both AgNO 3 and NaOH concentrations.The response surface (peak area) for AgNPs synthesis therefore is provided by the following second-order polynomial: Pareto analysis percentages are shown in Table 7 for the wavelength at peak maximum λ 0 and the peak area A quadratic model terms.In both cases, the largest contribution comes from the NaOH concentration (X 3 ) with values of 59.53% (wavelength) and 52.53% (area).A total of 97.8% of the peak wavelength is influenced by the linear and quadratic term of NaOH concentration, in contrast to 57.61% for the peak area.The peak area is correlated to the quantity of formed nanoparticles, which should depend on both AgNO 3 (20.74%)and OE concentrations (3.85%).This is not sufficient, however, for the synthesis of nanoparticles, as the presence of NaOH plays a crucial role in both the number of formed nanoparticles (area) and their size (wavelength).This agrees with previous work reporting the effect of pH on nanoparticle size [36,38,40].A total of 96.9% contribution from the linear term of pH on nanoparticle size was reported on green synthesis of silver nanoparticles from gallic acid [8].In contrast, in a previous work [21], the linear term of pH contributes only 10% to the peak wavelength, with the largest contribution (59%) from the third-order interaction term ( BPE 2 × pH (BPE = Banana Peel Extract concentration, see Supporting Information Table S4).The observed different contributions of pH from different plant extracts can be attributed to different compounds involved in metal salt reduction and nanoparticle formation.Examination of the data (Table 1) revealed that the best UV-Vis spectra in terms of minimum wavelength λ 0 at peak maximum, minimum FWHM, and maximum area A can be obtained for the factor combination corresponding to experimental run 23.This run corresponds to an actual OE concentration of 0.8% v/v, AgNO 3 concentration of 1 mM, and NaOH concentration of 1 mM.The measured peak wavelength of 409 nm is smaller than the values reported by other groups [1,[17][18][19][20] who have not investigated pH effects.

XRD
The XRD pattern of the dry powder obtained from the formed AgNPs synthesized using oregano revealed the amorphous nature of the sample, as evidenced by a broad peak at ~25 • .This peak is possibly due to the oregano, although there are discernible Ag contributions from the AgNPs, which overlap with this broad pattern.This behavior is rational since the characteristic peaks of AgNPs are, in general, not easily recognizable when synthesized using natural products.However, in our case the more intense peaks of AgNPs corresponding to (111), ( 200), (220), and (311) reflections are still visible at 38.14 • , 43.69 • , 64.24 • , and 77.40 • , respectively (Figure 4), indicating the successful formation of silver nanoparticles [21,[42][43][44][45][46][47][48].

FTIR
FTIR was used to identify the ligands that surround the nanoparticle surface.Seven absorption bands appear in the spectrum (Figure 5).The weak band at 3749 cm −1 indicates the presence of polyphenols due to the binding of silver ions with hydroxyl group [21,49].The band at 3438 cm −1 originates either from O-H or NH stretching vibration [50,51].The band at 2963 cm −1 indicates C-H stretching for an alkane [52].The small shoulder formed at 2850 cm −1 and 2918 cm −1 arises from the C-H stretching vibrations either from -C-H-or -C-H2-aliphatic compounds [50,51].The band at 1633 cm −1 is attributed to the C-N and C-C stretching [21,49].The sharp band at 1384 cm −1 corresponds to the N=O symmetry stretching, typical of the nitro compounds [21,49].The bands at 1060 cm −1 and 1112 cm −1 are assigned to stretching vibration C-O [53].The band around 836 cm −1 could be attributed to out-of-plane C-H wagging vibrations, the most significant signal used in distinguishing between different types of aromatic ring substitution [54].

FTIR
FTIR was used to identify the ligands that surround the nanoparticle surface.Seven absorption bands appear in the spectrum (Figure 5).The weak band at 3749 cm −1 indicates the presence of polyphenols due to the binding of silver ions with hydroxyl group [21,49].The band at 3438 cm −1 originates either from O-H or NH stretching vibration [50,51].The band at 2963 cm −1 indicates C-H stretching for an alkane [52].The small shoulder formed at 2850 cm −1 and 2918 cm −1 arises from the C-H stretching vibrations either from -C-H-or -C-H 2 -aliphatic compounds [50,51].The band at 1633 cm −1 is attributed to the C-N and C-C stretching [21,49].The sharp band at 1384 cm −1 corresponds to the N=O symmetry stretching, typical of the nitro compounds [21,49].The bands at 1060 cm −1 and 1112 cm −1 are assigned to stretching vibration C-O [53].The band around 836 cm −1 could be attributed to out-of-plane C-H wagging vibrations, the most significant signal used in distinguishing between different types of aromatic ring substitution [54].

FTIR
FTIR was used to identify the ligands that surround the nanoparticle surface.Seven absorption bands appear in the spectrum (Figure 5).The weak band at 3749 cm −1 indicates the presence of polyphenols due to the binding of silver ions with hydroxyl group [21,49].The band at 3438 cm −1 originates either from O-H or NH stretching vibration [50,51].The band at 2963 cm −1 indicates C-H stretching for an alkane [52].The small shoulder formed at 2850 cm −1 and 2918 cm −1 arises from the C-H stretching vibrations either from -C-H-or -C-H2-aliphatic compounds [50,51].The band at 1633 cm −1 is attributed to the C-N and C-C stretching [21,49].The sharp band at 1384 cm −1 corresponds to the N=O symmetry stretching, typical of the nitro compounds [21,49].The bands at 1060 cm −1 and 1112 cm −1 are assigned to stretching vibration C-O [53].The band around 836 cm −1 could be attributed to out-of-plane C-H wagging vibrations, the most significant signal used in distinguishing between different types of aromatic ring substitution [54].

Figure 2 .
Figure 2. Effect of pH on UV-Vis spectra, with the addition of NaOH or HCl at different concentrations.AgNO3 concentration, 1 mM; OE concentration, 2% v/v; incubation temperature, 60 °C; and incubation time, 1 h.

Figure 2 .
Figure 2. Effect of pH on UV-Vis spectra, with the addition of NaOH or HCl at different concentrations.AgNO 3 concentration, 1 mM; OE concentration, 2% v/v; incubation temperature, 60 • C; and incubation time, 1 h.

Table 2 .
ANOVA for the quadratic model for wavelength at peak maximum λ 0 .
df = degrees of freedom, SS = Sum of Squares, MS = Mean Square, * F statistic.

Table 3 .
ANOVA for the quadratic model for peak area A.
Df = degrees of freedom, SS = Sum of Squares, MS = Mean Square, * F statistic.

Table 4 .
ANOVA for quadratic model for FWHM.
df = degrees of freedom, SS = Sum of Squares, MS = Mean Square, * F statistic.

Table 5 .
Regression coefficients for wavelength at peak maximum λ 0 .

Table 6 .
Regression coefficients for peak area A.

Table 7 .
[27]to analysis[27]for significant terms in the quadratic model for both the peak wavelength λ 0 and peak area A.