The Impact of Bacteria of the Genus Bacillus upon the Biodamage/Biodegradation of Some Metals and Extensively Used Petroleum-Based Plastics

: This paper tackles bacteria of the genus Bacillus as both biodamaging/biodegrading and biocontrolling agents. The article addresses the said bacteria’s ability to form bioﬁlms and corrosive, antimicrobial and antibioﬁlm proactive compounds, primarily, siderophores. Their role depends on the species, microorganism strain, production of antimicrobial substances, bioﬁlm formation, and the type of damaged material. The bacteria under analysis have demonstrated the ability to cause as well as inhibit biodamage. The involvement of bacteria of the genus Bacillus in microbiologically inﬂuenced corrosion processes is determined by the production of corrosive metabolites and the impact of certain bioelectrochemical mechanisms. Lipopeptides generated by Bacillus subtilis (surfactin, iturin and fengycin) are capable of modifying surfaces’ hydrophobic properties and impacting the microbes’ adhesion to surfaces. Produced by Bacillus velezensis , the siderophore bacillibactin at a high concentration is capable of inhibiting the formation of bacterial bioﬁlms, thus slowing down the degradation of materials. Further study of siderophores as green inhibitors of microbiologically inﬂuenced corrosion may be promising as the said compounds possess antibioﬁlm-forming properties and high-intensity inhibitory capabilities.


Introduction
In the context of rapid development of technology and construction, as well as creation of new materials, the issue of material biodamage and appropriate protection appears as the focus of substantial research [1][2][3]. Biodamage (biodegradation) of materials can be responsible for human-made ecological catastrophes [1]. Bactericides have traditionally been used to prevent microbiologically influenced corrosion (MIC), although they pose health, safety and environmental problems [4]. Derivatives of substandard pesticides are proposed as inhibitors of MIC [5].
On the other hand, the processes of biodegradation involve chemical elements in geochemical cycles leading to the removal of xenobiotics from the environment [3].
As an alternative, the use of microorganisms (biocides) is suggested as a protective means against biodamage [6]. However, the research in the field of biological control has been conducted under laboratory conditions and its effectiveness has not yet been confirmed [7].
Sulfate-reducing bacteria (SRB) are most commonly associated with MIC, while little attention has thus far been paid to the representatives of other taxonomic groups [7]. Bacteria of the genus Bacillus deserve attention both as biodamaging/biodegradable and biocontrolling agents, as they are able to form corrosive compounds [8], polymer-degrading compounds [9], antimicrobials [10] and antibiofilm-forming compounds [11]. Therefore,  [19,20].

Reaction Type Reaction Equation
Oxidation The B. licheniformis biofilm on a C1018 (UNS G10180) carbon steel coupon surface was observed via a scanning electronic microscope (SEM) [19]. In this study, pitting data indicate that B. licheniformis is more aggressive than typical SRB.
Electrochemical and surface analyses and live/dead staining were performed by Wan et al. [20] to study the corrosion of X80 pipeline steel in the presence of B. cereus. As the results of SEM and live/dead staining testify, some B. cereus appeared to adhere to X80 steel. Electrochemical impedance spectroscopy showed that B. cereus could accelerate the corrosion of X80 steel. In addition, surface morphology observations indicated that B.
cereus could accelerate pitting corrosion in X80 steel [20]. The corrosive effect of B. cereus strain SNB4 on mild steel coupons is shown by Bano et al. [21].
The synergistic effect of slime-forming bacteria B. cereus var. mycoides strain CECT 193 and SRB Desulfovibrio desulfuricans strain DSM 642 was investigated by Santana et al. [22]. This study discusses B. cereus's stimulation of the development of sulfatereducing bacteria and, accordingly, intensifying the tendency to progress corrosion [22]. A seawater system with sodium lactate containing both investigated strains demonstrated a clear decrease in the polarization resistance throughout the test duration (14 days). The value of the corrosion potential tends to negative values to a greater extent than the other systems, which indicates the synergic effect of both bacteria. The authors noted that B. cereus var. mycoides is a facultative anaerobic bacterium and, therefore, it favors the development of SRB and consequently determines a greater tendency towards corrosion after an initial phase of enhanced protection [22].
The influence of Bacillus mycoides (B. mycoides) upon samples of Zn, Al and steel was studied over 2 years under controlled humidity (97%) and temperature (26 • C) [23]. The corrosion activity was evaluated periodically by measurements of polarization resistance via electrochemical impedance spectroscopy. Acceleration of zinc corrosion under the influence of B. mycoides is discussed in [23].
Surface analysis methods, a mass loss method and electrochemical tests were employed to investigate the corrosion behavior of Q235 steel under the synergistic effect of Thiobacillus thiooxidans (T. thiooxidans) and Bacillus [24]. The study explicates that circular corrosion poles, much different from the ones in the single-bacterium cultures, appeared on the surface of the sample immersed in the mixed culture. The corrosion rate identified via the mass loss method in the microbial association was close to the average values typical for a single-bacterium system. Electrochemical impedance spectroscopy shows that two time constants existed in the T. thiooxidans + Bacillus system after 2 days of immersion, where the corrosion resistance of the film was initially enhanced and then weakened [24]. Karn et al. [25] recorded different levels of peroxidase and catalase enzyme production by strains of Bacillus sp. In a specific range, the enzymes can induce corrosion, however, this is a strain characteristic [25]. In the experiment, Bacillus paralicheniformis (B. paralicheniformis) strain 720 R2A_5R_0.5, isolated as a part of the International Space Station microbial community, was aerobically and anaerobically incubated together with Cupriavidus metallidurans strain pH5_R2_1_II_A and Cutibacterium avidum strain R7A_A1_IIIA with untreated aluminum alloy platelets, anodized aluminum alloy platelets and pieces of NOMEX®fabric [26]. The NOMEX®fabric itself remained intact over a period of 6 weeks, but served as an excellent attachment surface for B. paralicheniformis biofilms. B. paralicheniformis adhered to neither the untreated nor anodized aluminum alloy. However, the untreated aluminum alloy which was co-incubated with B. paralicheniformis showed only some signs of corrosion compared to the untreated negative control incubated in sterile medium [26]. Lipopeptides produced by B. subtilis (surfactin, iturin and fengycin) decreased the hydrophobicity of Teflon [27]. Table 2 provides generalizations on the involvement of the genus Bacillus in the processes of biodamage of metals and alloys.
Therefore, the bacteria of the genus Bacillus are representatives of microorganisms investigated in the processes of MIC of metals and alloys in both monocultures and associative cultures. The involvement of these bacteria in MIC processes is associated with the production of corrosive metabolites and the involvement of bioelectrochemical mechanisms. Table 2. Diversity of members of the genus Bacillus involved in biodamage of metals and alloys.

Bacteria of the Genus Bacillus in the Biodegradation of Some Synthetic Plastics
In this study, we focused on the diversity of bacteria of the genus Bacillus, which biodegrade polyethylene (PE), polypropylene (PP), polystyrene (PS), polyvinyl chloride (PVC), poly (ethylene terephthalate) (PET) and polyurethane (PUR). These polymers are synthesized from fossil hydrocarbons, a non-renewable resource, and comprise more than 90% of the global total production of polymeric materials [28]. Enzymes released by microorganisms during growth and development act as aggressive media in biodamage of insulating materials [1]. In particular, such compounds are able to produce the bacterium B. mesentericus (B. subtilis), found on polymer coatings [1]. Degradation of polyethylene can be classified as abiotic (caused by temperature and UV irradiation) or biotic (biodegradation caused by the action of microorganisms). Microorganisms modify and consume the polymer, leading to changes in its properties. Bacteria of the genus Bacillus, among other bacterial strains, are involved in the biodegradation of polyethylene [29,30]. B. amyloliquefaciens, B. brevis, B. cereus, B. circulans, B. halodenitrificans, B. mycoides, B. pumilus, B. sphericus and B. thuringiensis appear to be particularly active agents causing biodegradation of this material. Restrepo-Flórez et al. [29] highlight that although the damage to polyethylene is connected to only one of these two damage modes, both typically act cooperatively in nature [31]. The abiotic mechanisms of deterioration of polyethylene have been described in [31]. The biodegradation of polyethylene and mechanisms associated with this process are analyzed in review publications [29,30]. The biodegradation of polyethylene under normal conditions is extremely slow, while the knowledge of complete metabolic pathways involved in the process, as well as the inventory and structure of respective enzymes, is quite basic [29]. The authors discuss changes of PE in the presence of microorganisms: (1) functional groups on the surface; (2) the surface topography; (3) the hydrophobicity/hydrophilicity of a surface; (4) mechanical properties; (5) crystallinity; (6) molecular weight distribution. It is indicated that the loss of molecular weight and the oxidation of the molecules are the result of synergistic effects caused by biotic and abiotic factors (photo-oxidation or heat treatment) [29]. In particular, thermo-irradiation pretreatment was important for the biodegradation of PE by Bacillus amyloliquefaciens (B. amyloliquefaciens) [32]. Biofilm colonization is the initial step in the degradation of this polymer [29]. Bacteria that form biofilms are capable of producing surfactants, molecules that can mediate the attachment process of microorganisms to a hydrophobic surface [29]. Hydrocarbon polymers are resistant to biodegradation, which results from highly stable C-C and C-H covalent bonds [33]. Restrepo-Flórez et al. [29] note the theoretical possibility of polyethylene being used as a carbon source for microorganisms, similar to many other hydrocarbons, but subject to the reduction in PE molecular weight by the chemical/biochemical processes. The presence, in some members of the genus Bacillus, of enzymes related to the Pseudomonas putida GPo1 membrane-bound alkane hydroxylase system [34] increases this probability. Such enzymes are involved in a complicated chemical reaction: the regio-and stereospecific activation of C-H bonds. There are reports that the weight loss of degradable polyethylene (PE with chemical or photoinitiators or both) positively correlated with CO 2 emission in the consortium of Pseudomonas frequentans + B. mycoides under the condition of treatments with or without preheating [35]. Based on this, the researchers conclude that the disposal of degradable polyethylene by these bacteria is a source of carbon.
The initial step involves hydroxylation of C-C bonds, generating primary or secondary alcohols, which are further oxidized to aldehydes or ketones, and then to carboxylic acids [36]. Thus, microbial oxidation decreases the number of carbonyl groups due to the formation of carboxylic acids. Carboxylated n-alkanes are analogous to fatty acids, which can be catabolized by bacteria via the β-oxidation system pathway ( Figure 1). However, neither the breaking of C-C bonds within the backbone of PE polymers nor the generation of long carbon chain carboxylic acid hydrolysis products have been reported [36].
Corros. Mater. Degrad. 2021, 2, FOR PEER REVIEW 5 ylene (PE with chemical or photoinitiators or both) positively correlated with CO2 emission in the consortium of Pseudomonas frequentans + B. mycoides under the condition of treatments with or without preheating [35]. Based on this, the researchers conclude that the disposal of degradable polyethylene by these bacteria is a source of carbon. The initial step involves hydroxylation of C-C bonds, generating primary or secondary alcohols, which are further oxidized to aldehydes or ketones, and then to carboxylic acids [36]. Thus, microbial oxidation decreases the number of carbonyl groups due to the formation of carboxylic acids. Carboxylated n-alkanes are analogous to fatty acids, which can be catabolized by bacteria via the β-oxidation system pathway ( Figure  1). However, neither the breaking of C-C bonds within the backbone of PE polymers nor the generation of long carbon chain carboxylic acid hydrolysis products have been reported [36]. Thus, bacterial isolates В. amyloliquefaciens contributed to the depolymerization of biodegraded products in extracellular media, indicating the biodegradation process of PE [37]. The participation of B. brevis in PE biodegradation is noted in the work of Wasserbauer et al. [38]. B. cereus degraded UV-irradiated PE associated with a pronounced extracellular production of both laccases and MnP [39]. Biodegradable properties against PE were also observed for B. cereus strain Ma-Su CECRI-1 [40] and B. cereus strain A5,a Thus, bacterial isolates B. amyloliquefaciens contributed to the depolymerization of biodegraded products in extracellular media, indicating the biodegradation process of PE [37]. The participation of B. brevis in PE biodegradation is noted in the work of Wasserbauer et al. [38]. B. cereus degraded UV-irradiated PE associated with a pronounced extracellular production of both laccases and MnP [39]. Biodegradable properties against PE were also observed for B. cereus strain Ma-Su CECRI-1 [40] and B. cereus strain A5,a [41]. In the latter case, a high biodegradable activity (35.72 ± 4.01%) in relation to PE was registered [41]. The ability to biodegrade PE is also inherent to B. subtilis [42]. B. subtilis produced surface active compounds (biosurfactants) that enhance the degradation process of PE [43].
The ability of B. mycoides and B. subtilis (Bacillus species indigenous to the Niger Delta mangrove soil) to biodegrade polyethylene was studied by Ibiene et al. [44].
Bacillus safensis and B. amyloliquefaciens have demonstrated the biodegradable ability for low-density polyethylene thermoplastic. Moreover, B. safensis had better biodegradable ability than B. amyloliquefaciens, shown by the registered weight reduction [45].
It is worth noting that only genus (Bacillus) identification of bacteria has been established in most studies. Thus, in a number of studies, Bacillus sp. are indicated as polyethylene-degrading bacteria [46][47][48][49][50][51], the ability of which to form a biofilm on the surface of this material and reduce its hydrophobicity by isolated bacteria was noted in the article of Yang et al. [49]. The biofilm formation on the surface of polyethylene and its biodegradation were also observed for B. mycoides [35].
A brief summary of the articles devoted to the biodegradation of PE with the participation of bacteria of the genus Bacillus is presented in Table 3.
Biodegradation of polypropylene has been improved by using polymer blends of carbohydrates, starch or cellulose blends such as that reported for polyethylene and polystyrene [56]. The use of the blends facilitates adhesion of the microorganisms to the surface of the polymer and acts as a co-metabolite. Biodegradation of polycaprolactone blended PP has also been demonstrated using lipase since lipase is well known to degrade the ester linkages of polycaprolactone [56].
Strains B. subtilis and B. cereus formed biofilm on PET and poly (lactic acid), demonstrating biochemical activity and accelerating biodegradation of both plastic materials [64]. B. cereus was also identified as part of two consortia capable of biofilm formation and PET degradation [65]. B. megaterium formed a biofilm on PET film [28]. Carboxylesterases from B. licheniformis and B. subtilis partially hydrolyzed PET fibers and showed a high activity against PET oligomers [66].
B. flexus has been proved to biodegrade poly (vinyl chloride) (PVC) film [67]. Bacteria of this species have been able to form dense biofilm on the plastic film surface and cause a decrease in the mean molecular weight of the PVC film [67]. Bacillus sp., triggering degradation of PVC, caused weight loss of the material of 0.26 ± 0.02% in comparison to initial weights after 90 days [51].
The involvement of bacteria of the genus Bacillus in the biodegradation of polyurethanes is discussed in a review article by G.T. Howard [68]. PUR-degrading bacteria are B. chitinolyticus and B. pumilus [69] and B. subtilis [70][71][72].
Oxidative degradation has been generally associated with poly(ether-urethane) [73]. This mechanism is illustrated by the following reactions (Table 4).   The formation of the Penicillium-Bacillus biofilm and its architecture help in the effective transport of the bacterium, colonization of PE and subsequent degradation of its surface by enzymatic reactions boxylesterases from B. licheniformis and B. subtilis partially hydrolyzed PET fibers and showed a high activity against PET oligomers [66].
The mechanism of PET biodegradation is demonstrated in Figure 2. The PET-digesting enzyme labeled as PETase converts PET to mono(2-hydroxyethyl) terephthalic acid (MHET), with minimal amounts of terephthalic acid (TPA) and bis(2-hydroxyethyl)-TPA as secondary products [56]. B. flexus has been proved to biodegrade poly (vinyl chloride) (PVC) film [67]. Bacteria of this species have been able to form dense biofilm on the plastic film surface and cause a decrease in the mean molecular weight of the PVC film [67]. Bacillus sp., trigger-  Table 4. Reactions of the oxidative degradation poly(ether-urethane) [73].

Radical initiation
Thus, the reactive oxygen species initiate degradation of polyether urethanes through oxidative attack of the soft segment. This reactive oxygen species abstracts an alphamethylene hydrogen atom from the polyether soft segment. The addition of a hydroxyl radical to the carbon radical forms a hemiacetal, which oxidizes to an ester. Acid hydrolysis of the ester results in chain scission of the soft segment and formation of acid end groups. Significant chain scission results in the solubilization and extraction of low molecular weight degradation products [73].
A similar oxidative mechanism was proposed for hard segment degradation [73]. Oxygen radicals abstract an alpha-methylene hydrogen atom from the chain extender at the urethane. Additional hydroxyl radicals combine with the chain radical to form a highly reactive carbonyl hemiacetal. Oxidative hydrolysis of the carbonyl hemiacetal results in chain scission and formation of an unstable carbamic acid and carboxylic acid end groups [73]. The carbamic acid decarboxylates readily to form a free amine. The mechanism of polyurethane biodegradation with the participation of polyurethane esterases is shown by Mohanan et al. [56] (Figure 3).
Oxygen radicals abstract an alpha-methylene hydrogen atom from the chain extender at the urethane. Additional hydroxyl radicals combine with the chain radical to form a highly reactive carbonyl hemiacetal. Oxidative hydrolysis of the carbonyl hemiacetal results in chain scission and formation of an unstable carbamic acid and carboxylic acid end groups [73]. The carbamic acid decarboxylates readily to form a free amine. The mechanism of polyurethane biodegradation with the participation of polyurethane esterases is shown by Mohanan et al. [56] (Figure 3). Ru et al. [74] present the metabolic pathways of degradation of the plastics considered by us (Figure 4). Table 5 shows generalizations the biodiversity of bacteria of the genus Bacillus, which are involved in the biodegradation of synthetic plastics. Table 5. Diversity of bacteria of the genus Bacillus, which are involved in the biodegradation of synthetic plastics.   Ru et al. [74] present the metabolic pathways of degradation of the plastics considered by us (Figure 4).

The Application of Bacteria of the Genus Bacillus to Materials' Biodamage Control
It should be noted that today the question of the application of biological control for protection against corrosion damage is debatable, as none of the methods for corrosion inhibition by microorganisms found to be successful reached the practical application stage [7]. However, there are noteworthy publications on the possibility of using bacteria of the genus Bacillus to control the biodamage of materials.
The inhibition of corrosion by bacteria is often accomplished by: (1) a decrease in the corrosive action of the medium in restricted parts of the metal-bulk solution interface, for instance, by neutralizing the acidity of the medium; (2) the formation of protective films on the metal surface or providing new protective films, in particular through the production of EPS with metal-binding abilities; and (3) decreasing the cathodic reaction due to the consumption of a cathodic electron acceptor by microbes [6].
In addition, the biocontrol properties of some microorganisms are determined by their high antibacterial properties associated with the formation of antimicrobial compounds [75] and antibiofilm-forming properties due to their ability to affect the quorum sensing system [11]. Such microorganisms include members of the genus Bacillus. Thus, a number of studies have proved that corrosion results from the formation of biofilms, while Bacillus sp. [24,76], B. thuringiensis strain SN8 [21], B. cereus [77], B. licheniformis (including genetically modified ones) [78], B. subtilis [79][80][81], B. firmus strain H2O-1 [82,83] and B. brevis [79] are responsible for producing antimicrobial compounds.
In particular, in conditions of artificial seawater in the presence of a protective biofilm of B. subtilis strain WB600, passivation of Al 2024 was recorded. The addition of antibiotics led to the death of bacteria in the biofilm, which was reflected in the impedance spectra. Adding antibiotics to sterile artificial seawater had no effect on corrosion processes [81].
The inhibiting effect of B. thuringiensis strain SN8 on steel is shown in the publication by Bano et al. [21]. B. thuringiensis strain SN8 inhibited the MIC of materials in soil conditions over a period of 150 days. The corrosion-preventing properties of the B. thuringiensis strain SN8 dissipated after this period. It stands to reason that corrosioninhibiting/protective properties of biological agents must be verified in term of the maximum time frame for their effectiveness [84].
The inhibitory effect of a biofilm formed by B. cereus was shown by Aїmeur et al. [77].
Ornek et al. evaluated the effect of aluminum-chelating anionic peptides, which release biofilms of natural and genetically modified Bacillus on the pitting of aluminum alloy in continuous reactors [78]. The corrosion rate of aluminum alloy 2024 was reduced by 90% due to γ-polyglutamate-forming biofilm of B. licheniformis. Meanwhile, one of the peptides that secreted the genetically engineered biofilm of B. subtilis only slightly reduced the pitting compared to the biofilm on the control material, which already significantly reduces the corrosion of aluminum compared to the sterile control one.
From thermophilic B. licheniformis on a steel substrate, the bacterial biofilm and the nature of its extracellular polymeric substances have been probed chemically and electrochemically for their influences on metal dissolution within an incubation period [85]. Corrosion inhibition in the presence of varying concentrations (in CFU/ml) of these bacteria in biotic inoculate systems is explained in terms of corrosion resistance and biofilm capacity. Steel's corrosion rate is reduced significantly in saline culture medium within the range of concentrations of bacteria under study compared with the sterile control. This is attributed to the adhesion of relatively compact and dense "beneficial" biofilm as well as the secretion of corrosion-inhibiting substances from the bacterial biofilm as revealed during surface analysis [85].
Jayaraman et al. [79] found that biofilms of genetically engineered B. subtilis secreting the antibiotics indolicidin, bactenecin and probacterin are able to inhibit the growth of SRB that cause corrosion (D. vulgaris and D. gigas) and significantly reduce corrosion in a continuous culture.
The gramicidin S peptide, which naturally produced the biofilm-forming strain of B. brevis, also inhibited the colonization of SRB and reduced the corrosion of the steel [86]. It should be noted that antibiotics, such as ampicillin, inhibited only the growth of SRB when added prior to the colonization of SRB. At the same time, the associative culture of B. brevis (producing S-gramicidin) with SRB completely blocked the growth of the latter.
Bacillus sp. strain H2O-1, isolated from the connate water of a Brazilian reservoir, produces an antimicrobial substance (denoted as AMS H2O-1) that is active against sulfatereducing bacteria, which are the major bacterial group responsible for biogenic souring and biocorrosion in petroleum reservoirs. AMS H2O-1 is a mixture of four surfactin-like homologues, and its biocidal activity and surfactant properties suggest that this compound may be a good candidate for sulfate-reducing bacterial control. Thus, it is a potential alternative to the chemical biocides or surface-coating agents currently used to prevent SRB growth in petroleum industries [82].
A new antimicrobial substance is being developed by using biosurfactant produced by indigenous oil reservoir Bacillus sp. to prevent and eradicate biofilm [76]. The biosurfactant is able to inhibit Pseudomonas sp. strain 1 and Pseudomonas sp. strain 2 attachment to carbon steel ST37 surfaces and also able to eradicate preformed biofilm on steel surfaces. This study also showed the reduction of corrosion rate in carbon steel ST37 as a result of material treatment with biosurfactants. The authors suggest that the biosurfactant in this study could be a good candidate for a new anticorrosion agent [76].
The effects of bacteria of the genus Bacillus depend not only on the formation of antimicrobial compounds and protective biofilm, but also on the type of damaged material. In particular, Juzeliunas and co-authors found that B. mycoides accelerates zinc corrosion, inhibits aluminum corrosion and does not affect mild steel [23].
Bacillus sp. strain ΠКИ-12Лis considered to be a promising biological agent for the creation of a biological product for the protection of polymeric composite materials from biological damage due to its fungicidal activity [87].
The synthesis of extracellular molecules such as biosurfactants or proteins should have major influence on bacterial adhesion. These molecules may be adsorbed on surfaces and modify their energy characteristics. Under these conditions, adhesion rates are not dependent upon the initial characteristics of the substrate but on those of fouled surfaces [88].
Lipopeptides produced by B. subtilis (surfactin, iturin and fengycin) are able to modify the surface hydrophobicity of stainless steel and Teflon and, consequently, influence microbial adhesion to their surfaces [27]. The authors showed that these effects depend on the lipopeptide type, the concentration and the substratum. Thus, iturin A had no effect in relation to stainless steel; surfactin and fengycin increased the hydrophobicity of steel. The bioconditioning of surfaces using microbial surfactants has been suggested as a new strategy for reducing adhesion of bacteria to surfaces [27].
In the article of Wang et al. [91], high activity against marine fouling by proteases isolated from B. velezensis strain SM-1 was noted. This may be the basis of the modern eco-friendly approach to creating materials against fouling. Khan et al. isolated the bacterium B. methylotrophicus WY with the ability to quench the quorum, which can be used to control membrane biofouling [11]. In particular, it was discovered that this strain has significant influence on the degradation of acylhomoserinlactone (AHSL)-a kind of signaling molecule required for the development of biofilm. The inhibitory activity of B. velezensis strain K68 against the biofilm of Streptococcus mutans on polystyrene was studied [92]. Bacillus sp. strain H2O-1 (with 99.8 and 99.5% similarity of the 16S rRNA gene sequence between it and the type strains of B. amyloliquefaciens and B. methylotrophicus, respectively) produced an antimicrobial substance that was active against sulfate-reducing bacteria [82].
High concentrations of the catalase and peroxidase enzymes produced by some strains of Bacillus sp. can inhibit corrosion [25]. However, the exact mechanism and enzymatic role are unknown. Further research targets the potential role of these enzymes [25].

Siderophores of Bacteria in Corrosion Damage of Materials
It is known that the corrosion process takes place in a biofilm formed with the participation of a microbial community, the main participants of which are SRB [1,7,93]. From the end of the 20th to the beginning of the 21st century, the prospect of preventing corrosion damage to materials by forming protective aerobic bacterial biofilms capable of producing siderophores was discussed [94]. Siderophores are low molecular weight compounds that chelate Fe (III) ions, convert insoluble Fe (III) to the bioavailable form of Fe (II) and are synthesized by some bacteria, fungi and plants with iron ion deficiency in the medium [95,96]. Kostakioti et al. note [97] that chelating agents inhibit and/or disrupt the formation of the biofilm at stages 2 and 3 of biofilm formation, the formation of microcolonies and the maturation of the biofilm, respectively [97]. Siderophores are able to prevent the formation of biofilms of SRB on surfaces [98]. We studied the formation of SRB biofilms on the surface of polypropylene, which is used in the construction of pipelines [99,100] and PET under the influence of bacillibactin-producing strains of B. velezensis [98]. Thus, a significant positive effect of supernatant (7% by volume) of B. velezensis strains NUChC C1 and NUChC C2b cultures in meat-peptone broth (MPB) on the biofilm formation of sulfate-reducing bacteria of Desulfovibrio oryzae (D. oryzae) strain NUChC SRB1 on the surface of polypropylene was noted [101]. Due to the production of B. velezensis strains NUChC C1 and NUChC C2b siderophore bacillibactin [98], it is possible that under these conditions the concentration of Fe (III) ions in the medium increases, which increases the intensity of sulfate-reducing bacteria biofilm formation. According to Donlan [102], with increasing concentration of Fe (III), there is a better adhesion of bacterial cells to the surface, which occurs by reducing the repulsive forces between negatively charged bacterial cells and surfaces. The influence of ions of iron on SRB-influenced corrosion is a complex phenomenon: (1) the hydrogenase of SRB is regulated by Fe 2+ availability; (2) high levels of soluble iron prevent the formation of FeS protective layers [93].
However, with respect to D. oryzae strain NUChC SRB2 under these conditions, a slight significant inhibition of the intensity of biofilm formation was observed. Additionally, a significant decrease (2 times) in the intensity of sulfate-reducing bacterium D. oryzae strain NUChC SRB1 biofilm formation was registered on the surface of PET with a content in the medium of 22% MPB supernatant cultures of B. velezensis strains NUChC C1 and NUChC C2b [98]. It is possible to assume two mechanisms lowering the intensity of biofilm formation of SRB at a high concentration of bacillibactin. The first one involves bacillibactin as a siderophore chelator. When present in a high concentration in the supernatant, it apparently binds iron, reducing its amount, thus resulting in impaired bacterial biofilm formation. It is known that catecholate siderophores, which include bacillibactin, show a high affinity for iron [103][104][105]. The ability of chelators to inhibit the formation of biofilms is discussed in [97], while their capability of lowering the intensity of biofilm formation by reducing the concentration of iron is addressed in [106]. Under iron-deficient growth conditions, the microbial surface hydrophobicity decreases, which alters the surface protein composition and limits biofilm formation [107]. In general, the corrosion process involving bacteria of the genus Bacillus is associated with iron homeostasis as the increase in the content of ions of this metal stimulates the formation of biofilms (protective or corrosive, determined by the metabolism of a particular species and strain of bacteria). The second mechanism may be the modification of the surface properties of the material by bacillibactin from the supernatant in a high concentration, which affects the ability of SRB to form biofilms on it. In particular, it is indicated that catecholate siderophores constitute a class of natural products useful for surface modification [108]. We can assume that high concentrations of artificially introduced siderophore chelator will inhibit the corrosion process due to inhibition of biofilm formation and/or modification of the material surface properties. The validity of the proposed mechanisms has yet to be investigated.
Siderophores are environmentally unobjectionable compounds with high corrosion inhibitory properties on steel [109][110][111][112], promoting passivation of metals [113][114][115]. They are referred to as green corrosion inhibitors along with macromolecules, bacteria, alkaloids and polyphenols [89]. Bacillus sp. strain AS7 is a producer of siderophore desferrioxamine B [113]. The obtained siderophore worked as a green smart corrosion inhibitor of SAE-1010 carbon steel at a minimal concentration of 75 ppm [88]. Based on the obtained data, we believe that the supernatant from cultures of bacillibactin-producing strains of B. velezensis strains NUChC C1 and NUChC C2b can be used as a smart green inhibitor to prevent microbe-induced corrosion by inhibiting the development of SRB biofilms. A further prospect is the study of microbiologically influenced corrosion of steel under the influence of SRB and the presence of supernatant from these cultures of B. velezensis.
The generalization of the protective activity of bacteria of the genus Bacillus in relation to some biodegradation materials is presented in Tables 6 and 7. Table 6. Protective activity of bacteria of the genus Bacillus in relation to material biodegradation.

Progress, Challenges and Future Direction for This Work
The involvement of bacteria of the genus Bacillus in biodamage/biodegradation of materials has been actively studied in recent years. Today, it is known that they are either corrosively active participants in microbiologically influenced corrosion, or act as biological control agents, protecting materials from damage. The functions of bacteria of the genus Bacillus in MIC processes are associated with the production of corrosive metabolites and the impact of certain bioelectrochemical mechanisms. Among the compounds produced by bacteria of the genus Bacillus important for the control of biodamage are antibiotics, lipopeptides, biosurfactants, poly-γ-glutamic acid and siderophores [76,78,79,86,87,98,113]. Such compounds have either an antimicrobial effect or are able to modify the hydrophobicity of material surfaces, thereby affecting the adhesion of bacterial cells on it, which is reflected in the formation of the biofilm. These compounds are environmentally unobjectionable, and therefore are promising as the green corrosion inhibitors. As a prospect of research in this field, we see the study of siderophores as green inhibitors of microbe-induced corrosion, in particular bacillibactin, because these compounds combine antibiofilm-forming properties with high inhibitory properties.

Conclusions
Bacillus are representatives of microorganisms involved in the processes of microbiologically influenced corrosion of metals and alloys and biodegradation of synthetic plastics in both mono-and associative cultures. Their role depends on the species, strain of the microorganism, the production of antimicrobial substances, the biofilm formation and the type of damaged material. On the one hand, these bacteria can be agents of biodamage, and on the other hand they can inhibit biodamage. The involvement of bacteria of the genus Bacillus in MIC processes is associated with the production of corrosive metabolites and the impact of bioelectrochemical mechanisms. Lipopeptides produced by B. subtilis (surfactin, iturin and fengycin) are able to modify the surface hydrophobicity, to influence microbial adhesion to the surfaces. It is possible that siderophore chelators (bacillibactin) can also modify surface hydrophobicity and at high concentrations are able to inhibit bacterial biofilm formation, thus slowing down the degradation of materials. Therefore, the process of microbiologically influenced corrosion under the influence of bacteria, the genus Bacillus, producing siderophores, requires further investigations. Thus, the generalized scheme of mechanisms of participation of bacteria of the genus Bacillus in the processes of biodamage of some metals and plastics can be represented as follows ( Figure 5).
genus Bacillus in the processes of biodamage of some metals and plastics can be represented as follows ( Figure 5).