Influence of Nanoceramic-Plated Waste Carbon Fibers on Alkali-Activated Mortar Performance

: Waste carbon fibers as reinforcing elements in construction materials have recently gained increasing interest from researchers, providing outstanding strength performance and a lower environmental footprint compared to virgin fibers. Combination with cement-free binders, namely alkali-activated materials, is becoming increasingly important for sustainable development in the construction industry. This paper presents results relating to the potential use of waste carbon fibers in alkali-activated mortars. The waste carbon fiber fraction utilized in this research is difficult to integrate as reinforcement in ceramic–cementitious matrices due to its agglomerated form and chemical inertness. For this reason, a nanoceramic coating pretreatment based on nanoclay has been implemented to attempt improvements in terms of deagglomeration, dispersibility, and compatibility with alkali-activated materials. After chemical–physical and microstructural analysis on the nanoclay-plated fibers (including X-ray diffraction, IR spectroscopy, contact angle measurements, and electron microscopy) mortars were produced with four different dosages of treated and untreated waste fibers (0.25 wt.%, 0.5 wt.%, 0.75 wt.%, and 1 wt.%). Mechanical tests and fractographic investigations were then performed. The nanoclay coating interacts compatibly with the waste carbon fibers and increases their degree of hydrophilicity to improve their deagglomeration and dispersion. Compared to the samples incorporating as-received fillers, the addition of nanoclay-coated fibers improved the strength behavior of the mortars, recording a maximum increase in flexural strength of 19% for a fiber content of 0.25 wt.%. This formulation is the only one providing an improvement in mechanical behavior compared to unreinforced mortar. Indeed, as the fibrous reinforcement content increases, the effect of the nanoclay is attenuated by mitigating the improvement in mechanical performance.


Introduction
The cement industry is responsible for considerable emissions of climate-altering gases every year, accounting for about 7% of the global total carbon footprint [1].Hence, efforts in developing green alternatives to ordinary cementitious materials are of the utmost importance.Alkali-activated materials (AAMs) are recognized as the most attractive candidates to replace traditional concrete and mortars due to their lower ecological impact, high early strength, excellent corrosion durability, and high-temperature stability [1,2].
Particularly, considering sustainability issues, AAMs are produced from silica and aluminarich industrial and agricultural by-products (fly ash, slag, silica fume, rice husk ash, palm oil ash), bringing the potential to face challenges of limited available landfill spaces for the disposal of these waste materials [2].However, just like ordinary cement-based materials, AAMs are brittle, show poor strength to tensile and flexural loadings, and experience sudden failure, limiting their suitability for several structural applications.To address this issue, the inclusion of random short fibers (steel, polymers, carbon, minerals) as reinforcements in AAM composites enhances toughness, ductility, and mechanical strength by bridging and arresting the crack propagation [3].
The implementation of carbon fibers (CFs) as reinforcements for concrete applications provides several benefits in comparison to traditional steel reinforcement.CFs exhibit lower density, higher thermo-mechanical stability, higher strength-to-weight ratio, and most importantly, greater chemical stability and durability [4].Furthermore, CFs are the most used conductive fillers to realize electrically conductive cement matrices for smart structural heal monitoring (self-sensing cementitious composites) [5].These peculiarities enable the possibility of designing thinner structures without compromising their loadbearing capacity and durability while reducing their environmental impact and making construction more durable, sustainable, and cost-effective [6].However, the use of virgin fibers is very restricted in the construction materials industry because of their high cost and energy-intensive production process.Indeed, virgin CFs involve higher embodied energies than other synthetic fibers, such as glass fibers, and their utilization is limited in the application fields where the high costs can be justified by a substantial gain in mechanical performance and weight saving (e.g., the aerospace sector) [7].
A "circular" route to strengthen cementitious and alkali-activated concrete or mortars with CFs is the use of recycled fibers.Recycled carbon fibers (rCFs), mainly derived from pyrolysis of CF-reinforced polymeric composites (CFRPs), were recently investigated in the performance of cement-based composites [8][9][10].Lamba et al. [8] investigated the influence of the aspect ratio (15 mm and 25 mm fiber length) and volume fraction (from 0.2 vol.% to 1 vol.%) of rCF on the mechanical properties and impact resistance of high-strength concrete mixtures.Experiments revealed that increasing the dosage and aspect ratio of rCFs boosted the flexural and impact strengths of the materials.The results also showed a high level of agreement with the American Concrete Institute (ACI) technical code, enabling the possibility of applications in structural engineering and construction.Patchen et al. [9] studied the addition of short rCFs in ultra-high-performance concrete (UHPC) mixtures, comparing their effect with those of virgin reinforcing fibers in terms of microstructure and mechanical behavior.The authors demonstrated that recycled fibers increased the tensile and compressive strength of UHPC, and their improving effect was comparable to steel fibers and commercially available aerospace-grade CF.Interestingly, rCFs displayed better interfacial bonding with the cement matrix due to the rough surface morphology induced by the recovery processing, resulting in reduced pull-out phenomena.Wang et al. [10] explored the surface modification of rCFs with different chemical treatments (acid, alkaline, and acid-base neutralization) to assess the impact on the mechanical and conductivity properties of cement pastes.With respect to the mixtures incorporating untreated fibers, the surface modification increased the wettability and surface roughness of the rCFs, bringing some improvements in the material's performance, including an increase in workability (up to 20%), increment in flexural strength (up to 18%), and improvement in electrical conductivity property (up to 40%).Indeed, the treatments remove the residual resin on the fiber surface, increase the roughness, and introduce functional groups to turn rCFs from hydrophobic to hydrophilic.
As discussed, there are several research efforts on the use of rCFs in ordinary cementitious matrices, while the reinforcing effect of these reclaimed fibers in the AAM system is still missing.To the best of the authors' knowledge, the only contribution comes from Li et al. [11], who investigated the addition of pyrolyzed rCFs in fly ash (FA)-ground granulated blast-furnace slag (GGBS)-based alkali-activated composites.The authors also implemented an electrochemical oxidation treatment on fibers to improve the compatibility with the matrix.The results revealed that the incorporation of untreated and treated rCFs (1 wt.%) reduced the early-age strength of the composites due to reduced workability and a hindered reaction process.After 28 days of curing, the rCFs improved the flexural strength (+8% with respect to the unreinforced sample).By applying surface oxidation treatment to the fibers, flexural properties were further enhanced due to boosted interfacial adhesion, but this was at the expense of a worsening in compression behavior.
From the survey of the state-of-the-art, two issues requiring further understanding and investigation emerge.Firstly, there is a need to expand knowledge on the functionalization of alkali-activated mortars and concretes using rCFs in the direction of fiber-reinforced composites with augmented performance and eco-friendliness.Secondly, the compatibilization of recycled fibers to enhance the interaction with alkali-activated matrices requires special attention.Regarding the latter aspect, recycled fibers present a fluffy morphology, form bundles, and tend to remain as agglomerates in the binder due to their hydrophobic property and low surface energy.These facts affect their reinforcing ability.Then, treatment after the recycling process of fibers is desired to assist their deagglomeration and good dispersion inside the matrix with the aim of ensuring adequate rheological and mechanical properties [12].In a previous work [13], the authors developed a surface activation treatment on waste carbon fibers (WCFs) based on nanoclay slurry for integration into cementitious mortars.The fibers stabilized with the nanoceramic coating significantly improved the mechanical performance of the mortars, reporting an increment in flexural strength of more than 75% compared to the plain mixture (no fibers) and exceeding 100% compared to the fiber-reinforced mortar doped with untreated carbon fibers.Furthermore, the proposed treatment did not involve harsh conditions like high temperatures or the use of harmful solvents, resulting in a green method without impairing the economic and ecological benefits of the recycling process.
In the present study, this type of WCF was used for the first time in the production of fiber-reinforced AAM mortars.Considering the successful results achieved with the cementitious systems [13], the simple and non-hazardous surface activation method based on nanoclay was also implemented for alkali-activated matrices to enable full utilization of the WCFs' strength.This work can provide valuable insights into the possibility of using waste fibers in more sustainable cement-free construction materials.The research moves toward achieving sustainable development goals (SDGs) within the construction material industry through the implementation of low-carbon cementitious materials as well as by valorizing clean recycling solutions for composite material wastage.

WCFs
The WCFs involved in this study were provided by the Italian company Carbon Task Srl (Biella, Italy).This fibrous fraction does not come directly from the pyrolysis of post-consumer CFRP parts as in most studies in the literature.WCFs are processing wastes driven by the conversion of scrap CFs (from fabric production) into carbon woven/nonwoven fabrics.This fibrous waste appeared as fluffy carbon agglomerates composed of intertwined fibers of different lengths (Figure 1).

Surface Activation on WCFs
Surface activation on WCFs involved the preparation of a ceramic slur ing the fiber agglomerates in a nanoclay-based aqueous solution.The attapu (ANC) used in this work (Figure 2) was purchased from Lawrence Industr worth, UK).The experimental characterization of ANC conducted in prev [13,14] revealed a bulk density of 7690 kg/m 3 , hydrodynamic diameters fro 3.38 µm, and a maximum residue level of 45%.The treatment is comprehensively described in ref. [13] and essentiall mixing WCFs and ANC (at the same weight ratio) in water (Figure 3).The fi dosage used for the slurry was designed to produce the AAM mixtures.Firs amount of WCFs and water were mixed for 1 min at 500 rpm by means o

Surface Activation on WCFs
Surface activation on WCFs involved the preparation of a ceramic slurry by dispersing the fiber agglomerates in a nanoclay-based aqueous solution.The attapulgite nanoclay (ANC) used in this work (Figure 2) was purchased from Lawrence Industries Ltd. (Tamworth, UK).The experimental characterization of ANC conducted in previous research [13,14] revealed a bulk density of 7690 kg/m 3 , hydrodynamic diameters from 0.75 µm to 3.38 µm, and a maximum residue level of 45%.The characteristics of WCFs, experimentally determined in Refs.[13,14 rized in Table 1.Surface activation on WCFs involved the preparation of a ceramic slu ing the fiber agglomerates in a nanoclay-based aqueous solution.The attapu (ANC) used in this work (Figure 2) was purchased from Lawrence Indust worth, UK).The experimental characterization of ANC conducted in pre [13,14] revealed a bulk density of 7690 kg/m 3 , hydrodynamic diameters fr 3.38 µm, and a maximum residue level of 45%.The treatment is comprehensively described in ref. [13] and essential mixing WCFs and ANC (at the same weight ratio) in water (Figure 3).The fi dosage used for the slurry was designed to produce the AAM mixtures.Firs amount of WCFs and water were mixed for 1 min at 500 rpm by means o stirrer (Ika-Werke GmbH, Staufen, Germany).Then, ANC was added, and rpm was continued for an additional 30 min.The slurry containing the trea used as the liquid component in the preparation of the "one-part" AAM sa The treatment is comprehensively described in ref. [13] and essentially consisted of mixing WCFs and ANC (at the same weight ratio) in water (Figure 3).The fiber and water dosage used for the slurry was designed to produce the AAM mixtures.First, the required amount of WCFs and water were mixed for 1 min at 500 rpm by means of an overhead stirrer (Ika-Werke GmbH, Staufen, Germany).Then, ANC was added, and stirring at 500 rpm was continued for an additional 30 min.The slurry containing the treated fibers was used as the liquid component in the preparation of the "one-part" AAM samples.Class F-FA, purchased from Cemex UK (Cemex, Coventry, UK), and GGBS, obtained from Hanson UK (Heidelberg Cement Group, Maidenhead, UK), were used as precursor to produce the binary "one-part" alkali-activated mortars.Sodium metasilicate (Na2SiO3 in powder form obtained from Fisher Scientific UK (Fisher Scientific, Maidenhead, UK with a purity of 97.5% and alkalinity modulus (SiO2/Na2O) of 1.6 was used as the alkal activator.Three types of natural aggregates were employed, including fine river sand (0-0.5 mm), coarse river sand (0.5-1 mm), and quartz sand (0.06-0.3 mm).A detailed charac terization of these raw materials has been reported in an author's previous work [15].A total of 7 different formulations of alkali-activated mortars were prepared and investi gated (Table 2).The control mixture (WCF0), without fibers, was used as a basic mix design to realize the fiber-reinforced AAM composites.The mix proportion of the WCF0 sample consisted of a tailored formulation developed by the authors in past research [15] for in tegrating waste materials and 3D printing processing.Thus, two sets of fiber-added AAM formulations were produced, considering three additions in weight of WCF (0.5 wt.%, 0.75 wt.%, and 1 wt.%) with respect to the total mass of the precursors (FA+GGBS).The firs set, consisting of WCF0.5, WCF0.75, and WCF1 mixes, involved adding untreated WCF by simply dispersing the fibers in the required water for 5 min at 500 rpm.The second set including WCF0.5-ANC, WCF0.75-ANC, and WCF1-ANC mixes, involved the addition o fibers activated with nanoclay-based treatment according to the procedure mentioned in Section 2.1.2.Class F-FA, purchased from Cemex UK (Cemex, Coventry, UK), and GGBS, obtained from Hanson UK (Heidelberg Cement Group, Maidenhead, UK), were used as precursors to produce the binary "one-part" alkali-activated mortars.Sodium metasilicate (Na 2 SiO 3 ) in powder form obtained from Fisher Scientific UK (Fisher Scientific, Maidenhead, UK) with a purity of 97.5% and alkalinity modulus (SiO 2 /Na 2 O) of 1.6 was used as the alkali activator.Three types of natural aggregates were employed, including fine river sand (0-0.5 mm), coarse river sand (0.5-1 mm), and quartz sand (0.06-0.3 mm).A detailed characterization of these raw materials has been reported in an author's previous work [15].A total of 7 different formulations of alkali-activated mortars were prepared and investigated (Table 2).The control mixture (WCF0), without fibers, was used as a basic mix design to realize the fiber-reinforced AAM composites.The mix proportion of the WCF0 sample consisted of a tailored formulation developed by the authors in past research [15] for integrating waste materials and 3D printing processing.Thus, two sets of fiber-added AAM formulations were produced, considering three additions in weight of WCF (0.5 wt.%, 0.75 wt.%, and 1 wt.%) with respect to the total mass of the precursors (FA+GGBS).The first set, consisting of WCF0.5, WCF0.75, and WCF1 mixes, involved adding untreated WCF by simply dispersing the fibers in the required water for 5 min at 500 rpm.The second set, including WCF0.5-ANC, WCF0.75-ANC, and WCF1-ANC mixes, involved the addition of fibers activated with nanoclay-based treatment according to the procedure mentioned in Section 2.1.2.To produce the "one-part" alkali-activated mixtures, all the solid ingredients (FA, GGBS, aggregates, and alkali activator) were dry-mixed for 2 min using a Hobart mixer.Then, tap water (plain, containing crude WCF or containing the fibers treated with ANC) was gradually added to the mixture, and the mixing was continued for a further 10 min.The obtained mixtures were cast in prismatic polystyrene molds (40 × 40 × 160 mm 3 ), heat cured at 60 • C for 24 h, then demolded and kept in a room environment (20 ± 3 • C and 50% RH) until testing.

Methods
First, the surface morphology, wettability, and physiochemical characteristics of fibers before and after the nanoceramic surface treatment were characterized by scanning electron microscopy (SEM), X-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR), and water contact angle (WCA) measurements.Then, the treated and untreated WCFs were employed to fabricate "one-part" alkali-activated mortars, investigating the influence of different fiber dosages (0 wt.%, 0.25 wt.%, 0.5 wt.%, 0.75 wt.%, and 1 wt.%).Eventually, the mechanical performance of the AAM composites was experimentally studied regarding the flexural and compressive properties.

Characterization of WCFs after ANC-Based Conditioning
A complete characterization of carbon fibers along the whole process of their conditioning is a prerequisite to understanding the effectiveness of the proposed treatment on the dispersion and, finally, the performance of the produced alkali-activated composites.The effects of ANC-based treatment on the physical and microstructural characteristics of WCF were investigated following different test methods.Samples of carbon fibers treated with nanoclay were obtained by taking a portion of WCF-ANC slurry and oven-drying it on a watch glass at 100 • C for 24 h.From the dried material, selected specimens were extracted and subjected to the experimental analysis below (Figure 4).
To produce the "one-part" alkali-activated mixtures, all the solid ingredients GGBS, aggregates, and alkali activator) were dry-mixed for 2 min using a Hobart m Then, tap water (plain, containing crude WCF or containing the fibers treated with A was gradually added to the mixture, and the mixing was continued for a further 10 The obtained mixtures were cast in prismatic polystyrene molds (40 × 40 × 160 mm 3 ), cured at 60 °C for 24 h, then demolded and kept in a room environment (20 ± 3 °C 50% RH) until testing.

Methods
First, the surface morphology, wettability, and physiochemical characteristics bers before and after the nanoceramic surface treatment were characterized by scan electron microscopy (SEM), X-ray diffractometry (XRD), Fourier transform infrared troscopy (FTIR), and water contact angle (WCA) measurements.Then, the treated untreated WCFs were employed to fabricate "one-part" alkali-activated mortars, inv gating the influence of different fiber dosages (0 wt.%, 0.25 wt.%, 0.5 wt.%, 0.75 wt.% 1 wt.%).Eventually, the mechanical performance of the AAM composites was experi tally studied regarding the flexural and compressive properties.

Characterization of WCFs after ANC-Based Conditioning
A complete characterization of carbon fibers along the whole process of their co tioning is a prerequisite to understanding the effectiveness of the proposed treatme the dispersion and, finally, the performance of the produced alkali-activated compo The effects of ANC-based treatment on the physical and microstructural characterist WCF were investigated following different test methods.Samples of carbon fibers tre with nanoclay were obtained by taking a portion of WCF-ANC slurry and oven-dry on a watch glass at 100 °C for 24 h.From the dried material, selected specimens extracted and subjected to the experimental analysis below (Figure 4).The structural characteristics of as-received WCFs, ANC powder alone, and A treated fibers were studied by XRD using a Philips X'Pert diffractometer (PANalytica Almelo, The Netherlands), operating at 40 KV and 40 mA with CuKα1 radiation, w scan range of 10-90° (2θ), feed step of 0.02°, and acquisition time of 2 s.
FTIR spectrometry was implemented to probe the chemical change on the WCF face induced by the ANC-based conditioning.For this purpose, a PerkinElmer Spec 3 FT-IR spectrometer (PerkinElmer, Waltham, MA, USA) was used.For each samp scans with a resolution of 4 cm −1 are taken for spectrum integration in the wavenu range of 4000 to 400 cm −1 .
WCA measurements were performed to compare the wetting behavior of WC fore and after the treatment with ANC.Contact angles on nude and treated fibers measured at room temperature using an OCA 15 Pro optical analyzer (DataPhysic struments, Filderstadt, Germany).The static sessile method was used with ultrapure ter as the testing liquid (droplet volume 3 µL) [16].WCA values and the droplet sprea at the fiber surface were recorded and analyzed using the SCA 20 image analysis soft The structural characteristics of as-received WCFs, ANC powder alone, and ANCtreated fibers were studied by XRD using a Philips X'Pert diffractometer (PANalytical BV, Almelo, The Netherlands), operating at 40 KV and 40 mA with CuKα1 radiation, with a scan range of 10-90 • (2θ), feed step of 0.02 • , and acquisition time of 2 s.
FTIR spectrometry was implemented to probe the chemical change on the WCF surface induced by the ANC-based conditioning.For this purpose, a PerkinElmer Spectrum 3 FT-IR spectrometer (PerkinElmer, Waltham, MA, USA) was used.For each sample, 4 scans with a resolution of 4 cm −1 are taken for spectrum integration in the wavenumber range of 4000 to 400 cm −1 .
WCA measurements were performed to compare the wetting behavior of WCF before and after the treatment with ANC.Contact angles on nude and treated fibers were measured at room temperature using an OCA 15 Pro optical analyzer (DataPhysics Instruments, Filderstadt, Germany).The static sessile method was used with ultrapure water as the testing liquid (droplet volume 3 µL) [16].WCA values and the droplet spreading at the fiber surface were recorded and analyzed using the SCA 20 image analysis software (DataPhysics Instruments, Filderstadt, Germany) provided with the instrument.The fiber's microstructure was investigated by SEM analysis.Secondary electron (SE) micrographs were acquired using a Tescan MIRA 3 FEG-SEM (Tescan, Brno, Czech Republic) at an operating voltage of 15 kV.Energy-dispersive X-ray spectroscopy (EDS) analysis was also conducted on these samples using an Edax Octane Elect EDS system detector (Edax, Mahwah, NJ, USA).

Test Methods for Fiber-Reinforced AAM Composites
After the curing time of 7 days, the flexural and compression strength of each AAM formulation were evaluated following the testing standard BS EN 196-1:2016 [17].An Instron 5960 Series Universal Testing System (Instron, Pianezza, Italy) was utilized for conducting these tests.For the flexural test, the specimens of size 160 × 40 × 40 mm, three for each formulation, were subjected to a three-point configuration with a span length of 100 mm.The average values of flexural strength were computed based on the results obtained from these three specimens.After the flexural test, the remaining parts of the tested specimens were subjected to compression tests.The values of compression strength reported are the averages obtained from the results of these four specimens.A loading rate of 1 mm/min was selected for both mechanical tests.
Fractography analysis of the alkali-activated mortars was conducted using SEM (Supra 35VP, Carl Zeiss, Oberkochen, Germany).The inspection was performed on fractured pieces collected for mortar prisms after mechanical testing.Prior to the analysis, the samples were gold coated using an Edwards S150B (Edwards Ltd., Burgess Hill, UK) sputter coater to prevent surface charging effects.SE images of the surface were acquired at an accelerating voltage of 7 kV to ensure meaningful observation.

Influence of Nanoceramic-Plating on Crystallite Structure of WCFs
The changes in the crystallite structure of WCF following the conditioning with ANC were examined using XRD.The X-ray diffractogram of as-received fibers (Figure 5a) displays two main peaks at around 25 • and 45 • , which are attributed to (002) and (100) reflections of the stacking of the graphitic planes, respectively [18].The mineral composition of ANC (Figure 5b) comprises attapulgite, quartz, and montmorillonite.These peaks appear at the same angular position as those detected by other researchers [19].Figure 5c confirms the presence of nanoclay on the WCF surface.Indeed, the crystalline peaks of the nanoclay associated with quartz and attapulgite overlap the broad graphitic band of carbon fibers (~25 • ).Furthermore, the patterns reveal all the peaks found in ANC, demonstrating that an effective nanoceramic deposition on the fiber surface occurred.However, the evidence that the carbon-related peaks remain after the nanoclay-based treatment suggests a predominantly physical interaction between the fiber and the ceramic coating which will also be confirmed by the FT-IR analysis below.

Influence of Nanoceramic-Plating on Surface Chemistry of WCFs
The FTIR analysis (Figure 6) again proves the ANC successfully coated the surface of WCF.The ANC spectrum (orange line) shows four main absorption regions.The band around 3500-3700 cm −1 can be assigned to the stretching of O-H coordinated with metal species (Al, Mg) within the clay structure.The absorption at ~1650 cm −1 is correlated with the O-H bending vibration peak of the adsorbed water.The band around 1200 cm −1 is ascribed to the Si-O stretching vibration.The absorption region below 500 cm −1 results from combined vibrations of Mg-O stretching and O-Si-O and Al-O-Si bending [13,20].The FTIR spectrum of WCF after conditioning with ANC (black line) highlights the same peak distribution, and no shift of the absorption bands compared to nanoclay alone is detected.Then, ANC-based coating has adequately covered the fiber surface after the treatment.The absence of shifts in the FTIR spectrum confirms that the bond between fiber and nanoclay is based on a physical interaction based on Van der Waals interactive forces and other dispersive interactions.Furthermore, the surface roughness of the fibers would promote the mechanical interlocking of the nanoceramic coating on the WCFs [13].
Ceramics 2024, 7, FOR PEER REVIEW The FTIR spectrum of WCF after conditioning with ANC (black line) highlights th peak distribution, and no shift of the absorption bands compared to nanoclay a detected.Then, ANC-based coating has adequately covered the fiber surface a treatment.The absence of shifts in the FTIR spectrum confirms that the bond betwe and nanoclay is based on a physical interaction based on Van der Waals interactiv and other dispersive interactions.Furthermore, the surface roughness of the fibers promote the mechanical interlocking of the nanoceramic coating on the WCFs [13

Influence of Nanoceramic-Plating on Surface Hydrophilicity of WCFs
The effectiveness of fibers for enhancing the structural performance of cemen materials or AAM is strongly affected by the degree of fiber dispersion.The poor sion of fibers into the cement paste results in a weak strengthening action.Deaggl tion and dispersion of the fibers can be attained by improving their hydrophilicity cement or AAM pastes are water-based.The hydrophilic characteristics of fiber modified by specific surface treatment before incorporation into the mixture [21].I tion, increasing the fiber hydrophilicity, which means a low WCA value (<90°), he establishment of a strong interface cohesion with the matrix resulting in a beneficia ence of the reinforcing agent in terms of mechanical properties and durability [ blíková et al. [23] implemented a plasma treatment at different argon atmosphere prove the wettability of CF with the AAM matrix.The results showed that the angle reduced from >90° (untreated fibers) to 35° after the plasma treatment and a quent positive effect in terms of CF/geopolymer interfacial strength measured by a laminar shear strength (ILSS) test.Zhang et al. [24] addressed the challenge related agglomeration and poor dispersion of carbon nanofibers in the AAM matrix by usi ymer surfactant agents to chemically modify the fiber surface, reducing the surfa sion of the dispersion, and preventing aggregation phenomena.Dispersed CF im the strength of the resulting AAM composite and refined the material's pore str

Influence of Nanoceramic-Plating on Surface Hydrophilicity of WCFs
The effectiveness of fibers for enhancing the structural performance of cement-based materials or AAM is strongly affected by the degree of fiber dispersion.The poor dispersion of fibers into the cement paste results in a weak strengthening action.Deagglomeration and dispersion of the fibers can be attained by improving their hydrophilicity, as the cement or AAM pastes are water-based.The hydrophilic characteristics of fiber can be modified by specific surface treatment before incorporation into the mixture [21].In addition, increasing the fiber hydrophilicity, which means a low WCA value (<90 • ), helps the establishment of a strong interface cohesion with the matrix resulting in a beneficial influence of the reinforcing agent in terms of mechanical properties and durability [22].Diblíková et al. [23] implemented a plasma treatment at different argon atmospheres to improve the wettability of CF with the AAM matrix.The results showed that the contact angle reduced from >90 • (untreated fibers) to 35 • after the plasma treatment and a subsequent positive effect in terms of CF/geopolymer interfacial strength measured by an interlaminar shear strength (ILSS) test.Zhang et al. [24] addressed the challenge related to the agglomeration and poor dispersion of carbon nanofibers in the AAM matrix by using polymer surfactant agents to chemically modify the fiber surface, reducing the surface tension of the dispersion, and preventing aggregation phenomena.Dispersed CF improved the strength of the resulting AAM composite and refined the material's pore structure, reducing the porosity and pore size.
The hydrophilicity of ANC combined with its cost-effectiveness and environmental compliance were exploited to favorably modify the surface tension of the CFs and facilitate their deagglomeration and dispersion in the AAM matrix.The clay nanoparticles' adhesion onto WCFs led to a significant increase in the water wettability.As expected, the bare WCF showed marked hydrophobicity (Figure 7a), accounting for a WCA value of 138 • (average value of 10 measurements).The effectiveness of the surface activation of the fibers with nanoclay is illustrated in Figure 7b.Prior to the complete absorption of the water drop (at 30 ms), a contact angle of about 30 • C was measured.Then, the water drop was instantly absorbed by the treated fiber bundle after deposition (50 ms), resulting in a complete hydrophilization of the surface that enhances the water affinity and the fiber declustering.A similar method was studied by Lindstrom et al. [25], who investigated the effect of nanoclay surface plating on cellulosic fibers to avoid floc formation and interfiber bonding and give better compatibility with the surrounding matrix.
Ceramics 2024, 7, FOR PEER REVIEW 10 fibers with nanoclay is illustrated in Figure 7b.Prior to the complete absorption of the water drop (at 30 ms), a contact angle of about 30 °C was measured.Then, the water drop was instantly absorbed by the treated fiber bundle after deposition (50 ms), resulting in a complete hydrophilization of the surface that enhances the water affinity and the fiber declustering.A similar method was studied by Lindstrom et al. [25], who investigated the effect of nanoclay surface plating on cellulosic fibers to avoid floc formation and interfiber bonding and give better compatibility with the surrounding matrix.The morphology of the ANC deposit was examined with the aid of the SEM technique and such observations were performed directly on the fiber surface after the nanoclay-based conditioning and drying of WCF bundles.From Figure 8, the first noticeable feature is the uniform nanoceramic coating along the entire length of the fibers, showing the typical needle-like morphology of ANC [26].The fibers also exhibit a large number of longitudinal grooves indicative of partial oxidation on the fiber surface resulting from the pyrolysis treatment.It is presumable that the roughest texture of WCF facilitates the physical grafting of the nanoclay particles on the fiber surface [27].Furthermore, as previously mentioned, such efficient adhesion is also based on van der Waals and other dispersion interactions between nanoclay particles and the WCFs' surface.

Influence of Nanoceramic-Plating on Microstructure of WCF
The morphology of the ANC deposit was examined with the aid of the SEM technique and such observations were performed directly on the fiber surface after the nanoclay-based conditioning and drying of WCF bundles.From Figure 8, the first noticeable feature is the uniform nanoceramic coating along the entire length of the fibers, showing the typical needle-like morphology of ANC [26].The fibers also exhibit a large number of longitudinal grooves indicative of partial oxidation on the fiber surface resulting from the pyrolysis treatment.It is presumable that the roughest texture of WCF facilitates the physical grafting of the nanoclay particles on the fiber surface [27].Furthermore, as previously mentioned, such efficient adhesion is also based on van der Waals and other dispersion interactions between nanoclay particles and the WCFs' surface.).The analysis als highlights the absence of Calcium (Ca), one of the elements present in nanoclay [13].Thi occurs because after deposition the carbon (C) signal deriving from the fiber predomi nated and overlaid that of Ca (the emission peaks are energetically very close) and there fore the Ca-signal is no longer discriminable in the spectrum. ).The analysis also highlights the absence of Calcium (Ca), one of the elements present in nanoclay [13].This occurs because after deposition the carbon (C) signal deriving from the fiber predominated and overlaid that of Ca (the emission peaks are energetically very close) and therefore the Ca-signal is no longer discriminable in the spectrum.

Flexural and Compression Mechanical Testing
Figure 10 displays the flexural test results of alkali-activated mortars reinforc WCF.The addition of untreated WCF (red plot) induces a worsening effect on the strength which progressively reduces as the fiber content increases.Compared to trol AAM (WCF0 sample), a decrease from 14% (WCF0.25 sample) up to 22% (WC ple) has been detected.The primary reason for this detrimental effect can be asc the lack of adequate deagglomeration of the WCF clusters and, consequently, p persion of the reinforcing fibers in the matrix.Indeed, for achieving an improved bution in terms of strength performance, a homogeneous distribution of the fibe be promoted to form a structural support for the material and enable typical streng mechanisms of fiber-reinforced cementitious composites, including crack bridg crack arresting [28].In addition, when the WCF content is large, the number of agglomerates in the AAM matrix increases, acting as weak zones for cracking.ANC conditioning of fibers resulted in marked improvement in the flexural perform AAM composites (blue plot) compared to the respective counterparts loaded w treated WCF.With respect to the AAM formulations incorporating untreated fi nanoclay treatment led to a strength increment of 19% and 11% in WCF0.25-AWCF0.5-ANC samples, respectively.For fiber dosages above 0.5 wt.%, the increas was + 9% for both formulations (WCF0.75-ANCand WCF1-ANC samples).It was served that by the addition of 0.25 wt.% of nanoclay-activated WCF, the flexural s was slightly enhanced compared to plain AAM mortar (WCF0).However, the s decreased with further fiber additions, up to 15%, which is recorded for the WC mix.The achieved results suggest that the proposed treatment of fibers with n benefits the fibers' dispersion and strength performance of the composite up to a limit (in this case 0.25 wt.%).When the WCF content is higher, the effect of ANC tr seems to be ineffective due to the fasciculation mechanisms of the fibers [29,30] presence of a growing concentration of residual fibrous clusters that do not unde agglomeration following the conditioning.

Flexural and Compression Mechanical Testing
Figure 10 displays the flexural test results of alkali-activated mortars reinforced with WCF.The addition of untreated WCF (red plot) induces a worsening effect on the flexural strength which progressively reduces as the fiber content increases.Compared to the control AAM (WCF0 sample), a decrease from 14% (WCF0.25 sample) up to 22% (WCF1 sample) has been detected.The primary reason for this detrimental effect can be ascribed to the lack of adequate deagglomeration of the WCF clusters and, consequently, poor dispersion of the reinforcing fibers in the matrix.Indeed, for achieving an improved contribution in terms of strength performance, a homogeneous distribution of the fibers must be promoted to form a structural support for the material and enable typical strengthening mechanisms of fiber-reinforced cementitious composites, including crack bridging and crack arresting [28].In addition, when the WCF content is large, the number of fibrous agglomerates in the AAM matrix increases, acting as weak zones for cracking.ANC-based conditioning of fibers resulted in marked improvement in the flexural performance of AAM composites (blue plot) compared to the respective counterparts loaded with untreated WCF.With respect to the AAM formulations incorporating untreated fiber, the nanoclay treatment led to a strength increment of 19% and 11% in WCF0.25-ANC and WCF0.5-ANC samples, respectively.For fiber dosages above 0.5 wt.%, the increasing rate was + 9% for both formulations (WCF0.75-ANCand WCF1-ANC samples).It was also observed that by the addition of 0.25 wt.% of nanoclay-activated WCF, the flexural strength was slightly enhanced compared to plain AAM mortar (WCF0).However, the strength decreased with further fiber additions, up to 15%, which is recorded for the WCF1-ANC mix.The achieved results suggest that the proposed treatment of fibers with nanoclay benefits the fibers' dispersion and strength performance of the composite up to a specific limit (in this case 0.25 wt.%).When the WCF content is higher, the effect of ANC treatment seems to be ineffective due to the fasciculation mechanisms of the fibers [29,30] and the presence of a growing concentration of residual fibrous clusters that do not undergo deagglomeration following the conditioning.Compression strength test results are illustrated in Figure 11.The treatment o with ANC establishes an improvement in mechanical strength compared to the a tivated mortars loaded with untreated WCF for concentrations within 0.5 wt.%.H the effect of nanoclay is confirmed to be progressively more ineffective for high dosages.As verified for flexural behavior, if the fiber fraction is too high, the defec of the material (fibers agglomeration and clusters) inhibits the dispersing effec nanoclay, hindering the improvement of the strength.Regardless of the treatme ANC, the addition of WCF reduces the compressive strength compared to the simp ple (WCF0).Carbon fibers are high-modulus fibers; therefore, the load-bearing s cannot form in the matrix when fiber dispersion is not optimal.In this case, the e ment effect on compressive behavior is smaller than the negative effects of the caused by the WCF agglomerates [31].Compression strength test results are illustrated in Figure 11.The treatment of fibers with ANC establishes an improvement in mechanical strength compared to the alkaliactivated mortars loaded with untreated WCF for concentrations within 0.5 wt.%.However, the effect of nanoclay is confirmed to be progressively more ineffective for higher fiber dosages.As verified for flexural behavior, if the fiber fraction is too high, the defectiveness of the material (fibers agglomeration and clusters) inhibits the dispersing effect of the nanoclay, hindering the improvement of the strength.Regardless of the treatment with ANC, the addition of WCF reduces the compressive strength compared to the simple sample (WCF0).Carbon fibers are high-modulus fibers; therefore, the load-bearing skeleton cannot form in the matrix when fiber dispersion is not optimal.In this case, the enhancement effect on compressive behavior is smaller than the negative effects of the defects caused by the WCF agglomerates [31].
As previously mentioned, the authors studied the addition of the same waste fraction of carbon microfibers in an ordinary cement matrix [13].The influence of WCF on the mechanical performance of cement-based mortar was completely opposite to the behavior found in the AAM matrix detected in this research.The normalized flexural strength ratio [32], reported in Figure 12, is calculated to elucidate the effect of ANC-treated WCF on the strength performance of AAM and cementitious matrices.For each fiber-added mortar formulation (both cement matrix and AAM), the flexural strength value was divided by the strength of the "control" mortar without WCFs (normalized flexural strength ratio = 1).From the plot below, it appears evident that the WCFs induce a marked improvement in the mechanical characteristics of the cement mortar, and this is also confirmed for high fiber dosage.This would suggest that the dispersion of WCF in the cement paste occurs in a more favorable way than that found in the alkali-activated matrix.Consequently, the action of the ANC is also more efficient in ensuring the correct distribution of the reinforcement in the matrix.One possible explanation for this evidence can be the different rheological properties between the AAM and cement pastes.Criado et al. [33] analyzed and compared the rheology of alkali-activated and Portland cement systems.They observed that the plastic viscosity of AAM is much greater than the cement paste, mainly due to the morphological differences in the particles of the starting materials (angular-shaped cement particles vs. spherical-shaped FA particles) and the different reaction mechanisms leading to the creation of different hydration products (C-S-H gel short chains in cement system vs. cross-linked aluminosilicate gel in AAM system).Therefore, the higher viscosity of the alkali-activated mixtures hinders the effect of the nanoclay on the declustering and dispersion of the fibers in the matrix.Rheological measurements of the investigated systems can be planned in future research to optimize the fresh-state AAM mix design and achieve adequate rheological properties to ensure superior dispersion of the fibers, boosting their reinforcing effect.Compression strength test results are illustrated in Figure 11.The treatment of fibers with ANC establishes an improvement in mechanical strength compared to the alkali-activated mortars loaded with untreated WCF for concentrations within 0.5 wt.%.However, the effect of nanoclay is confirmed to be progressively more ineffective for higher fiber dosages.As verified for flexural behavior, if the fiber fraction is too high, the defectiveness of the material (fibers agglomeration and clusters) inhibits the dispersing effect of the nanoclay, hindering the improvement of the strength.Regardless of the treatment with ANC, the addition of WCF reduces the compressive strength compared to the simple sample (WCF0).Carbon fibers are high-modulus fibers; therefore, the load-bearing skeleton cannot form in the matrix when fiber dispersion is not optimal.In this case, the enhancement effect on compressive behavior is smaller than the negative effects of the defects caused by the WCF agglomerates [31].Ceramics 2024, 7, FOR PEER REVIEW 14 As previously mentioned, the authors studied the addition of the same waste fraction of carbon microfibers in an ordinary cement matrix [13].The influence of WCF on the mechanical performance of cement-based mortar was completely opposite to the behavior found in the AAM matrix detected in this research.The normalized flexural strength ratio [32], reported in Figure 12, is calculated to elucidate the effect of ANC-treated WCF on the strength performance of AAM and cementitious matrices.For each fiber-added mortar formulation (both cement matrix and AAM), the flexural strength value was divided by the strength of the "control" mortar without WCFs (normalized flexural strength ratio = 1).From the plot below, it appears evident that the WCFs induce a marked improvement in the mechanical characteristics of the cement mortar, and this is also confirmed for high fiber dosage.This would suggest that the dispersion of WCF in the cement paste occurs in a more favorable way than that found in the alkali-activated matrix.Consequently, the action of the ANC is also more efficient in ensuring the correct distribution of the reinforcement in the matrix.One possible explanation for this evidence can be the different rheological properties between the AAM and cement pastes.Criado et al. [33] analyzed and compared the rheology of alkali-activated and Portland cement systems.They observed that the plastic viscosity of AAM is much greater than the cement paste, mainly due to the morphological differences in the particles of the starting materials (angularshaped cement particles vs. spherical-shaped FA particles) and the different reaction mechanisms leading to the creation of different hydration products (C-S-H gel short chains in cement system vs. cross-linked aluminosilicate gel in AAM system).Therefore, the higher viscosity of the alkali-activated mixtures hinders the effect of the nanoclay on the declustering and dispersion of the fibers in the matrix.Rheological measurements of the investigated systems can be planned in future research to optimize the fresh-state AAM mix design and achieve adequate rheological properties to ensure superior dispersion of the fibers, boosting their reinforcing effect.

SEM Fractography Analysis
SEM micrographs in Figure 13 display the microstructure of alkali-activated mortars incorporating untreated WCF.The lack of adequate dispersibility of fibers brings in the presence of fibrous clusters inside the matrix (Figure 13a).These WCF agglomerates compromise the compactness of the material, causing the formation of voids inside the matrix.Then, under loading, these weak zones tend to induce stress concentrations in the mortar,

SEM Fractography Analysis
SEM micrographs in Figure 13 display the microstructure of alkali-activated mortars incorporating untreated WCF.The lack of adequate dispersibility of fibers brings in the presence of fibrous clusters inside the matrix (Figure 13a).These WCF agglomerates compromise the compactness of the material, causing the formation of voids inside the matrix.Then, under loading, these weak zones tend to induce stress concentrations in the mortar, where premature failure is prone to occur.The effect derived herein agrees with those verified in Ref. [34].The SEM image in Figure 13b probes the inner microstructure of the fibrous mass.It is noted that the WCF agglomerates trap the aluminosilicate precursors (FA particles) within them (see dotted circle), hindering the potential dissolution with the alkali activator and therefore mitigating their contribution to the proper strength and microstructural development of the AAM matrix.This fact is a further reason to corroborate the significant strength reduction experienced by fiber-reinforced mortars with unconditioned WCF.
Ceramics 2024, 7, FOR PEER REVIEW 15 where premature failure is prone to occur.The effect derived herein agrees with those verified in Ref. [34].The SEM image in Figure 13b probes the inner microstructure of the fibrous mass.It is noted that the WCF agglomerates trap the aluminosilicate precursors (FA particles) within them (see dotted circle), hindering the potential dissolution with the alkali activator and therefore mitigating their contribution to the proper strength and microstructural development of the AAM matrix.This fact is a further reason to corroborate the significant strength reduction experienced by fiber-reinforced mortars with unconditioned WCF.Conditioning the WCF permits the investigation of the single-fiber interfacial property with the surrounding alkali-activated matrix thanks to the slightly enhanced dispersion by nanoclay-based treatment.The fractography images in Figure 14 highlight the details of fiber-matrix interaction.Both micrographs display fibers well embedded in the Conditioning the WCF permits the investigation of the single-fiber interfacial property with the surrounding alkali-activated matrix thanks to the slightly enhanced dispersion by nanoclay-based treatment.The fractography images in Figure 14 highlight the details of fiber-matrix interaction.Both micrographs display fibers well embedded in the surrounding alkali-activated matrix, denoting that fiber breakage governs the failure of the fiber-reinforced mortar rather than the fiber pull-out.It is known that fiber breakage is the mechanism that occurs when an intimate bond is established between fiber and matrix and is uncommon in concrete materials due to the weak adhesion between fiber and matrix [35].This evidence would suggest that the nanoclay, in addition to improving the dispersibility of the fibrous clusters, makes the carbon fiber (typically inert towards ceramic-cementitious matrices) chemically more compatible with AAM.The effectiveness of ANC as a surface functionalizing agent was demonstrated by Chougan et al. [36], who increased the compatibility of wheat straw fillers in AAM-based composites, achieving remarkable improvement in strength performance.This effect slightly enhances the flexural behavior of the mortars for low fiber dosage.Once a certain threshold (0.25 wt.% of WCF) is exceeded, the re-agglomeration of the fibers and the presence of multiple residual WCF agglomerates not extricated from the ceramic pre-treatment prevail over the surface functionalization effect of ANC.The deterioration of the mechanical strength compared to the WCF0 sample is therefore noticeable.Gu et al. [37] observed that carbon fibers tend to agglomerate in FA-GBBS geopolymer composites when the amount exceeds 0.4 wt.%, inducing strength reduction.The authors found that over this threshold, the paste could not flow through the inside of the agglomerated carbon fibers, thus introducing air within the matrix, which forms porosity.
Ceramics 2024, 7, FOR PEER REVIEW 16 surrounding alkali-activated matrix, denoting that fiber breakage governs the failure of the fiber-reinforced mortar rather than the fiber pull-out.It is known that fiber breakage is the mechanism that occurs when an intimate bond is established between fiber and matrix and is uncommon in concrete materials due to the weak adhesion between fiber and matrix [35].This evidence would suggest that the nanoclay, in addition to improving the dispersibility of the fibrous clusters, makes the carbon fiber (typically inert towards ceramic-cementitious matrices) chemically more compatible with AAM.The effectiveness of ANC as a surface functionalizing agent was demonstrated by Chougan et al. [36], who increased the compatibility of wheat straw fillers in AAM-based composites, achieving remarkable improvement in strength performance.This effect slightly enhances the flexural behavior of the mortars for low fiber dosage.Once a certain threshold (0.25 wt.% of WCF) is exceeded, the re-agglomeration of the fibers and the presence of multiple residual WCF agglomerates not extricated from the ceramic pre-treatment prevail over the surface functionalization effect of ANC.The deterioration of the mechanical strength compared to the WCF0 sample is therefore noticeable.Gu et al. [37] observed that carbon fibers tend to agglomerate in FA-GBBS geopolymer composites when the amount exceeds 0.4 wt.%, inducing strength reduction.The authors found that over this threshold, the paste could not flow through the inside of the agglomerated carbon fibers, thus introducing air within the matrix, which forms porosity.

Conclusions
This study explored the influence of WCFs on the microstructure and mechanical behavior of "one-part" alkali-activated materials.The waste fibers were functionalized

Conclusions
This study explored the influence of WCFs on the microstructure and mechanical behavior of "one-part" alkali-activated materials.The waste fibers were functionalized with a nanoclay-based surface treatment to attempt improvements in terms of deagglomeration, dispersibility, and compatibility with the AAM matrix.The nanoceramic conditioning was implemented based on a previous work of authors on cement-based mortars to gain comprehensive knowledge about the possibility of using these waste fillers in construction applications.The following concluding remarks can be drawn:

•
Further targeted analysis conducted on post-conditioned fibers verified an adequate interaction of the nanoceramic coating with WCFs and a significant increase in hydrophilicity, thus promoting the deagglomeration of the fibrous clusters.• The mortars produced with ANC-treated WCF showed improvements in mechani- cal strength compared to those incorporating unconditioned fibers.The maximum increment in flexural strength (+19%) was found in WCF0.25-ANC.As the fiber dosage increased, the improving effect was gradually reduced due to the ineffectiveness of the nanoceramic treatment in compensating for fiber declustering.

•
Only the formulation with the lowest fiber content (WCF0.25-ANC)proved a slight improvement in flexural performance compared to the plain mortar.This result corroborates the above conclusion regarding the difficulty of ensuring a stable integration of the reinforcement for high WCF concentrations.

•
From the microstructural analysis, it was clear that the presence of WCF agglomerates, in addition to acting as structural defects, limited the alkaline activation and dissolution of the aluminosilicate precursors, mitigating the proper strength development of the matrix.In this sense, fiber declustering is crucial.Fiber breakage appeared to be the main failure mechanism of the mortars incorporating nanoceramic-functionalized fibers, indicating good fiber-matrix cohesion.

Figure 2 .
Figure 2. Photograph of ANC used in this study.

Figure 1 .
Figure 1.Photograph of WCFs used in this study.

Figure 1 .
Figure 1.Photograph of WCFs used in this study.

Figure 2 .
Figure 2. Photograph of ANC used in this study.

Figure 2 .
Figure 2. Photograph of ANC used in this study.

Figure 4 .
Figure 4. Procedure for obtaining test samples of WCF treated with ANC: (a) placing WCFslurry on watch glass for drying, (b) oven-dried sample, and (c) sample extraction.

Figure 4 .
Figure 4. Procedure for obtaining test samples of WCF treated with ANC: (a) placing WCF-ANC slurry on watch glass for drying, (b) oven-dried sample, and (c) sample extraction.

Figure 6 .
Figure 6.FTIR analysis of ANC and WCF after treatment with ANC.

Figure 6 .
Figure 6.FTIR analysis of ANC and WCF after treatment with ANC.

Figure 7 .
Figure 7. WCA profile for (a) bare WCF and (b) WCF treated with ANC.

Figure 8 .
Figure 8. SEM micrographs of WCF coated with ANC.EDS element analysis (Figure 9) confirms the presence of ANC on the fiber surface.The spectrum comprises Silicon (Si), Magnesium (Mg), Aluminum (Al), and Oxygen (O) referring to the crystalline phases of nanoclay, i.e., quartz (SiO 2 ), montmorillonite ([OH] 4 Si 8 Al 4 O 20 •nH 2 O), and attapulgite ([Mg,Al] 2 Si 4 O 10 (OH)•4[H 2 O]).The analysis also highlights the absence of Calcium (Ca), one of the elements present in nanoclay[13].This occurs because after deposition the carbon (C) signal deriving from the fiber predominated and overlaid that of Ca (the emission peaks are energetically very close) and therefore the Ca-signal is no longer discriminable in the spectrum.

Figure 9 .
Figure 9. EDS element analysis of WCF coated with ANC.

Figure 9 .
Figure 9. EDS element analysis of WCF coated with ANC.

Figure 10 .
Figure 10.Effect of WCF addition and ANC treatment of fiber on flexural strength of alkali-a mortars.

Figure 10 .
Figure 10.Effect of WCF addition and ANC treatment of fiber on flexural strength of alkali-activated mortars.

Figure 10 .
Figure 10.Effect of WCF addition and ANC treatment of fiber on flexural strength of alkali-activated mortars.

Figure 11 .
Figure 11.Effect of WCF addition and ANC treatment of fiber on compression strength of alkali activated mortars.

Figure 11 .
Figure 11.Effect of WCF addition and ANC treatment of fiber on compression strength of alkali activated mortars.

Figure 12 .
Figure 12.Effect of ANC-treated WCF addition on the flexural behavior of AAM (present work) and cement-based [13] mortars.

Figure 12 .
Figure 12.Effect of ANC-treated WCF addition on the flexural behavior of AAM (present work) and cement-based [13] mortars.

Figure 13 .
Figure 13.SEM analysis of alkali-activated mortar with unconditioned WCF (WCF0.5 sample): (a) fibrous agglomerate inside the matrix and (b) detail of the inner microstructure of the WCF cluster.Dotted circle highlights a fly ash particle trapped between the fibers.

Figure 13 .
Figure 13.SEM analysis of alkali-activated mortar with unconditioned WCF (WCF0.5 sample): (a) fibrous agglomerate inside the matrix and (b) detail of the inner microstructure of the WCF cluster.Dotted circle highlights a fly ash particle trapped between the fibers.
eramics 2024, 7, FOR PEER REVIEW Figure 1.Photograph of WCFs used in this study.The characteristics of WCFs, experimentally determined in Refs.[13,14 rized in Table