Enhanced UV-Blocking Capabilities of Polylactic Acid Derived from Renewable Resources for Food and Drug Packaging: A Mini-Review

: Plastic materials have revolutionized modern life, particularly in the domain of food packaging, owing to their versatility, lightweight nature, and ease of processing. However, the environmental ramiﬁcations of non-degradable plastics have raised concerns. Polylactic acid (PLA), derived from renewable sources, represents a sustainable alternative due to its biodegradability and exceptional barrier, mechanical, and safety properties. Nevertheless, the high UV transmittance of PLA limits its use for photosensitive food and pharmaceutical packaging, where UV radiation can lead to nutritional loss and spoilage. Various methods have been explored to enhance the UV-blocking capabilities of PLA, including the integration of inorganic nanoparticles and surface coatings. Despite advancements, these approaches often compromise the inherent transparency of PLA. Incorporating large conjugated groups can maintain transparency but introduces additional challenges. This paper reviews modiﬁcation methods to enhance PLA’s UV-barrier properties and anticipates its expanded utility in food and drug packaging, promoting UV resistance and diversifying PLA’s applications.


Introduction
The remarkable growth in the utilization of plastic materials has revolutionized modern society, enhancing convenience and efficiency across various sectors, particularly in food packaging.The undeniable advantages of plastics, such as their flexibility, lightweight nature, and ease of production, have led to their ubiquitous presence in daily life.However, this widespread reliance on plastics comes at a significant cost, as the environmental repercussions of nondegradable plastics loom large.Plastic pollution, stemming from inadequate waste management, inefficient recycling practices, and the persistence of traditional plastics in the ecosystem, poses an urgent global concern.The production, usage, and disposal of plastics collectively contribute to a complex web of environmental issues, spanning land, water, and air.As plastic waste accumulates in landfills, litters landscapes, and contaminates oceans, the need for sustainable solutions has become more pressing than ever before [1].
Non-degradable plastics, primarily derived from petroleum-based resources, present a considerable challenge due to their resistance to natural degradation processes.These plastics persist in the environment for centuries, contributing to environmental degradation, endangering wildlife, and compromising delicate ecosystems.The cumulative impact of these plastics necessitates an urgent transition to more environmentally friendly alternatives.The concept of degradable plastics has emerged as a potential remedy for plastic pollution.By designing plastics that can break down into non-harmful components, the burden of long-lasting waste can be mitigated.Degradable plastics encompass various categories, including photodegradable, biodegradable, and light-biodegradable.These materials offer the promise of reducing the environmental footprint associated with plastics.Polylactic acid (PLA), an innovative and sustainable biodegradable plastic, stands as a beacon of hope amid the plastic pollution crisis.Derived from renewable resources, such as corn starch, PLA offers a compelling alternative to conventional plastics.PLA possesses exceptional properties that make it an attractive candidate for a wide range of applications.Its rapid degradation into water and carbon dioxide, without leaving harmful residues, aligns with the principles of environmental responsibility.Beyond its biodegradability, PLA boasts impressive barrier properties, mechanical strength, and compatibility with food safety standards [2].This combination of attributes positions PLA as a versatile material with the potential to transform various industries.As the negative externalities of traditional plastics become increasingly evident, PLA emerges as a valuable tool in the pursuit of sustainable development.
The domain of food packaging presents fertile ground for PLA's application and impact.With food safety and environmental concerns taking center stage, PLA emerges as an ideal material for modern food packaging solutions.Its biodegradability, biocompatibility, and potential to replace conventional plastic packaging materials make it an attractive choice.Beyond meeting functional requirements, PLA aligns with the growing preference for eco-friendly packaging options [3].It serves as a primary packaging material for various food products and beverages, offering the crucial advantage of minimizing ecological harm.The intersection of PLA's characteristics with the evolving demands of the food packaging industry underscores its potential to revolutionize this space [4].Ultraviolet (UV) radiation holds a pivotal role in food preservation and sterilization processes.However, this radiation can also be a double-edged sword, as it can trigger photooxidation reactions in photosensitive components of food and pharmaceuticals.The consequences of ultraviolet radiation-induced photolysis during food preservation and sterilization can have significant implications for both the nutritional value and quality of the food.Firstly, the susceptibility of certain nutrients to oxidation under ultraviolet radiation can result in substantial nutrient loss.In particular, easily oxidizable nutrients such as vitamin C and vitamin A can rapidly decompose when exposed to ultraviolet radiation, leading to a reduction in the overall nutritional content of the food.It is vital to recognize that prolonged exposure to UV radiation during food preservation processes can potentially compromise the food's nutritional value.Secondly, the impact of ultraviolet radiation on the quality of food should not be overlooked.The photooxidation reactions triggered by UV radiation can greatly affect various components in food, including pigments, proteins, and fats.This can result in changes in the food's taste, color, and texture.Browning, brittleness, and oxidation are common issues arising from UV radiation exposure, causing a noticeable deterioration in the overall quality of the food.Lastly, it is important to acknowledge the bactericidal properties of ultraviolet radiation.UV radiation is widely utilized for its ability to inactivate bacteria and microorganisms present in food.The radiation effectively disrupts the DNA structure of these microorganisms, rendering them unable to reproduce and survive.However, careful consideration must be given to the intensity and duration of UV radiation, as excessive exposure can potentially compromise food quality and nutritional integrity.In conclusion, ultraviolet radiation can have significant implications for food preservation and sterilization.The potential consequences include nutrient loss, compromised food quality, and bacterial inactivation.Striking the right balance between UV radiation exposure and its beneficial effects is crucial in order to maximize food safety and quality.The optical resistance of PLA has been studied.It is found that PLA has almost no ultraviolet transmission in the lower UV-C band (190~220 nm).However, at 225 nm, the amount of ultraviolet light transmitted by PLA increases significantly.At 250 nanometers, 85% of ultraviolet light is transmitted.At 300 nanometers, 95% of ultraviolet light is transmitted.Therefore, although UV-C is not transmitted, almost all UV-B and UV-A light passes through the film.Because of this, PLA faces challenges in the field of packaging [5].
The potential consequences of UV-induced degradation, including nutritional losses and reduced product quality, underscore the importance of addressing this limitation.To unlock PLA's full potential in photosensitive packaging, innovative approaches are required to enhance its UV-barrier properties without compromising its transparency.
The quest for enhancing the UV-barrier properties of PLA has spurred the development of innovative methods.One avenue involves the incorporation of UV-blocking additives during the manufacturing process, effectively reducing the penetration of harmful UV radiation [6].Another approach entails the design of multilayer packaging structures, where a dedicated UV-blocking layer adds an extra layer of protection.These strategies expand the applicability of PLA to a broader range of packaging requirements while safeguarding the integrity of packaged contents.In parallel, researchers have explored the incorporation of inorganic nanoparticles directly into the PLA matrix or the application of specialized coatings to modify its UV behavior.For example, TiO 2 is selected as an additive to improve the UV resistance of the polymer.TiO 2 has good ultraviolet-light-resistance, as an ultraviolet additive, and due to its own excellent photocatalytic performance, it usually promotes the catalytic degradation of organic polymers, so the advantages of PLA degradability are fully guaranteed [7].While effective in bolstering UV resistance, these methods often compromise PLA's inherent transparency, limiting their widespread adoption.Alternatively, introducing large conjugated groups offers a promising route for absorbing UV light while maintaining material transparency.At the same time, through the introduction of conjugated groups of renewable resources such as lignin, tannin and aloin to give PLA a UV-blocking function, more renewable PLA materials can be maintained, ensuring the environmental advantages of PLA.However, this approach demands a careful balance between UV absorption, material safety, and potential migration of organic matter.This paper offers a comprehensive review of UV enhancement strategies for PLA and envisions its potential in food and pharmaceutical packaging.By augmenting PLA's UV resistance, we aim to broaden its scope of application, fostering its integration across diverse industries.

Titanium Dioxide-Based and Titanate-Based Materials
Titanium dioxide (TiO 2 ), recognized for its inertness, non-toxicity, affordability, high refractive index, and effective ultraviolet (UV) light absorption, has emerged as a promising candidate for improving PLA's UV resistance [8].The integration of TiO 2 within PLA matrices has garnered significant attention.
A research effort led by Man Changzhen showcased the integration of anatase titanium dioxide (A-TiO 2 ) and rutile titanium dioxide (R-TiO 2 ) into PLA matrices.Utilizing spin coating for thin films and extrusion injection for thick films, PLA/A-TiO 2 and PLA/R-TiO 2 composites were prepared [9].The findings revealed significant enhancement in the UV resistance of PLA with both A-TiO 2 and R-TiO 2 , particularly evident in the case of thin films.Moreover, the composite materials demonstrated commendable shading effects, minimizing amplitude attenuation upon UV exposure.However, a challenge emerged with anatase TiO 2 's sensitivity to air and water, resulting in photocatalysis and material instability.To address this, strategies like surface modification and stabilizer incorporation were explored, aiming to bolster UV stability and prolong the composite materials' service life.These efforts strive to harness the UV-blocking potential of PLA/TiO 2 composites for applications in packaging sensitive products like food and medicine.
Table 1 provides a comprehensive overview of the UV protection enhancements achieved through the integration of different forms of titanium dioxide (TiO 2 ) into polylactic acid (PLA) films.It highlights the effects on UV resistance, stability considerations, shading effects, application suitability, advantages, considerations, and future outlook for each type of composite [9].Despite promising results, compatibility issues between TiO 2 nanoparticles and PLA have been observed, leading to compromised physical properties of PLA, such as transparency, barrier attributes, and mechanical strength [10].Counteracting this challenge, researchers investigated diverse approaches.Surface modifications, like coupling agents and compatibilizers, aimed to improve the dispersion and interaction of TiO 2 nanoparticles within the PLA matrix, seeking to minimize adverse impacts while maximizing UVblocking efficiency.Advancements in nanotechnology, exemplified by core-shell structures where TiO 2 nanoparticles are enveloped with a polymer shell, address these compatibility hurdles [11].This innovative strategy enhances compatibility and dispersibility within the PLA matrix, leading to optimal UV-blocking effectiveness without sacrificing transparency, barrier properties, or mechanical strength.

•
Hydrophobic Modification for Enhanced Compatibility Naerin Baek's team also proposed hydrophobic modification using oleic acid to enhance compatibility between TiO 2 nanoparticles and PLA [10].The binding of oleic acid to TiO 2 surfaces improved dispersion within the PLA matrix, resulting in stable nanoparticle incorporation.This modification led to reduced oxygen permeability, water vapor permeability, and enhanced flexibility compared to pure PLA.Moreover, the UV absorption capacity of the composite improved, resulting in higher UVB protection.This advancement, however, showed less effective light absorption in the UVA and visible light regions.The hydrophobic modification with oleic acid not only improves compatibility but also enhances UV protection and barrier properties.

• Alternative Titanate Materials and Surface Modification
Moreover, recent research has extended beyond conventional TiO 2 materials to explore alternative titanate compounds.H. Attori's research team achieved the transformation of layered titanate K 2 Ti 2 O 5 into a novel titanate nanostructure material (Figure 1).This material exhibits a distinctive microporous titanate nanofiber structure, characterized by one-dimensional multi-microchannels.This novel material efficiently absorbs UV light while maintaining minimal catalytic activity.Its exceptionally low refractive index addresses TiO 2 's limitations by promoting transparency in composites, making it suitable for applications where clarity is paramount [11].By employing alternative titanate materials and optimizing their incorporation into PLA, researchers aim to enhance UV-blocking capabilities while preserving mechanical, optical, and barrier properties.The integration of titanium dioxide (TiO2) nanoparticles into polylactic acid (PLA) matrices holds promise for enhancing UV-blocking properties.While challenges persist, including compatibility issues and stability concerns with anatase TiO2, innovative strategies such as surface modification, core-shell structures, and alternative titanate materials are being explored.These efforts aim to achieve a delicate balance between UV protection, transparency, and mechanical properties.The resulting PLA/TiO2 composites exhibit potential for a wide range of UV-sensitive applications, particularly in industries like food and medicine packaging, where UV protection is paramount while maintaining material integrity.

Cerium Oxide (CeO2)-Based Materials
Cerium oxide (CeO2) is a highly significant and abundant rare earth material, esteemed for its exceptional physical and chemical attributes.Its stable face-centered cubic fluorite crystal structure has garnered substantial attention in recent times.Notably, research has illuminated CeO2's ability to influence the optical properties of plastic films by altering the reaction rate of the film's wallpaper [12].Incorporating CeO2 into polymer nanocomposites, such as polyvinyl alcohol (PVA), presents an avenue to tune the refractive index and reduce the absorption edge, thereby enhancing optical characteristics.Notably, CeO2 exhibits impressive UV absorbing and protecting capabilities, making it desirable for UV-sensitive applications in various sectors, including packaging, construction, and healthcare.The unique capacity of CeO2 to effectively absorb and block harmful ultraviolet radiation positions it as a valuable resource for materials necessitating stringent UV protection [13].Combining CeO2 with polymer matrices (Figure 2) presents a compelling prospect for achieving augmented UV protection, improved optical performance, and overall material properties [14].This synergy has driven extensive research into incorporating CeO2 into diverse polymeric systems, with the aim of harnessing its exceptional attributes to craft advanced materials boasting heightened UV-blocking capabilities.The integration of titanium dioxide (TiO 2 ) nanoparticles into polylactic acid (PLA) matrices holds promise for enhancing UV-blocking properties.While challenges persist, including compatibility issues and stability concerns with anatase TiO 2 , innovative strategies such as surface modification, core-shell structures, and alternative titanate materials are being explored.These efforts aim to achieve a delicate balance between UV protection, transparency, and mechanical properties.The resulting PLA/TiO 2 composites exhibit potential for a wide range of UV-sensitive applications, particularly in industries like food and medicine packaging, where UV protection is paramount while maintaining material integrity.

Cerium Oxide (CeO 2 )-Based Materials
Cerium oxide (CeO 2 ) is a highly significant and abundant rare earth material, esteemed for its exceptional physical and chemical attributes.Its stable face-centered cubic fluorite crystal structure has garnered substantial attention in recent times.Notably, research has illuminated CeO 2 's ability to influence the optical properties of plastic films by altering the reaction rate of the film's wallpaper [12].Incorporating CeO 2 into polymer nanocomposites, such as polyvinyl alcohol (PVA), presents an avenue to tune the refractive index and reduce the absorption edge, thereby enhancing optical characteristics.Notably, CeO 2 exhibits impressive UV absorbing and protecting capabilities, making it desirable for UV-sensitive applications in various sectors, including packaging, construction, and healthcare.The unique capacity of CeO 2 to effectively absorb and block harmful ultraviolet radiation positions it as a valuable resource for materials necessitating stringent UV protection [13].Combining CeO 2 with polymer matrices (Figure 2) presents a compelling prospect for achieving augmented UV protection, improved optical performance, and overall material properties [14].This synergy has driven extensive research into incorporating CeO 2 into diverse polymeric systems, with the aim of harnessing its exceptional attributes to craft advanced materials boasting heightened UV-blocking capabilities.•

Mechanism of UV Blocking by CeO2
By leveraging the unique properties of CeO2, researchers have overcome the limita- •

Mechanism of UV Blocking by CeO 2
By leveraging the unique properties of CeO 2 , researchers have overcome the limitations associated with other additives like TiO 2 .The enhanced compatibility and interaction between CeO 2 and PLA lay the foundation for the development of advanced UV-blocking materials boasting improved mechanical properties [15].This development holds immense potential across diverse industries, from packaging to electronics, where reliable UV protection is imperative.The UV-blocking mechanism of CeO 2 is attributed to its fluorite structure.Cerium dioxide (CeO 2 ) exhibits spontaneous hypoxia, leading to reversible valence state transitions between Ce 3+ and Ce 4+ (Figure 3) [12,16,17].This transition generates unstable oxygen vacancies that facilitate the absorption and conversion of UV light into heat.CeO 2 functions by absorbing a portion of UV radiation while scattering and reflecting the rest, effectively blocking UV penetration through the PLA film.This dual action underscores the effectiveness of CeO 2 in providing long-term UV protection.

Organic Compounds for UV Protection in Polymer Films
There are two main ways to improve the UV-blocking performance of PLA-one is to reflect UV light by introducing inorganic materials, and the other is to use conjugated groups in organic compounds to absorb UV light and give PLA UV-blocking properties.Among these methods, the use of lignin and other renewable resources to improve the UV-blocking performance of PLA, compared with the use of inorganic nanoparticles, to a greater extent to maintain the advantages of polylactic acid renewable, has advantages in environmental protection.Therefore, with the increase in people's attention regarding environmental protection, more and more researchers are looking for more efficient renewable organic compounds to give PLA UV-blocking properties.Therefore, in addition to the well-established domain of inorganic nanoparticles, the exploration of organic compounds as UV-absorbing agents has emerged as a promising avenue in UV protection research [18].These compounds, when thoughtfully integrated into polymer matrices through copolymerization, exhibit the potential to revolutionize UV-blocking strategies.Among these organic compounds, hydroxy-benzophenone UV stabilizers have garnered particular attention due to their remarkable efficacy in absorbing and blocking harmful UV radiation.Table 2 provides a comprehensive overview of each material type's advantages, considerations, and potential applications in enhancing UV protection within polymer films.

•
Lignin-Derived Additives: Lignin, a UV-absorbing material, can enhance UV protection but may cause compatibility issues with PLA.The synthesized TP-G-lignin improves UV shielding and maintains tensile strength.However, stress concentration points need addressing.

• Superior Compatibility and Enhanced Properties
In the context of enhancing UV protection, the integration of cerium oxide (CeO 2 ) into polylactic acid (PLA) matrices has shown considerable promise.Yincai Wu's research team embarked on a study exploring PLA/CeO 2 blends, specifically targeting UV-blocking enhancements [15].In their experiment, a PLA/CeO 2 blend was prepared with a defined mass ratio, leading to the creation of a UV-blocking polylactic acid material.The resultant film, obtained through a hot-pressing process, demonstrated significant reductions in UV light transmittance with increasing PLA content.In comparison to traditional anti-UV additives like titanium dioxide (TiO 2 ) modified with PLA, the compatibility between CeO 2 and PLA emerges as superior.This compatibility is attributed to the interaction between CeO 2 and PLA, facilitated by oxygen bridges, notably involving carboxyl groups.This interaction mechanism strengthens the adhesion between components, ensuring the film's integrity and mechanical properties are preserved.Furthermore, the improved compatibility allows for optimized dispersion of CeO 2 nanoparticles within the PLA matrix, preventing aggregation and enhancing overall film performance.

• Mechanical Properties and UV-Blocking Efficiency
Yincai Wu et al.'s study findings revealed that the incorporation of 2% PLA resulted in a notable decrease in UV light transmittance to 0.47%.Additionally, the mechanical properties of the PLA/CeO 2 blend were evaluated, indicating increased tensile strength and elongation at break compared to pure PLA [15].These results highlighted a substantial reduction in UV light transmittance, a noteworthy enhancement in tensile strength, and a significant increase in elongation at break, signifying the blend's improved UV-blocking efficiency and mechanical integrity.

Organic Compounds for UV Protection in Polymer Films
There are two main ways to improve the UV-blocking performance of PLA-one is to reflect UV light by introducing inorganic materials, and the other is to use conjugated groups in organic compounds to absorb UV light and give PLA UV-blocking properties.Among these methods, the use of lignin and other renewable resources to improve the UV-blocking performance of PLA, compared with the use of inorganic nanoparticles, to a greater extent to maintain the advantages of polylactic acid renewable, has advantages in environmental protection.Therefore, with the increase in people's attention regarding environmental protection, more and more researchers are looking for more efficient renewable organic compounds to give PLA UV-blocking properties.Therefore, in addition to the well-established domain of inorganic nanoparticles, the exploration of organic compounds as UV-absorbing agents has emerged as a promising avenue in UV protection research [18].These compounds, when thoughtfully integrated into polymer matrices through copolymerization, exhibit the potential to revolutionize UV-blocking strategies.Among these organic compounds, hydroxy-benzophenone UV stabilizers have garnered particular attention due to their remarkable efficacy in absorbing and blocking harmful UV radiation.Table 2 provides a comprehensive overview of each material type's advantages, considerations, and potential applications in enhancing UV protection within polymer films.

•
Lignin-Derived Additives: Lignin, a UV-absorbing material, can enhance UV protection but may cause compatibility issues with PLA.The synthesized TP-G-lignin improves UV shielding and maintains tensile strength.However, stress concentration points need addressing.

•
Tannins: Tannin-derived chelates effectively block UV radiation and act as crosslinking agents, but their hyperbranched structure can reduce PLA chain mobility and cause coloration.• Hyperbranched structure of tannin can limit PLA chain mobility, reducing elongation at break.

•
Coloration of composite material due to chelates may limit applications in packaging.
Enhancing UV protection and tensile properties.
Hydroxyl Alkylated Tannic Acid • mTA and h-mTA offer strong UV-blocking capabilities.

•
Excellent compatibility with PLA due to strong hydrogen bond interface.
Color change in composite material may affect its applicability.
Enhancing UV protection without compromising transparency.
Aloe-Derived UV-Resistant PLA Synthesized PLA material with inherent UV protection through ESIPT process.
Further optimization needed for mechanical properties and long-term stability.
Providing UV protection alongside transparency.

Regenerated Cellulose Fiber
CMF reinforcement improves UV-blocking and barrier properties.
Reduction in transparency due to CMF presence.
Enhancing UV protection with improved mechanical properties.

Lignin-Derived Additives for UV Protection
The rich aromatic ring structure of lignin makes it an effective UV absorber.The exploitation of lignin, a ubiquitous and intricate natural polymer, for its inherent ability to absorb ultraviolet (UV) light has garnered substantial interest.The aromatic ring structure within lignin imparts exceptional UV-absorbing properties, positioning it as a potential game-changer in UV protection strategies for polymer matrices.However, the translation of this potential into practical applications is not devoid of challenges, particularly regarding compatibility and mechanical integrity [14].
The mechanism behind lignin's UV-absorbing prowess resides in the conjugated structure of its aromatic rings, allowing for efficient dissipation of UV radiation energy.In recent research pursuits, attention has turned to enhancing lignin's compatibility with polymer matrices, ultimately optimizing its UV-blocking capabilities.An innovative approach in this realm is the development of TP-G-lignin, achieved through grafting polymerization (Figure 4).The researchers first dissolved PEPA first in dimethylformamide (DMF).Then, TMI was added to the solution and continued to react at 50 • C for 4 h.After the reaction, the reaction mixture was poured into distilled water to precipitate and filter, and TP was obtained.Next, NaCl was added to a single-neck flask containing DMF, stirred, lignin was added after NaCl was completely dissolved, stirred and slowly heated to 50 • C.Then, the pre-designed TP was dripped into the solution, and H 2 O 2 was added.After being kept at 50 • C for 24 h, the mixture was slowly poured into the overdiluted HCl solution to stop the grafting reaction.After the precipitation was filtered and washed and dried, the target product TP-G-lignin was obtained.This advanced additive is engineered to address the often-troublesome compatibility issues between lignin and polymer matrices.Through covalent bonding between lignin and a phosphorous/nitrogen-containing vinyl monomer (TP), TP-G-lignin establishes a robust interface with the polymer matrix.
dried, the target product TP-G-lignin was obtained.This advanced additive is engineered to address the often-troublesome compatibility issues between lignin and polymer matrices.Through covalent bonding between lignin and a phosphorous/nitrogen-containing vinyl monomer (TP), TP-G-lignin establishes a robust interface with the polymer matrix.The rich aromatic ring structure in lignin makes it highly capable of absorbing ultraviolet (UV) light, thereby imparting excellent UV-shielding properties.As a result, lignin has gained significant attention for its potential as a UV-absorbing additive.To enhance its functionality, a multifunctional lignin-derived additive, known as TP-G-lignin, was synthesized through the grafting polymerization of a phosphorous/nitrogen-containing vinyl monomer (TP) with lignin.When lignin alone is used as an additive, poor interface adhesion between lignin and the polylactic acid (PLA) matrix can result in the formation of micro-cracks during the tensile process.This, in turn, leads to a reduction in mechanical strength.However, the TP-G-lignin developed by the research team effectively addresses this issue.The TP-G-lignin not only exhibits excellent UV-shielding properties for PLA, but also ensures the preservation of tensile strength due to its good compatibility with the PLA matrix.Moreover, the addition of TP-G-lignin does not significantly compromise the transparency of the PLA material.Nevertheless, during the tensile test, some clumps of TP-G-lignin act as stress concentration points, leading to the formation of microcracks.Consequently, the fracture strain of the material is reduced.This highlights the need to improve the dispersion of TP-G-lignin within the PLA matrix to mitigate such stress concentration effects.Further research is focused on optimizing the TP-G-lignin synthesis process and enhancing its dispersion in the PLA matrix.This will help minimize the formation of stress concentration points and improve the overall mechanical properties of the material.Additionally, investigations into the impact of TP-G-lignin on the long-term stability and performance of PLA-based products are ongoing.The development of TP-G-lignin as a UV-absorbing additive offers great potential for expanding the range of applications for PLA materials.Its compatibility with PLA, combined with its UV-shielding properties, makes it a valuable choice for industries such as the packaging, textiles, and electronics industries, where UV protection is essential.Continued research in this area The rich aromatic ring structure in lignin makes it highly capable of absorbing ultraviolet (UV) light, thereby imparting excellent UV-shielding properties.As a result, lignin has gained significant attention for its potential as a UV-absorbing additive.To enhance its functionality, a multifunctional lignin-derived additive, known as TP-G-lignin, was synthesized through the grafting polymerization of a phosphorous/nitrogen-containing vinyl monomer (TP) with lignin.When lignin alone is used as an additive, poor interface adhesion between lignin and the polylactic acid (PLA) matrix can result in the formation of micro-cracks during the tensile process.This, in turn, leads to a reduction in mechanical strength.However, the TP-G-lignin developed by the research team effectively addresses this issue.The TP-G-lignin not only exhibits excellent UV-shielding properties for PLA, but also ensures the preservation of tensile strength due to its good compatibility with the PLA matrix.Moreover, the addition of TP-G-lignin does not significantly compromise the transparency of the PLA material.Nevertheless, during the tensile test, some clumps of TP-G-lignin act as stress concentration points, leading to the formation of microcracks.Consequently, the fracture strain of the material is reduced.This highlights the need to improve the dispersion of TP-G-lignin within the PLA matrix to mitigate such stress concentration effects.Further research is focused on optimizing the TP-G-lignin synthesis process and enhancing its dispersion in the PLA matrix.This will help minimize the formation of stress concentration points and improve the overall mechanical properties of the material.Additionally, investigations into the impact of TP-G-lignin on the long-term stability and performance of PLA-based products are ongoing.The development of TP-G-lignin as a UV-absorbing additive offers great potential for expanding the range of applications for PLA materials.Its compatibility with PLA, combined with its UV-shielding properties, makes it a valuable choice for industries such as the packaging, textiles, and electronics industries, where UV protection is essential.Continued research in this area holds promise for the development of innovative and sustainable materials with improved UV-shielding capabilities and mechanical performance [19].
While TP-G-lignin represents a significant advancement, critical examination reveals that challenges remain.The composite's mechanical behavior is notably affected by the uniform dispersion of TP-G-lignin within the polymer matrix.The aggregation of TP-Glignin clusters can lead to the creation of stress concentration points during mechanical processes, ultimately undermining the composite's full mechanical potential [18].This calls for an in-depth exploration of strategies to achieve homogenous distribution and effective stress transfer mechanisms within the material.
The road ahead for lignin-derived UV protection additives involves targeted research endeavors.The optimization of TP-G-lignin synthesis processes and its dispersion within the polymer matrix must be prioritized to minimize stress concentration effects.This optimization could encompass innovative strategies to mitigate clustering and to ensure that TP-G-lignin acts as a consistent reinforcing agent throughout the composite material.Moreover, the long-term stability and performance of TP-G-lignin within diverse polymer matrices necessitate thorough investigation to gauge its potential for industrial-scale applications.Looking beyond the immediate challenges, the incorporation of lignin-based additives into polymer matrices offers the dual advantage of enhanced UV protection and sustainable material sourcing.As the scientific community grapples with issues related to compatibility and mechanical behavior, the overarching aim remains the creation of UV-resistant materials that preserve mechanical integrity.This pursuit aligns seamlessly with the broader sustainability goals of materials science, contributing to the development of environmentally conscious solutions.
In conclusion, the incorporation of lignin-derived additives into polymer matrices for UV protection is an intricate journey, characterized by the interplay of scientific innovation, engineering optimization, and sustainable material design.The advent of TP-G-lignin represents a pivotal step, yet its full potential hinges on addressing existing challenges and charting future research paths.As advancements in UV protection technology continue, the marriage of lignin's UV-absorbing capability and polymer matrices holds the promise of resilient and sustainable UV-resistant materials with profound implications across industries.

Tannins as UV Absorbers and Crosslinking Agents
Tannins, aromatic compounds abundant in biological sources, have emerged as intriguing candidates for enhancing ultraviolet (UV) shielding capabilities in polylactic acid (PLA) materials [20,21].However, their application presents a complex interplay between UV protection enhancement and mechanical property modulation due to their dual role as UV absorbers and potential crosslinking agents.The incorporation of tannins into PLA matrices capitalizes on their inherent ability to form chelates, reinforcing the UV-shielding properties of the resulting composite materials [22].Through the formation of chelates, such as the tannin-Fe 3+ complex (TAFe) (Figure 5), a UV absorption capacity spanning the 250-350 nm range is achieved.The chelate's aromatic ring undergoes a π → π* transition upon UV irradiation, enabling effective UVA and UVB radiation absorption.Current research has elucidated the correlation between TAFe concentration and UV-blocking efficacy, demonstrating that a higher TAFe content enhances UV protection.However, the integration of tannins into PLA matrices introduces certain chall While TAFe acts as a potent UV absorber, its hyperbranched structure simultaneou erts physical crosslinking effects on the PLA polymer chains.This crosslinking im rigidity to the polymer matrix, impacting its mechanical properties, particularly it gation at break [23].Furthermore, the characteristic dark blue coloration of tannin ch poses aesthetic limitations in applications where color uniformity is paramount.However, the integration of tannins into PLA matrices introduces certain challenges.While TAFe acts as a potent UV absorber, its hyperbranched structure simultaneously exerts physical crosslinking effects on the PLA polymer chains.This crosslinking imparts rigidity to the polymer matrix, impacting its mechanical properties, particularly its elongation at break [23].Furthermore, the characteristic dark blue coloration of tannin chelates poses aesthetic limitations in applications where color uniformity is paramount.Future research endeavors should focus on addressing the dual role of tannins to maximize their UV protection potential while minimizing the adverse impact on mechanical properties.Strategies to fine-tune the balance between UV absorption and flexibility restoration hold promise.Exploring modified tannins or surface treatments to mitigate the crosslinking effect could yield PLA composites with improved mechanical integrity.Additionally, advancements in color modulation techniques may alleviate the coloration drawback, expanding the range of potential applications.
Moreover, the interplay between UV protection and mechanical integrity remains a central theme in tannin-based UV absorbers.The challenge lies in devising methodologies to strike an optimal equilibrium between enhanced UV shielding and preserved mechanical properties.By innovatively modifying tannin structures or incorporating them at specific concentrations, researchers can potentially surmount the current limitations and engineer PLA composites that excel in both UV protection and mechanical performance.Meanwhile, aesthetic considerations in tannin-based UV-absorbing PLA materials are also of significance, particularly in applications where coloration is a determining factor.While the coloration effect is currently a limiting factor, innovative strategies to mitigate or leverage this phenomenon can unlock new application domains.Future exploration in material design and processing could lead to tannin-based composites that offer both effective UV protection and aesthetic versatility.
To sum up, tannins have unveiled a captivating dual role as UV absorbers and potential crosslinking agents in PLA composites.As research advances, a nuanced understanding of tannin behavior within the polymer matrix is crucial.The pursuit of optimized formulation strategies, mechanical property enhancement techniques, and color modulation methods will collectively drive the integration of tannins into UV-protective PLA materials.Balancing UV shielding, mechanical performance, and aesthetics presents a multifaceted challenge, but one that promises innovative solutions with applications across diverse industries.

Hydroxyl Alkylated Tannic Acid for Enhanced UV Protection
Hydroxyl alkylated tannic acid (mTA) and its highly grafted counterpart (h-mTA) have emerged as intriguing contenders in the pursuit of enhancing ultraviolet (UV) protection within polylactic acid (PLA) materials.Their synthesis and integration showcase an exquisite balance between UV-shielding efficacy, PLA compatibility, and the challenge of coloration.Xuhui Zhang's team developed a novel approach to enhance the UV-blocking properties of polylactic acid (PLA) by designing hydroxyl alkylated tannic acid (TA), known as mTA, with grafted isopropyl alcohol oligomers [24].The mTA was synthesized based on TA molecules, which possess 25 active phenolic hydroxyl groups.The hydroxyl alkylated mTA, particularly the highly grafted mTA variant (h-mTA), demonstrated excellent compatibility with PLA due to the strong affinity and hydrogen bond interface between the isopropyl alcohol oligomers and PLA.To assess the UV-blocking properties of PLA and h-mTA composites, the team conducted experiments.The results revealed that the PLA/h-mTA composite films effectively blocked UV radiation, while maintaining higher transmittance in the visible region compared to pure PLA films (Figure 6).When incorporating 5 wt% h-mTA, the transmittance at 300 nm significantly decreased from 90.12% to 31.89%, while the transmittance at 550 nm only slightly decreased from 91.87% to 90.54%.Notably, the addition of 20 wt% h-mTA further reduced the transmittance at 300 nm to 2.74%, while maintaining a high transmittance of 84.35% at 550 nm.This highlights the remarkable UVshielding performance and excellent transparency achieved by the PLA/h-mTA composite films.These findings demonstrate the potential of hydroxyl alkylated TA, particularly the highly grafted h-mTA, as an effective UV absorber and compatibilizer for PLA.The incorporation of h-mTA into PLA matrix not only enhances the UV-blocking capabilities of the composite but also preserves its optical transparency in the visible range.This makes the PLA/h-mTA composite films highly desirable for applications in industries such as packaging, where UV radiation protection and visual clarity are crucial.The synthesis of mTA and h-mTA revolves around augmenting the inherent UV-absorbing capabilities of tannic acid by introducing isopropyl alcohol oligomers.This strategic integration capitalizes on the strong affinity and hydrogen bond interface between the isopropyl alcohol moieties and the PLA matrix.This, in turn, facilitates a harmonious incorporation of mTA and h-mTA into PLA materials, rendering them compatible additives.
5 wt% h-mTA, the transmittance at 300 nm significantly decreased from 90.12% to 31.89%, while the transmittance at 550 nm only slightly decreased from 91.87% to 90.54%.Notably, the addition of 20 wt% h-mTA further reduced the transmittance at 300 nm to 2.74%, while maintaining a high transmittance of 84.35% at 550 nm.This highlights the remarkable UVshielding performance and excellent transparency achieved by the PLA/h-mTA composite films.These findings demonstrate the potential of hydroxyl alkylated TA, particularly the highly grafted h-mTA, as an effective UV absorber and compatibilizer for PLA.The incorporation of h-mTA into PLA matrix not only enhances the UV-blocking capabilities of the composite but also preserves its optical transparency in the visible range.This makes the PLA/h-mTA composite films highly desirable for applications in industries such as packaging, where UV radiation protection and visual clarity are crucial.The synthesis of mTA and h-mTA revolves around augmenting the inherent UV-absorbing capabilities of tannic acid by introducing isopropyl alcohol oligomers.This strategic integration capitalizes on the strong affinity and hydrogen bond interface between the isopropyl alcohol moieties and the PLA matrix.This, in turn, facilitates a harmonious incorporation of mTA and h-mTA into PLA materials, rendering them compatible additives.However, the advancement of h-mTA as a UV-absorbing additive is not devoid of challenges.The introduction of h-mTA, while enhancing UV protection, may lead to the coloration of the resulting composite material.This color change poses limitations, However, the advancement of h-mTA as a UV-absorbing additive is not devoid of challenges.The introduction of h-mTA, while enhancing UV protection, may lead to the coloration of the resulting composite material.This color change poses limitations, particularly in applications where color uniformity is pivotal.Addressing this challenge represents an essential area for further exploration and optimization.The synergy between UV protection and PLA compatibility exhibited by mTA and h-mTA presents exciting prospects for a range of industries.Their compatibility-driven integration into PLA materials could be harnessed in various sectors, such as packaging, textiles, and electronics, where UV shielding and transparency are imperative.Research aimed at mitigating the coloration issue could unlock even broader applications, thus maximizing the potential of these compounds.
Moreover, the journey of mTA and h-mTA in enhancing UV protection is a dynamic endeavor that requires striking a delicate balance between UV absorption, compatibility, and coloration.Navigating these intricacies demands not only a thorough understanding of material science but also innovative strategies for material design.Future research efforts should be channeled towards refining the formulation and optimizing the concentration of these derivatives to fine-tune their UV protection and coloration aspects.In addition, mTA and h-mTA's compatibility-driven UV protection offers a promising avenue for advancing UV-resistant materials.The ability to simultaneously enhance UV shielding and maintain transparency opens avenues for their deployment in industries where both factors are paramount [24].As research delves deeper into overcoming the coloration challenge, the potential for these derivatives to redefine UV protection in diverse applications becomes increasingly evident.
In conclusion, hydroxyl alkylated tannic acid derivatives, particularly mTA and h-mTA, have demonstrated their mettle in the realm of UV protection enhancement within PLA materials.Their journey is characterized by a harmonious interplay between UV shielding, compatibility, and coloration.As these compounds continue to evolve, their role in delivering multifaceted UV protection while addressing coloration challenges holds great promise.The scientific community's concerted efforts towards optimizing these derivatives could usher in a new era of UV-resistant materials with wide-ranging applicability.

Aloe-Derived UV-Resistant PLA Material
In the quest for UV protection innovation, a remarkable breakthrough has emerged: the synthesis of UV-resistant polylactic acid (PLA) material by ingeniously incorporating the UV-absorbing prowess of aloin, a compound extracted from aloe leaves.This pioneering approach marks a significant stride towards UV protection, leveraging the intrinsic mechanisms of nature to create a material with exceptional UV-blocking capabilities and versatile applications.At the heart of this innovation lies the incorporation of aloin, a natural UV-protective compound, into the PLA matrix.Aloin's UV-absorbing group is adept at harnessing ultraviolet radiation and efficiently dissipating its energy through the excited state intramolecular proton transfer (ESIPT) process [25,26].This strategic integration imbues the PLA material with the unique ability to absorb and neutralize harmful UV radiation, thereby safeguarding against its detrimental effects.
Aloin, an extract of aloe leaf, is a UV-protective intramolecular hydrogen-bonded hydroxy-anthraquinone derivative whose excited-state intramolecular proton transfer (ESIPT) can absorb harmful ultraviolet radiation and dissipate harmless thermal energy through very rapid internal conversion (Figure 7).[27].They added an appropriate amount of Sn(Oct)2/THF solution and aloin (cetyl alcohol) into the polymerization tube filled with argon gas, vacuumed it and sealed it with an alcohol burner.The tubes were then placed in an oil bath at 135 °C and stirred.When the reactant melted, the reaction stopped after 5 h.After cooling, the product was dissolved in chloroform, and then the solution was dropped into the stirred ethanol to precipitate.Then, it was washed with ethanol until there was no UV absorption signal of aloin in the eluent, followed by vacuum drying.Then, a sample of lactide was obtained.This unique approach allowed for the connection of the UV-absorbing group of aloin to the polymer chain, resulting in a material with inherent UV protection properties that do not migrate.The newly synthesized polylactide material exhibits similar ultraviolet light absorption and emission characteristics to aloin itself.Moreover, it possesses a significant Stokes shift, enabling the dissipation of ultraviolet radiation energy through the excited Mengyao Wang et al. developed a novel UV-resistant polylactic acid (PLA) material by synthesizing it through the ring-opening polymerization of L-lactide, utilizing aloin as an initiator [27].They added an appropriate amount of Sn(Oct)2/THF solution and aloin (cetyl alcohol) into the polymerization tube filled with argon gas, vacuumed it and sealed it with an alcohol burner.The tubes were then placed in an oil bath at 135 • C and stirred.When the reactant melted, the reaction stopped after 5 h.After cooling, the product was dissolved in chloroform, and then the solution was dropped into the stirred ethanol to precipitate.Then, it was washed with ethanol until there was no UV absorption signal of aloin in the eluent, followed by vacuum drying.Then, a sample of lactide was obtained.This unique approach allowed for the connection of the UV-absorbing group of aloin to the polymer chain, resulting in a material with inherent UV protection properties that do not migrate.The newly synthesized polylactide material exhibits similar ultraviolet light absorption and emission characteristics to aloin itself.Moreover, it possesses a significant Stokes shift, enabling the dissipation of ultraviolet radiation energy through the excited state intramolecular proton transfer (ESIPT) process.This exceptional property allows the aloin group to maintain structural stability under ultraviolet light exposure and effectively function over an extended period.Importantly, the incorporation of aloin as a UV-absorbing group does not compromise the transmission of visible light through the material.As a result, the transparency of the polylactic acid film material remains intact, ensuring its suitability for applications where optical clarity is paramount.This innovative UV-resistant PLA material holds promise for various industries, such as packaging, where protection against UV radiation is necessary.Its ability to absorb and dissipate UV radiation through the ESIPT process enables prolonged and efficient UV protection, enhancing the durability and stability of products made from this material.
While the aloe-derived PLA material presents a breakthrough in UV protection, the journey is not devoid of areas for refinement.Exploring avenues to further optimize the integration of aloin and enhance its dispersion within the PLA matrix holds promise for improving the material's overall performance [28].Addressing this aspect could unlock even greater UV protection efficiency.The emergence of the aloe-derived UV-resistant PLA material signifies a convergence of scientific innovation and natural inspiration.As research continues to unravel the intricacies of the ESIPT process and the interaction between aloin and PLA, opportunities for fine-tuning and optimizing the material's properties abound.The future outlook revolves around harnessing this potential to create a new generation of UV-resistant materials with improved performance and expanded applications.
The synthesis of UV-resistant PLA material through the infusion of aloin epitomizes the harmony between scientific ingenuity and nature's design.The material's ability to emulate and enhance nature's UV protection mechanisms underscores the transformative power of biomimicry in material science.As researchers delve deeper into the mechanics of ESIPT and material formulation, the possibilities for innovation become boundless.This novel approach unlocks a world of opportunities, where transparency, UV protection, and versatile applications converge.The ongoing journey to optimize and harness the potential of this material presents a vibrant avenue for further advancements in UV-resistant materials, ushering in a future where the union of nature and science creates sustainable and innovative solutions.

Reinforcing PLA with Regenerated Cellulose Fiber
In the realm of enhancing PLA materials, an innovative avenue emerges with the incorporation of regenerated cellulose fiber, specifically cellulose microfibers (CMF).This strategic union aims not only to fortify mechanical properties, but also to elevate UV protection capabilities, offering a multifaceted approach to material enhancement.The driving force behind this advancement is the utilization of CMF as a reinforcement material within the PLA composite matrix.CMF, with its inherent strength and unique structure, intertwines with PLA to create a synergistic composite material.Inherent properties of CMF, such as its composition and microstructure, contribute to the enhancement of both mechanical strength and UV protection capabilities of the PLA composite.
However, the active hydroxyl group of cellulose fiber can form intramolecular and intermolecular hydrogen bonds, which reduces the dispersion ability of cellulose fiber in polylactic acid, resulting in poor mechanical properties and barrier properties of the composite [29,30].To improve its compatibility problem, Rabaharan Graceraj Ponnusamy's team chose CMFs extracted from cotton fiber as reinforcing materials.Cotton wool is a short cotton fiber (1.32 mm long), and its surface contains about 0.5-1 wt% of natural wax, which makes cellulose fibers hydrophobic and enhances the dispersion of CMF in PLA [31].Using cotton yarn as a raw material, the team prepared the composite fiber via the ball milling method.The control film and composite film were prepared via the solvent casting method.They dried PLA pellets and cotton brocade in an oven at 55 • C for 48 h to evaporate the absorbed water, then added the dried polylactic acid pellets to DCM solvent and mixed them at room temperature until dissolved.Secondly, CMF and PEG were added to completely dissolved PLA solution, and after mixing and degassing, the solution was poured into a glass Petri dish, the Petri dish was covered with aluminum foil, and DCM was slowly evaporated at room temperature in the hood.After drying, the film was removed from the Petri dish 24 h later, and stored in a 50%RH dryer for more than 48 h, then characterization studies were carried out.The results show that CMF has strong interfacial adhesion in the PLA polymer matrix and good compatibility with polylactic acid.The introduction of CMF not only improves the UV-blocking properties of polylactic acid, but also improves the tensile properties and water vapor blocking properties (Table 3) [32].Compared with tannin, CMF can effectively improve the tensile properties of polylactic acid, but there is still a problem in that it can reduce the transparency of polylactic acid.While the incorporation of CMF yields commendable improvements in mechanical and UV protection properties, a careful balance is necessary.The enhanced mechanical strength achieved through CMF infusion can inadvertently lead to a reduction in material transparency.This trade-off necessitates a thorough assessment of the intended application, where mechanical strength and UV protection are weighed against transparency requirements [33].
The ongoing research journey in the realm of CMF-reinforced PLA materials rests upon achieving an optimal equilibrium between enhanced mechanical properties, UV protection, and transparency.Fine-tuning the concentration and dispersion of CMF within the PLA matrix holds promise for mitigating transparency challenges while preserving the material's newfound strengths.As investigations evolve, the future horizon of CMF-reinforced PLA materials appears bright.The dynamic balance between mechanical reinforcement, UV protection, and transparency hinges upon meticulous formulation and material engineering.Future research will delve deeper into unraveling the intricacies of CMF-PLA interactions, optimizing processing techniques, and broadening the material's scope of applications.The integration of CMF as a reinforcement material within PLA composites reshapes the landscape of material science.The pursuit of enhanced mechanical properties and UV protection through such bio-based reinforcements is a testament to sustainability and innovation.As research endeavors advance, the potential for creating tailored CMF-PLA materials for specific industries gains prominence, underscoring the transformative power of strategic material combinations [33].
The collaboration between natural cellulose fibers and engineered PLA encapsulates the essence of sustainable materials evolution.Through harnessing nature's building blocks, researchers are driving the development of advanced materials that are resilient against UV radiation while upholding mechanical integrity.This journey harmonizes technological innovation with ecological consciousness, laying the groundwork for versatile and environmentally friendly solutions.The integration of regenerated cellulose fibers, CMF, into PLA materials marks a pivotal chapter in UV protection and mechanical enhancement.As research advancements converge with real-world applications, the profound impact of synergistic material combinations emerges.The path forward lies in striking a harmonious balance between transparency, strength, and UV resistance, ushering in a new era of reinforced materials that embody the essence of innovation, sustainability, and functionality.

Exploring the Landscape of UV Protection Enhancement
The quest to enhance the ultraviolet (UV) protection properties of polylactic acid (PLA) materials has sparked a multifaceted journey encompassing inorganic nanoparticles and bio-based organic compounds.While inorganic nanoparticles, notably titanium dioxide (TiO 2 ), have been a focal point, the horizon of research is expanding to embrace alternative materials like zinc oxide, poised to carve new pathways in UV protection.

Inorganic Nanoparticles: Diversification and Evolution
The realm of inorganic nanoparticles has witnessed substantial exploration, with TiO 2 emerging as a prominent player.However, the ongoing pursuit of UV protection is expected to shift towards innovative inorganic materials such as zinc oxide [34].This transition is fueled by the pursuit of sustainable solutions that transcend the limitations of traditional inorganic options.

Bio-Based Organic Compounds: A Sustainable Revolution
In an era of heightened environmental consciousness, the adoption of bio-based organic compounds to enhance PLA's UV-shielding capabilities is gaining traction.Prominent contenders, including lignin, tannic acid, and aloin, exhibit both enhanced UV protection and compatibility with PLA, marking a significant stride towards sustainable UV protection technology [35][36][37].

Navigating Coloration and Application Realms
While the incorporation of bio-based compounds yields promising UV protection benefits, the challenge of potential coloration of composite materials arises.The distinct blue hue introduced by tannin chelates and the sandy brown shade resulting from hydroxyl alkylated tannic acid (h-mTA) underscore the importance of tailoring material properties to specific application requirements.The implications of enhanced UV protection extend far beyond packaging, finding resonance in medical and textile domains.The development of UV-resistant PLA films and UV-protective polylactic acid cotton fabrics presents novel opportunities in medicine and textiles, setting the stage for innovative applications in these fields [38].

Conclusions
The journey towards augmenting UV protection in PLA materials unfolds as a testament to the dynamic nature of materials science.The transition from conventional inorganic nanoparticles to sustainable bio-based compounds reflects a broader shift towards holistic and environmentally conscious solutions.The utilization of established bio-based materials like lignin, tannin, and cellulose offers a promising avenue to address current limitations.By harnessing the inherent properties of these materials, researchers aim to overcome challenges while elevating PLA's UV-barrier capabilities.The pursuit of optimal UV protection propels researchers to explore novel biomolecules with exceptional performance attributes.Aloe emodin [28] and riboflavin [39] exemplify such biomolecules, offering the potential to bolster UV protection through advanced polymerization techniques.By strategically incorporating these biomolecules, researchers aspire to not only enhance UV protection but also maintain transparency and mechanical strength [40,41].Amid the tapestry of UV protection methodologies explored, the journey toward UV-enhanced PLA materials holds the promise of greater depths.As sustainability, innovation, and performance intersect, researchers are uniquely positioned to redefine material landscapes, providing industries and environments with robust and advanced UV-protected PLA materials that transcend traditional boundaries.

Figure 6 .
Figure 6.(a) UV−vis absorption spectra of the THF solution of TA and mTAs at 0.01 mg/mL; the UV−vis transmittance spectra, (b) and images, (c) of neat PLA and PLA/h-mTA films with various h-mTA contents.Adapted with permission from [24].Copyright 2013 Zhang, X. et al.

Figure 6 .
Figure 6.(a) UV−vis absorption spectra of the THF solution of TA and mTAs at 0.01 mg/mL; the UV−vis transmittance spectra, (b) and images, (c) of neat PLA and PLA/h-mTA films with various h-mTA contents.Adapted with permission from [24].Copyright 2013 Zhang, X. et al.

Figure 7 .
Figure 7. ESIPT of aloin I (3, 8-dihydroxy-1-methyl-9, 10-dioxy-9, 10-dihydroanthracene 2 carboxylatemethylester). Adapted with permission from [25].Copyright 2007 Nagaoka, S.-I.Mengyao Wang et al. developed a novel UV-resistant polylactic acid (PLA) material by synthesizing it through the ring-opening polymerization of L-lactide, utilizing aloin as an initiator[27].They added an appropriate amount of Sn(Oct)2/THF solution and aloin (cetyl alcohol) into the polymerization tube filled with argon gas, vacuumed it and sealed it with an alcohol burner.The tubes were then placed in an oil bath at 135 °C and stirred.When the reactant melted, the reaction stopped after 5 h.After cooling, the product was dissolved in chloroform, and then the solution was dropped into the stirred ethanol to precipitate.Then, it was washed with ethanol until there was no UV absorption signal of aloin in the eluent, followed by vacuum drying.Then, a sample of lactide was obtained.This unique approach allowed for the connection of the UV-absorbing group of aloin to the polymer chain, resulting in a material with inherent UV protection properties that do not migrate.The newly synthesized polylactide material exhibits similar ultraviolet light absorption and emission characteristics to aloin itself.Moreover, it possesses a significant Stokes shift, enabling the dissipation of ultraviolet radiation energy through the excited

Table 2 .
Organic compound's advantages, considerations, and potential applications in enhancing UV protection within polymer films.

Table 3 .
Light transmittance of PLA and CMF-PLA composite films at 600, 400 and 233 nm wavelengths.