Effect of Ce Content on Properties of Al-Ce-Based Composites by Powder-in-Tube Method

: Al-Ce based alloys have gained recent interest and have proven to have excellent strength without heat treatment and high thermal stability. Challenges with the production of Al-Ce samples from elemental powders arise due to the elemental material before alloying being susceptible to rapid oxidation. The methodology for making superconductive wire, powder-in-tube, was used as a consolidate Al and Ce elemental powder, and Al-8 wt % Ce-10 wt % Mg composite powder into bulk nanostructured material. Powder samples are fabricated in an inert controlled atmosphere, then sealed in a tube to avoid oxidation of powders. Therefore, most of the powder is used without much loss. We used 316 stainless-steel tubes as a sheathing material. For Al-xCe wt % (x = 8 to 14) samples of elemental powder, liquid phase sintering was used and for Al-Ce-Mg powder solid-state sintering. Characterization of the bulk consolidated material after sintering, and before and after heat treatment, was made using optical and Scanning Electron Microscope imaging, Energy Dispersive Spectroscopy, Microhardness and Rockwell Hardness test. We demonstrated that microstructure stability in Al-Ce-based specimens can be retained after thermomechanical processing. Densiﬁcation was achieved and oxidation of powder was avoided in most samples. In addition, we found that Fe and Ni in the sheathing material react with Al in the process, and Ce concentration modiﬁes the reactivity the sheath. Microstructural stability of ﬁne structure in Al-Ce specimens can be retained after thermomechanical processing at elevated temperatures above 700 ◦ C used in PIT liquid phase sintering and 400 ◦ C HT to yield a bulk ﬁne structured composite. Nanostructuring Al-Ce-based material is possible and understanding the processing methodology and its effect on the properties of the material is necessary. This study indicates that the PIT processing methodology is highly compatible with Al-Ce based composites due to the stability of ﬁne microstructure during thermomechanical processing and high temperature HT. work effect on the properties of the material is necessary. This study indicates that the PIT processing methodology is highly compatible with Al-Ce based composites due to the stability of fine microstructure during thermomechanical processing and high temperature HT.


Introduction
Traditionally, aluminum-based alloys have been one of the most used automotive and aerospace materials. Aluminum is a very attractive material for engineering applications since it is a lightweight metal able to attain high strength levels via heat treatment. Recently, aluminum-cerium-based alloys have been studied as an alternative for structural applications at room and high temperatures [1]. Researchers claim that the entire Al-Ce alloys family (including ternary and quaternary alloys) could retain much of their yield strengths at high temperatures compared to traditional Al alloys, enabling the new alloys for high temperature applications [2]. Accordingly, Al-Ce-Mg alloys should have a good performance and thermal stability at high temperature. Sims et al., reported that if Ce is used as a major alloying element for aluminum (over 10 wt %) and the industry remains utilizing Al at the same consumption level, Ce demand will be 21,772.4 metric ton annually, which will lead to the rare earth (RE) industry lowering cost of production [3]. This circumstance compelled scientists and engineers to develop Al-Ce alloys with a high cerium concentration to raise the demand for this metal and impact the RE industry economy. 2

of 14
The binary Al-Ce phase diagram has been reevaluated by empirical experimentation and has been corrected several times [4,5]. Recent research placed the Al-Ce eutectic point at 12 wt % Ce [6], while previous calculations that located the eutectic point at 17.8 wt % Ce [7].
Powder metallurgy (PM) has been an important manufacturing process to produce aluminum matrix composites [8]. One technique based on PM is the powder-in-tube (PIT), which has been used for making superconductive tape and wire, to counteract the brittleness of some materials that require a sheath for the wire extrusion process; this also helps prevent oxidation of the final product [9]. PIT method involves filling a tube of a sheath material with the powder of interest in an inert atmosphere, sealing both ends; then, the tube undergoes mechanical or thermomechanical deformation that bonds the powder to form a solid material. Further, the production methodology is convenient when working with powders and volatile material. In addition, variables such as tube material composition, compression pressure, sintering time and temperature, and heat treatment temperature and holding time, can be tailored and scaled up in a production setting.
When oxygen reactions with powders must be avoided, an alternative production methodology should be used. The present research proposes the PIT technique as a production method of an Al-Ce composite by using pure aluminum and cerium elemental powders and using 316 stainless steel tubes as sheath material. Reactive liquid phase sintering was selected for consolidating and bonding the elemental powders and solidstate sintering was selected for powders from gas atomization of homogenous melts. Both composite powders and elemental powders were placed in similar containments and underwent mechanical deformation via PIT. Since the present research requires hot processing, we anticipated a reaction between the very reactive pure Al and Ce powders with iron (Fe) and nickel (Ni) that are part of the composition of the stainless-steel sheath material [10]. Thus, an opportunity arises to determine whether there is a correlation between Ce level and possible reaction with the sheath material.

Materials and Methods
Upon the first PIT method was used for making the Al-Ce composite material ranging from 8 wt % to 14 wt % cerium. We selected liquid phase sintering because we wanted to make a composite via liquid state reaction starting from Al and Ce elemental powder, to form intermetallic reinforcements in the microstructure. Pure elemental powders (0.044 mm, 99.7% Al, 0.25 mm, 99.9% Ce, Alfa Aesar) where mixed and funneled into a commercially available 316 stainless steel 19 mm O.D. tube with a pressed-sealed end (62-72 wt % Fe, 16-18 wt % Cr, 10-14 wt % Ni, 6 wt % max others). The tube was prepared with a basic cleaning using ethanol. The procedure was made in a glove box under argon atmosphere. The open end was isolated from oxygen by placing a cap of rubber material, and out of the glove box, this end was sealed by folding in a hydraulic press. Then, the tube was compressed in a 136.07 metric ton hydraulic press. The pressed tube was placed and sealed in a capsule with argon and placed into a furnace for 30 min. Temperature for the liquid phase sintering process was 751 • C for 8% Ce, 747 • C for 10% Ce, 741 • C for 12% Ce and 771 • C for 14% Ce. The different liquid phase sintering temperatures were selected to be at least 100 • C over melting temperature of each composition, using the binary Al-Ce phase diagram [6]. Figure A1 in Appendix A shows the tubes after liquid phase sintering and polished samples after discarding the sheathing material. Polishing not only assisted in the microstructure evaluation but also removed any roughness left by the tube inside surface. Some samples were not heat treated (HT) and labeled RT (room temperature), while others were HT at 200 • C and 400 • C for 8 h.
The second methodology included the use of Al-8Ce-10Mg wt % composite powder made at Eck Industries, Inc. (Manitowoc, WI, USA) by gas atomization. The composition of this alloyed powder does not change during the experiment. All the Mg was found in solid solution. Solid-state sintering was selected to preserve the nanoscale intermetallics found in the powder. The as-provided powder was sieved; fine powder (<45 µm) and coarse powder (>45 µm) were selected. A third set was made by combining fine and coarse powder in equal weight amounts; this powder size was labeled "mixed 50-50." To fabricate Al-Ce-Mg bulk specimens we continued using the same PIT procedure as the reacted powder. The solid-state sintering process was at 450 • C for 3 h. and some samples were heat treated at 400 • C for 24 h. and 72 h. Some specimens (RT) were not heat treated. Appendix A ( Figure A2) shows in more detail the experimental flow diagram used in the PIT Al-Ce samples. In addition, the test matrix table of Al-Ce and Al-Ce-Mg is included in the said Appendix A (Tables A1 and A2).
For the elemental powder 200 • C and 400 • C were selected as Heat Treatment temperature and for the Al-8Ce-10Mg wt % 400 • C, to not affect the morphology of the intermetallics and induce only diffusion in the matrix and densification of the PIT samples. It has been reported the thermal stability of Al-Ce and Al-Ce-Mg alloys, also, that Al-Ce alloys undergo minor intermetallics changes when heat treated below 520 • C for 20 h [2].
It should be noted that this is not a comparative study of Al-Ce vs. Al-Ce-Mg PIT composites samples. Instead, this research seeks to understand the basic properties of Al-Ce-based composite materials obtained via PIT and the effects of Ce level in the properties of the resulting composites.
We used Rockwell hardness (HR) tests on the Al-Ce composites and Vickers hardness (HV) tests on the Al-Ce-Mg samples. Since the specimens made from elemental powder were more compositional modulated on a longer scale length scale, HR allows for larger indents, which are more representative of the bulk structure. Microhardness test was carried out with a Buehler Micromet III microhardness tester that applied 1.96 N for 15 s (HV 0 . 2 test). Rockwell hardness was measured using a Leco LCR-500 hardness tester with maximum load of 147.1 N with a 1/6" steel ball indenter (HR15TS test).
The Sartorius density determination kit measured the experimental density of the Al-Ce composite before and after heat treatment.
The samples mounted in epoxy and polished were carbon coated to improve their electrical conductivity for scanning electron microscopy (SEM) and optical imaging observation. SEM imaging and energy dispersive X-ray spectroscopy (EDS), performed at Oak Ridge National Laboratory, allowed quantifying the elemental composition of the specimens. A Siemens ® D500 diffractometer with Cu Kα radiation (λ =0.154178 nm) allowed acquiring the X-ray diffraction (XRD) spectra at the University of Puerto Rico-Mayagüez labs.

PIT Reacted Al and Ce Powder
PIT sample micrographs after sintering show a multiphase microstructure. Boundaries between grains can be easily observed on samples at all Ce levels ( Figure 1). Dark phases (labeled 1) in the samples are apparent and large (>50µm) in some areas. However, intermediate atomic mass phase (in grey contrast) of irregular shape (labeled 2) are across grain boundaries, whereas needle-like phases (labeled 3) are present in the samples ranging from 8 to 12 Ce wt %, but not in the hypereutectic composition (i.e., 14 wt % Ce). As expected, there is a significant difference between the microstructure of the hypoeutectic and hypereutectic Al-14Ce wt % samples. Upon further investigation, we completed an SEM micrograph analysis on hypoeutectic Ce 8 wt % and hypereutectic 14 wt % Ce specimens. Figure 2 provides a side-byside comparison of the microstructure of Al-8Ce and Al-14Ce wt % by SEM. These images reveal that at 8 wt % Ce, the microstructure developed small bright disordered phases (same phases labeled "1" in Figure 1) and needle-like one are also present. Moreover, at Ce 14 wt % only the small bright phases are visible, and the grain boundaries can be easily distinguished.  Upon further investigation, we completed an SEM micrograph analysis on hypoeutectic Ce 8 wt % and hypereutectic 14 wt % Ce specimens. Figure 2 provides a side-by-side comparison of the microstructure of Al-8Ce and Al-14Ce wt % by SEM. These images reveal that at 8 wt % Ce, the microstructure developed small bright disordered phases (same phases labeled "1" in Figure 1) and needle-like one are also present. Moreover, at Ce 14 wt % only the small bright phases are visible, and the grain boundaries can be easily distinguished. Upon further investigation, we completed an SEM micrograph analysis on hypoeutectic Ce 8 wt % and hypereutectic 14 wt % Ce specimens. Figure 2 provides a side-byside comparison of the microstructure of Al-8Ce and Al-14Ce wt % by SEM. These images reveal that at 8 wt % Ce, the microstructure developed small bright disordered phases (same phases labeled "1" in Figure 1) and needle-like one are also present. Moreover, at Ce 14 wt % only the small bright phases are visible, and the grain boundaries can be easily distinguished.  XRD patterns for PIT 14 wt % Ce sample in Figure 3 display diffraction peaks located in almost identical diffraction angles and with similar intensity values of Al FCC (ICSD:187080) and Al 11 Ce 3 [3]. In contrast, sample containing 8 wt % Ce present more peaks with a broader one at 44.8 • (2θ). This is consistent with Al FCC and Al 71 Ni 24 Fe 5 [11]. The pattern in consistent with more disordered phases that are compositionally modulated. Additional peaks are indicative of more phases present in the microstructure, i.e., Al 20 Cr 2 Ce (ICSD:236266) and Fe 3 Al [12].
J. Compos. Sci. 2021, 5, x 5 of XRD patterns for PIT 14 wt % Ce sample in Figure 3 display diffraction peaks locat in almost identical diffraction angles and with similar intensity values of Al FC (ICSD:187080) and Al11Ce3 [3]. In contrast, sample containing 8 wt % Ce present mo peaks with a broader one at 44.8° (2θ). This is consistent with Al FCC and Al71Ni24Fe5 [1 The pattern in consistent with more disordered phases that are compositionally mod lated. Additional peaks are indicative of more phases present in the microstructure, i Al20Cr2Ce (ICSD:236266) and Fe3Al [12]. EDS analysis allowed assessing the elemental composition of the different phas present in the PIT samples microstructures (Table 1). Figure 4a,b show the SEM ima displaying the selected EDS analysis points on different phases present in the Al-8Ce % sample and Al-14Ce wt. %, respectively. Figure 4c,e present the EDS spectra for ea point. The intermediate atomic mass phase labeled as spectrum 1, contained Al (68.25% Ce (18.96%), Cr (12.25%) and Ni (0.54%). The needle-shape phase labeled as spectrum contained Al (68.97%), Ni (15.92%) and Fe (15.11%). This Fe-rich needle-like phase is co sidered a detrimental phase to the properties of aluminum alloys due to local stress co centration leading to very short elongation to failure [13]. EDS identified the bright pha as mostly elemental cerium at 92.7% for Al-8Ce wt % sample and 93.3% for Al-14Ce wt ( Figure 4d). Cerium is unreacted either in the phase of stirring or in the sintering proce Using ImageJ software (version I.X.), we calculated the precipitants concentration the microstructure. The samples of Al-8Ce wt % contained in average Al-Ce mat (66.24%), intermediate atomic mass phase Al-Ce-Cr (17.16%), needle-like phase Al-Fe-(13.68%), bright Ce rich phase (1.78%) and pores (1.14%) Figure A3. For the Al-14Ce wt we calculated average concentration of precipitants as Al-Ce matrix (96.74%), Ce ri phase (2.83%) and pores (0.43%) Figure A4. EDS analysis allowed assessing the elemental composition of the different phases present in the PIT samples microstructures (Table 1). Figure 4a,b show the SEM image displaying the selected EDS analysis points on different phases present in the Al-8Ce wt % sample and Al-14Ce wt %, respectively. Figure 4c,e present the EDS spectra for each point. The intermediate atomic mass phase labeled as spectrum 1, contained Al (68.25%), Ce (18.96%), Cr (12.25%) and Ni (0.54%). The needle-shape phase labeled as spectrum 2, contained Al (68.97%), Ni (15.92%) and Fe (15.11%). This Fe-rich needle-like phase is considered a detrimental phase to the properties of aluminum alloys due to local stress concentration leading to very short elongation to failure [13]. EDS identified the bright phase as mostly elemental cerium at 92.7% for Al-8Ce wt % sample and 93.3% for Al-14Ce wt % (Figure 4d). Cerium is unreacted either in the phase of stirring or in the sintering process.
Using ImageJ software (version I.X.), we calculated the precipitants concentration in the microstructure. The samples of Al-8Ce wt % contained in average Al-Ce matrix (66.24%), intermediate atomic mass phase Al-Ce-Cr (17.16%), needle-like phase Al-Fe-Ni (13.68%), bright Ce rich phase (1.78%) and pores (1.14%) Figure A3. For the Al-14Ce wt % we calculated average concentration of precipitants as Al-Ce matrix (96.74%), Ce rich phase (2.83%) and pores (0.43%) Figure A4.   The microstructure of the Al-8Ce wt % samples after HT at 400 °C was homogenized and very different from the samples before HT ( Figure 5). During HT the Ce intermetallics form into a discrete phase that are finely distributed within domains of Al solid solution. In addition, the treatment spheroidized the Fe-Ni rich phases, as no needle-like phases are apparent in the microstructure. This finding agrees with previous research that stated that after thermal exposure the Fe-rich phases change from a needle-like shape to a finer spherical morphology [14]. The microstructure of the Al-8Ce wt % samples after HT at 400 • C was homogenized and very different from the samples before HT ( Figure 5). During HT the Ce intermetallics form into a discrete phase that are finely distributed within domains of Al solid solution. In addition, the treatment spheroidized the Fe-Ni rich phases, as no needle-like phases are apparent in the microstructure. This finding agrees with previous research that stated that after thermal exposure the Fe-rich phases change from a needle-like shape to a finer spherical morphology [14].  Table 2 shows the Rockwell hardness test (HR15TS) results for the PIT composites before and after HT. Figure 6 shows the results of Rockwell hardness test (HR) for PIT composites before and after HT. Hardness increased in all hypoeutectic samples after both HT conditions. Conversely, at 14 wt % Ce, there is no significant HR difference for the  Table 2 shows the Rockwell hardness test (HR15TS) results for the PIT composites before and after HT. Figure 6 shows the results of Rockwell hardness test (HR) for PIT composites before and after HT. Hardness increased in all hypoeutectic samples after both HT conditions. Conversely, at 14 wt % Ce, there is no significant HR difference for the heattreated composites. This is indicative of a more complete reaction processes between Al and Ce during the elevated temperature PIT process, that rendered a stable microstructure that is unchanged after HT at 200 and 400 • C. Considering that the hypoeutectic Al-8Ce wt % diffractogram revealed less crystallinity after HT, the increment in HR for this samples can be attributed to the formation of new phases and the transformation of the needle-like Fe rich phase after HT. After HT these composites had less porosity, and therefore, higher density. This finding differs from previous literature, which found that the spheroidization of the Fe rich needle-like phase after thermal exposure further negatively affects HV on Al-1.75Fe-1.25Ni wt % alloy [14]. This increment difference in our research may be due to Ce content in our samples (8 wt %) preventing the phase coarsening by diffusion upon HT. It was addressed that the Fe-Ni rich phases have a detrimental effect in the characteristics of the composite. This is proven when, after heat treatment the hardness for the Al-8Ce wt % samples improve significantly, coinciding with the disappearance of the needle-like Fe-Ni rich phases. It will be hard to address, before and after the heat treatment, the impact of the Fe-Ni-Cr, because we don't have Al-8Ce wt % processed by the same PIT method that does not contain Fe, Ni and Cr, thus we cannot make a comparison in hardness.  Experimental density (ρ) was measured from all reacted elemental PIT samples (before and after HT). Comparing with the sample before HT, there was a density increase in all heat-treated samples. The smallest difference in ρ increase was in the Al-12Ce wt % HT at 200 °C (+0.17%) and the largest on the Al-14Ce wt % HT at 400 °C (+4.31%). The changes in ρ for the heat-treated samples demonstrates the effect of the HT Table 3. Experimental density (ρ) was measured from all reacted elemental PIT samples (before and after HT). Comparing with the sample before HT, there was a density increase in all heat-treated samples. The smallest difference in ρ increase was in the Al-12Ce wt % HT at 200 • C (+0.17%) and the largest on the Al-14Ce wt % HT at 400 • C (+4.31%). The changes in ρ for the heat-treated samples demonstrates the effect of the HT Table 3. The presence of Ni and Fe rich needle-like phases in the hypoeutectic samples were the result of reaction and diffusion of atoms from the stainless-steel tube used as sheath material. It is known that pure Al (in our case, elemental Al powder) is highly reactive with stainless-steel at HT. At 14 wt % Ce, the solid-state reaction between Fe, Ni and Ce takes place at the interface during pressing (at RT) or upon sintering. The high Ce content favors the formation of the phases containing Fe and Ni at the tube/sample interface avoiding further Fe and Ni reaction with Al and Ce powder inside the samples (Figure 7).

PIT Al-8Ce-10Mg wt % Composite Powder
Micrographs of sample of atomized Al-8Ce-10Mg wt % coarse powder before extrusion is shown in Figure 8, where the inset shows in detail the nanoscaled intermetallics in the composite. The microstructure of Al-8Ce-10Mg wt % PIT composites made with all powder sizes, before and after HT is shown in Figure 9. There is no visible difference in

PIT Al-8Ce-10Mg wt % Composite Powder
Micrographs of sample of atomized Al-8Ce-10Mg wt % coarse powder before extrusion is shown in Figure 8, where the inset shows in detail the nanoscaled intermetallics in the composite. The microstructure of Al-8Ce-10Mg wt % PIT composites made with all powder sizes, before and after HT is shown in Figure 9. There is no visible difference in microstructure before and after HT at 400 • C for 24 and 72 h. Similar results can be observed on samples made of Al-Ce-Mg coarse and mixed 50-50 powder, where the microstructure does not seem to achieve better densification (less porosity) after HT.  There is a correlation between HT, holding time and HV results ( Figure 10). All powder size samples showed higher HV values after heat treatment for 24 h. This increment was even larger after HT for 72 h. for the fine powder samples. The larger difference in HV increment on the fine and coarse powder samples is due to the preservation of phases  There is a correlation between HT, holding time and HV results ( Figure 10). All powder size samples showed higher HV values after heat treatment for 24 h. This increment was even larger after HT for 72 h. for the fine powder samples. The larger difference in HV increment on the fine and coarse powder samples is due to the preservation of phases There is a correlation between HT, holding time and HV results ( Figure 10). All powder size samples showed higher HV values after heat treatment for 24 h. This increment was even larger after HT for 72 h. for the fine powder samples. The larger difference in HV increment on the fine and coarse powder samples is due to the preservation of phases in the microstructure and better densification that occurred after HT. Mixed 50-50 samples revealed the best densification of all powder conditions before heat treatment. As a result, the microstructure characteristics were retained, and densification did not change appreciably after HT. Thus, the difference in HV before and after heat treatment is not significant for these mixed 50-50 powder samples. the microstructure characteristics were retained, and densification did not change appreciably after HT. Thus, the difference in HV before and after heat treatment is not significant for these mixed 50-50 powder samples.

Conclusions
The present research proposes powder-in-tube as an alternative processing method for Al-Ce and Al-8Ce-10Mg wt % composites starting from reacted and composite powders, respectively. For reacted Al-Ce powders, the PIT process works partially, because the Al-Ce reaction has not completed. Even though distribution of Al-Ce phases occurred, some pure Ce particles were retained in the Al-14Ce wt % composite. Reacted Al-Ce powder via PIT presented porosity, indicating that higher pressure before sintering may be required for better densification.
Hypoeutectic Al-8Ce wt % composition show needle-like phases that are confirmed by SEM/EDS analysis to be Fe and Ni-rich phases. On the other hand, the hypereutectic Al-14Ce wt % composite did not present these phases. We attributed this to the high Ce content causing the formation of stable Ce-Fe and Ce-Ni intermetallics at the interface between the samples and the stainless-steel sheath. We found that Ce levels affect the Fe reactivity with Al. These intermetallics protected the samples by preventing further reaction between Al-Fe and Al-Ni inside the material. PIT process is self-limiting: The Ce level needs to be over 14 wt % to avoid the reaction with the sheathing material.
Al-Ce reacted powder PIT composites at hypoeutectic Ce level presented better densification after heat treatment resulting in higher hardness. For 8wt % Ce, this can be attributed to dissolution of the needle-like Fe rich phases. This finding disagrees with the surveyed literature, which reported that the spheroidization of the Fe rich needle-like phase after thermal exposure lowered the HV, e.g., of Al-1.75Fe-1.25Ni wt % alloys. In our research, the difference may be due to the Ce content in the samples preventing the coarsening of the material after HT.
The Al-8Ce-10Mg wt % composite mixed 50-50 powder samples had better densification, less porosity and higher HV values. In fact, all powder sizes led to steeper HV values after HT, the highest being mixed 50-50 powder samples bearing an HV0.2 = 123.8 after HT for 72 h.
Microstructural stability of fine structure in Al-Ce specimens can be retained after thermomechanical processing at elevated temperatures above 700 °C used in PIT liquid phase sintering and 400 °C HT to yield a bulk fine structured composite. Nanostructuring

Conclusions
The present research proposes powder-in-tube as an alternative processing method for Al-Ce and Al-8Ce-10Mg wt % composites starting from reacted and composite powders, respectively. For reacted Al-Ce powders, the PIT process works partially, because the Al-Ce reaction has not completed. Even though distribution of Al-Ce phases occurred, some pure Ce particles were retained in the Al-14Ce wt % composite. Reacted Al-Ce powder via PIT presented porosity, indicating that higher pressure before sintering may be required for better densification.
Hypoeutectic Al-8Ce wt % composition show needle-like phases that are confirmed by SEM/EDS analysis to be Fe and Ni-rich phases. On the other hand, the hypereutectic Al-14Ce wt % composite did not present these phases. We attributed this to the high Ce content causing the formation of stable Ce-Fe and Ce-Ni intermetallics at the interface between the samples and the stainless-steel sheath. We found that Ce levels affect the Fe reactivity with Al. These intermetallics protected the samples by preventing further reaction between Al-Fe and Al-Ni inside the material. PIT process is self-limiting: The Ce level needs to be over 14 wt % to avoid the reaction with the sheathing material.
Al-Ce reacted powder PIT composites at hypoeutectic Ce level presented better densification after heat treatment resulting in higher hardness. For 8 wt % Ce, this can be attributed to dissolution of the needle-like Fe rich phases. This finding disagrees with the surveyed literature, which reported that the spheroidization of the Fe rich needle-like phase after thermal exposure lowered the HV, e.g., of Al-1.75Fe-1.25Ni wt % alloys. In our research, the difference may be due to the Ce content in the samples preventing the coarsening of the material after HT.
The Al-8Ce-10Mg wt % composite mixed 50-50 powder samples had better densification, less porosity and higher HV values. In fact, all powder sizes led to steeper HV values after HT, the highest being mixed 50-50 powder samples bearing an HV 0 . 2 = 123.8 after HT for 72 h.
Microstructural stability of fine structure in Al-Ce specimens can be retained after thermomechanical processing at elevated temperatures above 700 • C used in PIT liquid phase sintering and 400 • C HT to yield a bulk fine structured composite. Nanostructuring Al-Ce-based material is possible and understanding the processing methodology and its effect on the properties of the material is necessary. This study indicates that the PIT processing methodology is highly compatible with Al-Ce based composites due to the stability of fine microstructure during thermomechanical processing and high temperature HT.