Studies of Effects of Calcination Temperature on the Crystallinity and Optical Properties of Ag-Doped ZnO Nanocomposites

Ag-doped ZnO nanocomposites are successfully synthesized at different calcination temperatures and times through a simple, effective, high-yield and low-cost mechanochemical combustion technique. Effects of calcination temperature on the crystallinity and optical properties of Ag/ZnO nanocomposites have been studied by X-ray diffraction (XRD), UV−visible diffuse reflectance spectroscopy (UV-DRS), photoluminescence spectroscopy (PL) and X-ray photoelectron spectroscopy (XPS). The XRD patterns of the synthesized Ag/ZnO exhibit a well-crystalline wurtzite ZnO crystal structure. The grain size of Ag/ZnO nanocomposites is found to be 19 and 46 nm at calcination temperatures of 400 ◦C and 700 ◦C, respectively. The maximum absorption in the UV region is obtained for Ag/ZnO nanocomposites synthesized at a calcination temperature of 500 ◦C for 3 h. The peak position of blue emissions is almost the same for the nanocomposites obtained at 300–700 ◦C calcination temperatures. The usual band edge emission in the UV is not obtained at 330 nm excitation. Band edge and blue band emissions are observed for the use of low excitation energy at 335–345 nm.


Introduction
Nano-sized semiconductors are of great interest because of their extraordinary physicochemical properties, which differ from their bulk counterparts [1].Zinc oxide (ZnO) is a wide direct band-gap (3.2 eV) semiconductor with large exciton binding energy of 60 meV at room temperature [2].ZnO also has excellent optical and electrical properties, catalytic activity, chemical stability as well as environmental friendliness [3].The n-type ZnO semiconductor has higher electron mobility, high breakdown voltages and higher breakdown field strength [4].Zinc oxide is promising for applications including gas sensors, memory devices, UV-light emitting diodes, solar cells, piezoelectric transducers, photodiodes, photodetectors and photocatalysts [5][6][7].In addition, modified ZnO has also been used as transparent conducting electrodes for several types of optoelectronic devices [2].
Fabrication of efficient devices based on semiconductor nanostructures requires an in-depth understanding of their optoelectronic behaviors, which depend on their shape, size and impurity contents.Due to the vast optoelectronic applications of ZnO nanostructures, several theoretical and experimental studies have been conducted on the optical properties of ZnO nanostructures with

Chemicals and Materials
Zinc acetate dehydrate (C 4 H 6 O 4 Zn•2H 2 O), oxalic acid dehydrate (C 2 H 2 O 4 •2H 2 O), silver acetate (C 2 H 3 O 2 Ag) and pure water (resistivity >18 MΩ cm) were used for the synthesis of the sample.All the reagents were of analytical grade and used without further purification.

Preparation of Ag/ZnO
Ag/ZnO was prepared by the mechanochemical combustion technique with controlled combustion method (Figure 1).In a typical synthesis, 2.195 g of zinc acetate dihydrate and 2.521 g of oxalic acid dihydrate were taken in agate mortar and the mixture was ground for 10 min in order to obtain a paste of zinc oxalate dihydrate and acetic acid.The existence of acetic acid was confirmed by its typical smell.The loss of acetic acid byproduct in the form of fumes became a driving force for the reaction.Silver acetate was added to the above paste as a source of silver, and the grinding process was continued for the next 10 min to obtain zinc oxalate-silver oxalate precursor.The Ag doped zinc oxide crystallites were obtained by calcination of precursor powders at the temperature of 300−700 • C under an air atmosphere.The undoped ZnO was also synthesized by calcination of a paste of zinc oxalate and acetic acid for the comparison.

Characterization of Ag/ZnO
The powder X-ray diffractometer (XRD, RIGAKU Ultima IV, sample horizontal type) was used in order to record the diffraction patterns of photocatalysts employing Cu Kα radiation of wavelength 0.15406 nm with tube current of 50 mA at 40 kV in 2θ angle range from 10° to 80° with a scan speed of 4°/min and a step size of 0.02°.A Hitachi S-4000 scanning electron microscope (SEM) was employed to observe the morphologies of oxides.The particle size was measured by

Characterization of Ag/ZnO
The powder X-ray diffractometer (XRD, RIGAKU Ultima IV, sample horizontal type) was used in order to record the diffraction patterns of photocatalysts employing Cu Kα radiation of wavelength 0.15406 nm with tube current of 50 mA at 40 kV in 2θ angle range from 10 • to 80 • with a scan speed of 4 • /min and a step size of 0.02 • .A Hitachi S-4000 scanning electron microscope (SEM) was employed to observe the morphologies of oxides.The particle size was measured by transmission electron microscopy (TEM, JEOL, JEM−1011, Peabody, MA, USA) working at 100 kV.The diffuse reflectance spectra (DRS) of photocatalysts were recorded over a range of 200−800 nm with a Shimadzu UV-2450 UV/vis system equipped with an integrating sphere diffuse reflectance accessory using the reference material BaSO 4 as a reference standard material.Photoluminescence (PL) spectra of oxide powders were measured at room temperature using a Shimadzu RF-5300PC system equipped with solid sample holder.X-ray photoelectron spectroscopy (XPS) measurements were carried out with PHI Quantera SXM photoelectron spectrometer using Al Kα radiation.220) and (311) planes of face-center-cubic (fcc) structure of Ag (JCPDS card no.04-783), respectively [21].The half peak widths of the characteristic peaks gradually reduce with increasing calcination temperatures.This fact suggests that ZnO particle sizes increase with increasing calcination temperature.The diffraction intensities and angles of Ag do not significantly change with increasing calcination temperatures.The grain size of the Ag-doped ZnO have been obtained from the full width at half maximum (FWHM) of the most intense peaks of the respective crystals using the Scherrer equation, D = 0.9λ/βcosθ, where λ is the X-ray wavelength, D the average crystallite size, θ the Bragg diffraction angle and β the full width at half-maximum.The grain size is found to be 19 and 46 nm at calcination temperatures of 400 °C and 700 °C, respectively.Potti and Srivastava have also reported that the crystallite size of the oxides expanded with increasing the calcination temperatures [22].

Structural Analysis
The Figure 3   The half peak widths of the characteristic peaks gradually reduce with increasing calcination temperatures.This fact suggests that ZnO particle sizes increase with increasing calcination temperature.The diffraction intensities and angles of Ag do not significantly change with increasing calcination temperatures.The grain size of the Ag-doped ZnO have been obtained from the full width at half maximum (FWHM) of the most intense peaks of the respective crystals using the Scherrer equation, D = 0.9λ/βcosθ, where λ is the X-ray wavelength, D the average crystallite size, θ the Bragg diffraction angle and β the full width at half-maximum.The grain size is found to be 19 and 46 nm at calcination temperatures of 400 • C and 700 • C, respectively.Potti and Srivastava have also reported that the crystallite size of the oxides expanded with increasing the calcination temperatures [22].
The Figure 3 illustrates XRD analysis of Ag/ZnO at different calcination times from 0.5 h to 4 h.The diffraction intensities and angles of ZnO and Ag does not remarkably shift with increasing calcination time.
The half peak widths of the characteristic peaks gradually reduce with increasing calcination temperatures.This fact suggests that ZnO particle sizes increase with increasing calcination temperature.The diffraction intensities and angles of Ag do not significantly change with increasing calcination temperatures.The grain size of the Ag-doped ZnO have been obtained from the full width at half maximum (FWHM) of the most intense peaks of the respective crystals using the Scherrer equation, D = 0.9λ/βcosθ, where λ is the X-ray wavelength, D the average crystallite size, θ the Bragg diffraction angle and β the full width at half-maximum.The grain size is found to be 19 and 46 nm at calcination temperatures of 400 °C and 700 °C, respectively.Potti and Srivastava have also reported that the crystallite size of the oxides expanded with increasing the calcination temperatures [22].
The Figure 3 illustrates XRD analysis of Ag/ZnO at different calcination times from 0.5 h to 4 h.The diffraction intensities and angles of ZnO and Ag does not remarkably shift with increasing calcination time.

Morphology study
Figure 4 displays SEM and TEM micrographs of the Ag/ZnO synthesized at the calcination temperature at 500 °C for 3 h.From the Figure 4, it is seen that the Ag/ZnO is heterogeneous in nature and distributed over the surface with the rod-shaped branches of building blocks.The average size of the particles is in the nanometer range, which is consistent with the XRD results.

Diffuse Reflectance Spectroscopic (DRS) Spectra
The spectra of Ag-doped ZnO samples are measured by UV-diffuse reflectance spectroscopy.The absorption peaks at the UV region correspond to the absorption of ZnO.The zinc oxide-silver nanocomposites display strong absorption in the UV region and weak absorption in the visible region, which is related to the ZnO bands and surface plasmon resonance (SPR) bands of Ag nanoparticles, respectively [23,24].The optical property of Ag/ZnO nanocomposites synthesized at different calcination temperatures has been studied by DRS (Figure 5a).The largest absorbance for all the nanocomposites is in the UV-region, whereas the Ag/ZnO nanocomposite prepared at a calcination temperature of 500 °C shows the maximum absorption.
The reflectance data has been converted to the Kubelka−Munk equation which is expressed as

Diffuse Reflectance Spectroscopic (DRS) Spectra
The spectra of Ag-doped ZnO samples are measured by UV-diffuse reflectance spectroscopy.The absorption peaks at the UV region correspond to the absorption of ZnO.The zinc oxide-silver nanocomposites display strong absorption in the UV region and weak absorption in the visible region, which is related to the ZnO bands and surface plasmon resonance (SPR) bands of Ag nanoparticles, respectively [23,24].The optical property of Ag/ZnO nanocomposites synthesized at different calcination temperatures has been studied by DRS (Figure 5a).The largest absorbance for all the nanocomposites is in the UV-region, whereas the Ag/ZnO nanocomposite prepared at a calcination temperature of 500 • C shows the maximum absorption.The effect of different calcination times on the optical properties of Ag/ZnO is investigated by DRS (Figure 6a).The best absorption intensity of an Ag/ZnO composite is obtained for 3 h of calcination time.The Tauc plots are shown in Figure 6b.

Photoluminescence Study
The room temperature photoluminescence (PL) spectra of Ag/ZnO are recorded over the wavelength range 350−600 nm. Figure 7 present the PL of Ag/ZnO synthesized at different calcination temperatures.In the PL spectra for ZnO, typically there are emission bands in the ultraviolet (UV) and visible (green, yellow, blue and violet) regions [28].The Ag/ZnO composite shows a strong emission peak at around 389 nm in the UV region, which is attributed to near band edge emission and also related to the electron-hole charge recombination process [29].The weak emission at 400-600 nm corresponds to intrinsic or extrinsic defects in ZnO and oxygen vacancies.It is estimated that the blue band emission is due to the transition from extended interstitial Zn states to the valence band [30].The peak position of the blue emissions is almost the same for the samples obtained at 300-700 °C calcination temperatures and the usual band edge emission is not obtained at the high excitation energy (330 nm) for Ag/ZnO (Figure 7a).The band edge and blue band emissions are observed for the use of low excitation energy at 335-345 nm, as presented in Figures 7 (b-d).The The reflectance data has been converted to the Kubelka−Munk equation which is expressed as F(R) = (1 − R) 2 /2R.The band gap of the oxides is deduced from the Tauc plot of [F(R)hν] 2 versus photon energy.The Tauc plots are shown in Figure 5b.A slight decrease in the band gap of Ag/ZnO is obtained at the 500 • C calcination temperature, compared with those observed at other temperatures.The conduction and valence band positions of the semiconductor at the point of zero charge can be calculated by the following formula [25,26]: where E VB is the potential of the valence band, χ is the electronegativity of the semiconductor.The electronegativity value for Ag/ZnO is 5.79 eV [27].The E e is the energy of free electrons on the hydrogen scale (4.5 eV) and E g is the band gap energy of the Ag/ZnO nanocomposites (3.24 eV).The E VB and E CB of Ag/ZnO prepared at the calcination temperature of 500 • C are 2.91 and -0.33 eV, respectively.The effect of different calcination times on the optical properties of Ag/ZnO is investigated by DRS (Figure 6a).The best absorption intensity of an Ag/ZnO composite is obtained for 3 h of calcination time.The Tauc plots are shown in Figure 6b.The effect of different calcination times on the optical properties of Ag/ZnO is investigated by DRS (Figure 6a).The best absorption intensity of an Ag/ZnO composite is obtained for 3 h of calcination time.The Tauc plots are shown in Figure 6b.

Photoluminescence Study
The room temperature photoluminescence (PL) spectra of Ag/ZnO are recorded over the wavelength range 350−600 nm. Figure 7 present the PL of Ag/ZnO synthesized at different

Photoluminescence Study
The room temperature photoluminescence (PL) spectra of Ag/ZnO are recorded over the wavelength range 350−600 nm. Figure 7 present the PL of Ag/ZnO synthesized at different calcination temperatures.In the PL spectra for ZnO, typically there are emission bands in the ultraviolet (UV) and visible (green, yellow, blue and violet) regions [28].The Ag/ZnO composite shows a strong emission peak at around 389 nm in the UV region, which is attributed to near band edge emission and also related to the electron-hole charge recombination process [29].The weak emission at 400-600 nm corresponds to intrinsic or extrinsic defects in ZnO and oxygen vacancies.It is estimated that the blue band emission is due to the transition from extended interstitial Zn states to the valence band [30].The peak position of the blue emissions is almost the same for the samples obtained at 300-700 • C calcination temperatures and the usual band edge emission is not obtained at the high excitation energy (330 nm) for Ag/ZnO (Figure 7a).The band edge and blue band emissions are observed for the use of low excitation energy at 335-345 nm, as presented in Figure 7b-d.The near band edge is weak at 330 nm excitation due to low the exciton recombination and strong near band edge is observed on excitation at 340 nm due to the high exciton transition from the localized level below the conduction band to the valence band.near band edge is weak at 330 nm excitation due to low the exciton recombination and strong near band edge is observed on excitation at 340 nm due to the high exciton transition from the localized level below the conduction band to the valence band.Figure 8 present the PL of Ag/ZnO synthesized at different calcination times.The peak positions of the blue emissions are almost the same for the composites obtained for calcination times (Figure 8).The usual band edge emission in the UV region cannot be obtained at 330 nm excitation (Figure 8a).At excitation energies of 335-345 nm, the usual band edge and deep-level emission in the blue band can be seen, as shown in Figures 8 (b-d).
The dependence of the intensity of UV and blue emissions on calcination temperatures can be clearly associated in Figure 9a.The rapid increases of intensity at 390 nm and 467 nm using 340 nm excitation are well demonstrated with increasing calcination temperatures.Figure 9b shows the calcination times dependence of the intensity of UV and blue emissions using 340 nm excitation for Ag/ZnO.The blue emissions intensity at 468 nm is almost flat for all of calcination times.Figure 8 present the PL of Ag/ZnO synthesized at different calcination times.The peak positions of the blue emissions are almost the same for the composites obtained for calcination times (Figure 8).The usual band edge emission in the UV region cannot be obtained at 330 nm excitation (Figure 8a).At excitation energies of 335-345 nm, the usual band edge and deep-level emission in the blue band can be seen, as shown in Figure 8b-d

X-Ray Photoelectron Spectroscopic (XPS) Spectra
XPS is a sensitive technique for investigating the chemical composition of the surface of a material.The surface compositions and chemical states of the pure ZnO are determined by XPS. Figure 10a displays the fully scanned spectrum of ZnO synthesized at a calcination temperature of 500 °C for 3 h.In Figure 10b, the peak of Zn 2p1/2 and Zn 2p3/2 is located at 1044.1 and 1021.0 eV, respectively [31].At 373.6 eV (Ag 3d3/2) and 367.6 eV (Ag 3d5/2), the peaks are not detected in undoped ZnO (Figure 10c) [32].The O1s spectra of ZnO are shown in Figure 10d.The 529.6 eV peak belongs to the crystal lattice oxygen (OL) in ZnO, while the 531.2 eV peak can be assigned to the oxygen of surface hydroxyl (OH) on the catalyst surface [33].The dependence of the intensity of UV and blue emissions on calcination temperatures can be clearly associated in Figure 9a.The rapid increases of intensity at 390 nm and 467 using 340 nm excitation are well demonstrated with increasing calcination temperatures.Figure 9b shows the calcination times dependence of the intensity of UV and blue emissions using 340 nm excitation for Ag/ZnO.The blue emissions intensity at 468 nm is almost flat for all of calcination times.

X-Ray Photoelectron Spectroscopic (XPS) Spectra
XPS is a sensitive technique for investigating the chemical composition of the surface of a material.The surface compositions and chemical states of the pure ZnO are determined by XPS. Figure 10a displays the fully scanned spectrum of ZnO synthesized at a calcination temperature of 500 °C for 3 h.In Figure 10b, the peak of Zn 2p1/2 and Zn 2p3/2 is located at 1044.1 and 1021.0 eV, respectively [31].At 373.6 eV (Ag 3d3/2) and 367.6 eV (Ag 3d5/2), the peaks are not detected in undoped ZnO (Figure 10c) [32].The O1s spectra of ZnO are shown in Figure 10d.The 529.6 eV peak

X-Ray Photoelectron Spectroscopic (XPS) Spectra
XPS is a sensitive technique for investigating the chemical composition of the surface of a material.The surface compositions and chemical states of the pure ZnO are determined by XPS.
Figure 10a displays the fully scanned spectrum of ZnO synthesized at a calcination temperature of 500 • C for 3 h.In Figure 10b, the peak of Zn 2p 1/2 and Zn 2p 3/2 is located at 1044.1 and 1021.0 eV, respectively [31].At 373.6 eV (Ag 3d 3/2 ) and 367.6 eV (Ag 3d 5/2 ), the peaks are not detected in undoped ZnO (Figure 10c) [32].The O1s spectra of ZnO are shown in Figure 10d.The 529.6 eV peak belongs to the crystal lattice oxygen (O L ) in ZnO, while the 531.2 eV peak can be assigned to the oxygen of surface hydroxyl (O H ) on the catalyst surface [33].Figure 11a show the scan survey spectra for the representative Ag/ZnO synthesized at the calcination temperature at 500 °C for 3 h.All of the peaks on the curve can be ascribed to Ag, Zn and O elements and no peaks of other elements were observed (Figure 11).Therefore, the sample is composed of Ag, Zn and O only and these results are agreement with the XRD patterns.The positions of Zn 2p3/2 peak for Ag/ZnO nanocomposites (Figure 11b) are nearly same value, compared with that of the prepared undoped ZnO nanoparticles, which confirms that Zn element exists mainly in the form of the Zn 2+ chemical state on the sample surfaces.The difference between the two bonding energies of Zn 2p1/2 and Zn 2p3/2 for Ag/ZnO samples is 23.1 eV, which also suggests that the Zn is in a +2 oxidation state [34].Figure 11c illustrates the Ag 3d XPS spectra for Ag/ZnO samples.The difference between the peaks of Ag 3d5/2 and 3d3/2 is 6.0 eV, indicates the presence of metallic Ag [35].The high-resolution spectra of O 1s are shown in Figure 11d.O 1s profile is asymmetric, which can be attributed to the lattice oxygen of ZnO and physical adsorbed oxygen, respectively [34].Patil et al. have mentioned only OL in the O 1s spectrum of the Ag-ZnO sample at a binding energy of 529.75 eV [36].The data is similar to our synthesized Ag/ZnO nanocomposites and no OH peak is present at the binding energy of about 531.2 eV (Figure 11d).Figure 11a show the scan survey spectra for the representative Ag/ZnO synthesized at the calcination temperature at 500 • C for 3 h.All of the peaks on the curve can be ascribed to Ag, Zn and O elements and no peaks of other elements were observed (Figure 11).Therefore, the sample is composed of Ag, Zn and O only and these results are agreement with the XRD The positions of Zn 2p 3/2 peak for Ag/ZnO nanocomposites (Figure 11b) are nearly same value, compared with that of the prepared undoped ZnO nanoparticles, which confirms that Zn element exists mainly in the form of the Zn 2+ chemical state on the sample surfaces.The difference between the two bonding energies of Zn 2p 1/2 and Zn 2p 3/2 for Ag/ZnO samples is 23.1 eV, which also suggests that the Zn is in a +2 oxidation state [34].Figure 11c illustrates the Ag 3d XPS spectra for Ag/ZnO samples.The difference between the peaks of Ag 3d 5/2 and 3d 3/2 is 6.0 eV, indicates the presence of metallic Ag [35].The high-resolution spectra of O 1s are shown in Figure 11d.O 1s profile is asymmetric, which can be attributed to the lattice oxygen of ZnO and physical adsorbed oxygen, respectively [34].Patil et al. have mentioned only O L in the O 1s spectrum of the Ag-ZnO sample at a binding energy of 529.75 eV [36].The data is similar to our synthesized Ag/ZnO nanocomposites and no O H peak is present at the binding energy of about 531.2 eV (Figure 11d).

Figure 1 .
Figure 1.Schematic representation of the synthesis process of Ag/ZnO.

Figure 1 .
Figure 1.Schematic representation of the synthesis process of Ag/ZnO.

Figure 2 .
Figure 2. X-ray diffraction patterns of ZnO and Ag/ZnO synthesized at different calcination temperatures.

Figure 2 .
Figure 2. X-ray diffraction patterns of ZnO and Ag/ZnO synthesized at different calcination temperatures.

Figure 3 .
Figure 3. XRD patterns of Ag/ZnO synthesized at different calcination times.

Figure 3 .
Figure 3. XRD patterns of Ag/ZnO synthesized at different calcination times.

Figure 4 displays
Figure 4 displays SEM and TEM micrographs of the Ag/ZnO synthesized at the calcination temperature at 500 • C for 3 h.From the Figure4, it is seen that the Ag/ZnO is heterogeneous in nature and distributed over the surface with the rod-shaped branches of building blocks.The average size of the particles is in the nanometer range, which is consistent with the XRD results.
Figure 8  present the PL of Ag/ZnO synthesized at different calcination times.The peak positions of the blue emissions are almost the same for the composites obtained for calcination times (Figure8).The usual band edge emission in the UV region cannot be obtained at 330 nm excitation (Figure8a).At excitation energies of 335-345 nm, the usual band edge and deep-level emission in the blue band can be seen, as shown in Figure8b-d.

Figure 9 .
Figure 9. Changes of relative intensity with (a) different calcination temperatures and (b) different calcination times.

Figure 9 .
Figure 9. Changes of relative intensity with (a) different calcination temperatures and (b) different calcination times.

Figure 9 .
Figure 9. Changes of relative intensity with (a) different calcination temperatures and (b) different calcination times.

Intensity (a.u.) 2θ (degree)
illustrates XRD analysis of Ag/ZnO at different calcination times from 0.5 h to 4 h.The diffraction intensities and angles of ZnO and Ag does not remarkably shift with increasing calcination time.