Development of Concrete Incorporating Recycled Aggregates, Hydrated Lime and Natural Volcanic Pozzolan

: Recycling of construction and demolition waste is a central point of discussion throughout the world. The application of recycled concrete as partial replacement of mineral aggregates in concrete mixes is one of the alternatives in the reduction of pollution and savings in carbon emissions. The combined inﬂuence of the recycled crushed concrete, lime, and natural pozzolana on the mechanical and sustainable properties of concrete materials is ﬁrstly proposed in this study. In this research, unconventional construction materials are employed to produce concrete: the recycled crushed concrete is used as coarse aggregate, while lime and natural pozzolana are used as a partial replacement for cement. Substitutions of 10%, 20%, 50% of gravel are made with recycled aggregates, and 2%, 5%, 10% of cement with lime and natural pozzolan. Tests on the fresh and hardened properties, destructive (compressive strength) and non-destructive tests (sclerometer rebound and ultrasound) of mixtures are carried out. It is shown that the use of recycled materials can provide an increase in compressive strength of up to 34% with respect to conventional concrete. Life cycle cost and sustainability assessments indicate that concrete materials incorporating recycled aggregate possess good economic and environmental impacts.


Introduction
Interactions between concrete materials and alternative fillers such as hydrated lime and natural pozzolana have been investigated in the past decades [1,2]. With the former, it provides compacting capabilities to concrete since its particles are finer than those of conventional cement [2]. The addition of hydrated lime increases the mechanical strengths and ductility of concrete mixes at the same time. For the latter, pozzolana is a siliceous material that is reactive in the presence of water and calcium hydroxide [3]. The reaction products of pozzolanas and alkali solutions possess cementitious properties, leading to lowpermeability concrete which has high durability and improvement in resistance to chemical attacks. Pozzolans correspond to materials that are also used as an alternative component to elaborate Portland cement [4]. By using hydrated lime and natural pozzolana materials with crushed recycled aggregates, it will generate an improvement in the mix design [5]. By making concrete with partial dosages of recycled aggregates concrete (RAC) [6,7], lime, and natural volcanic pozzolan, it is expected to obtain more sustainable concretes for use in civil engineering projects [8]. The elaboration of concrete with recycled aggregates, lime, and natural pozzolana faces the search for optimal dosages to achieve the highest mechanical performance and thus comply with the phases and tests applied for its responsible use in civil works.
The application of recycled concrete as a partial or complete replacement of natural mineral aggregates in concrete mixes has drawn significant research interests in the past few decades. Recent research points to a processing value of 25,000 million tons per year, which is equivalent to about 6000 million trucks of mortar per day [9]. Studies have pointed out that the use of recycled concrete comes with the intervention of recycled aggregates that in their composition will differ from natural aggregates, mainly since they will demonstrate an increase in water absorption, lower resistance, lower density, lower hardness, and these properties they will directly affect the new concrete in question [9][10][11]. Standardised guidance, such as ASTMD692, has also included crushed concrete as part of coarse aggregates accepted for its construction use fulfilling the due specifications [12]. Previous studies have also reported that the recycled aggregates of crushed concrete consist of 70% by volume of natural original aggregate and 30% by volume of cementitious mass [13].
As discussed, partial replacement of mineral aggregates with recycled concrete aggregates (RA) leads to the potential reduction in mechanical properties and fresh properties of concrete mixes [9,10]. It has been shown that the reduction in the mechanical strength is a function of the amount of RCA used [14,15]. Regardless of the reduction in mechanical strengths, studies have also reported that due to the lower density of RA compared to natural aggregate, RA shows a clear advantage in the application of lightweight concrete [16]. Detailed studies have also shown that the sources of RA have a clear influence on the mechanical properties of concrete mixes. RA from high strength concrete processes low water absorption and behaves similar to natural aggregates. Whereas concrete mixes using RCA from low strength concrete with high water absorption show lower elastic modulus [15].
Studies on the performance of concrete structural members using RA have also been reported in the past decades. It is shown that with the increase of RA content, the loadbearing capacities of RAC members decrease accordingly, while the failure mechanisms of RAC structural beams, columns, and slabs are the same as those with conventional concrete, and the behaviour of reinforcement and stirrups are also comparable to those in conventional reinforced concrete members [17][18][19]. Studies on the hysteretic behaviour indicate that the energy dissipation capacity of RAC members is lower than that of conventional RC members [17]. Although the addition of RAC causes the reduction of yielding and ultimate strengths of structures under seismic loads, the reduction is proved to be less than that of the mechanical properties of RAC materials. In addition, the energy dissipation and stiffness degradation properties of RAC members are also comparable to reinforced concrete structures [17,20,21]. It can be noted that although the replacement of natural aggregates with RA causes the strength reductions of reinforced concrete structural members, the RAC structural performance under static and seismic loadings are both comparable to conventional RC members.
Studies have also focused on the enhancement in binding properties of cement and recycled aggregates [22][23][24]. Although previous studies have shown that lime and pozzolana can be regarded as reactive binders to improve the strengths and durability of concrete materials, and the mechanical properties of recycled concrete have been reported in the literature, the combination of recycled aggregate and these fillers received limited research attention even though they can provide enhanced strengths and sustainability of concrete materials. Moreover, due to the little practice with this recycled material in Ecuador, detailed studies on the properties of concrete materials incorporating natural lime and pozzolana are limited.
To this end, a series of experimental investigations are proposed in this study to examine the performance of concrete materials incorporating recycled aggregates and a range of the amount of hydrated lime and natural volcanic pozzolan. As a collection process for this project, discarded concrete cylinders from the university lab were used as recycled concrete aggregate. Slump tests and mechanical strength tests are performed to evaluate the influence of the above-mentioned binders and recycled aggregates on concrete materials. The combined influence of recycled aggregate, lime, and pozzolan on the mechanical properties of concrete mixes are investigated, while the mix design of RAC with alternative binders is also proposed based on the experimental findings. The outcomes provide key information on the fundamental properties of the sustainable concrete material and potential ways of reducing the environmental impact caused by the manufacturing of conventional concrete.

Materials and Methods
The recycled concrete material described in this paper contains Portland Cement, lime, and volcanic pozzolana as binders. Aside from binders, the mixes included Anropevi sand as fine aggregate, limestone with the maximum aggregate size of 19 mm, and recycled crush concrete. The latter material was obtained from the crushing of cylinders in the laboratory.
The properties of pozzolans depend on their chemical composition and structure. They mainly have three oxides: silicic oxide (SiO 2 ), aluminium oxide (Al 2 O 3 ), and ferric oxide (Fe 2 O 3 ). The chemical analysis of the pozzolan employed in this research work fulfils the specifications of the ASTM C-618 [25]. There it states that that the minimum content of the total components of silicic oxide, aluminium oxide, and ferric oxide should be at least 70%. For this analysis, the pozzolana employed has a content of 80%.
The pozzolana can be described by its colour. This can generally be greyish or brown, depending on the origin and the concentrations of silicon oxides. There are also other types of natural colours such as red or black due to the presence of other oxides. For its part, the particle size depends on the origin and the grinding that is carried out on the material.
Another typical material added to the concrete is limestone. Calcium carbonate comprises most of the limestone, which at temperatures around 900 • C decomposes and forms the oxide of lime and carbon dioxide. When the lime is hydrated, it mixes with water to generate calcium hydroxide. During this process of converting the lime, the material is heated. This is why it expands, and it is converted into a very fine powder. This powder is ready to be used as cement in construction. The results obtained from the analyses of this powder from the producer were compared with the established materials from the standards [26,27], where the chemical analysis in the X-ray refractometer is showing 80.32% of CaO.
The chemical characteristics of this compound are detailed below as stated by some researchers and the technical sheet from the manufacturer:

•
May react with strong acids generating carbon dioxide. • Colour: white when they are pure, but changes colour between grey and black because of the carbonaceous impurities they contain. The cement used in the mix design has the following properties (Table 1and Table 2).  The details such as the origin of the materials used in this study are listed in Table 3.  The details such as the origin of the materials used in this study are listed in Table 3.  The details such as the origin of the materials used in this study are listed in Table 3.  The details such as the origin of the materials used in this study are listed in Table 3.  The details such as the origin of the materials used in this study are listed in Table 3.  A previous step to the design of the concrete mix was to perform the granulometric analysis of the materials involved, such as the sieving analysis, rodded volumetric weight, loose volumetric weight, dry surface density, absorption, humidity, fineness modulus. In the granulometric analysis [28] for the materials is by the coding by size of the different fractions, the responsibility of UNE EN 933-2: 96 [29] is prescribed, which establishes as a basic sequence of sieves the one formed by the following: 0.063-0.125-0.250-0.500-1-2-4-8-16-31.5-63-125 mm. For fine aggregate, only sieves of the series are used. For coarse aggregate, use the 10-20-40 mm sieves together, which are included in the complementary R 20 series admitted by the indicated Standard [28,30].
The properties will allow us to correctly understand the functionality of concrete, which will allow us to define the proportions that will be used in the project ( Figure 1 and Table 4). Figure 1 highlights the optimum curves obtained by using Bolomey's and Fuller's design methods.  A previous step to the design of the concrete mix was to perform the granulometric analysis of the materials involved, such as the sieving analysis, rodded volumetric weight, loose volumetric weight, dry surface density, absorption, humidity, fineness modulus. In the granulometric analysis [28] for the materials is by the coding by size of the different fractions, the responsibility of UNE EN 933-2: 96 [29] is prescribed, which establishes as a basic sequence of sieves the one formed by the following: 0.063-0.125-0.250-0.500-1-2-4-8-16-31.5-63-125 mm. For fine aggregate, only sieves of the series are used. For coarse aggregate, use the 10-20-40 mm sieves together, which are included in the complementary R 20 series admitted by the indicated Standard [28,30].
The properties will allow us to correctly understand the functionality of concrete, which will allow us to define the proportions that will be used in the project ( Figure 1 and Table 4). Figure 1 highlights the optimum curves obtained by using Bolomey's and Fuller's design methods. A previous step to the design of the concrete mix was to perform the granulometric analysis of the materials involved, such as the sieving analysis, rodded volumetric weight, loose volumetric weight, dry surface density, absorption, humidity, fineness modulus. In the granulometric analysis [28] for the materials is by the coding by size of the different fractions, the responsibility of UNE EN 933-2: 96 [29] is prescribed, which establishes as a basic sequence of sieves the one formed by the following: 0.063-0.125-0.250-0.500-1-2-4-8-16-31.5-63-125 mm. For fine aggregate, only sieves of the series are used. For coarse aggregate, use the 10-20-40 mm sieves together, which are included in the complementary R 20 series admitted by the indicated Standard [28,30].
The properties will allow us to correctly understand the functionality of concrete, which will allow us to define the proportions that will be used in the project (Figure 1 and Table 4). Figure 1 highlights the optimum curves obtained by using Bolomey's and Fuller's design methods.     The aim is to use tests and to be able to correctly analyse the product and be able to foresee any prior anomaly or inconsistency. The tests will be carried out with different dosages of material to compare their different behaviours, because each percentage will affect the strength, appearance, durability, and functionality of the new concrete. Likewise, the tests, granulometric designs, granulometric curves, concrete mix designs, will be carried out based on the corresponding regulations.
Among the methods and processes involved for the development of the project were: obtaining materials, mainly discarded concrete, crushing discarded concrete in 3/4 ", obtaining natural volcanic lime, and pozzolana, obtaining cement, sand, stone 19 mm, and clean water. Other necessary analyses are to establish the percentage of air included, determine the water and cement ratio, volume of coarse aggregate.
Also, the determination of the water and cement ratio, the volume of coarse aggregate, and the percentage of air included are among the additional analyses required (Table A1).
The strength of reference conventional concrete mix was designed to be f c = 28 MPa. A total of 7 concrete mixes were prepared, as shown in Figure 2. Apart from the conventional concrete mix NC, three mixes with partial replacement of 10%, 20%, and 50% of coarse aggregates with recycled concrete were prepared (RC10-0LV, RC20-0LV, and RC50-0LV respectively). Three additional mixes with recycled concrete were prepared with 2%, 5%, and 10% of cement replaced with lime and volcanic pozzolan in equal weights. Details of all the mix designs are listed in Table 5. The aim is to use tests and to be able to correctly analyse the product and be able to foresee any prior anomaly or inconsistency. The tests will be carried out with different dosages of material to compare their different behaviours, because each percentage will affect the strength, appearance, durability, and functionality of the new concrete. Likewise, the tests, granulometric designs, granulometric curves, concrete mix designs, will be carried out based on the corresponding regulations.
Among the methods and processes involved for the development of the project were: obtaining materials, mainly discarded concrete, crushing discarded concrete in 3/4 ", obtaining natural volcanic lime, and pozzolana, obtaining cement, sand, stone 19 mm, and clean water. Other necessary analyses are to establish the percentage of air included, determine the water and cement ratio, volume of coarse aggregate.
Also, the determination of the water and cement ratio, the volume of coarse aggregate, and the percentage of air included are among the additional analyses required (Table  A1).
The strength of reference conventional concrete mix was designed to be fc = 28 MPa. A total of 7 concrete mixes were prepared, as shown in Figure 2. Apart from the conventional concrete mix NC, three mixes with partial replacement of 10%, 20%, and 50% of coarse aggregates with recycled concrete were prepared (RC10-0LV, RC20-0LV, and RC50-0LV respectively). Three additional mixes with recycled concrete were prepared with 2%, 5%, and 10% of cement replaced with lime and volcanic pozzolan in equal weights. Details of all the mix designs are listed in Table 5.   Specimens were prepared to investigate the fresh properties and compressive strength of each mix design on 7, 14, and 28 days. Non-destructive tests were performed to examine the flexural-compressive strength ratios of recycled concrete specimens. The experimental study and data analysis process embedded in this study started from the test planning, review of materials and equipment, obtaining materials, specimen tests, analysis of data obtained, and finally, the discussion.

Results
In the data analysis process, the activities are structured from the review of the sources of information provided by the trials (Figure 3).  Specimens were prepared to investigate the fresh properties and compressive strength of each mix design on 7, 14, and 28 days. Non-destructive tests were performed to examine the flexural-compressive strength ratios of recycled concrete specimens. The experimental study and data analysis process embedded in this study started from the test planning, review of materials and equipment, obtaining materials, specimen tests, analysis of data obtained, and finally, the discussion.

Results
In the data analysis process, the activities are structured from the review of the sources of information provided by the trials (Figure 3). In this study, the fresh properties of conventional concrete mix (NC) and mixes with recycled concrete (RC10-0LV, RC20-LV, RC50-0LV, and RC10-5LV) were investigated, Figure 4. The slump test results for mixes containing different ratios of recycled concrete are listed in Table 6. As expected, the recycled crushed concrete has the same constituents. In this study, the fresh properties of conventional concrete mix (NC) and mixes with recycled concrete (RC10-0LV, RC20-LV, RC50-0LV, and RC10-5LV) were investigated, Figure 4. The slump test results for mixes containing different ratios of recycled concrete are listed in Table 6. As expected, the recycled crushed concrete has the same constituents. It can be noted that the recycled aggregate concrete does not influence the workability of the mixtures. Due to the same constituents in the crushed recycled concrete and the designed  [31]. In the mix designs, the average values measured for the air content and the density were 1.9% and 2320 kg/m 3 , respectively.  The compressive strengths of mixes NC, RC10-0LV, RC20-0LV, RC50-0LV, and RC10-5LV on 7, 14, and 28 days were investigated through cylindrical specimens with the size of Φ100 × 200 mm. The curing dates for the specimens were 7, 14, and 28 days. This test is described in ASTM C39 [32]. The test results are shown in Figure 5, and it is observed that recycled concretes have greater resistance compared to natural ones for the same water-cement ratio. It can be concluded that the partial replacement of coarse aggregates with crushed recycled concrete improves the compressive of the mixture. As shown in Figure 4, the compressive strength of the mix was increased by 18% as 10% of the aggregates were replaced. Further increase of the recycled concrete reduces the compressive strength of the mixtures. The main difference between the RAC and the natural aggregates is the amount of mortar included that the former incorporate due to the mortar from which they come. The dose of mortar included makes the RAC present different properties from the natural ones that are reflected in their properties, such as an increase in water permeability, and lower consistency. The concrete made with these aggregates will be directly restricted by these properties [33]. There is no regulated way to value these amounts, although methods that try to remove it from the outside of the aggregate are  The compressive strengths of mixes NC, RC10-0LV, RC20-0LV, RC50-0LV, and RC10-5LV on 7, 14, and 28 days were investigated through cylindrical specimens with the size of Φ100 × 200 mm. The curing dates for the specimens were 7, 14, and 28 days. This test is described in ASTM C39 [32]. The test results are shown in Figure 5, and it is observed that recycled concretes have greater resistance compared to natural ones for the same watercement ratio. It can be concluded that the partial replacement of coarse aggregates with crushed recycled concrete improves the compressive of the mixture. As shown in Figure 4, the compressive strength of the mix was increased by 18% as 10% of the aggregates were replaced. Further increase of the recycled concrete reduces the compressive strength of the mixtures. The main difference between the RAC and the natural aggregates is the amount of mortar included that the former incorporate due to the mortar from which they come. The dose of mortar included makes the RAC present different properties from the natural ones that are reflected in their properties, such as an increase in water permeability, and lower consistency. The concrete made with these aggregates will be directly restricted by these properties [33]. There is no regulated way to value these amounts, although methods that try to remove it from the outside of the aggregate are often used to establish the proportion by weight that corresponds to the mortar attached to the aggregate. Another representation to evaluate it consists of making a concrete mix design with RAC and with coloured cement. The specimens made are cut and polished, from there, the exteriority of the mortar is measured with a planimeter, distinguishing itself from the original by its tonality [33]. In all the studies available from the literature, it has been seen that the increase in the amount of mortar has a negative impact on its mechanical properties [33][34][35]. A higher strength was obtained with the mix RC10-5LV (35.7 MPa), indicating that the lime and volcanic pozzolan improve the binding between cement pastes and aggregates.
Infrastructures 2021, 6, x FOR PEER REVIEW 9 of 16 often used to establish the proportion by weight that corresponds to the mortar attached to the aggregate. Another representation to evaluate it consists of making a concrete mix design with RAC and with coloured cement. The specimens made are cut and polished, from there, the exteriority of the mortar is measured with a planimeter, distinguishing itself from the original by its tonality [33]. In all the studies available from the literature, it has been seen that the increase in the amount of mortar has a negative impact on its mechanical properties [33][34][35]. A higher strength was obtained with the mix RC10-5LV (35.7 MPa), indicating that the lime and volcanic pozzolan improve the binding between cement pastes and aggregates. Additionally, a study to correlate the resistance of the concrete both in compression as well as for bending was carried out. These non-destructive tests are known as sclerometer rebound and ultrasound [36]. This is important since, as it is known, concrete is used in multiple works such as buildings, houses, and bridges where the focus is on the behaviour of concrete in compression as well as on pavements [36]. The following results for the sclerometer and ultrasound test show the results from two specimens of each mix, cured in water for 28 days. Figure 6 shows how the concrete rebound increases when lime and pozzolana are included in the mix design. However, it can be noticed that the concrete rebound is higher in all the measures, which means that the concrete is uniform in all the mix designs. Additionally, a study to correlate the resistance of the concrete both in compression as well as for bending was carried out. These non-destructive tests are known as sclerometer rebound and ultrasound [36]. This is important since, as it is known, concrete is used in multiple works such as buildings, houses, and bridges where the focus is on the behaviour of concrete in compression as well as on pavements [36]. The following results for the sclerometer and ultrasound test show the results from two specimens of each mix, cured in water for 28 days. Figure 6 shows how the concrete rebound increases when lime and pozzolana are included in the mix design. However, it can be noticed that the concrete rebound is higher in all the measures, which means that the concrete is uniform in all the mix designs.  Figure 7 shows the ultrasound versus the compressive strength. This non-destructive test is a tool that helps to determine the concrete quality. It has been used in many countries instead of performing destructive tests such as compressive or flexural strength. It can be noticed that the concrete in all the mix designs presents a good condition according to the ultrasound test [37].  Figure 7 shows the ultrasound versus the compressive strength. This non-destructive test is a tool that helps to determine the concrete quality. It has been used in many countries instead of performing destructive tests such as compressive or flexural strength. It can be noticed that the concrete in all the mix designs presents a good condition according to the ultrasound test [37].  Figure 7 shows the ultrasound versus the compressive strength. This non-destructive test is a tool that helps to determine the concrete quality. It has been used in many countries instead of performing destructive tests such as compressive or flexural strength. It can be noticed that the concrete in all the mix designs presents a good condition according to the ultrasound test [37].  As can be seen in Figure 8, there is an increase in the flexural strength of concrete. Also, it can be concluded that it can also be used in pavements where the range of resistance to flexure was between 3 to 4.5 MPa.
Infrastructures 2021, 6, x FOR PEER REVIEW 11 of 16 As can be seen in Figure 8, there is an increase in the flexural strength of concrete. Also, it can be concluded that it can also be used in pavements where the range of resistance to flexure was between 3 to 4.5 MPa.

Life Cycle Analysis
The Life Cycle Analysis is a process that allows the evaluation of the environmental quality of a product or its components in a global way. This will focus on the environmen-

Life Cycle Analysis
The Life Cycle Analysis is a process that allows the evaluation of the environmental quality of a product or its components in a global way. This will focus on the environmental aspects and potential impacts in the stages of its corresponding life cycle. One of the fundamental objectives of this analysis is to help during the making decision process, especially, to understand the environmental consequences that can be generated by using the product or its components [38]. Therefore, the Life Cycle Analysis is a tool that helps to quantify the impact of the construction of buildings since it is based on objectively studying the different environmental impacts, analysing in-depth the environmental behaviour of aspects such as energy, raw materials, and water used (inputs) and its outputs (general waste and emissions transmitted to the atmosphere) [39].
In this study, a life cycle cost analysis (LCCA) was carried out to investigate the benefits of using recycled concrete as alternatives to replace mineral aggregates in structural concrete. Considering the practical application of RAC, a prototype of reinforced concrete structure is accounted for in the LCCA. The LCCA model embedded in this study comprises the costs of four phases as shown in Figure 9. According to ISO 15686-5 [40], LCCA needs to cover a long enough period of time for the consideration of maintenance and end-of-life cost. A reinforcement ratio of 2% in the structural concrete prototype was chosen in order to assess the influence of recycled aggregate on each phase of the LCCA model. quality of a product or its components in a global way. This will focus tal aspects and potential impacts in the stages of its corresponding l fundamental objectives of this analysis is to help during the making pecially, to understand the environmental consequences that can be the product or its components [38]. Therefore, the Life Cycle Analysi to quantify the impact of the construction of buildings since it is based ying the different environmental impacts, analysing in-depth the en iour of aspects such as energy, raw materials, and water used (inp (general waste and emissions transmitted to the atmosphere) [39].
In this study, a life cycle cost analysis (LCCA) was carried out to efits of using recycled concrete as alternatives to replace mineral agg concrete. Considering the practical application of RAC, a prototype o structure is accounted for in the LCCA. The LCCA model embedde prises the costs of four phases as shown in Figure 9. According to ISO needs to cover a long enough period of time for the consideration end-of-life cost. A reinforcement ratio of 2% in the structural concrete sen in order to assess the influence of recycled aggregate on each model. The material cost of each component used in this study is listed in Table 7. It can be noted that compared to natural aggregate, the recycled aggregate concrete aggregate had a lower cost in the local area. The cost of reinforcement was taken as the cost of black steel bars [41], and total costs of 1 m 3 of mix NC, RC50-0LV, and RC10-10LV (with reinforcement) are listed in Table 7 according to the mix design as shown in Table 5. It can be noted that replacing natural aggregates with recycled concrete shows a minor influence on the material price of structural concrete. Construction cost includes transportation, labour, and equipment for the manufacturing of reinforced concrete structures, while maintenance cost mainly comprises the expenses of repairs, replacements, or reconstructions during the service life of RC structures. The end-of-life cost refers to the demolish and landfill of the materials. In common practice, the construction, maintenance, and end-of-life costs are evaluated as a percentage of the material cost directly [42,43]. Consequently, the LCCA of RC structures shows that although the addition of recycled materials (recycled concrete, lime, and volcanic pozzolan) has a positive influence on the mechanical strengths of the material, the life cycle cost of RC structures with RAC are similar to those with NC materials.
In addition to the life cycle cost consideration, the extraction of natural aggregates and the consumption of non-renewable energies are leading us to a non-reversible situation [44]. The use of materials such as recycled concrete, lime, and natural pozzolana along with others. Although all recycled or discarded materials are not going to be suitable for use in the construction industry, public and private support is necessary for the analysis and research of new unconventional construction materials present in our surroundings. This is in order to raise awareness of people seeking to take care of the environment without the need to reduce the development of the construction field, rather than being able to find a synergy between both fields, the environment, and construction.
The excessive environmental impact caused by the life cycle of concrete materials is one of the major concerns of sustainable development. Conventional concrete is one of the largest consumers of natural resources, as well as the main source of construction demolish waste [6,45]. In addition, the manufacturing of concrete materials consumes a high level of total primary energy and causes severe greenhouse gas (GHG) emissions, which account for approximately 5% of the world's CO 2 emissions [46,47]. Amongst the constituents of the conventional concrete mixes, Portland cement is the primary source of GHG emissions and embodied energy (EE) (up to more than 80% of total emissions of concrete) [48][49][50]. Replacing the main constituents, such as cement and aggregates, with more sustainable materials is effective to reduce the environmental impact generated by conventional concrete.
In this study, recycled crushed concrete was acquired directly from the university lab to partially replace the coarse aggregate of conventional concrete. Figure 10 demonstrates the system boundaries of the concrete production system. In general, the average GHG emission of mineral aggregates is between 14-40 kg CO 2 eq./t, which contributes to approximately 14% of the total GHG emission of concrete mixes [51,52]. Consequently, the reduction of GHG emission of concrete materials due to partial replacement of mineral aggregates with recycled concrete is insignificant [6,52]. Nevertheless, the major difference in environmental impact caused by conventional concrete and recycled aggregate concrete lies in the transportation aspect. In general, the transport distance of natural mineral aggregate is between 0.3 and 280 km, whereas recycled aggregate concrete has a significantly lower transportation distance between 0 and 40 km [53]. It can be noted that in addition to alleviating the problem of construction and demolition waste caused by wasted concrete materials, the application of crushed concrete as recycled aggregate has a clear impact on the reduction of transportation loads of materials.
Infrastructures 2021, 6, x FOR PEER REVIEW 13 of 16 In this study, recycled crushed concrete was acquired directly from the university lab to partially replace the coarse aggregate of conventional concrete. Figure 10 demonstrates the system boundaries of the concrete production system. In general, the average GHG emission of mineral aggregates is between 14-40 kg CO2 eq./t, which contributes to approximately 14% of the total GHG emission of concrete mixes [51,52]. Consequently, the reduction of GHG emission of concrete materials due to partial replacement of mineral aggregates with recycled concrete is insignificant [6,52]. Nevertheless, the major difference in environmental impact caused by conventional concrete and recycled aggregate concrete lies in the transportation aspect. In general, the transport distance of natural mineral aggregate is between 0.3 and 280 km, whereas recycled aggregate concrete has a significantly lower transportation distance between 0 and 40 km [53]. It can be noted that in addition to alleviating the problem of construction and demolition waste caused by wasted concrete materials, the application of crushed concrete as recycled aggregate has a clear impact on the reduction of transportation loads of materials.

Conclusions
This paper examined the performance of concrete materials incorporating recycled aggregates, hydrated lime, and natural volcanic pozzolan. Fresh and mechanical properties were evaluated to assess the influence of the mix constituents, as well as a life cycle cost and environmental impacts were determined. Overall results indicate that materials such as recycled concrete aggregates can be used as a partial replacement for the natural aggregate and local lime or natural pozzolana can replace part of the binders. The main key findings are listed below.

Conclusions
This paper examined the performance of concrete materials incorporating recycled aggregates, hydrated lime, and natural volcanic pozzolan. Fresh and mechanical properties were evaluated to assess the influence of the mix constituents, as well as a life cycle cost and environmental impacts were determined. Overall results indicate that materials such as recycled concrete aggregates can be used as a partial replacement for the natural aggregate and local lime or natural pozzolana can replace part of the binders. The main key findings are listed below.

•
A good relationship between the workability and the satisfactory mechanical behaviour that the concrete was obtained with the presence of these three unconventional materials for concrete designs.

•
The introduction of recycled aggregates, lime, and volcanic pozzolan (replacement 10% crushed aggregate + 10% binder) leads to an increase of up to 34% in compressive strength compared to the conventional concrete mix.

•
The non-destructive tests show a good performance in the concrete's quality where the concrete rebound increases when lime and pozzolana are included in the mix design.

•
The life-cycle-cost analysis indicates that partial replacement of mineral aggregates with recycled aggregates shows a minor reduction in the total cost of concrete mixes.

•
The sustainable investigation shows that although recycled concrete aggregates possessed similar greenhouse gas emissions with natural mineral aggregates, the low transport distance of recycled concrete contributes significantly to the environmental impact of the concrete manufacturing system.
From this research, several investigative branches can start for new methodologies, environmentally friendly construction materials, knowing the contamination that occurs in the manufacture of the raw material for cement and concrete, not to mention the immense energy consumption at which all days we are protagonists; seeking to know, experiment and work with new materials allowing progressively to reduce the environmental impact that is generally attacked by the construction field and its activities related to construction.

Data Availability Statement:
The data presented in this study are available on request from the corresponding author.