Bio-Inspired Eco-Friendly Superhydrophilic/Underwater Superoleophobic Cotton for Oil-Water Separation and Removal of Heavy Metals

Effective integrated methods for oil-water separation and water remediation have signifi-cance in both energy and environment fields. Materials with both superlyophobic and superlyophilic properties toward water and oil have aroused great attention due to their energy-saving and high-efficient advantages in oil-water separation. However, in order to fulfill the superlyophobicity, low surface tension fluorinated components are always being introduced. These constituents are environmentally harmful, which may lead to additional contamination during the separating process. Moreover, the heavy metal ions, which are water-soluble and highly toxic, are always contained in the oil-water mixtures created during industrial production. Therefore, material that is integrated by both capacities of oil-water separation and removal of heavy metal contamination would be of significance in both industrial applications and environmental sustainability. Herein, inspired by the composition and wettability of the shrimp shell, an eco-friendly chitosan-coated (CTS) cotton was developed. The treated cotton exhibits the superhydrophilic/underwater superoleophobic property and is capable of separating both immiscible oil-water mixtures and stabilized oil-in-water emulsions. More significantly, various harmful water-soluble heavy metal ions can also be effectively removed during the separation of emulsions. The developed CTS coated cotton demonstrates an attractive perspective toward oil-water separation and wastewater treatment in various applications.


Introduction
Pollutions caused by industry-induced heavy metal-contaminated oil-water mixtures have become a pressing issue in areas such as marine conservation, manufacture and resource recovery [1][2][3][4]. Effective integrated methods for oil-water separation and water remediation have significance in both energy and environment fields.
For oil-water separation, traditional methods, such as hydrocyclone and sedimentation, which are generally used for immiscible oil-water mixtures separation, are either energy-intensive or time-consuming [5,6]. For more complex oily wastewater and emulsions, electrochemical and biological treatments are commonly used. These methods, however, are inefficient or have high energy consumption [1,7]. Since the early 2000s, materials with both superlyophobic (liquid contact angle greater than 150 • and tilt angle smaller than 10 • ) and superlyophilic (liquid contact angle smaller than 10 • ) properties toward water and oil have aroused great attention due to their energy-saving and highefficient advantages in oil-water separation and wastewater treatment. These materials are generally divided into two types: superhydrophobic/superoleophilic (oil removing) and superoleophobic/superhydrophilic (water removing) material [8][9][10][11][12]. For the separation of have been developed [40][41][42][43]. Most of these materials preserve excellent performance in separating immiscible oil-water mixtures. However, these materials lack the metal ions-removing capacities because of the insufficient contact of the CTS and the aqueous solution. Hence, fabricating CTS-based materials with both superhydrophilic/underwater superoleophobic property for effective oil-water separation and sufficient liquid contact efficiency is still challenging.
In this study, an eco-friendly superhydrophilic/underwater superoleophobic CTSmodified cotton was developed by a facile method. Benefiting from the multitudinous fibrous structure and highly compressibility of the cotton substrate, the CTS-coated cotton can not only separate immiscible oil-water mixtures but also stabilized oil-in-water emulsions with a considerable separation capacity. Most noticeably, due to the sufficient contact of the liquid and the multitudinous fibers on the treated cotton, the harmful watersoluble heavy metal ions, such as bivalent cuprum (Cu 2+ ), trivalent iron (Fe 3+ ), univalent silver (Ag 1+ ) and hexavalent chromium (Cr 6+ ), can also be effectively removed during the separation of emulsions. This eco-friendly and effective CTS-coated cotton demonstrates an attractive perspective toward oil-water separation and wastewater treatment in various fields. move heavy metal ions during oil-water separation, can have great significance in cate liquid treatment. Unfortunately, integrated materials of this kind have rarely reported. Since sufficient contact of solution and chitosan (the adsorbents) is essentia removing metal ions. In general, the ion contaminants are removed by mixing and fi ing methods [37][38][39]. In recent years, superhydrophilic/underwater superoleophobic based porous materials have been developed [40][41][42][43]. Most of these materials pres excellent performance in separating immiscible oil-water mixtures. However, these m rials lack the metal ions-removing capacities because of the insufficient contact of the and the aqueous solution. Hence, fabricating CTS-based materials with both superhy philic/underwater superoleophobic property for effective oil-water separation and s cient liquid contact efficiency is still challenging.
In this study, an eco-friendly superhydrophilic/underwater superoleophobic modified cotton was developed by a facile method. Benefiting from the multitudi fibrous structure and highly compressibility of the cotton substrate, the CTS-coated co can not only separate immiscible oil-water mixtures but also stabilized oil-in-water e sions with a considerable separation capacity. Most noticeably, due to the sufficient tact of the liquid and the multitudinous fibers on the treated cotton, the harmful w soluble heavy metal ions, such as bivalent cuprum (Cu 2+ ), trivalent iron (Fe 3+ ), univ silver (Ag 1+ ) and hexavalent chromium (Cr 6+ ), can also be effectively removed durin separation of emulsions. This eco-friendly and effective CTS-coated cotton demonst an attractive perspective toward oil-water separation and wastewater treatment in ous fields.

Preparation of CTS-Coated Cotton
The preparation process is shown in Figure 1b: 2.0 g chitosan was initially dissolved in 50 mL 1% (w%) acetic solution and magnetically stirred for 1 h to make the chitosan coating; then a piece of prewashed cotton was immersed into the coating solution and ultrasonic shake for 2 h before drying at 80 • C for 3 h; the treated cotton was finally washed with hot water (~50 • C) several times and then dried at 80 • C before use.

Separation of Immiscible Oil-Water Mixtures
To separate immiscible oil-water mixtures, 0.5 g of treated cotton was firstly flattened by a polyfluortetraethylene plate. The flattened cotton was then sandwiched between a glass tube and a suction flask. The gaps between the tubes were then sealed with silicone sealant. The combination was then set above the beaker with the cotton side up. The cotton was totally wetted by water before separation. Immiscible oil-water mixtures (volume ratio between water and the corresponding oil is 1:1) was poured onto the CTS-coated cotton. For the separation test in the harsh environment, the pH of water was pre-adjusted by hydrochloric acid (HCL) and NaOH before mixing with oil liquids.

Separation of Heavy Metal Ion-Contaminated Emulsions
The of metal ion-contaminated oil-in-water emulsions were prepared by mixing the metal ion-contaminated aqueous solution with an emulsifier and the corresponding oil. Fe 3+ , Cu 2+ and Cr 6+ were selected as target pollutants. Diesel, soybean oil and hexadecane were selected as oils. In detail, 20 mg L −1 of the corresponding ion-contaminated aqueous solution was obtained by diluting a standard stock solution (2.0 g/L). TWEEN 60, the corresponding oil and metal ion-contaminated aqueous solution were mixed in a ratio of 1:10:100 by volume. Each mixture was vibrated with an ultrasonic homogenizer (Xinzhi JY92-11N, 20 kHz frequency) for 3 h to form an emulsion.
For the emulsion separation, a piece of chitosan-coated cotton (~1 g) was pushed into an injector barrel as tightly as possible, the density of the compressed cotton was about 0.28 g cm −3 . In order to prewet the CTS-coated cotton, 5 mL of deionized water was firstly added into the barrel, then the oil-in-water emulsion was poured into a barrel, followed by a gravity-driven continuous separation of 30 mL test sample.

Characterization and Measurement
The morphology characterization was performed by the laser scanning confocal microscope (Zeiss LSM700) and Scanning Electron Microscopy (SEM, Carl Zeiss Jena, Germany) at a 10 kV acceleration voltage at a working distance of 8 mm. The chemical constituents were detected by Fourier Transform infrared spectrophotometer (FT-IR, Nicolet iS50, Thermo Scientific). The contact angles were measured by the optical contact angle meter (DropMeterTM Element A-60, Maist, Ningbo, China) at ambient environment conditions and each data was determined by the average value of 5 times experiments. The oil distributions in the feeds and filtrates were characterized by Leica DVM6s 3D Microscope (Leica, Germany). The oil content in the filtrate was measured by the total organic carbon analyzer (TOC, ANALYTIKJENA Multi N/C, Jena, Germany). The metal ions in water were detected by inductively coupled plasma mass spectrometry (ICP-MS, 7800, Agilent, Santa Clara, CA, USA). For the measurement of the oil content and metal ion concentration, the data was obtained by taking an average of 5 test results with separate experiments.
The flux Q and separation efficiency η were calculated by Equation (1) and Equation (2), respectively.
where V is the volume of the separated emulsion, S is the sectional area of the injector barrel, and t represents the time of the separation process. C feed and C filtrate represent the concentrations of oil in the emulsion feed and filtrate, respectively. The removal efficiency q e was calculated by Equation (3): where C 0 and C e are concentrations of heavy metal ions in the feed aqueous solution in the emulsion (20 mg L −1 ) and collected filtrate after separation, respectively.

The Characterization of the CTS-Coated Cotton
The chemical composition of the pristine and CTS-coated cotton was characterized by the Fourier transform infrared spectrophotometer (FTIR), as shown in Figure 2a. It is observed that compared with the spectra of pristine cotton, several bands were detected on CTS-coated cotton. The bands at 3428 cm −1 were attributed to O-H stretch vibration. The peaks at 2924 cm −1 and 2853 cm −1 corresponded to saturated alkyl groups. The peaks at 1645 cm −1 and 1587 cm −1 were attributed to N-H and amide groups, respectively [44]. These peaks demonstrate that chitosan was attached to the cotton substrate.
The SEM morphology of the pristine cotton, prewashed cotton and CTS-coated cotton was also detected, as shown in Figure 2b. Compared with pristine cotton fiber which is smooth and flat, the prewashed cotton fiber was corrugated and wizened. The corrugation was caused by the treatment of an alkaline solution, during which the wax layer on pristine cotton was removed and led to the exposure of hydroxyl groups. The corrugation and the hydrophilic hydroxyl groups will help the CTS coating to attach better with the fibers. The cotton fibers after modification, as shown in Figure 2b, were mostly covered by CTS coating. It is observed that some agglomerated CTS particles, which were precipitated from the coating during the heating process, were also attached to cotton fibers. These particles and the coated cotton fibers constructed the hierarchal structure, which plays an important role in the construction of superwettability. To further demonstrate the change in roughness, the morphology of pristine and CTS-coated cotton was also detected by laser scanning confocal microscopy, as shown in Figure 3. The average surface roughness R q on pristine cotton and pre-washed cotton were 0.51 µm and 0.68 µm, respectively. Whereas, the roughness R q increased to 1.65 µm on CTS-coated cotton. Combined with the chemical composition variation and the SEM images, which are shown in Figure 2, it can be speculated that the CTS has been successfully modified on the cotton fibers. The increased roughness factor also indicates the formation of hierarchal structure, which is beneficial for enhancing the superwettability of the treated cotton. The SEM morphology of the pristine cotton, prewashed cotton and CTS-coated cotton was also detected, as shown in Figure 2b. Compared with pristine cotton fiber which is smooth and flat, the prewashed cotton fiber was corrugated and wizened. The corrugation was caused by the treatment of an alkaline solution, during which the wax layer on pristine cotton was removed and led to the exposure of hydroxyl groups. The corrugation and the hydrophilic hydroxyl groups will help the CTS coating to attach better with the fibers. The cotton fibers after modification, as shown in Figure 2b, were mostly covered by CTS coating. It is observed that some agglomerated CTS particles, which were precipitated from the coating during the heating process, were also attached to cotton fibers. These particles and the coated cotton fibers constructed the hierarchal structure, which plays an important role in the construction of superwettability. To further demonstrate the change in roughness, the morphology of pristine and CTS-coated cotton was also detected by laser scanning confocal microscopy, as shown in Figure 3. The average surface roughness Rq on pristine cotton and pre-washed cotton were 0.51 µm and 0.68 µm, respec-

The wettability of the CTS-Coated Cotton
The selective superwettability in the liquid environment is an essential requirement for the separation of oil-water mixtures. Therefore, the wettability of the CTS-coated cotton in a liquid environment was firstly tested, as shown in Figure 4a,b. The oil droplet can slide freely without adhesion on the CTS-coated cotton. In contrast, the water droplet in the oil environment spread and permeated rapidly into the CTS-coated cotton upon contact.

The Wettability of the CTS-Coated Cotton
The selective superwettability in the liquid environment is an essential requirement for the separation of oil-water mixtures. Therefore, the wettability of the CTS-coated cotton in a liquid environment was firstly tested, as shown in Figure 4a,b. The oil droplet can slide freely without adhesion on the CTS-coated cotton. In contrast, the water droplet in the oil environment spread and permeated rapidly into the CTS-coated cotton upon contact.

The wettability of the CTS-Coated Cotton
The selective superwettability in the liquid environment is an essential requ for the separation of oil-water mixtures. Therefore, the wettability of the CTS-coa ton in a liquid environment was firstly tested, as shown in Figure 4a,b. The oil dro slide freely without adhesion on the CTS-coated cotton. In contrast, the water dr the oil environment spread and permeated rapidly into the CTS-coated cotton up tact. The underwater superoleophobicity and the underoil superhydrophilicity ca plained by the following Equations (4) and (5)   The underwater superoleophobicity and the underoil superhydrophilicity can be explained by the following Equations (4) and (5) [45][46][47]: where θ ow and θ wo are the underwater oil contact angle and underoil water contact angle on the flat fiber surface, respectively. γ oa and γ wa are the surface tensions of oil and water, respectively. γ ow is the surface tension at the oil-water interface. Since the CTS surface is lyophilic (θ o and θ w are less than 90º) and the surface tensions of oil are much less than that of water. Thus, γ oa cos θ o − γ wa cos θ w is negative and γ wa cos θ w − γ oa cos θ o is positive. The CTS surface exhibits underwater oleophobic and underoil hydrophilic properties (Figure 4c). According to Wenzel theory, the contact angle on a rough surface can be expressed as: where θ l the contact angle on a flat surface, R f is the roughness factor which is always greater than 1 for the surface with a certain roughness. Thus, the underwater oleophobicity and underoil hydrophilicity were greatly emphasized by the hierarchical roughness created by the numerous coated fibers and resulted in the formation of underwater superoleophobicity and underoil superhydrophilicity. The consequent selective superwettability in a liquid environment enables the CTS-coated cotton to remove water from oil-water mixtures during the separation process.
To further demonstrate the underwater superoleophobic property of the CTS-coated cotton, the contact angles of oils with various surface tensions and densities (Table 1) were measured, as shown in Figure 5. It is observed that the underwater contact angles of the test oils were greater than 150 • , demonstrating the underwater oil-repellent behavior of the CTS-coated cotton. f l where l θ the contact angle on a flat surface, f R is the roughness factor which i greater than 1 for the surface with a certain roughness. Thus, the underwater ole city and underoil hydrophilicity were greatly emphasized by the hierarchical ro created by the numerous coated fibers and resulted in the formation of underwate oleophobicity and underoil superhydrophilicity. The consequent selective superw ity in a liquid environment enables the CTS-coated cotton to remove water from o mixtures during the separation process.
To further demonstrate the underwater superoleophobic property of the CT cotton, the contact angles of oils with various surface tensions and densities (Table measured, as shown in Figure 5. It is observed that the underwater contact angl test oils were greater than 150°, demonstrating the underwater oil-repellent beh the CTS-coated cotton.

Separation of Immiscible Oil-Water Mixtures
The CTS-coated cotton exhibits the ability in the separating immiscible oil-wa tures due to its selective superwettability. The separation of the immiscible oil-wa ture is shown in Figure 6a. During separation, continuous water flowed through coated cotton, and oil was rejected on the CTS-coated cotton. The separation e and flux during the separation of various kinds of immiscible oil-water mixtures w measured, as shown in Figure 6b. It is observed that the average separation eff were higher than 99% for the separation of various immiscible oil-water mixtures separation flux was up to 42,000 L m −2 h −1 , demonstrating the effectiveness and p bility in the separation of immiscible oil-water mixtures. In order to evaluate the of the CTS-coated cotton, the separating performance of the CTS-coated cotton environments was tested. Figure 6c illustrates the underwater oil contact angle a ration efficiency in aqueous environments with different pH values (from pH = 3

Separation of Immiscible Oil-Water Mixtures
The CTS-coated cotton exhibits the ability in the separating immiscible oil-water mixtures due to its selective superwettability. The separation of the immiscible oil-water mixture is shown in Figure 6a. During separation, continuous water flowed through the CTS-coated cotton, and oil was rejected on the CTS-coated cotton. The separation efficiency and flux during the separation of various kinds of immiscible oil-water mixtures were also measured, as shown in Figure 6b. It is observed that the average separation efficiencies were higher than 99% for the separation of various immiscible oil-water mixtures and the separation flux was up to 42,000 L m −2 h −1 , demonstrating the effectiveness and practicability in the separation of immiscible oil-water mixtures. In order to evaluate the stability of the CTS-coated cotton, the separating performance of the CTS-coated cotton in harsh environments was tested. Figure 6c illustrates the underwater oil contact angle and separation efficiency in aqueous environments with different pH values (from pH = 3 to pH = 11). It is observed that there were no obvious variation on underwater oil contact angles during variation of pH values, demonstrating the stability of the underwater superoleophobcity of the CTS-coated cotton. The oil-water separation efficiency was stable above 99% in the range of pH = 5 to pH = 11, whereas the separation efficiency decreased to 98% when pH = 3. 11). It is observed that there were no obvious variation on underwater oil contact angles during variation of pH values, demonstrating the stability of the underwater superoleophobcity of the CTS-coated cotton. The oil-water separation efficiency was stable above 99% in the range of pH = 5 to pH = 11, whereas the separation efficiency decreased to 98% when pH = 3. The separation efficiency and the flux during the separation of immiscible diesel-water, soybean oil-water and hexadecane-water mixtures, the average separation efficiencies were higher than 99% for the separation of various immiscible oil-water mixtures and the separation flux was up to 42,000 L m −2 h −1 . (c) The separation efficiency and underwater oil contact angle in aqueous environments with pH values of pH = 3 to pH = 11. There were no obvious variation on underwater oil contact angles during variation of pH values, the oil-water separation efficiency was stable above 99% in the range of pH = 5 to pH = 11, whereas the separation efficiency decreased to 98% when pH = 3.

Separation of Heavy Metal Ion-Contaminated Emulsions
The oil-in-water emulsion is a more intensive type of oil-water mixture in which microdroplets of oil (normally smaller than 20 µm) are dispersed in water. High toxic heavy metal ion-contaminated aqueous solution widely exists in the emulsions which are created in industrial production. Benefit from the flexible compressibility of the substrate and the excellent chelation performance of CTS. The developed compressed CTS-coated cotton can not only separate stabilized oil-in-water emulsions but also remove various heavy metal ions dissolved in the aqueous solution of the emulsions during separation. The mechanism of this process is shown in Figure 7. The heavy metal ion-contaminated aqueous solution continuously flows through the CTS-coated cotton, during which the metal ions are absorbed by CTS due to the chelation interaction with the -NH2 and -OH groups. Meanwhile, the microdroplets of oil dispersed in the emulsion are rejected due to the underwater superoleophobicity of the CTS-coated cotton. The separation efficiency and the flux during the separation of immiscible diesel-water, soybean oil-water and hexadecane-water mixtures, the average separation efficiencies were higher than 99% for the separation of various immiscible oil-water mixtures and the separation flux was up to 42,000 L m −2 h −1 . (c) The separation efficiency and underwater oil contact angle in aqueous environments with pH values of pH = 3 to pH = 11. There were no obvious variation on underwater oil contact angles during variation of pH values, the oil-water separation efficiency was stable above 99% in the range of pH = 5 to pH = 11, whereas the separation efficiency decreased to 98% when pH = 3.

Separation of Heavy Metal Ion-Contaminated Emulsions
The oil-in-water emulsion is a more intensive type of oil-water mixture in which microdroplets of oil (normally smaller than 20 µm) are dispersed in water. High toxic heavy metal ion-contaminated aqueous solution widely exists in the emulsions which are created in industrial production. Benefit from the flexible compressibility of the substrate and the excellent chelation performance of CTS. The developed compressed CTS-coated cotton can not only separate stabilized oil-in-water emulsions but also remove various heavy metal ions dissolved in the aqueous solution of the emulsions during separation. The mechanism of this process is shown in Figure 7. The heavy metal ion-contaminated aqueous solution continuously flows through the CTS-coated cotton, during which the metal ions are absorbed by CTS due to the chelation interaction with the -NH 2 and -OH groups. Meanwhile, the microdroplets of oil dispersed in the emulsion are rejected due to the underwater superoleophobicity of the CTS-coated cotton.
To demonstrate the effect of separation and metal ion-removal capacity, various oilin-water emulsions severely contaminated by Fe 3+ , Cu 2+ and Cr 6+ , were selected as test samples. On the one hand, it is noted that the mass of coated CTS plays a key role in removing metal ions. In theory, the treated cotton with more CTS-coated fibers preserves higher metal ions removing efficiency. On the other hand, the emulsion separation efficiency and the separation flux depend on the compressed density and thickness of the CTS-coated cotton. Thus, in order to optimize the thickness of the compressed CTS-coated cotton, the separation efficiency and the corresponding separation flux using CTS-coated cotton with constant compressed density (0.28 g cm −3 ) and different mass was tested. As shown in Figure 8a, it is observed that the separation efficiency gradually increases with the increase of mass (thickness); the separation efficiency is stable when the mass of the CTScoated cotton is larger than 0.75 g. The separation flux decreases with the increase of mass; this is because the increase of the cotton (thickness) enhances the resistance for liquid penetration. Thus, 1 g of the CTS-coated cotton with 0.28 g cm −3 of compressed density was selected as the optimization for emulsion separation. The separation efficiency and flux during separating different kinds of emulsions were also measured; the data is shown in Figure 8b,c. It can be observed that the optimized compressed CTS-coated cotton preserves a high efficiency over 98%, along with flux varying from 30 L m −2 h −1 to 48 L m −2 h −1 for separation various stabilized oil-in-water emulsions, which demonstrate the validity of the treated cotton in the emulsion separation applications. To demonstrate the effect of separation and metal ion-removal capacity, various oilin-water emulsions severely contaminated by Fe 3+ , Cu 2+ and Cr 6+ , were selected as test samples. On the one hand, it is noted that the mass of coated CTS plays a key role in removing metal ions. In theory, the treated cotton with more CTS-coated fibers preserves higher metal ions removing efficiency. On the other hand, the emulsion separation efficiency and the separation flux depend on the compressed density and thickness of the CTS-coated cotton. Thus, in order to optimize the thickness of the compressed CTS-coated cotton, the separation efficiency and the corresponding separation flux using CTS-coated cotton with constant compressed density (0.28 g cm −3 ) and different mass was tested. As shown in Figure 8a, it is observed that the separation efficiency gradually increases with the increase of mass (thickness); the separation efficiency is stable when the mass of the CTS-coated cotton is larger than 0.75 g. The separation flux decreases with the increase of mass; this is because the increase of the cotton (thickness) enhances the resistance for liquid penetration. Thus, 1 g of the CTS-coated cotton with 0.28 g cm −3 of compressed density was selected as the optimization for emulsion separation. The separation efficiency and flux during separating different kinds of emulsions were also measured; the data is shown in Figure 8b,c. It can be observed that the optimized compressed CTS-coated cotton preserves a high efficiency over 98%, along with flux varying from 30 L m −2 h −1 to 48 L m −2 h −1 for separation various stabilized oil-in-water emulsions, which demonstrate the validity of the treated cotton in the emulsion separation applications. The effect in the separation of oil-in-water emulsions was also evaluated, as shown in Figure 9. It is observed that all the test feeds were emulsified and milky, whereas the filtrates were transparent and clear. The separation effect was further demonstrated by the microscopic images before and after separation. The oil droplets whose diameters are smaller than 20 µm were detected in all the feed samples before separation, whereas there The effect in the separation of oil-in-water emulsions was also evaluated, as shown in Figure 9. It is observed that all the test feeds were emulsified and milky, whereas the filtrates were transparent and clear. The separation effect was further demonstrated by the microscopic images before and after separation. The oil droplets whose diameters are smaller than 20 µm were detected in all the feed samples before separation, whereas there were no droplets of oil detected in the corresponding filtrates.
Biomimetics 2022, 7, x FOR PEER REVIEW 12 of 15 Figure 9. The effect of separation of contaminated diesel-in-water, soybean oil-in-water and hexadecane-in-water emulsions. Oil droplets which were smaller than 20 µm were detected in the feed before separation, whereas there were no droplets of oil detected in the filtrates.
In order to evaluate the capacity in the removal of the heavy metal ions, the concentration of the remaining metal ion (Fe 3+ , Cu 2+ and Cr 6+ ) in the corresponding filtrate liquid after separation of the metal ion-contaminated oil-in-water emulsion was measured. The removal efficiency of the metal ion was calculated by Equation (3), and the data is exhibited in Figure 10. It is observed that the concentration of the metal ions remaining in all test filtrates experienced a noticeable decrease compared with the feed emulsions. The initial concentration of the metal ion pollutants in all the feed emulsions was 20 mg L −1 , whereas the metal ion concentrations in the corresponding filtrates were no higher than 6.5 mg L −1 . It is speculated that the relatively low separation flux endows the contaminated aqueous solution to have extended contact with the CTS, which leads to effective absorption of metal ions during penetration. The considerable removal efficiency which varies from 70% to 85% demonstrates effectiveness and practicability of the CTS-coated cotton in removing heavy metal ions. Figure 9. The effect of separation of contaminated diesel-in-water, soybean oil-in-water and hexadecane-in-water emulsions. Oil droplets which were smaller than 20 µm were detected in the feed before separation, whereas there were no droplets of oil detected in the filtrates.
In order to evaluate the capacity in the removal of the heavy metal ions, the concentration of the remaining metal ion (Fe 3+ , Cu 2+ and Cr 6+ ) in the corresponding filtrate liquid after separation of the metal ion-contaminated oil-in-water emulsion was measured. The removal efficiency of the metal ion was calculated by Equation (3), and the data is exhibited in Figure 10. It is observed that the concentration of the metal ions remaining in all test filtrates experienced a noticeable decrease compared with the feed emulsions. The initial concentration of the metal ion pollutants in all the feed emulsions was 20 mg L −1 , whereas the metal ion concentrations in the corresponding filtrates were no higher than 6.5 mg L −1 . It is speculated that the relatively low separation flux endows the contaminated aqueous solution to have extended contact with the CTS, which leads to effective absorption of metal ions during penetration. The considerable removal efficiency which varies from 70% to 85% demonstrates effectiveness and practicability of the CTS-coated cotton in removing heavy metal ions. Biomimetics 2022, 7, x FOR PEER REVIEW 13 of 15 Figure 10. The concentration of heavy metal ions in the feed and filtrate and the corresponding removal efficiency during the separation of (a) contaminated diesel-in-water emulsion, (b) contaminated soybean oil-in-water emulsion and (c) contaminated hexadecane-in-water emulsion.

Conclusions
In summary, a bioinspired eco-friendly, multi-functional chitosan-modified cotton was fabricated by coating chitosan solution on a cotton substrate. The treated cotton, which exhibits superhydrophilic and underwater superoleophobic properties, is nontoxic and can be used in the separation of both immiscible oil-water mixtures and oil-inwater emulsions due to the flexible compressibility of the cotton substrate. More significantly, by taking advantage of the chelate behavior between the chitosan molecule and the metal ions, it preserves the high-efficient ability of removing toxic heavy metal ions in an aqueous solution during the separation of emulsions. This eco-friendly CTS-coated cotton, which integrated both oil-water separation and purification capacities, demonstrates an attractive prospect for wastewater treatment in various applications.

Conclusions
In summary, a bioinspired eco-friendly, multi-functional chitosan-modified cotton was fabricated by coating chitosan solution on a cotton substrate. The treated cotton, which exhibits superhydrophilic and underwater superoleophobic properties, is non-toxic and can be used in the separation of both immiscible oil-water mixtures and oil-in-water emulsions due to the flexible compressibility of the cotton substrate. More significantly, by taking advantage of the chelate behavior between the chitosan molecule and the metal ions, it preserves the high-efficient ability of removing toxic heavy metal ions in an aqueous solution during the separation of emulsions. This eco-friendly CTS-coated cotton, which integrated both oil-water separation and purification capacities, demonstrates an attractive prospect for wastewater treatment in various applications.