Concepts for Reusing Composite Materials from Decommissioned Wind Turbine Blades in Affordable Housing

: The very rapid growth in wind energy technology in the last 15 years has led to a rapid growth in the amount of non-biodegradable, thermosetting ﬁber reinforced polymer (FRP) composite materials used in wind turbine blades. This paper discusses conceptual architectural and structural options for recycling these blades by reusing parts of wind turbine blades in new or retroﬁtted housing projects. It focuses on large-sized FRP pieces that can be salvaged from the turbine blades and can potentially be useful in infrastructure projects where harsh environmental conditions (water and high humidity) exist. Since reuse design should be for speciﬁc regional locations and architectural characteristics the designs presented in this paper are for the coastal regions of the Yucatan province in Mexico on the Gulf of Mexico where low-quality masonry block informal housing is vulnerable to severe hurricanes and ﬂooding. To demonstrate the concept a prototype 100 m long wind blade model developed by Sandia National Laboratories is used to show how a wind blade can be broken down into parts, thus making it possible to envision architectural applications for the different wind blade segments for housing applications.


Introduction
A typical 2.0 MW turbine with three 50 m blades has approximately 20 tonnes of fiber reinforced polymer (FRP) material and an 8 MW turbine has approximately 80 tonnes of glass (G) and carbon (C) fiber reinforced polymer (FRP) material (1 MW~10 tonnes of FRP, see [1][2][3][4].) As of December 2016, the global cumulative installed wind power capacity was 486,790 MegaWatts (MW) (Figure 1) [5]. Based on a predicted moderate growth scenario from the Global Wind Energy Council [6] for future global wind power installations a total of 16.8 million tonnes of FRP materials will need to be disposed of or recycled by 2030 and 39.8 million tonnes by 2050 ( Figure 2). However beneficial to sustainable energy production, this sharp growth in the wind industry will also lead to substantial and potentially unsustainable amounts of non-biodegradable composite material to be dealt with in the future.  The Mexican wind industry has been installing wind turbines over the past nine years. Figure 3 shows a forecast of the installed capacity (12,823 MW total) for each of Mexico's provinces in 2020 [7]. The two provinces with the largest anticipated wind energy capacities in 2020 are Oaxaca and Yucatan. Large numbers of wind turbine blades facing inevitable decommissioning close to vulnerable communities on the Gulf of Mexico coast would make it feasible to transport blade segments to these communities for reuse.
Over the past 40 years formal and informal settlements have developed in small towns along the northern coast of the Yucatan in the Gulf of Mexico. To assess the vulnerability of these settlements to the effects of climate change, 628 household surveys were conducted in seven communities in his region in the summer of 2014 [8]. The housing in this region is constructed of hollow concrete (CMU) blocks confined by cast-in-place corner columns. The roof is constructed of precast inverted T-beams and matching hollow blocks. After assembly the roof is covered with a 15-20 mm layer of cast-in-place pea-gravel concrete. The foundation is compacted rubble with a cast-inplace strip footing. Concrete lintels and header beams are cast-in-place. Houses are typically single or multi-room measuring 30-50 m 2 . A house under construction is shown in Figure 4. The edge of the roofing system can be seen on the house alongside to the left in Figure 4. The interior of an approximately 30 year old house is shown in Figure 5. The underside of the inverted-T-beam and the roofing blocks can be seen. Severe effects of moisture damage to both the roof and walls is also observed. The household surveys revealed that home owners were most concerned about the damage caused by wind-driven rain and flooding due to hurricanes and also normal weather conditions [8].   The Mexican wind industry has been installing wind turbines over the past nine years. Figure 3 shows a forecast of the installed capacity (12,823 MW total) for each of Mexico's provinces in 2020 [7]. The two provinces with the largest anticipated wind energy capacities in 2020 are Oaxaca and Yucatan. Large numbers of wind turbine blades facing inevitable decommissioning close to vulnerable communities on the Gulf of Mexico coast would make it feasible to transport blade segments to these communities for reuse.
Over the past 40 years formal and informal settlements have developed in small towns along the northern coast of the Yucatan in the Gulf of Mexico. To assess the vulnerability of these settlements to the effects of climate change, 628 household surveys were conducted in seven communities in his region in the summer of 2014 [8]. The housing in this region is constructed of hollow concrete (CMU) blocks confined by cast-in-place corner columns. The roof is constructed of precast inverted T-beams and matching hollow blocks. After assembly the roof is covered with a 15-20 mm layer of cast-in-place pea-gravel concrete. The foundation is compacted rubble with a cast-inplace strip footing. Concrete lintels and header beams are cast-in-place. Houses are typically single or multi-room measuring 30-50 m 2 . A house under construction is shown in Figure 4. The edge of the roofing system can be seen on the house alongside to the left in Figure 4. The interior of an approximately 30 year old house is shown in Figure 5. The underside of the inverted-T-beam and the roofing blocks can be seen. Severe effects of moisture damage to both the roof and walls is also observed. The household surveys revealed that home owners were most concerned about the damage caused by wind-driven rain and flooding due to hurricanes and also normal weather conditions [8]. The Mexican wind industry has been installing wind turbines over the past nine years. Figure 3 shows a forecast of the installed capacity (12,823 MW total) for each of Mexico's provinces in 2020 [7]. The two provinces with the largest anticipated wind energy capacities in 2020 are Oaxaca and Yucatan. Large numbers of wind turbine blades facing inevitable decommissioning close to vulnerable communities on the Gulf of Mexico coast would make it feasible to transport blade segments to these communities for reuse.
Over the past 40 years formal and informal settlements have developed in small towns along the northern coast of the Yucatan in the Gulf of Mexico. To assess the vulnerability of these settlements to the effects of climate change, 628 household surveys were conducted in seven communities in his region in the summer of 2014 [8]. The housing in this region is constructed of hollow concrete (CMU) blocks confined by cast-in-place corner columns. The roof is constructed of precast inverted T-beams and matching hollow blocks. After assembly the roof is covered with a 15-20 mm layer of cast-in-place pea-gravel concrete. The foundation is compacted rubble with a cast-in-place strip footing. Concrete lintels and header beams are cast-in-place. Houses are typically single or multi-room measuring 30-50 m 2 . A house under construction is shown in Figure 4. The edge of the roofing system can be seen on the house alongside to the left in Figure 4. The interior of an approximately 30 year old house is shown in Figure 5. The underside of the inverted-T-beam and the roofing blocks can be seen. Severe effects of moisture damage to both the roof and walls is also observed. The household surveys revealed that home owners were most concerned about the damage caused by wind-driven rain and flooding due to hurricanes and also normal weather conditions [8].            Three end-of-life (EOL) options for FRP wind blades [9] are currently possible-disposal, recovery, and reuse. The two options to dispose of FRP composites at the present involve landfilling or incineration (with or without energy recovery and/or silica ash recovery). Recovery options consist of reclamation of the constituent fibers or the resins by thermo-chemical methods or recovering of small pieces of granular FRP material for use as filler material in concrete or other composites by cutting, shredding, or grinding [10,11]. Reuse options consist of reusing the entire FRP blade or large parts of it in new structural applications. Reuse options are the primary focus of this paper since landfilling and incineration are environmentally harmful and recovery methods are not currently economical for glass fiber reinforced polymer (GFRP), of which the vast majority of current blades are fabricated. There is significant current research [10] in recovering carbon fiber reinforced polymer (CFRP) materials which have higher value as recycled materials.

Wind Blade Computational Models
A publically available 100 m long prototype wind turbine blade model (SNL-100-01) that was designed by Sandia National Laboratories [12] was used in this study for demonstration purposes. This model, which has not been manufactured, has GFRP in most of the shell/skin structure, and a smaller amount of CFRP in the shear webs and spar caps. The geometry is defined by 25 different airfoil shapes. A total of 393 solid and sandwich composite material lay-ups are used in the blade. The software tool Numerical Manufacturing and Design Tool (NuMAD) [13] was used build the three-dimensional model. Model parameters are the airfoil types, station parameters, division points, composite materials, and shear web division points. Figure 6 shows a finalized version of the SNL-100-01 100 m blade. The different colors in the figure represent the locations of the different materials in the blade. Blades in the 30-50 m length range are typically made of only GFRP. Longer blades (50-80 m) also use some CFRP for increased stiffness. Blade designs are proprietary and wind power companies do not release specific details of their materials and shapes. This study used the Sandia 100 m long glass and carbon blade model as an example. The architectural graphics software Rhino 3D [14] was used to render the blade. Rendering the blade with its actual material thicknesses and real shape is required to extract realistic segments for architectural applications. For structural and aerodynamic modeling only a wireframe finite-element model is typically needed. Figure 7 shows a rendered isometric view of the SNL-100-01 blade. Three end-of-life (EOL) options for FRP wind blades [9] are currently possible-disposal, recovery, and reuse. The two options to dispose of FRP composites at the present involve landfilling or incineration (with or without energy recovery and/or silica ash recovery). Recovery options consist of reclamation of the constituent fibers or the resins by thermo-chemical methods or recovering of small pieces of granular FRP material for use as filler material in concrete or other composites by cutting, shredding, or grinding [10,11]. Reuse options consist of reusing the entire FRP blade or large parts of it in new structural applications. Reuse options are the primary focus of this paper since landfilling and incineration are environmentally harmful and recovery methods are not currently economical for glass fiber reinforced polymer (GFRP), of which the vast majority of current blades are fabricated. There is significant current research [10] in recovering carbon fiber reinforced polymer (CFRP) materials which have higher value as recycled materials.

Wind Blade Computational Models
A publically available 100 m long prototype wind turbine blade model (SNL-100-01) that was designed by Sandia National Laboratories [12] was used in this study for demonstration purposes. This model, which has not been manufactured, has GFRP in most of the shell/skin structure, and a smaller amount of CFRP in the shear webs and spar caps. The geometry is defined by 25 different airfoil shapes. A total of 393 solid and sandwich composite material lay-ups are used in the blade. The software tool Numerical Manufacturing and Design Tool (NuMAD) [13] was used build the three-dimensional model. Model parameters are the airfoil types, station parameters, division points, composite materials, and shear web division points. Figure 6 shows a finalized version of the SNL-100-01 100 m blade. The different colors in the figure represent the locations of the different materials in the blade. Blades in the 30-50 m length range are typically made of only GFRP. Longer blades (50-80 m) also use some CFRP for increased stiffness. Blade designs are proprietary and wind power companies do not release specific details of their materials and shapes. This study used the Sandia 100 m long glass and carbon blade model as an example. The architectural graphics software Rhino 3D [14] was used to render the blade. Rendering the blade with its actual material thicknesses and real shape is required to extract realistic segments for architectural applications. For structural and aerodynamic modeling only a wireframe finite-element model is typically needed. Figure 7 shows a rendered isometric view of the SNL-100-01 blade.

Root-Foundation System
The root segment of the SNL-100-01 blade has circular and elliptical cross sections. The top and bottom halves of the blade shell consist of a variety of FRP materials arranged in different layers: gelcoat; resin; triaxial fiber fabrics; and unidirectional fiber [12]. At its thickest point, the root has an Based on the Yucatan 2014 surveys [8], flooding is the second most damaging environmental occurrence to informal houses (wind and rain being the first). Elevating homes is proposed to avoid flooding damage. By cutting the wind blade root section (closest to the turbine hub) into short segments, platforms suitable for home elevations can be obtained. The resulting platforms have cylindrical or elliptical cross sections. One meter high platforms of different root sections are shown alongside a rendering of a typical rectangular masonry house with dimensions of 7 m long, 5 m wide, and 2.7 m high are shown in Figure 8. The platforms would have to be driven into the ground. If a higher elevation for a house is desired, larger segmented platforms can be extracted from the root to provide adequate embedment. The inside of the platform may be filled with a rubble. Figure 9 shows houses being elevated off the ground by such platforms (scaled down for the 100 m blade to fit the size of the house).

Root-Foundation System
The root segment of the SNL-100-01 blade has circular and elliptical cross sections. The top and bottom halves of the blade shell consist of a variety of FRP materials arranged in different layers: gelcoat; resin; triaxial fiber fabrics; and unidirectional fiber [12]. At its thickest point, the root has an Based on the Yucatan 2014 surveys [8], flooding is the second most damaging environmental occurrence to informal houses (wind and rain being the first). Elevating homes is proposed to avoid flooding damage. By cutting the wind blade root section (closest to the turbine hub) into short segments, platforms suitable for home elevations can be obtained. The resulting platforms have cylindrical or elliptical cross sections. One meter high platforms of different root sections are shown alongside a rendering of a typical rectangular masonry house with dimensions of 7 m long, 5 m wide, and 2.7 m high are shown in Figure 8. The platforms would have to be driven into the ground. If a higher elevation for a house is desired, larger segmented platforms can be extracted from the root to provide adequate embedment. The inside of the platform may be filled with a rubble. Figure 9 shows houses being elevated off the ground by such platforms (scaled down for the 100 m blade to fit the size of the house).

Root-Foundation System
The root segment of the SNL-100-01 blade has circular and elliptical cross sections. The top and bottom halves of the blade shell consist of a variety of FRP materials arranged in different layers: gelcoat; resin; triaxial fiber fabrics; and unidirectional fiber [12]. At its thickest point, the root has an Based on the Yucatan 2014 surveys [8], flooding is the second most damaging environmental occurrence to informal houses (wind and rain being the first). Elevating homes is proposed to avoid flooding damage. By cutting the wind blade root section (closest to the turbine hub) into short segments, platforms suitable for home elevations can be obtained. The resulting platforms have cylindrical or elliptical cross sections. One meter high platforms of different root sections are shown alongside a rendering of a typical rectangular masonry house with dimensions of 7 m long, 5 m wide, and 2.7 m high are shown in Figure 8. The platforms would have to be driven into the ground. If a higher elevation for a house is desired, larger segmented platforms can be extracted from the root to provide adequate embedment. The inside of the platform may be filled with a rubble. Figure 9 shows houses being elevated off the ground by such platforms (scaled down for the 100 m blade to fit the size of the house).

Doors and Window Covers
Most door and window fixtures in the informal houses along the Yucatan coast are scavenged and are particularly susceptible to water ingress. Three shear webs connect the top and bottom halves of the blade shell and run along the length of the blade. The shear webs are made of a sandwich composite that has a 60-mm-thick foam core (shown in yellow in Figure 10 Figure 10 shows the three shear webs extracted from the SNL-100-01 wind blade model. Two rectangular virtual cutting planes, one meter apart, are superimposed onto the shear webs. These two planes show the longitudinal cuts that would be needed to produce solid straight one meter high sandwich panels. Figures 11 and 12 show cut-out segments of the shear webs being used as doors and windows covers for the model house, respectively.

Doors and Window Covers
Most door and window fixtures in the informal houses along the Yucatan coast are scavenged and are particularly susceptible to water ingress. Three shear webs connect the top and bottom halves of the blade shell and run along the length of the blade. The shear webs are made of a sandwich composite that has a 60-mm-thick foam core (shown in yellow in Figure 10

Doors and Window Covers
Most door and window fixtures in the informal houses along the Yucatan coast are scavenged and are particularly susceptible to water ingress. Three shear webs connect the top and bottom halves of the blade shell and run along the length of the blade. The shear webs are made of a sandwich composite that has a 60-mm-thick foam core (shown in yellow in Figure 10 Figure 10 shows the three shear webs extracted from the SNL-100-01 wind blade model. Two rectangular virtual cutting planes, one meter apart, are superimposed onto the shear webs. These two planes show the longitudinal cuts that would be needed to produce solid straight one meter high sandwich panels. Figures 11 and 12 show cut-out segments of the shear webs being used as doors and windows covers for the model house, respectively.   Figure 10 shows the three shear webs extracted from the SNL-100-01 wind blade model. Two rectangular virtual cutting planes, one meter apart, are superimposed onto the shear webs. These two planes show the longitudinal cuts that would be needed to produce solid straight one meter high sandwich panels. Figures 11 and 12 show cut-out segments of the shear webs being used as doors and windows covers for the model house, respectively.

Roof Frames
In Figure 13, the leading-edge (the rounded panels at the front of the blade shell) has been removed from a blade segment to leave the three shear webs and the trailing-edge panels. The leading top and bottom panels have then been separated to make two roof frames. The shear webs (discussed above) run up to 80 m down the blade length, are over 2 m high at their highest point, most importantly, they are straight, making them easy to line up geometrically with other structural elements found in housing construction. To extract the roof frames, the panels must be sliced at an angle so that the cut bisects the shear webs and passes through the joint at the tip of the trailing-edge as seen in Figure 13. Bisecting the blade segment in this manner results in one roof frame from the bottom of the blade and another from the top. These two roof frames are similar, but not identical. Both have the same cross-sectional length, height, and material construction. However, the top roof frame has a concave-down roof curvature, while the bottom roof frame has an inflection point midway along its roof curvature. This geometric difference can be observed in Figure 14, where both half-trusses are displayed next to one another.

Roof Frames
In Figure 13, the leading-edge (the rounded panels at the front of the blade shell) has been removed from a blade segment to leave the three shear webs and the trailing-edge panels. The leading top and bottom panels have then been separated to make two roof frames. The shear webs (discussed above) run up to 80 m down the blade length, are over 2 m high at their highest point, most importantly, they are straight, making them easy to line up geometrically with other structural elements found in housing construction. To extract the roof frames, the panels must be sliced at an angle so that the cut bisects the shear webs and passes through the joint at the tip of the trailing-edge as seen in Figure 13. Bisecting the blade segment in this manner results in one roof frame from the bottom of the blade and another from the top. These two roof frames are similar, but not identical. Both have the same cross-sectional length, height, and material construction. However, the top roof frame has a concave-down roof curvature, while the bottom roof frame has an inflection point midway along its roof curvature. This geometric difference can be observed in Figure 14, where both half-trusses are displayed next to one another.

Roof Frames
In Figure 13, the leading-edge (the rounded panels at the front of the blade shell) has been removed from a blade segment to leave the three shear webs and the trailing-edge panels. The leading top and bottom panels have then been separated to make two roof frames. The shear webs (discussed above) run up to 80 m down the blade length, are over 2 m high at their highest point, most importantly, they are straight, making them easy to line up geometrically with other structural elements found in housing construction. To extract the roof frames, the panels must be sliced at an angle so that the cut bisects the shear webs and passes through the joint at the tip of the trailing-edge as seen in Figure 13. Bisecting the blade segment in this manner results in one roof frame from the bottom of the blade and another from the top. These two roof frames are similar, but not identical. Both have the same cross-sectional length, height, and material construction. However, the top roof frame has a concave-down roof curvature, while the bottom roof frame has an inflection point midway along its roof curvature. This geometric difference can be observed in Figure 14, where both half-trusses are displayed next to one another.

Interlocking Roof System
The FRP material found in the sandwich panels of the leading-edge of the blade comprises up to a third of the entire wind blade structure. A substantial amount of the FRP material can be salvaged from the leading-edge (rounded front) portion of a decommissioned blade. It is important to understand the geometric arrangement and material composition of the panels if large-sized FRP blade segment are to be extracted and used for architectural/structural applications. Figure 15 shows two blade segments extracted from 30 and 47 m from the root of the blade. Also in Figure 15, the leading edge FRP panels are cut and extracted from the rest of the blade segments. These panels are then reduced down into smaller shells, as shown in Figure 16, where the virtual cuts are represented by the black planes.
Arranging the cut-out segments in a configuration as seen in Figure 17 yields a possible roofing system for affordable housing.
There are two important issues to consider when extracting the leading edge panels and repurposing them for use in this roofing system.
First, there is a slight warping in blade geometry that is due to the twist along the length of the wind blade. The most noticeable effect of this can be observed at the transition between the root and wing segment of the blade. As the blade tapers off, the angle of twist decreases and the warping is less significant. Nonetheless, the extracted leading edge shells will not be perfectly straight, making the interlocking roof configuration difficult to arrange. The gaps formed in between the shell segments may prove to be an issue when providing a leak-proof roofing system. This may be

Interlocking Roof System
The FRP material found in the sandwich panels of the leading-edge of the blade comprises up to a third of the entire wind blade structure. A substantial amount of the FRP material can be salvaged from the leading-edge (rounded front) portion of a decommissioned blade. It is important to understand the geometric arrangement and material composition of the panels if large-sized FRP blade segment are to be extracted and used for architectural/structural applications. Figure 15 shows two blade segments extracted from 30 and 47 m from the root of the blade. Also in Figure 15, the leading edge FRP panels are cut and extracted from the rest of the blade segments. These panels are then reduced down into smaller shells, as shown in Figure 16, where the virtual cuts are represented by the black planes.
Arranging the cut-out segments in a configuration as seen in Figure 17 yields a possible roofing system for affordable housing.
There are two important issues to consider when extracting the leading edge panels and repurposing them for use in this roofing system.
First, there is a slight warping in blade geometry that is due to the twist along the length of the wind blade. The most noticeable effect of this can be observed at the transition between the root and wing segment of the blade. As the blade tapers off, the angle of twist decreases and the warping is less significant. Nonetheless, the extracted leading edge shells will not be perfectly straight, making the interlocking roof configuration difficult to arrange. The gaps formed in between the shell segments may prove to be an issue when providing a leak-proof roofing system. This may be

Interlocking Roof System
The FRP material found in the sandwich panels of the leading-edge of the blade comprises up to a third of the entire wind blade structure. A substantial amount of the FRP material can be salvaged from the leading-edge (rounded front) portion of a decommissioned blade. It is important to understand the geometric arrangement and material composition of the panels if large-sized FRP blade segment are to be extracted and used for architectural/structural applications. Figure 15 shows two blade segments extracted from 30 and 47 m from the root of the blade. Also in Figure 15, the leading edge FRP panels are cut and extracted from the rest of the blade segments. These panels are then reduced down into smaller shells, as shown in Figure 16, where the virtual cuts are represented by the black planes.
Arranging the cut-out segments in a configuration as seen in Figure 17 yields a possible roofing system for affordable housing.
There are two important issues to consider when extracting the leading edge panels and repurposing them for use in this roofing system.
First, there is a slight warping in blade geometry that is due to the twist along the length of the wind blade. The most noticeable effect of this can be observed at the transition between the root and wing segment of the blade. As the blade tapers off, the angle of twist decreases and the warping is less significant. Nonetheless, the extracted leading edge shells will not be perfectly straight, making the interlocking roof configuration difficult to arrange. The gaps formed in between the shell segments may prove to be an issue when providing a leak-proof roofing system. This may be addressed by cutting a small amount of materials off to produce tapered edges (in thickness direction) to make them perfectly fit. An alternative is to seal the gaps due to misfit with other materials. addressed by cutting a small amount of materials off to produce tapered edges (in thickness direction) to make them perfectly fit. An alternative is to seal the gaps due to misfit with other materials.   Second, as the wind blade tapers off after reaching its maximum chord length, the material thickness for the foam decreases. This means that at some points along the blade closer to the root the FRP pieces will be thicker than the pieces found further down the blade. This will raise some concerns when selecting curved segments for the interlocking-roof system. Having segments that are too thin or thick with respect to their adjacent segments will create additional gaps that need filling.  addressed by cutting a small amount of materials off to produce tapered edges (in thickness direction) to make them perfectly fit. An alternative is to seal the gaps due to misfit with other materials.   Second, as the wind blade tapers off after reaching its maximum chord length, the material thickness for the foam decreases. This means that at some points along the blade closer to the root the FRP pieces will be thicker than the pieces found further down the blade. This will raise some concerns when selecting curved segments for the interlocking-roof system. Having segments that are too thin or thick with respect to their adjacent segments will create additional gaps that need filling.  addressed by cutting a small amount of materials off to produce tapered edges (in thickness direction) to make them perfectly fit. An alternative is to seal the gaps due to misfit with other materials.   Second, as the wind blade tapers off after reaching its maximum chord length, the material thickness for the foam decreases. This means that at some points along the blade closer to the root the FRP pieces will be thicker than the pieces found further down the blade. This will raise some concerns when selecting curved segments for the interlocking-roof system. Having segments that are too thin or thick with respect to their adjacent segments will create additional gaps that need filling. Second, as the wind blade tapers off after reaching its maximum chord length, the material thickness for the foam decreases. This means that at some points along the blade closer to the root the FRP pieces will be thicker than the pieces found further down the blade. This will raise some concerns when selecting curved segments for the interlocking-roof system. Having segments that are too thin or thick with respect to their adjacent segments will create additional gaps that need filling. However, this would not be an issue if all the concave segments are tapered in one direction and all the convex segments are tapered in the opposite direction.

A Conceptual Housing Community
Building or retrofitting an affordable housing community with salvaged wind blade parts might resemble something like that depicted in Figure 18. In this representation, the root-foundation system has been used in all the houses, elevating them off the ground. All doors and windows have been modelled using the shear webs panels. Lastly, the roof frame and the interlocking roof configuration are shown in different scenarios. However, this would not be an issue if all the concave segments are tapered in one direction and all the convex segments are tapered in the opposite direction.

A Conceptual Housing Community
Building or retrofitting an affordable housing community with salvaged wind blade parts might resemble something like that depicted in Figure 18. In this representation, the root-foundation system has been used in all the houses, elevating them off the ground. All doors and windows have been modelled using the shear webs panels. Lastly, the roof frame and the interlocking roof configuration are shown in different scenarios.

Conclusions
The purpose of this paper was to present a conceptual solution to the impending issue of recycling decommissioned wind turbine blades. As discussed, a wind turbine blade, in this case, the SNL-100-01, can be presented as a wireframe model. From this rudimentary wireframe model, a blade can be reassembled as a 3D model for better architectural/mechanical analysis. Computer software like NuMAD and Rhino 3D made it possible to extract segments from a decommissioned SNL-100-01 wind blade and find real-life structural applications for affordable housing communities. However, this paper is a first step towards making the disposal of wind blades efficient and environmentally friendly. In time, this process of repurposing decommissioned wind blade parts must be further researched with regards to mechanical systems (MEP), structural analysis, logistics, and detailing, other architectural and infrastructural applications; cost and ease of dis-and reassembly; social accessibility and acceptability.

Conflicts of Interest:
The authors declare no conflict of interest. The funding sponsors had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, and in the

Conclusions
The purpose of this paper was to present a conceptual solution to the impending issue of recycling decommissioned wind turbine blades. As discussed, a wind turbine blade, in this case, the SNL-100-01, can be presented as a wireframe model. From this rudimentary wireframe model, a blade can be reassembled as a 3D model for better architectural/mechanical analysis. Computer software like NuMAD and Rhino 3D made it possible to extract segments from a decommissioned SNL-100-01 wind blade and find real-life structural applications for affordable housing communities. However, this paper is a first step towards making the disposal of wind blades efficient and environmentally friendly. In time, this process of repurposing decommissioned wind blade parts must be further researched with regards to mechanical systems (MEP), structural analysis, logistics, and detailing, other architectural and infrastructural applications; cost and ease of dis-and re-assembly; social accessibility and acceptability.