Facile Synthesis of Ordered Mesoporous Orthorhombic Niobium Oxide (T-Nb 2 O 5 ) for High-Rate Li-Ion Storage with Long Cycling Stability

: Herein, we describe the synthesis and evaluation of hierarchical mesoporous orthorhombic niobium oxide (T-Nb 2 O 5 ) as an anode material for rechargeable lithium-ion batteries (LIB). The as-synthesized material addresses key challenges such as beneﬁcial porous structure, poor rate capability, and cycling performance of the anode for Li-ion devices. The physicochemical characterization results reveal hierarchical porous nanostructure morphology with agglomerated particles and a 20 to 25 nm dimension range. Moreover, the sample has a high speciﬁc surface area (~65 m 2 g − 1 ) and pore volume (0.135 cm 3 g − 1 ). As for the application in Li-ion devices, the T-Nb 2 O 5 delivered an initial discharging capacity as high as 225 mAh g − 1 at 0.1 A g − 1 and higher rate capability as well as remarkable cycling features (~70% capacity retention after 300 cycles at 250 mA g − 1 ) with 98% average Coulombic efﬁciency (CE). Furthermore, the scan rate-dependent charge storage mechanism of the T-Nb 2 O 5 electrode material was described, and the ﬁndings demonstrate that the electrode shows an evident and highly effective pseudocapacitive Li intercalation behaviour, which is crucial for understanding the electrode process kinetics. The origin of the improved performance of T-Nb 2 O 5 results from the high surface area and mesoporous structure of the nanoparticles.


Introduction
The ever-increasing worldwide population and the use of huge quantities of fossil fuel exacerbate environmental pollution challenges, prompting a quest for alternate or renewable energy sources in recent decades [1,2].Finding an excellent alternative energy system is only part of the problem, whereas creating a suitable energy storage system is essential.For this reason, many energy storage technologies have been researched during the past few years [3][4][5].Substantial energy density, high power characteristics, extended cycle lifetime, and superior safety are required for energy storage devices [6,7].Supercapacitors deliver charges rather quickly because charge storage comprises physical adsorption and desorption of charges on the surface of the electrode materials [8,9].Supercapacitors, on the other hand, have a low energy density [10,11].In contrast, most LIBs have large energy densities due to the ability of the bulk structure to hold Li ions and the high operating voltage of the intercalation compounds [12].However, the slow solid-state Li +

ion diffusion
Batteries 2023, 9, 357 2 of 13 in the bulk host structure results in poor power characteristics and significant volume changes during repeated intercalation/extraction procedures, limiting the ability to satisfy current needs [13].Reducing the size of intercalation-based active materials to the nanoscale improves the cyclability and rate performance of LIBs.The energy properties deteriorate with this method due to the substantial amplification of undesirable side effects in the anodic potential area [14].Innovative electrode materials and complex designs are required to build enhanced energy storage devices with superior energy and power densities and long cycle lifetimes.
Carbonaceous materials, mainly graphite, have been widely used as anode materials due to their low working voltage, abundant production, and low cost [15].However, their use in high-energy LIBs is severely limited by their low theoretical capacity and poor rate capability [15,16].Transition metal oxides (TMO x ; TM = Fe, Mn, Ni, Co, Sn, Si, Cu, and so on) with high theoretical capacities have recently attracted a lot of interest for anode materials in the next generation of batteries because they provide high Li + storage capacities [17,18].Unfortunately, the Li + insertion and reinsertion process causes huge volume expansion and severe particle aggregation, resulting in electrode pulverization and particle contact breaking, leading to considerable capacity loss and poor cycle capability [18].Lithium titanate (Li 4 Ti 5 O 12 ) is another notable anode material that provides a high chargedischarge voltage of 1.55 V (vs.Li/Li + ) and extremely stable cycling stability owing to small volume change that occurs during the Li + insertion and reinsertion process [19].However, the poor electronic conductivity, low theoretical capacity (170 mA h g −1 ), and high working voltage have restricted its practical production.Recently, Nb 2 O 5 has been investigated as an appealing anode material for LIBs due to its intercalation pseudocapacitance characteristic, which enables insertion/extraction mechanism for Li ions with an enhanced potential range, preventing the formation of Li dendrites [6,[20][21][22].The rich redox chemistry of Nb 2 O 5 (Nb 5+ /Nb 4+ , Nb 4+ /Nb 3+ ) contributes to high specific capacity [2].Nb 2 O 5 has significant safety benefits because of its suitable working voltage plateau (1.0−2.0V).Due to its affordability, environmental friendliness, high corrosive resistance, and stability, it is an ideal electrode material in LIBs [21][22][23][24].
Furthermore, the electrochemical properties of Nb 2 O 5 materials are largely influenced by their crystalline structure, morphology, and porous architecture [25].There are several polymorphic forms of Nb 2 O 5 , such as monoclinic, pseudohexagonal, orthorhombic, and amorphous Nb 2 O 5 forms [10].Among polymorphs, the orthorhombic phase (T-Nb 2 O 5 ) stands out as promising because the Li+ ion intercalation reaction may occur both at the crystal's surface and within its interior [26].The overall kinetics of the intercalation process in T-Nb 2 O 5 were unaffected by the solid-state diffusion of Li ions due to the mostly empty octahedral sites between (001) planes [27].As a result, the T-Nb 2 O 5 demonstrates pseudocapacitive behavior for fast Li + intercalation and reversible and quick electrochemical kinetics [16,28,29].According to evidence, the T-Nb 2 O 5 had the highest capacity for charge storage.Researchers have studied a variety of T-Nb 2 O 5 nanostructures as anodes for LIBs, including nanorods [17], nanobelts [24,30], micro flowers [25], nanowires [26], nanofibers [31], hollow spheres [32], urchins [21], nanobelts [27], nanofilms [28], microspheres [22] and so forth.Among them, mesoporous nanostructures are more appealing due to their vast surface area and multiple paths for lithium-ion transport [2].
Several fabrication approaches have been used to create mesoporous Nb 2 O 5 [33].Using a graphene-silica nanosheet template assisted by the vapour hydrolysis method at 600 • C, Wang et al. synthesized mesoporous Nb 2 O 5 nanosheets with pores ranging from 3 to 20 nm [14].Li et al., made the mesoporous Nb 2 O 5 using template procedures and annealed it in air to produce non-uniform macropores of about 200 nm [19].Using a sophisticated template process, Chen et al. created mesoporous Nb 2 O 5 with pore sizes ranging from 4.3 to 7.5 nm [34].Using three-step oxidation phases, Kong et al. created a mesoporous Nb 2 O 5 @carbon core-shell structure with pore diameters of 2-3 nm [30].Recently, Pligovka et al., employed highly sophisticated and advanced techniques such as successive sputtering and sequential anodization followed by potentiodynamic re-anodization to fabricate niobium oxide nanocolumns with modulated diameters onto Al/Nb bilayer specimen silicon wafer [35] and skittle-, medusa-, and goblet-like niobia embryos onto Al/Nb bilayer specimen silicon wafer [36].Using these methods to generate mesoporous structures are inherently time-consuming, challenging and need a specialized template.Therefore, finding a quick and effective approach to prepare a porous T-Nb 2 O 5 is still challenging.A sol-gel approach was chosen to prepare T-Nb 2 O 5 nanoparticles because of its low working temperatures and the ability to make consistent particle sizes (i.e., significant control of particle sizes) with specific morphologies, as well as the ease of carrying out experiments compared to other synthesis methods [37,38].It is a standard, commercial, and economical approach to modifying the texture of substrates using the sol-gel technique.
In this study, we report the synthesis of mesoporous T-Nb 2 O 5 nanoparticles by heating the peroxo niobic acid sol (Nb 2 (O 2 ) 2 O 3 •6H 2 O), produced by peptizing the niobic acid precipitate with aqueous H 2 O 2 solution.The structural characteristics and charge-discharge performance of Nb 2 O 5 were investigated using a combination of physicochemical and electrochemical techniques.The synthesized Nb 2 O 5 crystallized in the orthorhombic phase and exhibited a nanoparticle shape with enhanced specific surface area (65 m 2 g −1 ).The T-Nb 2 O 5 displayed a high discharge capacity and improved rate capability, a remarkable cycle life (70% capacity retention) and an average CE of 98% over 300 cycles.

Synthesis of Nb 2 O 5 Nanoparticles
Niobium (V) oxide (Nb 2 O 5 ) nanoparticles have been produced using a previously disclosed method [38].Under vigorous stirring, 0.5 g of niobium pentachloride (NbCl 5 , 99%, Alfa Aesar) powder was dissolved in 2 mL of ethanol solution (EtOH, 99.5%, Alfa Aesar) and left until a clear NbCl 5 EtOH yellow solution appeared.By dropwise addition of 20 mL aqueous ammonia solution (0.3 M), a white-coloured precipitate of niobic acid (Nb 2 O 5 •nH 2 O) emerged from this solution.The residue was centrifuged and rinsed with deionized water numerous times.The resultant solid product of Nb 2 O 5 •nH 2 O precursor was then dispersed in 10 mL of 30 wt% H 2 O 2 (Merck Chemicals) and agitated for 5 min in an ice bath, yielding a transparent yellow-sol (from now on referred to as "peroxo niobic acid sol, (Nb 2 (O 2 ) 2 O 3 •6H 2 O)").This sol was transferred to a 20 mL autoclave and baked at 80 • C for 48 h.The resultant product was dried and sintered at 700 • C for 3 h at a heating rate of 5 • C/min to generate T-Nb 2 O 5 nanoparticles.

Materials Characterization
Thermogravimetric analysis (TGA) and differential thermal analysis (DTA) of the precursor were done in air using thermal analysis (TA) in a TGAQ500V20.10Build 36 instrument from 25 to 800 • C with a heating rate of 20 • C min −1 .The X-ray diffraction (XRD) studies were performed on a Rigaku Ultima IV powder X-ray diffractometer equipped with a Ni-filtered Cu Kα radiation source.To get the lattice parameters and structural parameters, the resulting XRD data was refined using Rietveld analysis using the GSAS software program.Scanning electron microscopy (FESEM; FEI, Quanta 400; SEMTech Solutions, Inc., North Billerica, MA, USA), transmission electron microscopy (TEM, JOEL JEM 3010; JEOL Ltd., Freising, Germany), and high-resolution TEM examinations were undertaken to expose the sample shape and structure.Prior to TEM examinations, the sample powder was diluted in ethanol using a sonicator before being drop-cast onto a Cu grid and vacuum dried.Nitrogen adsorption-desorption measurements were studied at 77 K with a Micromeritics ASAP 2020 physisorption tool.Before determining the isotherm, the sample was degassed in a vacuum for 12 h at 150 • C. The BET (Brunauer-Emmett-Teller) model was used to compute the specific surface area.The Barrett-Joyner-Halenda (BJH) approach was used to estimate the pore-size distribution curve based on the isotherm's desorption branch.The maximum position in the pore-size distribution was used to calculate the pore diameter.X-ray photoelectron spectroscopy (XPS) spectra were taken at the core-level using Omicron Nanotechnology equipment and a monochromatic Mg Kα (hν = 1253.6eV) radiation source.The binding energy (BE) was calibrated using containment carbon (C1s = 284.5 eV).

Electrochemical Measurements
The electrochemical properties of mesoporous T-Nb 2 O 5 were studied using galvanostatic cycling in a CR2025-type coin cell.The active component (T-Nb 2 O 5 ) was blended with acetylene black and the binder (polyvinylidene fluoride, PVDF, soaked in N-methyl pyrrolidinone) in a 75:15:10 weight ratio.Using a doctor blade, the slurry was then evenly applied to Cu-disk current collectors.After that, the electrodes were vacuum-dried overnight at 80 • C. The loading density of electroactive substances was approximately 1.5 mg cm −2 .In an argon-filled glove box (both moisture and oxygen levels were 0.3 ppm), the electrodes were assembled in CR2025 coin cells.The reference and counter electrodes were Li metal, whereas the separator was a porous polypropylene membrane (Celgard 2500; Celgard, Charlotte, NC, USA).The Celgard 2500 separator had a porosity of 55% and an average pore size of 28 nm.The electrolyte was a 1:1 v/v mixture of EC and DMC solvents.A LAND battery test device was used to measure the galvanostatic charge-discharge (GCD) performance of the coin cells'.Electrochemical data from cyclic voltammetry (CV; 1-3 V) and impedance spectroscopy were recorded using a Versa-STAT MC multichannel potentiostat/galvanostat electrochemical workstation (Princeton Applied Research).

Structural Characterizations
Based on literature reports [39,40], we described a possible reaction process for the synthesis of T-Nb 2 O 5 which includes the following steps: (i) precipitation of niobic acid (Equations ( 1)-( 4)), (ii) formation of peroxo niobic acid sol (Equation ( 5)), and (iii) formation of T-Nb 2 O 5 by thermal annealing of the peroxo niobic acid sol at 700 • C (Equation ( 6)): TGA and DTG analysis was used to estimate the weight loss of Nb 2 (O 2 ) 2 O 3 •6H 2 O precursor with temperature, as shown in Figure 1.The steady weight loss that was seen up to 450 • C and the weight loss recorded below 100 • C were caused by the removal of adsorbed water molecules.The weight loss seen in multiple stages between 100 and 400 • C is ascribed to the loss of crystalline water and the pyrolysis of "peroxo niobic acid sol" due to the creation of the Nb 2 O 5 phase [22].No discernible weight loss between 400 and 700 • C indicates that Nb 2 O 5 nanoparticles crystallize at these temperatures.Thus, a sintering temperature of 700 • C was chosen to synthesize T-Nb 2 O 5 nanoparticles.The Nb ions in the T-Nb 2 O 5 crystal structure coordinate with six or seven oxygen ions, generating highly deformed octahedral (NbO 6 ) and pentagonal bipyramid (NbO 7 ) frameworks.These polyhedra were linked together via edge-or corner-sharing in the ab-plane and cornersharing along the c-axis, resulting in a framework similar to the "room and pillar [41,42].The distinctive "room-and-pillar" NbO 6 /NbO 7 framework structure can offer a stable host as well as simple diffusion pathways for Li intercalation [43].distinctive "room-and-pillar" NbO6/NbO7 framework structure can offer a stable host as well as simple diffusion pathways for Li intercalation [43].The XRD pattern of uncalcined peroxo niobic acid precursor powder reveals wide diffraction peaks (Figure 2B), showing that the substance is amorphous in nature.The material clearly shows crystalline diffraction peaks after annealing the precursor powder at 700 °C, which is indexed to orthorhombic Nb2O5 (T-Nb2O5, space group: Pbam).It is worth noting that the absence of additional diffraction peaks implies that the produced orthorhombic Nb2O5 is of excellent purity.The Rietveld refinement approach was then used to investigate the crystalline phase development and lattice properties of T-Nb2O5.The experimental results and the X-ray Rietveld refinement based on the orthorhombic phase are shown in Figure 2C.The structure refinement parameters are Rp = 5.0%, Rwp = 6.5%, and χ 2 = 6.9, respectively.The lowered χ 2 indicates that The X-ray Rietveld refinement exercise fits the experimental data well.The refined lattice constants are a = 6.142, b = 29.119,c = 3.908 and V = 707.29 Å 3 ; these values agree with the literature [42].SEM and TEM examinations were used to study the surface shape and structure of the sample (Figure 3). Figure 3A,B show that all the particles in the T-Nb2O5 sample were agglomerated and have an interlocking porous structure.The TEM image (Figure 3C) reveals a uniform distribution of nanoparticles with dimensions ranging from 20 to 25 nm, and the particles are agglomerated.The lattice fringe spacing in the high-resolution TEM (Figure 3D) is 0.386 nm, corresponding to the (001) plane of T-Nb2O5.
The surface textural characteristics of the as-prepared T-Nb2O5 were determined by implementing nitrogen sorption isotherms at 77 K using nitrogen adsorbent.As seen from Figure 4A, the T-Nb2O5 isotherm exhibits a typical type IV with a clear H3-type hysteresis loop (based on IUPAC classification) [44] with a broad capillary condensation range starting at high relative pressures (P/P0) of 0.4 and extending to 0.8, demonstrating that the mesoporous characteristic of the sample gives rise to a relatively high specific surface area of 65 m 2 g −1 and pore volume of 0.135 cm 3 g −1 .The BJH approach was used to analyze the pore-size distribution (Figure 4B).The sample's pore-size-distribution curve shows a bimodal pore-size distribution, with most pores constituted of micropores and mesopores less than 3.5 nm and an average pore width of 2.20 nm, representing mesoporous characteristics.It is worth mentioning that the computed BET-specific surface area of our T-Nb2O5 nanoparticles is much greater than that of previously reported Li-ion battery anodes [22,23,27,31] and Li-selective adsorbates [45][46][47][48].The high specific surface area, large pore volume, and critical micro-and mesopores of T-Nb2O5 would be advantageous because they provide many electro-active sites for the uptake and release of Li + ions from the electrolyte during repeated charge-discharge cycling.As a result, T-Nb2O5 The XRD pattern of uncalcined peroxo niobic acid precursor powder reveals wide diffraction peaks (Figure 2B), showing that the substance is amorphous in nature.The material clearly shows crystalline diffraction peaks after annealing the precursor powder at 700 • C, which is indexed to orthorhombic Nb 2 O 5 (T-Nb 2 O 5 , space group: Pbam).It is worth noting that the absence of additional diffraction peaks implies that the produced orthorhombic Nb 2 O 5 is of excellent purity.The Rietveld refinement approach was then used to investigate the crystalline phase development and lattice properties of T-Nb 2 O 5 .The experimental results and the X-ray Rietveld refinement based on the orthorhombic phase are shown in Figure 2C.The structure refinement parameters are R p = 5.0%, R wp = 6.5%, and χ 2 = 6.9, respectively.The lowered χ 2 indicates that The X-ray Rietveld refinement exercise fits the experimental data well.The refined lattice constants are a = 6.142, b = 29.119,c = 3.908 and V = 707.29 Å 3 ; these values agree with the literature [42].SEM and TEM examinations were used to study the surface shape and structure of the sample (Figure 3). Figure 3A,B show that all the particles in the T-Nb 2 O 5 sample were agglomerated and have an interlocking porous structure.The TEM image (Figure 3C) reveals a uniform distribution of nanoparticles with dimensions ranging from 20 to 25 nm, and the particles are agglomerated.The lattice fringe spacing in the high-resolution TEM (Figure 3D) is 0.386 nm, corresponding to the (001) plane of T-Nb 2 O 5 .
The surface textural characteristics of the as-prepared T-Nb 2 O 5 were determined by implementing nitrogen sorption isotherms at 77 K using nitrogen adsorbent.As seen from Figure 4A, the T-Nb 2 O 5 isotherm exhibits a typical type IV with a clear H3-type hysteresis loop (based on IUPAC classification) [44] with a broad capillary condensation range starting at high relative pressures (P/P0) of 0.4 and extending to 0.8, demonstrating that the mesoporous characteristic of the sample gives rise to a relatively high specific surface area of 65 m 2 g −1 and pore volume of 0.135 cm 3 g −1 .The BJH approach was used to analyze the pore-size distribution (Figure 4B).The sample's pore-size-distribution curve shows a bimodal pore-size distribution, with most pores constituted of micropores and mesopores less than 3.5 nm and an average pore width of 2.20 nm, representing mesoporous characteristics.It is worth mentioning that the computed BET-specific surface area of our T-Nb 2 O 5 nanoparticles is much greater than that of previously reported Liion battery anodes [22,23,27,31] and Li-selective adsorbates [45][46][47][48].The high specific surface area, large pore volume, and critical micro-and mesopores of T-Nb 2 O 5 would be advantageous because they provide many electro-active sites for the uptake and release of Li + ions from the electrolyte during repeated charge-discharge cycling.As a result, T-Nb 2 O 5 nanoparticles greatly improved battery performance, including high specific capacity and high cycle stability.tion XPS spectra of Nb 3d (Figure 4C) exhibit two unique peaks centered at BE of 207.5 eV for Nb 3d5/2 and 210.2 eV for Nb 3d5/2 [23].The BE values agreed with the literature and verified that the bulk of the Nb element in the synthesized material is mostly Nb 5+ with minimal Nb 4+ , owing to surface reduction at high temperatures [33,39].Figure 4D shows the deconvolution of the O 1s XPS spectra into two peaks.The strong peak at BE of 529.8 eV corresponds to O-Nb, while the peak at 532.1 eV belongs to adsorbed oxygen [39,41].

Electrochemical Studies
To evaluate the electrochemical performance of Li + ion intercalation into or deintercalation from mesoporous T-Nb2O5, coin cell-based batteries were assembled with mesoporous T-Nb2O5 as the working electrode and Li foil as the counter and reference electrodes.Figure 5A represents the initial three sequential CV curves of the T-Nb2O5 electrode collected at a sweep rate of 5 mV s −1 within the applied potential window of 1.0-3.0V (vs.Li + /Li).Three CV curves overlap nicely and reveal excellent reversibility of Li-storage characteristics.Furthermore, the shape of the CV curves reveals a prominent redox response with a couple of broad redox peaks within the applied potential range due to Li + insertion/extraction and the redox of niobium ions i.e., Nb 5+ ↔Nb 4+ and Nb 4+ ↔Nb 3+ , according to the eqn.To further evaluate the electrochemical kinetic characteristics of the mesoporous T-Nb2O5 electrode, CV curves were generated at various sweep rates ranging from 0.5 to 30 mV s −1 (Figure 5B).Peak currents (both anodic and cathodic) vary drastically as the scan rate increases, owing to diffusion-controlled ohmic contributions [39,50].The kinetic XPS was used to evaluate the surface elemental compositions and chemical states of metal ions in T-Nb 2 O 5 .XPS is a popular non-destructive technology for identifying the chemical states of metal and nonmetal ions that are commonly utilized in investigating Li-ion battery electrode materials.Due to the strong spin-orbit splitting, the high-resolution XPS spectra of Nb 3d (Figure 4C) exhibit two unique peaks centered at BE of 207.5 eV for Nb 3d 5/2 and 210.2 eV for Nb 3d 5/2 [23].The BE values agreed with the literature and verified that the bulk of the Nb element in the synthesized material is mostly Nb 5+ with minimal Nb 4+ , owing to surface reduction at high temperatures [33,39].Figure 4D shows the deconvolution of the O 1s XPS spectra into two peaks.The strong peak at BE of 529.8 eV corresponds to O-Nb, while the peak at 532.1 eV belongs to adsorbed oxygen [39,41].

Electrochemical Studies
To evaluate the electrochemical performance of Li + ion intercalation into or deintercalation from mesoporous T-Nb 2 O 5 , coin cell-based batteries were assembled with mesoporous T-Nb 2 O 5 as the working electrode and Li foil as the counter and reference electrodes.Figure 5A represents the initial three sequential CV curves of the T-Nb 2 O 5 electrode collected at a sweep rate of 5 mV s −1 within the applied potential window of 1.0-3.0V (vs.Li + /Li).Three CV curves overlap nicely and reveal excellent reversibility of Li-storage characteristics.Furthermore, the shape of the CV curves reveals a prominent redox response with a couple of broad redox peaks within the applied potential range due to Li + insertion/extraction and the redox of niobium ions i.e., Nb 5+ ↔Nb 4+ and Nb 4+ ↔Nb 3+ , according to the eqn.[6,[49][50][51].
where a denotes the variable parameter and b is the parameter linked with the charge storage mechanism, which may be obtained by calculating the slope of the log (i) vs. log (ν) plot.Usually, the b = ∼0.5 indicates the electrochemical process is a diffusion-controlled and battery-type reaction, and the b = ∼1 represents a surface-controlled pseudocapacitive.The b-values (Figure 5C) were calculated to be ∼0.74 and ∼0.72, respectively.For both anodic and cathodic peaks, this suggests a contribution from both the diffusion and capacitive processes.The discharging-charging performance of the mesoporous T-Nb2O5 electrode was assessed via GCD measurements between 1.0 and 3.0 V (Figure 6). Figure 6A depicts typical GCD patterns for the first ten cycles of the T-Nb2O5 electrode at 100 mA g −1 .Similar to some other reports [22,39,48], all of the GCD curves exhibit a smooth sloping profile, attributable to the change of Nb2O5 ↔ LixNb2O5, a characteristic of insertion-type electrochemical reactions.At the beginning of discharging, it exhibits a discharging capacity as high as 225 mAh g −1 .With an initial charging capacity of 180 mAh g −1 , the T-Nb2O5 electrode had 80% initial CE, however, it lost some of its capacity.The subsequent (from the second to the tenth) cycle discharge capacities were 190, 183, 180, 178, 177, 177.6, 178, 178, and 179 mAh g −1 , respectively.The high discharge capacity and low CE of the first cycle may be caused by the formation of SEI film on the electrode surface [29].To further evaluate the electrochemical kinetic characteristics of the mesoporous T-Nb 2 O 5 electrode, CV curves were generated at various sweep rates ranging from 0.5 to 30 mV s −1 (Figure 5B).Peak currents (both anodic and cathodic) vary drastically as the scan rate increases, owing to diffusion-controlled ohmic contributions [39,50].The kinetic information of the Li + intercalation can be obtained by the relationship between the peak current (i) vs. sweep rate (ν, mV/s) [6,[52][53][54]: where a denotes the variable parameter and b is the parameter linked with the charge storage mechanism, which may be obtained by calculating the slope of the log (i) vs. log (ν) plot.Usually, the b = ~0.5 indicates the electrochemical process is a diffusion-controlled and battery-type reaction, and the b = ~1 represents a surface-controlled pseudocapacitive.The b-values (Figure 5C) were calculated to be ~0.74 and ~0.72, respectively.For both anodic and cathodic peaks, this suggests a contribution from both the diffusion and capacitive processes.
The discharging-charging performance of the mesoporous T-Nb 2 O 5 electrode was assessed via GCD measurements between 1.0 and 3.0 V (Figure 6). Figure 6A depicts typical GCD patterns for the first ten cycles of the T-Nb 2 O 5 electrode at 100 mA g −1 .Similar to some other reports [22,39,48], all of the GCD curves exhibit a smooth sloping profile, attributable to the change of Nb 2 O 5 ↔ Li x Nb 2 O 5 , a characteristic of insertion-type electrochemical reactions.At the beginning of discharging, it exhibits a discharging capacity as high as 225 mAh g −1 .With an initial charging capacity of 180 mAh g −1 , the T-Nb 2 O 5 electrode had 80% initial CE, however, it lost some of its capacity.The subsequent (from the second to the tenth) cycle discharge capacities were 190, 183, 180, 178, 177, 177.6, 178, 178, and 179 mAh g −1 , respectively.The high discharge capacity and low CE of the first cycle may be caused by the formation of SEI film on the electrode surface [29].The as-prepared T-Nb2O5 GCD profiles of the electrode at different current densities ranging from 100 to 5000 mA g −1 are shown in Figure 6B.It is evident that as the current density increases, the discharge curves drop and the charge curves rise, indicating an increase in polarization.It is evident that as current density increases the discharge curves drop and the charge curves rise, indicating that the polarization is increased.Surprisingly, the mesoporous T-Nb2O5 nanoparticles electrode can operate smoothly even at a high applied current density of 5 A g −1 ; nevertheless, there is some noticeable capacity loss at high current densities.The gradual evolution of charging-discharging voltage profiles suggests that T-Nb2O5 remains in a stable structure even after repeated discharging-charging cycling.Figure 6C depicts the discharge capacity of the T-Nb2O5 electrode as a function of current density.The graph clearly shows how the electrode's capacity rapidly degrades as the applied current density increases.At high current densities, this is usually caused by the sluggish diffusion of Li + into the T-Nb2O5 interior [16,55,56].The discharge capacity could be restored to its initial condition after a series of rate tests when the current density was reversed back to 100 mA g −1 , demonstrating that the T-Nb2O5 electrode possessed significant reversibility.
For the development of Li-ion batteries to be used in practical applications, the electroactive materials must exhibit long-term cycle stability.To study the long-cycle retention properties in more detail, the T-Nb2O5 electrode was exposed to a GCD test at 0.25 A g −1 in a potential window of 1.0 to 3.0 V (Li/Li + ) for up to 300 cycles (Figure 6D).The electrode gradually lost capacity with increasing cycle number and maintained a discharge capacity of 142 mAh g −1 (70%) even at the end of 300 cycles.Meanwhile, the cell continued a high average CE of 98% over 300 cycles.It is worth noting that the performance of T-Nb2O5 in terms of its specific capacity, cyclability, and rate capability is comparable and even superior to that reported for other T-Nb2O5 nanostructures [22,24,25,41].The enormous specific surface area, mesoporous structure, and nanoparticle shape of T-Nb2O5 improve performance because they can offer a large number of electroactive sites for the uptake and For the development of Li-ion batteries to be used in practical applications, the electroactive materials must exhibit long-term cycle stability.To study the long-cycle retention properties in more detail, the T-Nb 2 O 5 electrode was exposed to a GCD test at 0.25 A g −1 in a potential window of 1.0 to 3.0 V (Li/Li + ) for up to 300 cycles (Figure 6D).The electrode gradually lost capacity with increasing cycle number and maintained a discharge capacity of 142 mAh g −1 (70%) even at the end of 300 cycles.Meanwhile, the cell continued a high average CE of 98% over 300 cycles.It is worth noting that the performance of T-Nb 2 O 5 in terms of its specific capacity, cyclability, and rate capability is comparable and even superior to that reported for other T-Nb 2 O 5 nanostructures [22,24,25,41].The enormous specific surface area, mesoporous structure, and nanoparticle shape of T-Nb 2 O 5 improve performance because they can offer a large number of electroactive sites for the uptake and release of Li + ions from the electrolyte and also shorten the diffusion distance for both the ions and electrons.
To further examine the electrochemical kinetics of the Li intercalation/deintercalation process within the T-Nb 2 O 5 electrode, an AC impedance measurement was performed at OCV in the frequency range of 0.01 Hz-1M Hz.As seen in Figure 7, the Nyquist plot (imaginary part, Z vs. real part, Z ) of the electrode consists of a high-frequency semicircle followed by a low-frequency spike.Using the RelaxIS program, the resultant impedance data was suitably matched to an equivalent circuit illustrated in the inset of Figure 7.In the equivalent circuit, R s (~2.45 Ω) indicates the electrolyte solution resistance, which can be calculated from the x-intercept of the beginning curve in the high-frequency region, and CPE (~35 µF) represents the constant phase element corresponding to the double-layer capacitance [48,56].A semicircle in the middle-frequency region shows the interfacial charge transfer resistance (R ct = 181.79Ω).In contrast, the Warburg resistance (Z w = 0.36 Ω s −1/2 ) quantifies the diffusion of Li ions and is represented by an inclined low-frequency line [57].A spike in the low-frequency describes the Li + intercalation or deintercalation behavior of the electrode.
Batteries 2023, 9, x FOR PEER REVIEW 10 of 13 release of Li + ions from the electrolyte and also shorten the diffusion distance for both the ions and electrons.
To further examine the electrochemical kinetics of the Li intercalation/deintercalation process within the T-Nb2O5 electrode, an AC impedance measurement was performed at OCV in the frequency range of 0.01 Hz-1M Hz.As seen in Figure 7, the Nyquist plot (imaginary part, Z″ vs. real part, Z′) of the electrode consists of a high-frequency semicircle followed by a low-frequency spike.Using the RelaxIS program, the resultant impedance data was suitably matched to an equivalent circuit illustrated in the inset of Figure 7.In the equivalent circuit, Rs (∼2.45 Ω) indicates the electrolyte solution resistance, which can be calculated from the x-intercept of the beginning curve in the high-frequency region, and CPE (∼35 µF) represents the constant phase element corresponding to the doublelayer capacitance [48,56].A semicircle in the middle-frequency region shows the interfacial charge transfer resistance (Rct = 181.79Ω).In contrast, the Warburg resistance (Zw = 0.36 Ω s −1/2 ) quantifies the diffusion of Li ions and is represented by an inclined low-frequency line [57].A spike in the low-frequency describes the Li + intercalation or deintercalation behavior of the electrode.

Conclusions
In conclusion, we detailed the synthesis of hierarchical mesoporous T-Nb2O5 nanoparticles by heating the peroxo niobic acid sol formed by peptizing the niobic acid precipitate with an aqueous H2O2 solution.The as-prepared electrode containing T-Nb2O5 nanoparticles had a high BET-specific surface area (65 m 2 g −1 ) and good Li intercalation characteristics.The T-Nb2O5 electrode had a high specific capacity of 68 mAh g −1 at 5 A g −1 , remarkable cycling stability over 300 cycles (with 70% capacity retention), and potential high-rate performance.Furthermore, kinetic analysis reveals that a pseudocapacitive mechanism dominates energy storage at a high rate.Because of their unique structure and shape, mesoporous T-Nb2O5 nanoparticles exhibit outstanding electrochemical properties.They have a short Li ion transport channel and a wide contact area between the active material and electrolyte.Consequently, T-Nb2O5 nanoparticles are a suitable material for Li-ion interaction electrodes.

Conclusions
In conclusion, we detailed the synthesis of hierarchical mesoporous T-Nb 2 O 5 nanoparticles by heating the peroxo niobic acid sol formed by peptizing the niobic acid precipitate with an aqueous H 2 O 2 solution.The as-prepared electrode containing T-Nb 2 O 5 nanoparticles had a high BET-specific surface area (65 m 2 g −1 ) and good Li intercalation characteristics.The T-Nb 2 O 5 electrode had a high specific capacity of 68 mAh g −1 at 5 A g −1 , remarkable cycling stability over 300 cycles (with 70% capacity retention), and potential high-rate performance.Furthermore, kinetic analysis reveals that a pseudocapacitive mechanism dominates energy storage at a high rate.Because of their unique structure and shape, mesoporous T-Nb 2 O 5 nanoparticles exhibit outstanding electrochemical properties.They have a short Li ion transport channel and a wide contact area between the active material and electrolyte.Consequently, T-Nb 2 O 5 nanoparticles are a suitable material for Li-ion interaction electrodes.

Figure 1 .
Figure 1.TGA and DTA of the as-synthesized peroxo niobic acid sol precursor.

Figure 1 .
Figure 1.TGA and DTA of the as-synthesized peroxo niobic acid sol precursor.
battery performance, including high specific capacity and high cycle stability.

Figure 4 .
Figure 4. (A) Nitrogen adsorption-desorption isotherm at 77 K and (B) BJH pore size distribution analysis of T−Nb2O5.High-resolution XPS spectra of (C) Nb 3d and (D) O 1s for the T−Nb2O5.

Figure 4 .
Figure 4. (A) Nitrogen adsorption-desorption isotherm at 77 K and (B) BJH pore size distribution analysis of T−Nb 2 O 5 .High-resolution XPS spectra of (C) Nb 3d and (D) O 1s for the T−Nb 2 O 5 .

Figure 5 .
Figure 5. Electrochemical characteristics of the T−Nb2O5: (A) CV profiles of the first three cycles; (B) CV profiles at different sweep rates ranging from 0.5 to 30 mV s −1 , and (C) corresponding logarithmic relationships between the scan rates and peak currents.

Figure 5 .
Figure 5. Electrochemical characteristics of the T−Nb 2 O 5 : (A) CV profiles of the first three cycles; (B) CV profiles at different sweep rates ranging from 0.5 to 30 mV s −1 , and (C) corresponding logarithmic relationships between the scan rates and peak currents.

Figure 6 .
Figure 6.(A) Typical charging-discharging profiles at 100 mA g −1 for the first ten cycles, (B) the charging and discharging curves at different current rates, (C) the rate performance, and (D) the cycle performance at 250 mA g −1 for the T-Nb2O5 electrode.

Figure 6 .
Figure 6.(A) Typical charging-discharging profiles at 100 mA g −1 for the first ten cycles, (B) the charging and discharging curves at different current rates, (C) the rate performance, and (D) the cycle performance at 250 mA g −1 for the T-Nb 2 O 5 electrode.The as-prepared T-Nb 2 O 5 GCD profiles of the electrode at different current densities ranging from 100 to 5000 mA g −1 are shown in Figure6B.It is evident that as the current density increases, the discharge curves drop and the charge curves rise, indicating an increase in polarization.It is evident that as current density increases the discharge curves drop and the charge curves rise, indicating that the polarization is increased.Surprisingly, the mesoporous T-Nb 2 O 5 nanoparticles electrode can operate smoothly even at a high applied current density of 5 A g −1 ; nevertheless, there is some noticeable capacity loss at high current densities.The gradual evolution of charging-discharging voltage profiles suggests that T-Nb 2 O 5 remains in a stable structure even after repeated discharging-charging cycling.Figure6Cdepicts the discharge capacity of the T-Nb 2 O 5 electrode as a function of current density.The graph clearly shows how the electrode's capacity rapidly degrades as the applied current density increases.At high current densities, this is usually caused by the sluggish diffusion of Li + into the T-Nb 2 O 5 interior [16,55,56].The discharge capacity could be restored to its initial condition after a series of rate tests when the current density was reversed back to 100 mA g −1 , demonstrating that the T-Nb 2 O 5 electrode possessed significant reversibility.For the development of Li-ion batteries to be used in practical applications, the electroactive materials must exhibit long-term cycle stability.To study the long-cycle retention properties in more detail, the T-Nb 2 O 5 electrode was exposed to a GCD test at 0.25 A g −1 in a potential window of 1.0 to 3.0 V (Li/Li + ) for up to 300 cycles (Figure6D).The electrode gradually lost capacity with increasing cycle number and maintained a discharge capacity of 142 mAh g −1 (70%) even at the end of 300 cycles.Meanwhile, the cell continued a high average CE of 98% over 300 cycles.It is worth noting that the performance of T-Nb 2 O 5 in terms of its specific capacity, cyclability, and rate capability is comparable and even superior to that reported for other T-Nb 2 O 5 nanostructures[22,24,25,41].The enormous specific surface area, mesoporous structure, and nanoparticle shape of T-Nb 2 O 5 improve performance because they can offer a large number of electroactive sites for the uptake and