Processing of Aqueous Graphite–Silicon Oxide Slurries and Its Impact on Rheology, Coating Behavior, Microstructure, and Cell Performance

: The mixing process is the basis of the electrode microstructure, which deﬁnes key cell performance indicators. This work investigated the effects of varying the energy input within the mixing procedure on slurry rheology, coating behavior, mechanical and electrical properties of dry electrodes and electrochemical performance of cells fabricated from these negative electrodes. Energy input differences were achieved by varying the solids content within the mixing procedure; however, the ﬁnal total solids content of the slurries was always the same. The slurries, produced with graphite and silicon oxide as active materials and carboxymethylcellulose (CMC) and styrene-butadiene rubber as binders, showed large differences in ﬂow behavior which were explained by changes in CMC adsorption and mechanical degradation because of increasing energy input. Low shear viscosity and the degree of shear thinning decreased with increasing energy input, resulting in a narrower stability window for slot-die coating. The resistance between the electrode and current collector decreased as more CMC was adsorbed on the active material. Electrode adhesion drastically dropped at the highest energy input, presumably due to a change in SBR distribution. Despite these variations, all fabricated pouch cells demonstrated excellent electrochemical performance and a slight trend of increased charge capability was observed in cells prepared with higher energy input.


Introduction
Lithium-ion batteries are one of the key technologies in the global effort to reduce carbon emissions.This leads to a growing demand for lithium-ion cells (LICs) with advanced high-performance active materials (AMs) and well-managed production processes [1].Within LIC production, the first and also product-defining step is the mixing of electrode suspensions, the so-called slurries [2][3][4][5][6].These suspensions are used to make electrodes by coating them onto a metal current collector foil.After drying, the electrodes are compressed and cut into the desired shape for downstream processing into cells [7,8].
The slurry typically consists of an electrochemical AM, a conductive additive, a binder and a solvent.Each of these components has a specific purpose.The AM is the major component of the solid fraction and defines the polarity of the subsequent electrode and its electrochemical characteristics.To name a few, typical AMs in positive electrodes are metal oxides such as lithium cobalt (III) oxide (LCO), lithium nickel manganese cobalt oxide (NCM) or polyanionic compounds such as lithium iron phosphate (LFP).Negative electrodes use AMs such as lithium titanium oxide (LTO), natural or synthetic graphite (Gr), silicon or silicon-based compounds such as silicon oxide (SiO x ).A comprehensive review of AMs in LICs is given in [9].Due to recent advances, AMs containing silicon are becoming more prominent in improving the energy density of the cell [10][11][12].However, compositions with silicon still struggle with cyclability, hysteresis, high changes in volume during lithiation and delithiation, just to name some, and are often used in combination with Gr to mitigate these issues [13][14][15].Conductive additives improve the electronic conductivity of electrodes, where particulate carbons such as CB are widely used.They have high BET surface areas with a primary particle size in the nanometer range.More performance-oriented electrode compositions use fiber-like or tubular carbon materials, e.g., multi-wall or single-wall carbon nanotubes, but these are expensive [16].The role of the binder within the electrode is very diverse: the dissolved binder defines the flow behavior of the slurry, stabilizes the suspension and, once dried, provides mechanical strength to the electrode, which ultimately affects the cycle life of the LIC [17,18].In addition, adsorbing binders such as CMC can act as dispersing agents and provide steric stabilization to the slurry [19,20].When CMC is used as a binder, a second polymer is needed to provide adhesion to the current collector and often styrene-butadiene rubber (SBR) is used for this purpose [21].In conventional slurries, N-methyl-2-pyrrolidone (NMP) or water is used as the solvent.For industrial applications, it is desirable to keep the amount of solvent as low as possible, as the evaporation process is energy consuming and therefore expensive; furthermore, the use of solvents like NMP should be reduced due to their hazardous nature [22].For this reason, the compositions studied here have a rather high total solids content (TSC).
Due to the physical and chemical diversity of materials, slurries come in many different consistencies.The key factors of a "good" slurry are a well-dispersed AM and conductive additive fraction, meaning the AM fraction has few to none agglomerates or aggregates remaining in the slurry and the conductive additives are dispersed to form a conductive network [23].Furthermore, flow behavior has to be adjusted to guarantee stable processing conditions, particularly in the widely used slot-die coating application [24].To achieve the desired quality criteria, a great deal of effort goes into the development of good mixing procedures, especially when scaling up from the laboratory to the plant scale.Some of the most prominent mixing process design considerations in the literature are steps such as dry blending of CB and AM, wet predispersion of conductive additives and mixing or kneading at high solids content [2][3][4][5][6][25][26][27].However, while these processes are often the subject of comparison, variations within the process have rarely been the subject of research.
To gain a better understanding regarding the effect of small variations, such as adding more or less solvent during the mixing procedure, aqueous slurries (Gr-SiO x ) with the same composition were made using an industrially relevant intensive mixer.Varying the solids content during mixing resulted in a significant change in energy input, and it will be shown that this had a major effect on the mechanical degradation of CMC, used here as a binder together with SBR, and its absorption on the surface of AM particles.This in turn changes the flow behavior of the slurry dramatically and we thoroughly investigated how this affects coatability on a prototypical slot-die roll-to-roll coater.The operating limits obtained for slurries with different flow behavior are compared with Ruschak's [28] visco-capillary model, which is widely used to predict the operating limits of coating processes [29].Furthermore, electrodes were made from the different slurries and were characterized in terms of microstructure, resistivity and peel strength, and finally, cells were made, and C-rate capability was analyzed to provide a full picture of the impact of mixing procedures on the application case.

Mixing Setup
An intensive mixer (EL 1, Maschinenfabrik Gustav Eirich GmbH, Hardheim, Germany) was used to disperse the electrode suspensions and prepare the polymer solutions.In principle, the mixer consists of a pan rotating at a circumferential speed of ω P and a dispersing tool running at a circumferential speed of ω w , as shown in Figure 1a; both the tool and the pan rotate clockwise.The dispersion tool has a star-like shape, with pins welded onto the tips-six pins on the top, two on the bottom.To create a mass flow, the pan conveys the material to a static scraper, which directs the mass towards the dispersing tool, creating an elliptical flow pattern, hence the mass does not fully cover the pan floor.The mixer was used in a horizontal position, at room temperature (22 • C).

Mixing Setup
An intensive mixer (EL 1, Maschinenfabrik Gustav Eirich GmbH, Hardheim, Germany) was used to disperse the electrode suspensions and prepare the polymer solutions.In principle, the mixer consists of a pan rotating at a circumferential speed of ω and a dispersing tool running at a circumferential speed of ω , as shown in Figure 1a; both the tool and the pan rotate clockwise.The dispersion tool has a star-like shape, with pins welded onto the tips-six pins on the top, two on the bottom.To create a mass flow, the pan conveys the material to a static scraper, which directs the mass towards the dispersing tool, creating an elliptical flow pattern, hence the mass does not fully cover the pan floor.The mixer was used in a horizontal position, at room temperature (22 °C).

Slurry Mixing
In a preliminary step, the binder solution was prepared by dissolving CMC (molecular weight MW = 875 kDa, degree of substitution DS = 0.9, Walocel CRT 30,000 P BA, DDP Specialty Products Germany GmbH & Co. KG, Walsrode, Germany) in deionized water overnight at a concentration of  = 2 wt%.This CMC solution was used to prepare the slurry.Artificial graphite (SCMG-CF-C, Showa Denko Materials (Europe) GmbH, Düsseldorf, Germany) with a volume weighted mean diameter D50 of 6.2 µm and a BET surface area of 3.5 m 2 g −1 (according to the manufacturer) was used as the main active material and silicon oxide (SiOx; grade H80; D50 = 5.5 µm, BET = 8.0 m 2 g −1 ; Daejoo Electronic Materials Co., Ltd., Siheung, Korea) was used as a secondary AM for slurry preparation.The mixing weight ratio of both AMs was 9:1 (Gr:SiOx) and the total dry active material content was set to 96.2 wt%.Carbon black (C-NERGY SUPER C45, Imerys Graphite & Carbon, Bodio, Switzerland) was used as conductive additive.CB, CMC and SBR (BM-451; Zeon Europe GmbH, Düsseldorf, Germany) were added in mass according to Table 1.The total solids content of the slurries was set to 60 wt.%.

Slurry Mixing
In a preliminary step, the binder solution was prepared by dissolving CMC (molecular weight M W = 875 kDa, degree of substitution DS = 0.9, Walocel CRT 30,000 P BA, DDP Specialty Products Germany GmbH & Co. KG, Walsrode, Germany) in deionized water overnight at a concentration of c CMC = 2 wt%.This CMC solution was used to prepare the slurry.Artificial graphite (SCMG-CF-C, Showa Denko Materials (Europe) GmbH, Düsseldorf, Germany) with a volume weighted mean diameter D 50 of 6.2 µm and a BET surface area of 3.5 m 2 g −1 (according to the manufacturer) was used as the main active material and silicon oxide (SiO x ; grade H80; D 50 = 5.5 µm, BET = 8.0 m 2 g −1 ; Daejoo Electronic Materials Co., Ltd., Siheung, Republic of Korea) was used as a secondary AM for slurry preparation.The mixing weight ratio of both AMs was 9:1 (Gr:SiO x ) and the total dry active material content was set to 96.2 wt%.Carbon black (C-NERGY SUPER C45, Imerys Graphite & Carbon, Bodio, Switzerland) was used as conductive additive.CB, CMC and SBR (BM-451; Zeon Europe GmbH, Düsseldorf, Germany) were added in mass according to Table 1.The total solids content of the slurries was set to 60 wt.%.The slurry mixing procedure follows the sequences shown in Figure 2. In the first step, the active and conductive materials were mixed dry for one minute at a circumferential tool speed ω w = 10 m s −1 , after which a 2.0 wt% CMC solution was added to the powder.To achieve the desired difference in solids content x i during high solids content mixing (HSCM) (step 2), a varying amount of water was added to the mixture, resulting in x i = 60, 63, 66 and 69 wt%, as seen in Figure 1b-the corresponding mixing procedures are labeled as P i .In step 3, SBR was added and finally, in step 4, the slurry was finalized by dilution to the desired composition, as shown in Table 1.
The slurry mixing procedure follows the sequences shown in Figure 2. In the first step, the active and conductive materials were mixed dry for one minute at a circumferential tool speed ωw = 10 m s −1 , after which a 2.0 wt% CMC solution was added to the powder.To achieve the desired difference in solids content  during high solids content mixing (HSCM) (step 2), a varying amount of water was added to the mixture, resulting in  = 60, 63, 66 and 69 wt%, as seen in Figure 1b-the corresponding mixing procedures are labeled as  .In step 3, SBR was added and finally, in step 4, the slurry was finalized by dilution to the desired composition, as shown in Table 1.Due to the variation in water addition in step 2, the mixer's degree of filling varied throughout the procedure; therefore, the occupied sample volume  varied, which has to be considered when calculating the specific energy input.
A short and slow mixing sequence with ωw = 1.3 m s −1 was introduced into the procedure to avoid splashing or the formation of dust clouds after the addition of new materials in steps 2, 3 and 4. Following this slow sequence, the actual sequence with the desired fast tool speed started.
In order to shed light on the adsorption and shear-induced degradation of CMC during slurry preparation, a series of aqueous solutions of the CMC used in the slurries, as well as of a low-molecular-weight CMC grade (MW = 500 kDa, DS = 0.9, TEXTURECEL™ 2000 PA, DDP Specialty Products Germany GmbH & Co. KG, Walsrode, Germany), was prepared and their flow curves were determined using rotational rheometry.
In the second step of the mixing procedure, the stirrer speed was 20 m s -1 , corresponding to a high energy input, as will be discussed below.For reference, the slurry  was prepared at a significantly lower speed of ωw = 3 m s −1 in this mixing step and the solids content in this step was set to  = 60 wt%; the detailed procedure can be seen in Supplementary Figure S1.Due to the variation in water addition in step 2, the mixer's degree of filling varied throughout the procedure; therefore, the occupied sample volume V Step varied, which has to be considered when calculating the specific energy input.
A short and slow mixing sequence with ω w = 1.3 m s −1 was introduced into the procedure to avoid splashing or the formation of dust clouds after the addition of new materials in steps 2, 3 and 4. Following this slow sequence, the actual sequence with the desired fast tool speed started.
In order to shed light on the adsorption and shear-induced degradation of CMC during slurry preparation, a series of aqueous solutions of the CMC used in the slurries, as well as of a low-molecular-weight CMC grade (M W = 500 kDa, DS = 0.9, TEXTURECEL™ 2000 PA, DDP Specialty Products Germany GmbH & Co. KG, Walsrode, Germany), was prepared and their flow curves were determined using rotational rheometry.
In the second step of the mixing procedure, the stirrer speed was 20 m s −1 , corresponding to a high energy input, as will be discussed below.For reference, the slurry S Low was prepared at a significantly lower speed of ω w = 3 m s −1 in this mixing step and the solids content in this step was set to x i = 60 wt%; the detailed procedure can be seen in Supplementary Figure S1.

Treatment of Slurry
For further investigation of the binders, the slurry was treated in a centrifuge (Z366, Hermle Labortechnik GmbH, Wehingen, Germany) for 12 h at a relative centrifugal force of RCF = 6300 to separate the solid fraction from the liquid fraction.

Energy Input
The power consumption P el of the rotor of the dispersing tools was tracked by the machine and integrated over time t, resulting in the energy consumption E of the rotor.
Specific energy input E sp was calculated by subtracting idle energy consumption E idle from rotor energy consumption E. This effective energy input E e f f was then divided by the sample volume occupied during the mixing step V Step to give E sp .

Rheology and Coating
Rheological measurements were carried out using a rotational rheometer (MCR 302e, Anton Paar Germany GmbH, Ostfildern, Germany).A plate-plate setup with a diameter of 50 mm and a gap height of 0.3 mm was used as the measurement geometry.The temperature was set to 25 • C.
Shear-rate-controlled measurements were performed using a logarithmic shear rate ramp ranging from .γ = 0.05 to 1000 s −1 with a measurement duration ranging from 80 s at the lowest shear rate to 2 s at the highest shear rate.For stress-controlled measurements, shear stress τ was increased logarithmically, from 0.01 to 1000 Pa with a measurement time of 18 s for each stress value.
When analyzing the coating experiments, the shear rate within the coating layer was calculated as the ratio of the line speed U L and the slot-die gap, i.e., the distance between the slot-die lips and the substrate G, see Figure 3.

Coating Experiment
The coating trials were carried out using a roll-to-roll coater manufactured by Mathis AG (Niederhasli, Switzerland).The slot-die was installed with a 300 µm thick shim sheet  and with a slot width of 50 mm.The slurry was fed by a progressing cavity pump.Before the trials, the coater pump was calibrated at the highest stable  * for each speed of the test run to ensure a constant capacity loading of 3.3 mAh cm −2 at each speed.This was performed by coating, drying and weighing cut coins at line speeds from 2 to 10 m min −1 , varying in steps of 2 m min −1 .The experiments were carried out in a dry room (dew point < −45 °C) at 22 °C.
Two coating defects, air entrainment and widening of the coating, were monitored visually as stability criteria.Here, the upper stability limit (USL) describes the highest val- The dynamic viscosity η corresponding to this shear rate was obtained by interpolating the experimental viscosity vs. shear rate data.
In order to establish the relationship between surface tension σ, dynamic viscosity η and line speed U L , the dimensionless capillary number Ca was calculated as follows [29,30].
The surface tension of the slurry was set equal to that of pure water at 22 • C, σ = 72.3mN m −1 [31], which was considered a fair approximation for this hardly accessible quantity since no surface-active ingredients were added to prepare the slurry.
The viscosity data used to calculate Ca were determined at 25 • C; since slot-die coating was performed at 22 • C, this results in a small systematic error.Since the temperature dependence of slurry viscosity is essentially determined by that of water, as the main ingredient of the slurries disperse phase [32], we can estimate this error to be smaller than 7%.
The dynamic gap G * was calculated as the ratio of the slot-die gap G and the height of the wet film W, see Figure 3.While G is given by the dimensions and setup of the coater itself, W was calculated from electrode loading, slurry TSC and slurry density, resulting in W = 87.6 µm.

Coating Experiment
The coating trials were carried out using a roll-to-roll coater manufactured by Mathis AG (Niederhasli, Switzerland).The slot-die was installed with a 300 µm thick shim sheet S and with a slot width of 50 mm.The slurry was fed by a progressing cavity pump.Before the trials, the coater pump was calibrated at the highest stable G * for each speed of the test run to ensure a constant capacity loading of 3.3 mAh cm −2 at each speed.This was performed by coating, drying and weighing cut coins at line speeds from 2 to 10 m min −1 , varying in steps of 2 m min −1 .The experiments were carried out in a dry room (dew point Two coating defects, air entrainment and widening of the coating, were monitored visually as stability criteria.Here, the upper stability limit (USL) describes the highest values of G * where no air entrainment was observed and the lower stability limit (LSL)the lowest value of G * where no increase in coating width was measured.Air entrainment as a coating defect after exceeding the USL is shown in Figure 4a.Conversely, the widening of the coating after exceeding the LSL was measured by the coater's camera measurement system.Within the stability limits, the coating was uniform and showed no defects, as shown in Figure 4b.

Coating Experiment
The coating trials were carried out using a roll-to-roll coater manufactured by Mathis AG (Niederhasli, Switzerland).The slot-die was installed with a 300 µm thick shim sheet  and with a slot width of 50 mm.The slurry was fed by a progressing cavity pump.Before the trials, the coater pump was calibrated at the highest stable  * for each speed of the test run to ensure a constant capacity loading of 3.3 mAh cm −2 at each speed.This was performed by coating, drying and weighing cut coins at line speeds from 2 to 10 m min −1 , varying in steps of 2 m min −1 .The experiments were carried out in a dry room (dew point < −45 °C) at 22 °C.
Two coating defects, air entrainment and widening of the coating, were monitored visually as stability criteria.Here, the upper stability limit (USL) describes the highest values of  * where no air entrainment was observed and the lower stability limit (LSL)-the lowest value of  * where no increase in coating width was measured.Air entrainment as a coating defect after exceeding the USL is shown in Figure 4a.Conversely, the widening of the coating after exceeding the LSL was measured by the coater's camera measurement system.Within the stability limits, the coating was uniform and showed no defects, as shown in Figure 4b.For the model-based estimation of the upper stability limit, the visco-capillary model (VCM) by Ruschak was utilized and the critical capillary number was calculated with a numerical prefactor of 0.65 [28,29].For the model-based estimation of the upper stability limit, the visco-capillary model (VCM) by Ruschak was utilized and the critical capillary number was calculated with a numerical prefactor of 0.65 [28,29].

Manufacturing of Electrodes
Slurries were degassed at 100 mbar for two minutes.Electrodes were cast using a porous vacuum table (510XL, Erichsen GmbH & Co. KG, Hemer, Germany) and a fixed film applicator frame (BYK-Gardner GmbH, Geretsried, Germany) in the range of 120 to 140 µm via doctor blade coating.Depending on slurry viscosity, the gap height was selected to produce electrodes with a loading of 3.3 mAh cm 2 at 7.9 mg cm −2 .Positive electrodes with a loading of 3.0 mAh cm −2 , a mass loading of 16 mg cm −2 and a compressed electrode thickness of roughly 49 µm were used to construct full pouch cells, containing 94.5 wt% NCM 811 as AM.
Dried table-coated negative electrodes were compressed using a laboratory calender (Ingecal SAS, Chassieu, France) operating at 0.8 kN mm −1 using 70 mm wide electrode strips without heating.The electrodes were compressed to an average density of 1.2 g cm −3 , resulting in an electrode thickness of roughly 66 µm.Negative electrodes originating from x i are labeled as A i .

Morphology
Cross-sectional images of the electrodes were taken using a scanning electron microscope (SEM; MIRA3, Tescan Orsay Holding a.s., Brno, Czech Republic).Electrode coins were stamped with a diameter of 15 mm and cut in half.The straight-cut edge was then treated using an ion milling system (IM4000Plus, Hitachi High-Tech Europe GmbH, Krefeld, Germany) and this treated cross-section was then examined.

Resistivity Measurement
The resistivity of the electrodes was measured using an electrode resistance measuring system (RM2610, Hioki E.E.Corporation, Nagano, Japan).The system presses a 46-pin probe head against the surface of the electrode and measures two resistances: volume resistivity ρ V in units of Ω cm, representing the resistivity of the electrode layer, and interface resistance ρ I in units of Ω cm 2 , representing the resistivity of the interface between the coating and the substrate [33,34].
Assuming that electron flow in the electrode is perpendicular to the current collector surface, the specific contact resistance ρ CN is given by the product of volume resistivity ρ V and electrode thickness h [35].

Peet Test
Peel strength was measured using a zwickiLine Zo.5 (ZwickRoell GmbH & Co. KG, Ulm, Germany) and a 90 • peel test setup.The electrodes were cut into 30 mm wide strips with a total substrate length of 200 mm and a coating length of 120 mm.After calendering, the electrode samples were attached to the setup with double-sided adhesive tape (tesa 05696, Tesa SE, Norderstedt, Germany) and the machine measured the force required to peel the substrate from the coating at a speed of 5 mm/s.Peel strength F Peel was calculated by dividing the measured force F total by the width of the sample W Sample .

Cell Manufacturing
Pouch cells with positive electrode dimensions of 25 mm × 40 mm were built using two single-sided negative electrodes and one double-sided positive electrode.The cells were filled with 0.4 mL of LiPF 6 electrolyte (carbonate solvent mixture and additive, Soulbrain, Northville Township, MI, USA).A ceramic separator (Enpass D22AEGK, SK innovation Co., Ltd., Seoul, Republic of Korea) with a thickness of 21 µm was used in this process.Cell building was performed in a dry room (dew point < −45 • C) and electrolyte filling was performed in an argon-filled glovebox atmosphere with less than 0.1 ppm O 2 and 0.1 ppm H 2 O.The pouches were evacuated and sealed in this glovebox.The cells balanced at a positive to negative ratio of 1.1 and a slightly larger negative electrode dimensions (27 mm × 42 mm) than the positive electrode surface area.

Electrochemical Measurements
Cell formation and later a C-rate test were carried out using a CTS (Basytec GmbH, Asselfingen, Germany) at 25 • C with a cut-off potential of 2.8 and 4.2 V.A set of four cells per electrode variation was investigated.The cells were pressurized by using plastic plates and clamps.
During formation, the cells were charged by applying a CCCV regime to them with C-rates ranging from 0.1 to 0.33 C. The discharge step occurred with the same C-rates as the charging step, following a CC regime.The C-rate tests can be divided into two segments, discharge C-rate and charge C-rate.Both segments started with 2 cycles at 0.33 C, followed by 10 steps consisting of 3 constant current cycles with increasing C-rate ranging from 0.5 C to 5 C. At the end of the test, two check-up cycles at 0.3 C were performed.

Energy Input
Variation in the mixing procedures here essentially refers to varying the solids content x i during the HSCM step.This variation resulted in different energy inputs within the process variations P i .Figure 5 shows the total power consumption of the mixer for steps 2 to 4 of the procedure; these are the steps where the solvent was included.Table 2 shows the specific energy inputs as calculated using Equation ( 1).It can be seen that an increase in   leads to a higher energy input.Comparing the two most extreme variations,  60 and  69 ,  69 differs from  60 by a factor of about 3; therefore, a  During the processing of P 60 , power consumption follows a typical profile for mixing suspensions [36], best seen in the fast HSCM step.On starting, the bulk mass transforms into a plastic mass, resulting in the peak of rotor power.As the wetting and dispersion of the particles continue, the plastic mass changes to a viscous suspension, while power consumption decreases and asymptotically approaches a constant level.It can be seen that as x i increases, total power consumption changes drastically.While P 63 and P 66 are comparable to the power consumption pattern of P 60 , procedure P 69 undergoes a drastic change in power consumption, and thus in energy input.Here, the HSCM step does not produce a fluid suspension, but rather a plastic mass.This mass moves through the mixer and sporadically touches the rotor, resulting in a constant formation of power peaks rather than a steady mass flow that eventually approaches a steady power level.For this reason, the duration of the HSCM step in procedure P 69 was slightly increased by 2 min to account for the initial period of no mixing.
Table 2 shows the specific energy inputs as calculated using Equation ( 1).It can be seen that an increase in x i leads to a higher energy input.Comparing the two most extreme variations, P 60 and P 69 , P 69 differs from P 60 by a factor of about 3; therefore, a stronger deagglomeration might be expected with increasing x i .It is noticeable that the largest contribution to energy input comes from the HSCM step, but in P 69 , the SBR addition step also contributes significantly.Comparing P 60 and P 69 , the specific energy input of this step differs by a factor of about 11.The "Finalization fast" step shows similar energy inputs for all slurries (see Figure 5), with an average value of 2.5 Wh dm 3 , which could lead to the false assumption that all slurries have similar flow behavior.As for the low-energy reference, P Low showed an energy input of roughly one-third of P 60 ; detailed consumption can be seen in Figure S1.

Flow Behavior
For a more detailed picture of flow behavior, the flow curves of all four slurries S 60 to S 69 as well as S Low and the CMC (M w = 875 kDa) solution with a concentration of 13.5 g L −1 , corresponding to the nominal CMC concentration in the aqueous phase of the slurry, are shown in Figure 6.All slurries have the same composition and TSC, but their flow behavior is very different.Overall, with increasing solids content x i during HSCM, the low shear viscosity of the slurries decreases up to two orders of magnitude, despite their identical composition.According to Stokes' law, it is to be expected that slurries with lower low shear viscosity will sediment faster and will therefore be less stable.In small batches, this may not be a problem, but on an industrial scale, this could lead to stability problems when using the slurry for a long period of time without stirring.
The low energy input sample S Low shows the highest viscosity values and demonstrates uniform, power-law-type shear thinning behavior.Slurries S 60 and S 63 also show monotonic shear thinning behavior, but their absolute viscosity values are lower and the degree of shear thinning is less pronounced than those of S Low .Absolute viscosity values further decrease with increasing x i or energy input during the HSCM mixing step.Furthermore, slurries S 66 and S 69 do not show strict shear thinning behavior.Slurry S 66 exhibits weak shear thinning behavior only at low shear rates, approaches a plateau between roughly 10 and 200 s −1 and finally the viscosity decreases again at higher shear rates.Slurry S 69 shows shear thickening behavior between 10 and 200 s −1 , followed by a shear thinning regime at higher .γ.
are shown in Figure 6.All slurries have the same composition and TSC, but their flow behavior is very different.Overall, with increasing solids content  during HSCM, the low shear viscosity of the slurries decreases up to two orders of magnitude, despite their identical composition.According to Stokes' law, it is to be expected that slurries with lower low shear viscosity will sediment faster and will therefore be less stable.In small batches, this may not be a problem, but on an industrial scale, this could lead to stability problems when using the slurry for a long period of time without stirring.

The low energy input sample 𝑆
shows the highest viscosity values and demonstrates uniform, power-law-type shear thinning behavior.Slurries  and  also show monotonic shear thinning behavior, but their absolute viscosity values are lower and the degree of shear thinning is less pronounced than those of  .Absolute viscosity values further decrease with increasing  or energy input during the HSCM mixing step.Furthermore, slurries  and  do not show strict shear thinning behavior.Slurry  exhibits weak shear thinning behavior only at low shear rates, approaches a plateau between roughly 10 and 200 s −1 and finally the viscosity decreases again at higher shear rates.Slurry  shows shear thickening behavior between 10 and 200 s −1 , followed by a shear thinning regime at higher  .These drastic differences in flow behavior for slurries of identical composition are direct evidence of different particle interactions and hence different microstructures due to different slurry treatment, i.e., different energy input during mixing.One reason for such changes in flow behavior could be a difference in particle deagglomeration and the existence of particle clusters trapping a substantial fraction of the solvent and thus leading  These drastic differences in flow behavior for slurries of identical composition are direct evidence of different particle interactions and hence different microstructures due to different slurry treatment, i.e., different energy input during mixing.One reason for such changes in flow behavior could be a difference in particle deagglomeration and the existence of particle clusters trapping a substantial fraction of the solvent and thus leading to a higher effective particle volume fraction at low energy input.However, all slurries appeared well dispersed, and SEM images of corresponding dry samples did not show evidence of remaining particle clusters.A potential mechanical destruction of the solids fraction and a corresponding change in particle size distribution is not expected to have affected slurry viscosity since the overall particle loading of about 40 vol% is too low [32] and SEM images of corresponding dry samples do not provide experimental evidence for that.Finally, the flow behavior of suspensions strongly depends on the colloidal interactions among the suspended particles, as well as on solvent rheology [32].For the slurries investigated here, these phenomena are closely related to the adsorption of CMC on the solid particle surfaces [37] and the mechanical degradation of CMC [38,39] during slurry preparation.The relevance of CMC adsorption and presumably also degradation already shows up when comparing the low shear viscosity of slurries S 66 and S 69 to that of the CMC solution representing the disperse phase of these slurries.The low absolute viscosity values of slurries S 66 and S 69 can only be rationalized taking into account these adsorption and degradation phenomena, as will be discussed in more detail below.
The pronounced shear thickening of sample S 69 is attributed to the formation of hydrodynamic clusters.Such clusters can only form when none or only weak, short-range repulsive interactions among particles are present [32]; this also results in low viscosity at low shear rates, as observed for S 69 .In this case, the steric repulsion inferred from an adsorbed CMC layer seems to just compensate for the always present van der Waals attraction.The latter, on the other hand, seems to dominate in the shear thinning samples S 60 , S 63 and particularly S Low .Obviously, energy input during the HSCM mixing step has a significant impact on CMC adorption.Additionally, the mechanical degradation of CMC has to be considered, since it affects both the viscosity of the solvent and the strength and range of the steric repulsion provided by the CMC adsorbed on the active particle surface.The reference sample S Low prepared in a different manner and at a low energy input exhibits the highest viscosity level and the strongest degree of shear thinning, clearly indicating that attractive particle interactions dominate in this slurry.
Figure 7 shows the flow curves for the supernatants (SU i ) obtained from the centrifugation of the slurries S i .It should be noted that the supernatant of slurry S Low was diluted with deionized water at a ratio 1:26 (supernatant/water) due to its high viscosity not allowing for the determination of zero shear viscosity; therefore, the dilution is labeled as S Low−Di .The viscosity functions of these supernatants are essentially determined by the concentrations and molecular weights of the dissolved CMC; the contribution of suspended SBR particles or residual active material is negligible.The absolute viscosity values differ by about an order of magnitude, indicating that the degree of CMC removed from the disperse phase via adsorption on the active particles is strongly affected by the slurry preparation procedure.The sample with the highest energy input during the HSCM mixing step has the lowest disperse-phase viscosity, indicating that a larger fraction of CMC is adsorbed on the particles in this case, consistent with the flow behavior of the slurry itself.Moreover, supernatants SU 60 , SU 63 and the diluted supernatant SU Low−Di exhibit shear thinning behavior, whereas samples SU 66 and SU 69 show Newtonian flow behavior.This provides further insight into the mechanically induced adsorption and degradation of CMC in these slurries.Highly diluted CMC solutions show Newtonian flow behavior and solutions with different molecular weights and concentrations may exhibit the same absolute viscosity value.More highly concentrated solutions, however, are shear thinning and the absolute value of zero shear viscosity and the shape of the flow curve are a unique signature of a solution with a certain molecular weight and CMC concentration [40].Figure 7 includes the flow curves of CMC solutions with M w = 875 kDa and M w = 500 kDa, matching the zero shear viscosity of supernatants SU 60 and SU Low−Di , respectively.Obviously, a higher concentration is required for the solution of CMC with lower molecular weight to achieve the same zero shear viscosity as for the solution of CMC with higher molecular weight.Moreover, shear thinning is significantly more pronounced for the solution of CMC with higher molecular weight.The CMC solution with M w = 875 kDa and c CMC = 0.3 g L −1 almost matches the flow curve of the diluted supernatant SU Low−Di .Its slightly more pronounced shear thinning indicates that some mechanical degradation also occured in this case, but for the sake of simplicity, we neglected that.Under this assumption, the difference between this concentration and the input concentration of 13.5 g L −1 (see Table 1 and Figure 6) directly denotes the amount of CMC adsorbed on the particles.As exemplarily demonstrated using the solution with M w = 500 kDa and c CMC = 2.3 g L −1 , solutions of CMC with other molecular weights yield different shear thinning behaviors even if their zero shear viscosities matches.For supernatant SU 60 , the situation is different; in this case, the CMC solution with M w = 875 kDa matching its zero shear viscosity exhibits much more pronounced shear thinning than the supernatant.This is direct evidence that the CMC molecules experienced degradation during the mixing process.In contrast, the CMC solution with M w = 500 kDa and c CMC = 5.8 g L −1 resembles the absolute values and shape of the flow curve in the whole investigated shear rate range well.We conclude that the CMC experienced mechanical degradation roughly to this average molecular weight and, again, we can calculate the amount of the adsorbed CMC as the difference between the concentration of this solution and the CMC input concentration.
supernatant.This is direct evidence that the CMC molecules experienced degradation during the mixing process.In contrast, the CMC solution with Mw = 500 kDa and  = 5.8 g L −1 resembles the absolute values and shape of the flow curve in the whole investigated shear rate range well.We conclude that the CMC experienced mechanical degradation roughly to this average molecular weight and, again, we can calculate the amount of the adsorbed CMC as the difference between the concentration of this solution and the CMC input concentration.Finally, we conclude that for  , almost 57 wt% of added CMC adsorbed on the surface of the active particles and for  , about 42 wt% was adsorbed, taking into account supernatant dilution (see Supplementary).The supernatants  and  show rather Newtonian flow behavior and it is not possible to assign the measured viscosity unambiguously to a certain Mw and concentration of the dissolved CMC.Assuming that with increasing energy input, no further degradation of molecular weight takes place, we  Finally, we conclude that for S 60 , almost 57 wt% of added CMC adsorbed on the surface of the active particles and for S Low , about 42 wt% was adsorbed, taking into account supernatant dilution (see Supplementary).The supernatants SU 66 and SU 69 show rather Newtonian flow behavior and it is not possible to assign the measured viscosity unambiguously to a certain M w and concentration of the dissolved CMC.Assuming that with increasing energy input, no further degradation of molecular weight takes place, we can determine the CMC concentration in the supernatant from the η 0 vs. c CMC data for a series of CMC solutions with M w = 500 kDa shown in the Supplementary Information (Figure S2).Under this constraint, it turns out that the fraction of adsorbed CMC increases with increasing energy input and for slurry S 69 , almost all CMC is adsorbed on the particles.This is consistent with the observed changes in the flow curves of the corresponding slurries, which can be rationalized assuming a stronger steric repulsion for S 69 finally balancing the attractive van der Waals force.On the other hand, if we assume a pronounced further degradation of CMC chains with increasing energy input, then the measured supernatant viscosity curves would imply that a smaller fraction of shorter CMC chains was adsorbed onto the active material particles, which contradicts the observed decrease in slurry viscosity.This supports the assumption that no further mechanical CMC degradation took place in the slurries prepared at higher energy input than S 60 .
A similar effect of mechanical energy input on CMC adsorption was recently published by Park et al. [41] However, the group did not consider mechanical degradation as they already used a low molecular weight CMC.
Weber at al. [42] investigated the impact of dry mixing CB and Gr as a preliminary step before mixing it with the solvent in an extruder.Varying the tip speed during dry mixing resulted in different flow behavior in the final slurries, ranging from a rather monotonous shear thinning behavior to a discrete plateau.Perhaps the pretreatment of the powder resulted in different surface availability or different energy input during extrusion, resulting in a varying degree of polymer adsorption and degradation, finally changing particle-particle interactions and thus flow behavior as discussed above.

Coating
To investigate the influence of the slurries' flow behavior on coating, experiments were carried out with slurries S 60 and S 69 , as they showed the greatest differences in flow behavior.The two slurries were coated at different line speeds; the maximum and minimum G were determined for the upper and lower stability limits.The results are shown in Figure 8a, which shows the dynamic gap G * of both stability limits as a function of line speed U L .For slurry S 60 , the USL slightly decreases with increasing line speed, ranging from a dynamic gap of 1.9 to 1.7.The difference ∆G * between USL and LSL increases with increasing U L , from 2 to 10 m min −1 , roughly to ∆G * = 0.3.Slurry S 69 shows a more radical change in its stability limits.Its initially high USL of roughly G * = 2.5 at 2 m min −1 decreases to G * = 1.4 at 10 m min −1 .The corresponding LSL decreases in a similar way; however, at 10 m min 1 , the lower limit closes up to the upper limit with G * = 1.3.Whereas S 60 demonstrates a broad corridor of stable operation limits in this coater setup, S 69 displays a rather narrow window of stable operating parameters.Such a narrow window makes the coating of S 69 difficult, especially at higher speeds.
they already used a low molecular weight CMC.
Weber at al. [42] investigated the impact of dry mixing CB and Gr as a preliminary step before mixing it with the solvent in an extruder.Varying the tip speed during dry mixing resulted in different flow behavior in the final slurries, ranging from a rather monotonous shear thinning behavior to a discrete plateau.Perhaps the pretreatment of the powder resulted in different surface availability or different energy input during extrusion, resulting in a varying degree of polymer adsorption and degradation, finally changing particle-particle interactions and thus flow behavior as discussed above.

Coating
To investigate the influence of the slurries' flow behavior on coating, experiments were carried out with slurries  and  , as they showed the greatest differences in flow behavior.The two slurries were coated at different line speeds; the maximum and minimum  were determined for the upper and lower stability limits.The results are shown in Figure 8a, which shows the dynamic gap  * of both stability limits as a function of line speed  .For slurry  , the USL slightly decreases with increasing line speed, ranging from a dynamic gap of 1.9 to 1.7.The difference ∆ * between USL and LSL increases with increasing  , from 2 to 10 m min −1 , roughly to ∆ * = 0.3.Slurry  shows a more radical change in its stability limits.Its initially high USL of roughly  * = 2.5 at 2 m min −1 decreases to  * = 1.4 at 10 m min −1 .The corresponding LSL decreases in a similar way; however, at 10 m min 1 , the lower limit closes up to the upper limit with  * = 1.3.Whereas  demonstrates a broad corridor of stable operation limits in this coater setup,  displays a rather narrow window of stable operating parameters.Such a narrow window makes the coating of  difficult, especially at higher speeds.In order to compare these results with the visco-capillary model of Ruschak [28], a stability map was plotted in the Ca -G * plane (Equations ( 4) and ( 5)), as shown in Figure 8b.It should be noted that the VCM of Ruschak [28] was developed on Newtonian fluids.Focusing on the upper limit, at 2 m min −1 , slurry S 60 could be coated with G * = 1.9 at Ca = 1.6 and at 10 m min −1 , a stable coating was achieved with G * = 1.7 at Ca = 4.1.This USL border is close to that predicted by Ruschak; however, the decay of Ca with increasing G* is more pronounced.In contrast, slurry S 69 maintained a USL at 2 m min −1 with G * = 2.5 at Ca = 0.8 and at 10 m min −1 with G * = 1.4 at Ca = 2.4.Here, only for very high G * = 2.5 is the VCM prediction approached.This comparison indicates that the coating behavior of monotonically shear thinning slurries such as S 60 can be predicted with respect to line speed and gap height settings, whereas more complex slurries such as the shear thickening S 69 are not represented by the model.Whenever the upper stability border was crossed, air entrainment was observed, which is related to the failure of the upstream meniscus.In the case of S 69 , this might be due to its overall lower viscosity.The resulting capillary number is significantly lower than that of S 60 , indicating that the viscous forces are less pronounced.Ultimately, this leads to a closing-up of the upstream meniscus towards the coating bead and the entrainment of air occurring at a lower G * than it would with S 60 .Due to the narrow stability window of S 69 , coating at higher speeds might be very challenging; here, the installation of a vacuum box upstream could be helpful.

Electrode Microstructure
Table-coated electrodes originating from the four slurries were characterized with a loading of 3.3 mAh cm −2 and an average compressed density of 1.2 g cm −3 .Electrodes A 60 to A 69 were analyzed using a scanning electron microscope equipped with a backscattered electron detector (BSE).A 60 and A 69 are shown in Figure 9. Due to the differences in E sp , an impact on particle deagglomeration, especially of carbon black, might be expected.Nevertheless, the overall active material distribution is equally homogeneous.However, A 60 electrodes show more and larger CB aggregates than A 69 , as shown in Figure 9c,d  Following up on the effect of dispersed CB, total electrode resistivity, divided into  and  (Equation ( 7)), is shown in Figure 10a.Resistivity decreases with increasing energy input from a total of about 4 ± 0.4 to 2.5 ± 0.2 mΩ cm 2 .This trend can be observed in both parts of the electrode: the resistivity of the coating and the resistance of the interface.However, the most noticeable difference in this series is interfacial resistance:  ; = 3.0 ± 0.1 and  ; = 1.7 ± 0.2 mΩ cm 2 .A possible reason for this decrease in interfacial resistivity could be that with increasing energy input, a greater fraction of CMC is adsorbed on the active material particles, as discussed in the rheology section above.Therefore, less CMC is available at the coating/substrate interface, thus lowering interfacial resistivity.On the Following up on the effect of dispersed CB, total electrode resistivity, divided into ρ I and ρ CN (Equation ( 7)), is shown in Figure 10a.Resistivity decreases with increasing energy input from a total of about 4 ± 0.4 to 2.5 ± 0.2 mΩ cm 2 .This trend can be observed in both parts of the electrode: the resistivity of the coating and the resistance of the interface.However, the most noticeable difference in this series is interfacial resistance: ρ I;A 60 = 3.0 ± 0.1 and ρ I;A 69 = 1.7 ± 0.2 mΩ cm 2 .A possible reason for this decrease in interfacial resistivity could be that with increasing energy input, a greater fraction of CMC is adsorbed on the active material particles, as discussed in the rheology section above.Therefore, less CMC is available at the coating/substrate interface, thus lowering interfacial resistivity.On the other hand, the resistivity of the coating layer itself does not vary much: ρ CN;A 60 = 1 ± 0.27 and ρ CN;A 69 = 0.8 ± 0.03 mΩ cm 2 .Although the size of the CB agglomerates decreases with increasing x i , this seems to have little effect on the resistivity of the coating layer in these graphite-based electrodes.
ergy input from a total of about 4 ± 0.4 to 2.5 ± 0.2 mΩ cm 2 .This trend can be observed in both parts of the electrode: the resistivity of the coating and the resistance of the interface.However, the most noticeable difference in this series is interfacial resistance:  ; = 3.0 ± 0.1 and  ; = 1.7 ± 0.2 mΩ cm 2 .A possible reason for this decrease in interfacial resistivity could be that with increasing energy input, a greater fraction of CMC is adsorbed on the active material particles, as discussed in the rheology section above.Therefore, less CMC is available at the coating/substrate interface, thus lowering interfacial resistivity.On the other hand, the resistivity of the coating layer itself does not vary much:  ; = 1 ± 0.27 and  ; = 0.8 ± 0.03 mΩ cm 2 .Although the size of the CB agglomerates decreases with increasing  , this seems to have little effect on the resistivity of the coating layer in these graphite-based electrodes.Adhesion between the electrode and the current collector was characterized by a 90 • peel test; corresponding data for A 60 to A 69 are shown in Figure 10b.While electrodes A 60 to A 66 show a similar peel strength of about 4.4 N m 1 , sample A 69 shows a drop in adhesion to a peel strength value of about 1.3 N m 1 .Such a low adhesion as that of A 69 might be challenging for automated processes within cell assembly due to delamination of the coating.Adhesion is mainly provided by the added SBR [43] and the high energy input in step 2 (HSCM) of the procedure apparently has a significant effect on SBR distribution, with a significantly lower SBR fraction at the current collector interface for A 69 which may be due to a shear-induced agglomeration of SBR particles.

Cell
Table-coated electrodes A 60 to A 69 were used to build small-format pouch cells.Figure 11 shows the discharge capacity of the formation on the left and the discharge capacity of the C-rate test on the right.Four cells per A i were measured.Within the formation, all cells run at very similar capacities, but cells originating from higher x i start to show less capacity, fading towards the seventh cycle.When discharging (cycles 1 to 32) at different C-rates, A 69 runs at the highest capacity, excluding 4.5 and 5.0 C, which is dominated by ionic limitations of the positive electrode.Charging at different C-rates (cycle 33 to 64) also shows that A 69 appears to outperform the other cells, indicating differences in microstructure.In the check-up, represented by the last two cycles of the C-rate test (cycle 65 and 66), A 69 again shows the highest capacity.capacity, fading towards the seventh cycle.When discharging (cycles 1 to 32) at different C-rates,  runs at the highest capacity, excluding 4.5 and 5.0 C, which is dominated by ionic limitations of the positive electrode.Charging at different C-rates (cycle 33 to 64) also shows that  appears to outperform the other cells, indicating differences in microstructure.In the check-up, represented by the last two cycles of the C-rate test (cycle 65 and 66),  again shows the highest capacity.Taking a closer look at the charge segment of the test, capacity follows a trend, with  having the highest values and  running at the lowest, see cycle 36.This correlates well with the resistance measurements in Figure 10, where  has the lowest resistance, which ultimately results in higher charge capabilities, due to a longer charging time before reaching cut-off criteria.As can be seen in the charge step 3C (cycle 51),  runs at 83.5 ± 0.4 mAh g −1 and  at 78 ± 0.7 mAh g −1 , showing a difference of roughly 6%.These data show that although the same materials and compositions were used in all four slurries, cell performance can be increased simply by mixing the slurry with a variation in solids content during kneading-thus changing the energy input of the mixing procedure.

Conclusions
Anode slurries containing graphite and silicon oxide as active materials, carbon black as the conductivity agent, and CMC and SBR as binders, with the same composition and total solids contents, were prepared at different energy inputs during slurry preparation and their impact on slurry rheology, coating behavior, mechanical and electrical properties of the resulting dry electrodes, and the electrochemical performance of cells made from these negative electrodes was investigated.Slurries were prepared using an Taking a closer look at the charge segment of the test, capacity follows a trend, with A 69 having the highest values and A 60 running at the lowest, see cycle 36.This correlates well with the resistance measurements in Figure 10, where A 69 has the lowest resistance, which ultimately results in higher charge capabilities, due to a longer charging time before reaching cut-off criteria.As can be seen in the charge step 3C (cycle 51), A 69 runs at 83.5 ± 0.4 mAh g −1 and A 60 at 78 ± 0.7 mAh g −1 , showing a difference of roughly 6%.These data show that although the same materials and compositions were used in all four slurries, cell performance can be increased simply by mixing the slurry with a variation in x i -solids content during kneading-thus changing the energy input of the mixing procedure.

Conclusions
Anode slurries containing graphite and silicon oxide as active materials, carbon black as the conductivity agent, and CMC and SBR as binders, with the same composition and total solids contents, were prepared at different energy inputs during slurry preparation and their impact on slurry rheology, coating behavior, mechanical and electrical properties of the resulting dry electrodes, and the electrochemical performance of cells made from these negative electrodes was investigated.Slurries were prepared using an intensive mixer and energy input varied over a wide range by adjusting the solids content during the mixing step, wherein water and a CMC solution were added to the dry mixture of graphite, SiO x and CB.This energy input during slurry preparation affects the deagglomeration of CB to some extent, but more importantly, it controls the mechanical degradation of CMC and its adsorption on the surface of the active material particles.The fraction of adsorbed CMC on the particles increases with increasing energy input and the corresponding increase in steric repulsion among the suspended particles leads to a drastic change in slurry rheology.The low shear viscosity and the degree of shear thinning decreases with increasing energy input, and at the highest energy level, steric repulsion balances the van der Waals attraction, resulting in an almost Newtonian flow behavior at low shear rates and pronounced shear thickening at high shear rates.The reduced viscosity at high energy inputs results in a narrower stability window during slot-die coating.The variation in CMC adsorption is also evident in the contact resistivity between the electrode layer and the current collector, which decreases as more CMC is adsorbed on the active material particles.Energy input also appears to have an effect on the distribution or agglomeration of SBR, as shown by a drastic drop in the peel strength of electrodes at the highest level of mixing energy input.Finally, the pouch cells built with the electrodes made from the differently prepared slurries all show good electrochemical performance.The cell based on the slurry prepared with the highest energy input exhibits a slightly higher charge capability compared to the cell made

Figure 1 .
Figure 1.(a) Schematic drawing of the intensive mixer showing the dispersion tool, the pan and the material; circumferential speed of the dispersing tool (ω ) and the pan (ω ); (b) solids content (square) and sample volume (circle) during the different mixing procedure steps.

Figure 1 .
Figure 1.(a) Schematic drawing of the intensive mixer showing the dispersion tool, the pan and the material; circumferential speed of the dispersing tool (ω w ) and the pan (ω P ); (b) solids content (square) and sample volume (circle) during the different mixing procedure steps.

Figure 2 .
Figure 2. Steps of the slurry mixing procedure; steps 2, 3 and 4 each comprise a first period with low and a second period with high stirring speed.* H2O adjustment to create different solids contents  in HSCM step; ** Second H2O dilution of the slurry to finalize it to the desired TSC.

Figure 2 .
Figure 2. Steps of the slurry mixing procedure; steps 2, 3 and 4 each comprise a first period with low and a second period with high stirring speed.* H 2 O adjustment to create different solids contents x i in HSCM step; ** Second H 2 O dilution of the slurry to finalize it to the desired TSC.

Figure 3 .
Figure 3. Schematic drawing of a slot-die, including flow pattern within the coating bead.

Figure 3 .
Figure 3. Schematic drawing of a slot-die, including flow pattern within the coating bead.

Figure 3 .
Figure 3. Schematic drawing of a slot-die, including flow pattern within the coating bead.

Figure 4 .
Figure 4. Inline photographs of the roll-to-roll coating experiments, web's direction from bottom to top; (a) coating outside stable operating window with visible air entrainment; (b) coating within the stable operating window.

Figure 4 .
Figure 4. Inline photographs of the roll-to-roll coating experiments, web's direction from bottom to top; (a) coating outside stable operating window with visible air entrainment; (b) coating within the stable operating window.

FOR PEER REVIEW 9 of 19 Figure 5 .
Figure5.Total rotor power consumption for the four variations of the mixing procedure   ; high solids content mixing (HSCM) occurred at   equal to 60 (a), 63 (b), 66 (c) and 69 (d) wt% solids content; legends refer to mixing steps 2, 3 and 4, as described in Figure2: high solids content mixing (HSCM), addition of SBR, and finalization by water addition to reach the target TSC 60 wt%.

Figure 5 .
Figure5.Total rotor power consumption for the four variations of the mixing procedure P i ; high solids content mixing (HSCM) occurred at x i equal to 60 (a), 63 (b), 66 (c) and 69 (d) wt% solids content; legends refer to mixing steps 2, 3 and 4, as described in Figure2: high solids content mixing (HSCM), addition of SBR, and finalization by water addition to reach the target TSC 60 wt%.

Figure 6 .
Figure 6.Viscosity as a function of shear rate for slurries with TSC = 60 wt%, but mixed at different solids content during HSCM;  = 60 (black), 63 (red), 66 (blue), 69 wt% (green) and low energy input reference slurry  (orange).The flow curve for a CMC solution (open symbols) with the same molecular weight Mw = 875 kDa as that used for slurry preparation and polymer concentration (13.5 g L −1 ) corresponding to that in the disperse phase of the slurry is shown for comparison.

Figure 6 .
Figure 6.Viscosity as a function of shear rate for slurries with TSC = 60 wt%, but mixed at different solids content during HSCM; x i = 60 (black), 63 (red), 66 (blue), 69 wt% (green) and low energy input reference slurry x Low (orange).The flow curve for a CMC solution (open symbols) with the same molecular weight Mw = 875 kDa as that used for slurry preparation and polymer concentration (13.5 g L −1 ) corresponding to that in the disperse phase of the slurry is shown for comparison.

Figure 8 .
Figure 8. Stability map for slot-die coating of slurries S 60 (black) and S 69 (green); USL-square symbol; LSL-triangle symbol; (a) dynamic gap as a function of line speed; (b) capillary number as a function of dynamic gap, including the VCM of Ruschak 1976 [28] (Equation 6, straight line).
. Since the total energy input varied by a factor of about three, this seems plausible.R PEER REVIEW 15 of 19

Figure 9 .
Figure 9. SEM cross-section of investigated compressed electrodes A 60 (a,c) and A 69 (b,d).

Figure 10 .Figure 10 .
Figure 10.(a) Resistivity of compressed electrodes  to  determined using an electrode resistance measurement system; (b) peel strength of compressed electrodes  to  .(a) (b)

Figure 11 .
Figure 11.Cycling data of investigated full pouch cells: (a) formation; (b) C-rate test.

Figure 11 .
Figure 11.Cycling data of investigated full pouch cells: (a) formation; (b) C-rate test.

Table 1 .
Gravimetric composition of the slurry with and without solvent.

Table 1 .
Gravimetric composition of the slurry with and without solvent.

Table 2 .
Specific energy input for all mixing procedure variations P i originating from the change in x i ; total amount of specific energy input and specific energy input at step 3, the dispersion of SBR.