Effect of Vinylene Carbonate Electrolyte Additive on the Surface Chemistry and Pseudocapacitive Sodium-Ion Storage of TiO2 Nanosheet Anodes

Although titanium dioxide has gained much attention as a sodium-ion battery anode material, obtaining high specific capacity and cycling stability remains a challenge. Herein, we report significantly improved surface chemistry and pseudocapacitive Na-ion storage performance of TiO2 nanosheet anode in vinylene carbonate (VC)-containing electrolyte solution. In addition to the excellent pseudocapacitance (~87%), the TiO2 anodes also exhibited increased high-specific capacity (219 mAh/g), rate performance (40 mAh/g @ 1 A/g), coulombic efficiency (~100%), and cycling stability (~90% after 750 cycles). Spectroscopic and microscopic studies confirmed polycarbonate based solid electrolyte interface (SEI) formation in VC-containing electrolyte solution. The superior electrochemical performance of the TiO2 nanosheet anode in VC-containing electrolyte solution is credited to the improved pseudocapacitive Na-ion diffusion through the polycarbonate based SEI (coefficients of 1.65 × 10−14 for PC-VC vs. 6.42 × 10−16 for PC). This study emphasizes the crucial role of the electrolyte solution and electrode–electrolyte interfaces in the improved pseudocapacitive Na-ion storage performance of TiO2 anodes.


Introduction
Lithium-ion batteries (LIBs) are widely used in the current generation of portable electronics, electric vehicles, and smart grids coupled with renewable energy sources [1][2][3][4]. Despite their high energy density, moderate power density, and good cycle life, there are concerns regarding the future large-scale implementation of LIBs due to the limited availability of expensive ($17,000 per metric ton) lithium resources, where market demand will be up to two to six times extraction capacity in the next two decades [5,6]. Rechargeable sodium-ion batteries (SIBs) are very attractive in this regard, due to the abundance of inexpensive sodium resources [3,5,7,8]. Moreover, the similar electrochemistry and redox potentials of lithium and sodium (−3.02 and −2.71 V vs. SHE, respectively), make it a suitable candidate for efficient electrochemical energy storage [9][10][11]. However, the larger size of Na-ions compared to Li-ions (1.02 and 0.76 Å radius, respectively) hinders their intercalation in the most commonly used Li-ion battery anode material, graphite (interlayer d-spacing of 3.4 Å) [1,12,13]. Shuttling of solvated Na-ions between individual electrodes is also sluggish, leading to the poor rate performance and cycling stability of Na-ion batteries [14]. Hence, numerous studies have focused on the development of alternative high-performance anode materials [15][16][17][18][19][20].
Carbonaceous materials with large interlayer spacing, such as hard carbon, graphene, and amorphous carbon have been widely investigated as anode materials [16,17]. However, these anodes exhibited low specific capacities, poor rate performances, and mediocre cycling stability. Despite the high specific capacity of conversion (Co 3 O 4 , SnO 2 , Fe 3 O 4 , Using electrolyte additives is one widely employed strategy to endow the SEIs with superior electrochemical properties [40,44]. Vinylene carbonate (VC) is one of the most commonly used electrolyte additives in the case of Li-ion batteries [41,44,45]. This has been mainly aimed at flexible SEI formation in large volume expansion conversion/alloying type anodes, and at preventing metal-ion leaching from high voltage cathodes [38,42,46]. The high electrochemical reactivity of VC results in the preferential formation of polymeric SEIs, which prevent further reaction of the electrode material with the electrolyte solution during extreme operating environments, including high temperature, and large volume change [40,44,47]. Use of VC in the case of Na-ion batteries is also mainly aimed at improving the cycling stability of high capacity conversion/alloying type anodes [46]. However, none of these studies investigated SEI composition tuning to enhance the pseudocapacitive Na-ion storage of TiO 2 anodes.
Herein, we report significantly improved pseudocapacitive Na-ion storage and surface chemistry of TiO 2 nanosheet anodes in VC-containing electrolyte solution. Vinylene carbonate, a widely used Li-ion battery additive was chosen in this case due to its ability to form SEIs with superior passivation and Na-ion diffusion properties. The presence of a double bond is mainly responsible for the preferential decomposition/polymerization of VC associated with the generation of polycarbonate based SEIs. Ultrathin, mesoporous, and high surface area TiO 2 nanosheets were selected as the preferred anode material in this case, to improve the contact with the electrolyte solution and thereby amplify the effect of the electrolyte additive on the surface chemistry and electrochemical performance. The excellent electrochemical performance of TiO 2 nanosheet anode in VC-containing electrolyte solution is credited to the superior pseudocapacitance, resulting from the faster Na-ion diffusion through the polycarbonate based surface film. Figure 1 shows the different solid electrolyte interface (SEI) composition on TiO 2 nanosheet anodes formed in vinylene carbonate (VC)-containing and VC-free electrolyte solutions.
Batteries 2021, 7, x FOR PEER REVIEW 3 of 22 also critical to prevent dissolution in the electrolyte solution, which can lead to continuous SEI formation at the expense of electrolyte decomposition, and cell failure. [38,41,44] Using electrolyte additives is one widely employed strategy to endow the SEIs with superior electrochemical properties. [40,44] Vinylene carbonate (VC) is one of the most commonly used electrolyte additives in the case of Li-ion batteries. [41,44,45] This has been mainly aimed at flexible SEI formation in large volume expansion conversion/alloying type anodes, and at preventing metal-ion leaching from high voltage cathodes. [38,42,46] The high electrochemical reactivity of VC results in the preferential formation of polymeric SEIs, which prevent further reaction of the electrode material with the electrolyte solution during extreme operating environments, including high temperature, and large volume change. [40,44,47] Use of VC in the case of Na-ion batteries is also mainly aimed at improving the cycling stability of high capacity conversion/alloying type anodes. [46] However, none of these studies investigated SEI composition tuning to enhance the pseudocapacitive Na-ion storage of TiO2 anodes.
Herein, we report significantly improved pseudocapacitive Na-ion storage and surface chemistry of TiO2 nanosheet anodes in VC-containing electrolyte solution. Vinylene carbonate, a widely used Li-ion battery additive was chosen in this case due to its ability to form SEIs with superior passivation and Na-ion diffusion properties. The presence of a double bond is mainly responsible for the preferential decomposition/polymerization of VC associated with the generation of polycarbonate based SEIs. Ultrathin, mesoporous, and high surface area TiO2 nanosheets were selected as the preferred anode material in this case, to improve the contact with the electrolyte solution and thereby amplify the effect of the electrolyte additive on the surface chemistry and electrochemical performance. The excellent electrochemical performance of TiO2 nanosheet anode in VC-containing electrolyte solution is credited to the superior pseudocapacitance, resulting from the faster Na-ion diffusion through the polycarbonate based surface film. Figure 1 shows the different solid electrolyte interface (SEI) composition on TiO2 nanosheet anodes formed in vinylene carbonate (VC)-containing and VC-free electrolyte solutions.

Materials Synthesis
TiO 2 nanosheets were synthesized through a solvothermal method [48]. In a typical synthesis, 4 mL of deionized water and 20% aqueous TiCl 3 (99.99%, Acros Organics) each were added dropwise in 50 mL of ethylene glycol (99.99%, Fisher Scientific) under continuous stirring. The dark brown solution was then heated to 150 • C for 6 h in a PTFE-lined stainless steel autoclave. The subsequent slurry was washed several times with Batteries 2021, 7, 1 4 of 21 deionized water and ethanol, and dried at 80 • C for 24 h to obtain bronze TiO 2 (TiO 2 -B) nanosheets. Hierarchical anatase-bronze hybrid TiO 2 nanosheets were obtained by heattreating TiO 2 -B nanosheets at 400 • C for 2 h under air flow (heating and cooling rates of 10 • C/min).

Materials Characterization
X-ray diffraction (XRD) patterns of the samples were collected using a PANalytical Empyrean high-resolution diffractometer equipped with a Cu-Kα X-ray source (λ = 1.5406 Å). The average crystallite size of the TiO 2 nanosheets was calculated using the Debye-Scherrer equation (D = K λ/β cosθ), where D is particle size, K is the shape factor 0.9, λ is the wavelength of the X-ray radiation of Cu-Kα, and β is the full width at half maximum (FWHM) of the highest intensity peak. Room temperature Raman analysis was performed with a Renishaw PLC Raman spectrometer equipped with a 532 nm Nd: YAG laser. Sample damage was avoided by limiting the laser power to 5 mW. FTIR spectra of pristine and cycled electrodes after washing with anhydrous acetonitrile (Sigma-Aldrich, 99.9%) were recorded using a Thermo Scientific Nicolet iS50 in attenuated total reflectance (ATR) mode, in the range of 4000-400 cm −1 . FTIR spectra of pristine, cycled and non-washed electrodes were also collected for comparison. Microstructural characterization of TiO 2 nanosheets was performed using a scanning electron microscope (FEI Helios NanoLab 600i) and highresolution transmission electron microscope (FEI Talos F200X FEG). X-ray photoelectron spectroscopy (XPS) measurements were performed using a SPECS PHOIBOS 150 9MCD instrument equipped with a Multi-Channeltron detector and a monochromatic X-ray source of twin Mg anodes. The binding energies of elements in the XPS spectra were set accordingly to the CC/CH component of the C 1s peak at 284.8 eV. For the quantitative analysis of SEI, high-resolution core-level spectra were used after removing the nonlinear Shirley background.
(1) k 1 v and k 2 v represent current contributions for diffusion-independent and diffusioncontrolled processes, respectively. k 1 and k 2 coefficients are the slope and intercept from the linear fit of the plot i(V) vs. v, respectively. Na-ion diffusion coefficients of TiO 2 nanosheets were determined using Equation (2).
where D is Na-ion diffusion coefficient at absolute temperature T, and R denotes the gas constant. Faraday's constant, Na-ion concentration in electrolyte, and electrode area are represented as F, C and A, respectively. Warburg impedance, σ w , was calculated from the slope of the linear plot of Z' vs. ω −1/2 .

Synthesis and Characterization of TiO 2 Nanosheets
Hierarchical TiO 2 nanosheets composed of anatase and bronze nanocrystallites were synthesized through a solvothermal method, followed by controlled heat treatment. Ethylene glycol was used as solvent to facilitate nanosheet formation through the interaction of OH groups of glycol with Ti-OH groups [48,49]. This resulted in the free energy change of the TiO 2 crystallographic planes and an associated anisotropic crystal growth [29,49]. Selection of a less reactive precursor TiCl 3 was aimed at controlled hydrolysis and condensation, which is necessary for the nanosheet formation [50]. The uniform size/shape distributions and ultrathin nature of the sheets were also assisted by the high viscosity of ethylene glycol [9]. Reaction between TiCl 3 and ethylene glycol resulted in the formation of Ti-glycolate complex during the hydrothermal reaction. Further hydrolysis and condensation formed TiO 2 bronze nanosheets, which was transformed to anatase-bronze hybrid nanosheets upon controlled heat treatment. Scanning electron microscopy (SEM) images of the TiO 2 nanosheets demonstrated their 2D morphology and (Figure 2a The presence of well-defined anatase-bronze nanograin boundaries is also evident from these images [9]. This was anticipated, due to the mismatch between anatase and bronze crystal structures. Nanograin boundaries present in metal oxides often result in unique physical/ chemical properties, including excellent catalytic and electrochemical performance [51]. Nanointerfaces present in these hierarchical TiO 2 nanosheets can also act as additional sites for Na-ion storage. Our previous study confirmed the advantages of such nanointerfaces for enhancing pseudocapacitive type Na-ion storage [9].   [9] The anatase and bronze content, calculated from the relative intensity of the (310) bronze peak and (004) anatase peak, was found to be 83% and 17%, respectively. Particle size calculation, using a Debye-Scherrer equation also revealed the existence of 7 ± 2 nm sized crystallites, which was in good agreement with the TEM results. A more surface sensitive technique, Raman spectroscopy was used to further confirm the phase  [9]. The anatase and bronze content, calculated from the relative intensity of the (310) bronze peak and (004) anatase peak, was found to be 83% and 17%, respectively. Particle size calculation, using a Debye-Scherrer equation also revealed the existence of 7 ± 2 nm sized crystallites, which was in good agreement with the TEM results. A more surface sensitive technique, Raman spectroscopy was used to further confirm the phase purity and uniform nanoscale distribution of the anatase and bronze polymorphs ( Figure 2e). Raman active modes were 144, 197, 399, 514, and 639 cm −1 for anatase, and 123, 145, 161, 172, 196, 201, and 259 cm −1 for bronze polymorphs [52]. These results and the quantification of anatase/bronze content from high-resolution Raman spectra ( Figure S1) were also in line with the XRD results, confirming the coexistence and nanoscale distribution of anatase and bronze nanocrystallites [52]. The textural property investigation of TiO 2 nanosheets was performed through N 2 adsorption-desorption analysis (Figure 2f). This active material exhibited a high surface area of 106 m 2 /g. Type IV isotherms and H3 type hysteresis, characteristic of a mesoporous structure were identified in this case [13]. Mesoporosity was also evidenced by the higher steepness of the isotherm at high relative pressure (P/P0 = 0.4-1.0) [13]. Barrett-Joyner-Halenda (BJH) method pore size distribution measurements (Figure 2f inset) further confirmed the mesoporosity of the TiO 2 nanosheets. Such high surface area and mesoporosity of the active material are advantageous for improved Na-ion storage due to the superior contact with the electrolyte solution, and the possibility of pore/defect assisted pseudocapacitive type ion storage [49]. Thus, it can be summarized that controlled hydrolysis and condensation of TiCl 3 in ethanol water mixture followed by calcination resulted in the formation of mesoporous hierarchical anatase-bronze hybrid TiO 2 nanosheets.

Electrochemical Performance of the TiO 2 Nanosheets
The sodium-ion storage electrochemical performance of the TiO 2 nanosheets was investigated in VC-containing (PC-VC/NaClO 4 ) and VC-free (PC/NaClO 4 ) electrolyte solutions. Second galvanostatic voltage profiles at different current densities (Figure 3a,b) indicated the marginally superior specific capacities of the TiO 2 nanosheet anodes in PC-VC/NaClO 4 electrolyte at various charge-discharge rates. First cycle coulombic efficiencies of 36% and 44.5% were observed in the PC/NaClO 4 and PC-VC/NaClO 4 electrolyte solutions, respectively ( Figure S2). Irreversible capacity loss in the first cycle was attributed to unavoidable electrolyte decomposition, and irreversible Na 2 O formation associated with sodiation. Coulombic efficiency reached~100% after the first charge-discharge in PC-VC/NaClO 4 electrolyte, demonstrating the complete formation of high quality SEI during the first cycle. However, coulombic efficiency never reached~100% on extended cycling in PC/NaClO 4 electrolyte, which indicated the formation of an SEI with inferior passivation properties. This is also apparent from the consecutive cyclic voltammograms presented (Figure 3c,d). The TiO 2 nanosheet anodes exhibited a similar electrochemical response, irrespective of the electrolyte composition. Three different electrochemical processes constitute the first cathodic response in both systems. The high-voltage region between 2.25 and 0.7 V represents diffusion-independent pseudocapacitive Na-ion intercalation [53]. SEI formation resulting from the electrolyte decomposition could be identified from the cathodic response between 0.7 and 0.5 V [9]. Lack of this signal in the second cathodic scan confirmed complete SEI formation in the first charge-discharge cycle [32,54]. A low voltage region between 0.2 and 0 V corresponded to the diffusion controlled Na-ion intercalation into the anatase and bronze crystal structure [36]. These electrochemical responses were in line with the plateau at low potential and sloping voltage profiles. Anodic response in the voltage range of 0.2 V, and a broad signal between 0.5 and 2.25 V represented Na-ion deintercalation through pseudocapacitive and diffusion dependent process, respectively. Batteries 2021, 7, x FOR PEER REVIEW 8 of 22 Sodiation over a wide voltage range was observed in this case, which was noticeably different from the intercalation reaction at specific potentials for previously reported TiO2 anodes. [27] Distinct Na-ion storage was also evidenced by the marginally different shape of the voltammograms compared to earlier reports. [37] Although cathodic signals corresponding to SEI formation disappeared in the first cycle, there was a clear indication of irreversibility and incomplete SEI formation during the consecutive cycles of the VC-free battery, which was not observed in the case of the VC-containing Na-ion half-cells. This was a clear indication of efficient SEI formation on the TiO2 nanosheet anodes in the VCcontaining electrolyte solution. Thus, disappearance of the SEI formation peak in the first cycle and stable consecutive cycles confirmed the highly reversible Na-ion intercalation reactions of the TiO2 nanosheet anodes in VC-containing electrolyte solution. The galvanostatic rate performance of the TiO2 nanosheet anodes in both VC-free and VC-containing electrolyte solutions is presented in Figure 4a. Second cycle specific capacities were 247 and 219 mAh/g, respectively. Slightly higher capacities were identified in the case of VC-containing electrolyte solution during the following cycles at 25 mA/g. Capacity differences became more prominent at higher current densities, and also increased on reducing the current density to 25 mA/g. This was a clear indication of the capacity fading Sodiation over a wide voltage range was observed in this case, which was noticeably different from the intercalation reaction at specific potentials for previously reported TiO 2 anodes [27]. Distinct Na-ion storage was also evidenced by the marginally different shape of the voltammograms compared to earlier reports [37]. Although cathodic signals corresponding to SEI formation disappeared in the first cycle, there was a clear indication of irreversibility and incomplete SEI formation during the consecutive cycles of the VCfree battery, which was not observed in the case of the VC-containing Na-ion half-cells. This was a clear indication of efficient SEI formation on the TiO 2 nanosheet anodes in the VC-containing electrolyte solution. Thus, disappearance of the SEI formation peak in the first cycle and stable consecutive cycles confirmed the highly reversible Na-ion intercalation reactions of the TiO 2 nanosheet anodes in VC-containing electrolyte solution. The galvanostatic rate performance of the TiO 2 nanosheet anodes in both VC-free and VCcontaining electrolyte solutions is presented in Figure 4a. Second cycle specific capacities were 247 and 219 mAh/g, respectively. Slightly higher capacities were identified in the case of VC-containing electrolyte solution during the following cycles at 25 mA/g. Capacity differences became more prominent at higher current densities, and also increased on reducing the current density to 25 mA/g. This was a clear indication of the capacity fading of TiO 2 anode in VC-free electrolyte, which was further verified during the extended galvanostatic cycling (Figure 4b).
Batteries 2021, 7, x FOR PEER REVIEW 9 of 22 of TiO2 anode in VC-free electrolyte, which was further verified during the extended galvanostatic cycling (Figure 4b). Both cells demonstrated ~100% coulombic efficiency after 750 cycles at a current density of 100 mA/g. Galvanostatic long-cycling performance of electrolyte solutions containing different amounts of VC confirmed 3% as the optimum concentration ( Figure S3). For instance, at a current density of 100 mA/g, TiO2 nanosheet anode in Na-ion half-cell configuration retained 90% of the initial capacity, with ~100% coulombic efficiency after 750 galvanostatic charge-discharge cycles. On the other hand, Na-ion half-cells containing VC-free electrolyte solution retained only 16% of the initial capacity, with ~98% coulombic efficiency.
Electrochemical impedance spectroscopy (EIS) of pristine and cycled electrodes (Figure 4c,d) is performed to gain further insights into the effect of SEI films on the charge transfer, and Na-ion diffusion characteristics. High-to-medium frequency part of the EIS pattern can be assigned to the sum of SEI/contact resistance and charge-transfer resistance and represented as RΩ and Rct respectively in the Randles-like equivalent circuit (Figure  4d inset). Low frequency sloping line corresponds to solid-state diffusion kinetics of Naions shown as Warburg impedance (Zw) while constant phase element (CPE) is used to model the surface storage of Na-ions. [7,49,55] Charge transfer resistances of pristine TiO2 nanosheet anodes in VC-free and VC-containing electrolyte solutions, obtained by fitting the Nyquist plot to the equivalent circuit, are 39 Ω and 171 Ω respectively. It is interesting Both cells demonstrated~100% coulombic efficiency after 750 cycles at a current density of 100 mA/g. Galvanostatic long-cycling performance of electrolyte solutions containing different amounts of VC confirmed 3% as the optimum concentration ( Figure S3). For instance, at a current density of 100 mA/g, TiO 2 nanosheet anode in Na-ion half-cell configuration retained 90% of the initial capacity, with~100% coulombic efficiency after 750 galvanostatic charge-discharge cycles. On the other hand, Na-ion half-cells containing VC-free electrolyte solution retained only 16% of the initial capacity, with~98% coulombic efficiency.
Electrochemical impedance spectroscopy (EIS) of pristine and cycled electrodes (Figure 4c,d) is performed to gain further insights into the effect of SEI films on the charge transfer, and Na-ion diffusion characteristics. High-to-medium frequency part of the EIS pattern can be assigned to the sum of SEI/contact resistance and charge-transfer resistance and represented as R Ω and R ct respectively in the Randles-like equivalent circuit (Figure 4d inset). Low frequency sloping line corresponds to solid-state diffusion kinetics of Naions shown as Warburg impedance (Z w ) while constant phase element (CPE) is used to model the surface storage of Na-ions [7,49,55]. Charge transfer resistances of pristine TiO 2 nanosheet anodes in VC-free and VC-containing electrolyte solutions, obtained by fitting the Nyquist plot to the equivalent circuit, are 39 Ω and 171 Ω respectively. It is interesting to observe such impedance difference in pristine batteries as VC is supposed to influence SEI formation only during the first charge-discharge cycle. This could be related to the spontaneous SEI formation resulting from the increased reactivity of high surface area TiO 2 nanosheets with the electrolyte solution even in the absence of applied potential. Such surface film formations were also observed previously in the case of pyrolytic graphite, carbon and silicon nanowire electrodes [41,56,57]. Charge transfer resistance in VC-free electrolyte solution increased to 517 Ω after 30 galvanostatic cycles. In contrast, resistance decreased to 105 Ω in the case of VC-containing half-cells. Na-ion diffusion coefficients of TiO 2 nanosheet anodes after 30 galvanostatic cycles in VC-free and VC containing electrolyte solutions calculated from the Nyquist plot are 6.42 × 10 −16 and 1.65 × 10 −14 correspondingly. Hence it is clear that VC-addition significantly reduces the charge transfer resistance and enhances the Na-ion diffusion kinetics, facilitating improved Na-ion diffusion into the TiO 2 nanosheets. These results are also in good agreement with the superior cycling performance of TiO 2 nanosheet electrodes in VC-containing electrolyte solution.
The sodium-ion storage mechanism of TiO 2 nanosheets in VC-free and VC-containing electrolyte solutions was further investigated by collecting cyclic voltammograms at various scan rates (Figure 5a,b). Considerable differences existed in the voltammograms in the two different electrolyte solutions. High peak current and area were identified for the TiO 2 nanosheets in the VC-containing electrolyte, which is in line with their improved Na-ion storage performance observed from the galvanostatic rate performance and cycling studies. The shapes of the voltammograms were also different suggesting different Na-ion storage mechanisms. Anodic and cathodic current increased with an increase of scan rate in both electrolyte solutions, which is indicative of pseudocapacitive type Na-ion storage [21].
Sodium ion intercalation of TiO 2 nanosheets, especially at higher scan rates, occurs over a wide voltage range in VC-containing electrolyte solution. Such broad signals indicate the increased diffusion independent behavior of Na-ion intercalation, which is typical in capacitive type electrode materials [58].
The sodium-ion storage of TiO 2 nanosheet anodes consists of both diffusion limited and surface controlled process [59]. These components can be differentiated from the relationship between peak current density and scan rates, as presented in Equation (3) [21] where current shown as i, the scan rate as v, and a and b are adjustable variables. If b = 0.5, storage process is identified as diffusion-controlled, and surface controlled if b = 1.0 [60]. Moreover, as the Randles-Ševcik equation dictates, the increase of current is proportional to the square root of scan rate [55,61,62]. The slope of peak current density vs. scan rate plot (Figure 5c,d) represented dominant pseudocapacitive type Na-ion storage (increased slope) in TiO 2 nanosheets, with a high degree of pseudocapacitance in the PC-VC/NaClO 4 electrolyte solution.
The diffusion limited and pseudocapacitive contributions of specific capacities were quantified to further investigate the effect of electrolyte solutions on the Na-ion storage mechanism. Capacitive and diffusion controlled contributions of Na-ion half-cells containing PC/NaClO 4 and PC-VC/NaClO 4 electrolyte solutions at different scan rates are presented in Figure 6a,b. TiO 2 nanosheet anode exhibited superior pseudocapacitive Na-ion storage in PC-VC/NaClO 4 electrolyte solution (83% @ 1 mV/s) compared to PC/NaClO 4 (63% @ 1 mV/s). Capacitance calculations were also performed after 30 galvanostatic cycles (Figure 6c,d) in order to investigate the capacity fading on extended cycling. The pseudocapacitance contribution of the TiO 2 nanosheets reduced considerably (37% @ 1 mV/s), and slightly increased (87% @ 1 mV/s) in the PC/NaClO 4 and PC-VC/NaClO 4 electrolyte solutions, respectively (Figure 6e,f). The entirely different shape of the cyclic voltammograms also signified different Na-ion storage mechanisms in these TiO 2 nanosheet anodes during extended cycling. It is worth noting that these results are in agreement with the EIS results presented earlier, where the impedance of the TiO 2 anodes continually increased during galvanostatic cycling in PC/NaClO 4 , and decreased in the PC-VC/NaClO 4 electrolyte solutions. These observations led to the conclusion that the SEI formed in the VC-containing electrolyte solutions facilitated improved pseudocapacitive Na-ion diffusion into the TiO 2 nanosheet anode. Hence, it is clear that the electrolyte composition played a crucial role in the cycling stability, impedance, and Na-ion storage mechanism of the TiO 2 nanosheet anodes. Sodium ion intercalation of TiO2 nanosheets, especially at higher scan rates, occurs over a wide voltage range in VC-containing electrolyte solution. Such broad signals indicate the increased diffusion independent behavior of Na-ion intercalation, which is typical in capacitive type electrode materials. [58] The sodium-ion storage of TiO2 nanosheet anodes consists of both diffusion limited and surface controlled process. [59] These components can be differentiated from the relationship between peak current density and scan rates, as presented in Equation (3). [21] = (3) where current shown as , the scan rate as , and and are adjustable variables. If b = 0.5, storage process is identified as diffusion-controlled, and surface controlled if b = 1.0. [60] Moreover, as the Randles-Ševcik equation dictates, the increase of current is proportional to the square root of scan rate.[55,61,62] The slope of peak current density vs scan rate plot (Figure 5c,d) represented dominant pseudocapacitive type Na-ion storage (increased slope) in TiO2 nanosheets, with a high degree of pseudocapacitance in the PC-VC/NaClO4 electrolyte solution.

Surface Chemical Characterization of TiO2 Nanosheets
It is crucial to understand the surface chemistry of TiO2 nanosheet electrodes cycled in VC-free and VC-containing electrolyte solutions due to the significant role of surface films on electrochemical performance. Surface chemical characterizations of these electrodes cycled in PC/NaClO4 and PC-VC/NaClO4 electrolyte solutions were performed using ex-situ XPS and FTIR techniques. Electrodes were thoroughly washed with acetonitrile and dried under vacuum to make sure that there was no residual NaClO4 salt and solvent left to interfere with these spectroscopic measurements. The quantification of elements present in the surface films formed in VC-free and VC-containing electrolyte solutions (Table 1) indicated the contribution of both solvent and Na-salt towards SEI formation. Higher oxygen and carbon concentrations found in the surface film confirmed solvent reduction as the major reaction responsible for SEI formation. Surface films

Surface Chemical Characterization of TiO 2 Nanosheets
It is crucial to understand the surface chemistry of TiO 2 nanosheet electrodes cycled in VC-free and VC-containing electrolyte solutions due to the significant role of surface films on electrochemical performance. Surface chemical characterizations of these electrodes cycled in PC/NaClO 4 and PC-VC/NaClO 4 electrolyte solutions were performed using ex-situ XPS and FTIR techniques. Electrodes were thoroughly washed with acetonitrile and dried under vacuum to make sure that there was no residual NaClO 4 salt and solvent left to interfere with these spectroscopic measurements. The quantification of elements present in the surface films formed in VC-free and VC-containing electrolyte solutions (Table 1) indicated the contribution of both solvent and Na-salt towards SEI formation. Higher oxygen and carbon concentrations found in the surface film confirmed solvent reduction as the major reaction responsible for SEI formation. Surface films formed in VC-containing electrolyte had a higher carbon and oxygen content, signifying the increased formation of numerous oxygen containing species, such as Na-carbonate, Na-alkyl carbonate, Na-alkoxides, and Na-polycarbonates, due to PC and VC reduction [63]. Lower Na and Cl content in this case was a clear indication of reduced Na-salt decomposition, which is vital to maintain good ionic conductivity during extended cycling. Increased Ti-content signifies the formation of surface films that allow superior X-ray/ electron penetration and detection of Ti-atoms underneath. XPS spectra of the elements of interest present in the TiO 2 anode surface films formed in both electrolyte solutions (PC/NaClO 4 and PC-VC/NaClO 4 ) are presented in Figures 7 and 8. These spectra demonstrated a significant difference in the chemical composition of surface films. Alkyl carbonate solvents (PC and VC in this case) can be easily reduced to organic and inorganic Na-salts under an applied potential [64].
Batteries 2021, 7, x FOR PEER REVIEW 14 of 22 formed in VC-containing electrolyte had a higher carbon and oxygen content, signifying the increased formation of numerous oxygen containing species, such as Na-carbonate, Na-alkyl carbonate, Na-alkoxides, and Na-polycarbonates, due to PC and VC reduction. [63] Lower Na and Cl content in this case was a clear indication of reduced Na-salt decomposition, which is vital to maintain good ionic conductivity during extended cycling. Increased Ti-content signifies the formation of surface films that allow superior Xray/ electron penetration and detection of Ti-atoms underneath. XPS spectra of the elements of interest present in the TiO2 anode surface films formed in both electrolyte solutions (PC/NaClO4 and PC-VC/NaClO4) are presented in Figures 7  and 8. These spectra demonstrated a significant difference in the chemical composition of surface films. Alkyl carbonate solvents (PC and VC in this case) can be easily reduced to organic and inorganic Na-salts under an applied potential. [64]    As presented in scheme 1, two electron PC reduction in the presence of Na-ions leads to sodium carbonate (Na2CO3) and propylene (CH2=CH-CH3), whereas one electron reduction results in sodium alkyl carbonate (CH2OCO2Na)2 and ethylene (CH2=CH2) formation. On the other hand, PC reaction with perchlorate anion (ClO4 -) forms hydrogen perchlorate (HClO4), carbondioxide, and acetaldehyde radical. [65] The sodium alkyl carbonate produced interacting with the trace amounts of water present in the electrolyte could produce more sodium carbonate (where R = -CH3, or CH3-CH2), carbondioxide, sodium hydroxide, and/or ROH species. [66] Protons generated by the dissociation of HClO4 could react with NaClO4 to form HCl, and sodium hydroxide (NaOH). Previously formed NaOH species reacted with the PC solvent to produce sodium alkyl carbonates. [67] Initially formed sodium alkyl carbonates react with the sodium carbonate and hydrochloric acid (HCl), and in the following steps generating sodium chloride (NaCl), desodiated alkyl carbonate (ROCO2H), and carbonic acid (H2CO3). This step can also form sodium bicarbonate (NaHCO3) instead of carbonic acid. [66] Most importantly, the increased reactivity of VC due to the presence of a double bond could form higher complexity sodiated polymers, such as sodium ethylene dicarbonate (NaO2CO-C2H4-OCO2Na), sodium butylene carbonate (CH2CH2OCO2Na)2, and poly-vinylene carbonate. [41,64,66] Hence, the effect of solvents on the salt reduction can be investigated by comparing the Cl-concentration in the surface film. Among the carbonate solvents used in this case, VC is more reactive than PC towards electrochemical reduction, which leads to the difference in the SEI composition and properties. [47] In the case of PC/NaClO4 electrolyte solution, high-resolution C 1s spectrum (Figure 7b) consisted of three distinct peaks located at 284.8 eV, 286.4 eV, and 289.6 eV, and characteristic of elemental carbon (C-C bonds), C-O-C/ C-O groups of RONa, and C=O groups of ROCO2Na/ Na2CO3 species, respectively. [28,68] Signals corresponding to alkoxy groups were absent in the case of the VCcontaining electrolyte solution (Figure 8b). The relative intensity of the ROCO2Na peaks was also less, which clearly indicated difference in the surface film composition. The O 1s As presented in Scheme 1, two electron PC reduction in the presence of Na-ions leads to sodium carbonate (Na 2 CO 3 ) and propylene (CH 2 =CH-CH 3 ), whereas one electron reduction results in sodium alkyl carbonate (CH 2 OCO 2 Na) 2 and ethylene (CH 2 =CH 2 ) formation. On the other hand, PC reaction with perchlorate anion (ClO 4 − ) forms hydrogen perchlorate (HClO 4 ), carbondioxide, and acetaldehyde radical [65]. The sodium alkyl carbonate produced interacting with the trace amounts of water present in the electrolyte could produce more sodium carbonate (where R = -CH 3 , or CH 3 -CH 2 ), carbondioxide, sodium hydroxide, and/or ROH species [66]. Protons generated by the dissociation of HClO 4 could react with NaClO 4 to form HCl, and sodium hydroxide (NaOH). Previously formed NaOH species reacted with the PC solvent to produce sodium alkyl carbonates [67]. Initially formed sodium alkyl carbonates react with the sodium carbonate and hydrochloric acid (HCl), and in the following steps generating sodium chloride (NaCl), desodiated alkyl carbonate (ROCO 2 H), and carbonic acid (H 2 CO 3 ). This step can also form sodium bicarbonate (NaHCO 3 ) instead of carbonic acid [66]. Most importantly, the increased reactivity of VC due to the presence of a double bond could form higher complexity sodiated polymers, such as sodium ethylene dicarbonate (NaO 2 CO-C 2 H 4 -OCO 2 Na), sodium butylene carbonate (CH 2 CH 2 OCO 2 Na) 2 , and poly-vinylene carbonate [41,64,66].
TiO2 nanosheet anodes cycled in PC-VC/NaClO4 electrolyte solution (Figure 9f-j ified homogeneous SEI formation. Hence, it is clear that the difference in pseu tance and cycling stabilities was a consequence of the different chemical compo the surface films rather than their thickness. This should be expected, considerin imal volume changes of the TiO2 anode during the charge-discharge process unlikely to form thicker SEI due to limited electrolyte consumption only in the cles. Hence, the effect of solvents on the salt reduction can be investigated by comparing the Cl-concentration in the surface film. Among the carbonate solvents used in this case, VC is more reactive than PC towards electrochemical reduction, which leads to the difference in the SEI composition and properties [47]. In the case of PC/NaClO 4 electrolyte solution, high-resolution C 1s spectrum (Figure 7b) consisted of three distinct peaks located at 284.8 eV, 286.4 eV, and 289.6 eV, and characteristic of elemental carbon (C-C bonds), C-O-C/ C-O groups of RONa, and C=O groups of ROCO 2 Na/ Na 2 CO 3 species, respectively [28,68]. Signals corresponding to alkoxy groups were absent in the case of the VC-containing electrolyte solution (Figure 8b). The relative intensity of the ROCO 2 Na peaks was also less, which clearly indicated difference in the surface film composition. The O 1s spectra of the TiO 2 anodes cycled in VC-free electrolyte solution (Figure 7c) could be deconvoluted into individual peaks located at 531.0 eV, 532.6 eV, and 533.3 eV, corresponding to alkoxides, ether, and carbonate groups present in the surface film [49,68,69].
Due to the presence of similar functional groups, it was difficult to distinguish ROCO 2 Na present in VC-free and polycarbonate groups formed in VC-containing electrolyte solutions. However, slightly increased O 1s binding energies (531.2, 532.8, 533.5 eV, respectively) and increased width in the case of PC-VC/NaClO 4 indicated ( Figure 8c) the presence of higher carbonate concentration in the SEI, possibly due to polycarbonate formation resulting from VC-decomposition. Increased oxygen and carbon content quantified from the high-resolution spectra (Table 1) also indicated the presence of higher carbonate content in the case of the VC-containing electrolyte solution. Hence, it can be concluded that the surface films formed in both VC-free electrolyte solutions consisted of alkoxides, carbonates, and ether species. Whereas alkoxides were absent in the polycarbonate rich surface film formed in the VC-containing electrolyte solution.
High-resolution Cl 2p spectra related to both the VC-free and VC-containing electrolyte solutions exhibited similar features (Figures 7d and 8d). Individual peaks at 198.1 and 199.7 eV correspond to the Cl 2p 3/2 and Cl 2p 1/2 components, respectively, of inorganic chlorides (mainly NaCl) present in the surface film [70]. Signals corresponding to organic chlorides were not identified in the case of both electrolyte solutions. Increased salt (NaClO 4 ) decomposition in the case of the VC-free electrolyte solution is also evidenced by the lower relative amount (Table 1) of inorganic chlorides in the surface film. This can be credited to the more pronounced ClO 4 − reduction in the absence of highly reactive VC electrolyte additive. High-resolution Na 1s spectra in the case of both electrolyte solutions (Figures 7e and 8e) were identical, with a prominent peak at 1071.4 eV indicating the presence of NaCl in the surface film [70]. High-resolution Ti 2p spectra in the case of the surface films formed in both electrolyte solutions (Figures 7f and 8f) exhibited signals at 458.1 eV and 463.9 eV, which are characteristic of the Ti 2p 3/2 and Ti 2p 1/2 components of Ti 4+ ions [53]. This is in good agreement with the intercalation-type pseudocapacitive Na-ion storage mechanism we reported earlier for these anatase-bronze hybrid nanosheets [9]. Identical Na 1s and Ti 2p signals also verified a similar Na-ion storage mechanism of TiO 2 nanosheets in both VC-free and VC-containing electrolyte solutions. Increased Na and Ti concentration in the case of PC/NaClO 4 and PC-VC/NaClO 4 can be attributed to the enhanced NaClO 4 decomposition in the absence of VC, and superior transparency of polycarbonate based surface film for X-rays/electron beam, correspondingly.
Further surface chemical studies of the TiO 2 were performed by ATR-FTIR spectral measurements. FTIR spectra of non-cycled TiO 2 nanosheet electrodes, after cycling in VC-free and VC-containing electrolyte solutions (Figure 9a), exhibited clear differences in the surface chemical composition. Presence of ROCO 2 Na and Na 2 CO 3 as the major components resulting from PC reduction was evident from these spectra [64,67,70]. Peaks indicative of the symmetric and asymmetric stretch mode of C-O bond (v C-O) present in ROCO 2 Na appeared in the 1450-1360 cm −1 and 1650-1540 cm −1 regions, respectively [67,71]. Scissoring vibrations for OCO 2 − (δ OCO 2 − ) from the same species appeared at 871/877 cm −1 for both electrolyte compositions [67,72]. C-H stretching (v C-H) bands appear at higher frequencies between 2999 and 2930, which were identical to the previous reports for electrodes cycled in VC-free electrolytes [57,67]. Signals in the 2340-2350 cm −1 range indicated the presence of atmospheric CO 2 [41]. Peaks at 1295 cm −1 , 1075 cm −1 , and 1067 cm −1 belong to CO stretching/ CH 3 deformation coming from the organic species containing -ONa and/or -OCO 2 Na functional groups and double bonds [57,71]. Peaks originating from the carbonate group of Na 2 CO 3 (v CO 3 −2 ) were clearly visible at 1398 cm −1 /1400 cm −1 in the spectra [72]. These signals were absent in the spectra of the pristine TiO 2 electrode, confirming surface film formation only during the electrochemical charge-discharge process. Interestingly, additional peaks corresponding to PC/VC solvents and NaClO 4 salts are not visible in the case of the non-washed electrodes ( Figure S4). This could be due to the dominant FTIR intensities of the SEI components compared to trace amounts of solvent and Na-salt. Similar FTIR spectra before and after washing confirmed that the SEI components were not damaged by acetonitrile solvent. could be due to the dominant FTIR intensities of the SEI components compared to trace amounts of solvent and Na-salt. Similar FTIR spectra before and after washing confirmed that the SEI components were not damaged by acetonitrile solvent. Thus, the FTIR signals clearly demonstrated the formation of alkoxides and carbonates formed as a result of electrolyte decomposition (Scheme 1). The spectra related to Thus, the FTIR signals clearly demonstrated the formation of alkoxides and carbonates formed as a result of electrolyte decomposition (Scheme 1). The spectra related to PC/NaClO 4 and PC-VC/NaClO 4 electrolyte solutions are somewhat similar. The major difference between these spectra is the presence of polycarbonate peaks at around 1780 cm −1 in the case of the VC-containing electrolyte [57]. It is indeed clear that VC-addition to PC/NaClO 4 electrolyte solution resulted in the formation of a polycarbonate rich surface film, along with Na 2 CO 3 and ROCO 2 Na species. Post-cycling SEM images (Figure 9b-e) of the TiO 2 nanosheet anode confirmed their structural stability during the sodiationdesodiation process. Individual petals of the agglomerated TiO 2 nanosheets were clearly visible through the surface films formed in both electrolyte solutions. EDX mapping of the TiO 2 nanosheet anodes cycled in PC-VC/NaClO 4 electrolyte solution (Figure 9f-j) also verified homogeneous SEI formation. Hence, it is clear that the difference in pseudocapacitance and cycling stabilities was a consequence of the different chemical compositions of the surface films rather than their thickness. This should be expected, considering the minimal volume changes of the TiO 2 anode during the charge-discharge process, which is unlikely to form thicker SEI due to limited electrolyte consumption only in the initial cycles.
Surface chemical analysis results obtained from the ATR-FTIR measurements were in line with the XPS results discussed above. These spectral studies enabled us to differentiate the surface chemical aspects responsible for the increased pseudocapacitive Na-ion storage in VC-containing electrolyte solution. Surface film formation in the two different electrolyte solutions can be described as follows: In PC/NaClO 4 electrolyte, PC reduction into Na 2 CO 3 and ROCO 2 Na are the primary processes contributing to the surface film. There exists a competition between the PC and VC reduction in the case of PC-VC/NaClO 4 electrolyte solution [47]. VC is the most reactive component, and surface films formed in this case constitute both VC polymerization and PC reduction products. Polycarbonates formed during the initial charge-discharge cycles, as a result of VC-decomposition, protect the highly reactive TiO 2 anode from further reaction with the electrolyte solution. Improved passivation also resulted in the reduced decomposition of the NaClO 4 salt, which is crucial for maintaining good ionic conductivity during extended charge-discharge cycles. Significantly improved pseudocapacitance resulted from the ultrafast Na-ion diffusion through the polycarbonate based surface film. It should be noted that improved electrochemical performance of graphite and silicon nanowire anodes in VC/ FEC containing electrolyte solutions has been observed previously [41]. Nevertheless, such drastic difference in the pseudocapacitive Na-ion storage mechanism has never been identified. In conclusion VC electrolyte additive resulted in excellent long term cycling stability and pseudocapacitive Na-ion storage, a consequence of the superior passivation and Na-ion transport properties of the polycarbonate-rich surface film.

Conclusions
The effects of vinylene carbonate (VC) as an electrolyte additive on the surface chemistry and Na-ion storage mechanism was thoroughly investigated. TiO 2 nanosheet anodes achieved enhanced long-term cycling stability and pseudocapacitance in VC-containing electrolyte solution compared to VC-free composition. FTIR and XPS surface chemical characterizations of TiO 2 nanosheets cycled in VC-containing electrolyte solution confirmed the formation of polycarbonate rich surface film. Whereas, the VC-free electrolyte solution resulted in the formation of a sodium alkyl carbonate and sodium carbonate based surface film. The superior electrochemical performance of the TiO 2 nanosheets in VC-containing electrolyte solution is credited to the faster pseudocapacitive Na-ion diffusion through the polycarbonate-based surface film. These results demonstrated that TiO 2 nanosheet anodes in VC-containing alkyl carbonate electrolyte solutions can be utilized for advanced high-performance Na-ion batteries.
Author Contributions: R.R.M. and V.E., conceptualize the idea; R.R.M., performed materials synthesis and characterization; R.R.M. and V.E., together wrote the manuscript; V.E., also performed supervision of the work. All authors have read and agreed to the published version of the manuscript.

Data Availability Statement:
The data presented in this study are available within the article and/or supplementary material.