Electrospun Al 2 O 3 Film as Inhibiting Corrosion Interlayer of Anode for Solid Aluminum–Air Batteries

: Solid Al–air batteries are a promising power source for potable electronics due to their environmentally friendly qualities and high energy density. However, the solid Al–air battery su ﬀ ers from anodic corrosion and it is di ﬃ cult to achieve a higher speciﬁc capacity. Thus, this work aims at suppressing the corrosion of Al anode by adding an electrospun Al 2 O 3 interlayer on to the surface of the anode. The Al 2 O 3 interlayer e ﬀ ectively inhibits the self-corrosion of the Al anode. Further, the e ﬀ ects of the thickness of the Al 2 O 3 ﬁlm on corrosion behavior were investigated. The results showed that the Al–air battery with a 4 µ m Al 2 O 3 interlayer is more suitable for a low current density discharge, which could be applied for mini-watt devices. With a proper thickness of the Al 2 O 3 interlayer, corrosion of the anode was considerably suppressed without sacriﬁcing the discharge voltage at a low current density. The Al–air battery with a 4 µ m Al 2 O 3 interlayer provided a signiﬁcantly high capacity (1255 mAh / g at 5 mA / cm 2 ) and an excellent stability. This wo presents a promising approach for fabricating an inhibiting corrosion interlayer for solid Al–air battery designed for mini-watt devices.


Introduction
Portable and wearable electronic devices have received widespread attention for practical applications such as smart sensors [1,2] and flexible devices [3,4]. The possibility of using solid batteries as power sources in electronic devices is in urgent demand. With respect to liquid batteries, the solid ones have the well-known advantages of excellent temperature stability, high electrochemical stability, flexibility and absence of leakage [5,6]. These characteristics enhance the safety issues associated with energy storage. Lithium-ion batteries (LIBs) have been recognized as the energy sources for flexible electronic devices due to their reasonable theoretical energy density (~400 Wh/kg) and cycle life (~5000 cycles) [7]. However, the performance of LIBs is highly dependent on the expensive raw materials for the cathode [8]. In addition, the safety issues of LIBs, such as thermal runaway, pose ongoing challenges for their application in personal electronics [9]. Solid metal-air batteries (including Zn [10,11], Al [12][13][14], Fe [15] and Li [16]) have been widely agreed upon as a next-generation energy storage system owing to their light weight, high safety and environmental friendliness [17]. Solid metal-air batteries generally use alkaline gel electrolyte instead of traditional liquid alkaline electrolyte [18][19][20][21]. More specially, the Al-air battery is a promising candidate due to its lower market price (76% of Zn), greater reserve (1093 times of Zn), higher theoretical energy density (six times of Zn) [13] and specific capacity (2980 mAh/g) [22]. However, these theoretical targets are difficult to achieve with the current Al-air batteries. One of the main obstacles is the corrosion of Al anode in the alkaline electrolyte [18]. The hydrogen evolution corrosion in the discharging process limits both the cell practical voltage and the metal utilization [23,24].
To solve the above issues, one method has been suggested of alloying the Al anode with other elements, such as Ga, Zn, Ti, Sn, Mg, and In [25][26][27]. The results showed that aluminum alloys could increase the hydrogen over-potential and reduce hydrogen evolution of the anode. For the electrolyte, the researchers have found that adding additives (including organic [21,28], inorganic [29] and hybrid inhibitors [30]) helps to make the electrolyte less corrosive. It is generally recognized that the inhibitor molecules act by adsorbing on the metal surface to form a protecting film, which would lead to a decrease in corrosion rate [31,32]. To better tune the Al/electrolyte interface, surface modifications on Al anode have been reported to suppress the corrosion. Mutlu et al. [33] modified Al anode with copper nanoparticles by electrodeposition process. It protects the Al from the corrosion reaction by forming a barrier interlayer between the anode and electrolyte. Similarly, Lee et al. [34] coated polyaniline (PANI) film onto the Zn surface by chemical synthesis to inhibit the corrosion of Zn anode for a Zn-air battery. The corrosion inhibition efficiency is closely related to the uniformity of the protecting interlayer. Electrospinning is considered to be an efficient and versatile technique to produce ultrathin films with continuous nanofibers [35]. The film fabricated through electrospinning is a 3D porous structure with high porosity. This technique is usually applied to prepare organic or inorganic materials [36].
In this work, we modified an Al 2 O 3 interlayer on the surface of an Al anode by electrospinning to inhibit the corrosion of the anode in alkaline electrolyte. Al 2 O 3 has been proven to be an efficient inhibitor for the hydrogen evolution reaction. The study by Lee et al. [37] suggested that Al 2 O 3 has a positive effect on controlling the hydrogen evolution reaction of Zn anode in alkaline electrolyte for Zn-air battery. In addition, they proved that the Al 2 O 3 film could be more effective to control corrosion than just adding Al 2 O 3 powder into the electrolyte. Wongrujipairoj et al. [38] fabricated an Al 2 O 3 film onto the surface of Zn anode by sol-gel method. The Al 2 O 3 film effectively mitigated the corrosion of the Zn anode. However, limited reports are available on the electrospun Al 2 O 3 film as an inhibiting corrosion interlayer of the Al anode for solid Al-air batteries.
Here, we demonstrate an efficient electrospinning method to fabricate an Al 2 O 3 interlayer for a solid Al-air battery. The electrospinning strategy could cause a uniform deposition of Al 2 O 3 on the surface of the Al anode. The surface structures and morphology of the Al anode were analyzed by scanning electron microscope (SEM) and X-ray diffraction (XRD). The electrochemical measurements were used to evaluate the anode performance. The solid Al-air battery with the modified Al anode exhibited a stable operating voltage and a fairly high Al anode utilization and discharge capacity.

Fabrication of Al 2 O 3 Interlayers
The precursor solution was prepared by dissolving 0.2 g Al(NO 3 ) 3 ·9H 2 O and 0.8 g PAN in 15 mL of DMF. The solution was maintained under constant magnetic stirring for 24 h at room temperature to obtain a homogeneous solution. Then, the precursor solution was loaded into a plastic syringe with a stainless-steel nozzle, which was connected to a high voltage power supply. The syringes were pushed by a syringe pump with a flow rate of 1 mL/h. A rotating cylinder coated with aluminum foil was used as a collector. The applied voltage and distance of tip to collector were set as 15 kV and 15 cm, respectively. Subsequently, the collected electrospun nanofibers were stabilized in air at 300 • C for 2 h with a heating rate of 5 • C/min. The preparation process is shown in Figure 1b.

Characterization and Electrochemical Tests
The morphology of the samples was characterized by SEM (Su-8010, Hitachi, Tokyo, Japan). The crystalline structures of the samples were characterized using an XRD instrument (Bruker D8 Advance, Bruker Corp., Billerica, MA, USA) with a Cu kα radiation of 0.1541 nm as an X-ray source. The thickness of the Al2O3 interlayer was measured by Dektak XT (Bruker, Karlsruhe, Germany) profile meter.
The polymer alkaline gel electrolyte and flexible air cathode were prepared according to our previous paper [6,39], respectively. A 3 × 4 cm aluminum foil served as the metal anode. The solid Al-air battery was assembled as the sandwich type, as schematically illustrated in Figure 1e. The Al anode modified with an Al2O3 interlayer is shown in Figure 1c. In order to analyze the electrochemical performance of the Al anode with Al2O3 film, cyclic voltammetry was carried out at a scan rate of 100 mV/s from −1.9 to −0.5 V in 4 M KOH solution by the Metrohm Autolab. The constant current discharge was carried out using a battery testing system (CT2001A, LAND Electronics Co., Ltd., Wuhan, China). The electrochemical tests were carried out by an electrochemical workstation (RST5000, Shiruisi, Zhengzhou, China). An Hg/HgO and a platinum wire were used as reference and counter electrodes. Potentiodynamic polarization was measured at a scan rate of 1 mV/s. Electrochemical impedance spectroscopy (EIS) measurements were tested with an AC amplitude of 10 mV and frequency from 0.01 Hz to 100 kHz. All the electrochemical tests for every material were repeated at least three times to ensure reproducibility.

Characterization of the Al2O3 Interlayer
The surface morphology of the electrospun interlayer after heat treatment was investigated by SEM, as shown in Figure 2a. A perfect fibers formation characterized by a similar size of about 450 nm was observed for the samples, as shown in Figure 2b. A higher roughness degree (Figure 1d) after heat treatment was due to the decomposition of Al(NO3)3·9H2O along the nanofibers. In addition, PAN in the nanofibers could be decomposed and burned at 250 °C [40]. XRD patterns of the electrospun samples were reported in Figure 2c. A peak of 2θ = 17° was attributed to the (001) reflection of the orthorhombic PAN [41]; this is because PAN could not decompose completely until 700 °C [42]. Characteristic diffraction peaks of the Al2O3 phase at 2θ = 25.

Characterization and Electrochemical Tests
The morphology of the samples was characterized by SEM (Su-8010, Hitachi, Tokyo, Japan). The crystalline structures of the samples were characterized using an XRD instrument (Bruker D8 Advance, Bruker Corp., Billerica, MA, USA) with a Cu kα radiation of 0.1541 nm as an X-ray source. The thickness of the Al 2 O 3 interlayer was measured by Dektak XT (Bruker, Karlsruhe, Germany) profile meter.
The polymer alkaline gel electrolyte and flexible air cathode were prepared according to our previous paper [6,39], respectively. A 3 × 4 cm aluminum foil served as the metal anode. The solid Al-air battery was assembled as the sandwich type, as schematically illustrated in Figure 1e. The Al anode modified with an Al 2 O 3 interlayer is shown in Figure 1c. In order to analyze the electrochemical performance of the Al anode with Al 2 O 3 film, cyclic voltammetry was carried out at a scan rate of 100 mV/s from −1.9 to −0.5 V in 4 M KOH solution by the Metrohm Autolab. The constant current discharge was carried out using a battery testing system (CT2001A, LAND Electronics Co., Ltd., Wuhan, China). The electrochemical tests were carried out by an electrochemical workstation (RST5000, Shiruisi, Zhengzhou, China). An Hg/HgO and a platinum wire were used as reference and counter electrodes. Potentiodynamic polarization was measured at a scan rate of 1 mV/s. Electrochemical impedance spectroscopy (EIS) measurements were tested with an AC amplitude of 10 mV and frequency from 0.01 Hz to 100 kHz. All the electrochemical tests for every material were repeated at least three times to ensure reproducibility.

Characterization of the Al 2 O 3 Interlayer
The surface morphology of the electrospun interlayer after heat treatment was investigated by SEM, as shown in Figure 2a. A perfect fibers formation characterized by a similar size of about 450 nm was observed for the samples, as shown in Figure 2b. A higher roughness degree (Figure 1d) after heat treatment was due to the decomposition of Al(NO 3 ) 3 ·9H 2 O along the nanofibers. In addition, PAN in the nanofibers could be decomposed and burned at 250 • C [40]. XRD patterns of the electrospun samples were reported in Figure 2c. A peak of 2θ = 17 • was attributed to the (001) reflection of the orthorhombic PAN [41]; this is because PAN could not decompose completely until 700 • C [42].

Electrochemical Characterization of Al-Air Batteries
The open-circuit potential (OCP) of Al anodes with different thickness Al2O3 films in 4 M KOH electrolyte is displayed in Figure 3a. Compared with a pure Al anode, the Al anode with thicker Al2O3 film has the more negative OCP in alkaline electrolyte solution. This indicates that the Al2O3 film can considerably shift the OCP negatively. The negative potential shift may be explained by the fact that the Al2O3 film protects the Al anode and alleviates the polarization reaction. To examine the effects of the protection of Al2O3 film on the Al anode, the Al anode with Al2O3 films was subjected to 1 h of OCP exposure in the electrolyte solution followed by 1 h of anodic polarization under a current density of 5 mA/cm 2 . Figure 3b shows the potential transient of the Al anode recorded during four continuous cycles. The results show that the potential transient of Al anode with Al2O3 film is more stable during the cycling and has a better discharge performance than the pure Al anode, especially for the case of 6 μm Al2O3 film.

Electrochemical Characterization of Al-Air Batteries
The open-circuit potential (OCP) of Al anodes with different thickness Al 2 O 3 films in 4 M KOH electrolyte is displayed in Figure 3a. Compared with a pure Al anode, the Al anode with thicker Al 2 O 3 film has the more negative OCP in alkaline electrolyte solution. This indicates that the Al 2 O 3 film can considerably shift the OCP negatively. The negative potential shift may be explained by the fact that the Al 2 O 3 film protects the Al anode and alleviates the polarization reaction. To examine the effects of the protection of Al 2 O 3 film on the Al anode, the Al anode with Al 2 O 3 films was subjected to 1 h of OCP exposure in the electrolyte solution followed by 1 h of anodic polarization under a current density of 5 mA/cm 2 . Figure 3b shows the potential transient of the Al anode recorded during four continuous cycles. The results show that the potential transient of Al anode with Al 2 O 3 film is more stable during the cycling and has a better discharge performance than the pure Al anode, especially for the case of 6 µm Al 2 O 3 film.

Electrochemical Characterization of Al-Air Batteries
The open-circuit potential (OCP) of Al anodes with different thickness Al2O3 films in 4 M KOH electrolyte is displayed in Figure 3a. Compared with a pure Al anode, the Al anode with thicker Al2O3 film has the more negative OCP in alkaline electrolyte solution. This indicates that the Al2O3 film can considerably shift the OCP negatively. The negative potential shift may be explained by the fact that the Al2O3 film protects the Al anode and alleviates the polarization reaction. To examine the effects of the protection of Al2O3 film on the Al anode, the Al anode with Al2O3 films was subjected to 1 h of OCP exposure in the electrolyte solution followed by 1 h of anodic polarization under a current density of 5 mA/cm 2 . Figure 3b shows the potential transient of the Al anode recorded during four continuous cycles. The results show that the potential transient of Al anode with Al2O3 film is more stable during the cycling and has a better discharge performance than the pure Al anode, especially for the case of 6 μm Al2O3 film.    Al are at −1.13 and −1.06 V vs. Hg/HgO. The cyclic voltammogram of the Al anode with an Al 2 O 3 film displays that the peak A and B shifted positively, and the peaks shift more significantly in the positive direction with the increasing thickness of the Al 2 O 3 film. The peak A in the anodic sweep is due to the oxidation of Al to Al(OH) 4 − , and peak B in the cathodic sweep is due to the dissolution of the passivated film of Al(OH) 3 . The Al anode is more difficult to oxidize when protected by the Al 2 O 3 film, which would result in less hydrogen evolution and reduced corrosion. In addition, the voltage separation between peaks A and B changes little in the four curves, indicating that the redox behavior is almost the same.
Batteries 2020, 6, x FOR PEER REVIEW 5 of 12 film, which would result in less hydrogen evolution and reduced corrosion. In addition, the voltage separation between peaks A and B changes little in the four curves, indicating that the redox behavior is almost the same. In order to understand the effect of the Al2O3 interlayer thickness, the electrochemical impedance spectroscopy of the Al-air batteries with different thicknesses of Al2O3 interlayers are given in Figure  5. A typical Nyquist plot of a single-cell practical Al-air battery is composed of two semicircles that correspond to different battery process, described by an equivalent circuit with five elements [43] (  Table 1. The solution resistance Rs increases with the thickness of Al2O3 interlayer, which indicates that the electrolyte resistivity increases and the diffusion of ions becomes more and more difficult [43]. int R is also much higher than the pure Al anode; this is because the Al2O3 interlayer hinders direct contact between the electrolyte and the electrode. The ct R is used to indicate the degree of ease of reaction with the metal when the electrolyte reaches the anode surface. The larger the charge transfer resistance ct R , the more difficult it is to react. Compared with pure Al, the value of the coating capacitance coat C decreases by more than two orders of magnitude, reaching 2.69 × 10 −7 F with 6 μm Al2O3. In addition, the double layer capacitance dl C decreases as the thickness of Al2O3 interlayer increases, which is related to the porosity of the Al2O3 interlayer. dl C directly corresponds to the exposed surface area of the electrode [44]. The thicker Al2O3 interlayers have less porosity and better protection for the Al anode. Similar conclusions have also been obtained in the research of Díaz et al. [45]. It can be seen that int R and ct R increase in the following order: pure Al < Al with 2 μm Al2O3 interlayer < Al with 4 μm Al2O3 interlayer < Al with 6 μm Al2O3 interlayer, indicating that the coating of an Al2O3 interlayer on the Al anode can effectively improve corrosion resistance. In order to understand the effect of the Al 2 O 3 interlayer thickness, the electrochemical impedance spectroscopy of the Al-air batteries with different thicknesses of Al 2 O 3 interlayers are given in Figure 5. A typical Nyquist plot of a single-cell practical Al-air battery is composed of two semicircles that correspond to different battery process, described by an equivalent circuit with five elements [43] ( Figure 5 inset), namely solution resistance (R s ), solid/electrolyte interface (R int ), charge transfer resistance during electrochemical process (R ct ), and two constant phase elements (C coat and C dl ). The fitting parameters of the different components of the samples are summarized in Table 1. The solution resistance R s increases with the thickness of Al 2 O 3 interlayer, which indicates that the electrolyte resistivity increases and the diffusion of ions becomes more and more difficult [43]. R int is also much higher than the pure Al anode; this is because the Al 2 O 3 interlayer hinders direct contact between the electrolyte and the electrode. The R ct is used to indicate the degree of ease of reaction with the metal when the electrolyte reaches the anode surface. The larger the charge transfer resistance R ct , the more difficult it is to react. Compared with pure Al, the value of the coating capacitance C coat decreases by more than two orders of magnitude, reaching 2.69 × 10 −7 F with 6 µm Al 2 O 3 . In addition, the double layer capacitance C dl decreases as the thickness of Al 2 O 3 interlayer increases, which is related to the porosity of the Al 2 O 3 interlayer. C dl directly corresponds to the exposed surface area of the electrode [44]. The thicker Al 2 O 3 interlayers have less porosity and better protection for the Al anode. Similar conclusions have also been obtained in the research of Díaz et al. [45]. It can be seen that R int and R ct increase in the following order: pure Al < Al with 2 µm Al 2 O 3 interlayer < Al with 4 µm Al 2 O 3 interlayer < Al with 6 µm Al 2 O 3 interlayer, indicating that the coating of an Al 2 O 3 interlayer on the Al anode can effectively improve corrosion resistance.  To further confirm the corrosion resistance of the Al2O3 interlayer, Figure 6 and Table 2 indicate the Tafel curves and the related corrosion parameters of pure Al and the Al anode modified with different thicknesses of Al2O3 interlayers in the 4 M KOH electrolyte, respectively. Parameter %  is the protection efficiency and is obtained by the following equation [46]  in KOH solution. Compared to the pure Al anode, after the modification of the Al2O3 interlayer, the Tafel slopes of the cathode and anode both decreased. The results showed that the Al2O3 interlayer improved the anticorrosion performance of the Al anode. As can be seen in Figure 6, the variation in the self-corrosion potential was little, indicating that the performance of anticorrosion works by the geometrical coverage effect [47]. In addition, after modifying the anode with an Al2O3 interlayer, the polarization curves of the anode and cathode were almost parallel, suggesting that the modification of the Al2O3 interlayer did not change the reaction mechanism. The protection efficiency increased with the Al2O3 interlayer thickness. The   To further confirm the corrosion resistance of the Al 2 O 3 interlayer, Figure 6 and Table 2 indicate the Tafel curves and the related corrosion parameters of pure Al and the Al anode modified with different thicknesses of Al 2 O 3 interlayers in the 4 M KOH electrolyte, respectively. Parameter η% is the protection efficiency and is obtained by the following equation [46] η% = I corr − I corr(inh) where I corr and I corr(inh) are the corrosion current densities without and with the Al 2 O 3 interlayer in KOH solution. Compared to the pure Al anode, after the modification of the Al 2 O 3 interlayer, the Tafel slopes of the cathode and anode both decreased. The results showed that the Al 2 O 3 interlayer improved the anticorrosion performance of the Al anode. As can be seen in Figure 6, the variation in the self-corrosion potential was little, indicating that the performance of anticorrosion works by the geometrical coverage effect [47]. In addition, after modifying the anode with an Al 2 O 3 interlayer, the polarization curves of the anode and cathode were almost parallel, suggesting that the modification of the Al 2 O 3 interlayer did not change the reaction mechanism. The protection efficiency increased with the Al 2 O 3 interlayer thickness. The I corr of the Al with 6 µm Al 2 O 3 interlayer (61.3 µA/cm 2 ) is much more smaller than that of pure Al (427.5 µA/cm 2 ), and η% reached 85.66%.  The electrochemical performance of the Al-air battery was investigated by recording polarization and power density curves with different thickness Al2O3 interlayers, as shown in Figure 7a,b. The Alair battery with an Al2O3 interlayer (2 and 4 μm) behaves similarly to the pure Al at a low current region (0.1-5 mA/cm 2 ). However, the power density and the voltage decreased significantly compared with the batteries using a pure Al anode at a high current region, indicating a significant hydroxyl shortage. This is because the Al2O3 interlayer effectively inhibits the direct contact between the electrolyte and the anode. The thin interlayer hinders the transport of hydroxide ions, leading to a decrease in conductivity of the electrolyte compared to the free electrolyte without the Al2O3 interlayer. It is worth noting that the Al-air battery with a 4 μm Al2O3 interlayer has a current reverse at a high current region. This phenomenon is much more obvious in the case of the 6 μm Al2O3 interlayer. When increasing the thickness of the Al2O3 interlayer, the battery performance gradually decreases, which is mainly due to the reduced electrolyte conductivity. The mass transport loss is also gradually aggravated, indicating that hydroxide ion concentration plays an important role in supporting a high discharge current density. The battery encounters a server mass transport loss at a high current density, but the corrosion of the Al anode is inhibited at the same time. The Al-air battery with an Al2O3 interlayer suppresses Al corrosion by sacrificing its high current density output in this manner. The Al2O3 interlayer thickness could affect the battery performance by two aspects. On the one hand, a thicker Al2O3 interlayer could better suppress anode corrosion, but it is unable to provide enough hydroxide ions. On the other hand, a thinner Al2O3 interlayer could lead to a lower ionic resistance, but the effect of inhibiting corrosion may be limited. In order to explore the effect of Al2O3 interlayer thicknesses on the battery characteristics, we have studied a single-cell anode and cathode polarization curves, as shown in Figure 7c. It can be seen that the cathode curves remained identical, while there were significant differences in the anode curves. The two polarization curves for 2 and 4 μm Al2O3 interlayers are likely the same at the low current region. This is because a lower concentration of hydroxide ions can meet the need of discharge. However, a 6 μm Al2O3 interlayer seriously affects the charge transfer, even at a low current region. At a high current density region, the phenomenon of hydroxyl starvation becomes more and more  The electrochemical performance of the Al-air battery was investigated by recording polarization and power density curves with different thickness Al 2 O 3 interlayers, as shown in Figure 7a,b. The Al-air battery with an Al 2 O 3 interlayer (2 and 4 µm) behaves similarly to the pure Al at a low current region (0.1-5 mA/cm 2 ). However, the power density and the voltage decreased significantly compared with the batteries using a pure Al anode at a high current region, indicating a significant hydroxyl shortage. This is because the Al 2 O 3 interlayer effectively inhibits the direct contact between the electrolyte and the anode. The thin interlayer hinders the transport of hydroxide ions, leading to a decrease in conductivity of the electrolyte compared to the free electrolyte without the Al 2 O 3 interlayer. It is worth noting that the Al-air battery with a 4 µm Al 2 O 3 interlayer has a current reverse at a high current region. This phenomenon is much more obvious in the case of the 6 µm Al 2 O 3 interlayer. When increasing the thickness of the Al 2 O 3 interlayer, the battery performance gradually decreases, which is mainly due to the reduced electrolyte conductivity. The mass transport loss is also gradually aggravated, indicating that hydroxide ion concentration plays an important role in supporting a high discharge current density. The battery encounters a server mass transport loss at a high current density, but the corrosion of the Al anode is inhibited at the same time. The Al-air battery with an Al 2 O 3 interlayer suppresses Al corrosion by sacrificing its high current density output in this manner. The Al 2 O 3 interlayer thickness could affect the battery performance by two aspects. On the one hand, a thicker Al 2 O 3 interlayer could better suppress anode corrosion, but it is unable to provide enough hydroxide ions. On the other hand, a thinner Al 2 O 3 interlayer could lead to a lower ionic resistance, but the effect of inhibiting corrosion may be limited. In order to explore the effect of Al 2 O 3 interlayer thicknesses on the battery characteristics, we have studied a single-cell anode and cathode polarization curves, as shown in Figure 7c. It can be seen that the cathode curves remained identical, while there were significant differences in the anode curves. The two polarization curves for 2 and 4 µm Al 2 O 3 interlayers are likely the same at the low current region. This is because a lower concentration of hydroxide ions can meet the need of discharge. However, a 6 µm Al 2 O 3 interlayer seriously affects the charge transfer, even at a low current region. At a high current density region, the phenomenon of hydroxyl starvation becomes more and more obvious as the thickness of the Al 2 O 3 interlayer increases. This illustrates that the Al-air battery with Al 2 O 3 interlayer is more suitable for a low current density discharge.
Batteries 2020, 6, x FOR PEER REVIEW 8 of 12 obvious as the thickness of the Al2O3 interlayer increases. This illustrates that the Al-air battery with Al2O3 interlayer is more suitable for a low current density discharge.  Figure 8 shows the discharge behavior of the Al-air battery with different thicknesses of Al2O3 interlayers at low current densities (1, 3 and 5 mA/cm 2 ). From the polarization curves in Figure 7a, the Al-air battery with 6 μm Al2O3 interlayer could only achieve a lower voltage even at a low current density. Therefore, the discharge performance in the case of 6 μm Al2O3 interlayer is not considered in the test. As shown in Figure 8a-c, the Al-air battery with an Al2O3 interlayer showed a longer discharge time than pure Al. The improved sustainability of the Al anode is due to the suppression of corrosion. The Al-air battery with a 4 μm Al2O3 interlayer has the longest discharge time. Only 0.016 g Al with a 4 μm Al2O3 interlayer as an anode could sustain a current density of 1 mA/cm 2 for 10.6 h, 3 mA/cm 2 for 5.75 h, and 5 mA/cm 2 for 4.16 h. The discharge voltage changes little compared to pure Al anode and is better sustained at all three current densities, indicating that the hydroxyl ions are enough to support such current densities. The battery finally encounters an instant drop in voltage because the amount of Al is exhausted at the end of the discharge process. In order to investigate stability during the discharge process, the rate discharge performance of Al-air batteries with different thicknesses of Al2O3 interlayers at different current densities are compared in Figure 8d. The Al-air battery with an Al2O3 interlayer exhibits significantly stable output voltage within current densities ranging from 1 to 5 mA/cm 2 . Within the range, the discharge voltage plateaus of Al-air batteries with 2 and 4 μm Al2O3 interlayers vary little compared with the Al-air battery at the same current density. The stable discharge performance can be attributed to that fact that the hydroxide ions provided by the electrolyte are sufficient for the anodic reaction, even if some of the hydroxide ions have been blocked by the Al2O3 interlayer. By increasing the current density to 10 mA/cm 2 , the discharge voltage of Al-air batteries with Al2O3 interlayer decreases significantly, especially for the case of the 4 μm Al2O3 interlayer, indicating that the hydroxide ions are not enough to meet such a large current discharge. This further illustrates that the Al-air batteries with an Al2O3 interlayer are more suitable for a low-current discharge.   Figure 7a, the Al-air battery with 6 µm Al 2 O 3 interlayer could only achieve a lower voltage even at a low current density. Therefore, the discharge performance in the case of 6 µm Al 2 O 3 interlayer is not considered in the test. As shown in Figure 8a-c, the Al-air battery with an Al 2 O 3 interlayer showed a longer discharge time than pure Al. The improved sustainability of the Al anode is due to the suppression of corrosion. The Al-air battery with a 4 µm Al 2 O 3 interlayer has the longest discharge time. Only 0.016 g Al with a 4 µm Al 2 O 3 interlayer as an anode could sustain a current density of 1 mA/cm 2 for 10.6 h, 3 mA/cm 2 for 5.75 h, and 5 mA/cm 2 for 4.16 h. The discharge voltage changes little compared to pure Al anode and is better sustained at all three current densities, indicating that the hydroxyl ions are enough to support such current densities. The battery finally encounters an instant drop in voltage because the amount of Al is exhausted at the end of the discharge process. In order to investigate stability during the discharge process, the rate discharge performance of Al-air batteries with different thicknesses of Al 2 O 3 interlayers at different current densities are compared in Figure 8d. The Al-air battery with an Al 2 O 3 interlayer exhibits significantly stable output voltage within current densities ranging from 1 to 5 mA/cm 2 . Within the range, the discharge voltage plateaus of Al-air batteries with 2 and 4 µm Al 2 O 3 interlayers vary little compared with the Al-air battery at the same current density. The stable discharge performance can be attributed to that fact that the hydroxide ions provided by the electrolyte are sufficient for the anodic reaction, even if some of the hydroxide ions have been blocked by the Al 2 O 3 interlayer. By increasing the current density to 10 mA/cm 2 , the discharge voltage of Al-air batteries with Al 2 O 3 interlayer decreases significantly, especially for the case of the 4 µm Al 2 O 3 interlayer, indicating that the hydroxide ions are not enough to meet such a large current discharge. This further illustrates that the Al-air batteries with an Al 2 O 3 interlayer are more suitable for a low-current discharge. Furthermore, Figure 9a,b summarize the corresponding discharge time and capacities of the Alair batteries. It is apparent that the solid Al-air battery with a 4 μm Al2O3 interlayer is more appropriate to work at low current densities in order to achieve better utilization of the Al anode. The highest specific capacity of 1255 mAh/g is achieved with a 4 μm Al2O3 interlayer at 5 mA/cm 2 . This value is still better than those of a conventional Al-air battery with a high-purity Al anode in both gelled [13] and liquid electrolyte [48]. Due to the limited contact of electrolyte and anode, together with the porous structure of Al2O3 interlayer, the amount of hydroxide ions and their diffusion to the Al anode is greatly suppressed. The high utilization of the Al anode is due to the special transfer of hydroxide ions.  Furthermore, Figure 9a,b summarize the corresponding discharge time and capacities of the Al-air batteries. It is apparent that the solid Al-air battery with a 4 µm Al 2 O 3 interlayer is more appropriate to work at low current densities in order to achieve better utilization of the Al anode. The highest specific capacity of 1255 mAh/g is achieved with a 4 µm Al 2 O 3 interlayer at 5 mA/cm 2 . This value is still better than those of a conventional Al-air battery with a high-purity Al anode in both gelled [13] and liquid electrolyte [48]. Due to the limited contact of electrolyte and anode, together with the porous structure of Al 2 O 3 interlayer, the amount of hydroxide ions and their diffusion to the Al anode is greatly suppressed. The high utilization of the Al anode is due to the special transfer of hydroxide ions. Furthermore, Figure 9a,b summarize the corresponding discharge time and capacities of the Alair batteries. It is apparent that the solid Al-air battery with a 4 μm Al2O3 interlayer is more appropriate to work at low current densities in order to achieve better utilization of the Al anode. The highest specific capacity of 1255 mAh/g is achieved with a 4 μm Al2O3 interlayer at 5 mA/cm 2 . This value is still better than those of a conventional Al-air battery with a high-purity Al anode in both gelled [13] and liquid electrolyte [48]. Due to the limited contact of electrolyte and anode, together with the porous structure of Al2O3 interlayer, the amount of hydroxide ions and their diffusion to the Al anode is greatly suppressed. The high utilization of the Al anode is due to the special transfer of hydroxide ions.

Conclusions
The present study aims to examine the impact of an Al 2 O 3 interlayer on anodic corrosion in a solid Al-air battery. The Al 2 O 3 interlayer was fabricated through electrospinning on the surface of the Al anode. SEM and XRD measurements confirmed the porous structure and composition of the electrospun interlayer. Electrochemical tests were performed to investigate the efficiency of the Al 2 O 3 interlayer and battery performance. It was established that the Al 2 O 3 interlayer had a significant effect on Al corrosion. The results showed that the Al-air battery with an Al 2 O 3 interlayer is more suitable for low current density discharges. The batteries could be applied for mini-watt devices with a low current requirement, such as portable electronics and biosensors. It achieves the purpose of suppressing anode corrosion by sacrificing high current output. In addition, the effect of the Al 2 O 3 interlayer thickness on corrosion resistance. As the Al 2 O 3 interlayer thickness increases, the corrosion resistance increases, but the transport of hydroxide ions is also suppressed. Discharge experiments showed that an Al-air battery with a Al 2 O 3 interlayer provided an excellent stability and a significantly high capacity. The specific capacities of the Al-air battery with 2 and 4 µm Al 2 O 3 interlayers are 816 ± 24 and 1255 ± 33 mAh/g at 5 mA/cm 2 , which is much more than pure Al anode (416 ± 35 mAh/g). Generally, the addition of an Al 2 O 3 interlayer on the surface of an anode can suppress the anodic corrosion, thus improving the capacity of the Al-air battery. The electrospun Al 2 O 3 interlayer for a solid Al-air battery is very promising for the mini-watt electronics.